The present inventive concept relates to a method of producing an elastic profile with longitudinally recurring transverse protrusions and an apparatus for manufacturing the same.
Elastic profiles are useful, for example, for joining and/or sealing between structures. They can be made from materials such as thermoplastic elastomers (TPEs), natural rubber, or synthetic rubbers such as EPDM. Such structures may be manufactured through extrusion through an extrusion die.
Geometrically, in a strict sense, a profile is three-dimensional object generated by sweeping a two-dimensional outline, corresponding to the extrusion die, in a third longitudinal dimension. Thus, it has a constant cross-section as one moves along the longitudinal direction.
However, in various applications, it is useful to have transverse protrusions that extend from the profile proper and that may vary in the longitudinal direction. Various methods for fabricating such profiles with “three-dimensional” structures are known in the prior art.
EP0203906A2 discloses, in the context of making a laminate, a process comprising providing at least one rotating drum having in the peripheral surface thereof a plurality of cavities, extruding onto the peripheral surface of said drum a molten thermoplastic material under sufficient pressure to cause the molten thermoplastic material to enter said cavities, to form a three-dimensional layer having a plurality of elongated projections extending from a backing having an exposed surface; and then, while said three-dimensional layer remains on said drum, applying a near molten extruded sheet subsubstrate layer of thermoplastic material onto the exposed surface of said three-dimensional layer, at least one of said layers being at temperatures sufficient to cause said layers to fusion bond to each other.
There is always a need to improve such manufacturing methods and apparatuses.
To this end, according to a first method aspect, there is provided a method of producing an elastic profile with longitudinally recurring transverse protrusions, comprising extruding a primary profile at a primary extruder; extruding a secondary profile at a secondary extruder, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotating molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; joining the primary profile and the substrate layer of the secondary profile through fusion bonding at a joining point, forming a composite structure; and pressing on the composite structure with a rotating pressing wheel, against a bedding separate from the molding wheel.
Pressing on the composite structure using a pressing wheel against a bedding separate from the molding wheel allows the pressing wheel to be specifically adapted to press the substrate layer of the secondary profile onto the primary profile without damaging the transverse protrusions. For example, the pressing wheel may have one or more recesses. The recesses may be shaped so that the pressing wheel only touches the substrate layer and not the transverse protrusions. This way, the pressing wheel may press harder on the composite structure than otherwise would be possible without damaging the transverse protrusions, leading to a better bond between the substrate of the secondary profile and the primary profile. For example, the pressing wheel may have recesses slightly wider and deeper than those of the molding wheel.
Rotation of the pressing wheel may be synchronized with rotation of the molding wheel to match up recesses of the pressing wheel with those of the molding wheel.
The primary profile and/or the secondary profile may at least partly comprise natural rubber or a synthetic rubber, such as EPDM. Alternatively, or additionally, the primary profile and/or the secondary profile at least partly comprises a thermoplastic elastomer (TPE).
The molding wheel may be internally water cooled, which allows for good control of the temperature of the wheel.
The joining point may be at the perimeter of the molding wheel and may be a nip, which may be formed between the molding wheel and a preferably flat bedding, wherein the bedding preferably is stationary. Such a nip allows for firm pressing on the composite structure already at the joining point, allowing to a good bonding between the substrate of the secondary profile and the primary profile in a relatively simple apparatus.
Further, according to a first apparatus aspect, there is provided an apparatus for producing an elastic profile with longitudinally recurring transverse protrusions, comprising a primary extruder arranged for extruding a primary profile, a secondary extruder arranged for extruding a secondary profile, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotatable molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; a joining point for joining the primary profile and the secondary profile through fusion bonding, forming a composite structure; and a rotatable pressing wheel arranged for pressing on the composite structure against a bedding separate from the molding wheel.
The pressing wheel may have one or more recesses providing clearance compared to the corresponding recesses of the molding wheel, i.e., if the corresponding recess of the molding wheel would be imagined to be transported to and compared with the recess of the pressing wheel, the surface of the recess of the molding wheel would be entirely contained within the surface of the recess of the pressing wheel, with the two aligned relative to how they each would align relative the same transverse projection of the composite structure.
Effects and features of this first apparatus aspect are analogous to those described above in connection with the first method aspect. Embodiments mentioned in relation to the first method aspect are compatible with the first apparatus aspect.
