METHOD AND DEVICE FOR PRODUCING THREE-DIMENSIONAL MODELS USING A BINDING AGENT SYSTEM

Abstract

The invention relates to a method, a device and a binding agent system for producing three-dimensional models.

Description

FIELD OF THE INVENTION

The invention relates to a method and a device as well as a binder system for producing three-dimensional models.

A method for producing three-dimensional objects from computer data is described in the European patent specification EP 0 431 924 B1. In this method, a particulate material is applied in a thin layer to a platform, and a binder material is selectively printed on the particulate material, using a print head. The particle area onto which the binder is printed sticks together and solidifies under the influence of the binder and, if necessary, an additional hardener. The platform is then lowered by a distance of one layer thickness into a build cylinder and provided with a new layer of particulate material, which is also printed as described above. These steps are repeated until a certain, desired height of the object is reached. A three-dimensional object is thereby produced from the printed and solidified areas.

After it is completed, this object produced from solidified particulate material is embedded in loose particulate material and is subsequently removed therefrom. This is done, for example, using an extractor. This leaves the desired objects, from which powder deposits are removed, for example by manual brushing.

Of all the layering techniques, 3D printing based on powdered materials and the supply of liquid binder is the fastest method. This method may be used to process different particulate materials, including natural biological raw materials, polymers, metals, ceramics and sands (not an exhaustive list).

For example, a solid in the particulate material may be used as the binding system. This solid is dissolved by means of a solvent which is expelled from the ink-jet print head. After the solvent evaporates, the particles stick together in the desired locations.

The component may be removed from the remaining loose powder after a certain waiting period. The waiting period is generally long, since the solvent is only slowly released from the dissolved material. The components are often weak after unpacking and can be plastically deformed. The volatilization of the solvent produces a certain deposit buildup on the component, which must be removed manually after unpacking. The solvent may additionally attack the print head. Moreover, the dissolution process and subsequent resolidification causes shrinkage in the component and thus also geometric deviations.

A solvent may also be loaded with molecules or particles and then used. This may reduce shrinkage. The aggressiveness of the solvent may also be decreased while maintaining the same component strength. However, the solvent must be completely removed before unpacking, and the problem of deposit buildup occurs here as well.

Another option is to use a system that chemically results in a solidification of the printed fluid and thereby causes a binding of the particles. The system components are kept separate in the system, if possible. The desired solidification reaction does not occur until the printing process. One example of a system of this type may be a method known as the cold resin process. An acid-encased sand is brought into contact with furfuryl alcohol. This results in a chemical reaction which causes the previously liquid components to be converted to a cross-linked plastic.

These systems significantly reduce the aforementioned shrinkage. The monomers used nevertheless present a danger to the print head. The monomers for processes of this type often have an aggressiveness that is comparable to that of solvents. The more or less latent cross-linked plastics pose a permanent risk to the print head, since they may solidify at any time, due to contaminants or undesirable catalysis reactions, and thus damage the print head.

Due to their high reactivity, both systems are hazardous material systems which may be harmful to the environment and may be used only in industrial environments.

Another way to further minimize the aforementioned problems is to use an initiator system which is not present in the powder. Radiation-hardening systems are frequently described in the literature. They have certain disadvantages, depending on the chemical and physical hardening system. In the case of UV-hardening systems, for example, the complete, layer-by-layer hardening is a disadvantage, since it results in a delay in the build process. Another disadvantage is that no layer bonding occurs with excessively hard irradiation. Pure IR-hardening systems also suffer from this problem.

One object of the invention was therefore to provide a binder system, a method and a device which avoids or at least reduces the disadvantages of the prior art.

BRIEF DESCRIPTION OF THE INVENTION

In one aspect, the invention comprises a method for producing three-dimensional (3D) molded bodies (components) by means of 3D printing.

In another aspect, the invention comprises a device for carrying out the 3D printing method according to the invention.

In one aspect, the invention comprises a binder system which includes at least two components.

DETAILED DESCRIPTION OF THE INVENTION

A number of terms in the invention are explained in greater detail below.

