Method and apparatus for separating ions of metallic elements in aqueous solution

Abstract

Methods and apparatus for separating ions of metallic elements are provided. Preferred methods utilize a hydrophobic chelating extractant, such as an organophosphorus compound, adsorbed onto carbon or graphite fibers in the form of felt. Also described is a new thallium-201 generator that comprises a column containing an acidic organophosphorus extractant adsorbed on carbon or graphite fibers, and a yttrium-90 generator system comprised of two extraction columns designed to selectively absorb yttrium-90 at different pH, to enable the separation of yttrium-90 from strontium-90. The two columns are connected in series for stepwise separation. The yttrium-90 product is freed from residual strontium-90 and metal contaminants and can be eluted from the second column with dilute acid, acetate buffer, water or saline for labeling biological targeted molecules. The new generator system provides rapid and efficient separation of yttrium-90 and is amenable to both scale-up and automation. Also described is a new 99mTc generator that comprises a column containing an acidic organophosphorus extractant adsorbed on carbon or graphite fibers designed to selectively absorb 99Mo at a selected pH, to enable the separation of 99mTc from 99Mo.

Description

FIELD

[0002] This invention is generally directed to methods and apparatus for separating ions of metallic elements in aqueous solution by chromatography. The elements to be separated may belong to the same or to different Groups in the long periodic table, including main group elements, transition metals, lanthanides and actinides. The present invention relates more particularly to an apparatus and a method for separating ions of radioisotopes such as 90Y, 201Tl, and 99mTc from their parent elements, and producing multicurie levels of same for medical applications while generating minimum waste.

BACKGROUND

[0003] Radioactive isotopes of many metallic elements have potential uses in the diagnosis and treatment of disease. The yttrium-90 isotope, for example, which has a half-life of 64 hours and emits a strong beta particle (Emax=2.28 MeV), has excellent promise in treating many human diseases, and recent advances in radioimmunotherapy and peptide targeted radiotherapy have created a great demand for 90Y. Another radioisotope, thallium-201, which has a half-life of 73 hours and emits photons of 135 and 167 keV, is widely used as a myocardial perfusion imaging agent. Numerous other examples of radioactive isotopes, and their potential use as radiopharmaceuticals are well known to those in the art.

[0004] One way to produce radioisotopes with potential use as radiopharmaceuticals is from the decay of radioactive species of elements from adjacent groups in the periodic table. For Example, 90Y can be produced from the 28-year half-life decay of 90Sr. Similarly, 201Tl is decayed from its parent 201Pb (T1/2=9.33 hour).

[0005] To be used as radiopharmaceuticals, the target isotopes generally need to be separated from the parent compounds. Many different techniques have been used to separate radioisotopes, including precipitation, solvent extraction, and ion-exchange chromatography, and the use of a number of organophosphorus extractants has been described. For example, di-2-ethylhexylphosphoric acid (DEHPA) has been widely used in extraction technology of rare earths and yttrium since the publication of Peppard, et al. (D. F. Peppard, et al., J. Inorg. Nucl. Chem. 4: 334, 1957) in 1957. DEHPA was also used in high level separations of fission products of rare earths and 90Y at Oak Ridge National Laboratory in 1959. A smaller scale procedure for millicurie quantities of 90Y was used at Oak Ridge National Laboratory (ORNL) (N. Case, et al., ORNL Radioisotope Manual, U.S.A.E.C. Report ORNL-3633, TID 4500, 30th edition, June 1964) from 1962 to 1990. This procedure was later modified for use in purification of reagents and is now used commercially to supply 90Y (J. A. Partridge, et al., J. Inorg. Nucl. Chem. 31: 2587-89, 1969; and Lane A. Bray, et al., U.S. Pat. No. 5,512,256, Apr. 30, 1996).

[0006] Another organophosphorus compound, 2-ethylhexyl 2-ethylhexylphosphonic acid (EHEHPA), was also developed by Peppard (D. F. Peppard, et al., J. Inorg. Nucl. Chem. 18: 245, 1961 and J. Inorg. Nucl. Chem. 27: 2065, 1965). This extractant became widely used to recover yttrium, other rare earths and trivalent actinides, because it was readily stripped with dilute acid. Several investigators have reported a specific preference for EHEHPA over DEHPA for yttrium recovery (Y. Mori, et al., Proc. Symp. Solvent Extr. 119-24, Jpn. Assoc. Solvent Extr. Hamamatsu, Japan, 1984; K. Inoue, et al., Nippon Kogyo Kaishi, 102: 491-4,1984; D. Li, et al., Int. Solvent Extr. Conf. (proc.) 3: 80-202, 1980; D. Li, et al., New Frontiers in Rare Earth Science and Applications, 1: 463-67, 1985; and P. V. Achuthan, et al., Separation Science and Technology, 35: 261-270, 2000).

[0007] The use of neutral organophosphorus compounds for recovery and purification of uranium, actinides and rare earths began in the 1950's (J. C. Warf, J. Am. Chem. Soc. 71: 3257, 1949) with tri-n-butyl phosphate (TBP). Other extractants with phosphine groups were tested in the 1960-70's with some success. The work at Argonne National Laboratory (R. C. Gatrone, et al., Solvent Extr. and Ion Exch. 5: 1075-1116, 1987) in developing a number of compounds of the carbamoylmethylphosphine oxides type led to a class of extractants for removing trivalent, quadri-valent and hexa-valent ions from nitric acid solutions. A number of papers from Argonne National Laboratory and from USSR in the 1980-83 period also demonstrated the use of the this type of extractant (D. G. Kalina, et al, Sep. Sci. Technol. 17: 859, 1981; T. Y. Medved, et al., Acad. Sci. U.S. S. R., Chem. Series, 1743, 1981; E. P. Horwitz, et. al., Sep. Sci. Technol. 17: 1261, 1982; M. K. Chmutova, et al., Sov. Radiochem. Eng. Transl. 24: 27, 1982; E. P. Horwitz, et al., Proceedings ISEC'83 1983; M. K. Chmutova, et al., J. Radioanal. Chem. 80: 63, 1983; A. C. Muscatello, et al., Proceedings ISEC'83, pp. 72, 1983; E. P. Horwitz, et al., Solvent Extr. Ion Exch. 3: 75, 1985; W. W. Shultz, et al., J. Less-Common Metals, 122: 125, 1986; J. N. Mathur, et al., Talanta, 39: 493-496, 1992; J. N. Mathur, et al., Waste Management, 13: 317-325, 1993). When using this technique, the ions are extracted as the metal nitrates from nitric acid solution. The extractants, loaded with the ions, are then back extracted with dilute acids or salt solutions (0.01-0.1N), which causes the ions to strip from the extractant, thereby permitting easy recovery without boil-down of the acids.

