Patent Application
20180214885
The invention relates to a method for transforming solid urban waste into aggregates. The invention also relates to an apparatus for transforming solid urban waste into aggregates.
Even in developed countries the collection, transport, separation and final disposition of the components of solid urban waste is both an economic and environmental problem since, in an ideal situation, the 100% of solid urban waste should be recycled for reuse: as raw material, as a source of valuable elements, etc.
For example, in the case of glass, plastics and metals, as raw material for manufacturing new containers: bottles, vessels, cans, etc.
In the case of organic matter of biological origin, for example, as raw material for preparing balanced feed, manure and fertilizers.
In less developed or developing countries, the collection, transport and final disposition of solid urban waste usually ends up in the formation of huge open dumps or dumps covered with a layer of soil.
In general, the invention relates to the treatment, recovery and recycling of those components that are part of solid urban waste.
Particularly, the present invention refers to a method and an apparatus for transforming organic and inorganic solid urban waste into aggregates once the batteries, ferrous and non-ferrous metal components, non-contaminated bottles, glass and plastic containers and possibly any organic or inorganic material that, owing to its hardness or volume—such as cobblestone and hard wood pieces—is not adequate for being treated by the process of the present invention, have been previously separated. The remaining waste that may not be recycled is referred to as ‘rejection’.
Rejection is understood as those organic and inorganic elements that, as a result of being inappropriately managed, are cross-contaminated and cannot be recycled, and which are generally buried.
The aim of this invention is to solve the problem that arises from this rejection.
In the context of the present invention, the expression ‘organic and inorganic solid urban waste’ means a combination of waste of mainly biological origin generated by people as a result of food consumption.
Examples of this waste are bones, meat remainders, cartilages, greases, oils, vegetables, fruits, cereals, oil plants, infusions, etc., generally accompanied by remaining inorganic waste, such as bags and plastic, paper, cardboard and glass containers, which are contaminated with organic waste.
On the other hand, in the context of the present invention, the term “aggregate” means a granulated, sterile, dry product of petrous nature, such as rubble and stones, which comply with the EPA SW486 and EPA 1310 standards. That is, a product that will be suitable for use in mortars and road backfills.
The object of the invention is a method for transforming solid urban waste into aggregates, comprising:
a selection and preparation stage of a rejection from solid waste, obtaining a parget characterised in that it comprises:
a feeding stage of an apparatus for transforming organic and inorganic solid urban waste into aggregates, said apparatus comprising an extruding machine and a reactor, wherein the extruding machine comprises an extrusion cylinder through which a piston circulates inside an extrusion cavity that defines an extrusion axis; the end of the extrusion cavity is hermetically connected to the reactor; the longitudinal shaft of the reactor comprises a rotatory shaft in which some blades are arranged; between the end of the blades and the wall or dome of the reactor there is a clearance, which is referred to as the boundary layer of the reactor; the rotatory shaft of the reactor and the blades are jointly referred to as rotor,
a compression stage where the parget is compressed by the piston of the extruding machine moving forward until it comes into contact with the blades of the reactor, which reject the parget, propelling it to the interior of the extrusion chamber, and prevent it from moving forward with the resulting increase of pressure
a processing stage where:
[a] when the piston moves forward, it further compresses the parget and forces it to penetrate the boundary layer of the reactor, forming a perimeter film, [b] the reactor shaft enters into resonance, where the potential energy built up by the rotor shaft is released as an emission of a shock wave train, subjecting the parget that is inside the extrusion cavity to violent stirring, and also subjecting the parget which is in the boundary layer to pressure peaks produced by the vibration of the rotor shaft, [c] once the resonance phenomenon is finished, the pressure on the piston of the extruding machine is reduced, decompressing the parget, and the compression of the parget on the rotor is repeated until it enters into resonance once again and there is a new emission of shock waves, and [d] the resonance and decompression cycles are repeated until the temperature of the parget reaches 85° C. to 98° C., preferably 92° C., and
a discharging stage.
In the dependant claims, various advantageous alternatives and preferred embodiments of the method according to the invention are described.