Within the meaning of the invention, “3D printing methods” are all methods known from the prior art which facilitate the construction of components in three-dimensional molds and are compatible with the described method components and devices. In particular, these are powder-based methods, for example SLS (selective laser sintering).

A “binder” or “binder system” within the meaning of the invention is composed of two components and generally relates to a novolak or resol system having a solvent. All known 3D printing-compatible phenols and alcoholic and aqueous solvents may be used which are known to those skilled in the art and therefore do not need to be described in greater detail here. Special components and phenols are indicated in the following description. Acids or bases are required for producing the novolak or resol systems of the invention, it being possible to use all acids and bases known for novolaks and resols which are known to those skilled in the art.

The “prepolymerisates” contained in the binders of the invention may vary depending on the application and are adapted to the other material components, such as particulate materials.

All materials known for powder-based 3D printing, in particular sands, ceramic powders, metal powders, plastics, wood particles, fibrous materials, celluloses and/or lactose powders, may be used as “particulate materials.” The particulate material is preferably a dry, free-flowing and a cohesive, firm powder.

“Temperature regulation” of the particulate material is understood to mean that the powder material applied to the build space is held in its totality within a certain temperature window.

Within the meaning of the invention, a “heating” or “heat treatment” after the application of binder is the selective heating of the material areas provided with binder for building up the component. The temperature is significantly increased compared to the ambient temperature and the temperature-regulated particulate material on the build space.

According to the invention, the selective heating is carried out no earlier than after each second application of particulate material or after a constant or varying number of application steps. Within the meaning of the invention, the particulate material is distributed evenly over the build space and is smoothed off before another application of particulate material takes place.

Within the meaning of the invention, “selective binder application” or “selective binder system application” may take place after each particulate material application or irregularly, depending on the requirements of the molded body and for the purpose of optimizing the production of the molded body, i.e., non-linearly and not in parallel after each particulate material application. “Selective binder application” or “selective binder system application” may thus be set individually and during the course of producing the molded body.

“Finishing treatment steps” or “additional treatment steps” within the meaning of the invention are all methods known to those skilled in the art, to which the molded body obtained by the 3D printing process may be subjected, for example another heat treatment.

“Molded body” or “component” within the meaning of the invention are all three-dimensional objects that are produced with the aid of the method according to the invention and/or the device according to the invention and which have a nondeformability.

Any known 3D printing device that contains the necessary components may be used as the “device” for carrying out the method according to the invention. Common components include a coater, a build space, a means for moving the build space or other components, a dosing device and a heating means and other components which are known to those skilled in the art and therefore do not need to be listed in greater detail here.

“Counting means” for the particle layer application within the meaning of the invention may be a mechanical or other type of means, which is suitable for measuring the number of particle layer applications. It may be coupled with a control unit for other components or functions and/or software.

The invention, along with its preferred specific embodiments, is described in greater detail below.

In particular, the invention relates to a method for producing a component (3D molded body), wherein (a) a particle layer is applied to a building platform (102) in a first step with the aid of a powder coater (101); (b) a binder (400) is selectively applied in a second step with the aid of a binder dosing device (100); (c) the applied layer or layers is/are subjected to a heat treatment in another step with the aid of a heat source (600); (d) the building platform (102) is lowered by the thickness of one layer, or the powder coater (101) and possibly additional device components is/are raised by the thickness of one layer; steps a) through d) are repeated until the component is built up, the heat treatment (c) being carried out after every second or additional layer application step.

The heat treatment is preferably carried out at a temperature of 100° C. to 170° C., preferably 130° C. to 160° C.

The invention also relates to a binder system which is suitable for a 3D printing method, comprising or including at least one adhesive and a solvent and possibly other additives.

The binder system according to the invention preferably contains a thermally secondarily cross-linkable prepolymerisate as the adhesive and one or multiple alcohols and/or water as the solvent. The binder system according to the invention particularly preferably comprises or includes a novolak and/or resol system and a solvent and possibly other additives.

A binder system which includes a novolak and/or resol system, as used in the shell molding method, has proven to be particularly suitable (e.g., Corrodur® from Hüttenes-Albertus Chemische Werke GmbH).

