Methane conversion

Abstract

A method for synthesizing hydrocarbons from a methane source which comprises contacting methane with an oxide of manganese at a temperature of about 500.degree. to 1000.degree. C. The oxide is reduced by the contact and coproduct water is formed. A reducible oxide of manganese is regenerated by oxidizing the reduced composition with molecular oxygen. The oxide Mn.sub.3 O.sub.4 is a particularly effective synthesizing agent.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to synthesis of hydrocarbons from a methane source. A particular application of this invention is a method for converting natural gas to more readily transportable material.

2. Description of the Prior Art

A major source of methane is natural gas. Other sources of methane have been considered for fuel supply, e.g., the methane present in coal deposits or formed during mining operations. Relatively small amounts of methane are also produced in various petroleum processes.

The composition of natural gas at the wellhead varies but the major hydrocarbon present is methane. For example the methane content of natural gas may vary within the range of from about 40 to 95 vol. %. Other constituents of natural gas may include ethane, propane, butanes, pentane (and heavier hydrocarbons), hydrogen sulfide, carbon dioxide, helium and nitrogen.

Natural gas is classified as dry or wet depending upon the amount of condensable hydrocarbons contained in it. Condensable hydrocarbons generally comprise C.sub.3 + hydrocarbons although some ethane may be included. Gas conditioning is required to alter the composition of wellhead gas, processing facilities usually being located in or near the production fields. Conventional processing of wellhead natural gas yields processed natural gas containing at least a major amount of methane.

Large-scale use of natural gas often requires a sophisticated and extensive pipeline system. Liquefaction has also been employed as a transportation means, but processes for liquefying, transporting, and revaporizing natural gas are complex, energy-intensive, and require extensive safety precautions. Transport of natural gas has been a continuing problem in the exploitation of natural gas resources. It would be extremely valuable to be able to convert methane (e.g., natural gas) to more easily handleable, or transportable, products. Moreover, direct conversion to olefins such as ethylene or propylene would be extremely valuable to the chemical industry.

In addition to its use as fuel, methane is used for the production of halogenated products (e.g., methyl chloride, methylene chloride, chloroform and carbon tetrachloride). Methane has also been used as a feedstock for producing acetylene by electric-arc or partial-oxidation processes. Electric-arc processes are operated commercially in Europe. In partial-oxidation processes, a feed mixture of oxygen and methane (the methane may contain other, additional hydrocarbons) are preheated to about 540.degree. C. and ignited in a burner. Representative processes of this type are disclosed in U.S. Pat. Nos. 2,679,544; 3,234,300; and 3,244,765. Partial oxidation produces significant quantities of CO, CO.sub.2 and H.sub.2, yielding a dilute acetylene-containing gas and thereby making acetylene recovery difficult.

The largest, non-fuel use of methane is in the production of ammonia and methanol (and formaldehyde). The first, methane conversion, step of these processes is the production of a synthesis gas (CO+H.sub.2) by reforming of methane in the presence of steam over, for example, a nickel catalyst. Typical reformers are tubular furnaces heated with natural gas, the temperature being maintained at 900.degree. C. and the pressure at about 225 atmospheres.

Pyrolytic or dehydrogenative conversion of methane or natural gas to C.sub.2 + hydrocarbons has previously been proposed. The conversion requires high temperatures (greater than about 1000.degree. C.) and is characterized by the formation of by-product hydrogen. The patent literature contains a number of proposals to catalyze pyrolytic reactions, allowing conversion at lower temperatures. See, for example, U.S. Pat. Nos. 1,656,813; 1,687,890; 1,851,726; 1,863,212; 1,922,918; 1,945,960; 1,958,648; 1,986,238 and 1,988,873. U.S. Pat. No. 2,436,595 discloses and claims a catalytic, dehydrogenative methane-conversion process which employs fluidized beds of heterogeneous catalysts comprising an oxide or other compound of the metals of group VI or VIII.

Including oxygen in a methane feed for conversion over metal oxide catalysts has been proposed. Margolis, L. Ya., Adv. Catal. 14, 429 (1963) and Andtushkevich, T. V., et al, Kinet. Katal. 6, 860 (1965) studied oxygen/methane cofeed over different metal oxides. They report the formation of methanol, formaldehyde, carbon monoxide and carbon dioxide from methane/oxygen feeds. Higher hydrocarbons are either not formed or are converted much faster than methane.