[0008] As noted above, 201Tl is produced by decay (electron capture) of its parent isotope, 201Pb. 201Pb is generally produced in a cyclotron by irradiating 203Tl with ˜30 MeV protons (203Tl(p, 3n)201Pb). Separation of 201Tl from the irradiated targets is traditionally performed in two steps. First, radioactive lead is separated from the 203Tl targets, and after an optimal waiting period to allow build up, the accumulated 201Tl daughter is separated from the parent lead isotopes. Various methods for performing the separation have been reported. E. Lebowitz, et al., J, Nucl. Med., 16:151-155 (1975), for example describes a production method in which EDTA complexing agent, hydrazine sulfate and a ion exchange column are first used to separate the lead activities from the thallium targets. Next, an anion exchange column is used to adhere the 201Tl+3 (oxidated by NaClO) and allow the lead activities to be eluted. Finally the 201Tl activity is then eluted with hot hydrazine-sulfate solution, reducing Tl+3 to Tl+1. S. M. Qaim, et al., Int J. Appl. Radiat. Isot., 30: 85-95, 1979, reported a procedure of precipitating quantitatively the carrier-free lead activities by Fe(OH)3 first, followed by an anion-exchange column separation of 201Tl. M. D. Kozlova, et al., Int J. Appl. Radiat. Isot., 35: 685-687, 1984, reported a procedure that includes the co-precipitation of the lead activities as strontium sulfate, followed by solvent extraction using butyl acetate and adding KBrO3 solution. J. L. Q. de Britto, et al., J. Radioanal. Nucl. Chem. Letters, 96: 181-186, 1985, reported a separation based on the properties of a chelating caboxylic acid ion exchange resin-column which at pH 4.5 retains lead while thallium is easily eluted. Both J. A. Campbell, et al., (J. Labelled Compounds and Radiopharmaceuticals, 13:437-443, 1977) and M. C. Lagunas-Solar, et al., (Int J. Appl. Radiat. Isot., 33: 1439-1443, 1982) suggested to use Dowex 50W-X8 system to adsorb lead and thallous ion, while thallic ion is eluted by 0.005N hydrochloric acid containing 0.1% chlorine gas. These methods all tend to be time consuming, hazardous, and expensive.

[0009] To be suitable for use in radiopharmaceuticals, it is also generally important for the radioisotope to be separated from the parent compounds to a high degree of purity. For example, for products containing 90Y, the level of 90Sr should be kept below 10−6Ci per Ci 90Y. Contamination by other metals such as Fe, Cu, Zn, and Ca should also be reduced, because the foreign metallic ions can compete with Y+3 for chelating agents that may be used in the pharmaceutical products. However, many different techniques for the separation of radioisotopes suffer from incomplete separation, and/or contamination by other metals. Consequently, the prior art has failed to provide a simple separation process for producing quality radioisotopes that meet these criteria.

[0010] Also, many of the known techniques have deficiencies in scaling up the separation process due to radiation damages to the materials and devices used in the separation. For example, J. S. Wike, et al., Appl. Radiat. Isot., 41: 861-865, 1990, discloses a separating technique using DEHPA in dodecane to extract 90Y. However, the complexity of the process, which involves repeated stripping of the organic extractant, leads to the accumulation of radiolysis products of the extractant in either the 90Sr stock solution or 90Y product. It is believed that both the DEHPA and radiolytic fragments of organic extractant cause the 90Y to stick to the wall of glass vessels used in the process, resulting in poor recovery of 90Y. Consequently, this method fails to provide a simple 90Sr/90Y separation process for producing quality 90Y in high yields.

[0011] Horwitz, et al., U.S. Pat. No. 5,368,736, discloses another separation technique that is capable of producing high decontamination factor of 90Y. This technique involves immobilizing strontium-selective extractant of hydrophobic crown ether carboxylic acid onto polymeric resin to selectively strip 90Sr away from 90Y after passing a 90Sr/90Y mixture through the crown ether column. The 90Y effluent is further purified by resin that is impregnated with rare-earth selective extractant, which is a mixture of octyl-(phenyl)-N,N-diisobutylcarbamoylmethylphosphine oxide (CMPO) and tri-butyl phosphate (TBP). The above separation technique avoids the use of organic solvent but requires at least three strontium-selective columns for the complete retention of 90Sr, which may limit its potential for multicurie scale-up. In addition this technique requires pH adjustment and volume concentration of 90Y between the crown ether and CMPO/TBP columns, which further complicate the process at the multicurie level.

[0012] Another present commercial method for supplying 90 y involves the extraction of 90Y from a mixture of 90Y and 90Sr using a DEHPA solvent extraction process that requires high concentrations of HNO3 or HCl (8-10 N) to strip the 90Y. When the excess acid is evaporated, the 90Y recombine with trace amounts (1-2 mg/liter) of DEHPA in the 90 y product, which results in loss of product on glassware (J. S. Wike, et al., J. Appl. Radiat. Isot., 41: 861-5, 1990), and in the shipping container. The recombination of 90Y with trace amounts of DEHPA can also result in precipitates, and incomplete tagging of the targeted molecule with 90Y. Consequently, the prior art has failed to provide a simple 90Sr/90Y separation process for producing quality 90Y in high yields.

[0013] What is needed is an improved method and apparatus for simple, low cost, separation of ions of metallic elements in aqueous solution, and, in particular, for separation of radioisotopes from their parent compounds. For example, a method that may be used to separate 90Y from 90Sr to provide 90Y ions with improved purity, concentrations and yields for use in radiotherapy. The process should also not require the use of any organic solvent, should minimize liquid waste discharge and also minimize waste of the radioactive parent

SUMMARY

[0014] In one embodiment of the invention, there is provided a method for separating ions of metallic elements in aqueous solution. The method comprises the steps of providing an ion exchange that comprises a carbon or graphite substrate impregnated with a hydrophobic chelating extractant. The extractant is one that has a greater affinity, at a selective pH, for ions of a first metallic element, than for ions of a second metallic element that is different than the first element. This method further entails the step of providing a solution that comprises ions of said first and second metallic elements, and contacting the solution with the ion exchange, at the selective pH, for a time sufficient for ions of said first element to become bound thereto.

[0015] Another embodiment of the invention provides an ion exchange that comprises a carbon or graphite substrate impregnated with a hydrophobic chelating extractant. The extractant is one that has a greater affinity, at a selective pH, for ions of a first metallic element, than for ions of a second metallic element that is different than the first element, and wherein said first element is bound to said extractant. The method further entails the step of providing a solution at a second selective pH and after a time sufficient for said second element to be produced from radioactive decay of said first element.

[0016] Another embodiment of the invention provides a method for separating ions of metallic elements in an aqueous acid solution by chromatography. This method comprises the following steps.

[0017] (A) Configuring a chromatographic system that comprises two separation columns. Each column contains an ion exchange having a greater affinity for ions of a first metallic element than for ions of a second metallic element at a selective pH. In this embodiment, the selective pH for the two ion exchanges is not the same.

