Patent Application
20200332377
The invention relates to a method for direct reduction of metal oxide-containing, preferably iron oxide-containing, starting materials, to produce metallized material by contact with hot reduction gas in a reduction unit. The product of the direct reduction is discharged from the reduction unit by a product discharge device which is flushed with seal gas and from which vent gas is drawn and subsequently de-dusted dry. The content of at least one gaseous constituent of the dry de-dusted vent gas is reduced. The invention also relates to a device for carrying out such a method.
In order to obtain metals from metal ores, it is necessary to lower the oxygen content in the ores. One method for lowering the oxygen content is so-called “direct reduction”, in which a reduction gas is allowed to act on the solid metal ore in a reduction unit. The solid product of the direct reduction is discharged from the reduction unit and can be processed further in different ways. For example, it is often hot-compacted, for example briquetted, in order to make it easier to handle, and to reduce its specific surface area in order that the procedure of reoxidation, for example as a result of reacting with atmospheric oxygen or H2O (for example in the form of steam), is made more difficult. It is also known, however, to process the solid product further in other units without compaction. It is often the case that the reduction unit in which the direct reduction proceeds is a so-called “reduction shaft”.
It is basically advantageous to protect the product against reoxidation between discharge from the reduction unit and then to subsequent devices, for example devices in which the briquetting proceeds, by handling the product under gas which, with respect to oxidation, is slow-reacting.
Particularly if the reduction gas is under a positive pressure in the reduction unit, it is necessary to ensure that, when removing the product, a simultaneous escape of the generally hot reduction gas is avoided. This occurs for example when a so-called “seal gas” is introduced into the device, by means of which the product is discharged from the reduction unit and which is, as a consequence, also referred to as a “product discharge device”. The seal gas is slow-reacting or inert with respect to reaction with the product and is under a pressure which is slightly above the pressure of the reduction gas in order, practically, for the seal gas to form a barrier against escape of the reduction gas.
In the case of iron ores, the product of the direct reduction is referred to, for example, as “direct reduced iron” (DRI) or “hot direct reduced iron” (HDRI) or “sponge iron” or “iron sponge”.
A method for direct reduction of metal oxides to produce metallized material by contact with hot reduction gas which is produced at least in part by catalytic reforming of natural gas. The heat for the endothermic reforming processes, which proceed during the reforming, is provided at least in part by combustion of a combustion gas. This is described for example in FIG. 1 of WO2011012452. It is referred to as a “MIDREX® method”. In such a MIDREX® method, the product is discharged from the reduction shaft, which is under elevated pressure, by means of a product discharge device. In this case, the product discharge device comprises a discharge member and a material-conveying device which is under a positive pressure, which pressure is lower in comparison with the reduction shaft, or is not under a positive pressure. A corresponding material-conveying device is, for example, often referred to as a “product discharge chamber” (PDC). For the purpose of sealing, that is for the purpose of preventing hot reduction gas from exiting the reduction shaft, slow-reacting seal gas is used, which is also often referred to as “bottom seal gas” (BSG) since it is intended to seal off the bottom end of the reduction shaft. This is shown for example in WO2008123962 and U.S. Pat. No. 4,188,022. The product discharge device is said to be flushed with the seal gas. In a MIDREX® plant, use is often made of dried flue gas from a reformer of a MIDREX® plant, which consists of approximately 80% nitrogen and approximately 20% carbon dioxide and is correspondingly slow-reacting with respect to oxidation of HDRI, as the BSG gas.
The BSG flows through the material column in the discharge member. In the present example, this is a material discharge tube filled with HDRI, also referred to as a “dynamic seal leg”, mostly from the point of introduction in the direction of the PDC and to a lesser extent in the direction of the reduction shaft. A large part of the BSG therefore flows into the PDC and has to be diverted therefrom. During the diversion from the PDC, the BSG, then referred to as “vent gas”, is laden with dust of the product of the direct reduction. The greater the amount of product of the direct reduction which is discharged by way of the PDC as dust, the less economical the direct reduction method is, since the dust cannot be used, or can be used only with increased effort, for, for example, steel production.
Within the context of this application, the term “vent gas” generally means “seal gas” which is drawn from a product discharge device and not only means seal gas which is diverted from the PDC of a MIDREX® method. The problem of dust being carried in seal gas always exists if seal gas flows through product of the direct reduction.
