The present invention relates to a method for the treatment of steel mill slag (i.e. slag generated during steel production), in particular of the so-called “black slag”, containing lime or lime-based compounds, silicates, aluminates as well as other oxides in lower percentages coming out of an electric furnace for the production of steel. The present invention also relates to an apparatus for implementing said method.
Therefore, the method and the apparatus for treating the slag according to the present invention find advantageous use in the technical sector of steel production and, more particularly, in the treatment of the black slag that is generated inside the electric furnace.
As is known, the electric arc furnace, used in the steel industry to produce steel starting from ferrous scrap, generates a further material called “steel mill slag” or “black slag”, which forms above the melting pool of the steel, as a result of the oxidation of the scrap and of the compounds generated by the additives inserted in the charge of the electric furnace.
Currently, as shown in
Subsequently, the black slag thus discharged into the cauldron 3 or on the ground is loaded and transported by first means 4 to a collection area 5, generally in a hole, possibly with initial sedimentation in the form of a chute.
In the collection area 5 the black slag is cooled by sending jets of water directly onto the slag itself. By coming into direct contact with the slag, the resulting water used for cooling said slag constitutes a polluting leachate for the environment that must be collected and treated by means of an appropriate plant.
Once cooled, the slag is then suitably deferred (for example by means of a magnet) to remove the largest and most evident pieces of iron.
Subsequently, the slag thus obtained is loaded and transported by second means 6 to a storage area 7 where it remains for a period generally from three to six months in order to obtain the complete extinguishing of the residual live crush present in the slag itself. The storage area 7 must have an extremely wide extension and this to allow the storage of the slag for at least three to six months, slag that is continuously generated during the subsequent work cycles of the furnace 2 which operates 24 hours a day for all days of the week. Furthermore, the storage area 7 must be equipped with a plant for collecting and treating the leachate deriving from rainwater to which the slag that remains in the storage area 7 for at least three to six months is inevitably subjected. The storage area 7 must also be lined with suitable flooring.
From the storage area 7 the slag thus obtained is loaded and transported by third means 8 towards a crushing apparatus 9 and subsequent screening 10 (with possible further iron removal) to separate the final product into various groups 11 based on the size of the grains resulting from the crushing.
Conveniently, the final product obtained from the slag thus treated can therefore be used as a secondary raw material for subsequent applications, for example as an inert aggregate for the production of asphalt, various concrete products, or as a starting material for the construction of the road flooring and in general of non-structural road works.
In this process, the stabilization phase of the black slag in the storage area 7 is essential, in order to obtain the complete extinguishing of the residual quicklime present in the slag itself, and thus avoid that said lime subsequently swells when it comes into contact with water (for example rainwater), thus causing undesirable damage to the asphalt or to the artifacts containing the product obtained from the aforementioned treatment of the black slag.
It is easy to understand how the traditional method for the treatment of black slag in order to obtain a product to be reused in other applications, and in particular as a secondary raw material, is particularly long, as well as requiring various means of handling (with inevitable consumption and costs), plants for the treatment of leachate and extremely large spaces.
GB1534528 describes a solution in which the melted slag from the blast furnace at a temperature of about 1300° C. is introduced into a rotating tubular cooling reactor, where it remains for a period of time of 2.5-6.5 minutes, to thus exit said reactor in the form of small pieces at a temperature of about 1000-1100° C. and thus pass directly inside a heat exchange tower to recover the heat of said pieces which, leaving the tubular cooling reactor, are still at a particularly high temperature.
WO2009/116684 describes a solution in which the cooling fluid is exclusively sprayed directly on the black slag to be cooled.
WO2009/069794 describes a solution in which the high temperature black slag leaving the electric furnace is first discharged into a hole where a first cooling takes place.
The purpose of the invention is to propose a method and/or an apparatus for treating the black slag, in particular the slag that is generated in the electric furnace in the steel production phase, which allow/allows to overcome, at least in part, the drawbacks of the known solutions.
Another purpose of the invention is to propose a method and/or apparatus for treating the black slag capable of increasing energy efficiency, while maintaining high quality standards (in particular in terms of stability) of the material obtained and of safety for operators and equipment.
Another purpose of the invention is to propose a method and/or an apparatus for treating the black slag that allow/allows to obtain a high quality final product (in particular in terms of stability), to be used as a secondary raw material for subsequent and various applications.
Another object of the invention is to propose a method which allows to considerably reduce the spaces required for the treatment of the black slag.
