Patent Application
20090205965
The present invention relates to an oxide coating method for coating a metal plate with an oxide and an oxide coating apparatus used for forming an oxide film.
It has been usual practice to give chemical treatment to the surface of a metallic material used for a container for packing food or drink, such as a steel sheet, a tin plate made by coating a steel sheet with tin, or aluminum, to form an oxide or hydroxide film on its surface to improve its corrosion resistance and coating adhesion, particularly its coating adhesion as required when it is processed. An oxide film is formed by forming an oxide directly on the surface of a metallic material, or by forming a hydroxide on the surface of a metallic material and causing it to react with oxygen in the air to form an oxide. There is also a hydroxide reacting only slowly with oxygen in the air. For simplicity of description, these oxides, hydrous oxides and hydroxides will hereinafter be referred to merely as oxides. A method relying on dipping a metal plate in a treating solution or a method relying on electrolysis in a treating solution is employed as a method of forming an oxide film. The method relying on dipping is a simple and convenient method of treatment, but is likely to be able to form only a film having too small a thickness to exhibit any satisfactory corrosion resistance or coating adhesion as intended. The method relying on electrolysis, which forms an oxide film instead of a film of metal plating, involves difficulty in achieving an adequate control of various conditions including the bath composition containing an oxidizing agent, its pH and the conditions of electrolysis and is not beneficial from a cost standpoint, either, as it requires a larger amount of electricity than metal plating.
Technique as shown below is, for example, disclosed as a technique for forming an oxide film on the surface of a metal plate. Patent Literature 1 discloses a method in which not a tin plate, but a DI tin can made by drawing and ironing a tin plate is brought into contact with a surface treating solution containing a water-soluble composition containing a phosphate ion, a condensed phosphate ion and a water-soluble polymer so that corrosion resistance and paint adhesion may be imparted to the can surface before coating or printing, but as it is a method of forming a film on the surface of a can body after its processing, and is not intended for improving the adhesion of a coating during its processing, but can form only a very thin film, it is not applicable as a method for chemical treatment of a flat sheet yet to be processed.
Patent Literature 2 discloses a method of forming a considerably thick film on a metallic material including a tin-plated steel sheet by its surface treatment with a metal surface treating agent for a precoated steel sheet containing a silane coupling agent and/or a hydrolysis condensate thereof, water-dispersible silica and a zirconium compound, but when this metal surface treating agent is applied to a tin-plated steel sheet used as a can material, no satisfactory corrosion resistance can be obtained if it is used without the addition of any water-dispersible silica as it makes a film too thick.
The following is the prior art literature information pertaining to the present application:
The present invention is aimed at providing by employing a simpler and more convenient method, a method of oxide coating which is inexpensive and has excellent corrosion resistance and coating adhesion, and an oxide coating apparatus used for forming an oxide film.
The oxide coating method of the present invention which solves the above problems is an oxide coating method characterized by applying a direct current voltage between an anode and a cathode formed from a metal plate to be coated with an oxide, which is positioned (situated) opposite the anode in an electrolyte, and supplying gas into the electrolyte to coat it with the oxide (claim 1), or
an oxide coating method as set forth above (claim 1), wherein the gas is oxygen, or a gas containing oxygen (claim 2), or
an oxide coating method as set forth above (claim 1 or 2), wherein the gas is supplied through bubble generating means situated below or beside the space between the anode and cathode (claim 3), or
an oxide coating method as set forth above (claim 1, 2 or 3), wherein the gas is supplied in the form of fine bubbles (claim 4), or an oxide coating method as set forth above (claim 1, 2, 3 or 4), wherein the gas is so supplied as to contact the cathode surface (claim 5).
The oxide coating apparatus of the present invention is an oxide coating apparatus characterized by having an anode and a cathode situated opposite the anode in an electrolyte and formed from a metal plate to be coated with an oxide, and bubble generating means for supplying gas into the electrolyte (claim 6), or
an oxide coating apparatus as set forth above (claim 6), wherein the anode is an insoluble anode (claim 7), or
an oxide coating apparatus as set forth above (claim 6 or 7), wherein the gas is oxygen, or a gas containing oxygen (claim 8), or
an oxide coating apparatus as set forth above (claim 6, 7 or 8), wherein the bubble generating means is situated below or beside the space between the anode and cathode (claim 9), or
an oxide coating apparatus as set forth above (claim 6, 7, 8 or 9), wherein the bubble generating means is a porous body connected to a source of gas supply (claim 10), or
an oxide coating apparatus as set forth above (claim 10), wherein the porous body has a pore diameter of 1 to 1,000 μm and a void ratio of 5 to 95% (claim 11), or
an oxide coating apparatus as set forth above (claim 10 or 11), wherein the porous body is a sintered body of any of a metal powder, a ceramic powder and an organic resin powder (claim 12), or a foamed product of any of a foamed metal, a foamed ceramic and a foamed organic resin having open cells (claim 13).
(Oxide Coating Method and Apparatus)
The present invention will now be described in detail by way of a preferred example in which oxygen gas is employed as the gas supplied into the electrolyte near the surface of a metal plate defining the cathode.