[0018] (B) Providing a feed solution at the selective pH, wherein the feed solution comprises ions of the first and second metallic elements.

[0019] (C) Loading the feed solution onto the first separation column for a time sufficient to allow at least a portion of the first metallic element to bind to the first ion exchange.

[0020] (D) Eluting the first metallic ion from the first ion exchange with a solution having a pH at which the first ion exchange has substantially no affinity for the first metallic ion.

[0021] (E) The eluant from Step (D) may then optionally be adjusted to the second selective pH, at which the second ion exchange has an affinity for the first metallic element.

[0022] (F) The eluant is then loaded onto the second separation column for a time sufficient to allow at least a portion of the first metallic element to bind to the second ion exchange.

[0023] (G) A second eluant is prepared by eluting at least a portion of the first metallic ion from the second ion exchange with an aqueous solution that has a pH at which the second ion exchange has substantially no affinity for the first metallic ion.

[0024] In another embodiment of the invention, a separation column for separating metallic elements is provided. The separation column comprises:

[0025] (a) a body portion having both an inlet and an outlet;

[0026] (b) an ion exchange housed within the body portion, that comprises a carbon or graphite substrate impregnated with a hydrophobic chelating extractant that has a greater affinity, at a selective pH, for ions of a first metallic element than for ions of a second metallic element; and

[0027] (c) a solution at the selective pH, that contains ions of the first and second metallic elements.

[0028] Yet another embodiment of the invention is a 201Tl generator comprising:

[0029] (a) a body portion having an inlet and an outlet;

[0030] (b) an ion exchange housed within the body portion.

[0031] The ion exchange comprises carbon or graphite fibers impregnated with an acidic organophosphorus extractant such as DEHPA, EHEHPA, or di(2,4,4-trimethylpentyl)phosphinic acid (DTMPPA). The ion exchange further comprises ions of 201Pb bound to the extractant.

[0032] Another embodiment of the invention is a 99mTc generator comprising:

[0033] (a) a body portion having an inlet and an outlet;

[0034] (b) an ion exchange housed within the body portion.

[0035] The ion exchange comprises carbon or graphite fibers impregnated with an acidic organophosphorus extractant such as DEHPA, EHEHPA, or DTMPPA. The ion exchange further comprises ions of 99Mo bound to the extractant.

[0036] A further embodiment of the invention provides a chromatographic extraction system that comprises:

[0037] (a) a first column comprising:

[0038] (1) a first body portion having an inlet and an outlet;

[0039] (2) a first ion exchange housed within the body portion, wherein the first ion exchange has a greater affinity for ions of a first metallic element than for ions of a second metallic element at a first selective pH; and

[0040] (b) a second column comprising:

[0041] (1) a second body portion having an inlet and an outlet, wherein the inlet of said second column is in flow communication with the outlet of said first column;

[0042] (2) a second ion exchange housed within the second body portion.

[0043] In this embodiment, the second ion exchange also has a greater affinity for ions of said first metallic element than for ions of a second metallic element, but at a different pH than the first selective pH.

[0044] In a further embodiment of the invention, there is provided a 90Y generator. This generator comprises:

[0045] (a) a first column comprising:

[0046] (1) a first body portion having an inlet and an outlet;

[0047] (2) a first ion exchange housed within the first body portion, wherein the first ion exchange comprises an acidic organophosphorus extractant;

[0048] (3) a feed solution within the first body portion and in contact with the first ion exchange, the feed solution comprising 90Sr ions and having a pH from about 1.5 to 2.5; and

[0049] (b) a second column comprising:

[0050] (1) a second body portion having an inlet and an outlet, wherein the inlet of the second column is in flow communication with the outlet of the first column;

[0051] (2) a second ion exchange within the second body portion, the second ion exchange comprising a neutral or bifunctional organophosphorus extractant adsorbed onto a carbon or graphite substrate.

[0052] Additional embodiments of the invention will be readily apparent to those of ordinary skill in the art upon review of the instant application.

BRIEF DESCRIPTION OF THE DRAWINGS

[0053] The numerous objects and advantages of the present invention may be better understood by those skilled in the art by reference to the accompanying detailed description and the following drawing, in which:

[0054] FIG. 1 is a schematic drawing of a process for separating 90Y from 90Sr.

DETAILED DESCRIPTION

[0055] The present invention provides improved methods and apparatus for separating ions of metallic elements in aqueous solution, thereby providing relatively pure samples of the desired metallic elements for use in a wide variety of applications in a wide number of industries, including mining, environmental decontamination, the pharmaceutical industry, and in the treatment and diagnosis of disease, to name but a few. Separation of ions is achieved with the use of ion exchanges that will preferentially bind ions of one element, while ions of another element remain in solution. As used herein, “separation” and “separating” means that at least about 90%, preferably greater than about 90%, more preferably greater than about 95% and even more preferably greater than about 99% of the ions of one metallic element present in the aqueous solution may be removed from the solution by the ion exchange, while at least about 90%, preferably greater than about 90%, more preferably greater than about 95% and even more preferably greater than about 99% of the ions of another, different metallic element remain in the aqueous solution. In preferred embodiments, solutions may be prepared in which a separation of greater than about 104, more preferably greater than about 106, and still more preferably about 108 may be achieved. In other words, taking the separation of 90Y from 90Sr as an example, using the methods and apparatus described herein, it is possible to obtain a sample of purified 90Y in which the 90Sr/90Y ratio is preferably less than about 10−6, and more preferably less than about 10−8.

[0056] In many applications, the methods and apparatus will be used to separate metallic elements belonging to different Groups in the long periodic table. However, the methods may be adapted to separate elements belonging to the same Group, as well. Groups in the long periodic table include main group elements, including Groups IA, IIA, IIIB, IVB, VB, VIB, transition metals, including Groups IIIA, IVA, VA, VIA, VIIA, VIIIA, IB, and IIB, Lanthanides, including elements with atomic atom from 57 to 71, and Actinides, including elements with atomic number from 89 to 103. Thus, suitable elements which may be separated using the methods and systems of the present invention include, for example, Li, Be, Na, Mg, Al, K, Ca, Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Ge, Rb, Sr, Y, Zr, Nb, Mo, Tc, Ru, Rh, Pd, Ag, Cd, In, Sn, Sb, Cs, Ba, La, Hf, Ta, W, Re, Os, Ir, Pt, Au, Hg, Ti, Pb, Bi, Po, Fr, Ra, Ac, Ku, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Th, Dy, Ho, Er, Tm, Yb, Lu, Th, Pa, U, Np, Pu, Am, Cm, Bk, Cf, Es, Fm, Md, No, and Lw.