Another object of the invention is to propose a method which reduces or avoids the movement of the black slag between various zones and/or stations.
Another object of the invention is to propose a method which does not require means for loading and moving the black slag between various areas and/or stations.
Another object of the invention is to propose a method which allows to reduce the treatment costs of the black slag.
Another object of the invention is to propose a method which allows to considerably reduce the times for the treatment of the black slag.
Another object of the invention is to propose a method which is highly eco-compatible.
Another object of the invention is to propose a method and/or an apparatus that does not require/require the implementation of plants for the treatment of leachate.
Another object of the invention is to propose a method and/or an apparatus that do/does not require the construction of complex and expensive structural or cladding/flooring works.
Another object of the invention is to propose a method and/or an apparatus which is/are usable/s substantially in all steel mills.
Another object of the invention is to treat the black slag in much smaller spaces.
Another object of the invention is to propose a method and/or an apparatus for treating the black slag that allow/allows to obtain a high energy efficiency.
Another object of the invention is to propose an apparatus for the treatment of the black slag which is constructively completely reliable.
Another object of the invention is to propose a black slag treatment apparatus which is resistant and robust.
Another object of the invention is to propose a method and/or an apparatus for the treatment of the black slag which is/are easily implementable and with low costs.
Another object of the invention is to propose an apparatus which is quick and easy to maintain and which, at the same time, allows to improve the energy efficiency in the recovery of the black slag, while at the same time maintaining high quality standards of the material obtained.
Another object of the invention is to propose a method and/or an apparatus for treating the black slag which is/are alternative/and improved with respect to the known solutions.
All these objects, considered both individually and in any combination thereof, and others which will result from the following description, are achieved, according to the invention, with a method of treating the black slag with the characteristics indicated in claim 1.
The present invention is further clarified hereinafter in some of its preferred embodiments reported for purely illustrative and non-limiting purposes with reference to the attached drawing tables, in which:
The present invention relates to a method and an apparatus, indicated as a whole with the reference number 15, for the treatment of black slag 1 or steel mill slag, which contains lime or lime-based compounds and which is generated in the electric furnace 2, preferably arc furnace (also known as “EAF”), which is used in the steel industry to produce steel starting from ferrous scrap.
In particular, the term “black slag” 1 hereinafter refers to the slag that forms above the steel melting bath, as a result of the oxidation of the scrap and of the compounds generated by the additives inserted in the charge of the electric furnace to produce steel starting from scrap. In particular, the black slag 1 is a waste material that contains various components and, in particular, contains lime (CaO) or lime-based compounds, and, therefore, is advantageously recoverable. Conveniently, the black slag 1 is about 70-95%, preferably about 80-90%, formed by the following components: CaO (lime), FeO, SiO2 and Al2O3; suitably, the quantities of the individual components vary according to the composition of the black slag.
Advantageously, the apparatus 15 according to the present invention can be operatively associated with a steel production plant and/or its derivatives or variants.
Conveniently, the apparatus 15 according to the present invention is suitable for use in a plant for the recovery of the black slag 1 that is generated inside the electric furnace 2 in the steel production phase.
The method according to the invention provides for cooling the black slag 1 leaving the electric furnace 2.
Preferably, the method according to the invention provides for immediately cooling the black slag 1 leaving the electric furnace 2 or for cooling it after its collection in a cauldron 3.
Preferably, the method according to the invention provides for cooling the black slag 1 immediately after its exit from the electric furnace 2 or immediately after its collection in a cauldron 3. Conveniently, this can be achieved by directly discharging the black slag 1 at the outlet from the electric furnace 2 inside a cooling device 20, or by unloading the black slag 1 exiting the electric furnace 2 first inside a cauldron 3 and then unloading it from the latter directly into a cooling device 20. Conveniently, the black slag 1 can remain in the cauldron 3 as long as it remains in the liquid or fluid state.
Conveniently, the method provides for cooling the black slag 1 leaving the electric furnace 2 and which is at a temperature corresponding to or close to the melting temperature of the steel, i.e. it is at a temperature of about 1400-1800° C., preferably of about 1600° C.
Preferably, in a possible implementation variant, the method according to the invention provides for cooling the black slag 1 immediately after being discharged, at the outlet from the electric furnace 2, into a cauldron 3.
Conveniently, the black slag 1 at the outlet from the electric furnace 2 is cooled indirectly, i.e. by indirect contact between the black slag and a cooling fluid (for example air and/or water).
