The invention pertains to the field of ovens and, in particular, to ovens for rapidly heating printing plates.
Printing operations undertaken in an offset printing press typically utilize lithographic printing plates. These lithographic printing plates are produced in a separate process involving the exposure of an image onto a plate substrate that typically comprises a thin aluminum alloy suitably treated so as to be sensitive to light or heat radiation.
One process of making a lithographic plate suitable for use on an offset printing press has been to employ a film mask. Exposing highly sensitive film media using a low power laser printer known as an “image-setter” typically produces this film mask. The film media is usually processed in some manner and is then placed in area contact with a photosensitive lithographic plate, which is in turn, “flood” or “area” exposed through the film mask. Such plates are referred to as “conventional printing plates”. The most common conventional printing plates used in such a process are sensitive to radiation in the ultraviolet region of the light spectrum. Typically, it is usually further necessary to amplify the difference between the exposed and un-exposed areas in a further chemical processing step that removes the unwanted coating and converts the plate into a lithographic printing surface ready for use on the press.
More recently, a method of exposing a lithographic printing plate directly through the use of a specialized printer known as a plate-setter has gained popularity. A plate-setter in combination with a computer system that receives and conditions image data for sending to the plate-setter is commonly known as a Computer-to-Plate or “CTP” system. CTP systems offer a substantial advantage over image-setters in that they eliminate the film mask and the associated process variation associated with that extra step. The CTP system receives the image data and formats it to make it suitable for outputting to an exposure head within the plate-setter. The exposure head in turn controls a radiation source, which is typically a laser, so as to image picture elements (pixels) on the lithographic plate according to the image data.
Lithographic printing plates imaged by CTP systems are typically referred to as “digital” printing plates. The radiation beams emitted by the exposure head induce a physical or chemical change to a coating on the digital plates. Currently, digital plates comprise either: 1) high-sensitivity photopolymer coatings (“visible light plates”) or 2) thermal photosensitive coatings (“thermal” plates). Visible light plates are typically exposed by a blue-violet laser diode of 10-100 mW. High power IR lasers in the range of 1 W to 100 W are used to expose thermal digital plates.
Like lithographic printing plates produced using film-based methods, many types of exposed or imaged digital printing plates typically undergo a further chemical processing step that removes the unwanted coating and converts the plate into a lithographic printing surface ready for use on the press.
Regardless of the method employed to image or expose a lithographic printing plate, the exposed printing plate is often pre-heated or pre-baked in an oven prior to being washed in a chemical solution during the subsequent chemical processing step. Additionally the processed printing plate can also be post-baked in another oven after the chemical wash step.
Once exposed or imaged, the printing plate typically undergoes the pre-heat step so as to render the image-wise exposed areas of the printing plate insoluble in the subsequent chemical development or processing steps. Hence, the un-exposed areas of the printing plate remain soluble and are washed away in the chemical baths to produce a final printing plate with the necessary differentiation between print areas and non-print areas. Typically, when the printing plates are exposed in a CTP plate-setter and then undergo this pre-heat step, the printing plates are referred to as “negative” or “negative-working” plates. Negative plates that are exposed with the use of conventional film masks are characterized such that the desired “printing image” will be exposed during the subsequent flood exposure. Likewise, negative plates that are imaged by a CTP system are characterized such that the desired “printing image” is imaged by the CTP plate-setter itself. In this context, the term “printing image” refers to the image that ultimately is printed on the press. In either case however, the printing image exposed on the printing plate is made insoluble by the pre-heat step such that it remains intact after the subsequent processing step. “Positive”, or “positive working” plates are essentially the opposite of negative plates. Accordingly, the background image or the non-printing image is directly exposed onto positive plates. Exposed positive plates typically do not undergo a pre-heat step. In fact, the exposed background images are rendered soluble upon exposure. Consequently, a positive plate can be chemically processed such that the exposed or imaged background is washed away to produce a final printing plate that comprises the necessary print image required on press.