[0057] To achieve such ends, the present invention makes use of hydrophobic chelating extractants. Suitable extractants for use in the present invention include: acidic organophosphorus extractants, for example DEHPA, EHEHPA and DTMPPA; neutral organophosphorus extractants, for example TBP and tri-n-octylphosphine oxide (TOPO), bifunctional organophosphorus extractants, for example CMPO and N,N,N′,N′-tetraoctyl-3-oxamentanediamide (TOGDA); basic extractants, for example tri-n-octylamine (TOA) and tricaprylmethylammonium chloride. Other extractants known to those of skill in the art may also be used, including hydroxyoximes, for example 5,8-diethyl-7-hydroxy-6-dodecane oxime and 2-hydroxy-5-nonylacetophenon oxime, crown ethers, for example di-t-butyl-dicyclohexano-18-crown-6, and dithiosemicarbazone.

[0058] Preferably, in the present invention the hydrophobic chelating extractant is adsorbed onto a substrate to provide an ion exchange. In preferred embodiments, the ion exchange is housed in a column. The column will have at least one inlet and at least one outlet. In two column systems, described more fully below, an outlet of the first column may be in flow communication with an inlet of the second column. Additional inlets and/or outlets may be present in either or both columns as well, to add or recover rinse solutions, excess feed solutions, and the like.

[0059] Although a wide variety of different substrates suitable for use in an ion exchange are known in the art, the inventors have discovered that substrates comprising carbon and graphite are particularly well suited to the methods and apparatus of the present invention. While it should not be construed as limiting the invention, it is thought that the hydrophobic interaction between the above-referenced extractants and carbon or graphite substrates is particularly strong, and does not interfere with the chelating portion of the extractants. The carbon and graphite substrates are also thought to have high stability in strong acids and bases, and may be more resistant than other types of substrates to the radiation fields that may be present when using the methods and apparatus of the present invention to separate radioactive metallic elements.

[0060] A variety of such carbon and graphite substrates may be used, including molded graphite and carbon, vitreous (glassy) carbon, pyrolytic graphite and carbon, carbon fibers, carbon composites, and carbon and graphite powders and particles. A common substrate for hydrophobic extractants is carbon coated inorganic materials prepared by decomposition of organic compounds in a 600° C. temperature gas stream, such as ZrO2. It has been suggested that the bonding of organic ionophores to carbon-coated ZrO2 involves not only hydrophobic attraction, but also involves electronic (pi-pi) interaction of the organic ionophore to the graphitic planer structure (Paul T. Jackson et. al, Anal. Chem. 69: 416-425, 1997). This strong bonding prevents leaching of the organic ionophore much better than is observed with polymeric matrixes, such as Chromosorb or XAD adsorbents, or materials coated with cross-linked polybutadiene.

[0061] Pure carbon or graphite fibers, formed at >1500° C., have been found to provide a very good substrate for most hydrophobic extractants commonly used in solvent extraction of the present invention, and are preferred in embodiments of the present invention that utilize carbon or graphite substrates. In preferred embodiments, the carbon or graphite fibers are in the form of carbon or graphite felt. Preferably, this carbon or graphite felt is used with no other substrate. The low bulk density of about 50 mg/cm3 and high surface area (estimated at 30-40 m2/gm) of this product, as well as the ability to selectively bind organophosphorus extractants, allows columns to be prepared that can be operated at fast flow rates, for example from about 1 to about 10 ml/cm2/min, with good performance. Additionally, the felt is easy to cut and pack into columns, is easy to weigh, and adsorbs specific amounts of organophosphorus extractants more predictably than do powdery or granular materials.

[0062] Carbon or graphite felt suitable for use in the present invention may be obtained from commercial vendors (for example, from Fiber Materials, Inc. Biddeford, Me) in the form of ⅛ inch thick sheets. These low density flexible felt materials are produced by the carbonization and graphitization of long, small diameter organic Rayon filaments at 2300° C. to produce a graphite felt with >99.7% purity. This material has only ppm amounts of Cu and S impurities. Preleaching with HNO3 solutions removes these impurities. The felt is dried at 110° C., and then loaded with the desired extractants in methanol solutions. After drying in air, the graphite felt is cut in circular pads using a Shim cutter of a diameter equal to or slightly larger than the diameter of the column. Several graphite felt pads, for example from about 5 to about 15 or more, depending on the size of the column, may be used in each column and compressed slightly to remove any voids.

[0063] The inventors of the present invention have also discovered that the affinity of various chemical organophosphorus extractants for different metallic elements is pH-dependent. For example, organophosphoric acids of the general formula (RO)2P(O)(OH), such as DEHPA, organophosphonic acids of the general formula (RO)RP(O)(OH), such as EHEHPA, and organophosphinic acids of the general formula R2P(O)(OH), such as DTMPPA, have a marked affinity for 90Y at relatively low acid concentrations and may thus be used to extract 90Y from 90Sr under these conditions. Similarly, we have found that DEHPA has an affinity for 201Pb at pH greater than or equal to 2.5, and may thus be used to readily separate 21Pb from 201Tl in a solution having such a pH level. In the presence of concentrated acid solutions, however, acidic organophosphoric extractants lose their affinity for these ions. Thus, a concentrated acid solution, such as a concentrated solution of hydrochloric acid, perchloric acid, sulfuric acid or nitric acid, may be used to elute ions that became bound to the extractant at a higher pH. As used herein, the term “concentrated” when used with regard to an acid refers to a solution having an acid concentration of at least about 4N.

[0064] In contrast, we have found that other organophosphorus compounds, such as CMPO and TBP, require much higher acid concentrations to retain 90Y. Thus, in a concentrated acid solution, 90Y becomes bound to CMPO, and the bound 90Y may then be eluted from the extractant in the presence of a dilute acid solution. As used herein, the term “dilute” when used with regard to an acid solution, refers to a solution having an acid concentration of less than about 0.1N. The discovery of these unique chemical properties have allowed the inventors of the present invention to develop a process and apparatus to separate 90Y from 90Sr wherein the process requires no concentration (evaporation) and acidity adjustments between the column separation of 90Y from 90Sr.

[0065] It has also been found that organophosphoric acids of the general formula (RO)2P(O)(OH), such as DEHPA, organophosphonic acids of the general formula (RO)RP(O)(OH), such as EHEHPA, and organophosphinic acids of the general formula R2P(O)(OH), such as DTMPPA have an affinity for 99Mo at a pH from about 1 to about 2 and may thus be used to readily separate 99Mo from 99mTc in a solution having such a pH level. In the presence of basic solutions, such as sodium hydroxide and ammonium hydroxide, however, these acidic organophosphoric extractants lose their affinity for 99Mo. Thus, a basic solution may be used to elute ions that became bound to the extractant at a lower pH.

[0066] In the present invention, an extractant is used that has a greater affinity for a ions of one metallic element, than for a second metallic element, optionally belonging to a different Group on the long periodic table, at a select pH. As used herein, “greater affinity” means that the affinity of the extractant for ions of the first metallic element, as compared to the affinity for elements of the second metallic element, is greater than about 10:1, preferably greater than about 100:1, more preferably greater than about 1000:1, and even more preferably greater than about 10,000:1.

