Method and device for processing preforms

Abstract

A method and a device for processing preforms which are made of a thermoplastic plastic material and are blow molded into containers. In a first production process, the preforms are produced by injection molding in the area of an injection molding tool. At least some areas of the preforms are impinged upon by a cooling device. The preforms are deformed by applying negative pressure, wherefore the cooling device can be made at least in part of a porous material.

Description

The invention relates to a method for processing preforms made from a thermoplastic plastic and intended for blow molding into containers and which are produced by injection molding in an injection molding tool and are deformed after removal from the injection molding tool.

The invention further relates to a device for processing preforms made from a thermoplastic plastic and intended for blow molding into containers and which are produced by injection molding in an injection molding tool, in which the preforms are impinged upon by at least one cooling device.

A method for processing preforms is described, for example, in PCT-WO 97/39874. Here the preforms, after removal from the injection tool, are transferred into cooling sleeves and pressed against the wall of the cooling sleeve by being impinged with internal pressure. In this manner the contact of the preform with the wall of the cooling sleeve is maintained during the entire cooling procedure, since any shrinkage of the preform as a result of cooling can be compensated for by the internal pressure acting upon it.

A blow molding deformation of preforms into containers inside a blow mold is disclosed in DE 41 28 438 A1. In this case the blow mold is provided with porous plugs which are connected to a pressure source. Compressed air is applied to the porous plugs providing a compressed air cushion which prevents surface damage to the blown container from the material sliding on the inner surface of the blow mold.

The object of the present invention is to improve a method of the kind described at the outset and which supports production of preforms requiring little time and with a simple physical layout.

This object is achieved according to the invention in that the preforms are deformed by the action of negative pressure.

A further object of the invention is to construct a device of the kind described at the outset which facilitates processing of the preforms by means of a simple mechanical design and at a low production cost of the device.

This object is achieved according to the invention in that at least part of the area of the cooling device is formed from a porous material.

The deformation of the preforms by the action of negative pressure following the manufacture by injection molding of the preforms confers a series of advantages. One advantage is that the preform can be drawn against the walls of a cooling sleeve by an external negative pressure and in this way direct contact between the preform and the wall of the cooling sleeve is maintained throughout the entire cooling process.

A further advantage can be seen in that negative pressure can be applied so that a deformation of the preform can take place longitudinally, radially and/or in a circumferential direction relative to the longitudinal axis of the preform, so that the preform can be given a conformation differing from the contour of the injection molding tool cavities. More particularly, the possibility exists of generating, by application of negative pressure, a distribution of material in the wall of the preform which would be beneficial for the subsequent production of oval bottles by blow molding. In this way, varying wall thickness could be provided in the circumferential direction of the preform.

Yet a further advantage consists in that preforms that are unintentionally deformed or have not been molded to their full extent by the injection molding tool can be remolded. In this way any warped preforms can be corrected or preform deformations compensated for. More particularly it is considered that, in the use of the method according to the invention and/or the device according to the invention, cycle times in the area of the injection molding tool can intentionally be reduced, or increased tolerances specified in the tool geometries of the injection molding tool. In such an intentionally premature deformation of the preform, warping of a preform that is ejected when it is too hot or the formation of shrink marks can be accepted, since these defects in the preform can be compensated for during remolding by the application of negative pressure. The very costly injection tool can in this way be operated with an increased productivity.

A typical deforming process takes place in such a way that the negative pressure acts on the preform externally.

It is also possible to have the negative pressure act on the preform internally.

A preferred embodiment consists in that the preforms are impinged by negative pressure inside a cooling device.

A low-cost supply of negative pressure can be achieved by applying the negative pressure to the preform through a porous material.

To achieve a uniform distribution of the negative pressure it is proposed that the negative pressure be applied to the porous material through negative pressure channels.

Handling of the preforms can be facilitated by the fact that the preforms are locally acted on by a pressurizing medium.

An additional impact on the sequence of the process can arise from the fact that the preforms are temporarily acted on by a pressurizing medium.

Improved control means are thereby provided to apply negative pressure to the preforms through local porous inserts.

An input of locally varying pressure conditions along an inner boundary of the cavity receiving the preform can be achieved by means of local porous inserts some of which are controllably connected to a pressure source and to a negative pressure source by means of control valves.

Deformation of the preform from the inside outwards can be achieved through the use of a porous (inner) mandrel.

