Patent Application
20100292823
The invention relates to a method and computer program for automatically preparing technological formulas for a heat treatment of metal workpieces in industrial furnaces. The formulas are prepared, after the specification and setting of the required parameters by the operator, by the computer program and can be repeated arbitrarily and stored and displayed as well as retrieved for autonomous performance of the heat treatment in the industrial furnace. Furthermore, the invention relates to an apparatus for automated performance of the method and computer program for the particular programmed heat treatment in the autonomous sequence of the industrial furnace.
The technical area designated at the beginning has already been studied multiple times in regard to its optimal technological preparation of the heat treatment to be performed later of the workpiece or the batch in an industrial furnace.
Accordingly, methods and devices for the heat treatment of metal workpieces in industrial furnaces are known, which rationalize the sequences, but the field of technological preparation offers still further potentials, of exploiting the developed state of the heat treatment method and furnace technology more efficiently and increasing the availability of an industrial furnace in this regard.
To determine the extent of the heat treatment of the material, it is taught according to DT 26 30 818 A1 that, according to the method, a signal representative for the heat treatment temperature is integrated over time using a formula of the heat treatment units, the times, a constant, the temperature, and the relative speed of the softening/hardening. The number of the heat treatment units is summed during the method performance, in order to determine the extent of the heat treatment. The signal may be integrated continuously and samples of the signal may be integrated after selected intervals. The setting of the number of the heat treatment units can be performed according to the lowest temperature. The fuel supply control is made possible after equalizing of various temperatures.
The associated device essentially comprises an apparatus for the integration of the signal and an apparatus for the summation of the number of the heat treatment units for performing the above method steps.
It is initially disadvantageous for this purpose that the plurality of the variants of the heat treatments, such as the tempering of metals, cannot be acquired complexly enough using the values to be integrated. Furthermore, target values must often be corrected during the beginning or during the performance of the heat treatment.
A further known device for the heat treatment of metal workpieces according to DE 20 2006 018 879 U1 has a control apparatus having measuring apparatus, which acquires target parameters for the treatment atmosphere and actual values for signal output and makes the heat treatment able to be terminated using a control unit in the event of inequality of target and actual values.
This device can control only a limited sequence of the method performance according to the object.
In addition, EP 0 556 176 B2/DE 91 04 377 T3 has already disclosed a special control system for planning the workpiece treatment in a heat treatment method. The heat treatment of parts is performed using a plurality of connected chambers, two of which are rotating chambers for carburization or carbonization. A plurality of part positions is subject to reactive or reaction-ready hydrocarbon gases at elevated temperatures. The parts are discharged into the rotating chambers or ejected independently of their function. The processing chambers process at least two parts simultaneously using unique processing times.
This control system has storage means for recording, for each part, specific processing times, target processing paths with sequence of the processing chambers, number and location of occupied part positions in each chamber, and diverse formula and/or instructional specifications and their calculations, time window recordings, status means for updating, a databank, and hardness depth values. The entry into the preheating chamber, slow cooling chamber, press and batch quenching chambers, and rotary tempering chamber are controlled. The method teaches the time planning and/or assignment of parts into the continuous furnace structure having the steps for storing/recording the functions of the control system.
Notwithstanding the application of the control system for the heat treatment of parts in a continuous furnace structure having a plurality of connected chambers, this control system and the method teaches neither the possibility of an autonomous sequence of the heat treatment nor a technological preparation of heat treatments in industrial furnaces according to the species. At that the control system can only be applied for the continuous furnace structures.
All known methods and devices similar to the species share the feature that the individual method parameters to be specified are largely a function of the heat-technology know-how of the technician or operator. The required heat-technology specific treatment of the workpiece having the properties to be achieved is therefore not always reached.
