The present invention relates to a method for treating a surface, a device making it possible to carry out said method, and the use of an aerogel to trap the matter ejected from a surface during the treatment to which that surface is subjected.
It is applicable in all fields where cleaning, satinizing, polishing, deburring, etching, marking, or surface preparation, e.g. the creation of roughnesses before adhesion, metallization, enameling, painting or varnishing operations are done.
It is more particularly useful in fields where these types of operations are done on pieces that, because they are small or precious or because they have embrittled surfaces, require high-precision treatments.
Such fields are in particular electronics, microelectronics, optics, optoelectronics, bijouterie, jewelry, and the restoration of art and antiques.
Many surface treatment techniques exist and, in particular, techniques for cleaning polluted surfaces, which are based on a chemical or physical interaction between the surface to be treated and an agent that is projected on that surface at a more or less high speed.
These primarily concern techniques that consist of projecting:
Regardless of the technique used, the user may wish, in particular in the context of cleaning a polluted surface, to recover the waste produced by the surface treatment either to analyze the waste, for example to determine its size or composition, or to prevent it from being redeposited on the surface to be treated or from contaminating the environment of that surface, for example if the waste is toxic or radioactive.
Techniques based on the projection of a liquid or an abrasive in a liquid medium make it possible to fairly easily recover the waste generated by the surface treatment, since the liquid that flows from the treated surface naturally tends to bring said waste with it. However, the volumes of liquid used and, therefore, of effluent produced are generally substantial and the operations necessary to isolate the waste from the rest of the effluent, for example if one wishes to analyze it, are expensive. Moreover, interactions inevitably occur between the waste and the liquid that result in physically and/or chemically modifying this waste and, as a result, distorting the analysis thereof.
In the case of techniques based on the projection of a gas, an abrasive in a gaseous medium, carbon dioxide in solid or supercritical state, or electromagnetic radiation, the waste produced by the surface treatment is generally conveyed in a gas flow that is led towards a fibrous or electrostatic filter in which this waste is retained. However, the use of a gaseous flow to convey the waste does not prevent part of said waste from being redeposited on the treated surface due to the turbulence generated. Moreover, the filters used at this time must be subjected to relatively heavy treatments if one wishes to extract the waste from them for analysis.
Furthermore, regardless of whether the waste is recovered in a liquid flow or a gas flow, this recovery is based, in most systems, on an aspiration of said flow. However, such systems are difficult to use in certain mediums and, in particular, in confined or cramped mediums, as well as under certain working conditions such as depression (vacuum) or high temperature conditions. Moreover, the aspiration noticeably increases the risk of the waste losing its physical integrity and, as a result, distorting the analysis thereof.
The inventor therefore aimed to provide a surface treatment method that is, in general, free from all of the aforementioned drawbacks.
More specifically, the inventor aimed to provide a surface treatment method making it possible to collect all of the waste produced by this treatment, while keeping the physical and chemical characteristics of said waste intact so as to guarantee the reliability of the analyses to which they are likely to be subjected later.
She also aimed for the method to be applicable to all types of surfaces, irrespective of their nature, size and state, and to be able to be implemented in all types of environments and conditions, in particular pressure and temperature.
She also aimed for this method to be easy to use, not require heavy or expensive equipment, and to have implementation costs compatible with industrial requirements.
She also aimed to provide a device that makes it possible to carry out this method.
These aims and others are achieved by the invention, which first proposes a method for treating a surface comprised by an object, which comprises:
Thus, according to the invention, the ejection of the matter from the surface to be treated can be done using:
According to the invention, it is preferable to use an ejection agent that does not generate waste other than that corresponding to the matter ejected from the surface. This is why it is preferable for this agent to be a gas, a fluid in supercritical state, dry ice, or electromagnetic radiation.
In the context of the invention, the term “aerogel” is used in its usual accepted meaning, i.e. it designates any gel whereof the liquid phase has been replaced by air (by freeze-drying, supercritical drying, etc.) and the liquid network of which has therefore been transformed into a network of pores.
Thus, the aerogel capable of being used as a trap in the inventive method can in particular be:
The structure of the aerogels, their properties, and the method for obtaining them have been greatly described in the literature. In this respect, the reader may, for example, see files N20 and J2230 of TECHNIQUES DE L'INGENIEUR, respectively entitled <<Aérogels. Aspect matériau>> and <<Elaboration des gels et aérogels>>.