Further, according to a second method aspect, there is provided a method of producing an elastic profile with longitudinally recurring transverse protrusions, comprising extruding a primary profile at a primary extruder; extruding a secondary profile at a secondary extruder, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotating molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; joining the primary profile and the substrate layer of the secondary profile through fusion bonding, forming a composite structure, the joining occurring at a joining point, the entire path along which the primary profile travels from the primary extruder to the joining point being straight.
An arrangement where the primary profile travels along an entirely straight path from the primary extruder to the joining point allows for the extruder to be placed closer to the joining point. This results in less heat being lost on the way, which in turn allows for better temperature control of the fusion bonding process, as no re-heating is required. Further, energy is saved.
For example, the output of the primary extruder may be placed within 20 cm or more preferably within 15 cm of the joining point.
The joining point may be at the perimeter of the molding wheel and may be a nip, which may be formed between the molding wheel and a preferably flat bedding, wherein the bedding preferably is stationary. Such a nip allows for firm pressing on the composite structure at the joining point, allowing to a good bond between the substrate of the secondary profile and the primary profile in a relatively simple apparatus.
The primary profile and/or the secondary profile may at least partly comprise natural rubber or a synthetic rubber, such as EPDM. Alternatively, or additionally, the primary profile and/or the secondary profile at least partly comprises a thermoplastic elastomer (TPE).
The molding wheel may be internally water cooled, which allows for good control of the temperature of the wheel.
Further, according to a second apparatus aspect, there is provided an apparatus for producing an elastic profile with longitudinally recurring transverse protrusions, comprising a primary extruder arranged for extruding a primary profile, a secondary extruder arranged for extruding a secondary profile, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotatable molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; and a joining point at the molding wheel for joining the primary profile and the secondary profile through fusion bonding, forming a composite structure, the primary extruder and the joining point being arranged so that the entire path along which the primary profile, during operation of the apparatus, travels between the primary extruder and the joining point is straight.
Effects and features of this second apparatus aspect are analogous to those described above in connection with the second method aspect. Embodiments mentioned in relation to the second method aspect are compatible with the second apparatus aspect.
Further, according to a third method aspect, there is provided a method of producing an elastic profile with longitudinally recurring transverse protrusions, comprising extruding a primary profile at a primary extruder; extruding a secondary profile at a secondary extruder, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotating molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; joining the primary profile and the substrate layer of the secondary profile through fusion bonding, forming a composite structure, the joining occurring at a nip formed between the molding wheel and a flat bedding.
Such a nip allows for firm pressing on the composite structure at the joining point, allowing to a good bond between the substrate of the secondary profile and the primary profile in a relatively simple apparatus.
The bedding may be stationary.
The primary profile and/or the secondary profile may at least partly comprise natural rubber or a synthetic rubber, such as EPDM. Alternatively, or additionally, the primary profile and/or the secondary profile at least partly comprises a thermoplastic elastomer (TPE).
The molding wheel may be internally water cooled, which allows for good control of the temperature of the wheel.
Further, according to a third apparatus aspect, there is provided an apparatus for producing an elastic profile with longitudinally recurring transverse protrusions, comprising: a primary extruder arranged for extruding a primary profile, a secondary extruder arranged for extruding a secondary profile, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotatable molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; and a nip formed between the molding wheel and a flat bedding for joining the primary profile and the secondary profile through fusion bonding, forming a composite structure.
Effects and features of this third apparatus aspect are analogous to those described above in connection with the third method aspect. Embodiments mentioned in relation to the third method aspect are compatible with the third apparatus aspect.
The above, as well as additional objects, features and advantages of the present inventive concept, will be better understood through the following illustrative and non-limiting detailed description of preferred embodiments, with reference to the appended drawings, where the same reference numerals will be used for similar elements, wherein:
The secondary profile 20 travels along the perimeter of the molding wheel 12 to a nip 16 between the molding wheel 12 and a bedding 18. The nip 16 functions as a joining point of the primary profile 6, which has traveled along a straight path between the primary extruder 4 and the nip 16, and the secondary profile 20, forming a composite structure 22. The outlet of the primary extruder 4 is placed close to the nip 16, preferably at a distance within 20 cm, for example at a distance of 15 cm. Downstream of the molding wheel 12, there is a second, pressing wheel 24 arranged for pressing on the composite structure.
As is evident from
Downstream of the pressing wheel 24, there is a sizing arrangement 28 with a profile 30 matching the outer profile of the composite structure 22. Finally, further again downstream, water is sprayed by nozzles 32 for cooling the composite structure 22.