Conveniently, for this purpose, the black slag 1 is discharged into a device 20 for cooling the black slag. Preferably, the black slag 1 exiting the electric furnace 2 is discharged into a device 20 for indirect cooling of the black slag, i.e. a device which is configured to cool the black slag in the face of an indirect (i.e. non-contact) heat exchange between the black slag 1 which enters and/or passes through the device and a cooling fluid which enters and/or passes through said device 20.
Preferably, the cooling device 20 is a tubular reactor.
Preferably, the cooling device 20 is a rotating tubular reactor. In a possible embodiment, the cooling device 20 comprises a rocking reactor. In a possible embodiment, the cooling device 20 comprises a vibrating reactor. In a possible embodiment, the cooling device 20 comprises a floating reactor.
Conveniently, the black slag 1 that is generated in the electric furnace 2 is discharged (generally due to the rotation of the furnace) directly and immediately inside the cooling device 20. In particular, the cooling device 20 is positioned and/or can be positioned at the exit of the black slag from the furnace 2.
Conveniently, the black slag 1 that is generated in the electric furnace 2 is first discharged into a cauldron 3 and then from the cauldron 3 is unloaded directly (i.e. without any passage in the hole) to the interior of the cooling device 20.
Preferably, the cooling device 20 can be movable. Preferably, the cooling device 20 is self-propelled or towed.
Advantageously, the cooling device 20 can be mounted on a support structure provided with movement means, such as wheels or tracks, to thus allow the movement of the cooling device towards/away from/to the furnace 2 and/or in correspondence with the furnace 2.
Conveniently, the cooling device 20 of the black slag treatment apparatus 15 can comprise a wall which internally delimits a chamber 16 for receiving and passing through the black slag to be cooled, extending between an inlet opening for the slag to be cooled and an outlet opening for the cooled slag.
Preferably, the inlet opening of the cooling device 20 receives the black slag 1 which exits directly from the electric furnace 2. In a possible alternative embodiment, the inlet opening of the cooling device can receive the black slag 1 from a cauldron 3 which, in turn, receives said black slag directly from a corresponding outlet of the electric furnace 2.
Conveniently, in the method according to the invention, the black slag 1 leaving the electric furnace 2 is never discharged into a hole, and in particular, it is not discharged into a hole before it enters the cooling device 20.
Conveniently, in the method according to the invention, the black slag 1 leaving the cooling device 20 is not discharged or moved inside a cooling tower heat exchange. Preferably, the black slag 1 leaving the cooling device 20 is ready to be crushed and sieved.
Conveniently, the cooling device 20 can comprise a loading hopper (not shown) for conveying the black slag 1 into the device itself directly from the outlet of the electric furnace 2 and/or immediately after its exit from said furnace and/or after its collection in a cauldron 3.
Advantageously, in correspondence with the inlet opening of the cooling device 20, a preferably vibrating protection grid can be provided to prevent any pieces of not yet melted scrap present on the furnace.
In a preferred embodiment, the cooling device 20 of the black slag treatment apparatus 15 can comprise at least one rotating reactor (or drum), substantially tubular (preferably cylindrical), equipped with at least one wall which internally delimits a chamber 16 for receiving and crossing the black slag to be cooled, extending between an inlet opening for the slag 1 to be cooled and an outlet opening for the cooled slag.
Advantageously, the cooling device 20 can comprise a rotating reactor for treating the slag which can be of any traditional type and, for example, can be of the type described in EP3247811 or EP3323898.
Preferably, the cooling device 20 comprises cooling means (not shown) of the wall which delimits the chamber 16 inside it, to thus indirectly cool the material (black slag) that passes through said chamber.
Conveniently, the cooling device 20 comprises means for indirectly cooling the black slag that passes through said chamber 16 and, in particular, these means may comprise:
Preferably, said cooling means of the supply device 20 can comprise at least one distribution circuit for the cooling fluid arranged at least partially around the device and configured to receive a cooling fluid (preferably water) from the supply means.
Operationally, the cooling fluid acts on the wall of the chamber 16 in such a way as to cool said wall, and consequently also indirectly cool the black slag contained in said chamber.
Advantageously, the apparatus 15 according to the invention further comprises means for feeding at least one cooling fluid (preferably water) to the cooling means (not shown) of the cooling device 20.
Conveniently, the means for feeding the cooling fluid are fluidically connected at the inlet to the cooling means to thus supply the latter with the cooling fluid.
