Metathesis Catalyst System for Polymerizing Cycloolefins

Abstract
A process to form a cyclic olefin polymerization catalyst which includes contacting a metal alkoxide with a transition metal halide to form a transition metal precatalyst, and contacting the transition metal precatalyst with a metal alkyl activator to form the activated catalyst comprising a transition metal carbene moiety. A cyclic olefin polymerization process is also disclosed.
Description
BACKGROUND

The active species of Ziegler-Natta (“ZN”) type metathesis polymerization catalyst for cycloolefin polymerization (Natta, G. et al. (1964) Angew. Chem. Int. Ed. Engl., v.3(11), pp. 723-729) have been formed in-situ by adding in sequence a metal compound such as WCl6, an alkoxide regulation ligand precursor such as a substituted aromatic alcohol, and an activator such as AlEt3. These catalysts may have an undefined structure, resulting in uncontrollable, non-reproducible processes and polymers having undesirable molecular weight distributions, stereo-selectivity (trans:cis ratio), and the like. Polymerization activity can be low due to dilution, an inefficient environment for catalyst activation, and/or generation of catalyst poisons such as HCl or Cl2, which are also hazardous.


Commercial scaling of cycloolefin polymerization is very challenging. Homogeneous ZN processes require the addition of a diluent quench, often ethanol, to stop polymerization, precipitate the product, and separate it from catalyst residue, which can result in an unusable, discolored product. Recovery and recycle of monomer and catalyst are difficult.


U.S. Pat. No. 3,607,853 discloses a three-component catalyst system, WCl6, t-BuOCl, and AliBu3, sequentially added to cyclopentene benzene solution that generates Cl2:





WCl6+t-BuOCl→WCl5(Ot-Bu)+Cl2


and forms undefined tungsten carbene compounds.


GB 1,389,979 discloses another three-component catalyst system, WCl6, 2-iPrPhOH or 2,6-diiPrPhOH, and AlEtCl2:





WCl6+4 ArOH→W(OAr)4Cl2+4HCl


This catalyst is prepared in a separate container followed by heating 100° C. to remove HCl, and then added to the cyclopentene nearly neat with the activator AlEtCl2 in a small amount of chlorobenzene solvent, presumably following the reaction below:





W(OAr)4Cl2+(2+x)AlEtCl2→W(OAr)4(═CH-Me)+Ethane+2AlCl3+xAlEtCl2


where ArOH is 2-iPrPhOH or 2,6-diiPrPhOH and x=0-5.5.


An example of the quench that these homogenous systems require to avoid Mw changes and discoloration during product isolation is disclosed in U.S. Pat. No. 3,607,853, where roughly 9 kg benzene were used for reaction, another 1 kg benzene with ethanol used for quenching, and 24 kg ethanol used to isolate 1.4 kg product. Such processes are laborious, non-reproducible, and generally not cost effective.


SUMMARY

This summary is provided to introduce a selection of concepts that are further described below in the detailed description. This summary is not intended to identify key or essential features of the claimed subject matter, nor is it intended to be used as an aid in limiting the scope of the claimed subject matter.


Disclosed herein is a process to form a cyclic olefin polymerization catalyst comprising contacting a metal alkoxide (IIIa) with a transition metal halide (IV) to form a transition metal precatalyst (VIIIa) according to the general formula:




embedded image


contacting the transition metal precatalyst (VIIIa) with a metal alkyl activator (A) to form the activated catalyst comprising a transition metal carbene moiety Mv=C(R*)2 according to the general formula:




embedded image


wherein Mu is a Group 1, 2, or 13 metal of valance u, preferably Li, Na, Ca, Mg, Al, or Ga; c is from 1 to 3 and ≤u; m=1/3, 1/2, 1, 2, 3, or 4 and c*m≤v−2; a is 1, 2, or 3 and a≤u; n is a positive number but a*n is in between 2 to 10; Mv is a Group 5 or 6 transition metal of valance v; X is halogen, each R′ is independently a monovalent hydrocarbyl comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table; each R is independently a C1 to C8 alkyl; and each R* is independently H or a C1 to C7 alkyl.


In embodiments according to the instant invention a cyclic olefin polymerization process comprises contacting a cyclic olefin polymerization catalyst according one or more embodiments herein with a C4-C20 cyclic olefin monomer comprising at least one cyclic olefin moiety in a polymerization reactor under conditions sufficient to form a reaction product mixture comprising a polymer, unreacted monomer, catalyst, and optionally a solvent; and recovering the polymer.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is an exemplary 13C NMR spectrum showing the chemical shift assignments of an exemplary cyclopentene polymer, also referred to as polypentenamer; and



FIG. 2 is the structure of a catalyst ligand precursor according to an embodiment, determined using X-ray single-crystal diffraction.





DETAILED DESCRIPTION

The term “alkyl” or “alkyl group” interchangeably refers to a saturated hydrocarbyl group consisting of carbon and hydrogen atoms. An alkyl group can be linear, branched, cyclic, or substituted cyclic.


The term “cycloalkyl” or “cycloalkyl group” interchangeably refers to a saturated hydrocarbyl group wherein the carbon atoms form one or more ring structures.


The term “aryl” or “aryl group” interchangeably refers to a hydrocarbyl group comprising an aromatic ring structure therein.


For the purposes of this disclosure and the claims thereto, the new numbering scheme for the Periodic Table Groups is used as in Chem. Eng. News (1985) v.63, pg. 27. Therefore, a “Group 4 metal” is an element from Group 4 of the Periodic Table.


Unless otherwise indicated, a substituted group means such a group in which at least one atom is replaced by a different atom or a group. Thus, a substituted alkyl group can be an alkyl group in which at least one hydrogen atom is replaced by a hydrocarbyl group, a halogen, any other non-hydrogen group, and/or a least one carbon atom and hydrogen atoms bonded thereto is replaced by a different group. Preferably, a substituted group is a radical in which at least one hydrogen atom has been substituted with a heteroatom or heteroatom containing group, preferably with at least one functional group, such as halogen (Cl, Br, I, F), NR*2, OR*, SeR*, TeR*, PR*2, AsR*2, SbR*2, SR*, BR*2, SiR*3, GeR*3, SnR*3, PbR*3, and the like or where at least one heteroatom has been inserted within the hydrocarbyl radical, such as halogen (Cl, Br, I, F), O, S, Se, Te, NR*, PR*, AsR*, SbR*, BR*, SiR*2, GeR*2, SnR*2, PbR*2, and the like, where R* is, independently, hydrogen or a hydrocarbyl.


For purposes herein, “heteroatom” refers to non-metal or metalloid atoms from Groups 13, 14, 15 and 16 of the periodic table, typically which supplant a carbon atom. For example, pyridine is a heteroatom containing form of benzene. Halogen refers to atoms from group 17 of the periodic table.


The terms “hydrocarbyl radical,” “hydrocarbyl group,” or “hydrocarbyl” interchangeably refer to a group consisting of hydrogen and carbon atoms only. A hydrocarbyl group can be saturated or unsaturated, linear, branched, cyclic or acyclic, aromatic or non-aromatic.


Substituted hydrocarbyl radicals are radicals in which at least one hydrogen atom has been substituted with a heteroatom or heteroatom containing group, preferably with at least one functional group, such as halogen (Cl, Br, I, F), NR*2, OR*, SeR*, TeR*, PR*2, AsR*2, SbR*2, SR*, BR*2, SiR*3, GeR*3, SnR*3, PbR*3, and the like or where at least one heteroatom has been inserted within the hydrocarbyl radical, such as halogen (Cl, Br, I, F), O, S, Se, Te, NR*, PR*, AsR*, SbR*, BR*, SiR*2, GeR*2, SnR*2, PbR*2, and the like, where R* is, independently, hydrogen or a hydrocarbyl.


In some embodiments, the hydrocarbyl radical is independently selected from methyl, ethyl, ethenyl and isomers of propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, nonadecyl, eicosyl, heneicosyl, docosyl, tricosyl, tetracosyl, pentacosyl, hexacosyl, heptacosyl, octacosyl, nonacosyl, triacontyl, propenyl, butenyl, pentenyl, hexenyl, heptenyl, octenyl, nonenyl, decenyl, undecenyl, dodecenyl, tridecenyl, tetradecenyl, pentadecenyl, hexadecenyl, heptadecenyl, octadecenyl, nonadecenyl, eicosenyl, heneicosenyl, docosenyl, tricosenyl, tetracosenyl, pentacosenyl, hexacosenyl, heptacosenyl, octacosenyl, nonacosenyl, triacontenyl, propynyl, butynyl, pentynyl, hexynyl, heptynyl, octynyl, nonynyl, decynyl, undecynyl, dodecynyl, tridecynyl, tetradecynyl, pentadecynyl, hexadecynyl, heptadecynyl, octadecynyl, nonadecynyl, eicosynyl, heneicosynyl, docosynyl, tricosynyl, tetracosynyl, pentacosynyl, hexacosynyl, heptacosynyl, octacosynyl, nonacosynyl, and triacontynyl. Also included are isomers of saturated, partially unsaturated and aromatic cyclic structures wherein the radical may additionally be subjected to the types of substitutions described above. Examples include phenyl, methylphenyl, benzyl, methylbenzyl, naphthyl, cyclohexyl, cyclohexenyl, methylcyclohexyl, and the like. For this disclosure, when a radical is listed, it indicates that radical type and all other radicals formed when that radical type is subjected to the substitutions defined above. Alkyl, alkenyl, and alkynyl radicals listed include all isomers including where appropriate cyclic isomers, for example, butyl includes n-butyl, 2-methylpropyl, 1-methylpropyl, tert-butyl, and cyclobutyl (and analogous substituted cyclopropyls); pentyl includes n-pentyl, cyclopentyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1-ethylpropyl, and neopentyl (and analogous substituted cyclobutyls and cyclopropyls); butenyl includes E and Z forms of 1-butenyl, 2-butenyl, 3-butenyl, 1-methyl-1-propenyl, 1-methyl-2-propenyl, 2-methyl-1-propenyl, and 2-methyl-2-propenyl (and cyclobutenyls and cyclopropenyls). Cyclic compound having substitutions include all isomer forms, for example, methylphenyl would include ortho-methylphenyl, meta-methylphenyl and para-methylphenyl; dimethylphenyl would include 2,3-dimethylphenyl, 2,4-dimethylphenyl, 2,5-dimethylphenyl, 2,6-diphenylmethyl, 3,4-dimethylphenyl, and 3,5-dimethylphenyl.


The term “Cn” group or compound refers to a group or a compound comprising carbon atoms at total number thereof of n. Thus, a “Cm-Cn” group or compound refers to a group or compound comprising carbon atoms at a total number thereof in the range from m to n. Thus, a C1-C50 alkyl group refers to an alkyl group comprising carbon atoms at a total number thereof in the range from 1 to 50.


The term “olefin,” alternatively termed “alkene,” refers to an unsaturated hydrocarbon compound having a hydrocarbon chain containing at least one carbon-to-carbon double bond in the structure thereof, wherein the carbon-to-carbon double bond does not constitute a part of an aromatic ring. The olefin may be linear, branched, or cyclic.


For purposes of this specification and the claims appended thereto, when a polymer or copolymer is referred to as comprising an olefin, including, but not limited to ethylene, propylene, and butene, the olefin present in such polymer or copolymer is the polymerized form of the olefin. For example, when a copolymer is said to have an “ethylene” content of 35 wt % to 55 wt %, it is understood that the mer unit in the copolymer is derived from ethylene in the polymerization reaction and said derived units are present at 35 wt % to 55 wt %, based upon the weight of the copolymer. A “polymer” has two or more of the same or different mer units. A “homopolymer” is a polymer having mer units that are the same. A “copolymer” is a polymer having two or more mer units that are different from each other. A “terpolymer” is a polymer having three mer units that are different from each other. “Different” as used to refer to mer units indicates that the mer units differ from each other by at least one atom or are different isomerically. Thus, an “olefin” is intended to embrace all structural isomeric forms of olefins, unless it is specified to mean a single isomer or the context clearly indicates otherwise. An oligomer is a polymer having a low molecular weight, such as an Mn of 21,000 g/mol or less (preferably 10,000 g/mol or less), and/or a low number of mer units, such as 100 mer units or less (preferably 75 mer units or less).


The term “cyclic olefin” refers to any cyclic species comprising at least one ethylenic double bond in a ring. The atoms of the ring may be optionally substituted. The ring may comprise any number of carbon atoms and/or heteroatoms. In some cases, the cyclic olefin may comprise more than one ring. A ring may comprise at least 3, at least 4, at least 5, at least 6, at least 7, at least 8, or more, atoms. Non-limiting examples of cyclic olefins include cyclopentene, cyclohexene, norbornene, dicyclopentadiene, bicyclo compounds, oxabicyclo compounds, and the like, all optionally substituted. “Bicyclo compounds” are a class of compounds consisting of two rings only, having two or more atoms in common.