Fatiadi has prepared an extensive review of reactions in which manganese dioxide is used for mild, selective heterogeneous oxidation of numerous classes of organic compounds. The use of manganese dioxide to form higher hydrocarbon products from methane is not mentioned. Fatiadi, A. J., "Active Manganese Dioxide In Organic Chemistry--Part I", Synthesis, 1976, No. 2, pp. 65, et seq. (February, 1976); Fatiadi, A. J., "Active Manganese Dioxide In Organic Chemistry--Part II", Synthesis, 1976, No. 3, pp. 133, et seq. (March, 1976).

It has been reported that manganese oxide forms manganese carbides from methane at 800.degree. C. Fisher, F., et al, Brenstoff--Chem., 10 261 (1929).

SUMMARY OF THE INVENTION

It has been found that methane may be converted to higher hydrocarbon products by contacting a methane-containing gas with an oxide of manganese at temperatures within the range of about 500.degree. to 1000.degree. C. Hydrocarbons produced include lower alkanes, lower olefins, and aromatics. The oxide of manganese is reduced by the methane contact and is easily reoxidizable by contact with an oxygen-containing gas.

The present process is distinguished from previously known pyrolytic methane conversion processes by the use of reducible oxides of manganese to synthesize higher hydrocarbons from methane with coproduction of water, rather than hydrogen.

The present process is also distinguished from previously suggested methane conversion processes which rely primarily on interactions between methane and at least one of nickel and the noble metals, such as rhodium, palladium, silver, osmium, iridium, platinum and gold. An example of this type of process is disclosed in U.S. Pat. No. 4,205,194. The present process does not require that methane be contacted with one or more of nickel and such noble metals and compounds thereof.

Morever, in a preferred embodiment, such contacting is carried out in the substantial absence of catalytically effective nickel and the noble metals and compounds thereof to minimize the deleterious catalytic effects of such metals and compounds thereof. For example, at the conditions, e.g., temperatures, useful for the contacting step of the present invention, these metals when contacted with methane tend to promote coke formation, and the metal oxides when contacted with methane tend to promote formation of combustion products (CO.sub.x) rather than the desired hydrocarbons. The term "catalytically effective" is used herein to identify that quantity of one or more of nickel and the noble metals and compounds thereof which when present substantially changes the distribution of products obtained in the contacting step of this invention relative to such contacting in the absence of such metals and compounds thereof.

Oxides of manganese which are reduced when contacted with methane at a temperature of about 500.degree.-1000.degree. C. include MnO.sub.2, Mn.sub.2 O.sub.3, Mn.sub.3 O.sub.4 or mixtures thereof. However, it has been further discovered that, of these reducible oxides of manganese, Mn.sub.3 O.sub.4 is the most effective in promoting high yields of hydrocarbon products. The spinel, Mn.sub.3 O.sub.4, is known to be formed by oxidation/decomposition of manganese compounds at temperatures above about 900.degree. C. and can be stabilized at lower temperatures, e.g., by being supported on silica.

This invention is further described in the following description of its presently preferred embodiments.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a plot of methane conversion and hydrocarbon product selectivity vs. time for the results reported in Example 3.

FIG. 2 is a plot of methane conversion vs. time for the results reported in Examples 2 and 5.

FIG. 3 is a plot of % C converted and hydrocarbon product selectivity vs. run time for the results reported in Example 10.

FIG. 4 is a plot of % C converted and hydrocarbon product selectivity vs. run time for the results reported in Example 11.

DETAILED DESCRIPTION OF THE INVENTION

Reducible oxides of manganese can be supplied from a variety of known sources. The term "reducible" is used to identify those oxides of manganese which are reduced by contact with methane at temperatures in the range of about 500.degree. to 1000.degree. C. Among the reducible oxides of manganese, those containing major amounts of Mn.sub.2 O.sub.3 and Mn.sub.3 O.sub.4 are preferred. A particularly preferred class of contacting agents are those comprising Mn.sub.3 O.sub.4.