A locally limited deformation of material is supported by applying local negative pressure on the preform from the mandrel.

A typical application consists of deforming the preform as an intermediate step in a single-stage injection-blow process.

It is also possible for the deformation of the preform to be performed as an intermediate step in the performance of a dual-stage injection-blow process.

An advantageous embodiment of the invention can be achieved by locating the porous material in the area of a cooling sleeve.

To provide sufficient mechanical stability, it is proposed to configure the porous material as an insert held in place by a frame.

Application of negative pressure inside the porous material with low flow resistances is achieved by locating at least one negative pressure channel in the area of the insert.

According to a further design embodiment, at least one cooling channel is located in the region of the frame.

The screening off of pressure from the outer environment can be achieved by covering at least some of the area of the insert with a seal.

To enable a pressure-supported mobility of the preform relative to the insert of porous material, it is proposed that the negative pressure channel extend into a cavity in the insert.

Targeted local input of the action of the pressure ratios can be achieved by covering at least some of the area of the mandrel with a seal.

For mere partial remolding of the preform, it is conceivable that the mandrel be covered by a seal in the region of the round end.

A further variant for remolding the preform has the mandrel provided with at least one membrane that defines a distributor chamber.

A typical choice of material would be to form the porous material from a porous metal.

Particularly good thermal conductivity can be attained by using aluminum as the porous metal.

A further embodiment has a sintered metal used as the porous material.

These materials can be employed with variable pore sizes, from as small as a few μm and upwards. The smaller the pore size, the better the surface quality of the preform. Too small a pore size leads to too high a pressure/vacuum requirement. Moreover, small pores tend to get blocked by dust.

The following typical porous (air-permeable) materials are commercially available:

• METAPOR® PORTEC AG;
• “ultraporex®” ultarfilter [sic] international AG;
• “PorceraxII®” International Mold Steel Inc.;
• “KuporeX™” KUBOTA Corporation.

The drawings schematically present typical embodiments of the invention. Shown are:

FIG. 1 a cross-section through a cooling device in which a cooling sleeve is formed from a porous element;

FIG. 2 an embodiment modified in respect to FIG. 1, in which both overpressure and negative pressure can be applied to the preform through the porous element;

FIG. 3 a cross-section through an embodiment in which are employed a quantity of porous inserts spatially separated from each other and which are controllably connectable to overpressure and/or negative pressure;

FIG. 4 a partial representation of a vertical section through a device in which a mandrel for the preforms made of porous material is used for a partial remolding in the direction of the longitudinal axis of the preforms;

FIG. 5 an embodiment, modified in respect to FIG. 4, in which the mandrel is configured for a complete remolding of the preform;

FIG. 6 an embodiment, modified in respect to to FIG. 5, in which the molding forces are applied to the preform through a membrane mounted on the mandrel;

FIG. 7 a cross-section through a preform located in an insert of porous material;

FIG. 8 a cross-sectional representation according to FIG. 7 of the molding of the preform through the effects of negative pressure and

FIG. 9 a schematic cross-sectional representation of a molded preform according to FIG. 8 and of a corresponding oval container contour after blow molding of the preform.

FIG. 1 shows a cross-section through a device for the processing of preforms (1), which has a frame (2) and an insert (3) in a porous material. The term “porous material” as used here includes both open-pored foamlike structures and sintered materials, or other comparable material structures. Owing to their high thermal conductivity, open-pore metal foams, for example of aluminum, have particularly proven themselves.

The preform (1) consists of a thermoplastic material, typically of PET (polyethylene phthalate), and is provided with a side wall (4), a support ring (5) and a mouth cutout (6). An internal space (7) of the preform extends along the preform longitudinal axis (8).

A negative pressure channel (9) extends through the frame (2) and is connected to a negative pressure channel (10) inside the insert (3). Also located in the area of the insert (3) are cooling channels (11) through which a cooling medium can circulate. In the region of the face (12) of the frame (2) a face of the insert (3) is closed off by a seal (13) to prevent the intake of ambient air when negative pressure is applied.

The preform (1) is introduced into a cavity (14) of the insert (3) in such a way that the support ring (5) abuts the area of the face of the insert (3). When negative pressure is applied to the insert (3), air located between the preform (1) and the cavity (14) is extracted and the ambient pressure in the inner space (7) of the preform (1) presses the side wall (4) of the preform (1) against the confining surface (15) of the cavity (14). The material contact thus caused leads to an improved cooling of the preform (1) and contributes to the preform (1) assuming the shape of the confining surface (15).