Unless specified otherwise, the term “substantially all” with respect to a molecule refers to at least 90 mol % (such as at least 95 mol %, at least 98 mol %, at least 99 mol %, or even 100 mol %).


Unless specified otherwise, the term “substantially free of” with respect to a particular component means the concentration of that component in the relevant composition is no greater than 10 mol % (such as no greater than 5 mol %, no greater than 3 mol %, no greater than 1 mol %, or about 0%, within the bounds of the relevant measurement framework), based on the total quantity of the relevant composition.


The terms “catalyst” and “catalyst compound” are defined to mean a compound capable of initiating catalysis and/or of facilitating a chemical reaction with little or no poisoning/consumption. In the description herein, the catalyst may be described as a catalyst precursor, a pre-catalyst compound, or a transition metal compound, and these terms are used interchangeably. A catalyst compound may be used by itself to initiate catalysis or may be used in combination with an activator to initiate catalysis. When the catalyst compound is combined with an activator to initiate catalysis, the catalyst compound is often referred to as a pre-catalyst or catalyst precursor. A “catalyst system” is combination of at least one catalyst compound, at least one activator, an optional co-activator, and an optional support material, where the system can polymerize monomers to form polymer.


All numerical values within the detailed description and the claims herein are modified by “about” or “approximately” the indicated value, and take into account experimental error and variations that would be expected by a person having ordinary skill in the art.


In the present disclosure, unless specified otherwise, percent refers to percent by weight, expressed as “wt %.”


In the present disclosure, all molecular weight data are in the unit of g·mol−1. Unless indicated otherwise, molecular weight of oligomer or polymer materials and distribution thereof in the present disclosure are determined using gel permeation chromatography employing a Tosoh EcoSEC High Temperature GPC system (GPC-Tosoh EcoSEC; Tosoh Bioscience LLC). GPC was used to determine the polypentenamer Mw, Mn and Mw/Mn using the high temperature gel permeation chromatograph equipped with a differential refractive index detector (DRI). Three high temperature TSK gel column (Tosoh GMHHR-H(20)HT2) were used. The nominal flow rate was 1.0 mL/min, and the nominal injection volume was 300 μL. The various transfer lines, columns, and dual flow differential refractometer were contained in an oven maintained at 160° C. The mobile phase Solvent for the experiment is prepared by dissolving 1.2 grams of butylated hydroxytoluene as an antioxidant in 4 liters of Aldrich reagent grade 1,2,4 trichlorobenzene (TCB). The TCB mixture was then filtered through a 0.1 μm teflon filter. The TCB was then degassed with an online degasser before entering the GPC instrument.


The polydispersity index (PDI), also referred to as the molecular weight distribution (MWD), of the material is then the ratio of Mw/Mn.


For purposes herein, the polymer trans:cis ratio was measured with a standard 13C NMR techniques according to methods known in the art. Samples were prepared with 66.67 mg/ml of CDCl3 (deuterated chloroform) in a 10 mm tube. The 13C NMR spectra were measured on a Bruker 600 MHz cryoprobe with inverse gated decoupling, 20 s delay, 90° pulse, and 512 transients. Assignments were based on assignments from O. Dereli et al. (2006) European Polymer Journal v.42, pp. 368-374. Three different positions were used for calculation of the trans/cis composition:




embedded image




    • 1. vinyl peaks with trans at 130.3 ppm and cis at 129.8 ppm;

    • 2. alpha position trans/cis (tc) at 32.2 ppm, trans/trans (tt) at 32.07 ppm, cis/cis (cc) at 26.9 ppm and cis/trans (ct) at 26.74 ppm;

    • 3. beta position cis/cis (cc) at 29.86 ppm, cis/trans (trans/cis) (ct+tc) at 29.7 ppm and trans/trans (tt) at 29.54 ppm;

    • 4. Trans=tt+0.5*(ct+tc); and

    • 5. Cis=cc+0.5*(ct+tc).


      The calculation for each of groups 1-3 above (i.e., vinyl, alpha, and beta) were averaged to get an average trans and cis composition. An exemplary 13C NMR spectra is shown in FIG. 1.





For purposes herein, small scale polymerization conversion rates were monitored and estimated with 1H NMR method using a Bruker 400 MHz instrument, as indicated. Pulse program zgcw30 was used with D1=60s and ns=2 or 4. CDCl3 was the lock solvent. The chemical shift of cyclopentene monomer double bond protons was measured to be about 5.75 ppm and the chemical shift of polypentenamer double bond protons was experimentally determined to be about 5.53 ppm. Integral from 5.45 to 6.00 ppm (Im+p) was used to cover the two chemical shifts, which was then set to 100% to represent total cyclopeneten. The integral from 4.55 to 5.60 ppm (Ip+RS) is assigned the polypentenamer overlap with the right 13C satellite chemical shift of cyclopentene. To substrate the 13C satellite contribution from the overlapped integral, the similar intensity left 13C satellite of cyclopentene was integrated from 5.93 to 5.97 ppm (ILS) and the conversion C calculated as follows:






C=(IP+RS−ILS)/Im+p


Appropriate 13C decoupling program was identified when the ILS was found to be zero.


The following abbreviations may be used through this specification: Bu is butyl, nBu is normal butyl, iBu is isobutyl, tBu is tertiary butyl, ptBu is para-tertiary butyl, Et is ethyl, Me is methyl, pMe is para-methyl, PDI is polydispersity index (Mw/Mn) Ph is phenyl, Pr is propyl, iPr is isopropyl, n-Pr is normal propyl, RT is room temperature (i.e., approximately 23° C.), THF is tetrahydrofuran, and tol is toluene.


In embodiments according to the instant invention, a process to form a cyclic olefin polymerization catalyst comprises:


contacting a metal alkoxide (IIIa) with a transition metal halide (IV) to form a transition metal precatalyst (VIIIa) according to the general formula:




embedded image


contacting the transition metal precatalyst (VIIIa) with a metal alkyl activator (A) to form the activated catalyst comprising a transition metal carbene moiety Mv=C(R*)2 according to the general formula:




embedded image


wherein Mu is a Group 1, 2, or 13 metal of valance u, preferably Li, Na, Ca, Mg, Al, or Ga; c is from 1 to 3 and ≤u;


m=1/3, 1/2, 1, 2, 3, or 4 and c*m≤v−2;


a is 1, 2, or 3 and a≤u;


n is a positive number but a*n is in between 2 to 10;


Mv is a Group 5 or 6 transition metal of valance v;


X is halogen,


each R′ is independently a monovalent hydrocarbyl comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table;


each R is independently a C1 to C8 alkyl;


each R* is independently H or a C1 to C7 alkyl; and


each Z is independently halide or a C1 to C8 alkyl radical.


Accordingly, Embodiments may include Group 2 metal and Group 13 metal dialkoxides (e.g., Mg(OR′)2) and trialkoxides (e.g., Al(OR′)2X) and Group 13 trialkoxide (e.g., Al(OR′)3). In embodiments, metal alkoxide IIIa may comprise a Group 1 metal, e.g., NaOR′ (u=1, c=1, d=0); a Group 2 metal, e.g., Mg(OR′)Cl (u=2, c=1, d=1) or Mg(OR′)2 (u=2, c=2, u=0); or a Group 13 metal, e.g., Al(OR′)Cl2 (u=3, c=1, d=2), Al(OR′)2Cl (u=3, c=2, d=1), or Al(OR′)3 (u=3, c=3, d=0).


In embodiments of the invention, the metal alkoxide (IIIa) is formed by contacting a compound comprising a hydroxyl functional group (I) with a Group 1 or Group 2 metal hydride Mu*(H)u according to the general formula:




embedded image


wherein Mu* is a Group 1 or 2 metal of valance u*, preferably Na, Li, Ca, or Mg;


c is 1 or 2 and c is ≤u*;


X is halogen; and


each R′ is independently a monovalent hydrocarbyl comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table.


In embodiments of the invention, the metal alkoxide (IIIa) is formed by contacting a compound comprising a hydroxyl functional group (I) with the metal alkyl activator (A) to form the metal alkoxide (IIIa) according to the general formula:




embedded image


wherein each R′ is independently a monovalent hydrocarbyl comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table; wherein Mu is a Group 1, 2, or 13 metal of valance u, preferably Li, Na, Ca, Mg, Al, or Ga; a is 1, 2, or 3; a is ≤u; and each R is independently a C1 to C8 alkyl.


In embodiments of the invention, the process further comprises contacting a mixture of metal alkoxides with one or more ligand donors (D) under conditions sufficient to crystallize and isolate the metal alkoxide (IIIa) as one or more dimeric coordinated metal alkoxide-donor composition according to the general structure (XXV-GD2):




embedded image


wherein Mu is a Group 1, 2, or 13 metal of valance u, preferably Li, Na, Ca, Mg, Al, or Ga; each R′ is independently a monovalent hydrocarbyl comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table; each L is R′O—, or halide X; each D is selected from dialkyl ethers, cyclic ethers, trialkyl amines, or a combination thereof, preferably tetrahydrofuran, methyl-tertbutyl ether, a C1-C4 dialkyl ether, a C1-C4 trialkyl amine, or a combination thereof, and n is 1, 2, 3, or 4.


In embodiments of the invention, a process to form a cyclic olefin polymerization catalyst comprises contacting an alkyl-metal alkoxide (IIIb) with a transition metal halide (IV) in a reaction mixture to form the activated catalyst (V) comprising a transition metal carbene moiety Mv=C(R*)2 according to the general formula:




embedded image


wherein Mub is a Group 2 or 13 metal of valance u, preferably Ca, Mg, Al, or Ga, most preferably Al; a is 1 or 2 and but <u; x is ½ or 1, 2, 3, or 4 but x*a< or =v−2; Mv is a Group 5 or 6 transition metal of valance v; X is halogen; each R′ is independently a monovalent hydrocarbyl comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table; each R is independently a C1 to C8 alkyl; and each R* is independently H or a C1 to C7 alkyl.


In embodiments of the invention, the reaction mixture further comprises a metal alkyl activator (A) according to the formula MuRaX(u-a), wherein Mu is a Group 1, 2, or 13 metal of valance u, preferably Li, Na, Ca, Mg, Al, or Ga; a is 1, 2, or 3; a≤u; and when present, X is halogen.


In embodiments of the invention, Mv is W, Mo, Nb, or Ta. In some embodiments, two or more R′O— ligands are connected to form a single bidentate chelating moiety.


In one or more embodiments of the invention, a process to form a cyclic olefin polymerization catalyst comprises:


i) contacting a compound comprising a hydroxyl functional group (I) with an alkyl aluminum compound (II) to form an aluminum precatalyst (III) and the corresponding residual (Q1+Q2) according to the general formula:




embedded image


wherein m is 1 or 2; a is 1 or 2; each Z is a C1 to C8 alkyl; each R′ is independently a monovalent hydrocarbyl comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table; each Y is a C1 to C8 alkyl, halogen, or an alkoxy hydrocarbyl moiety represented by —OR5, wherein each R5 is a C1 to C20 alkyl radical;


iia) wherein Y=C1 to C8 alkyl, contacting the aluminum precatalyst (III) with a transition metal halide (IV) to form an activated carbene containing cyclic olefin polymerization catalyst (V) comprising a transition metal carbene moiety Mv=C(R*)2 according to the general formula:




embedded image


wherein each R* is independently H or a C1 to C7 alkyl; or contacting the aluminum precatalyst (III) with a transition metal halide (IV) to form a transition metal precatalyst, (VIII) according to the general formula:




embedded image


wherein m=1, 2, or 3; y=1/3, 1/2, 1, 2, 3, or 4; y*m+3-m≤v−2; and


ii) contacting the transition metal precatalyst, (VIII) with a metal alkyl activator (A) to form the activated carbene containing cyclic olefin polymerization catalyst (V) comprising a transition metal carbene moiety Mv=C(R*)2 according to the general formula:




embedded image


wherein R* is a hydrogen or C1-C7 alkyl. Applicant has discovered that embodiments in which R* is C1-C7 alkyl provide improvement, since activators in which R* is an alkyl having 8 or more carbon atoms are not capable of directly activating the transition metal halide.


In one or more embodiments of the invention wherein a=3 such, the alkyl aluminum compound (II) is a trialkyl-aluminum (IX) and the residual is an alkane HR according to the general formula:




embedded image


wherein m=1 or 2; and each R is independently a C1 to C8 alkyl radical.