[0067] In certain embodiments of the invention, the first metallic element is eluted from the extractant by a solution having a second pH, at which the extractant has substantially no affinity for ions of the first metallic element. As used herein, the term “substantially no affinity” means that at such a pH, at least about 75% of any bound ions will be eluted. Preferably, at such a pH at least about 85% of any bound ions will be eluted, and more preferably at least about 95% of any bound ions will be eluted. In particularly preferred embodiments greater than about 95%, and even greater than about 99% of any bound ions will be eluted.

[0068] If the loading of the column with substrate impregnated with extractant is too low, insufficient binding of the first metallic element may occur. If the loading is too heavy, incomplete elution from the extractant may result. Most preferably, the column is loaded with substrate impregnated with extractant to provide greater than about 99% retention of the first metallic element at the selective pH, and greater than about 97% elution of the first metallic element at the second pH. The loading concentration of the extractant is determined experimentally for each extractant, but typically varies from about 0.1 to about 1.0 grams extractant per gram of graphite felt. For example, in one embodiment of the present invention, the optimum loading for EHEHPA is about 0.1 gram per gram of carbon or graphite felt, and for CMPO is about 0.25 gram/per gram of carbon or graphite felt. In this embodiment, EHEHPA on graphite felt at pH 1.5-2.5 allowed 90Y to be recovered from 90Sr as Sr(NO3)2 solution at pH 1.75-2.0 with a ⅜ inch column with >99% recovery, and a 104 separation from 90Sr, with <1% 90Y remaining on the column after elution with concentrated HNO3 solutions. It was found that DEHPA could be used on graphite felt in a similar manner as EHEHPA, but requires more concentrated acid to elute the 90Y. Determination of the optimal loading amounts for other extractants, and other substrates, may be readily determined by those of ordinary skill in the art.

[0069] Carbon or graphite felt has also been found to be a suitable substrate for bifunctional organophosphorus extracants such as CMPO. The CMPO is dissolved in methyl alcohol and dried on the substrate. Carbon or graphite fibers bind the CMPO strongly, and TBP is not needed to retain the CMPO. In an example of one embodiment of the invention, a column 0.325 inches diameter (8 mm) prepared from 15 graphite felt pads ⅛ inch thick loaded with 0.2 to 0.25 gram CMPO per gram of carbon or graphite felt is compressed to about 1.25 inches long. There is very little resistance to flow when the 90Y in 8 N HNO3 solution is loaded and washed with a total of about 30 ml 8 N HNO3. The column is pulled dry with the pump. Because the impregnated felt is very hydrophobic, water is removed efficiently from the column. The 90Y is eluted at a flow rate of 0.5 ml/minute with a minimum of eluant, 3-8 ml. In practice, about 15 ml is used. The eluant is passed though a small (0.325 inch diameter, 1.0-inch long column of XAD-4 to insure removal of any organic and filtered in line with a 0.45 micron filter to remove any particulates. Eluants successfully used in this manner included dilute hydrochloric acid, for example, 0.05 N HCl, dilute nitric acid, for example about 0.01 to about 0.05N HNO3, water, 0.9% NaCl, and various concentrations of ammonium acetate solution. Many other eluants that would be compatible with biochemical solutions can be used as well.

[0070] Thus, in a preferred embodiment of the present invention, a generator system comprised of two columns packed with organic extractant can separate yttrium-90 from stronium-90. The chromatographic extraction system used in the generator consists of an ion exchange column containing acidic organophosphorus extractants such as DEHPA, EHEHPA, or DTMPPA, in flow communication with a second column that contains a second ion exchange comprising a bifuctional organophosphorus extractant such as CMPO or a neutral organophosphorous extractants such as TBP (tri-n-butyl phosphate). Lightweight porous chemically inert carbon or graphite felt is used to absorb the organic extractant and serve as a column matrix. In the separation process, about 0.2M 90Sr(NO3)2 nitrate solution at about pH 1.75 is loaded onto an EHEHPA column. 90Sr ions pass through immediately, but 90Y ions are retained. The 90Sr solution is collected and stored in a shielded container for 90Y grow-in for subsequent separation. After rinses with nitric solution at a pH of about 1.75, the 90Y is eluted with a concentrated acid, such as about 8N HNO3, and passed onto the second column that is connected in series. The eluted 90Y ions are retained on second ion exchange in the second column and are further rinsed with additional concentrated acid. The 90Y ions are then eluted with a dilute acid, such as about 0.01N HNO3, or an ammonium acetate buffer. Both pH 1.75 and 8N nitric acid wash solutions are separated for any residual 90Sr. The decontamination factor for each column is greater than about 104. The 90Sr/90Y ratio in the second eluant is in the range of about 10−8 at time of production date. The 90Y obtained from the above separation has been shown to be of high chemical and radionuclidic purity and can be used for labeling targeted molecules having bearing chelators such as EDTA, DTPA and DOTA.

[0071] Other acidic organophosphorus extractants such as DEHPA and DTMPPA were also tested to separate 90Y from 90Sr. The separation of 90Y from 90Sr could be achieved at pH about 1, about 2 and about 3 when DEHPA, EHEHPA and DTMPPA were used, respectively, which are consistent with the acidic strength of DEHPA, EHEHPA and DTMPPA.

[0072] The elution of 90Y activity from the column was quantitatively similar regardless of which organic extractant was used. It is also preferable to use about 8N HNO3 to elute 90Y off an EHEHPA column and retain it on CMPO column, as any less concentrated HNO3 may result in some loss of 90Y in both columns.

[0073] There are several advantages of the process and apparatus of the present invention over known extracting processes in this field. Firstly, the contact time between the 90Y activity and organic extractant is short, thus eliminating radiolytic breakdown of organic extractant. Secondly, graphite felt is a better absorbent than polymeric resin due to high resistance toward both chemical and radiation damage. Thirdly, because EHEHPA retains 90Y at about pH 1.75 HNO3 and CMPO retains 90Y with concentrated HNO3, the separation is a continuous process and there is no pH adjustment and volume concentration between the two organic extraction columns, which further reduce the process time. Fourthly, no organic solvent is involved in the disclosed process and much less aqueous radio-waste is also generated.

[0074] The quality of 90Y obtained from the above process is suitable for therapeutic applications. The decontamination factor of both EHEHPA and CMPO column is in the order of about 104 and the overall process can achieve an about 108 decontamination factor. ICP analyses show low metal ions contamination. The radiochemical purity of 90Y radiolabeling of DOTA derived biological molecule is equivalent to that of commercial 90Y activity.

