Patent Application
20130189906
1. Field of the Invention
The present invention relates to the field of chemical mechanical planarization (CMP) and relates specifically to CMP pad conditioning apparatus and method of use.
2. Description of the Related Art
In modern integrated circuit (IC) fabrication, layers of material are applied to embedded structures previously formed on semiconductor wafers. Chemical mechanical planarization (CMP) is an abrasive process used to remove these layers and polish the surface of a wafer to achieve the desired structure. CMP may be performed on both oxides and metals and generally involves the use of chemical slurries applied in conjunction with a polishing pad in motion relative to the wafer (e.g., pad rotation relative to the wafer). The resulting smooth flat surface is necessary to maintain the photolithographic depth of focus for subsequent processing steps and to ensure that the metal interconnects are not deformed over contour steps. Damascene processing requires metal, such as tungsten or copper, to be removed from the top surface of dielectric using CMP to define interconnect structures.
Polishing pads are typically made of urethanes either in cast form (and filled with micro-porous elements) or from nonwoven felt coated with polyurethanes. During polishing, the pad surface undergoes deformation due to polishing forces. The pad surface therefore has to be “regenerated” through a conditioning process.
Conventional conditioning processes involve pressing a fine diamond covered disc against the pad surface while pad is rotated much like during polish process. One of the issues with diamond conditioning disks is that diamonds tend to lose their sharpness over time. The process is accelerated when diamond conditioning is used during wafer processing, as slurry chemicals tend to accelerate the wear.
Another problem with diamond conditioners is the attendant risk of diamonds getting loose and falling onto the pad. This can lead to severe damage to the semiconductor wafer resulting in loss of product. Further, diamond conditioners tend to be expensive and have a finite lifespan, therefore needing to be replaced after predetermined usage.
Hence, there exists a need for conditioning apparatus that does not suffer from disadvantages such as those discussed above and that provides repeatable performance at relatively low cost.
A polishing pad conditioning apparatus and method is described. The apparatus includes a laser beam generating unit and a system to transmit or focus the laser beam. The laser beam generating unit, or in some cases only the beam delivery unit, is mounted on a conditioning arm, such that the laser beam may be directed perpendicular to the plane of the polishing pad, which is next to a polishing platen. The conditioning arm is capable of moving across the polishing table to scan the pad radius, allowing the laser to traverse the pad radius. The beam is incident on the pad, creating a local deformation, the depth and shape of the deformation depends on the beam spot size and power. The beam may be traversed across the pad in a predetermined trajectory creating a desired micro grooving pattern. As the conditioning unit is traversed across the polish platen, onto which the polishing pad is mounted, the platen is rotated thereby allowing the beam to cover the entire pad. The rotation speed of the pad, traversing speed of the laser conditioning head, and rotation speed of the laser head unit itself can be varied to provide the desired micro groove pattern.
In varying embodiments of the present invention, the laser beam is mounted off-center from the conditioning head and is capable of rotation, which when combined with the pad rotation and traversing motion of the conditioning unit, can create multiple micro grooving patterns. In yet another embodiment, multiple beam units may be mounted on the conditioning head enabling multiple points to create the micro grooving texture rapidly and more uniformly.
In other embodiments, the laser beam may impinge the pad at a non-normal angle. This creates an angled microgroove pattern, which may be desirable in certain cases.
Various other embodiments of the present invention provide a polishing pad conditioning system, having a laser beam generation unit coupled to provide a laser beam via a fiber optic transmission and focusing unit; an atomized fluid delivery line coupled to direct a fluid stream proximate a vicinity at which the laser beam exiting the fiber optic transmission and focusing unit will be incident on a target; and a vacuum line coupled to remove fluid and debris from the vicinity at which the laser will be incident on the target.
Alternative embodiments of the invention provide a polishing pad conditioning system, having a laser beam generation unit coupled to provide a laser beam via a fiber optic transmission and focusing unit; an atomized fluid delivery line coupled to deliver a fluid into an interaction zone within a conditioning head of the polishing pad conditioning system and thru which the laser beam also passes; and a vacuum line coupled to remove fluid and debris from a vicinity at which the laser will be incident on a target.