Another object of the invention is an apparatus (100) for transforming organic and inorganic solid urban waste into aggregates, characterised in that it comprises: an extruding machine connected to a reactor;
wherein the extruding machine comprises an extrusion cylinder through which a piston circulates inside an extrusion cavity that defines an extrusion axis,
the end of the extrusion cavity is hermetically connected to the reactor;
the reactor is a drum with rotational symmetry whose longitudinal shaft is coupled (preferably transversally, at 90° to the extrusion axis), by means of an opening, with the end of the extrusion cavity of the cylinder of the extruding machine;
the longitudinal shaft of the reactor comprises a rotatory shaft that is inserted into the beds, which are arranged at the ends of the reactor; in said shaft some steel blades are arranged; between the end of the blades and the wall or dome of the reactor there is a clearance, referred to as boundary layer of the reactor,
wherein the rotatory shaft of the reactor and the blades are jointly referred to as rotor, and wherein the reactor has a discharge valve.
In the dependant claims, various advantageous alternatives and preferred embodiments of the apparatus according to the invention are described.
Further advantages and characteristics of the invention are appreciated from the following description, where, without limitations, some preferred embodiments of the invention are described, mentioning the attached drawings. The Figures show:
Then, reference will be made to a preferred embodiment of the procedure of the present invention at a pilot plant scale for the treatment of solid urban waste, that is, a procedure for the treatment of up to approximately 2000 kg per day of waste, even though the technical concepts are likewise applicable to an industrial plant that may process tens and hundreds of tons per day of waste.
The procedure of the present invention begins with a series of steps that are not novel per se and comprise the following stages:
a) Providing solid urban waste to a waste treatment plant;
b) Loading inorganic and organic waste, partially or totally mixed and cross-contaminated, in a shredder, tearing the bags, if any, and unloading their contents on a conveyor belt of wide exposure and predetermined speed for the initial selection of recyclable waste;
c) Successively extracting the following waste during the initial selection:
batteries, electronic components, microprocessors, home appliances, etc., by manual o mechanical selection;
bottles and glass and plastic containers by manual or mechanical selection;
ferromagnetic metals: sheets, iron, bolts, screws, nails, hinges, etc., through magnetic systems;
non-ferrous metals: lead, aluminium, bronze, copper, brass, by manual, mechanical, electromechanical or electromagnetic selection;
and sending this waste for its treatment outside the treatment plant;
d) Sending the remaining waste, referred to as rejection, to a grinding and crushing machine with articulated rollers, which rotate in a circular hopper, for homogenization; such remaining waste is referred to as rejection, which consists of solid and liquid organic remainders of biological origin, contaminated with inorganic and organic remainders that have not been extracted during the initial selection;
The percentage of rejection relative to the total weight of treated waste varies widely and depends significantly on the geographical area the urban waste comes from, the time of the year and the standard of living of the inhabitants that produce the waste.
e) Loading the rejection into the grinding and crushing machine and adding a binder and optionally rubble, through a worm drive, and water through a metering nozzle.
The binder is concrete, that is, the resulting material from the calcination of calcareous minerals and clays (clinker), together with the customary additives used for these types of supplies in the construction industry.
Rubble is to be understood as any type of surplus material coming from the construction industry, such as tiles and subfloors and subpavements, bricks, renders, etc.
The amount of concrete that is added to the grinding and crushing machine comprises between 20% and 30% relative to the amount of waste that is loaded into said machine.
Depending on the percentage content of water that the waste contain, which are loaded to the grinding and crunching machine, generally about 5-10%, water is added, in such a way that the final percentage of water content is between 25% and 35% of total weight of the mixture of waste/binder/water.
In the event of very high water content in the waste, the addition of rubble is expected, the function of which is absorbing the humidity excess of the final mixture, or any other material that has the same function.
The operation of the grinding and crushing machine is continuous. The materials that are added are ground, crushed and partially homogenized, and the supernatant material, whose granulometry is between 5 and 12 mm, is continuously removed by a ‘supplier’, located in the upper part of the machine, and which is monitored by a microprocessing unit that regulates the amount of material that is removed from the grinding and crushing machine, and it is sent to a conveyor belt.
The removed material is a non-homogeneous and irregular parget that is sent by a conveyor belt to a hopper that feeds a piston extruding machine, with hydraulic operation, connected to a reactor.
f) This and the following stages gather the novel and inventive characteristics of the invention.
The parget from the previous stage is poured into the hopper of the piston extruding machine, provided with a hydraulic pump that produces hydraulic pressure, which actuates a hydraulic cylinder that moves a piston into the extrusion cavity.
The extrusion cavity consists of a cylinder, inside which the piston moves, and which has three sections of approximately the same volume, e.g., 10 L in the case of a pilot plant.
The first section of the cylinder of the extrusion cavity is referred to as passive chamber, where the piston begins its travel until reaching the second section, referred to as entry chamber.