All suitable solvents may be used in the binder system according to the invention, the solvent being an alcohol, preferably ethanol and/or 2-propanol, and/or an aqueous solvent, preferably water and 2-propanol.

The binder system according to the invention preferably contains other additives, which are selected from the group of tensides and antifoaming agents.

In one preferred specific embodiment, the binder system according to the invention is characterized in that the solvent is alcohol-based and preferably contains no more than 30% resin.

On one particularly preferred specific embodiment, the binder system according to the invention furthermore includes up to 5% polyol, preferably glycol, propylene glycol or xylitol.

The binder system according to the invention preferably has one or multiple of the following advantageous characteristics at room temperature: In the preferred specific embodiment, the viscosity is between 5 and 40 mPas, particularly preferably between 8 and 20 mPas; a surface tension of 20 to 40 mN/m is preferred, 25 to 35 mN/m being particularly preferred. In one preferred specific embodiment, the vapor pressure of the binder system is no higher than 55 hPa, particularly preferably no higher than 40 hPa.

The method according to the invention advantageously represents a chemical system comprising a solvent and a binding component, in which it was surprisingly possible to achieve the fact that high unpacking and final strengths were obtained by selecting the special components. A high edge sharpness without deposits is also advantageously achieved, due to the lack of a reaction part in the particulate material. According to the invention, an aggressive solvent is furthermore avoided, and the print head is thus advantageously not subjected to the danger of damage. This guarantees continuous machine runtimes and avoids the need to repair or replace machine parts. On the whole, the avoidance of aggressive solvents, which are required in other methods according to the prior art, has many practical advantages, such as a reduced threat to material and personnel, as well as positive economical consequences, due to continuous machine runtimes and the avoidance of damage to the printing machines.

It has proven to be particularly advantageous if the heat treatment step in the method according to the invention is not carried out after each layer application and binder application but instead is carried out only after every second, preferably after every second to seventh, layer application. The heat treatment step is particularly advantageously carried out after every second, preferably after every fourth to sixth, layer application, most preferably after every fifth layer application.

The hardening operation is thus preferably carried out in layers but not with each consecutive layer. Among other things, this results in a faster workflow and thus an accelerated production speed.

This surprisingly achieves the fact that a better binding of the layers is achieved in the component and thus a frequently occurring “flaking” of the layers is avoided.

It has surprisingly proven to be particularly advantageous if the particulate material is temperature-regulated on the building platform. The component may be thereby produced in an even better quality, depending on the particulate materials (sands) used. It has proven to be advantageous if the particulate material is held at a temperature that is no less than 50° C. to 70° C., preferably no less than 55° C. to 65° C., most preferably no less than 60° C.

The component produced by means of the method according to the invention may be subjected to additional known work steps, such as an additional heat treatment step, preferably at a temperature of 150° C. to 200° C. This heat treatment step preferably takes place after unpacking.

In the method according to the invention, the binder described above or the binder system described above is preferably used. The binder or the binder system is preferably selectively applied with the aid of a binder dosing device and selectively solidifies the particulate material.

In principle, the method has the advantage that nearly all materials known in 3D printing methods may be used. The particulate material is preferably selected from the group comprising sands, ceramic powders, metal powders, plastics, wood particles, fibrous materials, celluloses and/or lactose powders. The particulate material is particularly preferably a dry, free-flowing powder, a cohesive, firm powder or a liquid-based dispersion.

The practical and economical advantages of the method according to the invention are excellent. The method is not bound to specific particulate materials (sands) and may be used practically universally, in contrast to known methods from the prior art. One example is the furan resin method, in which no alkaline sands may be used.

Compared to known methods, the particulate material (the sand) also does not have to be pretreated or premixed. The residual sand, which does not form the component, may be reused and recycled in the method without a great deal of effort. An admixture process, which is otherwise necessary, or complex cleaning steps are dispensed with. The material only has to be sieved. Material costs are thereby saved, while handling effort is reduced and labor costs cut. This has a positive effect on the component costs.

It is also possible to process the components without an additional heat treatment step.

