Method and device for storing and transporting flat glass in a contactless manner

Abstract

The invention relates to a method and a device for storing and transporting hot flat glass in a contactless manner during glass production, said storage and transportation being carried out on a gas bed which is constructed over a gas permeable bearing surface pertaining to a base (2). Pressurised gas is supplied to the base via a connection (5), said gas being guided through the gas permeable base and then re-evacuated. The aim of the invention is to obtain an optimum pressure distribution above the bearing surface, without any static pressure. In order to achieve this, the base (2) consists of a plurality of interspaced segments (21, 22 . . . 2n) respectively comprising a porous and/or perforated bearing surface (7a) as a gas outlet surface. Evacuation openings (61, 62 . . . 6n) are formed between said segments for evacuating the gas. The segments are preferably formed by bars (7) having a box profile.

Description

[0001] The invention relates to a method for storing and transporting hot flat glass in glass production on a gas bed, which is constructed over a gas-permeable support surface of a nest, in a contactless manner by passing a gas through the support surface.

[0002] The invention also relates to a device for performing this method.

[0003] In the conventional glass ceramicizing process typically used in the industry, the glass to be ceramicized, typically in the form of a platelike green glass body, rests on a solid nest. Since during the ceramicization process temperatures and viscosities are reached at which the glass surface can be harmed by mechanical contact with the nest, punctate prints from adhesion known as “pits” appear on the underside of the glass. From a shrinkage process during the ceramicization, a relative motion between the supported glass and the nest also occurs, creating scratches on the glass surface.

[0004] These disadvantages, resulting from the contact of the green glass plate with the solid nest, lead to the thought of employing principles from float glass production. However, in this respect it must be noted that the ceramicization process differs from the usual float glass tempering process in that substantially higher temperatures are required, as a rule up to about 950° C., but in special cases even up to 1250° C., instead of about 500° C. to 700° C. in the case of tempering and bending furnaces for float glass, and in addition, a temperature homogeneity in the range of a few Kelvins must be assured, to prevent deformations of the glass ceramic.

[0005] It is known to ceramicize glass in contactless fashion, by retaining the green glass molded body to be ceramicized on a gas bed in which the supporting gas, as a rule air, flows out of a permeable nest and builds up a load-bearing air bed between this nest and the green glass molded body. Since there is no direct contact between a solid nest and the green glass body, the aforementioned disadvantages cannot arise.

[0006] British Patent Disclosure gas bed 1,383,202 shows a corresponding device for contactless ceramicizing of a green glass plate on an air bed. This known device has various disadvantages, however, which result from the fact that work is done solely with a inlet air supply, that is, without outlet air, through the nest, and the inlet air is delivered through perforated plates. With typical perforations, a comparatively high permeability is achieved:

[0007] Calculations show that here in the middle region of the green glass plate to be ceramicized, the gas speed is nearly zero and as it were a “static” pressure is generated. A gas flow is created then essentially only in the vicinity of the edge of the plate. In contrast to the pressure in the edge region, the static pressure in the middle of the plate is indifferent to disruptions in the thickness of the gas film. Accordingly, no restoring moment resistant to geometric deviations in the plates from flatness or from the particular desired shape arises. The same situation means that the thickness of the gas film is very sensitively dependent on the magnitude of the pilot pressure and other process parameters. Disruptions in these parameters can therefore cause warping of the plates.

[0008] U.S. Pat. No. 3,607,198 shows a device for contactless retention and transporting of a hot glass plate on an air cushion that is built up above a solid nest. Here, in alternation along the transport route, by way of inlet-air and outlet-air slits, zones with static and dynamic gas pressure are created, each extending over the entire width of the glass plate. Since here the gas delivery is effected via narrow slits with large interstices between them, the result is a gas supply that is locally very nonhomogeneous, which in turn—because of the alternation between zones of high and low gas speed—makes a homogeneous temperature course in the glass difficult. Moreover, a complicated construction is employed, which for reasons of material is not suitable for use in the range of temperatures around 950° C., and certainly not for higher temperatures of up to about 1250° C., that can be necessary for the ceramicization.