In embodiments of the process, the aluminum precatalyst (III) is a dimer represented by structure (III-D) which is reacted with the transition metal halide (IV) to form the activated carbene containing cyclicolefin polymerization catalyst (V) according to the general formula:




embedded image


wherein each R is C1 to C8 alkyl; each R* is independently hydrogen or C1 to C7 alkyl; and each R′ is independently a monovalent hydrocarbyl comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table, or two or more of R′ are connected to form a bidentate chelating ligand. In embodiments wherein a=2 and Y is halogen such that the alkyl aluminum compound (II) is a dialkyl aluminum halide (VI), and the aluminum precatalyst is a di-halo tetrakis alkoxide aluminum dimer (VII) according to the general formula:




embedded image


and


the di-halo tetrakis alkoxide aluminum dimer (VII) is contacted with the transition metal halide (IV) to form a di-halo transition metal precatalyst (VIII) according to the general formula:




embedded image


and


wherein the di-halo transition metal precatalyst (VIII) is contacted with a metal alkyl activator (A) to form the activated carbene containing cyclic olefin polymerization catalyst (V) according to the general formula:




embedded image


wherein a=1, 2, or 3; and a is ≤u.


In one or more embodiments of the invention, a molar ratio of Mv to Mu-R in metal alkyl activator MuRaX(u-a) is from 1 to 2 to 1 to 15. In one or more embodiments the alkoxy ligand R′O— comprises a C7 to C20 aromatic moiety and wherein the O atom directly bonds to the aromatic ring; the compound comprising a hydroxyl functional group (I) is a bidentate dihydroxy chelating ligand (X′); the alkyl aluminum compound (II) is a dialkyl aluminum halide (VI), and the aluminum precatalyst (III) is an aluminum alkoxide mono-halide (XI) according to the general formula:




embedded image


wherein R1 is a direct bond between the two rings or a divalent hydrocarbyl radical comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table; R2 through R9 are each independently a monovalent hydrocarbyl radicals comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table, or two or more of R2 through R9 join together for form a ring having 40 or less atoms from Groups 14, 15, and/or 16 of the periodic table.


In one or more embodiments of the invention, the process further comprises contacting two equivalents of the aluminum alkoxide mono-halide (XI) with the transition metal halide (IV) to form a transition metal halo bis-alkoxide catalyst precursor (XII) according to the general formula:




embedded image


and contacting the transition metal halo bis-alkoxide catalyst precursor (XII) with a trialkyl aluminum compound (IX) to form the activated carbene containing cyclic olefin polymerization catalyst (XIII) according to the general formula:




embedded image


In embodiments, the process further comprises contacting one equivalent of the aluminum alkoxide mono-halide (XI) with a transition metal halide (IV) to form a transition metal halo alkoxide catalyst precursor (XIV) according to the general formula:




embedded image


and


contacting the transition metal halo alkoxide catalyst precursor (XIV) with a trialkyl aluminum compound (IX) to form the activated carbene containing cyclic olefin polymerization catalyst (XV) according to the general formula:




embedded image


In one or more embodiments of the process, the compound comprising a hydroxyl functional group (I) is a bidentate dihydroxy chelating ligand (X′); the alkyl aluminum compound (II) is a trialkyl aluminum (IX), and the aluminum precatalyst (III) is an alkyl aluminum alkoxide (XX) according to the general formula:




embedded image


wherein R1 is a direct bond between the two rings or a divalent hydrocarbyl radical comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table; R2 through R9 are each independently a monovalent hydrocarbyl radicals comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table, or two or more of R2 through R9 join together for form a ring having 40 or less atoms from Groups 14, 15, and/or 16 of the periodic table.


In embodiments, the process further comprises contacting two equivalents of the aluminum-alkyl alkoxide (XX) with a transition metal halide (V) to form the activated carbene containing cyclic olefin polymerization catalyst (XXI) according to the general formula:




embedded image


In embodiments of the invention, the process further comprises contacting one equivalent of the aluminum-alkyl alkoxide (XX) with a transition metal halide (V) to form the activated carbene containing cyclic olefin polymerization catalyst (XXIa) according to the general formula:




embedded image


In embodiments of the process, the compound comprising a hydroxyl functional group (I) is a mixture comprising a bidentate dihydroxy chelating ligand (X′) and a monodentate hydroxy ligand (XVI); the alkyl aluminum compound (II) is a trialkyl aluminum (IX), and the aluminum precatalyst (III) is an aluminum tri-alkoxide (XVII), the process further comprising i) forming the aluminum tri-alkoxide (XVII) according to the general formula:




embedded image


ii) contacting the aluminum tri-alkoxide (XVII) with a transition metal halide (IV) to form a transition metal alkoxide catalyst precursor (XVIII) according to the general formula:




embedded image


and


iii) contacting the transition metal alkoxide catalyst precursor (XVIII) with a trialkyl aluminum compound (IX) to form the activated carbene containing cyclic olefin polymerization catalyst (XIX) according to the general formula:




embedded image


wherein Mv is a Group 5 or Group 6 transition metal of valance v; X is halogen; R1 is a direct bond between the two rings of the bidentate ligand, or a divalent hydrocarbyl radical comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table; each of R2 through R14 is independently, a hydrogen, a monovalent radical comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table, a halogen, or two or more of R2 through R9 and/or two or more of R10 through R14 join together to form a ring comprising 40 atoms or less from Groups 14, 15, and 16 of the periodic table.


In embodiments of the invention, the compound comprising a hydroxyl functional group (I) is an aromatic compound comprising a phenoxy hydroxyl group Ar—OH (XXIV); the alkyl aluminum compound (II) is an alkyl aluminum halide, and the aluminum precatalyst (III) is a mixture of aluminum alkoxides (XXVa), (XXVb), and (XXVc), the process further comprising forming the mixture of aluminum alkoxides (XXVa), (XXVb), and (XXVc) according to the general formula:




embedded image


wherein x is from 1 to 2; and


ii) contacting the mixture of metal alkoxides with one or more ligand donors (D) under conditions sufficient to crystallize and isolate the metal alkoxide (IIIa) as one or more dimeric coordinated metal alkoxide-donor composition according to the general structure (XXV-GD2):




embedded image


wherein Mu is a Group 1, 2, or 13 metal of valance u, preferably Li, Na, Ca, Mg, Al, or Ga; each R′ is independently a monovalent hydrocarbyl comprising from 1 to 20 atoms selected from Groups 14, 15, and 16 of the periodic table; each L is R′O—, alkyl R as defined for structure A, or halide X; each D any O or N containing organic donor selected from ethers, preferably dialkyl ethers or cyclic ethers; ketones; amines, preferably trialkyl amines, aromatic amines, cyclic amines, and heterocyclic amines (e.g., pyridine); nitriles, preferably alkyl nitriles, aromatic nitriles, or a combination thereof, preferably tetrahydrofuran, methyl-tertbutyl ether, a C1-C4 dialkyl ether, a C1-C4 trialkyl amine, or a combination thereof; and n is 1, 2, 3, or 4.


In embodiments of the invention, a cyclic olefin polymerization process comprises contacting a cyclic olefin polymerization catalyst according to any one of the embodiments disclosed herein with a C4-C20 cyclic olefin monomer comprising at least one cyclic olefin moiety in a polymerization reactor under conditions sufficient to form a reaction product mixture comprising a polymer, unreacted monomer, catalyst, and optionally a solvent; and recovering the polymer.


In embodiments, the process further comprises separating the monomer from the reaction product mixture and recycling the monomer to the polymerization reactor; contacting the recovered catalyst with an activator prior to recycling to the polymerization reactor; or a combination thereof.


In one or more embodiments, the cyclic olefin polymerization process is continuous. In alternative embodiments, the cyclic olefin polymerization process is a batch process. In one or more embodiments, the polymerization comprises ring opening metathesis polymerization and the polymer comprises polyalkenamer, preferably polypentenamer, a cyclic olefin copolymer, and/or a cyclic olefin polymer.


In embodiments the cyclic olefin polymerization process further comprises recovering the catalyst and optionally the solvent from the reaction product mixture; and recycling at least a portion of the recovered catalyst, unreacted monomer, and/or optionally the solvent to the polymerization reactor.


In embodiments of the invention, the cyclic olefin polymerization process further comprises incorporating one or more C4-20 cyclic diolefins comprising at least one cyclic structure having the general formula:




embedded image


and/or


one or more functionalized C4-20 cyclic diolefins comprising at least one cyclic structure according to the general formula:




embedded image


as a comonomer into the reaction product mixture, wherein each functional group (FG) is integral to a corresponding cyclic structure and/or pendant to a corresponding cyclic structure, and wherein each FG is independently halogen, NR{circumflex over ( )}2, OR{circumflex over ( )}, SeR{circumflex over ( )}, TeR{circumflex over ( )}, PR{circumflex over ( )}2, AsR{circumflex over ( )}2, SbR{circumflex over ( )}2, SR{circumflex over ( )}, BR{circumflex over ( )}2, SiR{circumflex over ( )}3, GeR{circumflex over ( )}3, SnR{circumflex over ( )}3, PbR{circumflex over ( )}3, O, S, Se, Te, NR{circumflex over ( )}, PR{circumflex over ( )}, AsR{circumflex over ( )}, SbR{circumflex over ( )}, BR{circumflex over ( )}, SiR{circumflex over ( )}2, GeR{circumflex over ( )}2, SnR{circumflex over ( )}2, PbR{circumflex over ( )}2, or a combination thereof, and each R{circumflex over ( )} is independently hydrogen or a C1-C10 hydrocarbyl radical, r is greater than or equal to 1, and when present, s is greater than or equal to 1; preferably wherein the comonomer comprises norbornene, ethylidene norbornene, dicyclopentadiene, or a combination thereof.


In one or more embodiments of the invention, the cyclic olefin polymerization process further comprises:


(I) controlling Mw and/or a trans:cis ratio of the polymer by controlling a reactor temperature from −35° C. to 100° C.; controlling the amount of monomer recycled to the reactor; using the monomer as a reaction solvent; or a combination thereof;


(II) forming active catalyst species at a temperature less than or equal to about 5° C., followed by increasing the reaction temperature to a temperature less than 100° C.;


(III) incorporating an amount of an olefin, preferably an alpha olefin, preferably an alpha olefin comprising at least one hetero atom containing functional group into the cyclic olefin monomer to reduce the molecular weight of the polymer in the product mixture;


(IV) employing two or more cyclic olefin polymerization catalysts in the same or different reactors to produce polymer exhibiting:

    • i) a multi-modal Mw profile;
    • ii) a trans:cis molar ratio greater than 1;
    • iii) a trans:cis molar ratio less than 1; and/or


(V) employing multiple reactors connected in a sequence to produce heterophasic copolymers.


In one or more embodiments of the invention, the olefin comonomer has the general formula:





CH2═CH—(CH2)n—CH3;





CH2═CH—[(CH2)n(FG)s]—CH3; and/or





CH2═CH—(CH2)n-FG;


wherein each FG, when present, is independently halogen, NR{circumflex over ( )}2, OR{circumflex over ( )}, SeR{circumflex over ( )}, TeR{circumflex over ( )}, PR{circumflex over ( )}2, AsR{circumflex over ( )}2, SbR{circumflex over ( )}2, SR{circumflex over ( )}, BR{circumflex over ( )}2, SiR{circumflex over ( )}3, GeR{circumflex over ( )}3, SnR{circumflex over ( )}3, PbR{circumflex over ( )}3, O, S, Se, Te, NR, PR{circumflex over ( )}, AsR{circumflex over ( )}, SbR{circumflex over ( )}, BR{circumflex over ( )}, SiR{circumflex over ( )}, GeR{circumflex over ( )}2, SnR{circumflex over ( )}2, PbR{circumflex over ( )}2, or a combination thereof, and each R{circumflex over ( )} is independently a C1-C10 hydrocarbyl radical; n is greater than or equal to 1; and s, when present, is greater than or equal to 1.


In one or more embodiments of the invention, the transition metal Mv is preferably present in the catalyst at from 0.1 wt % to 30 wt %, based on the total amount of catalyst present. In embodiments, a molar ratio of transition metal M1 to aluminum (M1:Al) in the supported catalyst is preferably from 1:1000 to 4:10, based on the total number of moles of Mv and aluminum present.


In embodiments, the content of the catalyst metal may be controlled to prevent too high a loading. In embodiments, the transition metal loading may be controlled to achieve a desired activities by employing a metal alkyl such as MgR2 or AlR2X (X═R or halide; R═C1 to C20 alkyl) to replace a portion of the catalyst metal, e.g., AlR2X according to the following reaction scheme:




embedded image


In any embodiment of the invention, the process may preferably further comprise separating the monomer from the reaction product mixture and recycling the monomer to the polymerization reactor; contacting the catalyst with additional alkyl aluminum or another type of activator prior to recycling the catalyst to the polymerization reactor; or a combination thereof.