Post-baking of a processed printing plate is usually conducted to impart specific characteristics to the printing plate. Such characteristics can include increasing plate life on press. Some plate manufactures claim that plate life can be increased as much as five fold. Different criteria can be used to determine when plate has reached its end-of-life. One such criteria suggests that a plate has reached its end-of-life when more than 25% of 200 lpi 1% dots imaged on the plate are worn off during printing (as determined visually). The benefits of post-baking are not limited to any one type of plate. Conventional and digital plates can be post-baked in accordance with their respective manufacturer's instructions.
Pre-heat and post-bake ovens have typically been conveyor ovens. Such an oven is disclosed in U.S. Pat. No. 6,323,462 (Strand).
Conveyor ovens typically need to be kept on all the time since their warm-up time is lengthy. Conveyor ovens are typically very large in size and thus require substantial space requirements. These space limitations are further exasperated when a processing line requires both pre-heat and post-bake capability. Consistent and uniform oven temperatures have a significant effect on the quality of the processed plate, thus further increasing the complexity of conveyor ovens which includes a myriad of blowers, heating elements and extensive ductwork. Ovens that comprise inductive heating (also known as RF heating) means or microwave heating means can offer instant warm up, but are expensive since they require many kilowatts of power at high frequencies.
Pressurized fluid bearings (also known as hydrostatic bearings) are well known in the art of tribology and have been used in processing equipment. U.S. Pat. No. 5,239,327 (Frank) describes the use of a plurality of hydrostatic bearings within a chemical processing tank. The hydrostatic bearings are submerged within a processing solution that is used to process a film web. In this patent, each of the bearings comprise a pair of juxtaposed housings on opposite sides of the film web. Each of the housings includes an aperture for emitting liquid under pressure so as to support the web without it physically contacting the housings. Frank discloses that the film web within the processor does not follow a linear path, and as such, in the curved potions of the web path, the juxtaposed face surfaces of the bearing houses are curved to define the necessary web path there-between.
A pressurized air bearing (also know n as an aerostatic bearing) is similar to any pressurized fluid bearing, except the fluid is air. Like hydrostatic bearings, pressurized air bearings have a porous or perforated plate, known as a bearing pad, through which pressurized air is pumped through and prevents contact between the pad and the moving object. The bearing pads can incorporate any air-permeable arrangement and include uniform and distinctly shaped openings or randomly formed openings created by sintered plates as an example. An air bearing can be single or double sided. In the later embodiment, the object glides between two parallel pads without touching either one and with practically no friction.
It has been shown in the prior art, that air bearings are capable of exhibiting exceptionally fast heat transfer to a planar object such as a printing plate. In regular convection ovens most of the heated air bypasses the printing plate, therefore heat transfer efficiency is low. In a heated air-bearing oven, most of the heated air can be forced to flow through a relatively small parallel gap between the printing plate and the bearing pads, thereby resulting in very good heat transfer. Another advantage is that such a heated air bearing oven is very small and has low thermal mass since there is no requirement to heat up a large enclosure.
However, one disadvantage of an air-bearing oven is that that the heat transfer efficiency is greatest when the planar surface of the printing plate is within a very small distance of the heated bearing pads. Consequently, it is desired to keep this distance, or alternatively, the gap between any two adjacent heating pads as small as possible to promote rapid heating. A plate however typically distorts upon heating and this distortion can cause the plate to contact a heating pad when such small distances and gaps are employed. This contact can cause damage to the plate, especially to its relatively delicate photopolymer or thermal photosensitive coating. Such damage would be highly undesirable as it would likely lead to on-press printing artifacts. This damage may be avoided by increasing the air bearing distance or gap, but at a cost of reduced heat transfer efficiency.
EP 0 864 944 A1 (Oelbrandt et al.) discloses an air bearing device that comprises two flat, planar air bearings plates used to heat an imaging element that can include various forms of paper, film, plastics, laminates and printing plates. It also discloses that the spacing between the two flat air bearing plates is in the range of 2 to 20 mm and that hot air is applied to both sides of imaging element within this spacing such that substantially equal flows at substantially equal air temperatures are created.