[0009] U.S. Pat. No. 5,078,775 also shows a device for contactless retention and transporting of a flat glass plate, in the tempering of float glass, on an air cushion that is built up above a solid nest that likewise has alternating inlet-air and outlet-air slits. This known device, despite modifications in details, relies on the fundamental concept of U.S. Pat. No. 3,607,198, with the inlet-air and outlet-air slits in the nest, and thus with regard to ceramicization applications has comparable disadvantages.

[0010] The object of the invention is to conduct the method defined at the outset for contactless storing and transporting of flat glass, in which via a gas bed any contact whatever of the flat glass with the nest is avoided, in such a way, and to embody the associated device in such a way, that compared to the known ceramicization methods, flat glass ceramic of high smoothness can be produced, and in which the transporting can be done optionally through a path in the furnace with a predetermined temperature profile. Compared to the known methods and devices for tempering float glass above an air bed, the object to be attained is that these methods and devices can be employed in a structurally simple way in the temperature range up to 950° C. and higher, while achieving temperature homogeneity.

[0011] In terms of the method, taking as the point of departure the method defined at the outset for storing and transporting hot flat glass in a contactless manner in glass production on a gas bed, which is constructed over a gas-permeable support surface of a nest, in that a gas is passed through the support surface, this object is attained in that to attain a homogeneous delivery of gas sheetwise, the gas is pressed through spaced-apart planar porous and/or perforated segments of the support surface, and the gas is carried away into the interstices between the segments.

[0012] In terms of the device, taking the device defined at the outset for performing the methods as the point of departure, having a gas-permeable nest, disposed in a furnace, as a support surface for the flat glass to be stored and transported in contactless fashion, which nest has a connection for the delivery of gas under pressure, which is passed through the gas-permeable nest to build up a gas bed between the flat glass and the nest and is subsequently carried away again, this object is attained according to the invention in that the nest comprises a plurality of spaced-apart segments, each of which has a porous and/or perforated support surface as a gas exit face, and between which outlet-air openings for the removal of the gas are embodied.

[0013] By means of the outflow of the gas from the planar porous and/or perforated segments of the support surface, a gas film forms between the support surface and the supported glass, with a pressure distribution that is parabolic and that has no static pressure zones. Via the interstices between the segments, the gas can readily flow out, so that no backup of gas occurs in the middle of the glass that could cause deformation of the flat glass.

[0014] In one feature of the invention, compressed air is used as the gas. This feature allows a very simple conduct of the method by simple means, since suitable compressed air equipment is available on the market.

[0015] An advantageous contactless storage and transporting of the hot flat glass is possible in a method course in which the supported glass at least intermittently has a viscosity of ≦1013 dpas, corresponding to the so-called upper cooling point. For the so-called lower cooling point, the viscosity is ≦1014.5 dpas.

[0016] To obtain flat glass with predetermined properties, in one feature of the invention a method is performed in which during the handling of the glass, a defined rising and/or falling temperature profile is traversed.

[0017] Advantageously, a temperature profile is traversed by which the glass on the gas bed is ceramicized. In this way, it is possible with relatively simple means to produce a glass ceramic plate in contactless fashion relative to the nest, which plate does not have any punctate pits or scratches on the underside.

[0018] A favorable method course is obtained if during the ceramicization, the glass is moved over the gas bed. As a result, temperature differences in the furnace can be compensated for.

[0019] In one feature of the invention, to maintain the temperature homogeneity required for the ceramicization, preheated gas is used.

[0020] The tempering of the gas is effected, at least predominantly during the flowthrough, by porous and/or perforated support segments and thus to a great extent, the temperature homogeneity required for the ceramicization is achieved.

[0021] So that no contamination of the green glass to be ceramicized will occur, in a further feature of the invention the gas is delivered only via scale-free material.

[0022] An advantageous method course is obtained if the gas pressure in the individual segments is adjusted or regulated chronologically variably independently of one another. By creating a pressure gradient along the direction of motion of the glass, for instance, a contactless movement of the flat glass can thus be achieved.