The entry chamber has an opening connected to the hopper of the extruding machine, entering a fraction of 10 L of the parget into the entry chamber. After loading this parget volume in the entry chamber of the cylinder of the extruding machine, the parget inlet valve of the hopper closes.
Then, the piston actuated by the hydraulic pressure presses and pushes the parget volume into the third section of the cylinder of the extrusion cavity. This third section is referred to as compression chamber. In this compression chamber, the parget, as being pressed by the piston, fills up completely the cylinder section and is taken to the end of the cylinder of the extruding machine.
The end of the compression chamber is hermetically connected to a device referred to as reactor.
g) The reactor is a cylindrical steel drum whose longitudinal shaft is arranged horizontally and coupled transverselly, at 90°, through an opening, with the end of the compression chamber of the cylinder of the extruding machine (see below the description of the Figures).
The longitudinal shaft of the reactor comprises a rotatory steel shaft that is inserted in the beds, arranged at the ends (or ‘heads’) of the reactor. In the shaft, there are some steel blades whose ends play the roles of cutting, hammering, punching and hydraulic helix as they rotate. Between the end of the blades and the wall or dome of the reactor there is a 0.2-mm clearance.
In the context of the invention, this clearance or free space between the end of the blades and the wall of the reactor is referred to as boundary layer of the reactor.
The rotatory shaft of the reactor and the blades are jointly referred to as rotor. Furthermore, the reactor shaft is coupled with an electric motor that allows the rotor to rotate at high speed.
The structural and functional aspects of the reactor and rotor will be described in further detail in the detailed description of the apparatus of the present invention referenced in the Figures attached to this description.
Due to the number of blades and their geometrical shapes, the rotation at high speed makes the parget to ‘see and come to an invisible wall’ upon reaching the end of the compression chamber.
This effect can be better seen and understood recalling the example of the blades of a fan, which by rotating fast form an invisible wall that rejects any object that wants to penetrate it.
Correspondingly, once the parget pressed by the piston comes into contact with the rotor, the following series of events occur:
The first event that occurs, at low gauge pressure in the parget and low consumption of the electric motor, is a reverse bombardment or violent rejection of matter that comes into contact with the blades. The grinding and mixing occurs without pressure inside the parget.
The second event occurs as a consequence of the slight increase in the pressure of the piston that presses the parget against the rotor. The parget starts rotating in the opposite direction of the rotor, grinding and mixing at low pressure.
During the third event, a thinner grinding and a stronger mixing are continued. This event occurs at a pressure of approximately 490 kPa (approx. 5 kg/cm2) at the core of the parget.
During the fourth event, the pressure of the piston keeps rising and the temperature of the parget reaches 75° C. due to the effect of friction, producing an additional homogenization of the parget.
During the fifth event, the parget loses all the built up gas or possible trapped air bubbles.
During the sixth event, the pressure on the parget is very high, at about 980 kPa (approx. 10 kg/cm2), which gives rise to a new stage.
h) In this stage, the parget subjected to high pressure rotates between the piston and the rotating front of the rotor at approximately 30 km/h in the opposite direction of the rotor and is forced by the blades to penetrate the boundary layer of the reactor, thus forming a 0.2 mm-thick perimeter film that acts as a complete hydraulic seal for both the reactor/extruding machine.
The volume of this perimeter film constitutes 5% of the total parget volume; the remaining 95% continues rotating inside the compression chamber.
The perimeter film circulates at a speed of approximately 150 km/h and produces an exchange of total parget volume in just 2 seconds.
At this moment of the procedure, and when the parget is subjected to an increase in pressure that reaches approximately 1176 kPa (approx. 12 kg/cm2) of piston pressure on the parget at the compression chamber, a physics phenomenon occurs on the rotor shaft.
Therefore, as the pressure of the parget on the rotor blades increases, its shaft is slightly curved in the same direction as the forward movement of the parget, shifting up to 0.2 mm in the centre of the rotor shaft to a standing position and building up huge potential energy, equivalent to 2 tons on the rotor shaft.
At this moment, a physics event of resonance occurs consisting in the rotor shaft emitting a shock wave train comprising the fundamental wave and possible harmonics. That is, the rotor shaft, slightly rotating in a curvy manner, now transforms its potential energy into vibration or resonance kinetic energy.
The low frequency (less than 80 Hz) shock wave train subjects the parget that is inside the compression chamber at low circulation speed relative to the circulation speed of the boundary layer, to violent stirring.