The reducible oxide of manganese is preferably provided as solid particles. It may be supported by, or diluted with, a conventional support material such as silica, alumina, titania, zirconia, and the like, and combinations thereof. A presently preferred support material is silica.

The term "oxide of manganese" includes: (1) one or more manganese oxides of and/or (2) one or more oxygen-containing compounds of manganese, provided that such oxides and compounds have the capability of performing to produce higher hydrocarbon products as set forth herein. The reducible oxides of manganese may be employed alone or in combination with reducible oxides of other metals (see copending U.S. Application Ser. Nos. 522,944; 522,942; 522,905; 522,877; 522,876; and 522,906) and/or other oxidative synthesizing agents. Oxidative synthesizing agents are compositions comprising at least one oxide of at least one metal, which composition, when contacted with methane at a temperature selected within the range of about 500.degree. to 1000.degree. C., produces C.sub.2 + hydrocarbon products, coproduct water, and a composition comprising a reduced metal oxide.

Solids may be formed in conventional manner using techniques well known to persons skilled in the art. For example, supported solids may be prepared by conventional methods such as adsorption, impregnation, precipitation, coprecipitation, or dry-mixing.

A suitable method is to impregnate the support with solutions of a manganese compound. Some examples of manganese compounds are the acetate, acetylacetonate, oxide, carbide, carbonate, hydroxide, formate, oxalate, nitrate, phosphate, sulfate, sulfide, tartrate, fluoride, chloride, bromide or iodide. Such compounds of manganese may be dissolved in water or other solvent and the solutions combined with the support and then evaporated to dryness. Preferably, aqueous solutions are employed and water-soluble compounds of manganese are used. In some cases, the solutions may have acids and/or bases added to them to facilitate dissolution of the precursors of the oxide of manganese. For example, acids such as hydrochloric or nitric acid or bases such as ammonium hydroxide may be used as desired. The dried solids may then be screened or otherwise processed to form the desired shape, size, or other physical form of the finished solids. Finally, the solids are prepared for use by calcination at high temperatures for a period of time in accordance with conventional practice in this art. For example, the solids are placed in an oven or kiln, or in a tube through which oxygen (e.g., air or oxygen diluted with other gases) is passed, at an elevated temperature (e.g., about 500.degree. to 1200.degree. C., preferably about 700.degree. to 1200.degree. C., more preferably about 900.degree. to 1200.degree. C.). Use of higher calcination temperatures promotes the formation of Mn.sub.3 O.sub.4 in the finished solid.

The foregoing description regarding preparation of reducible oxides of manganese in a form suitable for the synthesis of hydrocarbons from a methane source is merely illustrative of many possible preparative methods, although it is a particularly suitable method and is preferred.

Manganese loadings on supported solids may be within the range of about 1 to 50 wt. % Mn (calculated as elemental metal).

In addition to methane, the feedstock employed in the method of this invention may contain other hydrocarbon or nonhydrocarbon components, although the methane content should be within the range of about 40 to 100 vol. %, preferably from about 80 to 100 vol. %, more preferably from about 90 to 100 vol. %.

Operating temperatures for the contacting of methane-containing gas and a reducible oxide of manganese are in the range of about 500.degree. to 1000.degree. C., preferably within the range of about 600.degree. to 900.degree. C.

Operating pressures for the methane contacting step are not critical to the presently claimed invention. However, both general system pressure and the partial pressure of methane have been found to effect overall results. Copending, concurrently filed U.S. application Ser. No. 522,935 discloses a method wherein an oxidative synthesizing agent comprising a reducible metal oxide is contacted with methane, the claimed improvement residing in the use of elevated pressures to promote the formation of C.sub.3 + hydrocarbon products.