In one or more embodiments of the invention, a cyclic diolefin comonomer is supplied to the polymerization reactor. In embodiments the comonomer comprises norbornene, ethylidene norbornene, dicyclopentadiene, or a combination thereof.


In one or more embodiments of the invention, the polymer is preferably a polyalkenamer and the process may preferably further comprise controlling the Mw and/or the trans:cis ratio of the polymer by a) controlling a reactor temperature from −35° C. to 100° C.; b) controlling the amount of monomer recycled to the reactor; c) using the monomer as a reaction solvent; or a combination thereof, and/or forming the active catalyst species at temperature less than or equal to about 5° C., followed by increasing the reaction temperature to a temperature less than 100° C.; and/or the catalyst system according to the instant disclosure are prepared as an isolated single-site like catalyst compound before adding the catalyst to the reactor.


In embodiments, the catalyst is prepared using components and reaction schemes which eliminate hazardous by-products. Accordingly, embodiments of the instant disclosure allow for increased activity, stereo-selectivity, Mw/PDI, and/or the like to be better controlled and reproduced.


In embodiments of the instant disclosure, the carbene containing catalysts can be synthesized through more economical and environmentally friendly routes involving formation of catalyst precursors through reactions involving various aluminum alkyls, referred to herein as aluminum centered intermediates and/or aluminum compounds according to pathways disclosed herein. These pathways preferably involve clean one-pot reactions.


In embodiments of the invention, these byproducts are eliminated during the formation of the catalyst by converting the hydroxyl group to alkali salt, e.g., sodium or potassium salt according to the following process:


i) ROH+NaH→RONa+H2

ii) 4RONa+WCl6→WCl2(OR)4+4 NaCl


iii) WCl2(OR)4+m AlR′nX3-n→W(OAr)4═CHR″+R1H+2/3 AlCl3+(m−2/3) AlR′nX3-n

    • where n=1, 2, 3;
    • m X n is greater than or equal to 2
    • Ar is a substituted phenols, e.g., 4-MePhOH, 2-iPrPhOH, and the like;
    • X is a halide, preferably I, Br, or Cl;
    • the alkoxide —OR is a C3-C20 hydrocarbyl, typically a hydrocarbon including aliphatic and aromatic groups;
    • R″=H or alkane, and R′ is H forming the corresponding alkane.


In embodiments, an improvement is obtained using an aluminum alkyl to react with the alcoholic compound, which is then reacted with the metal chloride to directly form the carbene containing compound in-situ. In other embodiments, the catalyst is pre-formed in one-pot reaction without the generation of any harmful gas according to the general process: 2 ROH+AlR′3→2 Al(OR)2R′+2 HR′ (having a non-harmful alkane as the byproduct); followed by:





2Al(OR)2R′+WCl6→W(OR)4═CHR″+R1H+2AlCl3.


In embodiments in which the catalytically active carbene W═CHR is unstable, the more stable precursor W(OR)4X2 can be made in large quantity for storage and used later with an activator aluminum alkyl, e.g., AliBu3 according to the process:


I) 2 ROH+AlR′2X→2 Al(OR)2X+2 HR′ (non-harmful alkane)


II) 2 Al(OR)2X+WX6→W(OR)4XX2+2AlX3


III) W(OR)4X2+Ali-Bu3→W(OR)4═CHR″+AliBuX2


wherein X is halogen, preferably chlorine. In embodiments, the product of step II may be formed and stored and then activated according to step III as needed. Examples of such embodiments include:




embedded image


Another example according to an embodiment of the invention utilizes a process in which a dichloro tungsten tetrakis alkoxide is first formed, following by activation with the aluminum alkyl at low temperature according to the following reaction scheme:




embedded image


In embodiments, two or more phenoxy moieties can be present on the same molecule, consistent with the following reaction pathway:




embedded image


where a chelating ligand intermediate is formed followed by the dichloro metal compound prior to activation.


In related embodiments, the active catalyst may preferably be formed directly according to the reaction pathway shown in the following example:




embedded image


In other embodiments, mixed ligands such as a combination of chelating ligands and substituted phenols, may preferably be employed to form the catalyst according to the reaction pathway shown in the following example:




embedded image


Chelating ligands are those in which the hydroxyl groups are physically located such that they form a bidentate ligand. In such embodiments, suitable chelating ligands preferably include 2,2′-biphenol, substituted 2,2′-biphenols, and the like.


As is known in the art, the intermediate aluminum compounds of Ziegler-Natta compounds containing mixed ligands may exist as multiple species, e.g., AlAB2 formed in a non-polar solvent can show a distribution of AlA2B (minor), AlAB2 (major), and AlB3 in a polar solvent, due to the fast ligand exchanging between two neighbor Al atoms. For example, (4-MePhO)2AlCl is difficult to crystallize in non-polar solvent such as toluene because multiple species exist in an equilibrium:





2(4-MePhO)2AlCl↔(4-MePhO)AlCl2+(4-MePhO)3Al


This phenomena renders (4-MePhO)3Al difficult to crystallize. However, it has been discovered that crystallization of such aluminum intermediates may be accomplished by addition of a donor group, typically an ether and/or at tertiary amine. For example, using THF as a donor compound, (4-MePhO)3Al may be readily crystallized as a dimeric five coordinated Al species with one THF for each Al according to the following formula:




embedded image


wherein Ar is 4-Mephenyl.


Applicant has discovered that such THF and other adduct form highly active catalysts when used to construct the active catalyst with WCl6. Although many W compounds can polymerize THF to block or destroy the carbene formation, the molecular level THF present may only alter the metathesis polymerization behavior and yield different polymer structures (different Mw, trans:cis ratio, etc.) with the same ligand structure except with or without the coordinated THF. Other donor can be used as the donor, e.g., Et2O, MeOtBu, NMe3.


In embodiments of the invention, polymerization processes conditions and reactants may be selected to control the Mw and/or the trans:cis ratio of the polymers produced. In embodiments, the supported catalyst according to one or more embodiments is employed in a reactor comprising a filtration element that retains the supported catalyst but which allows the solution of product polymer, e.g., polyalkenamer such as polypentenamer, to pass through such that the polymer is effectively separated from the supported catalyst as part of a continuous process.


In embodiments, the temperature of the process is selected within a range from about −35 to 100° C., depending on the monomers used and the desired properties of the polymer. In other embodiments, the monomer is separated from the polymer and then recycled, e.g., to the polymerization reactor. Applicant has discovered that by controlling the amount of monomer recycle, the deep color of the final product caused by retention of the catalyst in the product can be avoided, along with the massive amounts of solvent typically required for residue removal. In embodiments, the monomer is used as the reaction solvent thus eliminating the quenching step due to the separation of product from the catalyst.


In embodiments, the invention may further include selecting the temperature at which the active catalyst species is formed. In embodiments, the active catalyst is formed at a temperature of less than 5° C., preferably less than 0° C., preferably less than −5° C., preferably less than −10° C., preferably less than −20° C., preferably less than or equal to −35° C. Applicant has discovered that by forming the catalyst at such low temperatures, followed by increasing the temperature of the polymerization reaction to a temperature of about 100° C. or less, preferably from about 0 to 40° C. The Group 5 or Group 6 transition metals used to form the active catalyst species, i.e., the carbene species, for cyclic olefin polymerization have been discovered to be more stable at these lower temperature compared to room temperature or higher. Applicant discovered that when the process includes forming the catalyst prior to contacting the monomer, the preferred formation temperature is less than or equal to about 0° C., more preferably less than about −20° C. or less than −35° C. If the active catalyst is generated in-situ, applicant has discovered a corresponding benefit by selecting a polymerization reaction temperature which is lower at the beginning, e.g., −5 to −35° C., for a period of time sufficient to form the active catalyst, followed by increasing the temperature, e.g., 0 to 40° C., for a batch polymerization process. In continuous embodiments, the reaction temperature may be set below about 5° C. to obtain a similar benefit.


In embodiments, the Mw and other properties of the polymer e.g., formation of functionalized end groups, multi-modal Mw control, and the like, by incorporation of one or more comonomers into the process.


In embodiments, a linear olefin, e.g., 1-hexene, may be included in the cyclic olefin monomer to reduce the polymer molecular weight. Applicant has discovered that increasing the ratio of linear olefin to cyclic olefin results in a lower molecular weight product.


In embodiments, the straight olefin can bear functional groups such as siloxane, amine groups, and the like. Suitable examples include CH2═CH—(CH2)n—OSiMe3 (n=1-20); CH2═CH—(CH2)n—NMe2 (n=1-20), or combinations thereof. In other embodiments, multi-modal Mw polymers may be produced by selecting the ligands used to form the catalyst according to the present invention. Accordingly, in embodiments the polycycloolefins produced according to the instant disclosure may further comprise chain-end functionality. In embodiments, the olefin chain termination agent CH2═CH—R comprises an R group comprising one or more functional groups. Accordingly, in embodiments the polymer chains with the functionalized termination groups will have functionality at the chain ends. Both the concentration of the functionalized termination groups, and the selection of the functional groups allow for control over the physical properties of the resulting polymers. Applicant has further discovered that control may be achieved by selecting the relative bulkiness of the ligand used to form multiple ligand environments with the same metal centers or by employing ligands having the same relative size (i.e., ligand bulkiness) with different metal centers, or a combination thereof.


In embodiments, the cis:trans ratio of the polymer has been discovered to result in different physical properties. This phenomenon is thought to be due to the faster crystallization of trans conformation relative to the amorphous cis conformation. In embodiments, the cis:trans ratios of the polymers can be controlled by selecting the ligands used to form the catalysts, the metal used to form the catalysts, or a combination thereof.


In embodiments, the invention may further include copolymerization systems, wherein one or more different cyclic olefins serve as the comonomer to form the product copolymers. Examples include the establishment of routes to long chain branching by the incorporation of side chain unsaturation, e.g., through vinyl norbornene, ethylidene norbornene, and/or the like in the backbone of the polymer. In embodiments, the comonomers may then act as initiation points for ROMP or cross metathesis reactions. In alternative embodiments, DCPD may be used as a comonomer to form polymers in which both rings of the monomer have been opened to produce a four armed star.


In alternative embodiments, properties of the product polymers may be controlled by employing polymerization systems comprising two or more reactors connected in a sequence. Embodiments may further include producing heterophasic copolymers.


EXAMPLES

The present disclosure can be further illustrated by the following non-limiting examples.


Catalyst formation comprises reacting a catalyst precursor with an activator to form an active catalyst, also referred to herein as comprising a carbene functional group. The catalyst precursor comprises a Group 5 or Group 6 metal, preferably tungsten, tantalum, niobium, and/or molybdenum. The activator is an alkyl aluminum and/or an alkyl aluminum halide compound.




embedded image


For purposes herein, WCl6 and MoCl5 are used as the catalyst precursor, or in forming the catalyst precursor, also referred to as a transition metal compound. Other compounds which could be used include TaCl5 and/or NbCl5. The activator comprises moieties having the general formula AlRmZ*(3-m), where each Z* is H, C1-C7 alkyl, alkoxy, or halogen. Examples include AlMe3, AlMe2Cl, AlMeCl2, AlEt2Cl, AlEtCl2, AlEt2(OR), AlEt(OR)2, and the like, wherein OR is an alkoxy radical and R can be any C1 to C20, preferably C1 to C10 aliphatic or aromatic radical with or without substituents.


Polymerization reactions include cyclo-olefin ring opening metathesis polymerization (ROMP) consistent with the following reaction, wherein the active catalyst is according to any embodiment or combination of embodiments disclosed herein:




embedded image


In the examples, the cyclic olefin monomers include cyclopentene, denoted as “cC5=”, however, other 6 to 10 membered ring containing cyclo-olefins, e.g., cyclohexene, cyclooctene, cyclodecene, and the like may be used.


In the following examples, WCl6 and MoCl5, aromatic alcoholic compounds (2-isopropylphenol, 2,6-diisopropylphenol, 4-methylphenol), tertiary butyl hypochloride, aluminum alkyls (e.g., triethylaluminum (AlEt3 or TEAL), triisobutylaluminum (AliBu3 or TIBAL), diethylaluminum chloride (Et2AlCl or DEAC), Ethylaluminum dichloride (EtAlCl2 or EADC)), NaH, cyclopentene, 1-hexene, and solvents (benzene, toluene, isohexane, ethanol), and antioxidant Irgonox 1076 were purchased from Sigma-Aldrich and used without further purification unless explicitly stated otherwise. Silica ES70X was obtained from PQ Corporation (Malvern, Pa., USA) and was calcined at about 200° C. for 3-4 hours to form the “low-temperature” silica support, or at about 600° C. for 3-4 hours to form the “high temperature” silica support, prior to use. All solvents were anhydrous grade and were further treated with activated 3 Å molecular sieves by storing the solvent in a container with 5-10 wt % molecular sieves for at least 24 hours prior to use.


