The invention relates to a method and a device for depositing a nonmetallic, in particular ceramic coating on a substrate by means of cold gas spraying, according to the preambles of claims 1 and 15.
Cold gas spraying is a coating method by which metal layers, for instance copper, silver, aluminum and the like, can be deposited onto a substrate, for instance a workpiece to be coated.
It is only to a limited extent possible to produce ceramic layers by cold gas spraying, via the deposition of so-called composite layers. In this case, ceramic particles are embedded in larger metal particles and thereby co-deposited onto the substrate. Through suitable heat treatment of the layers deposited in this way, a ceramic layer can be generated by temperature-induced diffusion of the ceramic particles and the metal matrix.
DE 10 2004 059 716 B3 discloses a cold gas spraying method. A carrier gas flow is generated, and particles are introduced into it. The kinetic energy of the particles leads to layer formation on a substrate. The substrate has a structural texture, which is transferred onto the layer being formed. Using a suitable composition of the particles, a high-temperature superconducting layer can thereby be produced on the substrate. Here again, subsequent heat treatment of the substrate provided with the layer is proposed.
In contrast to the typical thermal or plasma spraying methods such as vacuum plasma spraying (VPS), atmospheric plasma spraying (APS) and high velocity oxy-fuel flame spraying (HVOF), ceramic particles cannot be used directly in the cold gas spraying method since they generally do not adhere to the substrate.
It is an object of the invention to provide a method with which it is possible to deposit even nonmetallic layers, in particular ceramic layers, on a substrate or workpiece by means of cold gas spraying.
The object is achieved by a method according to the features of claim 1, and a device according to the features of claim 15. Advantageous refinements of the invention may be found in the dependent claims and the following description.
The invention firstly provides a method for depositing a nonmetallic, in particular ceramic, coating on a substrate by means of cold gas spraying. The method according to the invention comprises the method steps:
The reactive gas flow may comprise a carrier gas which is conventionally used for cold gas spraying. For example, it is conceivable for the reactive gas flow to comprise a carrier gas which is conventionally used for cold gas spraying and a reactive gas which is added to the carrier gas. It is likewise conceivable for the carrier gas itself to be the reactive gas. The reactive gas flow may, for example, be generated by a reactive gas or a mixture of reactive gas and carrier gas, which is pressurized in a container, flowing out of the container for example through a pipeline or hose or the like.
Compared with conventional cold gas spraying, the method according to the invention adds the possibility of depositing nonmetallic, in particular ceramic, coatings on a substrate. When carrying out the method according to the invention to generate ceramic coatings, for example, metal powders may firstly be used as particles as in the conventional cold gas spraying method. In order to form a ceramic coating, the material of the particles must react with another chemical substance and form a chemical compound. To this end, a reactive gas
is used which gives the desired chemical coating by chemical reaction with the material of the particles. For example, nitrogen or oxygen are suitable as a reactive gas. Other reactive gases may also be envisaged for the generation of, for example, carbides. In order to permit reaction of the metal particles with the reactive gas and initiate the formation of a ceramic coating, a carrier gas, which can likewise be used in conventional cold gas spraying, is added to the reactive gas. However, merely adding the generally inert reactive gas to the carrier gases is not sufficient in order to generate, for example, metal nitride compounds such as titanium nitride (TiN). To this end, the method according to the invention additionally comprises carrying out activation of the reactive gas by generating reactive gas radicals in the mixture flow comprising the particles and reactive gas. To this end, for example, immediately after emerging from a nozzle on the way to the substrate, the mixture flow containing the particles is passed through a radiofrequency electromagnetic field, for example through microwaves, and/or UV light. This leads to deliberate activation of the reactive gas, by which reactive gas radicals are created from the reactive gas molecules. The reactive gas radicals, which are highly reactive, initiate the formation of chemical bonds between the particles and the reactive gas so that a ceramic coating is deposited on the substrate.
In an advantageous embodiment of the method according to the invention, the reactive gas radicals are generated in the mixture flow by exciting the reactive gas molecules in the mixture flow by means of electromagnetic radiation with a frequency and flux density suitable for cleaving the reactive gas molecules into reactive gas radicals. The electromagnetic radiation may have its frequency tuned deliberately to
the reactive gas molecules to be activated, which are intended to be cleaved into reactive gas radicals. It is conceivable for the reactive gas molecules in the mixture flow to be excited by means of electromagnetic radiofrequency waves and/or microwaves and/or ultraviolet light, and/or laser light. All these sources of electromagnetic waves are freely available, and therefore allow economical implementation of the method according to the invention.
According to an advantageous embodiment of the invention, the method comprises the additional method step of expanding the mixture flow after injection of the particles into the reactive gas flow and before generation of the reactive gas radicals in the mixture flow. Reactive gas radicals can be generated more easily and with less energy expenditure in the expanded flow. It is conceivable for the expansion to be carried out in a Laval nozzle. A Laval nozzle is suitable in particular for expanding subsonic flows of cold gaseous fluids. The expansion is preferably carried out in an environment with a pressure level below standard conditions. The static pressure in the mixture flow can be reduced even further in this way, so that the formation of reactive gas molecules is even more readily possible and can be carried out with even less energy expenditure.
According to another advantageous embodiment of the invention, the method comprises the additional method step of delivering additional reactive gas to the surface, which is to be coated, of the substrate. The reaction between the particles and the reactive gas takes place only to a limited extent during transport of the mixture flow to the surface to be coated. The reaction between the particles and reactive gas takes place predominantly when the particles strike the substrate. Adding or supplying
reactive gas in the vicinity of the surface to be coated therefore ensures a high partial pressure of activatable reactive gas, so that complete reaction takes place between the particles and the reactive gas to create the coating material on the surface of the substrate.