Contacting methane and a reducible oxide of manganese to synthesize higher hydrocarbons also produces reduced oxide of manganese and coproduct water. The exact nature of the reduced form of the synthesizing agent is unknown, and so is referred to herein as "a reduced oxide of manganese". Regeneration of a reducible oxide of manganese is readily accomplished by contacting the reduced composition with oxygen (e.g., an oxygen-containing gas such as air) for a period of time sufficient to produce a reducible oxide of manganese from at least a portion of the reduced composition. Oxygen contacting temperatures are preferably within the range of about 300.degree. to 1200.degree. C., more preferably within the range of about 700.degree. to 1200.degree. C., still more preferably within the range of about 900.degree. to 1200.degree. C. Higher reoxidation temperatures promote formation of Mn.sub.3 O.sub.4, the preferred reducible oxide of manganese.

A single reactor apparatus containing a fixed bed of solids, for example, may be used with intermittent or pulsed flow of a first gas comprising methane and a second gas comprising oxygen (e.g., oxygen, oxygen diluted with an inert gas, or air, preferably air).

Preferably, the methane contacting step and the oxygen contacting step are performed in physically separate zones with solids recirculating between the two zones. Thus, a suitable method for synthesizing hydrocarbons from a methane source comprises: (a) contacting a gas comprising methane and particles comprising a reducible oxide of manganese to form higher hydrocarbon products, coproduct water, and particles comprising a reduced oxide of manganese; (b) removing particles comprising a reduced oxide from step (a) and contacting the reduced particles with an oxygen-containing gas to form particles comprising a reducible oxide of manganese; and (c) returning particles comprising a reducible oxide of manganese formed in step (b) to step (a). Steps (a), (b) and (c) are preferably repeated at least periodically, and more preferably the steps are continuous. Thus, in this more preferred embodiment, solids are continuously circulated between at least one methane-contact zone and at least one oxygen-contact zone. This more preferred embodiment is disclosed and claimed in copending, concurrently filed U.S. application Ser. No. 522,938.

Particles comprising a reducible oxide of manganese may be contacted with methane in fixed, moving, fluidized, ebullating, or entrained beds of solids. Preferably, methane is contacted with a fluidized bed of particles comprising a reducible oxide of manganese.

Similarly, particles comprising a reduced oxide of manganese may be contacted with oxygen in fixed, moving, fluidized, ebullating or entrained beds of solids. Preferably, oxygen is contacted with a fluidized bed of particles comprising a reduced oxide of manganese.

The invention is further illustrated by reference to the following examples.

The supported manganese oxides employed in the following examples were made by impregnating the appropriate amount of manganese, as manganous acetate, onto the supports from water solutions. Supports used were Houdry HSC 534 silica, Cab-O-Sil, Norton alpha-alumina and Davison gamma-alumina. The impregnated solids were dried at 110.degree. C. for 4 hours and then calcined in air at 700.degree. C. for 16 hours.

Composition of the calcined solids is identified in the following examples as "wt. % Mn/(support)".

Methane-contact runs were made at about atmospheric pressure in a quartz tube reactor (12 mm. inside diameter) packed with 10 ml. of catalyst. The reactors were brought up to temperature under a flow of nitrogen which was switched to methane at the start of the run. Instantaneous samples of the effluent were taken throughout the run and analyzed by gas chromatography and gas chromatography-mass spectroscopy. A cumulative run sample was also collected.

Experimental results reported below include conversions and selectivities calculated on a molar basis.

Solids productivity, reported as g/g-hr., is grams of methane converted to C.sub.2 + hydrocarbon products/gram of solid oxidative synthesizing agent/hour.

Examples 1-4 demonstrate the effect of manganese oxide loading on methane conversion. Total conversion is shown to bear a direct relationship to loading.

EXAMPLE 1

A feed of 100% methane was passed over a bed of 5 wt. % Mn/SiO.sub.2 according to the procedure described above. Contact zone temperature was 800.degree. C. and the GHSV (gas hourly space velocity) was 600 hrs.sup.-1. Results are reported in Table I below. No carbon formation was detected on the solid present at the end of the run.