Preferably, the cooling fluid supply means comprise at least one fluidic circuit which is connected at the inlet with an external supply, in particular mains water, of the cooling fluid, while at the outlet it is connected with the cooling means of the device.
Conveniently, the method according to the invention provides for cooling, preferably indirectly, the black slag 1 leaving the electric furnace 2, and which is at a T1 of about 1400-1800° C., until it reaches at least an intermediate temperature or final T2 (which is less than T1).
Conveniently, the intermediate or final temperature T2 is the temperature at which the phase change of stable mineralogical structures containing lime (CaO) or lime-based compounds occurs, cf.
The temperature T2 varies according to the composition of the black slag itself and, for example, can be around 500-1200° C.
In a possible embodiment, the black slag 1 can comprise a calcium-based compound, in particular the dicalcium silicate (which has a stable β form between 675° C.-1420° C.), and suitably the black slag 1 at the outlet from the electric furnace 2, and which is at a T1 of about 1400-1800° C., is cooled so as to obtain the stable formation of the dicalcium silicate in its β phase.
Conveniently, the transition from temperature T1 to temperature T2 is particularly rapid, in order to avoid or thus decrease the formation/presence of free lime in the cooled slag.
Conveniently, the method according to the invention provides for cooling, preferably indirectly, the black slag 1 leaving the electric furnace 2, and which is at a T1 of about 1400-1800° C., until it first reaches said intermediate temperature T2 and then until it reaches a final temperature T3 which is suitable for the subsequent handling of the slag 1. In particular, for example, the final temperature T3 is equal to or lower than about 150°-300° C., preferably it is equal or less than about 70°−100° C.
Conveniently, the inlet temperature of the black slag in the cooler 20 corresponds to the temperature T1, while the outlet temperature of the black slag from the cooler 20 may correspond to the temperature T2 or T3.
Preferably, the outlet temperature of the black slag from the cooling device 20 corresponds to the temperature T3 which is suitable for the subsequent handling of the slag 1; preferably, the final temperature T3 is equal to or lower than about 150°-300° C., preferably it is equal to or lower than about 70°−100° C.
Conveniently, T2 is of/to T3. Basically, the temperature T2 can correspond to the final cooling temperature that the black slag reaches at the outlet of the cooler, or it can correspond to an intermediate cooling temperature that is higher than the temperature T3 that the black slag reaches at the outlet of the cooler.
Conveniently, in the method according to the invention the cooling rate of the black slag is such that the mineralogical structures stable at high temperature (i.e. at temperatures higher than T2) remain stable even at lower temperatures (i.e. at temperatures lower than T2), as it results from the diagram of
Conveniently, in the method according to the invention, the indirect cooling of the black slag leaving the electric furnace is carried out in a time shorter than the duration of the steel melting cycle inside the electric furnace and, in particular, takes place in less than approximately 30-45 minutes and, in particular, takes place in a time between about 10 and about 30 minutes. Appropriately, the indirect cooling of the black slag leaving the electric furnace is carried out for a time interval ranging from a minimum of about 10 minutes to a maximum of about 30-45 minutes.
Conveniently, the indirect cooling of the black slag leaving the electric furnace 2 is carried out inside the cooling device 20 for a time interval ranging from a minimum of about 10 minutes to a maximum of about 30-45 minutes, preferably in a time interval between about 10 minutes and about 30 minutes.
Preferably, the cooler is configured so that the cooling rate of the black slag—and in particular the time of passage of the black slag from the temperature T1 (which corresponds to the inlet temperature of the black slag into the cooler) to the temperature T2 or T3 (which also corresponds to the outlet temperature of the black slag from the cooler)—is less than the duration of the steel melting cycle inside the electric furnace and, in particular, takes place in less than about 30-45 minutes and, preferably, takes place in a time interval comprised between about 10 and about 30 minutes, in particular according to the chemical composition of the black slag and/or the steel.
Conveniently, the cooling of the black slag inside the cooling device 20, and in particular the residence time of the black slag inside said device, is carried out in a time shorter than the duration of the melting cycle of the steel. inside the electric furnace and, in particular, takes place in less than about 30-45 minutes and, preferably, takes place in a time interval between about 10 minutes and about 30 minutes, in particular depending on the chemical composition of the black slag and/or steel. Advantageously, this allows the cooling device to be promptly released from the cooled black slag, in order to be able to receive the black slag generated in the subsequent melting cycle.