In a certain number of cases and, in particular, when the surface treatment consists of cleaning, the inventive method is, preferably, carried out in a controlled atmosphere enclosure or chamber in which, for example, a pressure reigns that is lower than the atmospheric pressure, typically from 10−2 to 10−8 Pa, as well as potentially a temperature higher than the ambient temperature, for example a temperature from 50 to 300° C. This enclosure can in particular be a vacuum chamber.
The ejection agent is then projected on the surface to be treated using projection means that can be arranged inside or outside the enclosure depending on the nature of the ejection agent. Thus, if the ejection agent is electromagnetic radiation and, in particular, a laser beam, the ejection means can be arranged outside the enclosure. In the latter case, it is sufficient for the enclosure to be made from a material transparent to the wavelength of the electromagnetic radiation or to comprise a porthole made from such a material so that the electromagnetic radiation can penetrate said enclosure.
Furthermore, the ejection agent can be projected on the surface to be treated along an axis orthogonal to said surface or, on the contrary, along an axis that is inclined relative to the normal of said surface, the angle formed by this axis and this normal then generally being from 20 to 70° and, most often, from 30 to 60°.
Moreover, the ejection agent can reach the surface to be treated without passing through the aerogel piece or any one of the aerogel pieces or, on the contrary, reach said surface after having passed through the aerogel piece or one of the aerogel pieces. In the latter case, the aerogel piece thus passed through can be provided with a through opening with dimensions suitable for allowing the ejection agent to pass, or can be formed by several aerogel blocks not attached to each other, or also, if the ejection agent is electromagnetic radiation, and in particular a laser beam, be made up of an aerogel transparent to the wavelength of said radiation.
Thus, for example, certain aerogels such as silica-based aerogels and melamine/formaldehyde-based aerogels are transparent to visible light (λ=400-800 nm) and can advantageously be used in the event the chosen implementation configuration of the method involves the aerogel piece or at least one of the aerogel pieces provided to trap the matter ejected from the surface to be treated being transparent in the visible range.
According to one particularly preferable embodiment of the inventive method, the ejection agent is a laser beam due to the many advantages offered by the use of this type of beam in surface treatments and, in particular, the precision with which this treatment can be done, the absence of abrasive effects, and more generally aggressive effects for the surface to be treated, the absence of pollution related to this treatment (no contribution of matter, or gas emanation), and the simplicity of handling a laser.
The laser is preferably a gas laser of the excimer laser or CO2 TEA (“Transversely Excited Atmospheric pressure”) laser type, or a crystalline laser, typically with a YAG matrix, i.e. made up of an aluminum garnet enriched with yttrium, of the Yb:YAG type (doped with ytterbium) or Nd:YAG type (doped with neodyme).
It is generally used in pulsed mode, in which case the duration of the pulses, their frequency, and the fluence (i.e. the energy of the pulses per surface unit) must be adapted to the nature of the matter to be ejected from the surface to be treated, as well as that of the surface in the event the surface to be treated and the matter needing to be ejected therefrom are not of the same nature, which will, for example, be the case if the treatment of the surface consists of stripping.
Thus, for example, to strip the surface of a carbon substrate covered with a layer of gray epoxy paint, it is possible to use a pulsed laser of the Nd:YAG type, with a wavelength of 1064 nm, with a pulse length of 100 ns, a repetition rate of 10 kHz and a fluence greater than 1 J/cm2.
When the ejection agent is a laser beam, the matter ejected from the surface to be treated is contained in a plume called “plasma plume”, with an axis orthogonal to said surface and the morphology of which depends on the nature of the surface to be treated, usage parameters of the laser, and environmental conditions (pressure conditions, for example).
Thus, in this particularly preferred embodiment, the aerogel piece or one of the aerogel pieces is preferably arranged opposite the surface to be treated, while being parallel or substantially parallel thereto, and the projection of said piece in the axis of the plume has, in the plane perpendicular to said axis in which this plume has the largest dimensions (i.e. the largest diameter in the event the plasma plume has a circular transverse section), a perimeter in which the perimeter of said plume fits, so as to guarantee trapping of all of the matter ejected from said surface.
This aerogel piece can have any shape, but preferably assumes the form of a rhomb, in particular a rectangular rhomb such as a cube.
