The invention relates to a method and to a system for producing metal sheets from strand-shaped profiles having a low thickness, which are produced in particular from magnesium or magnesium alloys, by way of an extrusion system.
Producing sheet metal by casting liquid alloy between two rollers and subsequently using numerous rolling and heat treatment processes is generally known. Due to the large number of reduction passes from the heavy plate to the thin sheet, this method is very cost-intensive. The steps are necessary to achieve a formable wrought structure from a cast structure. The high number of reduction passes is cost-intensive.
DE 101 50 021 B4 discloses a method and a device for producing profiles or sheet metal parts from magnesium or magnesium alloys by way of forming, under compressive conditions using extrusion, rolling, forging or casting, wherein the liquid melt is introduced into a continuous casting or extrusion unit to produce a semi-finished product, and immediately thereafter this semi-finished product is given the net shape thereof by way of forming in the warm state, wherein the temperature of the material after solidification from the melt is maintained in a range of 250° C. to 530° during the entire manufacturing operation, and the manufacturing process from casting to cooling of the formed parts is carried out as a whole in an inert atmosphere or under vacuum.
The device for carrying out these method steps is characterized in that the system is composed of a chain of a melting furnace, a continuous casting or extrusion unit, with or without roil stand, a cutting unit, one or more presses, and a cooling unit, the collectivity or parts of the aforementioned units being disposed in a protective gas chamber or vacuum chamber.
Moreover a method for producing formed sheet metal parts from magnesium is described in DE 103 17 080 B4, in which a formed sheet metal part can be produced immediately following the rolling process by way of forming using at least one press in a temperature range of >350° C. to 450° C. The device described for carrying out this method, which is composed of a chain of a melting furnace or crucible, a continuous casting unit, one or more roll stands, a cutting unit, one or more presses, and a cooling unit and is operated in a protective gas chamber or vacuum chamber, is characterized in that a stamping unit, which can be used to introduce dimensionally and cross-sectionally stable stamped holes and/or formed holes into blanks coming from the cutting device, is provided between the cutting unit and the press designed as a forming press.
DE 102 47 129 A1 describes another method for producing profiles or formed sheet metal parts from magnesium or magnesium alloys, in which a semi-finished product in the form of a metal sheet is given the net shape thereof by way of forming, preferably by way of compression molding, wherein the surface is freed from impurities in a method step immediately prior to the forming operation by way of chip removing, and preferably by way of shaving.
The disadvantage that remains with this method is that it is only possible to produce parts having a limited width, since larger parts command significantly added effort for the working pressures that are to be controlled. The tool and the machine frame must withstand the pressing pressure that is present during the manufacture of the semi-finished products or the parts, together with a corresponding counter-pressure, and therefore must necessarily be dimensioned considerably larger.
DE 43 33 500 02 discloses a method for producing a metal sheet that is stepped in the cross-section and has a solid profile and different wall thicknesses, in which first a semi-finished product is produced, the cross-section of which is similar to the cross-section of the metal sheet in the thickness direction, and in which the semi-finished product is rolled to obtain a metal sheet, wherein, for the production of the semi-finished product, a hollow profile having a wall thickness progression that is distributed over the periphery and corresponds to the desired wall thickness progression of the semi-finished product is extruded, and the hollow profile is severed along a peripheral surface line and formed to obtain the semi-finished product. In addition, two complementary profiles are laid one upon the other, wherein at least one of the profiled contact sides of the complementary profiles is provided with a parting agent, and the two complementary profiles are rolled out simultaneously using cylindrical, which is to say norm stepped, rolls. Prior to rolling, the two complementary profiles are severed on two opposing peripheral surface lines.
This method is used to produce two parts, respectively. The manufacturing process is discontinuous, and only relatively narrow parts can be produced. Other disadvantages are that the manufacturing process is relatively complex due to the manufacturing of the semi-finished product that is implemented with two different wall thicknesses and a stepped roll system.
A method for producing formed sheet metal parts and a device for carrying out the method are known from DE 10 2008 048 576 A1. The method comprises the steps of—extruding or continuously casting a tubular body,—cutting open the tubular body in the longitudinal direction of the same,—expanding the tubular body to obtain a planar body, finishing the planar body to obtain a component in correspondence with the drawing by way of manufacturing technologies that are known per se. The device is essentially composed of a chain of a melting unit, a continuous casting or extrusion unit, a longitudinal cutting unit, a roll stand, and one or more forming units.