U.S. Pat. No. 5,181,329 (Devaney, Jr. et al.) discloses an apparatus for the drying of conventional film and paper during a photo processing operation. It also describes drying a web of paper or film between a pair of spaced, parallel air bearing members having flat surfaces defining a channel through which heated air is used to support the web. In addition to the air bearing air inlet holes, air bearing evacuation holes are provided at a predetermined distance from the inlet holes so as to maintain the heat transfer rate in the channel higher than the heat transfer rate in the web.
Clearly, there is a need for a simple oven capable of a rapid warm up. Further, such an oven should be compact and have a high thermal efficiency. Finally, such an oven should not contact the surface of the lithographic printing plate that is coated with a photopolymer or thermal photosensitive coating. Needless to say, any contact may result in damage to the exposed or imaged coating, ultimately resulting in undesired on-press printing artifacts.
The present invention provides a method for heating a planar printing plate, the method comprising:
a plurality of openings, the plurality of openings being operable to convey at least a part of the flow of air,
heated by the at least a part of the flow of air, and
is prevented from contacting the first curved surface by the at least a part of the flow of air.
In another aspect, this invention provides an apparatus for heating a planar printing plate, the apparatus comprising:
a plate feeding means operable for moving the planar printing plate along a substantially curved path within a gap,
a blower operable for creating a flow of air that is pressurized,
a heater operable for heating the flow of air, and
at least two curved surfaces arranged to establish the gap and the substantially curved path within the gap, wherein:
the at least two curved surfaces comprise a first convex surface and a second concave surface, the first convex surface and the second concave surface each having at least one substantially equal radius of curvature, and at least both the first convex surface and the second concave surface, each comprises a plurality of openings operable to convey a portion of the flow of air into the gap to heat at least a portion of the planar printing plate within the gap.
In accordance with this invention, a method and apparatus are disclosed for rapidly heating a planar printing plate as the plate moves through a heated air bearing. The heated air bearing comprises one or more curved heating surfaces. The planar printing plate is moved along a substantially curved path that is adjacent to at least one of the curved heating surfaces. While the plate is being moved along the substantially curved path, it is bent to substantially conform to the path. Each of the heating surfaces additionally comprises a plurality of openings that allow a flow of air to be conveyed towards the plate as the plate travels along the substantially curved path. Air is pressurized and heated and is conveyed through each of the heating surfaces. The planar printing plate is fed into heated air bearing and is bent by the flow of pressurized and heated air so as to conform and follow the contour of the substantially curved path. Alternatively, the printing plate can be bent or supported by additional mechanical means so as to conform and follow the substantially curved path through the air bearing. In either case, the portion of the planar printing plate moving along the substantially curved path is heated by the pressurized and heated flow of air. Since this portion of the plate has been bent to follow the curved path, the stiffness of this portion of the printing plate is increased considerably. This in turn helps to counter thermal distortion effects that occur from heating the plate from ambient temperature conditions and can cause the printing plate to distort and contact the heating surfaces, thus potentially damaging the plate. Therefore, this method of heating the printing plate allows for a smaller distance between the planar surface of the printing plate and any of the heated curved surfaces while minimizing potential damage to the plate itself. Consequently, the gap between two adjacent surfaces can also be made smaller. This smaller distance and gap, in turn increases the thermal heat transfer efficiency of the air bearing, thus promoting a rapid and energy efficient heating of the printing plate. A compact, energy efficient apparatus can be created to heat printing plates by this method. Such an apparatus additionally benefits from quick warm up times, and thus advantageously further reduces power consumption.
a shows a cross sectional view of the air bearing of an embodiment of the invention.
b shows a cross sectional view of the air bearing of another embodiment of the invention.
a shows a cross sectional view of the air bearing of yet another embodiment of the invention.
b shows another cross sectional view of the air bearing of yet another embodiment of the invention.
