Metal salts of hindered aromatic phenols

Abstract

Reaction of a phenol with a metal salt of an alcohol produces a metal phenolate salt of a phenol. When a hindered phenol is used a hindered metal phenolate is produced. Such hindered metal phenolate salts are useful in driving the synthesis reaction of hindered phenol esters and phosphite esters to completion.

Description

FIELD OF THE INVENTION

[0001] The present invention is directed to a method of making metal salts of phenols. More particularly the present invention is directed to a method of making metal salts of hindered phenols.

BACKGROUND OF THE INVENTION

[0002] Organic phosphites are used in the stabilization of a wide variety of polymeric systems. Many different phosphites have been proposed for use either alone or in combination with other stabilizers. Such phosphites and their utilities are described in U.S. Pat. Nos. 4,371,647, 4,656,302, 4,705,879, 5,126,475, 5,141,975, and 5,438,086. The importance of organic phosphites as stabilizers has lead to the development of a variety of specialty organic phosphites that have enhanced effectiveness for stabilization.

[0003] Sterically hindered organic phosphites, and in particular phosphites based upon glycols or polyhydric alcohols (e.g. pentaerythritol) and containing alkyl, aryl, or alkyl-substituted aryl groups wherein the substitution is selected from the group consisting of t-butyl, t-amyl, t-hexyl, cyclohexyl, t-pentyl, and t-octyl, are especially desirable compounds due to their enhanced hydrolytic stability, ease of handling and compatibility with a wide variety of polymeric systems. The phosphite esters prepared from sterically hindered alcohols are also especially preferred for their improved hydrolytic stability over other alkyl substituted phosphites as well as their enhanced compatibility with some polymeric resins, especially polyolefins.

[0004] The organic diphosphites are generally prepared using methods involving reactions between the appropriate hydroxy compounds and phosphorous trihalides, e.g., phosphorous trichloride. Such methods and other useful methods are described in U.S. Pat. Nos. 3,839,506, 4,116,926, 4,290,976, 4,440,696, and 4,492,661. The ease of substitution of the halides on the phosphorous trihalide decreases as each halide is replaced. For example, in the preparation of bis(aryl)pentaerithritol diphosphites, the pentaerithritol hydroxyls readily react with a phosphorous trihalide to yield a bis(disubstituted halo phosphite (i.e., an intermediate di-substituted diphosphorohalidite). The displacement of the third halo group is less than quantitative and is considerably slower in rate. Additionally, displacement of the third halo group by a sterically hindered phenol is even more difficult and requires elevated temperatures and/or use of a catalyst.

[0005] In order to increase the rate of reaction and the degree of completion for displacing the third halide with a sterically hindered moiety, various techniques have been generally utilized in the art. These techniques include: elevating the reaction mixture temperature and the use of hydrogen halide acceptors, e.g., amines. Such techniques are described in U.S. Pat. Nos. 3,281,506, 4,237,075, 4,312,818, 4,440,696, and 4,894,481.

[0006] Generally in the case of diphosphites derived from sterically hinderd alcohols, the procedures of the prior art result in undesirable product mixtures. Additionally, various by-product phosphite compounds are also formed leading to low yields of the desired product. The resulting phosphite mixture containing a halo-phosphite is extremely difficult to purify and the residual halo-phosphite can lead to acid impurities that affect the long term stability of the desired organic phosphite, as well as affecting the stability of thermoplastic compositoins where the phosphite is employed as a stabilizer.

[0007] Various processes have been described in the prior art yet each suffers from some undesirable limitation. For example, U.S. Pat. No. 4,739,090 describes a process utilizing xylene as a solvent. The final product is isolated by filtration and the filtrate can be recycled. This process is deficient in resulting in at least about five percent or more impurities that require further crystallization to remove. This patent is silent on the form of the pentaerythritol utilized in the reaction.

[0008] U.S. Pat. No. 5,103,035 describes low temperature reaction conditions in chlorinated solvents. This process is undesirable due the difficulties in safely handling chlorinated solvents and a second solvent has to be utilized in order to bring the final product out of solution.

[0009] U.S. Pat. No. 5,438,086 describes a process for making diphosphites based upon pentaerythritol and 2,4-dicumylphenol wherein the dicumyl phenol is first reacted with phosphorous trichloride followed by allowing the reaction with the pentaerythritol. This process afforded only a 66% yield and acid numbers of 2 to 6, both of which are unacceptable.

[0010] The process of making metal salts of hindered phenols has generally required an ammonia solution of an alkali metal to be reacted with the hindered phenol in order to yield the metal phenbolate salt (Houben-Weyl, Methoden der Organischen Chemie, Phenolen, vol. VI/1c, p. 1189 (1976)).

[0011] It is therefore apparent that a need continues to exist for improved processes for the preparation of phosphite esters prepared from sterically hindered alcohols and phenols.