[0075] Another embodiment of the present invention involves a generator system and method for providing 201Tl. 201Tl may be provided by radioactive decay of 201Pb. We have discovered that acidic organophosphorus extractants, such as DEHPA, EHEHPA, and DTMPPA have a strong affinity for 201Pb, but not for 201Tl, at pH greater than or equal to about 2.5. Thus, an embodiment of the present invention is provided that comprises a chromatographic column that contains an acidic organophosphorus extractant impregnated on a carbon or graphite substrate, as described elsewhere herein. When loaded with a solution of 201Pb having a pH greater than or equal to about 2.5, the 201Pb is retained on the column. As 201Tl is generated by the decay of the parent isotope, it is released from the extractant into solution. The system is allowed to decay for a time sufficient to provide a predetermined portion of 201Tl, and then rinsed with an aqueous solution having a pH greater than or equal to about 2.5. Suitable rinses include, inter alia, water, dilute hydrochloric or nitric acid, or any biocompatible buffer solution. Preferably, an about 0.9% NaCl solution at about pH 5.5 is used. The efficiency of this generator system, and the fact that 201Tl can be eluted simply with H2O or 0.9% NaCl, provide an advantage over any generator system for 201Tl production described previously.

[0076] Another embodiment of the present invention involves a generator system and method for providing 99mTc. 99mTc can be provided by radioactive decay of 99Mo. We have discovered that acidic organophosphorus extractants, such as DEHPA, EHEHPA, and DTMPPA have a strong affinity for 99Mo, but not for 99mTc, at a pH from about 1 to about 2. Thus, an embodiment of the present invention is provided that comprises a chromatographic column that contains an acidic organophosphorus extractant impregnated on a carbon or graphite substrate, as described elsewhere herein. When loaded with a solution of 99Mo having a pH from about 1 to about 2, the 99Mo is retained on the column. As 99mTc is generated by the decay of the parent isotope, it is released from the extractant into solution. The system is allowed to decay for a time sufficient to provide a predetermined portion of 99mTc, and then rinsed with an aqueous solution having a pH from about 1 to about 2. The absorbed 99Mo, if desirable, can be readily released by a basic solution such as 0.1 N sodium hydroxide or ammonium hydroxide.

EXAMPLES

[0077] The invention is further demonstrated in the following examples. All of the examples are actual examples. The examples are for purposes of illustration and are not intended to limit the scope of the present invention.

Example 1

Separation of 90Y from a 17 mCi 90Sr/90Y generator

[0078] After a 2 week 90Y build-up 0.2 M Sr(NO3)2 pH 1.75 containing 17 mCi 90Sr was loaded onto an EHEHPA column (0.1 g/g-wt. graphite felt) at 2.0 ml/min flow rate. The eluted 90Sr ions were collected in a shielded container. The adsorbed 90Y ions were washed with 30 ml HNO3 pH 1.75 at 2.0 ml/min. The first 3 ml wash was added to the 90Sr solution and the remaining wash solution was collected in a separate waste bottle for recycle of residual 90Sr. 15 ml of 8N HNO3 was used to elute the adsorbed 90Y from the EHEHPA column to a CMPO column (0.25 g/g-wt. graphite felt) at 0.5 ml/min. An additional 15 ml of 8 N HNO3 was used to rinse the CMPO column. 15 ml of 0.01N HNO3 at 0.5 ml/min was used to elute 90Y and 15.77 mCi was collected. The 8N HNO3 load or wash solutions did not contain any 90Y.

Example 2

Separation of 85Sr

[0079] 0.2M Sr(NO3)2 pH 1.75 containing 2.22 mCi 85Sr was loaded onto an EHEHPA column (0.1 g/g-wt. graphite felt) at 2.0 ml/min flow rate. 2.17 mCi 85Sr was eluted and collected in a shielded container. The EHEHPA column washed with 30 ml HNO3 pH 1.75 at 2.0 ml/min, the first 3 ml wash was counted and contained 0.047 mCi 85Sr (˜2%); 0.0021 mCi (˜0.1%) in the next 12 ml wash and 0.0002 mCi (˜0.01%) in the following 15 ml wash. 15 ml of 8N HNO3 was used to elute the EHEHPA column to a CMPO column (0.25 g/g-wt. graphite felt) at 0.5 m/min. An additional 15 ml of 8N HNO3 was used to rinse the CMPO column. Finally 15 ml of 0.01 N HNO3 at 0.5 ml/min was used to elute the CMPO column. There was no detectable 85Sr activity in the CMPO column washes.

Example 3

Separation of 90Y

[0080] 0.2M Sr(NO3)2 pH 1.75 containing 1.31 mCi 90Y was loaded onto an EHEHPA column (0.1 g/g-wt. graphite felt) at 2.0 ml/min flow rate. The Sr(NO3)2 solution was collected and had no 90Y. The adsorbed 90Y on the EHEHPA were rinsed with 30 ml HNO3 pH 1.75 at 2.0 m/min. The wash solution contained no 90Y. 15 ml of 8N HNO3 was used to elute the adsorbed 90Y from the EHEHPA column to a CMPO column (0.25 g/g-wt. graphite felt) at 0.5 ml/min. An additional 15 ml of 8N HNO3 was used to rinse the CMPO column. Neither the load nor wash 8N HNO3 contained any 90Y. 15 ml of 0.5M sodium acetate pH 6 at 0.5 ml/min was used to elute the 1.0 mCi of 90Y collected.

Example 4

Separation of 90Y from a 6.5 Ci 90Sr/90Y generator

[0081] After a 1 week 90Y build-up 0.2M Sr(NO3)2 pH 1.75 containing 6.5 Ci 90Sr was loaded onto an EHEHPA column (0.1 g/g-wt. graphite felt) at 2.0 ml/min flow rate. The eluted 90Sr were collected in a shielded container. The adsorbed 90Y were washed with 30 ml HNO3 pH 1.75 at 2.0 ml/min. 15 ml of 8N HNO3 was used to elute the adsorbed 90Y from the EHEHPA column to a CMPO column (0.25 g/g-wt. graphite felt) at 0.5 ml/min. An additional 15 ml of 8N HNO3 was used to rinse the CMPO column. 15 ml of 0.01N HNO3 at 0.5 ml/min was used to elute 90Y and 4.9 Ci was collected. The ratio of 90Sr to 90Y in the product was ˜10−8.

Example 5

Extraction of Tl-201 with DEHPA Column

[0082] DEHPA (10 pads, 0.325″ in diameter, 0.6 g/g graphite) was packed in a 0.75″×2.75″ glass column and followed by conditioned with 5 mL pH 2.5 and blown dry with 5 mL air. 200 uCi of 201Tl was added to 10 mL of pH 2.5 nitric acid. The pH of the 201Tl solution was measured and adjusted to pH 2.5 with NaOH. There was no 201Tl retained in the column after 10 ml loading followed by 10 ml water wash at 2 mL/min flow rate pumped with peristaltic pump. No 201Tl is retained in the column at other pH, such as 3, 4 and 5.