Regardless of whether a given printing plate is a “conventional” plate that is exposed through a film mask or a “digital” plate that is imaged by a CTP imager, the printing plate typically comprises a polyester or metal substrate. Further, aluminum and aluminum alloys are the preferred choice of most metal-based printing plates. Both polyester and metal printing plates are susceptible to thermal changes. Additionally, polyester is also susceptible to humidity changes. Both aluminum and polyester have coefficients of thermal expansion of approximately 20-23 μm/m/° C. (or 20-23 parts per million (ppm)/° C.). The coefficient of thermal of expansion is a material specific constant used to estimate the change in length or size that an object undergoes when heated or cooled from a known temperature. Required oven pre-heating temperatures are typically in range of from about 100 to about 250° C. above ambient conditions. As previously stated, the prior art has disclosed air bearing heating devices that comprise substantially planar air bearing pads. Experimentation has determined that when a printing plate is introduced into such a prior art device, its leading edge is heated as would be expected by the stated air bearing temperatures. This leading edge portion of the plate thus inclined to expand accordingly. For example, the leading edge portion of a typical aluminum printing plate approximately 0.3 mm thick and 1 meter in width, would be inclined to expand approximately 2 to 5 mm due to the 100 to 250° C. air bearing temperatures. However, the remaining portion of the plate that has not entered the heated air bearing does not expand since it is still exposed to ambient air temperatures. The heated leading edge portion of the plate is thus constrained from expanding due to the heated air bearing temperatures, and consequently the leading edge portion of the plate buckles. For the example given, the 1 meter wide plate may buckle up to 2 to 4 mm under these conditions. If these prior art planer air bearing pads are not sufficiently spaced apart, the buckled leading edge potion of the plate will strike at least one of the pads. Consequently, the imaged or exposed coating on the printing plate may be damaged and thus ultimately result in undesirable on-press printing artifacts.
These difficulties may be overcome by spacing the planar air bearing pads further apart to produce a large “air bearing gap” or “gap”. Although this may prevent damage to the printing plate coating, the thermal transfer efficiency of the heated air bearing is reduced. For a typical aluminum printing plate comprising a thickness of 0.3 mm, it has been shown that the greatest thermal heat transfer occurs when the air-bearing gap is under 1 mm, or approximately three times the thickness of the plate. If the air bearing gap where to increase to 2 mm, the thermal transfer efficiency would be reduced by from about 30% to about 50%. Gaps of from about 10 to about 20 mm substantially limit the air bearing thermal transfer. For example, in a heated air bearing comprising a 1 mm gap, a 0.3 mm thick plate was heated to 90% of final temperature in 5 seconds. The same plate, however took 20 seconds to reach same temperatures when the gap was increased to 10 mm and the same airflow and heating conditions were used. Therefore, it has been found that increasing the gap to counter the plate-buckling problem reduces the heating efficiency of the heated air bearing. Clearly, although a heated air bearing has the potential to produce a compact oven, improvements are needed to reduce printing plate coating damage while maintain high heating efficiency.
Referring now to
In the example of the invention shown in
In another embodiment of the invention, the airflow created by blower 60 is kept at a very low level when the heated air bearing is not in use while the air temperature is continuously maintained at its “heating mode” operating level. Because of the low airflow, power consumption is low as well. Typical airflow in this embodiment of the invention is approximately 10% of the levels required during actual heating of the plate (that is, 2 liters/sec as opposed to a 20 liters/sec heating mode value), and the actual power consumption in this mode is about 20% of normal for a well-insulated oven. In this embodiment, when printing plate 10 is sensed or detected, blower 60 increases the airflow to its heating mode value. Because the heater is already at the necessary heating temperature, warm up is achieved very quickly and is typically well under 1 minute. A suitable systems controller (not shown) can be used to control the operation of the plate feed mechanism, the blower and heater to control the warm-up time and operating heating conditions of any of the embodiments of the invention. In other embodiment of the invention the operation of plate feeding mechanism (e.g. rollers 20), blower 60, and heater 50 can be controlled by a CTP device that controls the imaging rate of plates and consequently determines when the oven should undergo any necessary warm-up cycle and when a given plate should be heated.