SUMMARY OF THE INVENTION

[0012] The process of the present invention provides for a process for the preparation of a metal phenolate comprising reacting a phenol having the formula: 1

[0013] wherein each R1, R2, and R3 is independently selected from the group consisting of hydrogen, methyl, ethyl, n-propyl, iso-propyl, n-butyl, t-butyl, t-amyl, t-hexyl, cyclohexyl, cumyl, t-pentyl, and t-octyl with a metal alcoholate having the formula (R4O)xQ where R4O is derived from the corresponding alcohol R4OH, Q is a metal cation having a valence x, to produce a metal phenolate and an alcohol R4OH wherein said metal phenolate has the formula: 2

[0014] wherein Q,x and each R1, R2, and R3 are as previously defined and removing the alcohol R40H from the metal phenolate. The present invention further provides for conducting the process of the invention in the presence of a solvent.

DETAILED DESCRIPTION OF THE INVENTION

[0015] The present invention comprises a process to convert phenols, abbreviated ΦOH, of the formula 3

[0016] wherein each R1, R2, and R3 is independently selected from the group consisting of hydrogen, methyl, ethyl, n-propyl, iso-propyl, n-butyl, t-butyl, t-amyl, t-hexyl, cyclohexyl, cumyl, t-pentyl, and t-octyl to a metal phenolate, abbreviated (ΦO)xQ, of the formula: 4

[0017] where each R1, R2, and R3 is selected from the group consisting of hydrogen, methyl, ethyl, n-propyl, iso-propyl, n-butyl, t-butyl, t-amyl, t-hexyl, cyclohexyl, cumyl, t-pentyl, and t-octyl, and Q is a metal cation having a valence x, i.e oxidation state. It should be noted that the choices for R1, R2, and R3 of the phenol become the choices for R1, R2, and R3 of the metal phenolate. Further when R1, R2, and R3 are selected from the group consisting of n-propyl, iso-propyl, n-butyl, t-butyl, t-amyl, t-hexyl, cyclohexyl, cumyl, t-pentyl, and t-octyl the phenol is considered a hindered phenol. The oxidation state or valence (used interchangeably herein) of the metal cation Q may vary in integer values between 1 and 4. Q may be any metal cation that is synthetically convenient, wherein the corresponding phenolate salt may correspond to the phenolate esters used for the preparation of the phosphite esters of hindered alcohols. The metal cations, Q, most suitable for the metal phenolate salt are selected from the group consisting of the alkali metals, the alkaline earth metals, the transition metals and the non-transition metals of Groups III, IV and V subject to the limitation that the halides of these metals are ionic salts. By halides the term includes the elements of Group VII of the periodic table, i.e. fluorine, chlorine, bromine, iodine and astatine. Preferred metals are the alkali metals and the alkaline earth metals; more preferred metals are the alkali metals; and the most preferred metals are sodium and potassium.

[0018] The present invention comprises the following process: (a) reacting ΦOH, preferably a hindered phenol, with (R4O)xQ, a metal alcoholate, in a reaction mixture to produce reaction products comprising R4OH and (ΦO)xQ, where x is as previously defined and (b) removing R4OH from the reaction products. R4OH is any alcohol where R4 is any monovalent organic radical, preferably R4 may be a 1 to 20 carbon atom organic monovalent radical. More preferably R4 is selected from the group of monovalent organic radicals consisting of methyl, ethyl, n-propyl, iso-propyl, n-butyl, 2-butyl, 2-methyl-propyl and tertiary butyl. The process of the present invention may be conducted in any chemically convenient fashion known in the art, particularly in solution. A particularly convenient method of preparation involves the use of an amine solvent for the phenol precursor, ΦOH, dissolving or in the case where the metal alcoholate is not soluble in the solvent slurrying a metal alcoholate, (R4O)xQ, therein, reacting the phenol precursor and the metal alcoholate to produce the metal phenolate, (ΦO)xQ, and R4OH and removing the R4OH.

[0019] The R4OH, or product alcohol, may be removed in any number of means known in the art, for example by distillation of the alcohol away from the reaction products, by distillation under vaccuum with or without the application of heat, by liquid liquid extraction, either concurrent or countercurrent, or by treatment with another solvent to induce a phase separation that also separates the two reaction products R4OH and (ΦD)xQ from each other. These various techniques of removing the product alcohol, R4OH, may be amplified in their efficacy by the application of a temperature differential, i.e. either by selectively heating or cooling to increase the amount of the R4OH removed from the reaction products.