If electrolysis is performed without any such gas being supplied into the electrolyte 17, on the other hand, the source of oxygen for the oxide film formed on the cathode 13 is limited to oxygen dissolved in the electrolyte, or oxygen formed at the anodes 12 during electrolysis and the arrival of oxygen at the cathode 13 determines the rate of formation of the oxide film.
As the metal plate 13, it is possible to employ not only a low carbon steel sheet as a container material, or plated steel sheet made by coating a low carbon steel sheet with tin or nickel, but also zinc-coated steel sheet, zinc alloy-coated steel sheet, stainless steel sheet, aluminum alloy sheet, copper sheet, copper alloy sheet, nickel sheet, nickel alloy sheet, etc.
The anodes 12 may be soluble anodes formed from the same metal as the metal forming the oxide film to be formed, and capable of supplying the ion of that metal, or insoluble anodes participating merely in the transportation of electrons.
The bubble generating means 14 preferably has a porous layer formed on its surface to form bubbles from the entire surface of its porous layer to generate fine bubbles of oxygen gas into the electrolyte 17. It may, for example, be formed by a hollow cylindrical body 21 composed of a porous body 22 and having one end 23 closed tightly, while a pipe connector 24 for supplying oxygen gas is formed at the other end 25 thereof, as shown in
The porous body 22 preferably has a pore diameter of 1 to 1,000 μm. A porous body 22 having a pore diameter of less than 1 μm is very difficult to produce and is easily clogged during its use. A porous body having a pore diameter exceeding 1,000 μm generates so large bubbles that an oxide film is difficult to form and is likely to be uneven in adhesion. The porous body 22 is also required to have a void ratio of 5 to 95%. A porous body having a void ratio of less than 5% generates so small an amount of bubbles that an oxide film is difficult to form, and a porous body 22 having a void ratio exceeding 95% makes the generation of bubbles uneven along its length, or along the width of the metal plate 13. The cylindrical body 21 may have any shape in cross section, such as circular, oval, square or otherwise polygonal.
It is preferable to employ pure oxygen or air as oxygen for the oxygen gas generated in the form of fine bubbles in the electrolyte 17, since it does not adversely affect the environment, and it is more preferable from the standpoints of work safety and cost to use air compressed by a compressor, etc.
The present invention does not preclude any electrolysis performed while supplying oxygen-free gas as gas for stirring the electrolyte and forming an oxide film, as its stirring accelerates the arrival of oxygen dissolved in the electrolyte or oxygen formed at the anodes by electrolysis, which is effective to some extent for the formation of an oxide film. It is desirable in that case, too, that gas in the form of fine bubbles be so supplied as to contact the surfaces of the cathode metal plate.
(Preparation of Sample Sheets)
Low-carbon steel sheet (having a thickness of 0.18 mm) employed as a substrate to be coated was electrolytically degreased in an aqueous alkali solution, pickled by dipping in sulfuric acid, and coated with tin on both sides (with a coating weight of 2.5 g/m2) by using a known ferrostan bath to make a tin-coated steel sheet.
Samples were prepared by forming on both sides of the tin-coated steel sheet an oxide film having the coating weight shown in Table 1 under the treatment conditions shown in Table 1 by employing the oxide coating apparatus shown in
1)In terms of metallic zirconium or aluminum.
As is obvious from the table, the oxide coating of any sample prepared by applying a voltage, while generating fine bubbles of gas containing oxygen in the electrolyte can be formed by employing only a by far smaller amount of electric charge than the oxide coating of any comparative sample prepared by applying a voltage without generating fine bubbles of gas containing oxygen in the electrolyte can, when they are formed with the same coating weight.
According to the present invention, the oxide coating method in which a direct current voltage is applied between the anodes and the cathode formed from a metal plate to coat it with an oxide, while gas is supplied into the electrolyte, and the oxide coating apparatus having the anodes, the cathode formed from a metal plate and the bubble generating means for supplying gas into the electrolyte, make it possible to form an oxide film having the necessary thickness by employing a smaller amount of electric charge than when electrolysis is performed without any oxygen or like gas supplied into the electrolyte. This is due to the fact that stirring by gas accelerates the arrival at the cathode of oxygen dissolved in the electrolyte and oxygen produced at the anodes by electrolysis and thereby exerts a positive effect on the formation of an oxide film. The constant supply of oxygen to the surface of the metal plate used as the cathode enables the formation of an oxide film to proceed more efficiently. The supply of fine bubbles of oxygen to the surface of the metal plate as the cathode enables the formation of an oxide film to take place still more efficiently. The supply of the gas in contact with the cathode surface is particularly effective for eliminating any variation occurring in concentration near the cathode surface and forming an oxide film very efficiently.
As it is possible to obtain a uniform film having the necessary thickness more reliably with a smaller amount of electric charge than when employing a treating solution prepared by adding an oxidizing agent to the electrolyte, it is possible to manufacture an oxide-coated metal sheet at a low cost.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2003-432983 | Dec 2003 | JP | national |
| 2004-314500 | Oct 2004 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP04/16565 | 11/9/2004 | WO | 00 | 4/23/2009 |