TABLE I______________________________________Time % % Selectivity(min) conv. CH.sub.2 CH.sub.2 CH.sub.3 CH.sub.3 C.sub.3 C.sub.4 -C.sub.6 CO CO.sub.2______________________________________Instantaneous Results1 4.00 24.5 37.4 1.99 1.8 19.9 21.02 1.02 17.6 59.8 1.47 trace 14.34 .243 20.5 77.3 2.058 .166 22.2 74.6 3.030 .134 26.8 67.9 5.2Cumulative Results30 .429 27.2 45.8 2.9 9.7 9.1______________________________________

EXAMPLE 2

A feed of 100% methane was passed over a bed of 10 wt. % Mn/SiO.sub.2 according to the procedure described above. Contact zone temperature was 800.degree. C. and the GHSV was 600 hrs.sup.-1. Results are reported in Table II below. No carbon formation was detected on the solid present at the end of the run.

TABLE II______________________________________Run Time % % Selectivity(min) Conv. CH.sub.2 CH.sub.2 CH.sub.3 CH.sub.3 C.sub.3 CO CO.sub.2______________________________________Instantaneous Results*1 22.4 40.7 18.2 2.1 17.1 18.9 4 .85 28.9 48.6 22.412 .32 36.6 36.6 26.730 .27 56.7 43.2Cumulative Results30 1.77 24.5 23.9 24.4 26.4______________________________________ *Solids Productivity (Instantaneous) = 0.145 g/g hr.

EXAMPLE 3

A feed of 100% methane was passed over a bed of 15 wt. % Mn/SiO.sub.2 according to the procedure described above. Contact zone temperature was 800.degree. C. and the GHSV was 600 hrs.sup.-1. Results are reported in Table III below. No carbon formation was detected on the solid present at the end of the run. FIG. 1 is a plot of % methane conversion and % selectivity to C.sub.2 + hydrocarbon products vs. run time.

TABLE III______________________________________RunTime % % Selectivity(min) Conv. CH.sub.2 CH.sub.2 CH.sub.3 CH.sub.3 C.sub.3 C.sub.4 -C.sub.7 CO CO.sub.2______________________________________Instantaneous Results*1 30.1 36.5 13.9 2.15 3.56 19.5 24.2 2 12.3 42.9 27.0 17.0 12.912 .402 55.8 44.130 .308 51.8 41.8Cumulative Results30 2.27 31.8 23.9 15.8 28.3______________________________________ *Solids Productivity at 1 min = 0.157 g/g hr.

EXAMPLE 4

A feed of 100% methane was passed over a bed of 50 wt. % Mn/SiO.sub.2 according to the procedure described above. Contact zone temperature was 700.degree. C. and the GHSV was 600 hrs.sup.-1. Results are reported in Table IV below. No carbon formation was detected on the solids present at the end of the run.

TABLE IV______________________________________Run Time % % Selectivity(min) Conv. CH.sub.2 CH.sub.2 CH.sub.3 CH.sub.3 C.sub.3 CO CO.sub.2______________________________________Instantaneous Results 1 22.8 2.3 3.46 .01 94.2 2 11.6 3.5 9.37 .05 .17 86.8 4 7.39 4.44 14.8 .08 81.112 2.31 5.76 22.0 .13 .86 71.130 1.08 11.9 22.0 .36 65.6Cumulative Results30 4.12 4.26 12.5 .09 .36 82.6______________________________________

EXAMPLE 5

This example demonstrates the recyclability of the Mn oxide, oxidative synthesizing agent of this invention. The reduced solid remaining at the end of the run described in Example 2 was regenerated under a flow of air at 800.degree. C. for 30 minutes. The reactor was then flushed with nitrogen. The regenerated, reoxidized solids were then contacted with methane at a temperature of 800.degree. C. and a GHSV of 600 hrs..sup.-1. Results are shown in Table V below. No carbon oxides were detected during the oxidation of the reduced solids. Comparison of the results reported in Tables II and V indicates substantially complete recovery of Mn oxide activity for the conversion of methane to higher hydrocarbons. FIG. 2 is a plot of methane conversion vs. time for the combined results of Examples 2 and 5.

TABLE V______________________________________Run Time % % Selectivity(min) Conv. CH.sub.2 CH.sub.2 CH.sub.3 CH.sub.3 C.sub.3 CO CO.sub.2______________________________________Instantaneous Results 1 21.1 38.9 17.5 2.4 18.8 19.9 4 1.05 26.1 42.3 31.512 .42 40.9 26.9 29.830 .36 64.8 35.2Cumulative Results30 1.56 25.2 18.1 1.3 24.7 30.7______________________________________

EXAMPLE 6

The runs of this example show the effect of temperature on the conversion process of this invention. A feed of 100% methane was passed over a bed of 5 wt. % Mn/SiO.sub.2 at a GHSV of 600 hr..sup.-1. Results obtained at various contact temperatures are shown in Table VI below.

