The invention relates to the production of organic devices in general and is more particularly related to the patterning of conductive layers used in such organic devices like e.g. organic light emitting devices (OLEDs), organic field effect transistors (OFETs) or organic photocells.
1. Background of the Invention
The rapid development of organic device technology increases the need for fast and cheap but reliable methods for the deposition of the desired layers as well as for the patterning of the layers, especially of the conductive layers. Methods for production of large areas are needed. Roll-to-roll processes with polymeric substrates are a promising approach. Due to the low stability of the organic semi-conducting and conducting materials against oxygen and water for most applications good barrier properties of the substrate are needed. Therefore often barrier coatings are deposited on polymeric substrates prior to the deposition of the layers of the organic devices. To keep these barrier properties the patterning process must be carried out in an adequate manner. Especially permanent deformation of the substrate has to be avoided. Up to now there is a lack of patterning methods which address all the points mentioned above.
2. State of the Art
For the patterning of layers or layer stacks in organic devices several techniques are available. Etching of metal or transparent conductive oxide layers is one of them. First of all a protective layer, a so-called resist, is deposited on the layer to be patterned. The desired pattern is then created in the resist layer e.g. by photolithography followed by a development step. The pattern can be transferred in the layer that is to be patterned by a wet or dry etching step which removes the unprotected areas. After the etching step the residual resist must be removed. The big advantage of this technique is the high resolution of the process (down to 65 nm). On the other hand the multiple steps of the process make it very slow and costly. Further the etching chemistry or the plasma of the dry etching process is critical for many organic materials as well as for polymeric substrates and the barrier coatings on top of them. Thus this technique is not well suitable for roll-to-roll production.
Printing processes are capable of producing patterned polymeric layers. Even conducting polymers like PEDOT:PSS can be printed with high speed in roll-to-roll processes e.g. by gravure printing. Mixtures containing conducting particles like indium tin oxide (ITO) or metal nanoparticles are likewise possible. The drawback of the printing approach is the limitation of the resolution of the printing processes. Especially patterned layers of about 100 nm with a well defined thickness at the edges of the pattern are difficult to realise. Further the conductivity of printed conducting layers is still much lower compared to vacuum deposited ones.
Yet another method for patterning of layers is based on laser irradiation. By choosing the appropriate wavelength and power metal or transparent conductive oxide (TCO) layers can be partially removed from a substrate. Due to the heat that is introduced in the layer or layer stack and/or the substrate the method alters or damages the layers or the substrate. Furthermore the technique is up to now not fast enough to be implemented in a roll-to-roll process and the investment and thus the costs are rather high.
Patterned deposition by shadow masks is a fast and economic technique. It can be used in vacuum deposition techniques such as evaporation or sputtering even in a roll-to-roll coater. The drawback of this technique is the limited resolution of larger than 200 μm.
Methods for patterning of layers based on die-cutting and the like are described in the following applications.
The patent application WO 01/60589 A1 describes a method for microstructuring polymer-supported material, suitable for use, for instance, as light polarizers, transflectors, microelectrode arrays, or liquid-crystal alignment layers. Layers of the material are microstructured by pressing a master with desired features into the polymer support. The depth of the features of the master generally exceeds the thickness of the layer or layers and the master is sufficiently hard and capable of cutting through the layers into the polymer substrate. The method is well suited for the mentioned applications but is inapplicable for patterning of conductive layers used in organic devices due to the deformation of the substrate.
In the patent application US2005/0071969 A1 a method for solid state embossing of polymer devices is described. It comprises depositing layers of conducting, semiconducting and/or insulating polymer by solution processing and direct printing and embossing microgrooves in the multilayer structure. This patent application focuses on embossing of complex organic multilayer devices such as vertical polymer thin-film transistors (TFT). The described method does not solve the problem of damaging the substrate by cutting through the layer or layers. Further no solution is provided for the problem of damaging the substrate and/or the deposited conductive layer due to the material flow during the embossing step.