Release of vent gas into the environment necessitates de-dusting. At present, wet de-dusting is generally carried out, especially in the case of reduction of iron ores. Wet de-dusting results in product of the direct reduction which is discharged with the vent gas, for example iron sponge, entering a slurry system and subsequently having to be disposed of without being able to be used directly for the production of downstream products, for example, in the case of iron sponge, for steel production.
Owing to reactions proceeding between hot DRI, which is also referred to as “hot direct reduced iron” (HDRI) or “hot iron sponge”, and carbon dioxide, and owing to outgassing of the hot iron sponge, the vent gas can also contain traces of CO, carbon monoxide. Release of the vent gas into the environment then necessitates sufficient dilution.
Dilution of vent gas is also necessary in order to reduce its temperature or in order to drop below explosion limits for oxidizable constituents of the vent gas, such as CO carbon monoxide, H2 hydrogen, CH4 methane or other hydrocarbons, which have possibly passed from the reduction unit into the PDC.
In the case of dilution with air, also referred to as “infiltrated air”, relatively large quantities of infiltrated air are necessary, which causes large quantities of gas to be de-dusted, and for this reason the de-dusting is demanding in terms of apparatus and is energy-intensive.
It is the object of the present invention to provide a method and a device which allow simple use of the product of the direct reduction, which is discharged with vent gas, for the production of downstream products. Furthermore, it is sought to reduce the effort associated with de-dusting of the vent gas and with the release thereof into the environment. Specifically, it is sought to make possible simple use of iron sponge, which is discharged with the vent gas from the PDC of a MIDREX® method, as iron sponge product or in subsequent production of steel from the iron sponge.
The object is achieved by
The seal gas is slow-reacting or inert with respect to reaction with the product and is under a pressure which is slightly above the pressure of the reduction gas in order, practically, to form a barrier for the escape of the reduction gas. In a MIDREX® plant, use is made for example of dried flue gas from a reformer of a MIDREX® plant, which consists of approximately 80% nitrogen and approximately 20% carbon dioxide and is correspondingly slow-reacting with respect to oxidation of HDRI.
The vent gas is preferably only de-dusted dry and not de-dusted wet up to release into the environment.
Preferably, the metal oxides are iron oxides. However, according to the Richardson-Jeffes diagram, it is furthermore also possible, for example, for oxidic ores of nickel, copper, lead and cobalt to be reduced.
The method for direct reduction may be, for example, a method according to the type MIDREX® with catalytic reforming of hydrocarbons for producing a reduction gas, wherein the reduction gas is produced at least in part by catalytic reforming of a mixture of gaseous hydrocarbons, wherein the heat for the endothermic reforming processes which proceed during the reforming is provided at least in part by combustion of a combustion gas, as described for example in WO2011012448 and WO2011012452, and the full disclosure of which, especially with regard to the reforming, is encompassed by the present application. However, the method may also be for example a direct reduction method on the basis of coal gasification or a smelting-reduction plant, for example in a COREX® DR combined system. In these cases, it would be possible for example for seal gas to be obtained from the reduction gas furnace for heating the reduction gas since, in comparison with the MIDREX® method, a corresponding reformer is not present as a source.
The product of the direct reduction of iron oxide-containing starting materials, DRI or HDRI, is preferably hot-briquetted, for example processed to form hot briquetted iron (HBI). However, it can also be discharged in the hot state from the reduction shaft and can be used directly in a steelworks, for example by being added in a hot state into an electric arc furnace. The degree of metallization is the ratio between metallic iron and total iron in the HBI and is ≥88% for HBI. According to current International Maritime Organization (IMO) regulations, the density of HBI is ≥5 kg/dm3. The density of the hot-briquetted briquetting product may also be below this density, for example if production is carried out from particular raw materials or for particular purposes.
In the case of hot-briquetting, a briquette can be produced directly, or strands, which are also referred to as “slugs”, which either break themselves or are broken into smaller pieces by means of breakers, can be produced.