The result of this physics phenomenon is that at the core of the parget a collapse occurs, due to vibration and friction, of all these complex structures of biological tissues, even partially or totally taking apart organic and inorganic, polymeric complex molecules, while this episode is accompanied by a geometrical increase of the temperature, possibly producing microvolumes within the parget subjected to very high temperatures.
This resonance phenomenon occurs because the rotor, which rotates at 2900 rpm, is pressed by the parget, which acts as an intermediate piston, and which in turn curves the rotor shaft that builds up huge potential energy, equivalent to 2 tons on the rotor shaft.
At this point, the rotor shaft returns the potential energy built up as a giant spring giving rise to the mechanical resonance, that is, the emission of a shock wave train.
Within the boundary layer, the collapse of said boundary layer occurs, in this case, even more radically while extreme pressure peaks are produced.
When the reactor enters into resonance, this event consumes a great amount of instant energy. In order to solve this problem, there is a flywheel that is coupled with the electric motor shaft and which builds up kinetic energy.
When the rotor slows down 100 rpm, the wheel delivers 74,570 J/s (approx. 100 HP) preventing the motor from leaving the electric synchronism and preventing the subsequent decrease of tension in the line.
The resonance phenomenon lasts approximately 1 to 2 seconds.
Subsequently, the hydraulic pressure on the extruder piston is removed for 1.5 to 2 seconds, and the compression cycle of the parget on the rotor is repeated until a new emission of shock waves is produced. The complete procedure is monitored automatically by a microprocessor connected to suitable sensors that the apparatus comprises according to the present invention.
This synchronized way of operating the extruding machine and both the reactor/rotor allows replacing the electric motor energy to the wheel, thus preventing the decrease of tension to abrupt consumption.
The compression and decompression cycles are repeated until the parget temperature reaches approximately 92° C. The sensors of the apparatus detect this temperature.
The number of compression cycles depends on the nature of the treated waste, but this procedure stage needs generally between 25 and 50 seconds.
i) Final procedure stage. After 25-50 seconds, the discharge valve of the reactor is opened and the extruding machine discharges, by piston pressure on the parget and through the boundary layer and openings arranged at the bottom of the reactor, the treated parget placing it on a conveyor belt that sends it to a storing area where the parget, in a granulated form, is set and is converted into an aggregate.
A preferred embodiment is described hereinafter in reference to the accompanying figures of this description.
The material coming from the grinding and crushing machine is sent through a conveyor belt to a hopper that feeds a piston extruding machine, hydraulically operated and connected to a reactor.
The parget is fed through a conveyor belt (not shown), to a hopper (101) of the extruding machine (102).
The extruding machine consists of an extrusion cylinder (103) through which a piston (104) circulates, actuated by the hydraulic pressure from a hydraulic pump (not shown), which produces hydraulic pressure that actuates a hydraulic cylinder (105) which moves the piston into the extrusion cavity (106).
The extrusion cavity consists of a 20-cm internal diameter cylinder, inside which the piston moves, and which has three sections of approximately the same volume, e.g., 10 L in the case of a pilot plant.
The first section of the cylinder of the extrusion cavity is referred to as the passive chamber (107), inside which the piston begins its 45-cm travel until reaching the second section, referred to as access chamber (110). For reasons of space, the passive chamber is represented in
The access chamber, of 45 cm in length, has an opening (109) connected to the hopper (101) which loads a 10-L fraction of the parget into the access chamber. After loading this parget volume into the access chamber of the cylinder of the extruding machine, the parget inlet valve (not shown) of the hopper is closed.
Then, the piston actuated by the hydraulic pressure presses and pushes the parget volume into the third section of the cylinder of the extrusion cavity. This third section, of 50 cm in length, is referred to as compression chamber (111).
In this compression chamber, the parget, as being pressed by the piston, fills up completely the cylinder section and is dragged to the end of the cylinder of the extruding machine.
The end of the compression chamber is hermetically connected to a device referred to as reactor (112).
The reactor is a cylindrical steel drum (113), of 23 cm in length and 30 cm of internal diameter, whose longitudinal shaft is horizontally arranged and transversely coupled, at 90° with the extrusion axis defined by the extrusion cavity, through an opening (114) with the end of the compression chamber (115) of the cylinder of the extruding machine.