Depending on the geometry, the binder content may furthermore be varied globally as well as selectively by means of the print resolution as well as selectively within the geometry. This is also not possible with known prior-art methods, since possible mixing ratios of the reactants may no longer be in the optimum range during printing, which results in quality problems. One example of this is the furanic system, since the acid causes problems in the sand unless the correct amount of reactant is present.

In another aspect, the invention is a device for 3D printing, which includes (a) a powder coater (101), a building platform (102), at least one binder dosing device (100), at least one heat source (600), preferably an IR emitter (604), preferably a lifting device (605) for lowering and raising the building platform (102) or the powder coater (101) and possibly other components, such as the binder dosing device (100) and the heat source (600), preferably an extraction device (606) and a counting means (607) for counting the particle powder layers applied. The device preferably also has a contact heater (602) or a hot air device (608).

In particular, the binder dosing device (dosing device) may comprise, for example, an ink-jet print head, which selectively doses the binder onto the build space in individually dispensable droplets. The binder dosing device may also comprise a filament dispensing system, the binder being selectively dosed onto the build space in the form of a thin, switchable filament.

The device according to the invention and the method according to the invention may be used in all 3D printing methods, preferably in powder-based 3D printing processes.

BRIEF DESCRIPTION OF THE FIGURES:

FIG. 1 shows a schematic representation of the components of a powder-based 3D printer in a sectional isometric view;

FIG. 2 shows a sequence of a conventional 3D printing process with the use of a layered radiation hardening technique;

FIG. 3 shows a sequence of a building process, using a radiation hardening technique, which does not take place with each layer;

FIG. 4 shows a diagram of the binder diffusion process;

FIG. 5 shows combined energy supplies via an IR emitter and convective heating of the powder;

FIG. 6 shows a chemical reaction equation for solidifying a novolak system, using a formaldehyde source with the introduction of heat;

FIG. 7 shows details of the reaction.

Additional details, preferred specific embodiments and advantages of the invention are discussed below.

According to the invention, a system is essentially used for building models in layers with the aid of ink-jet printing. The sequence according to the prior art is as follows: a layer of powder is applied to a building platform and leveled. A fluid is then printed onto the layer according to the layer data of the 3D model. The printed areas change one or multiple properties (strength, water solubility, etc.). The material usually solidifies due to a binding component in the liquid binder (e.g., an adhesive). The building platform is subsequently lowered, and the process begins all over again.

A very low viscosity is generally needed for the ability to print a liquid with the aid of an ink-jet print head. To do this, the liquid binding components (binder) usually have to be diluted. Solvents are generally used for this purpose. If each layer is heated, e.g., with the aid of radiation, the surface temperature of the layer to be printed is also very high. As a result, the solvent very quickly evaporates. The binder cannot penetrate deeply enough into the layer and thereby bind the layers together. The structural body will flake apart. In many cases, the strategy of heating less does not work, since the solidification sets in only above the evaporation temperature of the solvent. A positive process window cannot be found in known methods.

By means of the method according to the invention and the device according to the invention, a stable, firm-edged and well defined structural body may be advantageously produced, for example if hardening takes place only after every fifth layer application. The solidification is thus completed only after adequate diffusion of the binding component (binder/binder system). The evaporation of the solvent of the fifth layer surprisingly does not impair the structural body.

In test series, it was possible to document that the number of exposures can increase, while no relationship between the layering time, liquid supply and IR radiation power resulting in satisfactory structural bodies was found when exposing every layer.

The system according to the invention draws heavily on powder-based 3D printing. The mechanical engineering of the device according to the invention has been expanded according to the requirements of the method according to the invention.

The device according to the invention includes a power coater. Particulate material is applied thereby to a building platform and smoothed (FIG. 2(a)). The applied particulate material may comprise a wide range of materials. For example, sands, ceramic powders, metal powders, plastic, wood particles, fibrous materials, celluloses, lactose powders, etc. may be used. The flow characteristics of these materials may vary enormously. Different coater techniques permit layering from dry, free-flowing powders and cohesive, firm powders to liquid-based dispersions. The height of powder layers is determined by the building platform. It is lowered after one layer has been applied. During the next coating operation, the resulting volume is filled and the excess smoothed. The result is a nearly perfectly parallel and smooth layer of a defined height.