The molding wheel 12 has recesses 46 serving as molds for the protrusions 48 within the chamber 10 (cf.
Within the chamber 10, the recesses 46 of the molding wheel 12 serve as molds for the protrusions 48 of the secondary profile 20. Further, the secondary profile 20 will have a substrate layer formed by the space in the chamber 10 outside the molding wheel 12 and its recesses 46, ultimately being shaped by the gap 14 between the molding wheel 12 and the opposite wall of the chamber 10 at the lower end of the chamber 10. With the molding wheel 12 rotating, the secondary profile 20 is transported along the outer periphery of the molding wheel 12 to the nip 16, where the substrate layer of the secondary profile 20 meets the primary profile 6, for joining the two through fusion bonding. In the nip 16, the molding wheel 12 presses on the secondary profile 20 and the primary profile 6 against a flat, stationary bedding 18.
The resulting composite structure 22 then travels on to a second nip 26 between the pressing wheel 24 and the bedding 18, where the pressing wheel 24 presses on the composite structure 22. Thus, the pressing wheel 24, which is separate and distinct from the molding wheel 12, presses on the composite structure 22 against the bedding 18, which is separate and distinct from the molding wheel 12.
The recesses 44 of the pressing wheel 24 are larger, i.e., slightly wider and deeper than the corresponding recesses 46 of the molding wheel, so that the pressing wheel only touches the substrate layer of the secondary profile 20 and not the protrusions 48.
Summing up, with reference to
The composite structure 22 may be pressed on at the nip 26 with a rotating pressing wheel 24 separate from the molding wheel 20. The pressing wheel 24 may have one or more recesses 44 shaped so that the pressing wheel 24 only touches the substrate layer and not the transverse protrusions 48, in other words the recesses 44 providing clearance compared to the corresponding recesses 46 of said molding wheel 12.
The primary profile 6 travels along a straight path from the primary extruder 4 to the joining point in form of the nip 16.
In the above the inventive concept has mainly been described with reference to a limited number of examples. However, as is readily appreciated by a person skilled in the art, other examples than the ones disclosed above are equally possible within the scope of the inventive concept, as defined by the appended claims. For example, the joining of the primary profile 6 and the secondary profile 20 may happen between the molding wheel 12 and a second wheel or roll instead of against the bedding 18. The bedding 18 may be moving with the primary profile 6 and the composite structure 22 instead of being stationary. The transverse protrusions 48 and corresponding recesses 46 of the molding wheel 12 and the recesses 44 of the pressing wheel 24 are shown as being crescent shaped for illustration, however, this can be adjusted to any desires shape according to need. The molding wheel 12 and the pressing wheel 24 may be driven by any suitable driving mechanism or mechanisms, which may be different from the one described above in conjunction with
The following summarizes examples.
According to a first method aspect, there is provided a method of producing an elastic profile with longitudinally recurring transverse protrusions, comprising extruding a primary profile at a primary extruder; extruding a secondary profile at a secondary extruder, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotating molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; joining the primary profile and the substrate layer of the secondary profile through fusion bonding at a joining point, forming a composite structure; and pressing on the composite structure with a rotating pressing wheel, separate from the molding wheel.
Using a pressing wheel separate from the molding wheel allows the pressing wheel to be specifically adapted to press the substrate layer of the secondary profile onto the primary profile without damaging the transverse protrusions. For example, the pressing wheel may have one or more recesses. The recesses may be shaped so that the pressing wheel only touches the substrate layer and not the transverse protrusions. This way, the pressing wheel may press harder on the composite structure than otherwise would be possible without damaging the transverse protrusions, leading to a better bond between the substrate of the secondary profile and the primary profile. For example, the pressing wheel may have recesses slightly wider and deeper than those of the molding wheel.
Rotation of the pressing wheel may be synchronized with rotation of the molding wheel to match up recesses of the pressing wheel with those of the molding wheel.
The primary profile and/or the secondary profile may at least partly comprise natural rubber or a synthetic rubber, such as EPDM. Alternatively, or additionally, the primary profile and/or the secondary profile at least partly comprises a thermoplastic elastomer (TPE).
The molding wheel may be internally water cooled, which allows for good control of the temperature of the wheel.
The joining point may be at the perimeter of the molding wheel and may be a nip, which may be formed between the molding wheel and a preferably flat bedding, wherein the bedding preferably is stationary. Such a nip allows for firm pressing on the composite structure already at the joining point, allowing to a good bonding between the substrate of the secondary profile and the primary profile in a relatively simple apparatus.