Still further embodiments of the invention provide a polishing pad conditioning head, having a beam delivery unit, a fluid delivery unit and a vacuum line, each mounted on a pad conditioning arm that is adjacent a polishing table, the pad conditioning arm configured to traverse a radius of a polishing pad mounted on the polishing table.
In various embodiments of the invention, the laser beam delivery unit and the fluid delivery unit may be mounted separately from each other and/or mounted so that a laser beam produced by the laser beam delivery unit and a fluid stream produced by the fluid delivery unit are combined within the conditioning head prior to impinging upon a surface of the polishing pad. The fluid delivery line may be coupled to a fluid delivery system that uses compressed air. The laser beam generation unit may include an Er, Cr:YSGG laser or CO2 laser and the fluid delivery line may be coupled to a fluid delivery system configured to deliver deionized water, a pad cleaning solution, an acidic solution, a basic solution, or a film polish solution.
A further embodiment of the invention involves bringing a polishing pad conditioning head of a polishing pad conditioning apparatus in close proximity to a polishing pad surface while the polishing pad is being used to polish a wafer by pressing the wafer against the polishing pad, the polishing pad conditioning apparatus providing at least one laser beam and a fluid stream directed at the polishing pad and a vacuum for removing debris from a vicinity of the polishing pad near the polishing pad conditioning head, whereby surface micro grooves on the polishing pad are continually refreshed by action of the polishing pad conditioning head while the polishing pad polishes the wafer.
These and other features of the present invention are described in greater detail below.
So that the manner in which the above recited features of the present invention can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.
The present invention is illustrated by way of example, and not limitation, in the figures of the accompanying drawings, in which:
The present invention relates to the design and method of a non-contact polishing pad conditioning unit. The design involves a laser beam generating unit, and beam transmission and delivery optics as necessary. Additional lines to supply liquid(s), typically water, air and vacuum are also provided. The entire unit (e.g., a laser conditioning head), including the beam delivery hardware and atomized fluid and vacuum lines, is mounted on a movable arm capable of traversing the radius of the polishing pad, which is itself mounted on a polishing table. In some cases the laser-conditioning head may be mounted such that the beam is off-center on the conditioning head, which is capable of rotating. A rotating beam thus impinges on the pad surface creating circular grooving patterns. This, when coupled with pad rotation and traversing the beam across the radius of the pad, creates a micro groove pattern across the entire pad surface.
It is possible to use several types of laser units in this application such as a CO2 laser, diode lasers, an Nd—YAG laser, etc. Typical CO2 lasers used to cut or engrave plastics are in the range of 10-50 Watts. Pad conditioning may be accomplished with lasers as low as 1 Watt.
Another aspect of conditioning is that the polishing pads are wet during processing. CO2 lasers have wavelengths of 10.6 microns, which make them well suited for transmitting energy to water molecules. Lasers with lower wavelengths may also be used. When a laser is incident on a wet polishing pad, water heats up instantaneously and boils off, rupturing the pad's polymer surface with it. This process, in combination with the ability to cut the polymer surface itself, creates a unique microgroove texture on the pad surface. The laser may be coupled with water/fluid, which may be optionally atomized, to provide a beam thru the fluid. The atomized fluid stream serves several purposes. For example, the liquid provides a cooling aspect to the surface being impinged with the laser beam by absorbing some of the energy of the laser beam, and the atomized droplets can provide a “cooler” cutting action, thereby eliminating a burr/burn effect. A vacuum line enables removal of fluid and pad debris. Different fluids may be employed depending on the process and film being polished, for example in the case of a copper polishing process, the fluid may be a pad cleaning solution such as Electraclean™ from Applied Materials, Inc. of Santa Clara, Calif., or a copper polishing solution. In the case of an oxide polishing process, fluids with a pH approximately equal to the pH of the oxide polish slurry may be used.