According to the invention, the surface to be treated can be of any type. Thus, it can be an inorganic surface such as a surface made of stone, plaster, cement, glass, metal, metal alloy, ceramic, enamel, porcelain, mineral paint, etc., or organic such as a surface made of carbon, wood, plastic, elastomer, textile (e.g. fabric), organic paint, etc.
Moreover, the object to which the surface to be treated belongs can also be an object that can easily be moved, such as an electronic or optical device, or an object that cannot be moved and that therefore needs to be treated where it is located, such as the façade of a monument.
The treatment of this surface can in particular consist of cleaning, satinizing, polishing, deburring, etching, marking, or an operation consisting of preparing said surface to be subjected later to another treatment such as gluing, metallilation, enameling, painting, or varnishing.
It preferably involves cleaning—this term having to be understood in the broad sense, i.e. as encompassing stripping, pollution control, and decontamination from toxic, in particular radioactive, materials—, marking, or etching, the inventive method having, in fact, shown itself to be particularly useful in these three types of treatment.
Whatever the case may be, the inventive method can also comprise the analysis of the matter trapped in the piece(s) of aerogel.
This analysis can consist of a very simple analysis of the matter ejected from the surface to be treated such as, for example, a simple evaluation by weighing the mass of said matter or, on the contrary, can comprise an entire series of operations aiming to physically and/or chemically characterize the matter ejected from the surface to be treated and using techniques such as electronic scanning microscopy or mass spectrometry and, in particular, secondary ion mass spectrometry (SIMS).
The analysis can also consist of determining the ejection speed of the matter from the surface to be treated, in which case a calibration of the penetration depth in the aerogel as a function of the ejection speed is done beforehand.
The invention also relates to a device making it possible to carry out the surface treatment method just described, this device comprising:
For the same reasons as mentioned above, it is preferable for the means for projecting the ejection agent to be means that make it possible to project a gas, a fluid in supercritical state, dry ice, or electromagnetic radiation.
As before, the aerogel can in particular be chosen from inorganic aerogels based on a simple, mixed, or multiple metal oxide, organic aerogels, and organic-inorganic hybrid aerogels.
According to one preferred embodiment of the device according to the invention, it also comprises a controllable-atmosphere enclosure or chamber, i.e. provided with its own means for establishing and maintaining a controlled atmosphere in said enclosure. The enclosure, which can in particular be a vacuum chamber, comprises means for maintaining the object to which the surface to be treated belongs as well as means for maintaining the aerogel piece(s).
In this embodiment, the means for projecting the ejection agent can be situated inside or outside the enclosure depending on the nature of the ejection agent. Thus, if the ejection agent is provided to be electromagnetic radiation and, in particular, a laser beam, the ejection means can be situated outside said enclosure. In that case, the latter preferably comprises a porthole made from a material transparent to the wavelength of said electromagnetic radiation.
Moreover, the means for projecting the ejection agent and the means for maintaining the object in the enclosure can be positioned relative to each other so that the ejection agent can be projected on the surface to be treated along an axis orthogonal to said surface or, on the contrary, along an axis that is inclined relative to the normal at said surface, the angle formed by this axis and this normal then generally being from 20 to 70° and, most often, from 30 to 60°.
Furthermore, the means for projecting the ejection agent and the means for maintaining the aerogel piece(s) in the enclosure can be positioned relative to each other so that the ejection agent can reach the surface to be treated without passing through the aerogel piece or one of the aerogel pieces or, on the contrary, so that it can reach said surface after having passed through the aerogel piece or one of the aerogel pieces.
According to one particularly preferred embodiment of the inventive device, the means for projecting the ejection agent consist of a laser, preferably a gas laser or a crystalline laser, typically with a YAG matrix.
In this case, the means for maintaining the object and the means for maintaining the aerogel piece(s) are preferably positioned relative to each other so that the aerogel piece or one of the aerogel pieces can be located opposite said surface, while being parallel or substantially parallel thereto.
Moreover, the dimensions of this piece are preferably chosen so that its projection in the axis of the plume provided to be produced by the beam emitted by the laser can have, in the plane perpendicular to said axis in which this plume will have the largest dimensions, a perimeter in which the perimeter of said plume can fit.
The invention also relates to the use of an aerogel to trap the matter that is ejected from a surface comprised by an object during a treatment to which said surface is subjected.
