The invention relates to a method for electromagnetic spot welding of moulded parts, and to a device for electromagnetic spot welding. Spot welding in the context of the present application produces a discontinuous weld at one point of welding by providing a stationary inductor that, under alternating voltage, generates an electromagnetic field. This is in contrast with continuous welding in which the inductor is moved over moulded parts to be welded together along a trajectory of welding. Spot welding and continuous welding may not be compared. Heat generation in the moulded parts to be welded may be completely different for instance.
A number of technologies exist for joining moulded parts, for instance fibre reinforced thermoplastic or thermosetting composite parts. Mechanical fastening and adhesive bonding are traditionally used to join two contact surfaces of the moulded parts. However, both mechanical fastening and adhesive bonding appear to be costly and time consuming. Mechanical fastening for instance requires expensive hole locating, drilling, shimming, and fastener installation, while adhesive bonding requires complicated surface pre-treatments that may involve chemical substances.
Electromagnetic welding may eliminate the use of separate fasteners and potentially offers the ability to join contact surfaces of moulded composite parts at relatively high speeds and little, if any, pre-treatments. Electromagnetic welding generates an electromagnetic field in an induction-sensitive component of one or more of the moulded part(s) to heat a heat meltable coupling means of the moulded part(s) to above a melting temperature of the coupling means. The contact surfaces of the moulded parts are joined to each other by the molten coupling means. The coupling means may for instance be a thermoplastic resin of one or more of the parts to be joined, or may be a separately applied thermoplastic resin. For welding thermoplastic and thermoset moulded parts together, the thermoplastic resin that the induction-sensitive component melts may function as a hot melt adhesive for instance.
A number of welding methods are available for creating a spot-welded connection between moulded parts such as fibre reinforced composite moulded parts. In resistance welding, a foreign material needs to be added to act as a welding element. For conduction welding, the composite parts or laminates are heated through and through resulting in a tool print in the surface, and ultrasonic welding requires a specific energy director material, and is very sensitive for geometrical tolerance and partial recrystallization, for instance. Known methods of electromagnetic spot welding may produce joined products of inferior quality, particularly in high-grade applications in which relatively high mechanical strength and load-bearing capacity of the welded connection is desired, such as in the aviation industry.
Another problem is that (spot) welded connections may not provide enough strength in a direction perpendicular to a plane of the welded moulded parts. So-called out-of-plane loads tend to delaminate (parts of) the (spot) welded moulded parts.
It is an object of the invention to provide an improved method and device for spot welding of moulded parts. It is another aim of the invention to provide a method and device for spot welding of moulded parts that may produce welded moulded parts with an increased resistance against out-of-plane loads and delamination.
The invention provides for this purpose a device for electromagnetic spot welding of moulded parts, comprising a pressurizing body; first displacing means configured for moving a pressurizing surface of the pressurizing body against the moulded parts or vice versa to join contact surfaces of the moulded parts to be fused by welding under pressure; wherein the pressurizing body further comprises an inductor provided in the pressurizing body and configured to generate an electromagnetic field in at least the contact surfaces of the moulded parts; shielding provided in the pressurizing body around at least a part of the inductor configured to protect against overheating; and a heat sink provided in between the inductor and the pressurizing surface in direct contact with the inductor and the pressurizing surface; whereby the inductor comprises cooling means configured for cooling the inductor, the shielding and the heat sink.
With the device it is possible to realize a good-quality spot welded connection between the moulded parts in a rapid and efficient manner, wherein the spot welded product has a particularly good mechanical load-bearing capacity. The moulded parts comprise a heat meltable coupling means and an induction-sensitive component. The claimed device generates an electromagnetic field in at least the contact surfaces of the moulded parts by means of the inductor of the pressurizing body, thereby heat melting the coupling means by heating the induction-sensitive component. The claimed device, comprising the features of the pressurizing body as claimed, is configured to provide a geometrically focused heated volume in the moulded parts.
The heat sink is provided between the inductor and the pressurizing surface and in direct contact with both. The material of the heat sink is electrically insulating yet thermally conductive, and is configured for extracting heat from the surroundings. The heat sink acts as a passive heat exchanger that transfers the heat generated in a top part of the moulded parts to the surrounding air, or to the cooling means of the inductor. Suitable materials for the heat sink have a high thermal conductivity, but very low electrical conductivity.
A preferred embodiment of the device comprises a heat sink having a planar dimension in contact with the pressurizing surface larger than a cross-sectional dimension of the inductor. This embodiment not only improves heat transfer but also provides a more spread-out and uniform pressure on the moulded parts.