TABLE VI__________________________________________________________________________Time % % SelectivityTemp .degree.C. (min) conv. CH.sub.2 CH.sub.2 CH.sub.3 CH.sub.3 C.sub.3 C.sub.4 -C.sub.6 CO CO.sub.2__________________________________________________________________________Run AInstantaneous Results650 2 1.25 2.4 19.1 trace 39.0 39.4 4 .28 5.3 62.1 27.5 16 .081 8.6 91.3 30 .03 15.8 84.1Cumulative Results30 .223 6.7 52.0 21.5 19.7Run BInstantaneous Results700 2 1.95 10.5 39.2 .9 23.0 26.1 4 .896 9.9 53.5 .08 27.5 8 .31 13.0 87.1 trace 16 .087 13.7 86.2 30 .03 16.6 83.3Cumulative Results30 .319 14.1 67.1 9.4 9.4Run CInstantaneous Results750 2 2.65 18.2 44.0 1.5 19.9 16.3 4 .596 15.1 81.0 1.3 2.5 8 .164 14.6 85.3 16 .053 16.9 83.0 30 .041 17.0 83.0Cumulative Results30 .379 23.7 57.8 2.1 9.23 7.12__________________________________________________________________________ Example 1, supra, shows results of a similar run at 800.degree. C. Initial and cumulative conversions increase with temperature over the range of temperatures studied. Selectivities to higher, C.sub.3 +, hydrocarbons tend to increase with temperature as does the ratio of olefinic (e.g., ethylene) to paraffinic (e.g., ethane) hydrocarbon products. Formation of C.sub.3 + hydrocarbon products is promoted by higher temperatures.

EXAMPLE 7

Example 1 was repeated except that during preparation of the supported Mn oxide, the dried impregnated catalyst was calcined in air at 1000.degree. C. and the methane feed contained 16 vol. % methane, the remainder being N.sub.2. Contact temperature was 750.degree. C. and GHSV was 600 hrs..sup.-1. Results are shown in Table VII below. X-ray diffraction analysis of the calcined solid indicated that Mn was present as Mn.sub.3 O.sub.4.

TABLE VII______________________________________Run Time % % Selectivity(min) Conv. CH.sub.2 CH.sub.2 CH.sub.3 CH.sub.3 C.sub.3 CO CO.sub.2______________________________________Instantaneous Results 1 12.7 15.7 17.5 .39 19.0 47.3 2 10.1 18.7 27.9 .49 21.6 31.1 4 2.59 19.7 47.7 .77 16.5 15.2612 1.02 12.3 49.1 .48 38.130 .289 32.8 65.4 1.73Cumulative Results30 2.96 17.4 13.7 .23 24.3 44.28______________________________________

EXAMPLE 8

This example demonstrates the effect of space velocity on the methane conversion process of this invention. The procedure of Example 2 was repeated in the two Runs described in Table VIII below except that the space velocity of Run A was 1200 hrs.sup.-1 and space velocity of Run B was 300 hrs.sup.-1.

TABLE VIII______________________________________Run Time % % Selectivity(min) Conv. C.sub.2 H.sub.4 C.sub.2 H.sub.6 C.sub.3 C.sub.4 -C.sub.7 CO CO.sub.2______________________________________Run AInstantaneous Results.5 5.25 22.2 40.3 .15 27.0 8.81.0 .81 18.4 78.7 .85 1.94.0 .10 15.8 84.115.0 .08 22.6 77.3Cumulative Results15 .335 25.9 52.2 2.7 8.35 10.7Run BInstantaneous Results1 37.8 20.1 4.6 1.2 0.7 48.1 25.32 19.8 24.1 18.6 2.8 0.4 45.2 10.74 3.54 35.8 34.0 1.5 .5 28.212 2.21 34.7 55.0 1.5 0 8.830 1.75 30.0 68.7 1.3Cumulative Results30 3.85 33.2 19.2 1.4 .2 35.8 10.2______________________________________