For the proper performance of a specific heat treatment method for the heat treatment of metal workpieces, it is necessary on the operator side to specify corresponding method parameters for the method performance. Method parameters of this type may be temperature, pressure, processing time, and/or the like, for example. These method parameters to be specified on the operator side determine the method result, because of which it is decisively important, to achieve a desired method result to be reached, for the corresponding method parameters to be specified as precisely as possible and according to objective criteria.
Although experiential values may certainly be used suitably for the specification of method parameters for the performance of a specific heat treatment method, this is not free of disadvantages.
Thus, in particular operator-side incorrect estimations frequently occur and, resulting therefrom, incorrect inputs with respect to the method parameters, which can have the result that workpieces are incorrectly treated and the discard rate rises unnecessarily.
In particular for the operators of industrial furnaces, the need exists to be able to specify method parameters for the performance of a heat treatment method for the heat treatment of metal workpieces reliably, so that thereafter the heat treatment of the workpieces in the industrial furnace can run extensively free of incorrect inputs and autonomously.
The object of the invention is to provide a method and computer program for the automatic preparation of technological formulas for the heat treatment of metal workpieces in industrial furnaces and to allow conditions through a program-controlled determination, so that the performance of heat treatments of metal workpieces in industrial furnaces can be planned before the beginning of the heat treatment in the particular industrial furnace and can be performed running autonomously thereafter using an apparatus.
The direction, which material, and how it is to be treated are already to be programmed and specified deliberately so that the heat treatment can run in the furnace autonomously according to the objectively qualified technological specifications of the heat treatment process.
The formula programmed and generated according to the invention for the treatment in the furnace charged with the workpiece batch can then be activated, whereby the autonomous heat treatment sequence according to the program is finally secured. All method parameters are thus to be maintained from the beginning to the termination of the heat treatment in the industrial furnace extensively independently of subjectively qualified influences or knowledge (know-how) of the technician or operator.
The object is achieved according to the method and computer program using
After the third program step, in a first work step the desired target hardness can be selected and input as a directional value of a work hardness from a value range according to achievable work hardnesses as a function of the material.
After at least the third program step, in a second work step, an optimization setting can be established and set for a time-optimized or low-deformation treatment of the workpiece/the batch.
In a third work step, manual reworking and storage of the generated heat treatment formula in the programmed databank can be performed.
The method and program is capable of expansion in a fifth program step, in that the heat treatment formula is transmitted to the furnace. For this purpose, for the heat treatment of the workpiece/the batch running autonomously in the industrial furnace, the heat treatment program is retrieved from the programmed databank and mediated for the heat treatment in the industrial furnace.
The treatment method is already determined in the first program step from data of the material group and the material according to a first file, second file, and third file of a material databank.
The calculation of the virtual wall thickness in the second program step is performed according to an algorithm as the function=fV*according to the equation fV=fCG*fCA*fG1.
A rulebook is used in the program, which comprises a fourth file for the comparative geometry, a fifth file for the batch layout, a sixth file for the heating characteristic, and a seventh file for the quenching characteristic.
The fourth file in the rulebook comprises the data for the details of comparative geometries, such as sphere, cylindrical disc, hollow-cylindrical ring, cylindrical shaft, square plate, square rod, square cube.
The fifth file in the rulebook comprises the batch layout such as single-layer recumbent, single-layer upright, multilayer recumbent, multilayer upright, stacked
In the third program step, the heating characteristic is input according to the sixth file in the rulebook in the dimension of the number of preheating steps in slopes of ° C./min as the gradient and the quenching characteristic is input according to the seventh file in bar.
It is advantageous for the user that a time-temperature transformation (TTT) diagram, which is stored in the computer, and a stored tempering diagram are displayed already after the first program step.
Furthermore, it is advantageous that the desired work hardness is input according to an eighth file from the material databank.
The complex heat-technological formula, which is running in the industrial furnace and is generated and stored from parameters of a heat treatment of a specified technology, can be measured using a measuring unit having actual values, compared via a comparison circuit to the parameters of the specified technology, and readjusted without problems using a control unit in the event of inequality.
