Claims
- 1. A composition for providing a repulpable moisture vapor barrier coating for flexible packaging material, which comprises:
- a wax-free polymer emulsion wherein said polymer in said emulsion has a particle size distribution finer than about 10.mu., said polymer having moisture vapor barrier properties;
- a particulate material additive comprising carboxylated styrene-butadiene having a mean particle size smaller than about 10.mu., said particulate material additive being capable of interstitial combination with said polymer particles and of giving a coating on said flexible packaging material which preserves moisture vapor barrier properties provided by said polymer, and which upon repulping of the coated flexible packaging breaks up into pieces generally smaller than about 1.6 mm;
- said composition enabling said coating to break up into said pieces generally smaller than about 1.6 mm.
- 2. A composition according to claim 1, having a pH of 2 to 9.
- 3. A composition according to claim 1, wherein said additive additionally comprises hydrated alumina silicate.
- 4. A composition according to claim 2, having a pH of about 8.5.
- 5. A composition according to claim 3, having a pH of 8 to 8.6.
- 6. A composition for providing a repulpable moisture vapor barrier coating for repulpable wood-fiber based packaging, which comprises:
- a wax-free polyvinylidene chloride emulsion wherein the polyvinylidene chloride has moisture vapor barrier properties and is present as polyvinylidene chloride particles having a mean particle size distribution finer than about 10.mu.;
- said emulsion containing an additive comprising of carboxylated styrene-butadiene, said additive having a mean particle size distribution finer than about 10.mu., said additive particles being capable of interstitial combination with the polyvinylidene chloride particles to form a coating on said wood-fiber based packaging in which the moisture vapor barrier properties of the polyvinylidene chloride are preserved, wherein said coating, on repulping of the coated wood-fiber based packaging, breaks up into pieces small than about 1.6 mm,
- wherein said coating composition has a pH of between about 2 and 9.
- 7. A composition according to claim 6, wherein said additive further comprises hydrated aluminum silicate.
- 8. A repulpable moisture vapor barrier coating composition for repulpable wood-fiber based packaging, consisting essentially of:
- a wax-free polyvinylidene chloride emulsion, wherein the polyvinylidene chloride in the emulsion has a molecular structure that enables provision of crystalline regions and moisture vapor properties, and wherein polymer chains of the polyvinylidene chloride are arranged with interactive bonds between the polymer chains, said polyvinylidene chloride being present in said emulsion as particles having a mean particle size distribution finer than about 10.mu.,
- said emulsion containing an additive comprising polymer particles of carboxylated styrene-butadiene, said additive having a mean particle size distribution finer than about 10.mu., said additive particles being capable of interstitial combination with the polyvinylidene chloride particles to form a coating on said wood-fiber based packaging in which the moisture vapor barrier properties of the polyvinylidene chloride are preserved,
- wherein said polyvinylidene chloride emulsion, in the absence of said additive, forms a moisture vapor barrier coating on said wood-fiber based packaging, which in repulping of the coated packaging produces coating particles larger than 1.6 mm, in which the interactive bonds between the polymer chains are maintained, and which particles do not form a pulp with the repulped wood-fiber,
- wherein said polyvinylidene chloride emulsion containing said additive forms a moisture vapor barrier coating on said wood-fiber based packaging, which on repulping of the coated packaging breaks up into coating particles smaller than about 1.6 mm, which form a pulp with the repulped wood fiber, and
- wherein said coating composition has a pH between about 2 and 9.
- 9. A composition according to claim 8, wherein said additive further comprises hydrated aluminum silicate.
CROSS-REFERENCE
This application is a continuation-in-part of U.S. Ser. No. 08/588,724, filed Jan. 19, 1996, now U.S. Pat. No. 5,929,155 which is a continuation-in-part of U.S. Ser. No. 08/375,988, (now abandoned) filed Jan. 20, 1995, inventor Serge Berube.
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
5270103 |
Oliver et al. |
Dec 1993 |
|
Foreign Referenced Citations (1)
Number |
Date |
Country |
1583947 |
Feb 1981 |
GBX |
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
588724 |
Jan 1996 |
|
Parent |
375988 |
Jan 1995 |
|