A method for producing metal sheets or sheet metal parts from lightweight metal, preferable magnesium, is known from DE 10 2007 002 322 A1, wherein in one or more preceding method steps an extruded profile having an open structure, or a closed structure with subsequent cutting to form an open structure, is produced, and the same is subsequently subjected in one or more steps to a roller straightening process and a roller bending process across multiple rolling and bending stages.
It is the object of the invention to provide a method and a system for producing metal sheets from strand-shaped profiles have a low thickness, in particular from magnesium or magnesium alloys, wherein the open or closed extruded profiles exiting an extrusion die can be formed to obtain a metal sheet.
According to the invention, this object is achieved by the method and the system as in the claims. The open or closed extruded profile exiting the extrusion die of an extrusion press is shaped to obtain a flat metal sheet and is then subjected to a defined shaping process by way of stretch-forming.
The extruded profile exiting the die plate is cut corresponding to the length of the metal sheet to be produced, and the open or closed extruded profile is bent open to obtain a U-shaped profile, wherein the closed profile is previously severed along the peripheral surface line. Thereafter, the U-shaped profile is transferred into an unrolling unit and gripped by way of gripping elements on the longitudinal sides of the U-shaped profile, so as to shape the U-shaped profile by way of the outwardly moving gripping elements to obtain a metal sheet. Subsequently, the metal sheets are smoothed in a defined stretch-forming process.
Shaping of the U-shaped profile to obtain a metal sheet can be supported by a roller pair, which is moved into the U-shaped profile, and by moving each of the individual rollers in the direction of the edge regions located on the longitudinal sides.
Shaping to obtain the metal sheet preferably takes place in a temperature range above 200° C. and in a preferably inert atmosphere.
The system is composed of an extrusion press comprising a die plate generating the extruded profile and a shaping unit following the die plate, wherein the shaping unit is composed of a severing unit, a bending unit, and an unrolling unit. The unrolling unit can be composed of either two movable gripping elements or of one fixed gripping element and one movable gripping element. As an alternative, the unrolling unit can be composed of two movable rollers that can be moved into the U-shaped profile, wherein the individual rollers can be moved away from each other in the direction of the edge regions.
Another option of designing the unrolling unit is for the same to be formed of a combination of gripping elements and two movable rollers that can be moved into the U-shaped profile. So as to protect the surface of the metal sheet to be produced, the rollers can be provided with a heat-resistant elastic surface coating. The rollers that are used for this purpose are designed so as not to cause any surface damage.
Advantageous refinements and embodiments of the invention will be apparent from the remaining dependent claims and from the exemplary embodiment described hereafter in terms of the principle thereof.
The invention will be described in more detail based on one exemplary embodiment. In the drawings:
Using the extrusion press 1, a round billet made of a magnesium alloy is formed to obtain an extruded profile, for example a tubular profile. The extrusion press 1 is stopped when the tubular profile has reached the length that corresponds to the predefined length of the metal sheet. The tubular profile is cut to size by way of the severing unit 2.
The severing unit 2 can be composed of a revolving jet nozzle, a laser, cutting rollers, or a co-rotating saw. If the severing of the tubular profile is carried out by way of metal-cutting, a suction device is provided so as to minimize a risk of fire from magnesium chips or magnesium dust. There is also the option to introduce a notch having a depth of 25% to 85% of the wall thickness at the separation point and to tear off the section of the tubular profile.
The severed section of the tubular profile is then forwarded to the bending unit 3. Here, the section of the tubular profile is severed along a peripheral surface line and bent open to obtain a U-shaped profile by way of a slotted wedge and optionally several rollers. Contact with the tube occurs only in regions of the cut edges, which are later located in the waste region of the metal sheet. Severing can take place, for example, by way of a longitudinally displaceable suction jet nozzle, a laser cutting device or the like.
After severing and bending open to obtain a U-shaped profile, the same is forwarded to the unrolling unit 4. This unit is composed of a flat base area and two movable gripping elements, wherein the gripping elements grip the longitudinal sides of the U-shaped profile and unroll the U-shaped profile to obtain a flat metal sheet.