EXAMPLE 9

Each of the following runs were made over 10 ml. catalyst with a 14-16 vol. % CH.sub.4 in N.sub.2 feed. The feed rate (calculated at standard conditions) was 100 ml/min, equivalent to a GSHV of 600 hrs.sup.-1. In Run A, the solid contacting agent was 5 wt. % Mn/gamma alumina and the contacting zone temperature was 750.degree. C. In Run B, the solid contacting agent was 5 wt. % Mn/alpha-alumina and the contacting zone temperature was 750.degree. C. In Run C, the solid contacting agent was 5 wt. % Mn/SiO.sub.2 solids which had been subjected to at least 10 methane contact/oxidation cycles. In the oxidation portion of these cycles, reduced solids from the methane-contacting portion of the cycle were regenerated under a flow of air at 700.degree. C. for 15 to 30 minutes and the reactor was then flushed with nitrogen before starting the next methane run. The contacting zone temperature for Run C was 700.degree. C. The results reported in Table IX are cumulative results obtained over a 30 minute contact time. X-ray diffraction analysis of the solid contacting agent used in Run C indicated that Mn was present as Mn.sub.3 O.sub.4.

TABLE IX______________________________________ Solids Productivity% % Selectivity .times. 10.sup.3Run # Conv. C.sub.2 H.sub.4 C.sub.2 H.sub.6 C.sub.3 CO CO.sub.2 (g/g-hr)______________________________________A 6.12 11.4 .48 31.7 54.5 1.06B 9.64 6.56 12.9 .07 80.3 0.95C 1.23 12.0 51.6 .85 19.6 15.8 1.49______________________________________

EXAMPLE 10

A feed of 95 vol. % methane and 5 vol. % ethane was passed over a bed of 5 wt. % Mn/SiO.sub.2 according to the procedure described above. The contact temperature was 700.degree. C. and the GHSV was 860 hrs.sup.-1. Unlike the runs described in the previous examples, a carbonaceous, coke-like deposit was present on the solids at the end of an 11 minute run. The results for the run, reported in Table X, below, are based on C in the feed converted to gas phase products only and do not take coke formation into account. The amount of carbonaceous deposit formed over the 11 minute run was 14.8% of all feed converted. FIG. 3 is a plot of % carbon converted and % selectivity to C.sub.2 + hydrocarbon products vs. run time for the results of this example.

TABLE X__________________________________________________________________________% ConversionRun Time Total C % Selectivity to Gas Phase Products(min) In Feed CH.sub.4 C.sub.2 H.sub.6 C.sub.2 H.sub.4 C.sub.3 C.sub.4 C.sub.5 Benzene CO CO.sub.2__________________________________________________________________________Instantaneous Results1 4.34 2.08 22.9 57.0 2.5 0.5 0.05 0.05 8.3 31.62 2.80 0.83 19.3 78.3 3.0 0.6 0.06 0.2 17.93 2.05 0.29 16.9 96.0 3.3 0.6 0.02 0.16 1.56 0.31 12.2 96.7 2.6 0.4 0.00 0.310 1.05 0.19 8.4 97.7 1.9 0.2 0.00 0.2Cumulative Results11 1.89 0.70 12.2 87.1 2.7 0.5 0.02 0.1 1.5 7.9__________________________________________________________________________

EXAMPLE 11

A feed of 95 vol. % methane and 5 vol. % ethylene was passed over a bed of 5 wt. % Mn/SiO.sub.2 according to the procedure described above. The contact temperature was 700.degree. C. and the GHSV was 860 hrs..sup.-1. A carbonaceous, coke-like deposit was present on the solids at the end of an 11 minute run. The amount of carbonaceous deposit formed was 35.6% of all feed C converted. A wax-like condensate was also noted at the reactor outlet. The amount of this condensate was 5.0% of all feed C converted. Results for the run are tabulated in Table XI, FIG. 4 is a plot of % C converted and % selectivity to C.sub.2 + hydrocarbon products vs. run time for this example.