After a coating process, a liquid is printed on the layer with the aid of an ink jet print head (FIG. 2(b)). The print image corresponds to the section of the component at the present build height of the device. The fluid strikes and slowly diffuses into the particulate material.

After the binder, preferably the binder system according to the invention, is printed, the layer is solidified using the method according to the invention (FIG. 2 (c)). For this purpose, an IR emitter may be passed over the build space. This emitter may be coupled with the axis of the coating system. The solvent evaporates during heating. In the case of liquids that present a fire hazard, the evaporating material is extracted immediately.

The controller of a machine according to the invention may count the layers and change the sequence only after, for example, every second layer and trigger a solidification run (FIG. 3). Likewise, however, the energy supply may be estimated based on measured data, and the frequency of the solidification runs may be adapted. Examples include solidification runs after three, four, five or six layers of the particulate material and preferably the binder. The printed liquid quantities, which fluctuate depending on the layer image, are essentially an interference variable of a control of this type. Instead of control based on sensor data, the information may also be linked within the controller.

FIG. 4 shows an example of a droplet which penetrates the powder (particulate material). After steps (a) through (d), the penetration is deep enough to bind the layers. The diffusion quickly slows down, since the droplet has disappeared as a reservoir. If printing takes place on an excessively preheated layer, the solvent abruptly boils, and the binder becomes highly viscous. As a result, it remains in the state shown in FIG. 4(b). It therefore does not form a layer bond.

In addition to IR irradiation, the powder may also be preheated. Contact heaters, hot air or IR emitters are suitable for this purpose. This preheating makes it possible to effectively control the IR solidification process at low lamp powers and to achieve high process speeds.

After the solidification step, the building platform is lowered by the thickness of one layer (FIG. 2(d)). The complete component is created by repeating the aforementioned steps.

An exemplary representation of a chemical system which may be used according to the invention, based on a formaldehyde-hardenable novolak system, is as follows: novolaks are known from their use as a shell of sand having the designation Croning resin. Finished solutions of such resins and hardening additives, which are used for coating sand, may be purchased, for example, from Hüttenes-Albertus Chemische Werke GmbH. In preliminary tests, alcohol-based solutions have proven to be easily processed with the aid of ink-jet printing systems, due to their viscosity as well as their compatibility with the novolak system, the resin content preferably being less than 30%. Other additives, such as tensides and antifoaming agents, may be added to optimize printability, and up to 5% polyols, such as glycol, propylene glycol or xylitol, may be added to finely adjust the viscosity. The thermal hardening of the novolak after the selective introduction of the liquid into the particulate material takes place by the breakdown, e.g., of urotropine as the hardening additive in ammonia and formaldehyde and ultimately by a reaction with formaldehyde with the novolak according to the reaction equation in FIG. 7. The starting temperature of the hardening additive must be well removed from room temperature so that no undesirable reactions begin. The print solution set in this manner is then selectively introduced in layers into the particulate material with the aid of a print head, the particulate material having a temperature of preferably at least 60° C. during the entire build process. The evaporation speed of the excess solvent is increased, due to the temperature of the sand, and is continuously removed in the continuous extraction flow. The actual hardening process takes place by further supply of heat to the printed particulate material, preferably with the aid of an IR lamp, the temperature temporarily rising above 160° C. The exposure operation is preferably repeated every five layers, the build process always terminating with an exposure operation. During an exposure operation, a significant change in color of the printed areas, from ocher hues to brown, indicates the polymerization. Due to the formaldehyde and ammonia released at high temperature as a catalyst, the existing prepolymerisate is cross-linked in another condensation reaction to form a duroplast. After the final exposure step, the components are preferably left in the unprinted particulate material for another hour. To further increase the strength, the unpacked components may be preferably stored in the oven for another hour at a temperature between 150° C. and 200° C. The system is particularly characterized in that the components may be effortlessly removed from the unprinted sand and have a very high edge sharpness.

