The present disclosure generally relates to spray coating methods and apparatus and, more particularly, relates to a method and apparatus for microplasma spray coating a blade root of a compressor blade in a gas turbine engine.
Plasma coating methods and apparatus are known. For example, one patent relates to a method and apparatus for plasma flame spray coating material onto a substrate. The patent discloses a method and apparatus for plasma flame spray coating material onto a substrate by means of passing a plasma forming gas through a nozzle electrode, and passing an arc forming current between the nozzle electrode and a rear electrode to form a plasma effluent. The method includes introducing coating material into the plasma effluent, passing the plasma effluent axially through a wall shroud extending from the exit of said nozzle electrode, and forming a flame shroud for the plasma effluent. The coating is thereby applied to the substrate.
One area where such technology is particularly advantageous is in connection with coating various aircraft components, particularly gas turbine engines and their components. For example, the blade roots of compressor blades can be coated with material to meet dimensional tolerance requirements for sealing the compressor blade with the compressor wheel and the like. Metallic coatings consisting of copper-nickel, aluminum-copper, and other similar composition materials have been applied in this regard using various conventional plasma spray coating processes. Typically, the coating process requires the compressor blade to be masked in areas where the material transfer is not required and/or not desired. Furthermore, the compressor blade is typically coated in a dedicated facility such as an aircraft engine manufacturing plant or repair shop. Prior art methods and apparatus required masking the compressor blade and applying the coating in dedicated facilities because the coating equipment was large and not portable and the spray pattern was too wide to accurately control the coating process. It would be desirable to improve the accuracy of spray coating devices so that masking and the like would not be required, as well as permitting hand spray coating repairs in the field of operation.
In accordance with one aspect of the disclosure, a microplasma spray apparatus for coating at least a portion of a gas turbine compressor blade is provided. A microplasma gun includes an anode, cathode, and an arc generator for generating an electric arc between the anode and cathode. The apparatus includes an arc gas emitter for injecting gas into the electric arc. The electric arc is operable for ionizing the gas to create a plasma gas stream. A powder injector injects powdered material into the plasma gas stream. The compressor blade can be coated in a localized area with the powdered material without masking the compressor blade.
In accordance with another aspect of the present disclosure, a method for microplasma spray coating a gas turbine compressor blade is provided. The method includes providing a microplasma spray gun having an anode and cathode and means for generating an electric arc between the anode and the cathode. Inert arc gas is injected through the electric arc to ionize the gas and form a plasma gas stream. Powdered material is injected into the plasma gas stream. The method provides for coating a localized area of a compressor blade with the powdered material without masking the compressor blade.
In accordance with another aspect of the present disclosure, a method for repairing a gas turbine compressor blade using microplasma spray coating is provided. The compressor blade can be repaired with the microplasma spray coating in an operating field without utilizing a dedicated spray coating facility in a manufacturing environment. A hand controlled and operated microplasma gun is utilized for applying the coating. Inert arc gas is injected through an electric arc generated by the microplasma spray gun. The inert gas is ionized with the electric arc to form a plasma gas stream. Powdered material is injected into the plasma gas stream which coats a localized area of the compressor blade without masking portions of the compressor blade.
Other applications of the present invention will become apparent to those skilled in the art when the following description of the best mode contemplated for practicing the invention is read in conjunction with the accompanying drawings.
While the following disclosure is susceptible to various modifications and alternative constructions, certain illustrative embodiments thereof have been shown in the drawings and will be described below in detail. It should be understood, however, that there is no intention to limit the disclosure to the specific forms disclosed, but on the contrary, the intention is to cover all modifications, alternative constructions, and equivalents falling within the spirit and scope of the disclosure as defined by the appended claims.
Referring now to
While a number of different embodiments and structural variations can be constructed to practice such an invention, the following describes one currently known embodiment. Referring now to
In the depicted embodiment, the microplasma spray apparatus 10 includes the aforementioned microplasma gun 12 having an anode 16 and a cathode 18. The cathode 18 is further depicted to include an insulated body 26 with an electrode 28 extending therefrom. The cathode 18 can also include threads 30 for threadingly engaging the microplasma gun 12. The cathode 18 can also include an O-ring seal 32 to seal the leak path that is created at the interface between the cathode 18 and the microplasma gun 12.
In operation, an electric arc 20 (
A powdered material injector 22 injects powdered material 34 into the plasma gas stream 21. The powdered material 34 is heated and super plasticized in the plasma stream and is deposited on the compressor blade (not shown) where it cools and re-solidifies to form the coating. The powdered material injector 22 includes a powder hopper 36 for holding the powdered material 34. The hopper 36 is attached to the microplasma gun 12 via a connector 38 formed on the microplasma gun 12. The powder hopper 36 holds powdered material to be sprayed onto the compressor blade 72. The powdered material 34 is channeled through a discharge chute 40 and controlled by a valve 42 positioned in the discharge chute 40. The valve 42 can be mechanical or electromechanical as is known to those skilled in the art. Powder may also be injected into the plasma stream via a powder gas line from a standard powder feeder (not shown).