The apparatus for performing the method comprises a computer having databanks and a programmed storage of a particular generated heat treatment program and its retrieval for the activation of the heat treatment in an industrial furnace, a user interface being associated with the computer according to the invention, which has fields for displaying
Furthermore, the user interface has a first virtual slide control for the comparative geometry, which can be selected and changed by the operator, a second virtual slide control for the batch layout, which can be selected and changed by the operator, a third virtual slide control for the virtual wall thickness, which can be selected and changed by the operator, a fourth virtual slide control for the heating characteristic, which can be selected and changed by the operator, and a fifth virtual slide control for the quenching characteristic, which can be selected and changed by the operator.
Using these elements, the user interface is designed as a decisive technical means, which creatively supports the solution of the stated object.
Finally, the apparatus can be expediently implemented if a measuring unit for actual values measured in the industrial furnace, a comparison circuit for the comparison to parameters of the specified technology according to the generated heat treatment program, and a regulating unit for a readjustment in the event of inequality of parameters are provided.
The heat treatment of the workpiece/the batch running autonomously in the industrial furnace can be retrieved from the program databank via a button on the user interface after storage of the complex generated formula and mediated for heat treatment in the industrial furnace.
The particular generated heat treatment program can be shown in the user interface in symbolic sliders, processed manually therein, and stored via a further button.
It is advantageously provided according to the method that the actual method parameters of a heat treatment method may be measured as actual values.
It is accordingly possible to compare the method parameters measured as actual values to the method parameters specified as target values and to perform a readjustment of the method parameters in the event of inequality between measured actual values and specified target values.
In general, the method teaches that as a function of a first selected value, a list is determined, produced, or generated for the selection of a second selected value, and specified values are specified as a function of workpieces to be heat treated and/or as a function of a batch formed by a plurality of workpieces to be heat treated.
It is typical that firstly selected and/or specified values are selected or specified by the operator, but then the method parameters can be generated automatically by a corresponding computing unit executing a function as a function of these values. The method parameters thus determined are designated as pre-calculable parameters here, which can only be manipulated by the operator within objectively required limits.
Typically, i.e., if no operator-side manipulation occurs, the parameters thus precalculated are accepted as target values to be maintained in the method and thus for the technological formula. The heat treatment can then be performed according to the generated technological formula, in an autonomous sequence in the industrial furnace.
A manipulation of the parameters which are initially only determined by calculation is sometimes also required by the operator. Being able to perform changes on the parameters determined by calculation is therefore not precluded by the method according to the invention. This relates to optimization settings to be executed by the operator, if treatment is to be performed time-optimized or with low deformation, for example.
As a function of these optimization settings, which are only possible within specific limits determined by the system on the basis of the previously input selected and/or specified values, additional optimization of the method parameters for performing the generated heat treatment method can be achieved.
If needed, a plurality of both selected and/or specified values and also of optimization settings can be performed, in order to achieve the required heat treatment result.
To perform the method and computer program, the apparatus according to the invention can also be compiled from the complexes such as
The invention advantageously allows method parameters for the performance of a specific heat treatment method to be determined and fixed automatically. Determination and establishment of method parameters which is independent of operator-side experiential values are thus achieved for the performance of a heat treatment method for the heat treatment of metal workpieces.
Using the invention, it is thus possible to be able to specify a method parameter for the performance of the heat treatment method for the heat treatment of metal workpieces reliably and reproducibly. Desired treatment results may thus be achieved independently of the operator, i.e., independently of operator-side or subjective experiential and method values.
The invention has available fixed selected values from lists having predetermined data. This includes, inter alia, the material of the workpieces to be treated. Thus, for example, a list is provided for the selection of the material, in which the associated material groups are listed, such as high speed steel, cold worked steel, hot worked steel, and non-rusting steel, which is to be selected from by the operator to establish a first selected value
For a further selected value, the selection of the desired treatment method is provided. A list is also stored in this regard having possible treatment methods, such as hardening, hardening and tempering, hardening and warm bath, hardening and warm bath and tempering, tempering, soft annealing, solution annealing, strain annealing, and/or the like, from which a desired treatment method to be performed is to be selected by the operator.