Conveniently, in the method according to the invention, the black slag leaving the electric furnace is loaded discontinuously into the cooling device 20 which, therefore, is configured to work in “batch”. Preferably, the loading time of the black slag 1 to be cooled in the cooling device 20 is equal to or less than about five minutes, and more preferably it is equal to or less than about two minutes.
The method according to the invention then provides that the cooled black slag is crushed into pieces of various sizes, and subsequently sieved, to thus separate the finer pieces from the larger ones into two or more groups, that is, so as to separate into two or more groups the pieces having a smaller or larger size than at least one predetermined size.
The treatment apparatus 15 according to the invention comprises, downstream of the cooling device 20, a crushing module 9 for the cooled slag into pieces of various sizes and a sieving module 10 to thus separate the finer pieces from the larger ones into two or more groups 11, i.e. so as to separate into two or more groups the pieces having a size smaller or larger than at least one predetermined size.
Conveniently, in a possible embodiment of the cooling apparatus 15 (see
Conveniently, in another possible embodiment of the cooling apparatus (see
Advantageously, in a possible embodiment, the black slag 1 leaving the furnace 2 is mixed inside the cooling apparatus with known additives, for example inert materials (silicates, aluminates or others), to capture the any free lime (CaO), or its compounds, present in the slag itself.
Advantageously, in a possible embodiment, the feeding means of the cooling device 20 receive the cooling fluid from the same water network that feeds a steel production plant and/or the like.
The cooling fluid advantageously comprises water, in particular already used or usable in the steel production plant.
More in detail, the feeding means of the cooling device 20 take the high-pressure cooling fluid from an upstream plant, in particular from a steel production plant and transport it to the cooling means of the cooling device 20.
Advantageously the chamber 16 of the cooling device 20 is configured to advance the material to be cooled (i.e. the black slag) in a first direction of movement. Conveniently, the cooling means can be configured to move the cooling fluid from an inlet section to said outlet section in a second direction at least partially opposite to said first direction. In particular, the cooling fluid acts externally on the chamber 16 crossing it along its longitudinal development in a direction which is opposite to that with which the black slag 1 to be cooled crosses/advances inside said chamber.
In accordance with a preferential embodiment, the reactor of the cooling device 20 preferably has a substantially cylindrical shape and extends along a main axis X between a first end (not shown), in which the inlet opening is provided, and a second end, in which the outlet opening 5 is made. Conveniently, the cooling device 20 comprising a tubular reactor rotating around its longitudinal development axis X. Preferably, the first direction of movement of the slag to be cooled is substantially parallel to the main axis X and facing from the inlet opening towards the outlet opening.
Advantageously, the reactor of the cooling device 20 is made of thermally conductive material, in particular it is made of metallic material, such as for example steel.
Conveniently, in order to cool the black slag in an optimal manner, the reactor 2 is rotatably mounted on a support structure and can be rotated about the main axis X by motorization means.
Advantageously, the support structure is intended to be rested on the ground and comprises at least one lower support base and is preferably made of metallic material.
Preferably, the support structure supports the reactor in such a way that its main axis X is substantially horizontal or is at least partially inclined, from a greater height in correspondence with the inlet opening, to a smaller height in correspondence with the outlet opening. Conveniently, further motorization means (not shown) can be provided to vary the inclination of the reactor with respect to the horizontal.
Conveniently, the cooling device 20 comprises at least one electronic control unit (not shown) which is electronically connected to the motorization means and programmed to control them to vary the rotation speed of the reactor and/or the inclination of the reactor with respect to the horizontal. Preferably, the electronic control unit is programmed to control the rotation of the reactor in a first direction of rotation, for example clockwise, or counterclockwise. Conveniently, the electronic control unit can be programmed to rotate the reactor in more than one direction of rotation, alternately, in order to mix the black slag inside the chamber 16 and increase the cooling efficiency of the device 20.
Conveniently, the cooling device 20 comprises at least one temperature sensor operatively associated with the reactor, electronically connected to the electronic control unit and configured to detect at least one temperature measurement of the reactor and/or of the black slag to be cooled. The electronic control unit is advantageously configured to receive the temperature measurement and correspondingly control the motorization means for varying the rotation speed of the reactor and/or the inclination of the reactor.
Advantageously, the electronic control unit comprises at least one microcontroller, such as for example a PLC (programmable logic controller) or the like. Preferably, the electronic control unit further comprises at least one processing module programmed to process the temperature measurement and the flow measurement and generate a corresponding first control signal for the drive means.