The shielding is provided around at least a part of the inductor configured to protect against overheating. In an exemplary embodiment of the device, the pressurizing body has two side surfaces in addition to the pressurizing surface, and a top surface opposite the pressurizing surface, and the shielding is positioned between the inductor and the side surfaces.
The material of the shielding is preferably thermally insulating. Suitable materials from which the shielding may be manufactured include but are not limited to magneto-dielectric materials, and materials having metallic particles embedded in a binder, such as electrically insulated iron particles embedded in an organic binder. These materials are commercially available, for instance under the trade name Fluxtrol®. The geometry of the inductor, such as its cross-sectional shape, may in principal be chosen according to the needs. The cross-section may for instance be triangular, or circular. A useful embodiment relates to a device wherein the inductor has a quadrilateral cross-section.
The 3D shape of the inductor may also be chosen according to the needs. This may be relevant since, in some embodiments disclosed further below, the inductor not only needs to heat the moulded parts at the position of welding, but may also need to heat other parts of the device. The electromagnetic field in some embodiments therefore needs to be extended.
This may also be provided in an embodiment wherein the inductor of the pressurizing body comprises a first and a second inductor, or even a plurality of inductors.
In an embodiment, a device is provided wherein the inductor has a linear segment such that the inductor is configured to generate a substantially cylindrical electromagnetic field in at least the contact surfaces of the moulded parts. In this manner, the contact surface can be heated in highly selective manner, whereby a precise spot welded connection is obtained.
The position of the inductor in the pressurizing body may also be chosen according to the needs. In a practical embodiment of the device, the inductor is positioned in the pressurizing body such that the linear segment extends substantially parallel to the pressurizing surface of the pressurizing body.
In order to strengthen a spot weld made by the invented device, in particular in an out-of-plane direction that extends at a non-zero angle with the contact surfaces, a device according to an embodiment further comprises a mechanical fastener that is configured to be heated by the electromagnetic field generated by the inductor, or by other means, and second displacing means configured for moving the mechanical fastener towards the moulded parts and drive the heated mechanical fastener into the joined moulded parts to a position further than the contact surfaces of the moulded parts.
In such an embodiment, the second displacing means are preferably configured to drive the heated mechanical fastener into the joined moulded parts in a direction under a non-zero angle with the contact surfaces, and more preferably about perpendicular to the contact surfaces.
A practical embodiment relates to a device wherein the pressurizing body has a, optionally central, cavity that extends up to the pressurizing surface, and the second displacing means are configured for moving the mechanical fastener through the cavity.
The device according to the invention applies pressure onto the moulded parts to be spot-welded by means of the pressurizing body. Another embodiment of the device comprises counter-pressure means at a side of the joined moulded parts opposite to the first displacing means, either passive or active.
The device as claimed in a practical embodiment is provided at an end of a robotic arm or other tool as end-effector. This allows positioning the pressurizing body accurately on the joined moulded parts in order to effectuate a plurality of spot welds.
One or more of the moulded parts are preferably manufactured from a thermoplastic material which can be welded by fusion, although it is also possible to envisage arranging a thermoplastic material or a heat meltable adhesive only on the contact surface between the moulded parts as thermal coupling means.
Another aspect of the invention relates to a method for electromagnetic spot welding of moulded parts. The method comprises the steps of:
In the method, the moulded parts are generally provided with an electrically conductive component, for instance metal gauze, or this component is arranged between the moulded parts. Foucault currents or eddy currents are induced in the electrically conductive component by a fluctuating electromagnetic field which is generated by the inductor, preferably supplied with alternating current by a generator. Owing to the Joule effect, these Foucault currents generate the heat required to melt the heat meltable coupling means. By positioning the inductor above the position to be spot-welded, the moulded parts are mutually connected at the welded position.
The use of a substantially cylindrical electromagnetic filed in an embodiment of the method, enables a controlled, uniform and targeted heating, so that overheating in the moulded parts that need not be welded is prevented as far as possible. Overheating may result in degradation of material, and thereby cause undesirable weakening of the construction. A cylindrical electromagnetic field can moreover be made very narrow, up to a width of 10-20 mm.
For the purpose of heating the induction-sensitive component in the moulded parts, they must be in thermal contact with the heat meltable coupling means. This is for instance possible by mixing the induction-sensitive component and the heat meltable coupling means, such as in an injection mouldable compound.
Depending on the materials used, in particular the induction-sensitive component and the distance of the inductor from this component, a suitable power and frequency can be determined. The frequency determines inter alia the penetrative power of the electromagnetic field; the electric power of the inductor determines the strength of the fluctuating electromagnetic field and thereby the degree of heat generated in the induction-sensitive component.