A nozzle shroud 46 positioned on a forward wall 48 of the microplasma gun 12 holds a nozzle insert 50 and permits the electrode 28 to extend through a center aperture 52 formed in the nozzle shroud 46. The nozzle insert 50 can be threadingly attached to an end of the nozzle shroud 46. A shield gas cap 54 is positioned adjacent the nozzle shroud 46. An insulator 56 is positioned between the shield gas cap 54 and the nozzle shroud 46 to electrically isolate the shield gas cap 54 from the nozzle shroud 46. The shield gas cap 54 can be pressed to fit onto the nozzle shroud 46 and over the insulator 56. The shield gas cap 54 includes a plurality of through apertures 58 for permitting shield gas to flow therethrough and shield the arc gas from ambient atmosphere. A center aperture 60 formed in the shield gas cap 54 permits high velocity arc gas to pass through and into the electric arc.
Cooling fluid, such as water or the like, is utilized to cool the microplasma gun 12. The cooling fluid is delivered to the microplasma gun 12 via a cooling fluid hose 62. The cooling fluid traverses through internal passages (not shown) in the microplasma gun 12 and flows through an inlet passage 64, into an anode holder 66 and back through an outlet passage 68. The cooling fluid reduces the temperature of the anode 16 during operation of the microplasma gun 12. The cooling flow rate may be approximately 1.0-1.5 gallons per minute. A second conduit 70 is connected to the microplasma gun 12. The second conduit may be operable for providing electrical power, arc gas, and shield gas to the microplasma gun 12.
Referring now to
The microplasma gun 12 can apply coating material in narrow strips of approximately 2 mm in width. This permits accurate surface coating even with a hand held device. The narrow strips of coating substantially eliminate the need for masking or otherwise covering the compressor blade 72 in areas where the coating is unwanted. The narrow spray pattern is controlled by the nozzle opening size. The hand held version of the microplasma gun 12 is so accurate that coating can be sprayed on components while they remain installed in an engine or the like.
The arc gas flow rate of the microplasma apparatus 10 may be between approximately 1.5 and 3 liters per minute. As stated above, the arc gas and shield gas are typically argon, but any suitable inert gas can be utilized as is known to those skilled in the art. The shield gas flow rate ranges between approximately 2 and 4 liters per minute for a typical application. The coating material for the compressor blade 72 can be a copper-nickel alloy, a copper-aluminum alloy, or other alloys suitable for compressor blades having operating temperatures that are typically below 1000° F., as is known to those skilled in the art.
The powder hopper 36 holds the powdered material 34 prior to being injected into the plasma gas stream 21 by the powder injector 22. The powdered material 34 can be injected into the plasma gas stream 21 either through gravity feed or through a pressurized system (not shown). The shut-off control valve 42 controls the powdered material 34 feed rate into the plasma gas stream 21. Powdered material 34 is transferred to the compressor blade 72 from between approximately 1 to 30 grams per minute. The microplasma gun 12 can typically apply the coating from distances ranging from approximately 1.5 inches to 6.5 inches to the compressor blade 72, but can vary depending on the coating application requirements. The microplasma spray gun 12 can be oriented between a positive 45° angle and a negative 45° angle relative to a normal axis of the compressor blade and still provide adequate material coating with a gravity feed system. A pressure feed system provides unlimited angles or orientation for the microplasma gun 12. The microplasma spray gun 12 generates a relatively low noise level that ranges from between 40 and 70 decibels due to the low power output, thereby making the apparatus 10 suitable for hand held application. Current U.S. government regulations require hearing protection when environmental noise reaches 85 decibels. The microplasma spray apparatus 10 can be hand held or alternatively held in an automated fixture (not shown) that is computer controlled.
Referring now to
While the preceding text sets forth a detailed description of certain embodiments of the invention, it should be understood that the legal scope of the invention is defined by the claims set forth at the end of this patent. The detailed description is to be construed as exemplary only and does not describe every possible embodiment of the invention since describing every possible embodiment would be impractical, if not impossible. Numerous alternative embodiments could be implemented, using either current technology or technology developed after the filing date of this patent, which would still fall within the scope of the claims defining the invention.