[0023] With the method of the invention, either a closed glass ribbon or individual plates can be ceramicized. It is not absolutely necessary for the underside of the glass ribbon or of the plates to be smooth. It is also conceivable that the underside and optionally the top as well of the glass to be ceramicized be surface-structured, for instance studded. Also the underside in particular can be decorated.

[0024] With the provisions of the invention, a gas bed with a float height of between 30 μm and 1-3 mm can be created, which is sufficient for contactless storing and transporting of flat glass. Preferably, the range is between 50 μm and 1-3 mm.

[0025] In one embodiment of the device, the device is embodied such that the segments extend over the entire width of the flat glass to be handled. Uniform retention of the flat glass is thus possible.

[0026] An especially simple embodiment of the device is obtained if the outlet-air openings are embodied as slits between the segments.

[0027] A preferred embodiment of the device is obtained if the individual segments are embodied as beams that have a box profile, into whose interior the gas delivery is effected, and of which at least one wall, forming the support surface, is embodied as porous and/or perforated. This embodiment makes an especially simple embodiment of the segments and outlet-air openings between the beams possible.

[0028] The beams can be realized by various kinds of molded bodies. A particular embodiment is obtained if the beams are formed by a boxlike porous ceramic body. Such ceramic bodies are on the market and can be made available for very high temperatures, as are required in ceramicization.

[0029] In order to have an especially strong flow along the support surface, the ceramic body, with the exception of the wall forming the support surface, is enveloped with a gas-impermeable material. For instance, the ceramic body can have a suitable coating or be sheathed with a metal foil.

[0030] The device is preferably embodied such that the segments are extended into the cold region through openings in the lateral furnace walls, so that the connections for the compressed air can be ducted through to the segments without thermal stress.

[0031] An especially effective gas bed is obtained if the porous and/or perforated support surface of the segments from which the gas flows out amounts to at least 30% of the total area of the nest.

[0032] The mode of operation of the device is highly effective if a closed gas circulation is provided, in which the gas removed through the outlet-air openings is returned to the gas source again.

[0033] In one feature of the invention, a design of the nest that is mirror-symmetrical relative to the center face of the glass is provided, as a result of which the top and underside can be kept under exactly the same thermal conditions.

[0034] Besides the possibility already mentioned of moving the flat glass along a pressure gradient in the segments, an onward motion of the glass can be achieved by mechanical devices that contact it, such as rollers and slides.

[0035] To avoid such mechanical devices that employ contact and that always require their own drive mechanism, in a further feature of the invention the device is embodied such that the nest with the gas bed is inclined downward in the direction of motion of the flat glass. As a result, the flat glass slides on its own to the lower location by gravity.

[0036] The invention will be described in further detail in terms of an exemplary embodiment shown in the drawings.

[0037] Shown are:

[0038] FIG. 1, in a schematic longitudinal section, a furnace chamber, in which a nest is set up for a flat glass pane that is retained in contactless fashion via a gas bed created by the nest;

[0039] FIG. 2, in a schematic plan view, in a first embodiment, the design of the nest comprising a plurality of spaced-apart individual segments, which each have a porous and/or perforated support surface as a gas exit face, between which outlet-air openings for removing the gas are formed;

[0040] FIG. 3, in a schematic fragmentary cross-sectional view, the design of the individual segments by means of boxlike profiled ceramic bodies, which except for the support surface at the top have a gastight sheathing;

[0041] FIG. 4, a graph showing the pressure distribution in the longitudinal direction of the segments; and

[0042] FIG. 5, a second embodiment with a nest segmented in beamlike form.

[0043] FIG. 1, in a schematic view, shows a ceramicization furnace 1, in which a nest 2, embodied according to the invention and comprising the beam system to be explained later, for retaining the green glass plate 3 to be ceramicized is disposed by way of props 4. One prop 5 for the delivery of a suitable gas, preferably air, is connected to the nest 2 and this creates a gas bed, that is, an air cushion below the green glass plate 3, so that there will be no troublesome mechanical contact between the underside of the green glass plate 3 and the nest 2. Because of the incline predetermined by the disposition of the props 4, the green glass plate 3 slides automatically in the direction of the arrow during the ceramicization process, toward a mechanical transporting device, such as a roller 2a, which feeds the green glass plate perpendicular to the plane of the paper.