Example 6

Extraction of Pb-203 with DEHPA Column

[0083] DEHPA (10 pads, 0.325″ in diameter, 0.6 g/g graphite) was packed in a 0.75″×2.75″ glass column followed conditioned with 5 mL pH 2.5 nitric acid and blown dry with 5 mL air. 80 uCi of 203Pb was added to 10 mL of pH 2.5 nitric acid, pH of 203Pb solution was measured and adjusted to pH 2.5 with NaOH. 80 uCi of 203Pb retained in the column after 10 ml loading, followed by 10 ml water wash at 2 mL/min flow rate pumped with a peristaltic pump. Similar results were seen at other pH, such as 3, 4 and 5. Less than 80 uCi of 203Pb was adsorbed in the column when pH is less than 2.

Example 7

Elution of Daughter Tl-201 from Tl-201 Generator

[0084] A 201Tl generator was prepared by loading 20 mL of pH 2.5 nitric acid containing aliquot of irradiated 203Tl target solution on a DEHPA column (10 pads, 0.325″ in diameter, 0.6 g/g graphite), followed by rinsing the column with 20 mL of water. Flow rate was kept at 2 mL/min in the column preparation. The irradiated 203Tl target solution comprises 20 uL 201Pb solution (˜2.38 mCi of Pb-201, determined by Ge (Li)). Eighteen hours later, 221 uCi of 201Tl was collected in 40 mL of water eluant. Additional 24 hours later, 56 uCi of 201Tl was collected in 40 mL of water eluant from the same generator.

Example 8

Extraction of 99Mo with EHEHPA

[0085] A 99Mo solution was prepared by adding 0.5 ml pH 3 99Mo containing 0.94 mCi to 20 ml 0.1N HNO3. The mixture was loaded onto a 2.5 inch glass column packed with 12 pads of graphite felt laced with EHEHPA (0.1 g EHEHPA/g of graphite) at a 5 ml/min flow rate. After loading of the 99Mo activity, 10 ml 0.1N HNO3 was used to rinse the EHEHPA column. 0.83 and 0.02 mCi of 99mTc activity were collected in load and wash fractions respectively. Ge(Li) analysis determined about 0.02 mCi 99Mo was mixed with 99mTc eluates.

Example 9

Extraction of 99Mo with DEHPA

[0086] A 99Mo solution was prepared by mixing 6 mg molybdenum ion and 97 uCi 99Mo in 20 ml 0.1N HNO3. The mixture was loaded onto a DEHPA/graphite column (1.0 g DEHPA/g of graphite) at a 5 ml/min flow rate and 97 uCi of 99mTc activity was collected. Similar results were obtained when no cold molybdenum ion was used. This example demonstrates than an excess of cold molybdenum ion did not interfere with the binding of 99Mo.

Example 10

Extraction of 99Mo with DEHPA

[0087] A 99Mo solution was prepared by adding 0.1 ml pH 3 99Mo containing 1.01 mCi to 20 ml 0.1N HNO3. The mixture was loaded onto a 2.5 inch glass column packed with 12 pads of graphite felt laced with DEHPA (0.2 g DEHPA/g of graphite) at a 5 ml/min flow rate. After loading of the 99Mo activity, 20 ml 0.1N HNO3 was used to rinse the DEHPA column. 0.993 and 0.037 mCi of 99mTc activity were collected in load and wash fraction respectively. The column was eluted again after 23 hours and 0.65 mCi (˜94% yield) of 99mTc was obtained.

[0088] All publications, patents, and patent documents cited herein are incorporated herein by reference for all purposes, as though individually incorporated by reference. The invention has been described with reference to various specific and preferred embodiments and techniques. It should be understood, however, that many variations and modifications might be made while remaining within the spirit and scope of the invention.

Claims

1. A method for separating ions of metallic elements in aqueous solution comprising: providing an ion exchange comprising a carbon or graphite substrate impregnated with a hydrophobic chelating extractant having a greater affinity, at a selective pH, for ions of a first metallic element than for ions of a second metallic element, wherein said first element is different than said second element; providing a solution comprising ions of said first and second metallic elements; and contacting said ion exchange with said solution at said selective pH for a time sufficient for at least a portion of said ions of said first metallic element to become bound thereto.

2. A method according to claim 1, wherein said carbon or graphite substrate is selected from the group consisting of molded carbon or graphite, vitreous (glassy) carbon, pyrolytic carbon or graphite, carbon composites, carbon or graphite powders, carbon or graphite particles, and carbon or graphite fibers.

3. A method according to claim 2, wherein said carbon or graphite substrate comprises carbon or graphite fibers.

4. A method according to claim 3, wherein said carbon or graphite fibers are in the form of carbon or graphite felt.

5. A method according to claim 1, wherein said hydrophobic chelating extractant is selected from the group consisting of acidic organophosphorus extractants, neutral organophosphorus extractants, bifunctional organophosphorus extractants, basic extractants, hydroxyoximes, crown ethers, dithiosemicarbazones, and mixtures thereof.

6. A method according to claim 5, wherein the hydrophobic chelating extractant is an acidic organophosphorus extractant selected from the group consisting of DEHPA, EHEHPA, and DTMPPA.

7. A method according to claim 1, wherein said first metallic element is 201Pb and said second metallic element is 201Tl, and the pH of said aqueous solution in greater than or equal to about 2.5.

8. A method according to claim 7, wherein the hydrophobic chelating extractant is an acidic organophosphorus extractant selected from the group consisting of DEHPA, EHEHPA, and DTMPPA.

9. A method according to claim 8, wherein said acidic organophosphorus extractant is DEHPA.

10. A method according to claim 7, wherein said solution is an aqueous acid solution that comprises an acid selected from the group consisting of hydrochloric acid, perchloric acid, sulfuric acid and nitric acid.

11. A method according to claim 10, wherein said aqueous acid solution comprises nitric acid.

12. A method according to claim 1, wherein said first metallic element is 99Mo and said second metallic element is 99mTc, and the pH of said aqueous solution is from about 1 to about 2.

13. A method according to claim 12, wherein the hydrophobic chelating extractant is an acidic organophosphorus extractant selected from the group consisting of DEHPA, EHEHPA, and DTMPPA.

14. A method according to claim 13, wherein said acidic organophosphorus extractant is DEHPA.

15. A method according to claim 13, wherein said acidic organophosphorus extractant is EHEHPA.

16. A method according to claim 12, wherein said aqueous solution is an aqueous acid solution that comprises an acid selected from the group consisting of hydrochloric acid, perchloric acid, sulfuric acid, or nitric acid.

17. A method according to claim 16, wherein said aqueous acid solution comprises nitric acid.

18. The method according to claim 1 further comprising contacting said ion exchange with a second aqueous solution at a selective pH and after a time sufficient for said second element to be produced from radioactive decay of said first element.

19. The method according to claim 18 wherein said first metallic element is 201Pb and said second metallic element is 201Tl, and the pH of said second aqueous solution in greater than or equal to about 2.5.