In the embodiment according to FIG. 2 the negative pressure channel (10) extends as far as the cavity (14) of the insert (3). Further, cooling channels (11) are located in the area of the frame (2). Additionally to the negative pressure channel (9), a pressure medium channel (16) is located in the area of the frame (2) and discharges into a pressurizing medium connection (17) of the insert (3). Preferably, the pressurizing medium line is located at a short distance from the seal (13). In this way a flow of air is induced through the cavity (14) in the direction of the negative pressure channel (9), facilitating the introduction of the preform (1) into the cavity (14) and preventing scratching of the preform (1) from contact with the confining surface (15). This further prevents uneven contact of the preform (1) with the insert (3), which can lead to uneven cooling of the preform (1).

In the embodiment according to FIG. 3 the cavity (14) is formed in the area of the frame (2) and a number of porous inserts (3) are arranged in the area of the confining surface (15) of the cavity (14). Here, the porous inserts (3) are spatially separated from each other. Additionally, the inserts (3) are each connected with supply channels (18) which are controllably connected by means of control valves (19) to a pressure source (20) or a negative pressure source (21). In this embodiment, too, the negative pressure channel (9) extends into the area of the cavity (14). To ease the introduction of the preform (1) into the cavity (14), at first vacuum is applied only to the negative pressure channel (9). As soon as the preform (1) is fully located in the cavity (14), the negative pressure source (21) delivers a higher negative pressure in order to press the preform (1) against the confining surface (15).

The inserts (3), spatially separated from each other, form nozzle-type arrangements, which can cause local deformation of the preform (1) or generate compressed air cushions for the preforms (1). More particularly, the possibility exists of introducing controllably hot compressed air through the inserts (3) so as to heat the preform (1) locally to achieve a specified deformation.

In the embodiment according to FIG. 4, the preform (1) is acted upon by a mandrel (22) which is formed from a porous material. The mandrel (22) is provided with a channel for a pressurizing medium (23). The channel for the pressurizing medium (23) can provide both overpressure and negative pressure, depending on control settings. To prevent pressure losses the mandrel (22) is externally provided with a seal (24) for part of its area. In the embodiment according to FIG. 4 the mandrel (22) is configured for only regional remolding of the preform (1) in the area of the mouth cutout (6) and of a part of the sidewall (4) oriented towards the mouth cutout (6). In the region of the round end (25), therefore, the mandrel (22) also bears a seal (26).

In the embodiment according to FIG. 5 the mandrel (22) is configured for a remolding of the preform (1) along the total extension of the longitudinal axis (8) of the preform. The mandrel (22) therefore possesses a contour that is altered in respect of the embodiment shown in FIG. 4. A seal (26) in the region of the round end (25) is not required in this embodiment. As well, when the preform (1) is acted upon by the mandrel (22), according to the embodiment shown in FIG. 5, the preform (1) can be cooled by cooling air (27) acting on it externally.

In the embodiment according to FIG. 6 the pressurizing medium channel (23) is connected to distributor chambers (28) which are sealed off by membranes (29). When pressure is applied to the pressurizing medium channel (23) the membranes (29) are pressed against the side wall (4) of the preform (1) and cause the deformation of the preform (1). As well, the force generated by the membrane (29) can deform the preform (1) either against the inner wall of a cooling sleeve or as otherwise specified.

FIG. 7 shows a cross-section through an insert (3) with a preform (1) held in the cavity (14). The insert (3) is held in place by frames (2).

After application of negative pressure, the preform (1) according to FIG. 1 is molded into a preform as shown in FIG. 8. More particularly, it can be recognized in FIG. 8 that a varying wall thickness is created by deforming circumferentially. The preform configuration according to FIG. 8 is particularly suited for the production of oval bottles.

FIG. 9 shows the positioning of the preform (1) according to FIG. 8 for a container contour (30) of a container with oval cross-section. The material distribution in the preform (1) is selected so that those areas which are only relatively slightly extended in the subsequent blow molding will be formed more thinly than those areas which are more strongly extended in blow molding. With appropriate material distribution a blow-molded container can be given very uniform wall thicknesses and consequently uniform material characteristics.