[0044] FIGS. 2 and 3 show the nest 2, embodied according to the invention, for the green glass plate 3; specifically, FIG. 2 shows this in a plan view, and FIG. 3 in a cross-sectional view. The nest 2 comprises a plurality of segments 21, 22, . . . , 2n, to which the supply 5 of gas and in particular air is connected, and which have as homogenous an air outflow sheetwise as possible, which can be achieved by way of porous surfaces or surfaces with small perforations. The interstice 61, 62, . . . , 6n, between these segments, which as a rule is embodied as a slit, serves to remove the outlet air, which is represented by a downward-pointing arrow in FIG. 3.

[0045] As FIG. 2 shows, these segments and interstices extend over the full width of the furnace, bounded by the side walls 1a.

[0046] In the exemplary embodiment shown in FIG. 3, the air-permeable segments are each predetermined by the upper boundary 7a of a boxlike beam 7, which is formed by a porous material and/or has small openings, that is, perforations. As the drawings show, these segments, that is, the upper boundaries of the beams, define relative narrow air-permeable surfaces.

[0047] In the interior of these beams 71, 72, . . . , 7n, which as gas-permeable at the top, an overpressure of a suitable gas, such as air, is created by connecting the interior of each beam to a suitable pressure source. By means of the outflow of gas from the upper box wall 7a, which is reinforced by the fact that the other walls are provided with a gas-tight sheathing 8, a gas film develops between the top 7a of the beam and the supported glass 3. When porous material is used, the pressure distribution is parabolic, as shown in FIG. 4, and has no static pressure zones. The gas can flow out into the interstices 61, 62, . . . , 6n, between the beams 71, 72, . . . , 7n, so that there is no backup of gas in the middle of the glass.

[0048] A number of advantages are attained by means of the invention.

[0049] First, a homogeneous, planar gas delivery is made possible, without creating zones of static pressure. This is advantageous, both for stabilizing the layer thickness of the green glass plate and for making the temperature course homogenous. In the case of porous gas exit faces, the gas temperature is made additionally more homogenous as a result of the heat-exchanger effect of the porous structure.

[0050] Moreover, through the interstices between the segments, a removal of gas is assured even in the inner regions of the supported plates; as a result, arching and the development of zones of static pressure are avoided.

[0051] The preferred embodiment, with the use of beams that are perforated and/or porous at least on the top and are spaced apart, forming interstices, as segments, has the advantage of a very simple construction, particularly taking into account the requisite temperatures of up to 950° C. and higher. An essential point for this is that porous beams, for instance of temperature-resistant ceramics, are commercially available, and when the beams are removed from the hot region of the furnace, as shown in FIG. 2, the rest of the construction is exposed to only low temperatures and can be embodied correspondingly more simply.

[0052] In FIG. 5, a second embodiment of the invention is shown, with a nest 2′ of porous material that is structured in beamlike fashion. By means of conduitlike structures in the nest, porous segments 2′1, 2′2, 2′3, 2′4, 2′5, . . . , 2′n and outlet-air openings 6′1, 6′2, 6′3, 6′4, 6′5, . . . , 6′n are predetermined. The load-bearing inlet air, that is, the gas, flows through the segments, while conversely the gas is carried away via the outlet-air openings.

[0053] In the exemplary embodiments, for a preferred material, the porosity is approximately 15%.

[0054] The diameter of alternative perforation openings is on the order of 0.5 to 1 mm.

Claims

1. A method for storing and transporting hot flat glass in a contactless manner in glass production on a gas bed, which is constructed over a gas-permeable support surface of a nest, in that a gas is passed through the support surface, characterized in that to attain a homogeneous delivery of gas sheetwise, the gas is pressed through spaced-apart planar porous and/or perforated segments of the support surface, and the gas is carried away into the interstices between the segments.