a shows a cross section of the upper and lower heating pads 30 and 40 of an embodiment of the invention. Channels 11 and 12 are respectively insulated by thermal insulation 13 and 14. In this embodiment, channel surfaces 11a and 12a are curved such that each respective axis of curvature is perpendicular to the feed direction 100 of printing plate 10. Specifically, channel surface 11a has a concave shape while opposing surface 12a has a complimentary convex shape. Both channel surfaces 11a and 12a complimentary match one another to define a substantially equally sized gap 17 and a substantially curved path within gap 17. The substantially curved path is adjacent to at least one of the curved channel surfaces 11a and 12a. It is to be noted that other embodiments of the invention are not precluded from reversing the orientation of convex and concave surfaces. In the embodiment shown in
The substantially curved path defined by channel surfaces 11a and 12a can assume any continuous arc-like profile (e.g. segments of circular, parabolic, elliptical profiles). Profiles are chosen with a preferred radius of curvature of approximately 250 mm, although at least one radius of from about 200 to about 1000 mm was also found to work well. It is to be noted that as printing plate 10 travels through the substantially curved path established in the heated air bearing gap 17, the curvature imparted to printing plate 10 should be elastic in nature, since printing plate 10 should resume its inherent planar nature once it travels beyond heating pads 30 and 40. Maintaining the plate's inherent planar nature is important since the plate should remain flat during any subsequent chemical processing steps. Consequently, the arc-like profiles of channel surfaces 11a and 12a should be chosen to have a degree of curvature sufficiently large so as to not impart a permanent set or bend into printing plate 10 as it travels through the substantially curved path. Further, large lead-ins into channel surfaces 11a and 12a should also be incorporated so as to avoid imparting a permanent set into printing plate 10 as it enters gap 17.
It is conceivable that channel surfaces 11a and 12a can have substantially matching curved surfaces, each with a respective axis of curvature that is parallel to the feed direction 100 of printing plate 10. Such an embodiment may however pose additional challenges of “transitioning” an essentially planar printing plate 10 from the plate feeding mechanism into a curved entrance created by upper and lower heating pads 30 and 40. Such an embodiment would likely require additional space and means to transition the planar printing plate 10 into a suitable profile to successfully enter such a heated air bearing. Additionally, as previously stated, the embodiment of the invention shown in
Referring back to
b shows a cross section of a single-sided air bearing used by another embodiment of the invention. In this embodiment of the invention, a single heating pad 30 is positioned such that it is adjacent to the photopolymer or thermal photosensitive coating 10a of printing plate 10. Heated air is provided through a plurality of supply openings 15 so as to provide a heated air cushion for the heating of printing plate 10. Additionally, this heated air cushion separates photosensitive coating 10a from channel surface 11a, thus minimizing any potential damage to photosensitive coating 10a. The uncoated side 10b of printing plate 10 is supported by any suitably curved support means such as a plurality of heat resistant rollers 31. Uncoated side 10b is more resistant to damage than photosensitive coating 10a and has a lesser impact on preventing on-press printing artifacts. Consequently, uncoated side 10b can contact rollers 31 or any other contact based support means so long as the plate material itself is not kinked or galled. In this embodiment, the plurality of contact rolls 31 is arranged to minimize the distance between photosensitive coating 10a and channel surface 11a. Rollers 31 are further arranged to help define a substantially curved path through which printing plate 10 may be fed through during the heating operation. This distance is preferably minimized to increase thermal transfer efficiency. Heated air, provided through a plurality of supply openings 15, causes printing plate 10 to bend so as to be supported by rollers 31 and to conform to, and follow the substantially curved path. In other embodiments of the invention comprising a single-sided air bearing, printing plate 10 is bent by any mechanical means capable of applying a bending moment to printing plate 10. Such mechanical means are used to help conform printing plate 10 to a desired substantially curved path established adjacent to channel surface 11a. Such mechanical means can include a series of heat-resistant nip rollers positioned at the entrance and exit of the single-sided air bearing and arranged to bend printing plate 10 so as to transition it into and away from the desired substantially curved path. Such mechanical means can be used to as the primary means of bending the plate to conform to the substantially curved path, especially when printing plate 10 comprises a continuous web of plate material. Alternatively, the bending of printing plate 10 can additionally be supplemented by at least the “bending action” created by the flow of air through supply openings 15 in channel surface 11a.