Cyclopentene was treated with 3 Å molecular sieves the same way and was passed through an activated basic alumina column before use. All deuterated solvents (CDCl3, C6D6, CD2Cl2, d8-THF, and the like) were obtained from Cambridge Isotopes (Cambridge, Mass.) and dried over 3 Å molecular sieves before use. Other chemicals such as the aromatic alcohols, aluminum alkyls were used as received. All reactions were performed under an anhydrous inert nitrogen atmosphere using standard laboratory techniques unless otherwise stated.


A gel permeation chromatography method, Tosoh EcoSEC High Temperature GPC system (GPC-Tosoh EcoSEC), was used to determine the polypentenamer Mw, Mn and Mw/Mn using the high temperature gel permeation chromatography instrument (Tosoh Bioscience LLC), equipped with a differential refractive index detector (DRI). Three high temperature TSK gel column (Tosoh GMHHR-H(20)HT2) were used. The nominal flow rate was 1.0 mL/min, and the nominal injection volume was 300 μL. The various transfer lines, columns, and dual flow differential refractometer (the DRI detector) were contained in an oven maintained at 160° C. Solvent for the experiment is prepared by dissolving 1.2 grams of butylated hydroxytoluene as an antioxidant in 4 liters of Aldrich reagent grade 1,2,4 trichlorobenzene (TCB). The TCB mixture was then filtered through a 0.1 μm teflon filter. The TCB was then degassed with an online degasser before entering the GPC instrument.


Polymer solutions were prepared by placing dry polymer with about 10-15 wt % anti-oxidants of Irganox 1076 and Irgafos 168 in glass vials, adding the desired amount of TCB, then heating the mixture at 160° C. with continuous shaking for about 2 hours. All quantities were measured gravimetrically. The injection concentration was from 0.5 to 1.0 mg/mL, with lower concentrations being used for higher molecular weight samples. Flow rates in the apparatus was then increased to 1.0 mL/minute, and the DRI was allowed to stabilize for 2 hours before injecting the first sample. The molecular weight was determined relatively to polystyrene molecular weight standards in which the instrument was calibrated with a series of monodispersed polystyrene standards. All molecular weights are reported in g/mol unless otherwise noted.


A standard polycycloolefin sample, commercial neodymium butadiene rubber CB24 (ExxonMobil, Houston, Tex.) with known molecular weight Mw about 300 k was used to verify that the GPC method, and to confirm that the 160° C. temperature does NOT cause significant polymer cross-linking resulting in artificially high molecular weight determinations. The experimentally obtained result of a 339 k molecular weight for the commercial neodymium butadiene rubber CB24 indicates a non-significant cross-linking under the measurement conditions.


The polymer trans:cis ratio was measured with a standard 13C NMR instrument according to methods known in the art. Samples were prepared with 66.67 mg/ml of CDCl3 (deuterated chloroform) in a 10 mm tube. The 13C NMR spectra were measured on a Bruker 600 MHz cryoprobe with inverse gated decoupling, 20 s delay, 90° pulse, and 512 transients.


Assignments were based on assignments from O. Dereli et al. (2006) European Polymer Journal, v.42, pp. 368-374. Three different positions were used for calculation of the trans/cis composition:




embedded image




    • 1. vinyl peaks with trans at 130.3 ppm and cis at 129.8 ppm;

    • 2. alpha position trans/cis (tc) at 32.2 ppm, trans/trans (tt) at 32.07 ppm, cis/cis (cc) at 26.9 ppm and cis/trans (ct) at 26.74 ppm;

    • 3. beta position cis/cis (cc) at 29.86 ppm, cis/trans (trans/cis) (ct+tc) at 29.7 ppm and trans/trans (tt) at 29.54 ppm;

    • 4. Trans=tt+0.5*(ct+tc); and

    • 5. Cis=cc+0.5*(ct+tc).


      The calculation for each of groups 1-3 above (i.e., vinyl, alpha, and beta) were averaged to get an average trans and cis composition. An exemplary 13C NMR spectra is shown in FIG. 1.





As indicated, some small scale polymerization conversion rates were monitored and estimated with 1H NMR method using a Bruker 400 MHz instrument. Pulse program zgcw30 was used with D1=60 s and ns=2 or 4. CDCl3 was the lock solvent. The chemical shift of cyclopentene monomer double bond protons was measured to be about 5.75 ppm and the chemical shift of polypentenamer double bond protons was experimentally determined to be about 5.53 ppm. Integral from 5.45 to 6.00 ppm (Im+p) was used to cover the two chemical shifts, which was then set to 100% to represent total cyclopentene. The integral from 4.55 to 5.60 ppm (Ip+RS) is the polypentenamer overlapped with the right 13C satellite chemical shift of cyclopentene. To substrate the 13C satellite contribution from the overlapped integral, the similar intensity left 13C satellite of cyclopentene was integrated from 5.93 to 5.97 ppm (ILS) and the conversion C calculated as follows:






C=(IP+RS−ILS)/Im+p


Appropriate 13C decoupling programs produced an ILS equal to zero.


Polymerization of Cyclopentene with RO—X (X═H or Cl)+WCl6 (or MoCl5)+Al—R containing activator


Comparative Examples 1-1 to 1-5 and 1-7

Comparative example Cex1-1 and examples 1-2 is based on procedures known in the art, scaled to a 4 L jacketed filter reactor (Ace Glass Inc.) with a Lauda chiller capable of cooling to −35° C.


Examples 1-1 through 1-7 were prepared according to the following general procedure: in the 4 L Jacketed reactor, cyclopentene (cC5=) and optional solvent (toluene/benzene/hexane) was added. The reactor was then cooled to the desired temperature as noted. In a round bottom flask, transition metal basic catalyst WCl6 or MoCl5 and a solvent were added and mixed well with a magnet stirrer. Another round bottom flask was charged with the alkoxide precursor compound RO—X and a solvent. The RO—X solution was then slowly added to the solution WCl6 or MoCl5. The mixture was stirred for 1 hour. When required, N2 was blown on top of the reaction mixture to remove harmful gas such as HCl or Cl2 formed during the reaction process. Then prepared catalyst precursor was added to the cyclopentene solution in the 4 L jacketed filter reactor. The activator-aluminum-alkyl compound AlRmZ(3-m) was added to induce the polymerization and the reactor mixture was stirred and the temperature maintained for the desired reaction time.


A third flask was charged with Irgonox 1076 (BBHT), ethanol, solvent and NaHCO3. This reaction mixture was added to the stirring reactor to stop polymerization. The quenched reaction was then stirred for an additional 60 minutes.


The quenched reaction mixture (the polymer solution) was then added to 10 to 12 L of ethanol in a 5 gallon bucket and stirred to precipitate the resultant polymer from the reaction mixture and the polymer removed by filtration. Irgonox solution in toluene was then added on top of the polymer, and the resulting slurry was dried under vacuum in a vacuum oven at 50° C. for 24 hours. The catalyst preparation, polymerization conditions, and polymerization quench procedures for Examples 1 through 6 are summarized in Table 1. Yield, conversion, Mw, trans:cis ratio data are shown in Table 4.


Example 1-6

In example 1-6, the procedure further included addition of a straight chain alpha olefin in the reaction mixture to control molecular weight of the polymer. 0.5 g of 1-hexene (C6=) was added to form a (cC5=):(C6=) wt/wt ratio of 2000:1. As the example confirms, the chain length of the resulting polymer, i.e., the Mw, may be controlled by including an amount of an olefin chain termination agent CH2═CH—R, preferably a normal or straight-olefin chain termination agent, where R is a C1 to C20 hydrocarbon radical, preferably a straight-chain hydrocarbon radical.




embedded image


The ratio of straight chain olefin CH2═CH—R (e.g., 1-hexene) to cC5 determines the chain length and therefore the molecular weight of the polycycloolefins produced according to embodiments disclosed herein.


Example 1-6 suggests that inclusion in the reaction mixture of an alpha olefin bearing a functional group, e.g., a siloxy or amine group, can introduce the functionality to the polymer chain ends.









TABLE 1







Experiment Summary for Examples 1-1 to 1-7










Catalyst















Monomer/conditions
WCl6

Activator
RXN
Quench


















cC5═
Solvent
T
(MoCl5*)
RO—X
AIRmX(3−m)
Time
BBHT
EtOH
Solvent




















Run ID
g
Name
G
° C.
g
Formula
g
Name
g
min
g
ml
ml























CEx 1-1
1150
Benzene
1600
RT
3.0

tBuOCl

0.82
AliBu3
2.63
240
3
25
Bezene 400


CEx 1-2
960
Benzene
3000
0
3.0

tBuOCl

0.82
AliBu3
2.62
180
5
25
Benzene 400


CEx 1-3
848
Benzene
3200
30
1.0

tBuOCl

0.27
AliBu3
1
300
5
25
Benzene 400


CEx 1-4
1080
Hexane
2060
0
1.4
Cl5C6OH
1.82
AliBu3
0.43
240
3
15
Hexane 250


CEx 1-5
1434
Toluene
2000
5
3.2
2-iPrPhOH
6.15
AlEt3
2.51
90
3
45
Toluene 250


Ex 1-6
1000 + 0.5
Toluene
1000
5
1.16
2,6-Me2PhOH
1.44
AlEtCl2
15.08
150
3
45
Toluene 250



hexene


CEx 1-7
470
Non

−25
9.0*
Non

AlEt3
8.59
180
3
20
Hexane 250





*0.5 g of 1-hexene (C6═) was added, cC5═:C6═ wt/wt ratio of 2000:1.






Improved Catalyst Formation and Polymerization

The following examples were generated using synthetic pathways which eliminate the generation of harmful gas, improve activities, and provide different trans:cis ratio and molecular weight controls according to embodiments disclosed herein.


Polymerization of cyclopentene with (RO)2AlCl+WCl6+activator (Al—R containing compound)


Example 2-1-1 (RO=2-iPrPhO, Polymerization at 0° C.)

(2-iPrPhO)2AlCl Preparation—(2-iPrPhO)2AlCl was prepared from the reaction of R2AlCl, e.g., Me2AlCl or Et2AlCl (Aldrich product), with 2-iPrPhOH in hydrocarbon solvent (toluene and/or isohexane) by slow addition of 2 eq of neat or dilute 2-iPrPhOH to the aluminum alkyl solution at ambient temperature (i.e., 25° C.). The resultant solution was then used and/or the resultant oil obtained after solvent removal.


Catalyst Preparation—Neat (2-iPrPhO)2AlCl (504 mg, 1.518 mmol) was added to a solution of WCl6 (300 mg, 0.757 mmol) in toluene (10 mL). The resulting mixture was stirred for 2.5 hours at room temperature.


Polymerization—The solution of cC5=(100 g, 130 mL, purified by passing through alumina column) in toluene (300 mL) was added to a 2-necked round bottom Schlenk flask (2 L) containing a mechanical stirrer. Neat triethylaluminum (Et3Al, 173 mg, 1.517 mmol) was then added. Vigorous agitation was applied and the resulting solution was cooled down to 0° C. The solution of premade catalyst (A) was then injected into the reaction mixture. The reaction mixture became viscous after about 40 minutes of reaction time. After 3 hours at 0° C. (conversion:64%), the solution of BHT (338 mg, 1.513 mmol) in EtOH(50 mL)/toluene(100 mL) was added to quench the catalyst and the unreacted aluminum alkyls. The resulting mixture was subsequently slowly poured into EtOH (1 L) under intense mechanical mixing. The formed polymer was then washed with EtOH (3×500 mL) and dried in vacuo at 50° C. for 4 hours. Dried solid product was stored under nitrogen atmosphere. Alternatively, the solution of antioxidant (BHT) in ethanol was sprayed above the polymer surface to prevent cross-linking upon exposure to air. Isolated yield: 58.3 g, Cis/Trans ratio: 15/85%, Mw: 493 k; Mw/Mn: 2.00.


Example 2-1-2 (RO=2-iPrPhO, Polymerization at 0° C.)

(2-iPrPhO)2AlCl Preparation—(2-iPrPhO)2AlCl was prepared as described above.


Catalyst Preparation—the neat-oil (2-iPrPhO)2AlCl 1.007 g was added to the solution of WCl6 600 mg in 20 ml toluene and stirred for 1 hour at room temperature.