LIST OF REFERENCE NUMERALS

• 100 Binder dosing device (dosing device)
• 101 Powder coater
• 102 Building platform
• 103 Component (3D molded part)
• 104 Build space boundary
• 107 Powder layers
• 200 Solidifying unit
• 400 Binder
• 401 Powder particles
• 500 Heat effect
• 502 Storage device
• 503 Extraction system
• 600 Heat source
• 601 Lifting device
• 602 Contact heater
• 603 Hot air device
• 604 IR emitter
• 605 Lifting device
• 606 Extraction device
• 607 Counting means
• 608 Hot air device

Claims

1. A method for producing a component, wherein the component is a 3D molded body, comprising the steps of: (a) applying a particle layer to a building platform in a first step with the aid of a powder coater;(b) selectively applying a binder in a second step with the aid of a dosing device;(c) subjecting the applied layer or layers to a heat treatment in another step with the aid of a heat source;(d) lowering the building platform by the thickness of one layer, or raising the powder coater by the thickness of one layer;

2. The method according to claim 1, wherein the heat treatment is carried out at a temperature of 100° C. to 170° C.

3. The method according to claim 1, wherein the particulate material is selected from the group comprising sands, ceramic powders, metal powers, plastics, wood particles, fibrous materials, celluloses lactose powders, and any combination thereof, andthe particulate material preferably is a dry, free-flowing powder, a cohesive, firm powder or a liquid-based dispersion.

4. A device for 3D printing comprising:

5. The device according to claim 4, wherein the device additionally includes a contact heater or a hot air device, the dosing device preferably being designed in the form of an ink-jet printing system, the dosing device preferably being designed in the form of a liquid filament dispenser.

6. A binder system, suitable for a 3D printing method, according to claim 1, comprising or including at least one adhesive, which is hardenable by the supply of heat, and a solvent.

7. The binder system according to claim 6, wherein the adhesive is a thermally secondarily cross-linkable prepolymerisate, and the solvent is one or multiple alcohols and/or water, preferably comprising or including a novolak and/or resol system and a solvent and possibly other additives, preferably comprising or including a coating resin system for the shell molding method, the solvent preferably being an alcohol, preferably ethanol and/or 2-propanol, and/or an aqueous solution, preferably water and 2-propanol, the other additives preferably being selected from the group comprising tensides and antifoaming agents, the solvent preferably being alcohol-based and preferably containing no more than 30% resin, preferably furthermore including up to 5% polyol, preferably glycol, propylene glycol or xylitol, preferably characterized by a viscosity between 5 and 40 mPas, preferably 8 and 20 mPas, at room temperature, preferably characterized by a surface tension of 20 to 40 mN/m, preferably 25 to 35 mN/m, at room temperature, preferably characterized by a vapor pressure of the binder system which is no higher than 55 hPa, particularly preferably no higher than 40 hPa.

8. The method of claim 1, wherein the heat treatment step is carried out at a temperature of 130° C. to 160° C.

9. The method of claim 8, wherein the heat treatment step is carried out after every second to seventh layer application.

10. The method of claim 9, wherein the heat treatment step is carried out after every fourth to sixth layer application.

11. The method of claim 8, wherein the heat treatment step is carried out after every fifth layer application.

12. The method of claim 8, wherein the particulate material is temperature-regulated on the building platform and having a temperature which is no less than 50° C. to 70° C.

13. The method of claim 8, wherein the binder is selectively applied with the aid of an ink-jet print head or a filament dispenser.

14. The method of claim 1, wherein the component is subjected to another heat treatment step.

15. The method of claim 14, wherein the additional heat treatment step is after a step of unpacking the component.

16. The method of claim 15, wherein the additional heat treatment step is at a temperature of 150° C. to 200° C.

17. The method of claim 16, wherein the preferably taking place after unpacking.

18. The method of claim 1, wherein the binder includes at least one adhesive, which is hardenable by the supply of heat, and a solvent.

19. The method of claim 1, wherein the binder includes a novolak and/or a resol system.

20. The method of claim 18, wherein the binder system includes a coating resin system for a shell molding method and the solvent includes an alcohol.