TABLE XI__________________________________________________________________________% ConversionRun Time Total C % Selectivity to Gas Phase Products(min) In Feed CH.sub.4 C.sub.2 H.sub.4 C.sub.2 H.sub.6 C.sub.3 C.sub.4 C.sub.5 Benzene Toluene CO CO.sub.2__________________________________________________________________________Instantaneous Results1 4.62 3.31 17.7 9.5 8.5 5.0 0.9 1.2 0 26.9 48.12 2.58 1.66 11.8 15.1 14.2 8.8 1.8 3.0 0.6 28.4 28.13 1.68 0.78 9.8 17.9 26.2 14.9 3.0 6.0 1.2 23.2 7.76 0.38 0.13 2.7 5.0 55.4 22.2 2.6 12.2 2.610 0.23 0.13 1.3 0.5 56.1 26.1 4.3 12.5 0.5Cumulative Results11 1.52 1.01 6.2 9.4 20.7 11.8 1.9 4.4 0.7 12.5 38.7__________________________________________________________________________

Claims

1. A method for converting methane to higher hydrocarbon products which comprises contacting a gas comprising methane and a reducible oxide of manganese at a temperature within the range of about 500.degree. to 1000.degree. C., said contacting being carried out in the substantial absence of catalytically effective Ni, Rh, Pd, Ag, Os, Ir, Pt, Au and compounds thereof.

2. The method of claim 1 wherein the reducible oxide of manganese is contacted with a gas comprising methane at a temperature within the range of about 600.degree. to 900.degree. C.

3. The method of claim 1 wherein the gas contains about 40 to 100 vol. % methane.

4. The method of claim 3 wherein the gas contains about 80 to 100 vol. % methane.

5. The method of claim 4 wherein the gas contains about 90 to 100 vol. % methane.

6. The method of claim 1 wherein the gas comprising methane is natural gas.

7. The method of claim 1 wherein the gas comprising methane is processed natural gas.

8. The method of claim 1 wherein a gas consisting essentially of methane is contacted with the said reducible oxide.

9. The method of claim 1 wherein the reducible oxide of manganese comprises Mn.sub.3 O.sub.4.

10. The method of claim 1 wherein the oxide of manganese is associated with a support material.

11. The method of claim 9 wherein the oxide of manganese is associated with a support material.

12. The method of claim 10 wherein the support material is silica.

13. The method of claim 11 wherein the support material is silica.

14. A method for synthesizing hydrocarbons from a methane source which comprises:

(a) contacting a gas comprising methane with a solid comprising a reducible oxide of manganese at a temperature within the range of about 500.degree. to 1000.degree. C. to form C.sub.2 + hydrocarbons, coproduct water, and solids comprising a reduced oxide of manganese, said contacting being carried out in the substantial absence of catalytically effective Ni, Rh, Pd, Ag, Os, Ir, Pt, Au and compounds thereof;

(b) recovering C.sub.2 + hydrocarbons;

(c) at least periodically contacting the solids comprising the reduced oxide of manganese with oxygen containing gas to produce a solid comprising a reducible oxide of manganese; and

(d) contacting a gas comprising methane with the solids produced in step (c) as recited in step (a).

15. The method of claim 14 wherein the temperature of step (c) is within the range of about 300.degree. to 1200.degree. C.

16. The method of claim 14 wherein the temperature of step (c) is within the range of about 700.degree. to 1200.degree. C.

17. The method of claim 14 wherein the temperature of step (c) is within the range from about 900.degree. to 1200.degree. C.

18. The method of claim 17 wherein the reducible oxide of manganese comprises Mn.sub.3 O.sub.4.

19. The method of claim 16 wherein the said solid of step (a) comprises Mn.sub.3 O.sub.4 on a silica support.

20. The method of claim 14 wherein solids of step (a) are maintained in the methane-contacting zone as a fluidized bed.

21. The method of claim 20 wherein solids of step (c) are maintained in the oxygen-contacting zone as a fluidized bed.

22. The method of claim 21 wherein the temperature of step (a) is within the range of about 600.degree. to 900.degree. C.

23. The method of claim 22 wherein the temperature of step (c) is within the range of about 700.degree. to 1200.degree. C.