The patent application US2002/0094594 A1 discloses a method for patterning organic thin film devices using a die. It comprises coating a substrate with a first organic layer, followed by an electrode layer. Then a patterning die is pressed onto the electrode layer. This die is prepared such that the portions of the electrode layer which are in contact with the die stick to the die and thus are removed together with the die. A drawback of this patent application is that before the die can be reused it must be cleaned in an additional step. This slows down the speed of the process and increases the costs. For roll-to-roll applications this additional cleaning step is critical. Further the first organic layer must possess a weaker adhesion to the electrode layer than between the die and the electrode layer. This release function lowers the stability of the layer setup distinctly and limits the possible material combinations.
In the patent application WO2004/111729 A1 a method and an apparatus for manufacturing electronic thin-film components is described. It comprises the following steps. A conductive layer is formed directly on a dielectric substrate. Galvanically separated conductive areas are formed by exerting on the conductive layer a machining operation based on die-cutting, wherein the relief of the machining member causes a permanent deformation on the substrate. On top of this patterned electrode layer it is then possible to form a desired electronic thin-film component by depositing the required layers. Due to the permanent deformation of the substrate critical stress is induced in the conductive layer during the patterning process. Further the barrier properties of the substrate will be degraded.
A method for structuring layers of organic circuits by pressing an embossing tool at a defined temperature and with a defined pressure in an organic layer is disclosed in the patent application WO2005/006462. The structuring is performed in such a way that the organic layer keeps the structuring permanently. The main goal of this patent application is to provide a time-efficient method to structure an isolating organic layer between conducting or semi-conducting organic layers to get an interlayer connection.
An object of the present invention is to eliminate at least some of the drawbacks of the state of the art.
The invention provides a method of patterning layers of organic devices. It also provides organic devices with layers patterned according to the method as defined in the appended independent claims. Preferred, advantageous or alternative features of the invention are set out in dependent claims.
In a first aspect the present invention provides a method of patterning a conductive layer or a layer stack comprising at least one conductive layer in which between the layer or layer stack and the substrate there is a compressible spacer layer or a spacer layer stack comprising at least one compressible layer.
In a second aspect the invention provides organic devices with at least one conductive layer which is patterned according to the claimed method.
Organic devices such as organic light emitting devices (OLEDs), organic field effect transistors (OFETs) or organic photocells, possess one or more conductive layers in the layer setup. E.g. the simplest layer setup of an OLED is a three layer setup with a transparent anode layer, the light emitting layer and a cathode layer. To obtain the desired function of the devices the conductive layers need to be patterned in an appropriate manner. The central point of this invention is to pattern the conductive layer or layers by embossing, whereas between the substrate and the first conductive layer there is a compressible spacer layer or a spacer layer stack with at least one such compressible layer. The thickness of the compressible layer shrinks at the embossed areas due to the pressure applied by the embossing tool (see
Suitable substrates (1) for the organic devices are glass, polymer, especially polymeric foil, paper or metal. Flexible substrates are well suited for roll-to-roll processes. The substrate can be for example a flexible polymer foil like acrylonitrile butadiene styrene ABS, polycarbonate PC, polyethylene PE, polyetherimide PEI, polyetherketone PEK, poly(ethylene naphthalate) PEN, poly(ethylene therephtalate) PET, polyimide PI, poly(methyl methacrylate) PMMA, poly-oxy-methylene POM, mono oriented polypropylene MOPP, polystyrene PS, polyvinyl chloride PVC and the like. Other materials like paper (weight per area 20-500 g/m2, preferably 40-200 g/m2), metal foil, (for example Al-, Au-, Cu-, Fe-, Ni-, Sn-, steel-foil etc.), especially surface modified, coated with a lacquer or polymer, are suitable too. The substrate can be coated with a barrier layer (4) or a barrier layer stack (5) to increase the barrier properties (J. Lange and Y. Wyser, “Recent Innovations in Barrier Technologies for Plastic Packaging—a Review”, Packag. Technol. and Sci. 16, 2003, p. 149-158). E.g. inorganic materials like SiO2, Si3N4, SiOxNy, Al2O3, AlOxNy and the like are often used. They can be deposited e.g. in vacuum processes like evaporation, sputtering or chemical vapour deposition CVD, especially plasma enhanced CVD (PECVD). Other suitable materials are mixtures of organic and inorganic materials deposited in a sol-gel process. Such materials can even be deposited in a wet coating process like e.g. gravure printing. The best barrier properties at present are obtained by multilayer coatings of organic and inorganic materials as described in WO03/094256A2. In the following the term substrate shall denote substrates with and without barrier coatings.