20. A method according to claim 19, wherein said second aqueous solution is selected from the group consisting of dilute nitric acid, dilute hydrochloric acid, ammonium acetate buffer, brine, and water.

21. A method according to claim 20, wherein said brine is 0.9% NaCl.

22. The method according to claim 18 wherein said first metallic element is 99Mo and said second metallic element is 99mTc.

23. The method according to claim 22 wherein the pH of said second aqueous solution is from about 1 to about 2.

24. The method according to claim 23 wherein said second aqueous solution is selected from the group consisting of hydrochloric acid and nitric acid.

25. A method according to claim 1, wherein said first metallic element and said second metallic element belong to different Groups in the long periodic table.

26. A method according to claim 1, wherein said first metallic element and said second metallic element belong to the same Group in the long periodic table.

27. A method for separating ions of metallic elements comprising: providing an ion exchange comprising a carbon or graphite substrate impregnated with a hydrophobic chelating extractant having a greater affinity, at a first selective pH, for ions of a first metallic element than for ions of a second metallic element, wherein said first element is different than said second element; and wherein said first metallic element is bound to said extractant; and contacting said ion exchange with an aqueous solution at a second selective pH and after a time sufficient for said second element to be produced from radioactive decay of said first element.

28. A method according to claim 27 wherein said carbon or graphite substrate is selected from the group consisting of molded carbon or graphite, vitreous (glassy) carbon, pyrolytic carbon or graphite, carbon composites, carbon or graphite powders, carbon or graphite particles, and carbon or graphite fibers.

29. A method according to claim 28, wherein said carbon or graphite substrate comprises carbon or graphite fibers.

30. A method according to claim 29, wherein said hydrophobic chelating extractant is selected from the group consisting of acidic organophosphorus extractants, neutral organophosphorus extractants, bifunctional organophosphorus extractants, basic extractants, hydroxyoximes, crown ethers, dithiosemicarbazones, and mixtures thereof.

31. A method according to claim 30, wherein the hydrophobic chelating extractant is an acidic organophosphorus extractant selected from the group consisting of DEHPA, EHEHPA, and DTMPPA.

32. A method according to claim 27, wherein said first metallic element is 201 Pb and said second metallic element is 201Tl, and said first and second selective pH is greater than or equal to about 2.5.

33. A method according to claim 32, wherein said aqueous solution is selected from the group consisting of dilute nitric acid, dilute hydrochloric acid, ammonium acetate buffer, brine, and water.

34. A method according to claim 33, wherein said brine is 0.9% NaCl.

35. A method according to claim 27, wherein said first metallic element is 99Mo and said second metallic element is 99mTc and said first selective pH is from about 1 to about 2.

36. A method according to claim 35, wherein said second selective pH is from about 1 to about 2.

37. A separation column system for separating metallic elements comprising: (a) a body portion having an inlet and an outlet; (b) an ion exchange housed within said body portion, said ion exchange comprising a carbon or graphite substrate impregnated with a hydrophobic chelating extractant having a greater affinity, at a selective pH, for ions of a first metallic element than for ions of a second metallic element, wherein said first element is different than said second element; (c) a solution at said selective pH, said solution comprising ions of said first and second metallic elements.

38. A separation column system according to claim 37, wherein said first and second metallic elements belong to the same Group in the long periodic table.

39. A separation column system according to claim 37, wherein said first and second metallic elements belong to different Groups in the long periodic table.

40. A separation column system according to claim 37, wherein said carbon or graphite substrate is selected from the group consisting of molded carbon or graphite, vitreous (glassy) carbon, pyrolytic carbon or graphite, carbon composites, carbon or graphite powders, carbon or graphite particles, and carbon or graphite fibers.

41. A separation column system according to claim 38, wherein said carbon or graphite substrate comprises carbon or graphite fibers.

42. A separation column system according to claim 41, wherein said carbon or graphite fibers are in the form of carbon or graphite felt.

43. A separation column system according to claim 37, wherein said hydrophobic chelating extractant is selected from the group consisting of acidic organophosphorus extractants, neutral organophosphorus extractants, bifunctional organophosphorus extractants, basic extractants, hydroxyoximes, crown ethers, dithiosemicarbazones, and mixtures thereof.

44. A separation column system according to claim 43, wherein the hydrophobic chelating extractant is an acidic organophosphorus extractant selected from the group consisting of DEHPA, EHEHPA, and DTMPPA.

45. A separation column system according to claim 44, wherein said first metallic ion is 201Pb and said second metallic ion is 201Tl, and the pH of said solution is greater than or equal to about 2.5.

46. A separation column system according to claim 44, wherein said first metallic ion is 99Mo and said second metallic ion is 99mTc, and the pH of said solution is from about 1 to about 2.

47. A 201Tl generator comprising: (a) a body portion having an inlet and an outlet; and (b) an ion exchange housed within said body portion, said ion exchange comprising carbon or graphite fibers impregnated with an acidic organophosphorus extractant selected from the group consisting of DEHPA, EHEHPA, and DTMPPA, and said ion exchange further comprising ions of 201Pb bound to said extractant.

48. A 201Tl generator according to claim 47, further comprising: (c) an aqueous solution having a pH of greater than or equal to about 2.5 within said body portion and in contact with said ion exchange, said aqueous acid solution containing 201Tl that has been produced by radioactive decay of said 201Pb.

49. A 201Tl generator according to claim 48, wherein the pH of said aqueous solution is about 5.5.

50. A 201Tl generator according to claim 48, wherein said acidic organophosphorus extractant comprises DEHPA.

51. A 201Tl generator according to claim 48, wherein said aqueous solution is selected from the group consisting of dilute nitric acid, dilute hydrochloric acid, ammonium acetate buffer, brine, and water.

52. A 201Tl generator according to claim 51, wherein said brine is 0.9% NaCl.

53. A 99mTc generator comprising: (a) a body portion having an inlet and an outlet; and (b) an ion exchange housed within said body portion, said ion exchange comprising carbon or graphite fibers impregnated with an acidic organophosphorus extractant selected from the group consisting of DEHPA, EHEHPA, and DTMPPA, and said ion exchange further comprising ions of 99Mo bound to said extractant.

54. A 99mTc generator according to claim 53, further comprising: (c) an aqueous solution having a pH of from about 1 to about 2 within said body portion and in contact with said ion exchange, said aqueous acid solution containing 99mTc that has been produced by radioactive decay of said 99Mo.

55. A 99mTc generator according to claim 54, wherein the pH of said aqueous solution is about 1.

56. A 99mTc generator according to claim 54, wherein the pH of said aqueous solution is about 2.

57. A 99mTc generator according to claim 54, wherein said aqueous solution is selected from the group consisting of hydrochloric acid and nitric acid.

58. A 99mTc generator according to claim 53, wherein said acidic organophosphorus extractant comprises DEHPA.

59. A 99mTc generator according to claim 53, wherein said acidic organophosphorus extractant comprises EHEHPA.