Further, according to a first apparatus aspect, there is provided an apparatus for producing an elastic profile with longitudinally recurring transverse protrusions, comprising a primary extruder arranged for extruding a primary profile, a secondary extruder arranged for extruding a secondary profile, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotatable molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; a joining point for joining the primary profile and the secondary profile through fusion bonding, forming a composite structure; and a rotatable pressing wheel arranged for pressing on the composite structure, the pressing wheel being separate from the molding wheel.
The pressing wheel may have one or more recesses providing clearance compared to the corresponding recesses of the molding wheel, i.e., if the corresponding recess of the molding wheel would be imagined to be transported to and compared with the recess of the pressing wheel, the surface of the recess of the molding wheel would be entirely contained within the surface of the recess of the pressing wheel, with the two aligned relative to how they each would align relative the same transverse projection of the composite structure.
Effects and features of this first apparatus aspect are analogous to those described above in connection with the first method aspect. Embodiments mentioned in relation to the first method aspect are compatible with the first apparatus aspect.
Further, according to a second method aspect, there is provided a method of producing an elastic profile with longitudinally recurring transverse protrusions, comprising extruding a primary profile at a primary extruder; extruding a secondary profile at a secondary extruder, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotating molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; joining the primary profile and the substrate layer of the secondary profile through fusion bonding, forming a composite structure, the joining occurring at a joining point, the primary profile traveling along a straight path from the primary extruder to the joining point.
An arrangement where the primary profile travels along a straight path from the primary extruder to the joining point allows for the extruder to be placed closer to the joining point. This results in less heat being lost on the way, which in turn allows for better temperature control of the fusion bonding process, as no re-heating is required. Further, energy is saved.
For example, the output of the primary extruder may be placed within 20 cm or more preferably within 15 cm of the joining point.
The joining point may be at the perimeter of the molding wheel and may be a nip, which may be formed between the molding wheel and a preferably flat bedding, wherein the bedding preferably is stationary. Such a nip allows for firm pressing on the composite structure at the joining point, allowing to a good bond between the substrate of the secondary profile and the primary profile in a relatively simple apparatus.
The primary profile and/or the secondary profile may at least partly comprise natural rubber or a synthetic rubber, such as EPDM. Alternatively, or additionally, the primary profile and/or the secondary profile at least partly comprises a thermoplastic elastomer (TPE).
The molding wheel may be internally water cooled, which allows for good control of the temperature of the wheel.
Further, according to a second apparatus aspect, there is provided an apparatus for producing an elastic profile with longitudinally recurring transverse protrusions, comprising a primary extruder arranged for extruding a primary profile, a secondary extruder arranged for extruding a secondary profile, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotatable molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; and a joining point at the molding wheel for joining the primary profile and the secondary profile through fusion bonding, forming a composite structure, the primary extruder and the joining point being arranged so that the primary profile, during operation of the apparatus, travels along a straight path between the primary extruder and the joining point.
Effects and features of this second apparatus aspect are analogous to those described above in connection with the second method aspect. Embodiments mentioned in relation to the second method aspect are compatible with the second apparatus aspect.
Further, according to a third method aspect, there is provided a method of producing an elastic profile with longitudinally recurring transverse protrusions, comprising extruding a primary profile at a primary extruder; extruding a secondary profile at a secondary extruder, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotating molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; joining the primary profile and the substrate layer of the secondary profile through fusion bonding, forming a composite structure, the joining occurring at a nip formed between the molding wheel and a preferably flat bedding, wherein the bedding preferably is stationary.
Such a nip allows for firm pressing on the composite structure at the joining point, allowing to a good bond between the substrate of the secondary profile and the primary profile in a relatively simple apparatus.
The primary profile and/or the secondary profile may at least partly comprise natural rubber or a synthetic rubber, such as EPDM. Alternatively, or additionally, the primary profile and/or the secondary profile at least partly comprises a thermoplastic elastomer (TPE).
The molding wheel may be internally water cooled, which allows for good control of the temperature of the wheel.
Further, according to a third apparatus aspect, there is provided an apparatus for producing an elastic profile with longitudinally recurring transverse protrusions, comprising: a primary extruder arranged for extruding a primary profile, a secondary extruder arranged for extruding a secondary profile, the secondary profile comprising a substrate layer and transverse protrusions, the secondary extruder comprising an extrusion die, wherein a rotatable molding wheel forms a wall of the extrusion die, the molding wheel having recesses functioning as molds for the transverse protrusions within the extrusion die; and a nip formed between the molding wheel and a preferably flat bedding for joining the primary profile and the secondary profile through fusion bonding, forming a composite structure, wherein the bedding preferably is stationary.