It is advantageous if the heat meltable coupling means comprises a thermoplastic polymer. Thermoplastic polymers can be coupled in simple manner by fusion. Furthermore, it is easy to mix a thermoplastic polymer with an induction-sensitive component such as metal gauze or carbon fibres. Examples of particularly suitable thermoplastic polymers are polypropylene, polyamide, polyether imide, polyether ether ketone and polyphenylene sulphide, although the method is in principle suitable for any thermoplastic.
The component heatable by induction preferably comprises carbon fibres and/or a metal. These materials can be readily heated by induction and also have, in addition to electrical conduction, a good thermal conduction, whereby the generated heat is well distributed. Carbon fibres incorporated in a thermoplastic polymer are recommended because the carbon fibres also improve the material strength.
In another preferred embodiment of the method the component heatable by induction comprises ferromagnetic particles. Suitable particles are for instance described in WO0185827 and have the additional advantage that, when they reach the so-called Curie temperature thereof, they lose their magnetic dipoles, whereby they do not heat any further. This can form a protection against overheating.
The Foucault currents or eddy currents induced in the contact surface are bounded by the geometry of the moulded parts. Edges, corners and holes in the moulded parts influence the distribution of Foucault currents and therefore also influence the heat developed. Such disruptions of the field may result in heating of components which do not have to be heated for the welding process. Conversely, it is also possible that some parts are difficult to heat. These problems can be solved by repositioning the boundaries of the area where Foucault currents may begin to occur at determined locations of the thermoplastic moulded parts. With this preferred embodiment, parts that were formerly difficult to heat can nevertheless be heated and high temperatures at undesired locations can be prevented.
Another embodiment of the method further comprises moving a mechanical fastener that is configured to be heated by the electromagnetic field generated by the inductor, or by other means, by second displacing means towards the moulded parts and driving the heated mechanical fastener into the joined moulded parts to a position further than the contact surfaces of the moulded parts.
Preferably, the heated mechanical fastener is driven into the joined moulded parts by the second displacing means in a direction under a non-zero angle with the contact surfaces, preferably about perpendicular to the contact surfaces.
In a practical embodiment, the pressurizing body has a cavity that extends up to the pressurizing surface, and the second displacing means move the mechanical fastener through the cavity. The cavity may be positioned in a random position but is preferably positioned about centrally in the pressurizing body.
A pressure may be applied at a side of the joined moulded parts opposite to the first displacing means by counter-pressure means.
For application in the method as claimed in the invention, the inductor is connected to an alternating current generator, wherein the alternating current generator is electrically connected to the electrical connecting means of the inductor. Usable frequencies lie generally between 0.1-10 MHz. A frequency between 0.1 and 0.5 MHz is preferably used, and more preferably a frequency between 0.15 and 0.4 MHz. At such a preferred frequency an optimal balance is achieved between penetrative power of the electromagnetic field and rate of heating.
The inductor preferably has a plurality of windings. Such an inductor may be embodied compactly and preferably may be provided with flat side surfaces. It may be suitable for precisely determined induction.
It is advantageous if the inductor is substantially flat. This is possible for instance by embodying the inductor as an electrical conductor lying in one plane. Such a flat inductor is exceptionally compact and suitable for applying an electromagnetic field at a determined position in very precise and uniform manner.
In a further preferred embodiment the inductor is provided with at least one feed channel adapted for passage of a cooling medium, such as in sheath cooling. The temperature of the inductor can hereby be held constant during use, this also being favourable for the electrical resistance of the inductor. The cooling medium is preferably a liquid such as water, with a high heat capacity. The induction part can for instance be a metal tube bent into the desired form, through which the cooling medium is pumped while an electromagnetic field is caused through the metal of the tube itself with an alternating voltage.
The invention will now be elucidated with reference to the following figures, without however being limited thereto. In the figures:
As shown in more detail in
The robotic arm 50 is programmed to move a pressurizing surface 100 of the pressurizing body 10 against the moulded parts (2, 3) or vice versa. As shown in
According to
A shielding 12 is also provided in the pressurizing body 10 around at least a part of the inductor 11. The shielding is configured to protect against overheating, and is thereto made from a suitable heat isolating material, such as Fluxtrol®. The shielding 12 comprises a plate like structure and is positioned between the inductor 11 and the side surfaces (101a, 101b) of the pressurizing body 10.