Suitable materials for the compressible layer (2) are low density polymer like e.g. low density poly ethylene (LDPE) with a density of about 0.92 g/cc. Most isolating and conducting polymers possess densities >1.0 g/cc. E.g. Poly(methyl methacrylate) PMMA has a density of 1.19 g/cc, poly(styrene) PS of 1.05 g/cc, poly(carbonate) PC of 1.2 g/cc and poly(ethylene terephthalate) PET of 1.3-1.4 g/cc. The density of metals and TCOs is even distinctly higher. E.g. Aluminum (Al) has a density of 2.7 g/cc, Copper (Cu) of 8.96 g/cc, Silver (Ag) of 10.5 g/cc or Gold (Au) of 19.3 g/cc and tin doped indium oxide (ITO) of 7.14 g/cc. Thus the low density polymer possesses the lowest density of all materials in the organic device. Upon embossing such a compressible spacer layer is compressed leading to an increase in the density combined with a decrease in the layer thickness. A much better compressibility for the spacer layer is obtained by the use of meso- or nano-porous materials. E.g. sol-gel processed silica aerogel as described by Tsutsui et. al. (“Doubling Coupling-Out Efficiency in Organic Light-Emitting Devices Using a Thin Silica Aerogel Layer”, Adv. Mater. 13, 2001, p. 1149-2252) possess an index of refraction as low as 1.03 which is only possible if the majority of the volume of the layer is air or gas. This air or gas filled volume takes up the material upon embossing. Such porous layers can be produced by other techniques too. Inorganic oxides, e.g. silica or boehmite, in a mixture with a binder, like e.g. poly(vinyl alcohol) PVA or poly(vinylpyrrolidone) PVP, are capable of forming layer of high porosity and thus low density as described in the US2005/0003179 A1, EP1464511 A2 and the EP0614771 A1. In the mentioned documents the porous layer functions as an ink absorbing layer. As the conducting layer or the layer stack comprising at least one conducting layer is coated on top of the spacer layer (stack) a flat surface is advantageous. In most cases the porosity of the compressible meso- or nano-porous layer leads to a rough surface. To solve this problem a thin homogeneous and flat layer can be coated on top of the porous layer prior to the conducting layer or layer stack. This homogeneous layer can be made of inorganic dielectrics like SiO2, Al2O3 and the like or of polymer like but not limited to PMMA, PS or PVA. Suitable and preferred thickness ranges for the layers in the spacer layer stack is:
A further advantage of the porous layer is that due to the holes in the layer (similar to a sponge) residues of the embossed conducting layer can not stick well to the vertical walls. Thus shorts between the embossed and the not embossed parts of the conducting layers are less probable.
The conductive layers (3) are often made of metal like e.g. Al, Cu, Ag or Au. The metal layers can be semitransparent (depending on the metal with a thickness of a few tenth of nanometers up to 50 nm) or opaque (thickness of >50 nm). Other suitable materials are transparent conductive oxides (TCO) like e.g. ITO, aluminium doped zinc oxide (AZO) or gallium doped zinc oxide (GZO). Typical thickness of such a TCO layer is in the range of 50 nm up to 150 nm. Due to a distinct increase of the stress in inorganic layers above a thickness of roughly 200 nm (depending on deposition method and parameter) typical values of the conducting layers are below that threshold. Organic conducting layers are e.g. made of polymers like Poly(styrene sulfonate) doped Poly(3,4-ethylenedioxythiophene) PEDOT/PSS, Poly(aniline) PANI or Polypyrrole. The conducting polymer layers possess the same typical thickness range as the TCO layers. Also a combination of above mentioned layers may serve as conductive layer, e.g. an ITO layer coated with a polymer where the latter acts as injection layer as well as buffer layer to avoid cracking of the ITO or at least for binding ITO particles during the embossing process.