a and 3b show another embodiment of the invention. Unlike the embodiment shown in
In order to increase the efficiency of the air bearing, it may be desirable to provide a shallow depression around each of the plurality of supply openings 15 and 16. This increases the lifting force should printing plate 10 try to block any of the supply openings 15 and 16, and is standard practice in air bearing design. Such an opening pattern is shown in
Re-circulating and re-using the hot air after it passed across printing plate 10 can further increase thermal transfer efficiency. Other advantages of air re-circulation include avoiding heating up surrounding objects due to escaping hot air and the ability to filter the flow of air or to trap or destroy any volatile emissions emanating from the heated plate. In such a re-circulating system a return path is provided for the hot air, as shown in
By the way of example, a system was tested using the following parameters:
The heating time required to reach 150° C. with this oven was 5 seconds for the thickest plate (0.4 mm). The warm-up time for the whole oven was under 5 minutes from a cold start, and less than 30 seconds in a reduced airflow mode in which the oven stayed hot but the airflow was reduced when the oven was not in a heating mode. The system was used to pre-heat and post-bake thermal printing plates imaged on a Creo Trendsetter 3244 computer-to-plate imager. Because of the short warm-up, the oven was only turned on when the imaging of the plate was started and the oven was fully ready by the time the plate was imaged, resulting in major energy savings compared to a current system in which the conveyor oven is kept on all the time. Additionally, none of the tested printing plates had their imaged coating scratched or damaged within the heated air bearing. The overall size of the tested oven is 170 mm×200 mm×1000 mm for plates up to 900 mm wide. This represents 10% of the volume of a conventional pre-heat oven.
The apparatus of the invention can be incorporated into and used in a lithographic plate processing line. Embodiments of the invention may be used in pre-heat oven wherein plates are thermally pre-sensitized prior to chemical processing. Pre-heat ovens incorporating an embodiment of the invention will typically be compact in nature and are thus suitable as stand-alone devices or may be an integral component of the chemical processor unit itself. Further, the quick warm-up time associated with a pre-heat oven comprising an embodiment of the invention also allow such an oven to be incorporated as an integral part of a computer-to-plate (CTP) device.
Additionally, embodiments of the invention may be incorporated into post-bake ovens used to impart additional characteristics to processed printing plates. Since embodiments of the invention allow for a compact design, a post-bake oven comprising an apparatus of the invention can be a stand-alone unit or incorporated into the chemical process itself.
Embodiments of the invention can be used to heat many types of lithographic printing plates that are described in numerous publications. The printing plates can include conventional printing plates that are exposed using a film mask and also digital plates that are imaged in a CTP device. Such digital plates can include plates that comprise photopolymer coatings or thermal photosensitive coatings disposed on a suitable substrate. Although conventional and digital printing plates are typically used in sheet form, methods and apparatus of the invention can also be used for heating printing plate materials that are in web form. Such embodiments of the invention are especially suitable for the manufacturing process of printing plates, wherein the plates undergo several heating cycles especially during the application of the photopolymer or thermal photosensitive coatings to the plate substrate.
The method of the invention wherein the substantially curved path is adjacent to a second curved surface, the second curved surface comprising a plurality of openings operable to convey at least an additional part of the flow of air, and wherein the method further comprises:
heated by the at least an additional part of the flow of air, and
is prevented from contacting the second curved surface by the at least the additional part of the flow of air.
The method of the invention wherein the at least a portion of the planar printing plate along the substantially curved path comprises a photopolymer or thermal photosensitive coating, and the method further comprises:
heated by the at least a part of the flow of air, and
is prevented from contacting the first curved surface.
The method of the invention wherein the at least a portion of the planar printing plate along the substantially curved path comprises a photopolymer or thermal photosensitive coating, and the method further comprises:
heated by the at least a part of the flow of air, and
is prevented from contacting the first curved surface and the second curved surface.
The method of the invention comprising arranging the first curved surface and the second curve surface, wherein a gap is formed there between and the substantially curved path is established within the gap.
The method of the invention wherein the bending the planar printing plate comprises bending the at least a portion of the planar printing plate along the substantially curved path with at least one of:
the at least a part of the flow of air, and
the at least an additional part of the flow of air.
The method of the invention further comprising arranging the first curved surface and the second curved surface, wherein the gap is substantially uniform along the substantially curved path.