In certain circumstances, the preceding selection of a material fundamentally precludes a treatment method which is available for selection beforehand, because of which, according to significant features of the invention, values are generated, using which the further selected values can be generated as a function of a first selected value. Operator-side input errors or the input of incorrect experiential values may thus be fundamentally minimized or even avoided beforehand.
The selected values to be selected by the operator from the material databank are thus used for generating method parameters for performing a specific heat treatment method in the scope of the described technological formula.
In addition to the selected values, specified values are also used to establish these method parameters, these being understood in the meaning of the invention as those values which are to be specified as a function of workpieces to be heat treated and/or as a function of a batch formed by a plurality of workpieces to be heat treated.
These include the wall thickness of the workpieces to be treated, the comparative geometry, the workpiece or batch weight, and the batch layout. “Wall thickness of the workpiece to be treated” is to be understood as the thickness of the material of the workpiece to be treated or the workpiece part to be treated.
For example, the sphere, the cylindrical disk, the hollow-cylindrical ring, the cylindrical shaft, the square plate, the square rod, or the square cube may be specified as the comparative geometry.
On the basis of these specified values, which may also be designated as batch data, in consideration of the selected values of the rulebook previously selected by the operator, method parameters may be automatically determined for performing the determined heat treatment method. Method parameters of the rulebook in this meaning are the heating characteristic as well as the quench pressure and the target values and optimization settings.
The heating characteristic describes the intensity and form of the heating procedure for the hardening process. It specifies the number of the preheating steps from 0 to 4, for example, as well as the slope of the temperature target value, both between the individual preheating steps and also between the last preheating steps and the temperature target values to be reached. The slopes are, for example, in the range from 5° C. per minute up to 30° C. per minute, a temperature jump also optionally being able to be specified
Depending on the quenching gas used, the quench pressure is in the range from 2 bar to 12 bar, for example.
The method parameters which can be determined using the invention, such as heating characteristic and quench pressure, are used as initially calculated method parameters, which may be manipulated, i.e., readjusted by the operator within certain limits, i.e., upper and lower limits.
For this purpose, it is also provided that the “virtual”, i.e., an imaginable possible or apparent wall thickness is output, calculated and generated as an intermediate value, on the basis of the previously explained batch data.
This intermediate value can only be manipulated, i.e., readjusted, in specified limits by the operator. As a function of such a readjustment, method parameters result which can be determined automatically using the apparatus according to the invention and computing units. The apparatus according to the invention thus provides the possibility of being able to manipulate, i.e., readjust the automatically determined method parameters, but not according to arbitrary values.
Because of the possibility given by the invention of the operator being able to readjust method parameters within certain limits, the method parameters determined according to the acquired selected and/or template values are designated as calculated method parameters.
In an embodiment of the invention, the actual method parameters specified as target values for a desired performance of a heat treatment method are measured, compared, and optionally corrected during performance of the heat treatment.
The calculated method parameters typically determine the formula. As previously described, readjustment of the calculated method parameters is also provided, so that the readjusted method parameters ensure the target values to be maintained during the method performance.
Finally, the invention also comprises the operator-side possibility of performing the heat treatment generated as a formula in a time-optimized manner or optimized for low deformation in regard to the workpieces to be treated and without incorrect data. Notwithstanding this, obligatory specifications for the desired target hardness may also be set beforehand.
All settings to be performed by the operator, such as optimization settings, are used for the purpose of preparing the previously determined method parameters as optimized with respect to the heat treatment result to be achieved for the later autonomously running heat treatment.