Use of a laser conditioning system solves several problems. Most notably, the pad conditioning process becomes very repeatable and stable. By eliminating diamond conditioning discs, the risk of diamond loss is eliminated. This failure mode causes scratches on the product wafers resulting in catastrophic product loss and equipment down time. Also, the use of lasers provides a repeatable, long lasting and low cost method of producing micro grooving on a polishing pad surface, eliminating the diamond conditioning disc, which is an expensive consumable with a short life.
The focusing unit 208, fluid delivery line 212 and vacuum lines 214 are all separately and directly connected to the laser conditioning head assembly 359. Polishing pad 357 lies within an interaction zone so as to receive the laser beam at maximum intensity.
In operation, the laser energy exits the delivery system 319 and is applied to the pad surface according to a predetermined (e.g., programmed) conditioning cycle. A controller 353, which may include a computer processor and a memory storing instructions for directing the operation of the laser conditioning unit, may be used for this purpose. Fluid, which may be an air and water mixture, travels along line 212, and is directed at or near the same location as the laser beam. The fluid contacts and cools the pad surface as it is being cut and helps to remove materials cut by the laser.
Water is generally used in a variety of laser cutting operations in order to cool the target surface. Additionally, water is used in the initial pad surface preparation, also called pad break-in operations, for cooling the pad and removing cut materials therefrom. During or between polishing operations, pad conditioning processes use water or slurry during conditioning operations depending on whether conditioning is being performed during or in-between polishing operations. In the case of metal polishing, such as copper polishing, pad cleaning solutions may also be used.
According to one aspect of the present invention, a mist of atomized particles is placed into a volume of air above the pad surface to be conditioned, and a laser source is focused into the volume of air. The laser has a wavelength that is substantially absorbed by the atomized particles in the volume of air. This absorption of the laser energy by the atomized particles causes the atomized particles to explode and impart mechanical cutting forces onto the surface of the polishing pad undergoing conditioning. Accordingly, the laser does not directly cut the pad surface, rather, the exploded fluid particles are used to create a texture on the pad surface. These fluid particles may be conditioned with specific additives such as pad cleaning agents, film polishing fluids, pH adjustments, and other agents, as discussed above.
Since the laser energy is focused directly on the atomized, conditioned fluid particles, the cutting forces may be changed, depending upon the conditioning of the atomized fluid particles. The mechanical cutting efficiency is proportional (related) to the absorption of the laser energy by the fluid particles. The absorption characteristics can be modified by changing the fluid's composition. The fluids used for cooling a pad conditioning site and/or removing pad debris may further include chemical constituents for pad cleaning or film polishing.
According to an aspect of the present invention, the laser energy from delivery unit 319 is focuses onto atomized fluid in the interaction zone 362. Atomized fluid particles in the air absorb energy from the laser and explode. The explosive forces from these atomized fluid particles impart mechanical cutting forces onto the surface of the pad.
Intense energy is emitted from the delivery system 319. In embodiments of the invention, the laser source may be an erbium, chromium, yttrium, scandium, gallium garnet (Er, Cr:YSGG) solid state laser. A CO2 laser may also be used. When fluids besides mere water are used, the absorption of the light energy changes and cutting efficiency is thus affected. Laser systems of different wavelengths, such as neodymium yttrium aluminum garnet (Nd:YAG) lasers, may be selected to allow for high energy absorption by the fluid. Many of the above-discussed additives to the atomized fluid may change the absorption of the laser energy into the atomized fluid particles in the laser-induced mechanical cutting environment. Accordingly, the type of conditioning afforded by these fluid additives may affect the pad surface cutting ability of the system.
A pad conditioning apparatus configured in accordance with the present invention may have one or more laser sources such as those discussed above each with at least one laser beam incident on or near the pad surface. The laser conditioning system is configured to traverse the surface of the polishing pad with the laser beam(s) in order to effect a micro groove pattern on the pad using any or at of the pad surface cutting techniques described above. The beam(s) may be directed so as to be at any angle to the plane defined by the surface of the polishing pad as it rotates on the platen. In some instances, pad conditioning may be conducted at the same time as the pad is used for polishing substrates or other items (in situ conditioning), while in other cases condition may be performed between substrate polishing operations (ex-situ conditioning).