The method of the invention further comprising arranging the first curved surface and the second curved surface, wherein the gap is smaller when the planar printing plate is not moved along the substantially curved path.
The method of the invention wherein the planar printing plate includes a thickness, and the method further comprising arranging the first curved surface and the second curved surface, wherein the gap is not greater than three times the thickness of the planar printing plate.
The method of the invention wherein the planar print plate is additionally moved along a feed direction, and the substantially curved path has at least one axis of curvature that is substantially perpendicular to the feed direction.
The method of the invention further comprising arranging the first curved surface and the second curved surface, wherein the substantially curved path has at least one radius of curvature and, wherein the bending the planar printing plate comprises bending the at least a portion of the planar printing plate along the substantially curved path with a radius of curvature that is substantially equal to the at least one radius of curvature.
The method of the invention wherein the bending the planar printing plate comprises elastically bending the planar printing plate.
The method of the invention wherein the method further comprises supporting the at least a portion of the planar printing plate along the substantially curved path with a support means, wherein the coating is prevented from contacting the support means.
The method of the invention wherein the bending the planar printing plate comprises applying a bending moment to the planar printing plate.
The method of the invention wherein the conveying the at least a part of the flow of air commences less than 5 minutes before the planar printing plate is moved along the substantially curved path.
The method of the invention wherein the flow of air comprises an airflow and the method further comprises reducing the airflow before the planar printing plate is moved along the substantially curved path.
An apparatus wherein at least one of the at least two curved surfaces is further operable to rotate towards and away from another of the at least two curved surfaces.
An apparatus wherein at least one of the at least two curved surfaces is further operable to translate towards and away from another of the at least two curved surfaces.
An apparatus further comprising an airflow re-circulation means.
An apparatus further comprising an airflow filtration means.
An apparatus further comprising a catalytic converter.
An apparatus further comprising a systems controller operable for controlling at least one of: the plate feed means, the blower, and the heater.
An apparatus wherein the planar printing plate is a conventional printing plate that has been exposed with a film mask.
An apparatus wherein the planar printing plate is a digital printing plate that has been imaged in a computer-to-plate device.
An apparatus wherein the planar printing plate is a negative digital printing plate that has been imaged in a computer-to-plate device.
An apparatus wherein the apparatus is an oven.
An apparatus wherein the oven is a pre-heat oven.
An apparatus wherein the oven is a post-bake oven.
An apparatus wherein the oven is an integral component of a chemical plate processor.
An apparatus wherein the oven is an integral component of a computer-to-plate device.
An apparatus wherein the planar printing plate comprises a web of printing plate substrate that is coated with one of: photopolymer coating, or a thermal photosensitive coating.
The invention has been described in detail with particular reference to certain example embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.
This application relates to provisional application 60/634,748, filed Dec. 10, 2004.
Number | Name | Date | Kind |
---|---|---|---|
3668788 | Kobayashi | Jun 1972 | A |
3806575 | Fishburn | Apr 1974 | A |
3902041 | May | Aug 1975 | A |
4467537 | Trotscher | Aug 1984 | A |
4842664 | Baudin | Jun 1989 | A |
4981433 | Matsumoto et al. | Jan 1991 | A |
5181329 | Devaney, Jr. et al. | Jan 1993 | A |
5239327 | Frank | Aug 1993 | A |
5507102 | De Vroome et al. | Apr 1996 | A |
6001303 | Haynes et al. | Dec 1999 | A |
6091055 | Naka et al. | Jul 2000 | A |
6099782 | Holmes | Aug 2000 | A |
6293031 | Ringbom et al. | Sep 2001 | B1 |
6323462 | Strand | Nov 2001 | B1 |
6600137 | Nonomura et al. | Jul 2003 | B1 |
6855206 | Minato | Feb 2005 | B2 |
7278351 | Sugiyama et al. | Oct 2007 | B2 |
7363856 | Moulin | Apr 2008 | B1 |
Number | Date | Country |
---|---|---|
864 944 | Sep 1998 | EP |
Number | Date | Country | |
---|---|---|---|
20060124010 A1 | Jun 2006 | US |
Number | Date | Country | |
---|---|---|---|
60634748 | Dec 2004 | US |