The iron sponge is delivered for example by means of a product discharge chamber (PDC) from the reduction unit to the devices in which the briquetting proceeds. As explained in the corresponding preceding passages of the introduction to the prior art, the product discharge device is charged with seal gas, that is seal gas is introduced into the product discharge device, and vent gas is drawn from the product discharge device. If there is no change to the composition of the seal gas in the product discharge device, the composition of the vent gas corresponds to the seal gas. In comparison with the seal gas introduced, the vent gas is more heavily laden with dust from the product.
According to the invention, the vent gas is de-dusted dry. In this way, the water management and slurry disposal, which are associated with wet de-dusting, are no longer necessary. Moreover, the product of the direct reduction, for example iron sponge, which is discharged from the product discharge device, for example from a PDC, as dust in the vent gas is separated dry and can therefore be used in a simple manner. The dry de-dusting can be realized in a single-stage or multi-stage, for example two-stage, manner. In the case of single-stage dry de-dusting, de-dusting solely by means of filters is for example possible. In the case of two-stage dry de-dusting, firstly coarse de-dusting by means of a cyclone or coarse hot filter and subsequently finer de-dusting by means of dry filters is, for example, possible. Owing to the temperatures of the vent gas, hot-gas filters, for example composed of ceramic materials, are preferred. The dry filters preferably exhibit low pressure loss. In the case of direct reduction of iron ore, the iron sponge is used as iron sponge product or in subsequent production of steel.
For example, the iron sponge separated during the dry de-dusting is preferably a coarse iron sponge separated by means of a coarse hot filter or cyclone. It can be reintroduced into the material-conveying device, for example into a PDC, for example under the action of gravitational force if the dry de-dusting is realized above the PDC.
For example, the dust separated during the dry de-dusting—preferably iron sponge, can be supplied to devices in which briquetting proceeds. Especially for briquetting, the use of the dust from the vent gas is advantageous since this dust generally has a particle size up to a maximum of 3 mm. In the case of briquetting, such dust leads to briquettes of high quality, for example having high density, which can be used further in a particularly economical manner. The dust which is separated during the dry de-dusting can also be recycled with fines which are obtained during the briquetting and which are for example <6 mm. The dust which is separated during the dry de-dusting, for example iron sponge, can also be reintroduced into the reduction unit as metal oxide-containing starting material.
Iron sponge separated during the dry de-dusting can also be supplied as HDRI to corresponding consumers in a steelworks since, in contrast with wet de-dusting, this iron sponge is not cooled during the dry de-dusting.
The dry de-dusted vent gas is substantially free of dust load and is still hot. It has a temperature of approximately 250-750° C. in a MIDREX® method, in which BSG is supplied, for example, at 20-80° C. and dusty vent gas from a PDC has a temperature of approximately 250-750° C. Infiltrated air is not supplied. Vent gas from wet de-dusting has a temperature of approximately 30-100° C.
In comparison with conventional wet de-dusting, it is also the case that significantly smaller quantities of gas have to be handled because, in the dry de-dusting according to the invention, dilution with infiltrated air does not take place prior to the de-dusting step. In a conventional method following a MIDREX® direct reduction, the dust-laden vent gas is diluted to approximately 10-30 times the volume.
Owing to the relatively high temperature and the small quantity of gas, the de-dusted vent gas can be easily freed of undesirable gaseous constituents, for example CO. The vent gas possibly contains gaseous oxidizable constituents, such as CO carbon monoxide, H2 hydrogen, CH4 methane or other hydrocarbons, which have possibly passed from the reduction unit into the PDC.
According to the invention, the content of at least one gaseous constituent of the de-dusted vent gas is thus reduced. The complete removal of the constituent is also encompassed here. Said reduction occurs by conversion into CO2 and/or into H2O—by catalytic conversion using oxygen O2 and/or H2O in the form of steam,
and/or
Such conversions proceed in an optimum manner for example for CO and oxygen at 200-800° C. Specifically, oxidation by combustion proceeds at approximately 600-800° C., and catalytic conversion proceeds at temperatures starting from 200° C.
In order to provide for the conversion into CO2 or into H2C optimum conditions, for example with respect to temperature or oxygen content or steam content, it is possible for example for nitrogen, air or other oxygen-containing and/or steam-containing gases to be supplied. It is also possible for use to be made of gases obtained in the direct reduction method—for example gases such as wet seal gas, dry seal gas, purge gas or bottom seal gas, which are obtained in a MIDREX® method and which differ, for example in terms of steam content and pressure level. After being freed of undesirable constituents in such a way, the vent gas can be released into the environment in a problem-free manner without having to be diluted further.