The embossing tool (10) must be made of a material which is harder than the layers to be embossed. E.g. so called nickel shims are suitable. They are state of the art and widely used in the hologram manufacturing industry as well as in the CD/DVD production. If needed the structure size to be embossed can be down to a few tenth of nanometer. Such shims can be flat to emboss sheets or plane objects.
On the other hand they can be put around a roll for roll-to-roll embossing of flexible objects like polymeric foil or paper. To get the desired pattern in a nickel shim first of all this pattern is made in a master substrate by photolithography, e-beam lithography or another suitable technique. One possibility is to coat a flat glass substrate with a light sensitive polymer (a so called resist) of a certain thickness and illuminate it through a mask, e.g. a chromium mask, which possesses the pattern. Depending on the type of resist the illuminated pattern (positive resist) or the protected area (negative resist) can be removed in a development step. The thickness of the resist defines the height or depth of the pattern. By coating this patterned glass substrate with a conducting material, e.g. evaporated Nickel, Silver or Gold or sprayed Silver solution, a starting layer for the electroforming of the Nickel shim is deposited. After the electroforming step a first generation Nickel shim is obtained from which second and further generation shims can be made by additional electroforming steps. Another possible material for the embossing tool is hardened steel. The pattern can be transferred in this material class by diamond turning or other tooling techniques if the desired pattern is suitable for these techniques. Wet etching or dry etching techniques can be used likewise as described in the US2004/0032667 A1 which is incorporated herein by reference. The etching techniques are well suited for very small patterns, e.g. even subwavelength gratings are possible.
For organic devices the size of the pattern in the conducting layer varies at present from 5 μm×15 μm (matrix displays) up to a few cm2 or more (logos). The width of the separator between adjacent pixels should be as small as possible. In current matrix displays it is about 3 μm.
In one embodiment of the described invention the width of the separators is defined by the width of the embossed pattern. If the embossed parts of the conducting layer are used in the device too, the separator is defined by the width of the embossed edge. This width of the edges depends on the height of the pattern as the walls of the pattern in the embossing tool are not perfectly vertical. Values of <20 μm are easily obtainable. In one embodiment of the invention the depth or height of the pattern hpatt in the embossing tool is smaller than the thickness dcomp of the compressible layer. Suitable values for hpatt are <25 μm, preferred values are <9 μm.
The deposition of the compressible spacer layer or spacer layer stack can be done by several coating techniques. Low density polymers can be wet coated for example by spin-coating, by printing, especially flexo-printing, gravure printing, ink-jet-printing or screen-printing, by curtain or dip coating or by spraying. Porous spacer layer can be wet or vacuum coated. E.g. CVD processes are capable of forming porous silica layer if appropriate coating parameters are chosen. Other approaches use spin-, curtain- or cascade coating to deposit the porous layer. The latter two techniques are roll-to-roll processes and thus capable for large area production. Examples for the deposition of porous layers of inorganic oxides like silica and boehmite are described in EP1464511 A2 and EP0614771 A1.
The optional flat top layer can be deposited by several techniques. Top layers of inorganic materials like SiO2 can be vacuum deposited by e.g. evaporation, sputtering or CVD. Sol-gel processes are likewise possible (M. Mennig et. al. “Interference multilayer systems on plastic foil by a wet-web-coating technique”, Proceedings of the 5th International Conference on Coatings on Glass, p. 175). Organic top layers can be vacuum (PECVD) or wet coated. Again spin-coating, printing, especially flexo-printing, gravure printing, ink-jet-printing or screen-printing, curtain or dip coating or spraying are possible. In a preferred embodiment of the invention the flat organic top layer is coated on top of the porous spacer layer in the same process. This can be done e.g. by curtain- or cascade coating as described for example in the WO03/053597 A1. These processes are capable of coating more than ten layers of a multilayer stack in one step.