Polymerization—a solution of cC5=(270 mL) in toluene (700 mL) was prepared to which was added neat AlEt3, which was then cooled to 0° C.; and then added the catalyst mixture to the cC5=solution under vigorous stirring; the mixture became viscous after about 40 minutes reaction time. After 3 hours at 0° C., the solution of BHT in EtOH (50 mL)/toluene (150 mL) was added to the reaction mixture. The resulting mixture was added to EtOH (1 L) under intense mechanical mixing. The formed polymer was washed with EtOH (3×0.5 L) and dried in vacuo at 50° C. for 4 hours; isolated yield:160 g (77%); Cis/Trans ratio: 14/86; Mw: 218 k; Mw/Mn: 1.78


The two examples above show that (2-iPrPhO)2AlCl as the ligand precursor for the modification of the basic catalyst WCl6 displays markedly improved activities (conversion/hr) than comparative example AA2066 where 2-iPrPhOH is used as the ligand precursor. In addition, these examples confirm that different Mw and different trans:cis ratios may be produced.


Example 2-1-1 and 2-1-2 under the very close conditions that show significant different molecular weights are likely due to the scale difference where agitation for the larger scale was not as efficient as the smaller scale and the local heat was higher (especially when the conversion rate was higher). The examples further confirm substantial improvement of the catalyst may be obtained by selecting appropriate ligands according to electronic and/or steric modification of the catalyst active site. In embodiments, one of the halogens, e.g., a Cl atom on the catalyst precursor WCl6 (or MCl5, M=Mo, Ta, Nb) is replaced by an alkoxy group hearing different group(s) to effect a change in the ligand electronic and/or steric effects




embedded image


Such catalyst modifications result in improvement in catalyst activity, allow for control over the trans:cis ratio of the resulting polymer, and/or allow for control over the molecular weight of the polymer. However, it has been discovered that in embodiments, at least two halogen groups are retained on the transition metal compound to allow an activator (e.g., aluminum alkyl) to convert the two halo groups into the active carbene species. Accordingly, the maximum number of alkoxylated ligands on WCl6 and other hexavalent transition metals is limited to 4, and for MoCl5, TaCl5, and NbCl5 and other pentavalent transition metals the maximum number of alkoxylated ligands is limited to 3. The alkoxy groups (RO—) may comprises C1 to C20 hydrocarbon oxy group including aliphatic oxy or aromatic oxy group. In embodiments, the oxygen atom is directly connected to an aromatic ring.


Example 2-1-3 (RO=2-iPrPhO. Polymerization at 21-25° C.)

(2-iPrPhO)2AlCl preparation—(2-iPrPhO)2AlCl was prepared as described above.


Catalyst preparation—neat (2-iPrPhO)2AlCl (25 mg, 0.075 mmol) was added to the solution of WCl6 (15 mg, 0.038 mmol) in toluene (2 mL). The resulting mixture was stirred for 1.5 hours at room temperature then cooled down to −35° C.


Polymerization—neat Et3Al (9 mg, 0.13 mmol) was added to the solution of cyclopentene (5 g, 73 mmol) in toluene (15 mL). The mixture was cooled down to 0° C. before the catalyst solution was added under intense stirring. The reaction temperature was allowed to rise up to 25° C.; the mixture became viscous after about 10 minute reaction time. After stirring 3 hours at 25° C. (conversion: 91% by NMR), the solution of BHT (9 mg, 0.04 mmol) in EtOH(1 mL)/toluene(5 mL) was added. The resulting mixture was subsequently poured into EtOH (200 mL) under intense mechanical mixing. The precipitated polymer was washed with EtOH (2×200 mL) and dried in vacuo at 50° C. for 4 hours to give 3.81 g of a white polymer. The yield of this example is artificially low due to product precipitation and transfer issues. The following properties were determined: Mw: 193 k; Mw/Mn 1.99; Trans/cis 84/16.


This experiment shows that polymerization temperature has tremendous influence over the Mw, i.e., the higher the reaction temperature, the lower the molecular weight. However, the above example suggests that the trans:cis ratio is not significantly changed by the reaction temperature.


Example 2-2 (RO=4-MePhO, Polymerization at 0° C.)

(4-MePhO)2AlCl preparation—4-MePhOH and the dimethylaluminum chloride in 2:1 molar ratio, e.g., 3.55 g (33 mol) and 1.52 g (16 mmol), were dissolved in separate vessels in toluene, e.g., 30 g in each vessel. The p-cresol solution was then slowly added to the stirring solution of Me2AlCl. The solution stayed clear, but a vapor formed above the stirring reaction mixture. The reaction was allowed to stir overnight. The toluene was removed to give a viscous colorless residue. The residue was dissolved in pentane and the pentane was removed to give a fine white powder that contains 7 wt % toluene determined by NMR. (18-AD1410).


Catalyst preparation—the solid (4-MePhO)2AlCl (1.17 g) was added to a solution of WCl6 (0.75 g) in toluene (20 mL) and stirred for 1 hour at room temperature.


Polymerization—a solution of cC5=(336 mL) in toluene (900 mL) was prepared and neat AlEt3 (0.432 g) was added to the cC5=toluene solution. The solution was then cooled down to 0° C. and the catalyst solution was added under stirring; the mixture became viscous after about 10 minute reaction time. No stirring was possible after 40 minutes due to the high viscosity of the reaction mixture. After 3 hours at 0° C., the solution of BHT in EtOH(20 mL)/toluene(100 mL) was added to the viscous mixture. The resulting mixture was added to EtOH (1.5 L) under intense mechanical mixing. The formed polymer was washed with EtOH (3×500 mL) and dried in vacuo at 50° C. for 4 hours. Yield: 228 g (91%); cis:trans ratio: 17/83%; Mw: 315 k; Mw/Mn: 1.80.


Polymerization of cyclopentene with [(RO)3Al(THF)]2+WCl6+activator (Al—R containing compound)


Example 2-3-1 (RO=4-MePhO. Polymerization at 0° C.)

[(4-MePhO)3Al(THF)]2 preparation—the compound was prepared by reacting AlR3 (e.g., TEAL) toluene solution with 3 eq. 4-MePhOH in toluene solution, drying out solvent to obtained solid compound mixture, and following a 105° C. treatment in THF in a closed reactor to obtain the product. Typical procedure: A solution of 50 g 4-MePhOH (0.462 mol) in 100 m toluene was added dropwise to a solution of 11.13 g TMA (0.154 mol) in 300 mL toluene under intense stirring at ambient temperature and pressure. The addition was done in a controlled fashion to prevent an extensive gas formation and overheating of the reaction mixture. The mixture was stirred at 80° C. for 2 hours after which the solvent was boiled off to give a white product. This product was washed several times with hexane (3×100 mL) and dried in vacuo to yield 56 g. 1H NMR shows the presence of another product in the mixture. The obtained white solid was dissolved at 105° C. in THF (500 mL) in a closed high-pressure vessel and the resulting solution was allowed to cool down to room temperature. Precipitated white crystalline solid was washed several times with hexane (3×50 mL) and dried at 85° C. for 4 hours. 52 g of the targeted product were isolated. A small amount of the crystalline material was analyzed with X-ray single-crystal diffraction and the structure is shown in FIG. 2.


Catalyst Preparation—solid (4-MePhO)3Al(THF) (424 mg, 1.00 mmol) was added to the solution of WCl6 (300 mg, 0.757 mmol) in toluene (10 mL). The resulting mixture was stirred for 2.5 hours at room temperature.


Polymerization—the polymerization protocol is identical to that described above. cC5=130 mL (100 g) in 300 mL toluene. Reaction temperature: 0° C. Reaction time: 3 hours (viscous after 40 minutes). Conversion: 44%. Cis/Trans ratio: 25/75%, Mw: 601 k, Mw/Mn: 2.08. Example 2-3-2 (RO=4-MePhO, Polymerization at 21-25° C.)


[(4-MePhO)3Al(THF)]2 preparation—(4-MePhO)3Al(THF) prepared as for Example 2-3-1.


Catalyst Preparation—solid (4-MePhO)3Al(THF) (16 mg, 38 μmol) was added to the solution of WCl6 (15 mg, 38 μmol) in toluene (2 mL) cooled at ˜35° C. in the freezer in the drybox.


Polymerization—in a vessel cC5=6.5 mL (5 g) and 10 mL toluene were charged and placed in the freezer of drybox at −35° C. The cold cC5=solution was added ˜1 mg neat Et3Al. The cold catalyst solution was then added to the cC5=solution. The reaction temperature was increased from −35° C. to room temperature (˜21° C.). After 1 hour, the NMR showed the conversion was 56%. The mixture was allowed to stir overnight. Standard quenching procedure was applied. 1.83 g polymer was isolated. Cis/Trans ratio: 22/78%, Mw: 445 k, Mw/Mn: 2.22.


Examples 2-3-1 and 2-3-2 confirm that aluminum intermediates may be isolated by addition of a donor group, in this case THF. The (4-MePhO)3Al may be readily crystallized as a dimeric five coordinated Al species with one THF for each Al according to the following formula:




embedded image


wherein Ar is 4-Mephenyl.


As the Examples confirm, the THF adducts form highly active catalysts when used to construct the active catalyst with WCl6. Although many W compounds can polymerize THF to block or destroy the carbene formation, the molecular level THF present may only alter the metathesis polymerization behavior and yield different polymer structures (different Mw, trans:cis ratio, etc.) with the same ligand structure except with or without the coordinated THF. These examples suggest that other donors may include Et2O, MeOtBu, NMe3, and the like. Polymerization of cyclopentene with (RO)2AlR (as 2-in-1 ligand precursor and activator)+WCl6


Example 2-4-1 (RO=4-MePhO, Polymerization at 21-25° C.)

(4-MePhO)2AliBu preparation—a solution of 0.216 g 4-MePhOH in 2 g toluene was added slowly to a solution of 0.20 g TIBAL in 2 g toluene. Shaken it for 15 minutes at room temperature.


Catalyst preparation—the product was added to WCl6 solution (0.20 g in 2 g toluene) and shaken for 15 minutes.


Polymerization—after 24 hours the mixture was added to 50 g cyclopentene, which was purified by passing through a basic alumina column, and stirred for 24 hours. The conversion rate was monitor by NMR, which showed only 8%. The reaction did not proceed well, possibly due to being kept overnight at room temp which might have caused degradation of the active carbene species. The polymer was isolated using standard quenching procedure. Cis:trans=42:58; Mw=670 k; and Mw/Mn (or PDI)=2.3.


Example 2-4-2 (RO=4-MePhO, Polymerization at 21-25° C.)

Repeated Example 2-4-2, but added a drop of TIBAL to reactivate the proposed decomposed catalyst. The activity shows a marked improvement. The polymer was isolated using standard quenching procedure. Conversion: 19% in 1 hour; Cis:trans=40:60; Mw=671 k; and Mw/Mn (or PDI)=1.9.


Example 2-4-1 and Example 2-4-2 show that at RT polymerization condition high Mw polymer can be obtained and the cis:trans ratio can be controlled.


Polymerization of cyclopentene with chelating-A(RO)2AlCl+WCl6+Al-R containing activator


Example 2-5 (a(RO)2=BBHT without Active Protons, Polymerization at 21° C. to 25° C.



embedded image


(BBHT)AlCl preparation—in a drybox, a 20 mL vial was charged 0.340 g BBHT (Aldrich, >98.5%, 1.0 mmol) and 2 g toluene. The solution was added slowly to another 20 mL 15 vial containing 0.095 g Me2AlCl (1.0 mmol) and 2 g toluene and shaken well.


Catalyst preparation—the BBHT solution was added to a WCl6 solution (0.198 g (0.5 mmol) in 2 g toluene) and shaken for 15 minutes.


Polymerization—the catalyst solution was added to 50 g cyclopentene, which was purified by passing through a basic alumina column, and stirred for 3 hours. The conversion rate was monitor by NMR, which showed only 3%. The reaction did not proceed well, possibly due to steric hindrance of the active site by the relatively large size of the two BBHT ligands. The polymer was isolated using standard quenching procedure. Cis:trans=18:82; Mw=623 k; and Mw/Mn (or PDI)=2.21.


Polymerization of cyclopentene with A(RO)2Al(OR)+MoCl5+Al-R containing activator


Example 2-6 (Al(RO)2 is BBHT and OR is 2-iPrPhO, Polymerization at −35° C.)

(2-iPrPhO)Al(BBHT) preparation—in the drybox, a 20 mL vial was charged 0.340 g BBHT (Aldrich, >98.5%, 1.0 mmol) and 0.136 g 2-iPrPhOH (1.0 mmol) in 2 g toluene. The solution was added slowly to another 20 mL vial containing 0.114 g Et3Al (1.0 mmol) and 2 g toluene and shaken well.


Catalyst preparation—the above solution was added to MoCl5 solution (0.273 g (1.0 mmol) in 2 g toluene) and shaken for 15 minutes.