A further subject of the method is a device for carrying out a method according to the invention, which comprises
The reduction unit is for example a reduction shaft in which raw material is introduced at the top and product is discharged at the bottom. Reduction by means of reduction gas is realized during the passage through the shaft from the top downward following the gravitational force. Such a reduction shaft is operated for example in a MIDREX® method with reduction gas under a pressure of 0.03-0.3 MPag (positive pressure in comparison with the atmospheric pressure of the environment).
The product discharge device comprises, for example a discharge member and a material-conveying device. For example, these may be a material discharge tube with the connection of a seal gas supply line, and, for example, a cellular wheel conveyor.
In the case of a MIDREX® method. In comparison with the atmospheric pressure of the environment, the material-conveying device is under a positive pressure, which is lower in comparison with the reduction shaft, or not under a positive pressure. As already described in the introduction, a corresponding material-conveying device is usually referred to as a “product discharge chamber” (PDC) in a MIDREX® method. A discharge member is, in connection with the MIDREX® method, often referred to as a “dynamic seal leg” (see WO2008123962) or “dynamic gas seal”.
The vent gas removal line may depart for example from the PDC.
The vent gas removal line opens into a dry de-dusting device which is equipped, for example, with ceramic filter candles. The filter candles may also consist of CaSi fibers or AlSi or asbestos-like material. The dry de-dusting device may also comprise a cyclone for coarse de-dusting, and ceramic filter candles for fine de-dusting.
Dry dust from the product, for example dust from iron sponge, can, for example, be reintroduced into the PDC, or briquetting presses or material hoppers connected thereto can be provided with a supply, or the dust can be introduced into the reduction unit.
A diverting device for diverting dry de-dusted vent gas into the atmosphere diverts from the dry de-dusting device. The diverting device reduces the content of at least one gaseous constituent of the de-dusted vent gas. Thus, if appropriate, unwanted emissions can be reduced.
According to the invention, the device for reducing the content of at least one gaseous constituent of the de-dusted vent gas is a device for reducing the content
These are, for example, burner systems, and are, for example, noble metal-based catalysts, such as platinum, platinum/iron, platinum/ruthenium or platinum/palladium.
According to a preferred variant, the device for reducing the content of at least one gaseous constituent of the de-dusted vent gas is a device for reducing the CO content by
These are thus for example burner systems, and are thus for example noble metal-based catalysts, such as platinum, platinum/iron, platinum/ruthenium or platinum/palladium.
Preferably, the device for reducing the content of at least one gaseous constituent of the de-dusted vent gas, preferably the CO content, has at least one supply line for supplying oxygen-containing and/or steam-containing gases.
In comparison with a conventional method with wet de-dusting, the method according to the invention is more productive since the product discharged with the vent gas is not substantially lost as slurry for production of the metal product, but rather can be used easily as dry dust. Treatment of waste water from wet de-dusting is also not necessary, and as a result, outlay in terms of apparatus, investment costs and operating costs are reduced. Release of de-dusted vent gas into the environment is possible with less effort and is able to be realized in a simple manner with reduced content of undesirable constituents. The method according to the invention permits simple retrofitting into existing plants.
The present invention will be explained on the basis of schematically illustrated exemplary embodiments with reference to the following schematic exemplary figures.
In
Even though the invention has been illustrated and described in more detail by way of the preferred exemplary embodiments, the invention is not restricted by the examples disclosed, and other variations may be derived therefrom by a person skilled in the art without departing from the scope of protection of the invention.
The disclosure of the present application also encompasses the entire disclosure of WO08123962, U.S. Pat. No. 4,188,022, WO2011012448 and WO2011012452 incorporated herein by reference.
U.S. Pat. No. 4,188,022
| Number | Date | Country | Kind |
|---|---|---|---|
| 16173648.3 | Jun 2016 | EP | regional |
The present application is a 35 U.S.C. §§ 371 national phase conversion of PCT/EP2017/063974, filed Jun. 8, 2017, which claims priority of European Patent Application No. 16173648.3, filed Jun. 9, 2016, the contents of which are incorporated by reference herein. The PCT International Application was published in the German language.