The conducting layer can be likewise deposited in wet- or vacuum processes. Metal layers are often evaporated or sputtered in large areas. E.g. for security holograms or packaging applications roll-to-roll vacuum coaters with a web speed of more than 10 m/sec are state of the art (see e.g. http://www.galileovacuum.com). TCOs are mostly sputter deposited, but evaporation is possible too, if the required conductivity is not too high. First attempts are made to coat TCO layers by wet coating techniques. E.g. a spin-coating process for the deposition of ITO is described by Al-Dahoudi and Aegerter (“Comparative study of transparent conductive In2O3:Sn (ITO) coatings made using a sol and a nanoparticle suspension” Proceedings of the 5th International Conference on Coatings on Glass, p 585-592). Such TCO sol-gel or nanoparticle materials can be used in roll-to-roll coating techniques too. E.g. printing, especially gravure printing is a suitable method. Organic conducting layer can be deposited by several wet coatings techniques, like but not restricted to, spin-coating, printing, especially flexo-printing, gravure printing, ink-jet-printing or screen-printing, curtain or dip coating or spraying.
The embossing of the coated layers can be done in step by step machines or in roll-to-roll embossing machines. The former can be e.g. an EVG520HE semi-automated hot embossing system. It accepts substrates up to 200 mm. The stamps used can possess pattern sizes ranging from 400 nm to 100 μm (Nils Roos et. al., “Impact of vacuum environment on the hot embossing process”, SPIE's Microlithography 2003, Santa Clara, Calif., Feb. 22-28, 2003). One example of a roll-to-roll embossing machine is described on page 34 in the research activities in optoelectronics and electronics manufacturing report 2004 of VTT Electronics Finland (www.vtt.fi). This machine is capable of doing web gravure printing and web embossing in serial units. In general the applied pressure has to be adapted to the materials used in the layer stack, the web speed and the embossing temperature as well as the size and depth of the pattern to be embossed. The embossing can be done at room temperature or at elevated temperature (hot embossing). E.g. if a hard conducting material like ITO on top of a compressible porous spacer layer with an organic flat top layer needs to be patterned the stress in the conducting layer can be minimised by doing the embossing at a temperature above the glass transition temperature of the organic flat top layer.
After the embossing post treatments can be applied if necessary. E.g. plasma processes like oxygen plasma or argon plasma can be applied to remove residues of layers. Other post treatment possibilities are wet etching. E.g. an ITO etch solution (481 ml/l hydrochloric acid (32%), 38 ml/l nitric acid (65%) and 481 ml/l deionised water) can be used to remove ITO residues at the edges of the embossed areas to avoid possible shorts between the separated conducting areas. If an appropriate diluted concentration is chosen the needed conducting ITO areas are kept intact. A subsequent coating step of a polymer layer e.g. PEDOT/PSS could cover and repair possible cracks in the ITO layer.
The ability to do all deposition, patterning and (if necessary) post treatment steps in roll-to-roll processes enables the large area production of patterned conducting layers for organic devices at low costs.
The following examples illustrate the invention. The invention is not limited to these examples.
A 100 nm thick ITO anode is patterned on a compressible spacer layer stack analogously as explained in the description of
Source and drain electrodes consisting of 50 nm sputter deposited Au on top of a compressible layer stack are patterned analogously to the method in the description of
The same bottom ITO electrode pattern and method as described for fabricating OLEDs (see
Number | Date | Country | Kind |
---|---|---|---|
0523163.4 | Nov 2005 | GB | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/IB2006/003995 | 11/14/2006 | WO | 00 | 5/8/2008 |