Polymerization—the catalyst solution was added to 50 g cyclopentene, which was purified by passing through a basic alumina column and cooled to −35° C., and stirred for 3 hours. The conversion rate was monitor by NMR, which showed about 1%. The reaction did not proceed well, which is consistent with the possible steric hindrance observed in Example 2-5. These results further suggest that the Mo species is much less active than W. The polymer was isolated using standard quenching procedure. No characterization was done due to an insufficient amount of the polymer product.


As examples 2-5 and 2-6 show, in embodiments a chelating ligand may be employed to force the ligand framework to form a “cis-structure according to the following reaction scheme:




embedded image


This is compared to the formation of a non-chelating ligand have the more abundant “trans-structure”.




embedded image


As these examples show, such embodiments allow for control over catalyst activity, the trans:cis ratio of the resulting poly-cyclo-olefins, and/or the resulting polymer molecular weight.


In embodiments, the chelating ligands may be directly reacted with the catalyst precursor, e.g., WCl6, to form the same cis-structure end product without first reacting with the metal alkyl (or hydride) compound. However, such embodiments will result in the formation of harmful HCl gas.


Polymerization of cyclopentene with Al(OR)3+WCl6+Al-R containing activator


Example 2-7-1 (RO=2-iPrPhO, Polymerization at 0° C.)

Al(2-iPrPhO)3 preparation—the solution of 2-iPrPhOH (4.0 g, 29.4 mmol) in toluene (10 mL) was added dropwise to the solution of Me3Al (0.539 g, 7.5 mmol) in toluene (5 mL) at room temperature. The formation of a white precipitate was observed during the reaction. The suspension was stirred overnight. Formation of a precipitate was not observed. The mixture was stirred for additional 1 hour at 80° C. Volatiles were then removed in vacuo to give a white crystalline solid which was washed with hexane and dried in vacuo. Yield 2.78 g.


Catalyst preparation—solid Al(2-iPrPhO)3 0.436 g was added to a solution of WCl6 (0.300 g) in toluene (10 mL); stirred for 2.5 hours at room temperature.


Polymerization—To the solution of cC5=(130 mL) in toluene (300 mL); was added neat AlEt3 0.173 g and cooled to 0° C.; this mixture was added to the cC5=solution under stirring; the mixture became viscous after about 40 minute reaction time. After 3 hours at 0° C., the reaction mixture was allowed to warm up to room temperature. After 14 hours at room temperature (conversion: 82% by NMR), the solution of BBHT in EtOH(10 mL)/toluene(50 mL) was added. The resulting mixture was added to EtOH (1 L) under intense mechanical mixing. The formed polymer was washed with EtOH (2×500 mL) and dried in vacuo at 50° C. for 4 hours. Isolated yield: 87 g; Cis/Trans ratio: 12/88%; Mw: 389 k; Mw/Mn: 2.07.


Example 2-7-2 (RO=2-iPrPhO, Polymerization at −35° C. to RT)

This examples represents a scaled down repeat experiment of Example 2-6-1 at a reaction temperature of −35° C. No solvent was used for polymerization. 5 g cC5=was found to have 88% conversion after less than 1 hour polymerization at −35° C. (freezer cooling then placing outside freezer, i.e., room temperature). It was likely that the vigorous polymerization caused too fast an increase in the temperature to room temperature, the resultant polymer had a lower Mw of 238 k; Mw/Mn=1.93; cis:trans=26:74.


Polymerization of cyclopentene with (RO)Na+WCl6+Al-R containing activator


Example 2-8 (RO=2,6-iPr2PhO, Polymerization at RT)

(2,6-iPr2PhO)Na preparation—NaH was dissolved into 10 g toluene and 2,6-diisopropylphenol was added into 10 g toluene. NaH solution was added to 2,6-diisopropylphenol solution slowly and stirred at room temperature for 15 minutes. The resultant reaction product was filtered to obtain the solid sodium alkoxide. The solid was washed with hexane and dried under vacuum. Yield: 1.42 g.


Catalyst preparation—1.0 g of the solid sodium alkoxide was added slowly to the solution of WCl6 0.413 g in 10 g toluene and heated to 80° C. for 60 minutes.


Polymerization—a round bottom flask was charged with 50 g of cyclopentene and 0.198 g of TIBAL (WCl6: TIBAL=1:1) as the activator. The WCl6 reaction mixture was added to the flask slowly and the mixture stirred at room temperature for 1 hour. Standard workup procedures gave a yield of 2 g (4% in 60 min), trans:cis ratio is 73:27.


As these examples confirm, the active catalyst may be produced without the formation of harmful byproducts, which include HCl and other materials detrimental to the process and potentially detrimental to the environment. In the examples, an alcohol used to form a ligand of the transition metal compound is first converted into a metal alkoxide (R—OH to a R—O-M species wherein M is a group 1, 2, or 13 metal, e.g., Na, Mg, or Al) In such embodiments the formation of harmful byproducts is eliminated, such as the elimination of HCl or Cl2 in the following equation:




embedded image


In addition, these examples suggest a Grignard intermediate may be used, e.g., RMgX, wherein X=halide and R═C1-C20 alkyl. For example, Grignard agent RMgCl, R═C1-C20 alkyl may be used to convert the alcohol into an intermediate, which is then reacted with the transition metal compound according to the following reaction scheme:




embedded image


As the examples further confirm, an alkyl aluminum compound may be used (e.g., AlR2X or AlRX2, wherein X is halide and R is C1-C20 alkyl) to convert the alcohol into an intermediate, which is then reacted with the transition metal compound according to the following reaction scheme:




embedded image


Silica Supported Catalyst Formation and Polymerization

Example 3-1-1 demonstrates the route to form the silica supported W═CHR active carbene species from high temperature prepared silica as shown below.




embedded image


A suspension of silica PQ ES70 (0.5 g, calcinated at 600° C., about 0.6 mmol OH/g) in DCM (10 mL) was reacted with WCl6 (0.2 g) at room temperature for 2 hours. Supported silica was collected by filtration and washed in DCM (5×10 mL), then dried in vacuo to obtain the solid powder of supported catalyst. 0.1 g supported catalyst was mixed with 5 g cC5=at room temperature in a 20 mL vial. A drop of TEAL was added to the mixture and shaken well on a shaker. The mixture became viscous after 1 hour. The mixture was filtered through a glass frit and the solid was washed with DCM. The filtrate was dried in vacuo to obtain 0.2 g polymer (conversion 4%). The polymerization was repeated by mixing the solid with 5 g cC5= in another 20 mL vial, which was shaken for 2 hours. The mixture was filter through a similar glass frit and the solid was washed with DCM. The filtrate was dried in vacuo to obtain 0.2 g polymer (conversion 4%).


Example 3-1-2 demonstrates the alternative route to form the silica supported W═CHR active carbene species from high temperature prepared silica shown below. Quantitative Test based on Route II A-D-E-F-G.


A-D-E Formation.



embedded image


A suspension of silica (2 g, calcinated at 600° C., ˜0.6 mmol OH/g) in toluene (20 mL) reacted with TEAL (AlRX2=AlEt3) at room temperature for 1 hour. Solid 4-MePhOH (Ar=4-MePh-) was then added and the mixture was stirred for 40 minutes at 70° C. The treated silica was filtered and washed with hexane. Yield: 2.23 g. (AC6654)


Catalyst preparation—the treated silica 64 mg was added to a solution of WCl6 (0.154 g) in toluene (2 mL); stirred for 1.5 hours at room temperature then cool down to −35° C.


Polymerization—a solution of cC5=(5 g) in toluene (25 mL) was cooled to the temperature of −35° C.; neat TEAL (17 mg) was added to the mixture. The cooled treated silica suspension was added to the mixture under vigorous stirring. The temperature was allowed to rise up to room temperature; the reaction mixture was filtered after 40 minutes reaction time and the cyclopentene was removed under a stream of N2 to isolate 0.37 g polymer (contains small amount of toluene): cis:trans ratio 17:83; Mw 309 k; PDI 2.39.


The remaining catalyst removed by filtration was washed 4 times with toluene (5 mL each) and added to a new portion of cyclopentene (5 mL). After stirring for 3 hours at room temperature the conversion was measured at 4%, insufficient product prevented further characterization.


In these two examples a “high temperature” calcined silica is employed wherein the silica or other support is calcined at temperatures greater than about 600° C. These examples further demonstrate synthetic pathways which eliminate the formation of HCl by first converting the Si—OH groups into the metalated support Si—O-M, wherein M is a Group 1, 2, or 13 element. In these examples, the aluminum analog is formed as shown above. The metalated support is then contacted with the catalyst precursor, e.g., WCl6, to form the supported catalyst.


The two examples above further demonstrate that polypentenamer product can be separated from the supported catalyst and the quenching and product precipitation to isolating catalyst steps can be eliminated. The samples further confirm that the catalyst can be used in a continuous process wherein the catalyst is recycled and optionally reactivated along with any unreacted monomer. The examples further confirm that the monomer may be used as the solvent.


Self-Supported Catalyst Formation and Polymerization
Example 4-1 (Al—X-Bridging Bisphenol a Polymer as Self-Supported W Catalyst)

The self-supported catalyst example was prepared according to the following reaction scheme:




embedded image


0.72 g (9.9 mmol) TMA (═R2AlX, R═X=Me) and 5 g toluene were charged into a 40 mL vial; 2.20 g (9.6 mmol). 10 g of bisphenol A in toluene (not totally dissolved) was charged in to a 20 mL vial. The bisphenol A slurry was added slowly to the TMA solution. Because the reaction was slow, the bisphenol A could be added as solid. After all the bisphenol A was added, the resulting mixture was heated at 90° C., the slurry became viscous and then solidified as a foam and the volume noticeably increased. Approximately 1/10 of the wet solid was mixed with ˜0.05 g WCl6 and 5 g cC5=without additional Al—R activator and the mixture was shaken at room temperature. An apparent viscosity increase was observed after a 15 minute reaction time. After 24 hours, the entire reaction mixture had solidified.


The example confirms that a self-supported catalyst according to embodiments disclosed herein can be formed. In this example, non-chelating organic multi-alcoholic compounds are reacted with catalyst precursors to form a solid self-supported catalyst. The non-chelating dihydroxy compound (bis-phenol A) used to form the polymeric support has a low in solubility in non-polar organic solvents, which is required for ROMP polymerization. In this example, the 4,4′ bis-phenol compound (bis-phenol A) was employed since the placement of the two hydroxyls render the compound unsuitable for forming chelates of the transition metal:




embedded image


The example suggests non-chelating organic multi-alcoholic compounds which may be suitable for use include, but are not limited to, other bi-alcoholic, and/or tri-alcoholic or poly-alcoholic compounds, and/or mixtures of these compounds. Examples include:




embedded image


In embodiments, mono-alcoholic ligand, e.g., 4-MePhOH, may be used with the bi- and/or tri-alcoholic compounds, as support termination agents. These mono-hydroxyl compounds are employed to control the molecular weight of the self-support polymeric compound, i.e., used as a polymer end-point to regulate the support chain length.


This example serves as an evidence that polymeric non-chelating multi-alcoholic compound can form with aluminum alkyl served as bridging groups. The W active species can form on the support that serves also as the ligand precursor (Bisphenol A) and activator (aluminum alkyl bridge).


All polymerization results are summarized in Table 2.