This longitudinal shaft of the reactor is formed by a rotatory steel shaft (116) that is inserted into the beds (117), arranged at the ends (or heads) of the reactor. Along the shaft, there are some SAE 5560 steel blades (108), the ends of which play the roles of cutting, hammering, punch nipping and hydraulic helix as they rotate. Between the end of the blades and the wall or dome of the reactor there is a 0.2-mm thick clearance.
In the context of the invention, this clearance or free space between the end of the blades and the wall of the reactor is referred to as boundary layer of the reactor.
The rotatory shaft of the reactor and the blades are jointly referred to as rotor. Furthermore, the reactor shaft is coupled with an electric motor (not shown in
The free end of the blades displays an external surface whose width, in the direction of the longitudinal shaft of the reactor, is partially overlapped with the width of the adjacent blades, such that, as they rotate, the covering surface generated by all the blades is a continuous surface, where the width is to be understood as the distance, in the direction of the longitudinal shaft of the reactor, from the point of the external surface closest to an end of the reactor to the point of the external surface closest to the opposite end of the reactor.
Due to the number of blades and their geometrical shapes, rotation at high speed makes the parget to ‘see and come to an invisible wall’ by reaching the end of the compression chamber.
This effect can be better seen and understood recalling the example of the blades of a fan, which by rotating fast form an invisible wall that rejects any object that wants to penetrate it.
The rotor shaft (116) is made of SAE 4140 steel, whose hardness exceeds 25 Rc (Rockwell hardness), with a diameter of 50 mm and a bed support (total length of the shaft) of 30 cm.
These measures allow the longitudinal centre of the shaft to ripple and vibrate thus tuning with the fundamental wavelength and the possible harmonics.
The bearings (also referred to as roller-bearings) of the bed contain the shaft, which allows a slight angular variation and facilitates the shaft ripple and resonance.
The hubs (203) that are threaded in the shaft and that separate the blades of the rotor from one another have a curved geometry among them and act as vertebrae of the spine formed by the rotor shaft.
The blades, whose number is variable and dependant on the types of urban waste that are to be treated (7 blades in the case of
Each blade is 29.96 cm long, but its function is performed only in the last 3 cm closer to the boundary layer.
For this reason, the rotor is made of any steel capable of resounding while the reactor is built with very low-resonance foundry.
It is to be understood that the reactor should not resound, and it behaves as a non-resounding solid body. If it did resound, the effect produced by the shock waves generated by the rotor would be lost.
The rotor has internal blades, which carry out the parget processing, and side blades, which are arranged at the ends of the rotor and work basically as a hydraulic seal.
The blade (400) has a rectangular configuration in the shape of a helix (401), with a circular hole (402) located in the centre of the rectangle and designed for being threaded in the rotor shaft between two trapping hubs.
The external surface (403) of the blade has a longitudinal circular shape that imitates the curvature of the internal wall of the reactor, allowing the blade diameter, from the centre of the hole to the external surface of the helix, to have a 0.2-mm clearance between said external surface and the wall of the reactor.
Both side blades are located at each of the two ends of the rotor shaft and are mirror images.
In these final stages, characterised by the compression of the parget effected by the piston of the extruding machine, the rejection of the parget as a result of the circulation of the blades, the forced penetration of the parget into the boundary layer area, and the violent phenomenon that takes place once the rotor shaft delivers its potential energy, built up during the curvature of the rotor shaft by pressure, in the form of vibration or resonance energy, the valve (300) of the reactor being closed by a hydraulic device (303) which completely seals the reactor and prevents the parget in the boundary layer area from being released through the openings (304).
Once the parget has been completely processed through a series of pressure and decompression cycles, as described above, the discharge valve of the reactor opens automatically and the parget is released and sent to a conveyor belt.
This final stage of the procedure is consistent with the arrangement of the apparatus, as represented in
The hydraulic device (303) has retracted the discharge valve of the reactor (300) up to an ‘open’ position, thus allowing the parget present in the boundary layer area to be discharged through the openings (304), depending on the direction of the arrows (305) towards a conveyor belt (not shown).
All the parget present in the compression chamber is propelled by the piston of the extruding machine towards the boundary layer area and discharged through the openings of the discharge valve of the reactor towards the conveyor belt, which sends de parget, located in the initial stages of the setting process, towards a storing area, where the setting is completed.
Once the setting process of the parget finishes, a completely inert and non-polluting aggregate is obtained, which may be returned to nature as it behaves like sand.
The aggregate may also be used in the construction industry, for making eco-friendly bricks for the drying of road bases and as subfloors in any type of building.