The regulatory apparatus having measuring apparatus used during a performance of a heat treatment method can be used for the purpose of comparing the real actual values after measurement and the precalculated technological formula using a comparison circuit, in order to be able to perform a readjustment of the actual values if needed in the event of an established deviation between actual values on one side and target values on the other side, during the actual heat treatment method.
A permanent, i.e., continuous readjustment of the method parameters which decisively influence the method result is advantageously possible in this manner, if this proves to be necessary.
It is within the scope of typical measures of one skilled in the art to equip the measuring apparatus with corresponding sensors, such as temperature and/or pressure sensors, for determining the actual values.
In its entirety, the invention allows the method parameters which are necessarily to be preset to achieve a specific heat treatment result to be executed automatically according to the method and computer program using the apparatus according to the invention. The selected and/or specified values to be detailed are always those which can be objectively acquired free of any subjective or operator-side experiential values.
As a result, using the invention, the prepared formula for heat treatment of metal workpieces may advantageously be prepared and conditioned using program technology so that autonomous execution of the heat treatment method is possible thereafter.
Because the method parameters for performing a heat treatment method can be determined and established automatically, the advantage results overall that incorrect inputs by the operator with respect to the method parameters to be specified are fundamentally prevented. Incorrect treatment of workpieces may be practically prevented.
In the figures:
a) shows a flowchart of the structure according to the invention of the program steps in the user interface,
b) shows a flowchart of the elements of the program preparation,
a) shows a user interface associated with the computer for program operation having the symbolically displayed diagram of a TTT diagram (time-temperature transformation), and
b) as
The invention is initially described using the schematic figure according to
In a computer 1
The material databank 10 and the rulebook 11 comprise the parameters which can be determined and precalculated for a heat treatment program. A user-friendly and objective selection and/or display of the parameters acquired within limits is made possible.
The blocks “material data maintenance” and “user interface I-IV” indicate the functional relationships of the program to the material databank 10 and the rulebook 11 and a program databank 12. The heat-technology formula prepared according to the invention is stored in the program databank 12, it is transmittable to an industrial furnace 5 for heat treatment of the workpieces. A measuring unit 7 and a regulating unit 6 having interconnected comparative circuit 8 are associated with the industrial furnace 5.
The flowcharts according to
In the meaning of one skilled in the art of the invention, the selected terms, inter alia, are to be defined as follows from above-mentioned values of formula segments:
After the third program step III, according to
According to at least the third program step III, a time-optimized or low-deformation treatment of the workpiece/the batch can be established and performed in a second work step VI.
In a third work step VII, according to
In a fifth program step VII (
In the first program step I, the treatment method is determined from data of the material group and the material according to a first file, second file, and third file of the material databank 10.
In the second program step II, the virtual wall thickness is generated according to an algorithm as a function=fV*according to the equation fV=fCG*fCA*fG1.
The rulebook 11 comprises a fourth file for the comparative geometry, a fifth file for the batch layout, a sixth file for the heating characteristic, and a seventh file for the quenching characteristic.
The fourth file in the rulebook 11 contains the data for the detail of comparative geometries, such as sphere, cylindrical disk, hollow-cylindrical ring, cylindrical shaft, square plate, square rod, square cube.
The fifth file in the rulebook 11 contains the batch layout as single-layer recumbent, single-layer upright, multilayer recumbent, multilayer upright, stacked.
In the third program step III, the heating characteristic is input according to the sixth file in the rulebook 11 in the dimension of the number of the preheating steps in slopes of ° C./min as the gradient and the quenching characteristic is input according to the seventh file 2.9 in bar.
After the first program step I, a stored TTT diagram 20.2 (
The desired work hardness is input according to an eighth file from the material databank 10.
The complex heat-technology formula running in the industrial furnace 5 and generated and stored from parameters of a heat treatment of a specified technology is measured according to
The user interface 30 according to
This user interface 30 is both an expedient technological aid and also an aid in formal logic, which thus guides the operator during a program control for determining the technological formula of an objectively required heat treatment.