2. The method of claim 1, in which compressed air is used as the gas.

3. The method of claim 1 or claim 2, in which the supported glass at least intermittently has a viscosity of ≦1013 dpas, corresponding to the upper cooling point, or ≦1014.5 dpas, corresponding to the lower cooling point.

4. The method of claim 1, in which the glass, at least on its underside, has a surface structure, such as studs and/or a decoration.

5. The method of one of claims 1-4, in which during the handling of the glass, a defined rising and/or falling temperature profile is traversed.

6. The method of claim 5, in which a temperature profile is traversed by which the glass on the gas bed is ceramicized.

7. The method of claim 6, in which during the ceramicization, the glass is moved over the gas bed.

8. The method of claim 6 or 7, in which to maintain the temperature homogeneity required for the ceramicization, preheated gas is used.

9. The method of claim 8, in which the tempering of the gas is effected, at least predominantly during the flowthrough, by porous and/or perforated support segments and thus the temperature homogeneity required for the ceramicization is achieved.

10. The method of one of claims 6-9, in which the gas is delivered only via scale-free material.

11. The method of one of claims 1-10, in which the gas pressure in the individual segments is adjusted or regulated chronologically variably independently of one another.

12. The method of claim 11, in which a pressure gradient is created along the direction of motion of the glass.

13. The method of one of claims 1-12, in which a gas bed with a float height of between 30 μm and 1-3 mm is created.

14. A device for performing the methods of one of claims 1-13, having a gas-permeable nest (2), disposed in a furnace (1), as a support surface for the flat glass (3) to be stored and transported in contactless fashion, which nest has a connection (5) for the delivery of gas under pressure, which is passed through the gas-permeable nest to build up a gas bed between the flat glass and the nest and is subsequently carried away again, characterized in that the nest (2) comprises a plurality of spaced-apart segments (21, 22, . . . , 2n), each of which has a porous and/or perforated support surface (7a) as a gas exit face, and between which outlet-air openings (61, 62, . . . , 6n) for the removal of the gas are embodied.

15. The device of claim 14, characterized in that the segments extend over the entire width of the flat glass to be handled.

16. The device of claim 14 or 15, characterized in that the segments are formed by separate molded bodies (7).

17. The device of claim 16, characterized in that the outlet-air openings (61, 62, . . . , 6n) are embodied as slits between the spaced-apart separate segments.

18. The device of claim 16 or 17, characterized in that the individual segments (21, 22, . . . , 2n) are embodied as beams (71, 72, . . . , 7n) that have a box profile, into whose interior the gas delivery is effected, and of which at least one wall (7a), forming the support surface, is embodied as porous and/or perforated.

19. The device of claim 18, characterized in that the beams (71, 72, . . . , 7n) are formed by a boxlike porous ceramic body.

20. The device of claim 19, characterized in that the ceramic body, with the exception of the wall (7a) forming the support surface, is enveloped with a gas-impermeable material (8).

21. The device of claim 14 or 15, characterized in that the segments are formed by a beamlike segmentation of a porous molded body, in that conduitlike outlet-air structures are embodied in the molded body, on its top.

22. The device of one of claims 14-21, characterized in that the segments are extended into the cold region through openings in the lateral furnace walls (1a).

23. The device of one of claims 14-22, characterized in that the porous and/or perforated support surface (7a) of the segments from which the gas flows out amounts to at least 30% of the total area of the nest (2).

24. The device of one of claims 14-23, characterized in that a closed gas circulation is provided, in which the gas removed through the outlet-air openings (61, 62, . . . , 6n) is returned to the gas source again.

25. The device of one of claims 14-24, characterized by a design of the nest (2) that is mirror-symmetrical relative to the center face of the glass.

26. The device of one of claims 14-25, characterized in that the nest (2) is inclined obliquely downward, perpendicular to the direction of motion of the flat glass, and has a transport device (2a) at the low point.