The invention has many advantages, in particular because it provides for using an aerogel as trap.
Indeed:
Other advantages and features of the invention will emerge from the additional description that follows, relative to examples of devices according to the invention and in reference to the appended figures.
It goes without saying that these embodiments are provided solely as illustrations of the object of the invention and should in no way be interpreted as being a limitation of that object.
In
Thus, as shown in this figure, this device 10 comprises, on one hand, an enclosure 11 that is provided with means (not shown in
The enclosure 11 contains the object 13 whereof the surface 14 must be treated and, situated opposite said surface and parallel or substantially parallel thereto, a piece of an aerogel 15, with a generally parallelepiped shape.
The object 13 and the aerogel piece 15 are maintained in the enclosure 11 by maintenance means 16 and 17, respectively, which can consist of any device capable of maintaining an object in a determined location, such as an object holder, mounting foot, mounting arm, or similar device. Advantageously, at least one and, preferably, all of these mounting means are mobile and are provided with a system making it possible to adjust their position and, from there, those of the object 13 and the aerogel piece 15.
The enclosure 11 also comprises a porthole 18 opposite which the projection torch 19 of the laser 12 is positioned and which is made up of a material transparent to the emitting wavelength of the laser 12 so as to allow the beam 20 emitted by said laser to pass under in use conditions.
Thus, for example, the porthole 18 can be made from silica glass if the laser 12 emits in the visible range, while it can be made from Pyrex if the laser 12 emits in the near infrared.
The dimensions of the aerogel piece 15 are chosen so that under in use conditions, the projection in the axis of the plasma plume 21 generated by the beam 20 has, in the plane perpendicular to said axis in which the plasma plume 21 has the largest dimensions (which corresponds to plane AA′ in
Moreover, the distance D separating said piece from the surface 14 is chosen such that all of the matter that, under in use conditions, is ejected from said surface under the action of the beam 20 and that is therefore contained in the plasma plume 21 can be trapped in the aerogel piece 15. Typically, this distance goes from several micrometers to 10 cm depending on the pressure conditions under which the surface treatment is done.
The position of the means 16 for maintaining the object 13 is chosen such that under in use conditions, given the dimensions of the aerogel piece 15 and the distance D that separates said piece from the surface 14, the beam 20 reaches said surface along an axis that is inclined relative to the normal at said surface, without passing through or even touching the aerogel piece 15.
Thus, as an example, to clean the surface of a carbon piece measuring 3 cm long and 3 cm wide in a vacuum chamber provided with a silica quartz porthole and where a pressure reigns from 10−4 to 10−6 Pa and a temperature close to ambient temperature, one can use:
Thus, in this alternative, the aerogel piece 15, which is also situated opposite the surface 14, parallel or substantially parallel thereto, is located on the trajectory of the beam 20.
It is therefore either provided with a through opening 23 capable of allowing said beam to pass—as shown in FIG. 2—, or made up of several, for example two, aerogel blocks that are not attached to each other.
This device 10 differs from that illustrated in
The projection torch 19 of the laser 12 is situated directly in contact with the aerogel piece 15 so that under in use conditions, the latter can protect the laser 12 not only from matter ejected from the surface 14, but also from the high temperature likely to reign inside the enclosure 11.
Moreover, the physical and possibly thermal protection of the laser 12 is reinforced by the presence of one or several other aerogel pieces forming a protective sleeve 24 around the laser 12.
Whether the inventive device is of the type illustrated in
Indeed, one need only introduce the object whereof the surface must be treated and the aerogel piece(s) into the enclosure, position them in the chosen configuration using means with which said enclosure is provided to ensure maintenance thereof, close the enclosure, and establish the atmosphere inside this enclosure in which one wishes to perform the surface treatment to be able to start said treatment.
The laser beam is then projected on the surface to be treated and the matter ejected from said surface under the action of said beam is immediat4ely trapped in the aerogel piece(s).
When the treatment is finished, the object and the aerogel piece(s) are removed from the enclosure and an analysis of the matter contained in the aerogel may be done.
If necessary, the aerogel piece(s) can, of course, be replaced during treatment.
| Number | Date | Country | Kind |
|---|---|---|---|
| 08 56013 | Sep 2008 | FR | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP09/61517 | 9/7/2009 | WO | 00 | 5/24/2011 |