As schematically shown in
The invention makes itself more precise in the program steps according to selected data as follows, for example:
In the first program step I, a treatment method such as hardening plus 3× tempering here is determined from data of the material group, such as high-speed steel, and the exemplary material, such as HS6 5 2C, as a function of this selected material.
In the second program step II,
This generated wall thickness of 13 mm is calculated from the function fV=fCG*fCA*fG1, stored according to the invention in the program, using the factors fCG, fCA, and fG1 and the tables integrated in the program, such as
In the third program step III, a heating characteristic of 2 VW/15° C. and a quenching characteristic of 2 bar, as a function of the material, are integrated from the virtual wall thickness together with the data of the batch and the available parameters of the industrial furnace 5, which (as is obvious from
Steps of the heating characteristic as a function of the virtual wall thickness, the material, and the selected method (using the sixth file included in the rulebook 11 (
The proposed step of the heating characteristic as a function of the virtual wall thickness is ascertained according to the following table:
The number of the preheating steps is a function of both the selected method and also the material used.
The data for this purpose are stored in the material databank 10 and in the rulebook 11 (
The range of the possible slider steps for the heating characteristic is a function of the number of the preheating steps according to the following table.
The quenching characteristic, which is a function of the virtual wall thickness, the material, and the selected method, is ascertained as follows.
For each material, a table is also stored in the material treatment databank, which specifies the crunch pressure as a function of the virtual wall thickness. The virtual wall thicknesses are each grouped into four ranges.
In the first work step IV, a desired work hardness is selected and input as a directional value from a value range according to the tempering diagram 20.1 (
In the second work step VI, the generated heat treatment program can be set to a time-optimized or low-deformation treatment of the workpiece/the batch.
In the fourth program step V, the complex heat-technology formula having the program name VW(850,1080)H(1210)A540,540,510) is automatically generated, which can be repeated and stored in the program databank for a retrieval of an input to the industrial furnace 5 and can be displayed according to
In the third work step VII (
For the heat treatment of the workpiece/the batch running autonomously in the industrial furnace 5, the heat treatment program is retrieved from the program databank in the fifth program step VIII (
With reference to
The data for wall thickness are input as 10 mm in a field II.1 and the data for the batch weight are input as 100 kg in a field II.3, without files stored in the computer.
The optimization settings are performed in a field V.1 (
Finally, the name of the heat-technology formula appears in the field VI.1 (
The complex heat-technology formula having the program name VW(850,1080)H(1210)A540,540,510), which runs in the industrial furnace 5 and is generated and stored from parameters of the heat treatment of a specified technology, is measured according to
For this purpose, according to
The user interface 30 associated with the computer 1 according to
At a desired point in time of the heat treatment of the batch to be performed autonomously in the industrial furnace 5 corresponding to this complex generated formula, this generated program “VW(850,1080)H(1210)A540,540,510)” can be retrieved via a button (not shown) of the user interface 30 from the program databank according to the eighth program step VIII (
According to
a) and 2b) give an overview of the relationships of the programmed sequence of the preparation of the heat-technology formula according to the corresponding values up to the programmed storage of the generated heat treatment program and the retrieval from the program databank 12 for the activation of the heat treatment in the industrial furnace 5 as a flowchart. The fundamental program sequence according to the invention is obvious therefrom.
The contexts and relationships shown and explained in the individual blocks of
According to the internal tests and achieved results, it is ensured that the potential operators of industrial furnaces for the heat treatment of metal workpieces may achieve their concepts for autonomous operating processes during the heat treatment of workpiece patches efficiently and extensively independently of special knowledge of the operating personnel using the method and computer program according to the invention for preparing corresponding technological formulas and using the apparatus.
| Number | Date | Country | Kind |
|---|---|---|---|
| 20 2007 0140120.3 | Oct 2007 | DE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/DE08/01454 | 9/3/2008 | WO | 00 | 7/30/2010 |