Effects and features of this third apparatus aspect are analogous to those described above in connection with the third method aspect. Embodiments mentioned in relation to the third method aspect are compatible with the third apparatus aspect.
The following lists examples just summarized.
1. A method of producing an elastic profile with longitudinally recurring transverse protrusions, comprising:
2. The method of example 1, wherein said pressing wheel (24) has one or more recesses (44) shaped so that said pressing wheel (24) only touches said substrate layer and not said transverse protrusions (48).
3. An apparatus (2) for producing an elastic profile with longitudinally recurring transverse protrusions, comprising:
4. The apparatus (2) of example 3, wherein said pressing wheel (24) has one or more recesses (44) providing clearance compared to the corresponding recesses (46) of said molding wheel (12).
5. The method of example 1 or 2 or the apparatus of example 3 or 4, wherein rotation of said pressing wheel (24) is synchronized with rotation of said molding wheel (12).
6. A method of producing an elastic profile with longitudinally recurring transverse protrusions, comprising:
7. An apparatus (2) for producing an elastic profile with longitudinally recurring transverse protrusions, comprising:
8. The method of example 1, 2, 5, or 6 or the apparatus of example 3, 4, 5, or 7 wherein said joining point (16) is on the perimeter of said molding wheel (12).
9. The method of example 1, 2, 5, 6, or 8 or the apparatus of example 3, 4, 5, 7 or 8 wherein said joining point is at a nip.
10. The method or apparatus of example 9, wherein said nip (16) is formed between said molding wheel (12) and a preferably flat bedding (18), wherein said bedding (18) preferably is stationary.
11. A method of producing an elastic profile with longitudinally recurring transverse protrusions, comprising:
12. An apparatus (2) for producing an elastic profile with longitudinally recurring transverse protrusions, comprising:
13. The method or apparatus (2) of any one of the preceding examples, wherein said primary profile (6) and/or said secondary profile (20) at least partly comprises natural rubber or a synthetic rubber, such as EPDM.
14. The method or apparatus (2) of any one of the preceding examples, wherein said primary profile (6) and/or said secondary profile (20) at least partly comprises a thermoplastic elastomer (TPE).
15. The method or apparatus (2) of any one of the preceding examples, wherein said molding wheel (12) is internally water cooled.
| Number | Date | Country | Kind |
|---|---|---|---|
| 18154912 | Feb 2018 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2019/052400 | 1/31/2019 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2019/149831 | 8/8/2019 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3142599 | Chavannes | Jul 1964 | A |
| 4097634 | Bergh | Jun 1978 | A |
| 4849045 | Schmidt | Jul 1989 | A |
| 5508103 | Cope | Apr 1996 | A |
| 6210512 | Jones | Apr 2001 | B1 |
| 6709616 | Rhodes | Mar 2004 | B2 |
| 8678807 | Banker et al. | Mar 2014 | B2 |
| 20010042937 | Rhodes | Nov 2001 | A1 |
| 20020189752 | Wetsch | Dec 2002 | A1 |
| 20030161999 | Kannankeril et al. | Aug 2003 | A1 |
| 20060101626 | Gallant et al. | May 2006 | A1 |
| 20100239699 | Banker et al. | Sep 2010 | A1 |
| 20140057077 | Sato et al. | Feb 2014 | A1 |
| 20140322379 | Hsu | Oct 2014 | A1 |
| Number | Date | Country |
|---|---|---|
| 1781396 | Jun 2006 | CN |
| 203198264 | Sep 2013 | CN |
| 3609842 | Sep 1987 | DE |
| 102013108537 | Feb 2015 | DE |
| 0203906 | Dec 1986 | EP |
| 0203906 | Aug 1988 | EP |
| 0580073 | Jan 1994 | EP |
| 0580073 | Jun 1994 | EP |
| 0857563 | Aug 1998 | EP |
| 2516431 | Jan 2015 | GB |
| 2016202534 | Dec 2016 | WO |
| Entry |
|---|
| International Search Report and Written Opinion dated Apr. 2, 2019 for PCT/EP2019/052400 filed on Jan. 31, 2019, 14 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20210031427 A1 | Feb 2021 | US |