After the open tubular profile 8 has left the extrusion press, it is expanded. In a first step, the profile 8 is cut to the appropriate length by way of a severing unit. The expanding may take place by way of forming rollers 10. As is shown in
However, it is also possible to push the longitudinal opening of the severed open tubular profile 8 onto two displaceable angled gibs 11, or the open tubular profile can be pushed onto the displaceable angled gibs 11 immediately after leaving the press die (
The U-shaped profile 8 is then forwarded to an unrolling unit 4. Here, the longitudinal sides of the profile 8 are gripped by way of the collets 12 (
The collets 12 have a floating design and are connected on one side, or on both sides, to hydraulic cylinders, whereby an adaptation to the profiled ends 9 of the longitudinal edges of the profile 8 is achieved. Slightly concave or convex deflection at the profiled ends 9 on the longitudinal edges can thus be compensated for.
Following the hydraulic chucking process, the unrolled profile 8 is stretch-formed linearly by way of the hydraulic cylinders. The overpolishing rotational movement of the collets 12 is carried out by way of the pivotable hydraulic cylinders. In this way, the stretch-formed material is free of interfering bending forces (
During final stretch-forming, the floating collets 12 are oriented against fixed stops, whereby consistent stretch-forming across the entire sheet metal width is ensured. So as to minimize the heat dissipation via the collets 12, these are provided with a ceramic coating.
After the stretch-forming operation, the collets 12 are opened, and the stretch-formed metal sheet 13 is pushed out in the longitudinal direction by way of a pneumatic cylinder. The stretch-formed metal sheet 13 can subsequently be forwarded to a metal-forming working operation, for example using pressing, stamping or the like. However, it is also possible to cut the stretch-formed metal sheets 13—removing the profiled ends—and to stack the metal sheets 13.
A considerable advantage of the method and of the system is that stretch-forming of the metal sheet in the transverse direction can be carried out by way of the gripping elements. Stretch-forming in the transverse direction can be carried out in a range of 1% to 10%. As a result of stretch-forming the metal sheet, it is not only possible to decisively improve flatness, but also to achieve a thickness configuration for the metal sheet. It is also crucial that no surface defect-causing contact areas are present at what will later be the visible surfaces.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2013 008 635 | May 2013 | DE | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/DE2014/000246 | 5/13/2014 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2017/187442 | 11/27/2014 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 1133903 | Wright | Mar 1915 | A |
| 1423361 | Rockwell | Jul 1922 | A |
| 2133874 | Sparks | Oct 1938 | A |
| 2681734 | Braeuninger | Jun 1954 | A |
| 2692421 | Cozzo | Oct 1954 | A |
| 2716805 | Reed | Sep 1955 | A |
| 2742692 | Braeuninger | Apr 1956 | A |
| 2798286 | Anderson | Jul 1957 | A |
| 2802509 | Anderson | Aug 1957 | A |
| 3022255 | Grossu | Oct 1961 | A |
| 3342055 | Blankenship | Sep 1967 | A |
| 3442000 | Dornbos | May 1969 | A |
| 4187711 | Lavochkin | Feb 1980 | A |
| 5829298 | Linsenbardt et al. | Nov 1998 | A |
| 5848545 | Michisaka | Dec 1998 | A |
| 6070448 | Eipper | Jun 2000 | A |
| 6138489 | Eriksson | Oct 2000 | A |
| 6862911 | Birkenstock | Mar 2005 | B2 |
| 20110030439 | Maier et al. | Feb 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 101579817 | Nov 2009 | CN |
| 102179422 | Mar 2013 | CN |
| 103008377 | Oct 2015 | CN |
| 43 33 500 | Mar 1996 | DE |
| 102 47 129 | Apr 2004 | DE |
| 101 50 021 | Aug 2005 | DE |
| 103 17 080 | Apr 2006 | DE |
| 10 2007 002 322 | Jul 2008 | DE |
| 10 2008 048 576 | Mar 2010 | DE |
| 102008048496 | Apr 2010 | DE |
| 556061 | Sep 1943 | GB |
| 2469549 | Oct 2010 | GB |
| H07100553 | Apr 1995 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20160096221 A1 | Apr 2016 | US |