TABLE 2







Cyclopentene Polymerization Results












Monomer/Polymer
Reaction Conditions
Polymer Properties


















Charge/
Yld
T
t

Mw (k)
PDI
Trans:Cis
Catalyst


















Run ID
Yield (g)
(%)
(° C.)
min.
Solvent
GPC
GPC

13CNMR

MCln
RO—X
AlX3





















CEx 1-1
1150/580
50
30
240
Benzene
412
2.16
83/17
WCl6
Me3COCl
AliBu3


CEx 1-2
 960/770
80
0
180
Benzene
594
2.24
81/19
WCl6
Me3COCl
AliBu3


CEx 1-3
 848/170
20
30
300
Benzene
220
4.29
80/20
WCl6
Me3COCl
AliBu3


CEx 1-4
1000/510
51
0
240
Hexane
331
2.47
80/20
WCl6
Cl5C6OH
AlEtCl2


CEx 1-5
1080/800
74
5
90
Toluene
661
2.38
74/26
WCl6
2-iPrPhOH
AlEt3


Ex 1-6
   1000/500 ****
50
5
90
Toluene
337
2.11
89/11
WCl6
2,6-Me2PhOH
AlEt3


CEx 1-7
350/28
 8
−30
180
Non
339
9.6 
 <1/>99
MoCl5
Non
AlEt3


Ex 2-1-1
  91/58.3
64
0
180
Toluene
493
2.00
85/15
WCl6
(2-iPrPhO)2AlCl
AlEt3


Ex 2-1-2
 208/160
77
0
180
Toluene
218
1.78
86/14
WCl6
(2-iPrPhO)2AlCl
AlEt3


Ex 2-1-3
 4.18/3.81
91
21
180
Toluene
193
1.99
84/16
WCl6
(2-iPrPhO)2AlCl
AlEt3


Ex 2-2
 252/227
90
0
180
Toluene
315
1.75
84/16
WCl6
(4-MePhO)2AlCl
AlEt3


Ex 2-3-1
 97.5/42.9
44
0
180
Toluene
601
2.08
75/25
WCl6
(4-MePhO)3Al•THF
AlEt3


Ex 2-3-2
  5/1.8
 56*
−35/21
60
Toluene
445
2.22
78/22
WCl6
(4-MePhO)3Al•THF
AlEt3


Ex 2-4-1

50/4.0

 8
21
24 h
Non
670
2.3 
58/42
WCl6
(4-MePhO)2AliBu
Non


Ex 2-4-2

50/9.5

19
21
60
Non
671
1.9 
60/40
WCl6
(4-MePhO)2AliBu
AliBu3


Ex 2-5
50/6
 3
21
180
Non
623
2.21
82/18
WCl6
(BBHT)AlCl
AliBu3


Ex 2-6
 5/<1
 <1*
−35/21
24 hr
Non



MoCl5
2-iPrPhOAlBBHT
AlEt3


Ex 2-7-1
106/87
82
0
180
Toluene
389
2.07
88/12
WCl6
(2-iPrPhO)3Al
AlEt3


Ex 2-7-2
  5/4.4
 88*
−35/21
<1
Non
238
1.93
74:26
WCl6
(2-iPrPhO)3Al
AlEt3


Ex 2-8
50/2
 4
21
60
Non


73/27
WCl6
2,6-iPr2PhONa
AliBu3


Ex 3-1-1
  5/0.2
 4
21
60
Non



WCl6
Silica-OH
AlEt3


Ex 3-1-2
   5/0.37
 7
−35/21
40
Non
309
2.39
83:17
WCl6
Silica-OH
AlEt3


Ex 4-1
 5/>4
 >80**
21
24 h
Non



WCl6
Bisphenol A
Al—Me ***





*Conversion determined by NMR for the reaction mixture;


**estimated based on viscosity;


*** Moiety on AlMe3/Bisphenol A derived polymer;


**** 1-hexene (C6═) added: cC5═:C6═ is 2000:1






Although only a few example embodiments have been described in detail above, those skilled in the art will readily appreciate that many modifications are possible in the example embodiments without materially departing from this invention. Accordingly, all such modifications are intended to be included within the scope of this disclosure as defined in the following claims. In the claims, means-plus-function clauses are intended to cover the structures described herein as performing the recited function and not only structural equivalents, but also equivalent structures. Thus, although a nail and a screw may not be structural equivalents in that a nail employs a cylindrical surface to secure wooden parts together, whereas a screw employs a helical surface, in the environment of fastening wooden parts, a nail and a screw may be equivalent structures. It is the express intention of the applicant not to invoke 35 U.S.C. § 112, paragraph 6 for any limitations of any of the claims herein, except for those in which the claim expressly uses the words ‘means for’ together with an associated function.

Claims
  • 1. A process to form a cyclic olefin polymerization catalyst comprising: contacting a metal alkoxide (IIIa) with a transition metal halide (IV) to form a transition metal precatalyst (VIIIa) according to the general formula:
  • 2. The process of claim 1, wherein the metal alkoxide (IIIa) is formed by contacting a compound comprising a hydroxyl functional group (I) with a Group 1 or Group 2 metal hydride Mu*(H)u according to the general formula:
  • 3. The process of claim 1, wherein the metal alkoxide (IIIa) is formed by contacting a compound comprising a hydroxyl functional group (I) with the metal alkyl activator (A) to form the metal alkoxide (IIIa) according to the general formula:
  • 4. The process of claim 2, further comprising contacting a mixture of metal alkoxides with one or more ligand donors (D) under conditions sufficient to crystallize and isolate the metal alkoxide (IIIa) as one or more dimeric coordinated metal alkoxide-donor composition according to the general structure (XXV-GD2):
  • 5. A process to form a cyclic olefin polymerization catalyst comprising: contacting an alkyl-metal alkoxide (IIIb) with a transition metal halide (IV) in a reaction mixture to form the activated catalyst (V) comprising a transition metal carbene moiety Mv=C(R*)2 according to the general formula:
  • 6. The process of claim 5, wherein the reaction mixture further comprises a metal alkyl activator (A) according to the formula MuRaX(u-a) wherein Mu is a Group 1, 2, or 13 metal of valance u, preferably Li, Na, Ca, Mg, Al, or Ga;a is 1, 2, or 3;a≤u; andwhen present, X is halogen.
  • 7. The process of claim 1, wherein Mv is W, Mo, Nb, or Ta; wherein X is Cl, F or a mixture thereof;or a combination thereof.
  • 8. The process of claim 1, wherein two or more R′O— ligands are connected to form a single bidentate chelating moiety.
  • 9. A process to form a cyclic olefin polymerization catalyst comprising: i) contacting a compound comprising a hydroxyl functional group (I) with an alkyl aluminum compound (II) to form an aluminum precatalyst (III) and the corresponding residual (Q1+Q2) according to the general formula:
  • 10. The process of claim 9, wherein a=3 such that the alkyl aluminum compound (II) is a trialkyl-aluminum (IX) and the residual is an alkane HR according to the general formula:
  • 11. The process of claim 10, wherein the aluminum precatalyst (III) is a dimer represented by structure (III-D) which is reacted with the transition metal halide (IV) to form the activated carbene containing cyclic olefin polymerization catalyst (V) according to the general formula:
  • 12. The process of claim 9, wherein a=2 and Y is halogen such that the alkyl aluminum compound (II) is a dialkyl aluminum halide (VI), and the aluminum precatalyst is a di-halo tetrakis alkoxide aluminum dimer (VII) according to the general formula:
  • 13. The process of claim 1, wherein a molar ratio of Mv to Mu-R in metal alkyl activator MuRaX(u-a) is from 1 to 2 to 1 to 15.
  • 14. The process of claim 1, wherein the alkoxy ligand R′O— comprises a C7 to C20 aromatic moiety and wherein the O atom directly bonds to the aromatic ring.
  • 15. The process of claim 9, wherein the compound comprising a hydroxyl functional group (I) is a bidentate dihydroxy chelating ligand (X′); the alkyl aluminum compound (II) is a dialkyl aluminum halide (VI); and the aluminum precatalyst (III) is an aluminum alkoxide mono-halide (XI) according to the general formula:
  • 16. The process of claim 15, further comprising contacting two equivalents of the aluminum alkoxide mono-halide (XI) with the transition metal halide (IV) to form a transition metal halo bis-alkoxide catalyst precursor (XII) according to the general formula:
  • 17. The process of claim 16, further comprising contacting one equivalent of the aluminum alkoxide mono-halide (XI) with a transition metal halide (IV) to form a transition metal halo alkoxide catalyst precursor (XIV) according to the general formula:
  • 18. The process of claim 9, wherein the compound comprising a hydroxyl functional group (I) is a bidentate dihydroxy chelating ligand (X′); the alkyl aluminum compound (II) is a trialkyl aluminum (IX); and the aluminum precatalyst (III) is an alkyl aluminum alkoxide (XX) according to the general formula:
  • 19. The process of claim 18, further comprising contacting two equivalents of the aluminum-alkyl alkoxide (XX) with a transition metal halide (V) to form the activated carbene containing cyclic olefin polymerization catalyst (XXI) according to the general formula:
  • 20. The process of claim 18, further comprising contacting one equivalent of the aluminum-alkyl alkoxide (XX) with a transition metal halide (V) to form the activated carbene containing cyclic olefin polymerization catalyst (XXIa) according to the general formula:
  • 21. The process of claim 9, wherein the compound comprising a hydroxyl functional group (I) is a mixture comprising a bidentate dihydroxy chelating ligand (X′) and a monodentate hydroxy ligand (XVI); the alkyl aluminum compound (II) is a trialkyl aluminum (IX); and the aluminum precatalyst (III) is an aluminum tri-alkoxide (XVII), the process further comprising: i) forming the aluminum tri-alkoxide (XVII) according to the general formula:
  • 22. The process of claim 9, wherein the compound comprising a hydroxyl functional group (I) is an aromatic compound comprising a phenoxy hydroxyl group Ar—OH (XXIV); the alkyl aluminum compound (II) is an alkyl aluminum halide, and the aluminum precatalyst (III) is a mixture of aluminum alkoxides (XXVa), (XXVb), and (XXVc), the process further comprising forming the mixture of aluminum alkoxides (XXVa), (XXVb), and (XXVc) according to the general formula:
  • 23. A cyclic olefin polymerization process comprising: contacting a cyclic olefin polymerization catalyst according to claim 1 with a C4-C20 cyclic olefin monomer comprising at least one cyclic olefin moiety in a polymerization reactor under conditions sufficient to form a reaction product mixture comprising a polymer, unreacted monomer, catalyst, and optionally a solvent; andrecovering the polymer.
  • 24. The process of claim 23, further comprising: i) separating the monomer from the reaction product mixture and recycling the monomer to the polymerization reactor;ii) contacting the recovered catalyst with an activator prior to recycling to the polymerization reactor;or a combination thereof.
  • 25. The process according to claim 23, wherein the process is continuous.
  • 26. The process according to claim 23, wherein the process is a batch process.
  • 27. The process according to claim 23, wherein the polymerization comprises ring opening metathesis polymerization and the polymer comprises polyalkenamer, preferably polypentenamer, a cyclic olefin copolymer, and/or a cyclic olefin polymer.
  • 28. The process of claim 27, further comprising recovering the catalyst and optionally the solvent from the reaction product mixture; and recycling at least a portion of the recovered catalyst, unreacted monomer, and/or optionally the solvent to the polymerization reactor.
  • 29. The process according to claim 23, further comprising incorporating one or more C4-20 cyclic diolefins comprising at least one cyclic structure having the general formula:
  • 30. The process according to claim 23, further comprising: (I) controlling Mw and/or a trans:cis ratio of the polymer by controlling a reactor temperature from −35° C. to 100° C.; controlling the amount of monomer recycled to the reactor; using the monomer as a reaction solvent; or a combination thereof;(II) forming active catalyst species at a temperature less than or equal to about 5° C., followed by increasing the reaction temperature to a temperature less than 100° C.;(III) incorporating an amount of an olefin, preferably an alpha olefin, preferably an alpha olefin comprising at least one hetero atom containing functional group into the cyclic olefin monomer to reduce the molecular weight of the polymer in the product mixture;(IV) employing two or more cyclic olefin polymerization catalysts in the same or different reactors to produce polymer exhibiting: i) a multi-modal Mw profile;ii) a trans:cis molar ratio greater than 1;iii) a trans:cis molar ratio less than 1; and/or(V) employing multiple reactors connected in a sequence to produce heterophasic copolymers.
  • 31. The process according to claim 30, wherein the olefin comonomer has the general formula: CH2═CH—(CH2)n—CH3;CH2═CH—[(CH2)n(FG)s]—CH3; and/orCH2═CH—(CH2)n-FG;wherein each FG, when present, is independently halogen, NR{circumflex over ( )}2, OR{circumflex over ( )}, SeR{circumflex over ( )}, TeR{circumflex over ( )}, PR{circumflex over ( )}2, AsR{circumflex over ( )}2, SbR{circumflex over ( )}2, SR{circumflex over ( )}, BR{circumflex over ( )}2, SiR{circumflex over ( )}3, GeR{circumflex over ( )}3, SnR{circumflex over ( )}3, PbR{circumflex over ( )}3, O, S, Se, Te, NR{circumflex over ( )}, PR{circumflex over ( )}, AsR{circumflex over ( )}, SbR{circumflex over ( )}, BR{circumflex over ( )}, SiR{circumflex over ( )}2, GeR{circumflex over ( )}2, SnR{circumflex over ( )}2, PbR{circumflex over ( )}2, or a combination thereof, and each R{circumflex over ( )} is independently a C1-C10 hydrocarbyl radical;n is greater than or equal to 1; ands, when present, is greater than or equal to 1.
CROSS REFERENCE TO RELATED APPLICATION

This application claims priority to Provisional Application No. 62/733,993, filed Sep. 20, 2018, the disclosure of which is incorporated herein by reference. This application is related to concurrently filed U.S. Ser. No. 62/733,989 entitled Metathesis Catalyst System for Polymerizing Cycloolefins.

Provisional Applications (1)
Number Date Country
62733993 Sep 2018 US