The instant application is a divisional application of U.S. Ser. No. 12/765,176, filed Apr. 22, 2010, entitled METHOD AND APPARATUS FOR MICROPLASMA SPRAY COATING A PORTION OF A COMPRESSOR BLADE IN A GAS TURBINE ENGINE, which is a divisional application of U.S. Ser. No. 10/976,561, filed Oct. 29, 2004, entitled METHOD AND APPARATUS FOR MICROPLASMA SPRAY COATING A PORTION OF A COMPRESSOR BLADE IN A GAS TURBINE ENGINE, now U.S. Pat. No. 7,763,823.
Number | Name | Date | Kind |
---|---|---|---|
4121083 | Smyth | Oct 1978 | A |
4256779 | Sokol et al. | Mar 1981 | A |
4282418 | Wuestner | Aug 1981 | A |
4472619 | Ueda et al. | Sep 1984 | A |
4851636 | Sugimoto et al. | Jul 1989 | A |
5173328 | Reiter et al. | Dec 1992 | A |
5233153 | Coats | Aug 1993 | A |
5271971 | Herb et al. | Dec 1993 | A |
5285967 | Weidman | Feb 1994 | A |
5311103 | Asmussen et al. | May 1994 | A |
5556560 | Ahola et al. | Sep 1996 | A |
5560844 | Boulos et al. | Oct 1996 | A |
5723078 | Nagaraj et al. | Mar 1998 | A |
6042880 | Rigney et al. | Mar 2000 | A |
6238540 | Timoshenko et al. | May 2001 | B1 |
6264817 | Timoshenko et al. | Jul 2001 | B1 |
6571472 | Berry et al. | Jun 2003 | B2 |
6703579 | Rice | Mar 2004 | B1 |
6744005 | Beyer et al. | Jun 2004 | B1 |
6744006 | Johnson et al. | Jun 2004 | B2 |
6914210 | Grossklaus, Jr. et al. | Jul 2005 | B2 |
7008522 | Boucard et al. | Mar 2006 | B2 |
7404860 | Vardelle et al. | Jul 2008 | B2 |
20040043160 | Fusaro et al. | Mar 2004 | A1 |
20040075396 | Okumura et al. | Apr 2004 | A1 |
20050015980 | Kottilingam et al. | Jan 2005 | A1 |
20050067065 | Fernihough et al. | Mar 2005 | A1 |
Number | Date | Country |
---|---|---|
60307531 | Apr 2007 | DE |
Entry |
---|
Internet site for Process Welding Systems, Inc.; under http://www.processwelding.com/torches—slights—3.php; “Plasma Welding Torches—Micro Plasma Torches”. |
Microplasma Spraying Brochure, E.O. Paton Electric Welding Institute of the NAS of Ukraine, 11, Bozhenko St., 03680, Kiev, Ukraine. |
Surface Modification Technologies III; New Capabilities in Plasma Weld Surfacing; Proceedings of the 3rd International Conference held in Neuchatel, Switzerland; Aug. 28-Sep. 1; Warrendale, PA; 15086; USA; The Minerals, Metals and Materials Society, 1990, pp. 777-792. |
Lidong Zhao et al.; Untersuchung zur Beschichtung mit NiCrBSI mittels des Mikroplasmaspritzverfahrens; Werkstofftechnisches Kolloguium, Chemnitz, Sep. 30, 2004; (siehe hierzu auch den Veranstaltungskalender der Technishchen Universitat Chemnitz unter www.tu-chemnitz.de); pp. 89-95. |
Sayers, G. et al.; Life Extension of Turbine Blading by Plasma Transferred Arc Surfacing in Steam Turbines in Power Generation; the 1988 ASME Joint Power Generation Conference, Philadelphia, PA USA; 25-29.9.1988Bd. PWR-3, Sep. 1988; p. 87-90. |
Plasma Power Feed Welding; (Products) in Welding Design and Fabrication, Jul. 2003, p. 52. |
Plasma Ar Welding Torches; (Products/Literature) in Welding Design and Fabrication, Jul. 2003, p. 60. |
Yushchenko, K. et al.; Microplasma Spraying, Proceedings of the 15th International Thermal Spray Conference, May 25-29, 1995; Nice France; E.O. Paton Electric Welding Institute, Kiev, 25260, Ukraine, pp. 273-274. |
Grunendick, T.; Schweiben in der Luftfahrtindustrie; in IMW-Institutmitteilung Nr 22 (1997); pp. 25-30. |
Yushchenko, K. et al.; Microplasma Spraying, Proceedings of the 15th International Thermal Spray Conference, May 25-29, 1995; Nice, France; E.O. Paton Electric Welding Institute, Kiev, 25260, Ukraine, pp. 1461-1467. |
Number | Date | Country | |
---|---|---|---|
20130068729 A1 | Mar 2013 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 12765176 | Apr 2010 | US |
Child | 13664562 | US | |
Parent | 10976561 | Oct 2004 | US |
Child | 12765176 | US |