The invented device 10 further comprises a heat sink 13 that is incorporated in the pressurizing body 10 and is provided in between the inductor 11 and the pressurizing surface 100. The heat sink 13 moreover is positioned such that it is in direct contact with (a lower surface of) the inductor 11 and the pressurizing surface 100. Additional heat sink material 13a may also be provided between inductor parts 11, if appropriate. The heat sink 13 may be embodied as a plate like structure that moreover, may have a planar dimension 106 in contact with the pressurizing surface 100 that is larger than a cross-sectional dimension 110 of the inductor 11. The heat sink 13 is preferably made from a ceramic material.
As also shown, the inductor 11 is provided with sheath cooling 111, for instance embodied by a conduit through which a cooling liquid like water is running. The sheath cooling not only cools the inductor 11, but is also adapted to cool the shielding 12 and the heat sink 13, at least partly.
The embodiment shown in the figures further comprises a mechanical fastener in the form of a ribbed rivet 6 that is configured to be heated by the electromagnetic field generated by the inductor 11, or by other means, such as a separate thermal, IR, . . . heater (not shown). The device 1 in this embodiment is also equipped with second displacing means in the form of a plunger 7, configured—as shown in
With reference to
In an initial step (
In a subsequent step, the pressurizing surface 100 of the pressurizing body 10 is moved against the moulded parts (2, 3) or vice versa with the robotic arm 50 such that contact surfaces (20, 30) of the moulded parts (2, 3) to be fused by spot welding are brought together or joined (but not welded) under pressure. The moulded parts (2, 3) comprise a heat meltable coupling means and an induction-sensitive component to heat them up under the influence of an electromagnetic field, produced by the inductor 11. Thereto, the moulded parts (2, 3) may be manufactured from a thermoplastic polymer reinforced with carbon fibres, wherein the carbon fibres may serve as induction-sensitive component, whereas the thermoplastic polymer may serve as heat meltable coupling means. The moulded parts (2, 3) can for instance comprise carbon fibre-reinforced polyphenylene sulphide, for instance with a material thickness of 1-3 mm. The first moulded part 2 has a folded edge, and may for instance represent a stiffener, while the second moulded part 3 is a flat plate. Obviously, both moulded parts (2, 3) may have another shape, such as being curved.
Referring to
The above procedure may be repeated for another position where a spot weld needs to be made. The pressuring means 10 are moved to this other position and the sequence of events shown in
Another embodiment of the invention is shown in
In a next step, the heated rivet 6 is moved by the plunger 7 towards the joined moulded parts (2, 3) that are heated by the electromagnetic field generated by the inductor 11 over a volume 22. This volume 22 may be a bit larger than volume 21, for instance because the rivet 6 is also heated. The plunger 7 moves along the cavity 103 that extends up to the pressurizing surface 100 of the pressurizing body 10, and thereby moves the heated rivet 6 through the cavity 103.
Referring to
Referring to
In a final step, the pressuring body 10 is removed from the spot welded and mechanically riveted moulded parts (2, 3) with the robotic arm 50.
The above procedure may be repeated for another position where a riveted spot weld needs to be made. The pressuring means 10 are moved to this other position and the sequence of events shown in
Referring to
A shielding 12 is also provided in the pressurizing body 10 around at least a part of the inductor 11. The shielding is configured to protect against overheating, and is thereto made from a suitable heat isolating material, such as Fluxtrol®. The shielding 12 comprises a plate like structure and is positioned over the inductor 11 and further between the inductor 11 and the side surfaces (101a, 101b) of the pressurizing body 10.
The invented device 10 in the embodiment shown further comprises a heat sink 13 that is incorporated in the pressurizing body 10 and is provided between the inductor 11 windings and in between the inductor 11 and the pressurizing surface 100. The heat sink 13 moreover is positioned such that it is in direct contact with (a lower surface of) the inductor 11 and the pressurizing surface 100. The heat sink 13 may be embodied as a plate like structure that moreover, may have a planar dimension 106 in contact with the pressurizing surface 100 that is larger than a cross-sectional dimension 110 of the inductor 11. The heat sink 13 is preferably made from a ceramic material.
As also shown, the inductor 11 is provided with sheath cooling 111, as described above for other embodiments.
In an initial step of the method according to the present embodiment (
In a subsequent step, shown in
Referring to
The above procedure may be repeated for another position where a spot weld needs to be made. The pressuring means 10 are moved to this other position and the sequence of events shown in
| Number | Date | Country | Kind |
|---|---|---|---|
| 2027111 | Dec 2020 | NL | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2021/084262 | 12/3/2021 | WO |