Accordingly, in one embodiment of the invention, a polishing pad conditioning head of a polishing pad conditioning apparatus is brought in close proximity to a polishing pad surface while the polishing pad is being used to polish a wafer by pressing the wafer against the polishing pad. The polishing pad conditioning apparatus provides at least one (although sometimes more than one) laser beam and a fluid stream directed at the polishing pad and a vacuum for removing debris from a vicinity of the polishing pad near the polishing pad conditioning head. In this way, surface micro grooves on the polishing pad are continually refreshed by action of the polishing pad conditioning head while the polishing pad polishes the wafer. An alternative embodiment involves polishing a first wafer using a polishing pad by pressing the first wafer against a polishing surface of the polishing pad. Upon completion of the polishing (or during a pause in the polishing), a polishing pad conditioning head of a polishing pad conditioning apparatus is brought in close proximity to the polishing surface of the polishing pad surface and at least one (though sometimes more than one) laser beam and a fluid stream are directed at the polishing surface of the polishing pad. A vacuum or suction is provided for removing debris from a vicinity of the polishing pad near the polishing pad conditioning head. In this way, surface micro grooves on the polishing surface of the polishing pad are refreshed. Upon completion of the refreshing of the surface micro grooves (though in some cases only a portion of the polishing surface is refreshed) a second wafer is polished using the polishing pad (or polishing of the original wafer continues).
Thus, a polishing pad conditioning apparatus and method have been described. In various embodiments, the apparatus includes a laser beam generating unit along with means to transmit and/or focus a laser beam produced thereby, a fluid delivery system for providing a fluid stream and a vacuum line for removing debris. The laser beam may directly impinge on a polishing pad surface thereby creating cutting action, while an atomized fluid stream provides cooling and pad debris along with fluid are removed thru the vacuum line. In another embodiment, the laser beam is combined with the atomized fluid stream in a region above the pad surface and substantially imparts part of its energy to the fluid stream, generating high energy droplets which provide “cool” cutting action on the pad surface. The beam delivery system along with the atomized fluid line and vacuum line (together integrated in a laser conditioning head), are mounted on a moveable arm, such that the laser beam may be oriented at an angle (e.g., perpendicular or other than perpendicular) to a plane defined by the surface of the polishing pad, which is mounted on a polishing platen. The conditioning arm is capable of moving across the polishing platen to scan the pad radius, allowing the laser to traverse the pad radius. The beam is incident on the pad, creating a local deformation, the depth and shape of the deformation depending on the beam spot size and energy. The beam may be traversed across the pad, while the pad is rotated on the platen, in a predetermined trajectory creating a desired micro grooving pattern covering the entire pad. The rotation speed of the pad, traversing speed of the laser conditioning head, and rotation speed of the laser head unit itself can be varied to provide the desired micro groove pattern.
In varying embodiments of the present invention, the laser beam is mounted off center from the conditioning head and is capable of rotation, which, when combined with pad rotation and the traversing motion of the conditioning unit, can create multiple micro grooving patterns. In yet another embodiment, multiple beams may be generated using a beam splitter, mounted on the conditioning head, enabling multiple points to create the micro grooving texture rapidly and more uniformly.
In other embodiment, the laser beam may impinge the pad at a non-normal angle. This creates an angled microgroove pattern, which may be desirable in certain cases.
Although exemplary embodiments of the invention have been shown and described, many other changes, modifications and substitutions, in addition to those set forth above may be made by one having ordinary skill in the art without necessarily departing from the spirit and scope of this invention.
While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.
This application is a continuation of U.S. patent application Ser. No. 12/636,644, filed Dec. 11, 2009 (now U.S. Pat. No. 8,398,463) which is a continuation-in-part of U.S. patent application Ser. No. 11/369,876, filed Mar. 6, 2006 (now U.S. Pat. No. 7,762,871), which claims benefit of U.S. Provisional Application Ser. No. 60/659,384 filed Mar. 7, 2005, all of which are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12636644 | Dec 2009 | US |
| Child | 13785845 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11369876 | Mar 2006 | US |
| Child | 12636644 | US |