Conveniently, the electronic control unit can be connected to the sensors and to the motorization means in any manner known per se to those skilled in the art and therefore not described in detail below. For example, the electronic control unit may provide a wired connection or a wireless connection without thereby departing from the protection scope of this patent.
Advantageously, in a possible embodiment, the treatment apparatus 15 of the black slag comprises a unit for sending a nebulized cooling fluid (preferably water), for example by means of compressed air, directly on the black slag 1 leaving the furnace 2, preferably from the electric furnace. Conveniently, in a possible embodiment, the unit for sending a nebulized cooling fluid can be provided at the outlet of the black slag 1 from the furnace 2, and be positioned upstream and externally with respect to the device for indirect cooling 20 of the black slag. Conveniently, in a possible embodiment, the unit for sending a nebulized cooling fluid can be provided inside—and preferably at the inlet—of the device for indirect cooling 20 of the black slag.
Conveniently, the method according to the invention provides for cooling the black slag 1 leaving the electric furnace 2 indirectly and/or by direct contact with a nebulized cooling fluid, in particular with nebulized water, for example by means of compressed air. Preferably, the method according to the invention provides for cooling the black slag 1 leaving the furnace 2 first by means of a nebulized cooling fluid and subsequently by indirect cooling (i.e. by indirect heat exchange between a cooling fluid and the black slag). Conveniently, the nebulized cooling fluid can be the same or even different from the cooling fluid used for indirect heat exchange.
Conveniently, in one of its possible embodiments, the method according to the invention provides for cooling the black slag 1 leaving the furnace 2 by means of a jet/spray of a mix (for example an aerosol) of a gas (preferably air or other inert gas) and drops of a liquid (preferably water or other coolant). In particular, this mix of gas and liquid is sent directly onto the black slag 1. Conveniently, the gas acts mainly or only as a transport carrier for the drops of coolant (preferably water) so that, going into direct contact with the black slag, said drops of liquid cause the latter to cool and at the same time evaporate (i.e. change state), thus avoiding the need to set up a plant for collecting the leachate for the liquid. Advantageously, moreover, the use of a mix of air and water allows to reduce the amount of air used compared to known solutions in which air alone is used, and also avoids excessive consumption of water (which instead is at least an order of size lower than the water consumption required in case of indirect cooling, i.e. about the order of tens of liters per minute).
Conveniently, for this purpose, a module (not shown) can be provided configured to generate and send a jet/spray of said mix of gas and liquid drops towards the black slag 1 leaving the furnace 2. Advantageously, said module is configured so that the jet/spray of said mix of gas and liquid drops pushes the black slag coming out of the furnace against a wall of a container, so that the black slag cooled by the liquid drops then falls back onto a conveyor belt to make it thus advance towards the modules or subsequent treatment stations (crushing 9 and/or sieving 10).
Conveniently, said module can be provided in place of and/or in addition to the indirect cooling device 20 of the black slag 1. Conveniently, said module can be provided externally to the cooling device 20 and be positioned at the inlet/upstream with respect to the means of indirect cooling of the black slag. Conveniently, said module can be provided externally to the cooling device 20 and be positioned at the inlet/upstream with respect to the indirect cooling means of the black slag.
Conveniently, the method according to the invention therefore provides for a particularly rapid cooling—preferably in a time of less than about 30-45 minutes, more preferably in a time of between about 10 minutes and about 30 minutes depending on the chemical composition of the black slag and/or steel—the black slag immediately exiting directly from the electric furnace or immediately after the collection of said black slag in a cauldron 3. Conveniently, the faster the cooling, the lower the quantity of free lime, or its compounds, present in the cooled slag.
As is clear from what has been described, the method and/or the apparatus according to the invention is particularly advantageous, since:
In particular, the method according to the present invention differs from the solution of GB1534528 in that it provides indirect cooling of the black slag for a period of time between about 10 minutes and about 30-45, it differs from the solution of WO2009/116684 in that provides indirect cooling and also differs from the solution of WO2009/069794 in that it provides for cooling the black slag immediately after its exit from the electric furnace or its collection in a cauldron, thus avoiding unloading and preliminary cooling in a hole.
The present invention has been illustrated and described in some of its preferred embodiments, but it is understood that executive variations may apply thereto in practice, without however departing from the scope of protection of the present patent for industrial invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 102021000004892 | Mar 2021 | IT | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2022/051800 | 3/1/2022 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20240132980 A1 | Apr 2024 | US |