In a combined alternating loading of the insert (3) with negative pressure and overpressure a cleaning of material can be simply performed so that, with no preform (1) in place, application of a pressurizing medium can blow impurities away. Separation of the preform (1) from the mandrel (22) can also be effected by pressurizing the mandrel (22). In a combined use of the mandrel (22) and an insert (3) of porous material, the separation of the preform (1) from the mandrel (22) can also be facilitated by an external application of negative pressure.

Claims

1. Process for processing preforms made from thermoplastic plastic and intended for blow molding into containers and in which the preforms are manufactured in an injection molding tool using injection molding technology and after removal from the injection molding tool are deformed, characterized in that the preforms (1) are deformed by the action of negative pressure.

2. Process according to claim 1, characterized in that the negative pressure acts externally on the preforms (1).

3. Process according to claim 1, characterized in that the negative pressure acts internally on the preforms (1).

4. Process according to claim 1, characterized in that negative pressure is applied to the preforms (1) inside a cooling device.

5. Process according to claim 1, characterized in that negative pressure is applied to the preforms (1) through a porous material.

6. Process according to claim 1, characterized in that the negative pressure is supplied to the porous material through negative pressure channels (10).

7. Process according to claim 1, characterized in that the preforms (1) are locally impinged upon by a pressurizing medium.

8. Process according to claim 1, characterized in that the preforms (1) are temporarily impinged upon by a pressurizing medium.

9. Process according to claim 1, characterized in that the application of negative pressure to the preforms (1) takes place through local porous inserts (3).

10. Process according to claim 1, characterized in that local porous inserts (3) are temporarily and controllably connected by means of control valves (19) to a pressure source (20) and to one or more negative pressure sources (21).

11. Process according to claim 1, characterized in that deforming of the preform (1) is carried out using a porous mandrel (22).

12. Process according to claim 1, characterized in that a local negative pressure is exerted on the preform (1) from the mandrel (22).

13. Process according to claim 1, characterized in that the deformation of the preform (1) is carried out as an intermediate step in a single-stage injection-blow process.

14. Process according to claim 1, characterized in that the deformation of the preform (1) is carried out as an intermediate step in a dual-stage injection-blow process.

15. Device for processing preforms from a thermoplastic plastic, intended for blow-molding into containers and manufactured in an injection molding tool using injection molding technology, and in which the preforms are at least for part of their area acted upon by a cooling device, characterized in that the cooling device is at least for part of its area made of a porous material.

16. Device according to claim 15, characterized in that the porous material is located in the area of a cooling sleeve.

17. Device according to claim 15, characterized in that the porous material is formed as an insert (3), which is held in place by a frame (2).

18. Device according to claim 15, characterized in that at least one negative pressure channel (10) is located in the region of the insert (3).

19. Device according to claim 15, characterized in that at least one cooling channel (11) is located in the area of the insert (3).

20. Device according to claim 15, characterized in that at least one cooling channel (11) is located in the area of the frame (2).

21. Device according to claim 15, characterized in that the insert (3) is covered for at least part of its area by a seal (13).

22. Device according to claim 15, characterized in that the negative pressure channel (10) extends into the area of a cavity (14) of the insert (3).

23. Device according to claim 15, characterized in that the insert (3) is provided with a pressurizing medium connection (17).

24. Device according to claim 15, characterized in that the frame (2) has at least two inserts (3) made from a porous material and spatially separated from each other.

25. Device according to claim 15, characterized in that the separate porous inserts (3) can be controllably connected to a pressure source (20) and to one or more negative pressure sources (21).

26. Device according to claim 25, characterized in that the inserts (3) can be connected to the pressure source (20) and at least one negative pressure source (21) by at least one control valve (19).

27. Device according to claim 15, characterized in that the mandrel (22) is formed of a porous material for at least part of its area.

28. Device according to claim 15, characterized in that the mandrel (22) is covered by a seal (24) for at least part of its area.

29. Device according to claim 27, characterized in that the mandrel (22) is covered by a seal (26) in the region of its round end (25).

30. Device according to claim 15, characterized in that the mandrel (22) is provided with at least one membrane (29) which defines a distribution chamber (28).

31. Device according to claim 15, characterized in that the porous material is made from a thermally conductive material.

32. Device according to claim 31, characterized in that the porous material is a porous metal, such as aluminum, steel or a copper alloy.

33. Device according to claim 15, characterized in that the porous material is a sintered metal.