[0020] When it is desired to perform the process of the present invention in solution an aprotic organic solvent should be used. Depending on solubility concerns the aprotic solvent may be either non-polar or dipolar. Examples of aprotic organic solvents include aliphatic hydrocarbons e.g. pentane, hexane, heptane, octane and the like, iso-pentane, iso-hexane, iso-heptane, iso-octane and the like, aromatic hydrocarbons, e.g. benzene, toluene, and xylene, mesitylene, naphthalene and the like, halogentated aliphatic hydrocarbons, e.g. methylene chloride, chloroform, carbon tetrachloride, dichloromethane, 1,2-dichloro-ethane; halogenated aromatic hydrocarbons such as chlorobenzene and dichlorobenzene; esters such as ethyl acetate, butyl acetate and ethyl benzoate; ketones e.g. acetone, methyl ethyl ketone and the like; ethers such as diethylether, di-isopropylether, t-butyl methyl ether, dimethoxyethane, dioxane, tetrahydrofuran, glycolethers, such as ethyleneglycol-methylether, ethyleneglycol-ethylether, diethyleneglycol-monomethylether or diethyleneglycol-monoethylether and the like; nitrogen compounds such as alkyl amines such as tri-methyl amine, tri-ethyl amine tri-propyl amine, tri-propyl amine, tri-iso-propyl amine and the like, acetonitrile, dimethylacetamide, benzonitrile, N,N-dimethylformamide, N,N-dimethylacetoamide, nitrobenzene, N-methylpyrrolidone, aromatic N-heterocycles, such as pyridine, picoline or quinoline; sulfur compounds such as carbon disulfide and dimethyl sulfoxide; phosphorus compounds such as hexamethylphosphoramide; and combinations thereof.

[0021] The present invention describes the reaction of a phenol with a metal salt of an alcohol, i.e. a metal alcoholate, to produce a metal phenolate salt of a phenol. Preferably the process of the present invention utilizes a hindered phenol. Such salts are particularly useful in driving the synthesis reaction of hindered phenol esters (e.g. reactions with acyl halides) and phosphite esters (e.g reactions with halo-phosphites or halo-phosphates) to completion.

[0022] Experimental

[0023] 66.9 g of 2, 4, 6-tri-t-butylphenol was dissolved or dispersed into 213.5 g of tri-n-propyl amin. To this solution was added 13.5 of sodium methoxide. The mixture was heated in flask until reflux occurred at about 150° C. When the reflux temperature dropped below 150° C., distillate was condensed and removed from the reaction mixture until the vapor temperature in the flask rose above 150° C. then the mixture was again refluxed. When the vapor temperature dropped below 150° C., distillate was condensed and removed from the reaction mixture until the vapor temperature rose above 150° C. This alternate process of reflux and condensation was repeated until 8.0 g of methyl alcohol, CH3OH had been distilled Away from the reaction mixture. Approximately 112 g of tri-n-propyl amine was stripped from the reaction mixture leaving about 71 g of sodium 2,4,6-tri-t-butyl phenolate in about 100 g of tri-n-propyl amine as a 40 weight percent slurry of the phenolate salt in the amine solvent.

Claims

1. A process for the preparation of a metal phenolate comprising reacting a phenol having the formula:

2. The process of claim 1. A process for the preparation of a metal phenolate comprising reacting a phenol having the formula:

3. The process of claim 1 wherein R4 is a monovalent organic radical having from one to twenty carbon atoms.

4. The process of claim 2 wherein R4 is a monovalent organic radical having from one to twenty carbon atoms.

5. The process of claim 1 wherein R4 is selected from the group consisting of methyl, ethanyl, n-propyl, iso-propyl, n-butyl, 2-butyl, 2-methyl-propyl and tertiary butyl.

6. The process of claim 2 wherein R4 is selected from the group consisting of methyl, ethyl, n-propyl, iso-propyl, n-butyl, 2-butyl, 2-methyl-propyl and tertiary butyl.

7. The process of claim 1 where Q is selected from the group consisting of the alkali metals, the alkaline earth metals, the transition metals and the non-transition metals of Groups III, IV and V subject to the limitation that the halides of these metals are ionic salts.

8. The process of claim 2 where Q is selected from the group consisting of the alkali metals, the alkaline earth metals, the transition metals and the non-transition metals of Groups III, IV and V subject to the limitation that the halides of these metals are ionic salts.

9. The process of claim 1 wherein wherein each R1, R2, and R3 is independently selected from the group consisting of hydrogen, methyl, ethyl, n-propyl, iso-propyl, n-butyl, t-butyl, t-amyl, and t-hexyl.

10. The process of claim 2 wherein wherein each R1, R2, and R3 is independently selected from the group consisting of hydrogen, methyl, ethyl, n-propyl, iso-propyl, n-butyl, t-butyl, t-amyl, and t-hexyl.

11. The process of claim 2 wherein the solvent is selected from the group consisting of aliphatic hydrocarbons, aromatic hydrocarbons, halogentated aliphatic hydrocarbons, halogenated aromatic hydrocarbons, esters, ketones, ethers, glycolethers, nitrogen compounds, carbon disulfide, dimethyl sulfoxide; phosphorus compounds such as hexamethylphosphoramide; and combinations thereof.

12. The process of claim 11 where the nitrogen compounds are amines.

13. The process of claim 12 where the amine is tri-n-propyl amine.

14. The process of claim 13 where each R1, R2, and R3 is t-butyl.

15. The process of claim 14 where Q is an alkali metal.

16. The process of claim 15 where the alkali metal is sodium.

17. The process of claim 16 where R4 is methyl.

18. A process for the preparation of a metal phenolate consisting essentially of reacting a phenol having the formula:

19. The process of claim 18 conducted in the presence of a solvent.

20. A process for the preparation of a metal phenolate consisting of reacting a phenol having the formula: