Methane conversion using a magnesia/silica support

Abstract

An improved method for converting methane to higher hydrocarbon products by contacting a gas comprising methane with a contact agent at a selected temperature, the agent comprising a reducibile metal oxide, a support of at least two oxides, and an alkali metal.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to the synthesis of hydrocarbons from a methane source. A particular application of this invention is a method for converting natural gas to more readily transportable material using a methane conversion catalyst formed using a reducible metal oxide, a support of oxides of at least two metals, and an alkali metal.

2. Description of the Pertinent Art

A major source of methane is natural gas. Other sources of methane have been considered for fuel supply (e.g., the methane present in coal deposits or formed during mining operations). Relatively small amounts of methane are also produced in various petroleum processes.

The composition of natural gas at the wellhead varies, but the major hydrocarbon present is methane. For example, the methane content of natural gas may vary within the range of about 40 to about 95 volume percent. Other constituents of natural gas include ethane, propane, butane, pentane (and heavier hydrocarbons), hydrogen sulfide, carbon dioxide, helium, and nitrogen.

Natural gas is classified as dry or wet, depending upon the amount of condensable hydrocarbons contained in it. Condensable hydrocarbons generally comprise C.sub.3 +hydrocarbons, although some ethane may be included. Gas conditioning is required to alter the composition of wellhead gas; processing facilities usually being located in or near the production fields. Conventional processing of wellhead natural gas yields processed natural gas containing at least a major amount of methane.

Large-scale use of natural gas often requires a sophisticated and extensive pipeline system. Liquefaction has also been employed as a transportation means, but processes for liquefying, transporting and revaporizing natural gas are complex, energy intensive and require extensive safety precautions. Transport of natural gas has been a continuing problem in the exploitation of natural gas resources. It would be extremely valuable to be able to convert methane (e.g., natural gas) to more readily transportable products. Moreover, direct conversion to olefins such as ethylene or propylene would be extremely valuable to the chemical industry.

Recently, it has been discovered that methane may be converted to higher hydrocarbons by a process which comprises contacting methane with an oxidative synthesizing agent at synthesizing conditions (e.g., at a temperature selected within the range of about 500.degree. to about 1000.degree. C.). An oxidative synthesizing agent is a composition having as a principal component at least one oxide of at least one metal, which composition produces higher C.sub.2 + hydrocarbon products, water and a composition comprising a reduced metal oxide when contacted with methane at synthesizing conditions. Reducible oxides of several metals have been identified which are capable of converting methane to higher hydrocarbons. In particular, oxides of manganese, tin, indium, germanium, lead, antimony and bismuth are most useful.

The reaction products of such processes are mainly ethylene, ethane, other light hydrocarbons, carbon oxides, coke and water. It would be beneficial to these oxidative synthesis processes to reduce production of carbon oxides and coke.

Accordingly, an object of this invention is to provide an improved process for converting methane to higher hydrocarbons. A further object of this invention is an improved oxidative synthesizing agent--one capable of converting methane with reduced byproduct selectivities.

Other aspect, objects and the several advantages of this invention will become apparent to those skilled in the art upon reading this Specification and the appended claims.

SUMMARY OF THE INVENTION

An improved hydrocarbon conversion process has been discovered which comprises contacting hydrocarbons, preferably a gas comprising methane, with a contact agent at conditions to convert the hydrocarbons, preferably at a temperature selected within the range of about 500.degree. to about 1000.degree. C., which agent comprises:

(a) at least one reducible oxide of at least one metal, which oxide is reduced and produces higher hydrocarbon products and water when contacted with methane at the selected temperature;

(b) a support comprising at least two metal oxides; and

(c) an alkali metal.

DETAILED DESCRIPTION OF THE INVENTION

The contact agent of this invention is a composition comprising at least one reducible oxide of at least one metal and a support. The reducible oxide produces higher hydrocarbon products, water and a reduced metal oxide when contacted with methane at a temperature selected within the range of about 500.degree. to about 1000.degree. C. The term "reducible" is used to identify those oxides of metals which are reduced by contacting methane at synthesizing conditions. The term "oxide(s) of metal(s)" includes: (1) one or more metal oxides (i.e., compounds described by the general formula M.sub.x O.sub.y wherein M is a metal, O is oxygen, and the subscripts x and y designate the relative atomic proportions of metal and oxide in the composition); and/or (2) one or more oxygen-containing metal compounds; provided that such oxides and compounds have the capability of performing to produce higher hydrocarbon products as set forth herein.

The preferred agents comprise reducible oxides of metals selected from the group consisting of manganese, tin, indium, germanium, antimony, lead, bismuth, and mixtures thereof. The particularly preferred agents comprise reducible oxides of manganese and mixtures of reducible oxides of manganese with other oxidative synthesizing agents.

The support comprises at least two oxides. Preferably, at least one of the oxides is an alkaline earth oxide and the second oxide is selected from a group comprising silica, alumina, and mixtures thereof. More preferably, the first oxide comprises magnesia and the second oxide comprises silica.

The preferred mole ratio of the first oxide to the second oxide is 1:1 or greater, and more preferably is in the range of about 30:1 to about 5:1. Particularly good results are obtained when this ratio is about 5:1.

The preferred contact agent of this invention contains, in addition to the foregoing elements, at least one alkali metal. Sodium and/or compounds thereof are a particularly preferred alkali metal component. Except as noted elsewhere herein, the atomic ratio in which these materials are combined to form the contact agent is not narrowly critical. However, the preferred atomic ratio of the reducible oxide component (expressed as the metal, e.g., Mn) to the alkali metal component (expressed as the metal, e.g., Na) is within the range of about 0.1:1 to about 100:1, more preferably within the range of about 0.3:1 to about 10:1. The preferred mole ratio of silica or alumina to alkali metal is about 50:1 to about 1:1, and more preferably about 0.5:1 to about 10:1. Most preferably, the ratio is about 1:1 to about 3:1.

The alkali metal component may be added to the support before or during precipitation, coprecipitation, or impregnation of the reducible oxide and the support.

The support or agent may be contacted with a suitable alkali metal component which should not interfere with the support function, the reducible oxide function, or the process for combining the support with the reducible oxide. Preferably, the alkali metal component is a basic composition of the alkali metal. More preferably, the alkali metal component is selected from a group consisting of sodium hydroxide, sodium acetate, lithium hydroxide, lithium acetate, and mixtures thereof.

The contact agent can be prepared by any suitable method. Conventional methods such as precipitation, coprecipitation, impregnation, granulation, and spray drying can be used.

One suitable method of preparation of the contact agent includes the following steps.

An aqueous slurry of magnesia and silica gel is prepared and mixed with a solution of reducible oxides.

Suitable metal compounds useful for impregnation include the acetates, acetylacetonates, oxides, carbides, carbonates, hydroxides, formates, oxalates, nitrates, phosphates, sulfates, sulfides, tartrates, fluorides, chlorides, bromides or iodides.

After impregnation, the resulting composite is dried in an oven to remove solvent and the dried solid is prepared for use by calcining at elevated temperatures in an oxygen-containing gas (e.g., air) prior to use in the process of this invention. Particular calcination temperatures will vary, depending upon the particular metal compound or compounds employed. Preferably, the air temperature is selected within the range of about 300.degree. to about 1200.degree. C.

In addition to methane, the preferred feedstock employed in the method of this invention may contain other hydrocarbon or non-hydrocarbon components, although the methane content should typically be within the range of about 40 to about 100 volume percent, preferably about 80 to about 100 volume percent, more preferably about 90 to about 100 volume percent.

Operating temperatures for contacting the methane with the contact agent are preferably selected within the range of about 500.degree. to about 1000.degree. C.; the particular temperature selected depending upon the particular reducible metal oxide(s) employed in the contact agent. For example, reducible oxides of certain metals may require operating temperatures below the upper part of the recited range to minimize sublimation or volatilization of the metals (or compounds thereof) during methane contact. Examples include reducible oxides of indium, germanium and bismuth (operating temperatures will preferably not exceed about 850.degree. C.).

Operating pressures for the methane contacting step are not critical to the presently claimed invention. However, both general system pressure and partial pressure of methane have been found to affect overall results. Preferred operating pressures are within the range of about 1 to about 30 atmospheres.

Contacting methane and a reducible metal oxide to form higher hydrocarbons from methane also produces reduced metal oxides and water. The exact nature of the reduced metal oxides is unknown, and so is referred to herein as "reduced metal oxides". Regeneration of a reducible metal oxide is readily accomplished by contacting such reduced materials with oxygen (e.g., an oxygen-containing gas such as air) at elevated temperatures, preferably at a temperature selected within the range of about 300.degree. to about 1200.degree. C.; the particular temperature selected depending on the metal(s) included in the contact agent.

In carrying out the present process, a single reactor apparatus containing a fixed bed of solids may be used with intermittent or pulsed flow of a first gas comprising methane followed by intermittent or pulsed flow of a second gas comprising oxygen (e.g., oxygen, oxygen diluted with an inert gas, or air, preferably air). The methane contacting step and the oxygen contacting step may also be performed in physically separate zones with solids recirculating between the two zones.

Thus, a suitable method for synthesizing hydrocarbons from a methane source comprises: (a) contacting a gas comprising methane and particles comprising a contact agent to form higher hydrocarbon products, water and reduced metal oxide; (b) removing particles comprising reduced metal oxide from the first zone and contacting the reduced particles in a second zone with an oxygen-containing gas to form particles comprising a contact agent; and (c) returning the particles produced in the second zone to the first zone. The steps are preferably repeated at least periodically, and more preferably the steps are continuous. In the more preferred embodiment, solids are continuously circulated between at least one methane contact zone and at least one oxygen contact zone.

Particles comprising a reducible metal oxide which are contacted with methane may be maintained as fluidized, ebullating, or entrained beds of solids. Preferably, methane is contacted with a fluidized bed of solids.

Similarly, particles comprising reduced metal oxide which are contacted with oxygen may be maintained as fluidized, ebullating, or entrained beds of solids. Preferably, oxygen is contacted with a fluidized bed of solids.

In the more preferred embodiment of the present invention, methane feedstock and particles comprising a contact agent are continuously introduced into a methane contact zone maintained at synthesizing conditions. Synthesizing conditions include the temperatures and pressures described above. Gaseous reaction products from the methane contact zone (separated from entrained solids) are further processed (e.g., passed through a fractionating system wherein the desired hydrocarbon products are separated from unconverted methane and combustion products). Unconverted methane may be recovered and recycled to the methane contact zone.

Particles comprising reduced metal oxide are contacted with oxygen in an oxygen contact zone for a time sufficient to oxidize at least a portion of the reduced metal oxide to produce a reducible metal oxide and to remove (i.e., combust) at least a portion of any carbonaceous deposit which may form on the particles in the methane contact zone. The conditions of the oxygen contact zone will preferably include a temperature selected within the range of about 300.degree. to about 1200.degree. C., pressures of up to about 30 atmospheres, and average particle contact time within the range of about 1 to about 120 minutes. Sufficient oxygen is preferably provided to oxidize all reduced metal oxide to produce a reducible metal oxide and to completely combust any carbonaceous deposit material deposited on the particles. At least a portion of the particles comprising the contact agent which are produced in the oxygen contact zone are returned to the methane contact zone.

The rate of solids withdrawal from the methane contact zone is desirably balanced with the rate of solids passing from the oxygen contact zone to the methane contact zone so as to maintain a substantially constant inventory of particles in the methane contact zone, thereby enabling steady-state operation of synthesizing system.

The present invention is further illustrated by reference to the following Examples.

EXAMPLE I

27.6 grams of NaMnO.sub.4 -3H.sub.2 O (Pfaltz and Bauer SO-5560) was dissolved in 400 ml. of water. 138 grams of magnesia (Fisher MgO, heavy, U.S.P.) was calcined for 16 hours at 800.degree. C. The sodium permanganate solution and the calcined magnesia were slurried for 1 hour at 150.degree. F. The product was dried for 2 hours at 230.degree. F., crushed and then screened through a 60-mesh sieve. The powder was then calcined for 16 hours at 800.degree. C.

EXAMPLE II

27.6 grams of NaMnO.sub.4 -3H.sub.2 O (Pfaltz and Bauer SO-5560) was dissolved in 300 ml. of water. 122 grams of magnesia (Fisher MgO, heavy, U.S.P.) was calcined for 16 hours at 550.degree. C. The sodium permanganate solution, 100 grams of colloidal silica (Nalco 2326), and the calcined magnesia were slurried for 1 hour at 150.degree. F. The product was dried for 2 hours at 230.degree. F., crushed and then screened through a 60-mesh sieve. The powder was then calcined for 16 hours at 800.degree. C.

EXAMPLE III

27.6 grams of NaMnO.sub.4 -3H.sub.2 O (Pfaltz and Bauer SO-5560) was dissolved in 525 ml. of water. The solution and 144 grams of magnesia (Catalyst Resources, Inc. MgO-700 precursor (without addition of silica)) were slurried for 1 hour at 150.degree. F. The solid material was dried for 2 hours at 230.degree. C., crushed and then screened through a 60-mesh sieve. The powder was then calcined for 16 hours at 800.degree. C.

EXAMPLE IV

27.6 grams of NaMnO.sub.4 -3H.sub.2 O (Pfaltz and Bauer SO-5560) was dissolved in 300 ml. of water. The solution, 128 grams of magnesia (Catalyst Resources, Inc. MgO-700 precursor (without addition of silica)) and 100 grams of colloidal silica (Nalco 2326) were slurried for 1 hour at 150.degree. F. The solid material was dried for 2 hours at 230.degree. C., crushed and then screened through a 60-mesh sieve. The powder was then calcined for 16 hours at 800.degree. C.

EXAMPLE V

534 grams of NaMnO.sub.4 -3H.sub.2 O (Pfaltz and Bauer SO-5560) was dissolved in 1500 ml. of water and diluted up to 1900 ml. 2620 grams of magnesia (Basic Chemical Co. Magox 95) was calcined for 16 hours at 550.degree. C. The calcined magnesia was impregnated with the sodium permanganate solution. The product was dried for 2 hours at 230.degree. F., crushed and then screened through a 60-mesh sieve. The powder was then calcined for 16 hours at 800.degree. C.

EXAMPLE VI

27.6 grams of NaMnO.sub.4 -3H.sub.2 O (Pfaltz and Bauer SO-5560) was dissolved in 100 ml. of water. The sodium permangante solution, 100 grams of colloidal silica (Nalco 2326) and 307 grams of magnesia (Basic Chemical Co. Magox 95 precursor, mud) were slurried for 1 hour at 150.degree. F. The product was dried for 2 hours at 230.degree. F., crushed and then screened through a 60-mesh sieve. The powder was then calcined for 16 hours at 800.degree. C.

EXAMPLE VII

27.6 grams of NaMnO.sub.4 -3H.sub.2 O (Pfaltz and Bauer SO-5560) was dissolved in 400 ml. of water. 138 grams of magnesia (Malinckrodt MgO, U.S.P.) was calcined for 16 hours at 800.degree. C. The sodium permanganate solution and the calcined magnesia were slurried for 1 hour at 150.degree. F. The product was dried for 2 hours at 230.degree. F., crushed and then screened through a 60-mesh sieve. The powder was then calcined for 16 hours at 800.degree. C.

EXAMPLE VIII

27.6 grams of NaMnO.sub.4 -3H.sub.2 O (Pfaltz and Bauer SO-5560) was dissolved in 300 ml. of water. 122 grams of magnesia (Malinckrodt MgO, U.S.P.) was calcined for 16 hours at 550.degree. C. The sodium permanganate solution, 100 grams of colloidal silica (Nalco 2326) and the calcined magnesia were slurried for 1 hour at 150.degree. F. The product was dried for 2 hours at 230.degree. F., crushed and then screened through a 60-mesh sieve. The powder was then calcined for 16 hours at 800.degree. C.

Methane contact runs were made at about atmospheric pressure in quartz tube reactors (12 mm. inside diameter) partially packed with 10 ml. of contact solid. The reactors were brought up to temperature under a flow of heated nitrogen which was switched to methane at the start of the run. Unless otherwise indicated, all methane contact runs described in the Examples had a duration of two minutes. At the end of each methane contact run, the reactor was flushed with nitrogen and the solids were regenerated under a flow of heated air (usually at 800.degree. C. for 30 minutes). The reactor was then again flushed with nitrogen and the cycle repeated. Most of the results reported below are based on the cumulative samples collected after the contact solids were "equilibrated"; i.e., after the aberrant characteristics of the fresh contact solid had dissipated. This allows more meaningful comparison between the contact solid within the scope of the present invention and other contact solids. Three to six cycles of methane contact and regeneration are generally sufficient to equilibrate the contact solid.

Space velocities are reported as gas hourly space velocities (hr..sup.-1) (GHSV) and were 600 GHSV for the Examples. The results are shown in Table 1 below.

TABLE I______________________________________Ex. Test Atomic Ratio vs. Na % % % C.sub.2No. No. Na Mn Mg Si Conv. Selec. Yield______________________________________I 5511-09 1 1 24.0 -- 14.2 81.8 11.6II 5508-20 1 1 21.0 1.8 20.5 65.6 13.4III 5523-06 1 1 24.0 -- 14.2 11.2 1.6IV 5526-09 1 1 21.0 1.8 20.7 58.9 12.2V 5504-19 1 1 24.0 -- 13.0 52.6 6.8VI 5524-01 1 1 21.0 1.8 19.0 48.7 9.3VII 5515-01 1 1 24.0 -- 14.3 82.5 11.8VIII 5501-08 1 1 21.0 1.8 15.3 59.1 9.0______________________________________

The silica/magnesia support associated with the reducible oxide is shown to be more selective than its counterpart with the silica/magnesia support.

Claims

1. In an improved method for converting a gas comprising methane to higher hydrocarbons which comprises contacting said gas with a contact agent, said contact agent comprising:

(a) at least one metal, the oxide of which is reduced and produces higher hydrocarbons and water when contacted with methane at a selected temperature in the range of about 500.degree. to about 1000.degree. C.,

(b) an alkali metal, and

(c) a support,

the improvement which comprises employing said contact agent wherein said support comprises at least two oxides.

2. The method of claim 1 wherein said reducible oxide is selected from a group consisting of manganese, tin, indium, germanium, antimony, lead, bismuth, and mixtures thereof.

3. The method of claim 1 wherein said alkali metal is selected from a group consisting of lithium, sodium, potassium, rubidium, cesium, and mixtures thereof.

4. The method of claim 3 wherein said alkali metal is selected from a group consisting of sodium, sodium compounds, and mixtures thereof.

5. The method of claim 1 wherein said support comprises first and second oxides, said first oxide comprising alkaline earth metal.

6. The method of claim 5 wherein said support comprises magnesia.

7. The method of claim 5 wherein said second oxide is selected from a group consisting of silica, alumina, and mixtures thereof.

8. The method of claim 7 wherein said support comprises silica.

9. The method of claim 6 wherein said support comprises magnesia and silica.

10. The method of claim 5 wherein said support comprises a mole ratio of said first oxide to said second oxide of about 50:1 to about 1:1.

11. The method of claim 10 wherein the ratio of said magnesia to said silica in said support is about 30:1 to about 5:1.

12. The method of claim 5 wherein said mole ratio of said second oxide to said alkali metal is about 0.5:1 to about 10:1.