In an advantageous embodiment of the method according to the invention, the particles are agglomerated nanoparticles. The reaction of the reactive gas and metal particles takes place commensurately more completely when the active surface area of the particles is larger in relation to their mass. The use of agglomerated nanoparticles therefore reliably leads to the generation of a fully reacted coating.
In another advantageous embodiment of the method according to the invention, the reactive gas flow comprises a carrier gas suitable for cold gas spraying. It is conceivable for the carrier gas itself to be the reactive gas. The reactive gas may also be added to the carrier gas. The reactive gas preferably comprises nitrogen. The reactive gas may also comprise oxygen.
In a particularly advantageous embodiment of the method according to the invention, at least some of the particles comprise a metal which forms a nonmetallic, in particular ceramic, coating material by chemical reaction with the reactive gas, or with the reactive gas radicals.
The invention secondly provides a device for depositing a nonmetallic, in particular ceramic, coating on a substrate by means of cold gas spraying. The device according to the invention comprises
The device according to the invention makes it possible to carry out a method according to the invention as described above, and thus allows the advantages of the method according to the invention to be used.
An advantageous embodiment of the device according to the invention comprises means for expanding the mixture flow after injection of the particles into the reactive gas flow and before generation of the reactive gas radicals in the mixture flow. This is advantageous because the entire particle surfaces therefore enter into the reaction kinetics. The
means for expanding the mixture flow may, for example, comprise a Laval nozzle.
The means for generating the reactive gas radicals in the mixture flow may, for example, comprise an electromagnetic radiofrequency and/or microwave generator and/or a light source emitting ultraviolet light and/or a laser light source.
Another advantageous embodiment of the device according to the invention comprises means for additionally delivering reactive gas to the surface, which is to be coated, of the substrate. This is advantageous in order to ensure complete reaction between the particles and reactive gas to form the coating material.
The invention will be explained in more detail below with the aid of the drawing, in which:
A device 1 as represented in
gas flow 5 in the mixing chamber 3. A mixture flow of reactive gas and particles 4 is thereby created at the exit of the mixing chamber 3. A Laval nozzle 6, in which the mixture flow of reactive gas and particles 4 is expanded, is arranged following the mixing chamber. A microwave generator 7 following the Laval nozzle 6 is used to generate reactive gas radicals in the mixture flow, which initiate formation of the coating material from the reactive gas and the particles. Directly after the microwave generator 7, the mixture flow comprising reactive gas radicals and particles 4 strikes a surface, which is to be coated, of the substrate 2, so that a ceramic coating of a chemical compound of the material of the particles 4 with the reactive gas, i.e. one which is created by chemical bonding 4 of the material of the particles to the reactive gas, is deposited on the surface of the substrate 2.
In the present invention, a carrier gas and metal powder as particles may firstly be used as in the conventional cold gas spraying method. In order to permit reaction of the metal particles with a reactive gas such as molecular oxygen O2 or molecular nitrogen N2, and thereby initiate the formation of ceramic layers, a reactive gas, for example molecular oxygen O2, is added to the carrier gas.
As will be demonstrated below with reference to the example of nitrogen N as a reactive partner, merely adding generally inert nitrogen gas to the carrier gas, or using nitrogen gas as a carrier gas which is at the same time the reactive gas, is not sufficient in order to generate, for example, metal nitride compounds such as titanium nitride TiN. In order to make this possible, activation of the reactive gas is
additionally carried out according to the invention. To this end, immediately after leaving the Laval nozzle 6 on the way to the substrate 2, the mixture flow containing the particles is passed through a radiofrequency electromagnetic field, which may for example be generated by microwaves, ultraviolet light or the like. This leads to deliberate activation of the reactive gas being used, so that the reactive gas molecules are cleaved to form reactive gas radicals. The reactive gas radicals, which are then highly reactive, make it possible to form chemical bonds between the metal particles 4 and the reactive gas in order to create metal-reactive gas compounds such as titanium nitride TiN, titanium oxide TiO2 and the like. The reactive gas may naturally also be supplied additionally at the substrate 2, since the reaction of the metal particles 4 with the reactive gas takes place only to a limited extent during transport in the device 1 according to the invention comprising the mixing chamber 3, the Laval nozzle 6 and the microwave generator 7; instead, it predominately takes place when the particles 4 strike the substrate 2. Adding the reactive gas to the carrier gas of the cold gas process is advantageous since a high partial pressure of activatable reactive gas can therefore be ensured at the substrate 2.
It is important to emphasize that the reaction of the reactive gas and metal particles 4 takes place commensurately more completely when the active surface area of the particles 4 is larger in relation to their mass. Agglomerated nanoparticles are therefore preferably used as the particles 4, so that a fully reacted coating is created on the substrate 2.
Advantages of the invention will be presented below with reference to the example of titanium nitride TiN. By means of a cold gas spraying method, it is economically possible to produce very thick wear-resistant layers having a layer thickness of up to a few millimeters,
which are comparable in terms of their properties to those generated by means of physical vapor deposition (PVD) but at the same time can have a layer thickness which is greater by a factor of 100. The invention therefore opens up the completely new areas of application in the field of wear protection. The invention likewise makes it possible to deposit high-quality oxidic layers, and in particular to deposit high-temperature superconductor materials (HTS materials). Here, activation of the reactive gas not only facilitates formation of the desired phase, but also increases in particular its rate of formation. The latter leads to commercially lucrative processes for the production of superconductively coated bands which represent the starting material for a multiplicity of electrical engineering components, such as for shape memory effect (SME) materials, generators, transformers, superconducting current regulators or limiters, and the like.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/DE2006/001751 | 9/29/2006 | WO | 00 | 3/5/2010 |