Method and plant for making alumina cement and alumina cement

Abstract

The concentration d3 is alumina AL2O3, —A—, and the concentration d4 in lime CaO, —C—, in the initial mixture are such that d3/d4 ranges between 1.15 and 1.40. Grinding produces a cement with a size distribution as represented in a Rosin Rammler diagram has a gradient ranging between 0.75 and 0.90.

Description

[0001] The invention concerns a method for making alumina cement and alumina cement.

[0002] Alumina cement is traditionally made from a mixture of bauxite and limestone. The components of this mixture are sometimes crushed and ground then homogenised. This depends on the type of furnace used.

[0003] The batch composition thus obtained is baked at high temperature, close to 1500 degrees, in a furnace in order to form the clinker.

[0004] This clinker is then ground, whereas secondary constituents may be added to form the cement that is then routed to its place of usage.

[0005] We know that the clinker produced for the manufacture of alumina cement comprises alumina oxide Al2O3, represented in the abbreviated notation in the cement industry as A, and lime CaO represented in the same cement industry by the abbreviated notation C. This notation will be used at a later stage for easier reading of this text. The alumina oxide and the lime are crystallised partially in the form C12A7 on the one hand and in the form CA on the other.

[0006] According to the nature of the initial mixture, the alumina cement is more or less ferriferous.

[0007] Alumina cement is considered in the building chemistry as a raw material that, associated with other components, provides ready-made products such as concrete, mortar, glue, binder and plaster for the manufacture of slabs or cast objects or more generally for any concrete, mortar or plaster.

[0008] Seeking improvement in the qualities of the ready-made products leads to the formulation of products that would associate, to alumina cement, lime, Portland cement, calcium sulphate, as well as a number of additives or assistants.

[0009] It has also appeared that the quality of the ready-made products highly depends on the properties and on the quality of alumina cement.

[0010] Optimised alumina cement enables extending the workability of a mortar, as well as increasing its fluidity, while maintaining very quick hardening kinetics. In other words, the ready-made product using this kind of cement will be applicable for a longer time, but it will achieve final performances at least as rapidly.

[0011] The properties of alumina cements are more particularly expressed by the initial and final setting, the flow value in percentage, the resistance after 6 hours and the resistance after 24 hours.

[0012] The purpose of the invention is therefore the production of specific alumina cement whose properties enable the realisation of high quality ready-made products.

[0013] To this end, the invention concerns a method for making alumina cement as defined above wherein the concentration d3 in alumina Al2O3, —A— and the concentration d4 in lime CaO, —C— in the initial mixture are such that d3/d4 ranges between 1.15 and 1.40, and grinding produces a cement with size distribution as represented in a Rosin Rammler diagram that has a gradient ranging between 0.75 and 0.90. In the invention, the concentration d3 represents the percentage by weight of Al2O3 in the initial mixture, and the concentration d4 represent the percentage by weight of CaO in the initial mixture.

[0014] The combination of the mineralogical properties of the initial composition and of the chemical properties of the clinkers with particular size distribution enables reaching the expected results, independently from the other conventional operating conditions of the process. Therefore, while improving the properties of alumina cement, higher quality ready-made products are obtained.

[0015] Controlling the relative concentration in alumina d3 and in lime d4 in the initial mixture, whereas the ratio of these concentrations d3/d4 ranges between 1.15 and 1.40 and the firing process takes place under oxidising atmosphere, enables low concentration of C12A7 in the clinker.

[0016] The invention also relates to a plant for making alumina cement implementing the method defined above. Firing under oxidising atmosphere, if any, can take place in a reverberatory furnace, a rotary furnace or still an electric furnace. Conversely, the usual firing conditions are reducing conditions leading to high C12A7 content.

[0017] The invention also concerns an alumina cement wherein the concentration d3 in alumina, —A— and the concentration d4 in lime, —C— are such to that d3/d4 ranges between 1.15 and 1.40, and whose size distribution as represented in a Rosin Rammler diagram has a gradient ranging between 0.75 and 0.90.

[0018] The Blaine fineness of the cement ranges preferably between 2,000 and 5,000 cm2/g, advantageously around 3,500 cm2/g.

[0019] Certain embodiments of the invention will be described below in detail with reference to the examples and to the appended figures on which:

[0020] FIG. 1 is a very sketchy representation of a method for making alumina cement, according to prior art;

[0021] FIG. 2 is a schematic representation of a reverberatory furnace;

[0022] FIG. 3 is a schematic representation of the operating conditions of the reverberatory furnace of FIG. 2;

[0023] FIG. 4 is a schematic representation of a clinker grinder;

[0024] FIG. 5 is a schematic representation of the device implemented for determining the fineness of the cement by air-permeability (Blaine method);

[0025] FIG. 6 is an example of representation of the results of a size distribution analysis in a Rosin Rammler diagram.

[0026] Conventionally, as represented on FIG. 1, alumina cement 1 is obtained from a stock of raw material 2 consisting essentially of a mixture of bauxite and limestone that may have been crushed, baked in a furnace 3. The clinker thus produced is kept in a store 4, then ground by the grinder 5.

[0027] This method of manufacture is given for exemplification purposes, whereas methods for making alumina cement by sintering can also prove quite satisfactory.

[0028] The furnace 3 is advantageously a reverberatory furnace as represented on FIG. 2. The raw materials making up the unbaked material originating from the stock 2 are loaded into the feeding hopper 6 at the upper section of the vertical element 7 of the furnace. The unbaked material forms thus a slope 8 that is brought to high temperature, around 1,500 degrees by means of the nozzle 9 and produces the cast 10 that is evacuated through the nose 11 in the moulds 12. The furnace rests on a concrete plinth 13 and the fumes are evacuated through the chimney 14.

[0029] The reverberatory furnace has been described in detail for exemplification purposes. However, similar results can be obtained and the same parameters can be controlled by using another furnace such as, for instance, a tunnel furnace or an electrical furnace, with an induction or electrical arc system.

[0030] The operation of the furnace is more particularly represented on the diagram of FIG. 3. The quality of the clinker obtained is controlled by Theological analyses symbolised in 15 as well as chemical and mineralogical analyses symbolised in 16. A fluorescent analysis X enables following the ratio of the concentration in alumina d3 in relation to the concentration in lime d4 in the clinker. This concentration is controlled while modifying, when it is necessary, the composition of the raw material (of the unbaked stock).

[0031] A regulation loop 20 is thereby provided, enabling to control the chemical composition of the clinkers.

[0032] It has been shown that keeping a concentration ratio d3/d4 ranging between 1.15 and 1.40 maintains the concentration ratio in C12A7 d1 and in CA d2 at a value d1/d2 smaller than 0.09. These values d1 and d2 come from X-Ray Diffraction analysis, more precisely from the direct comparison of the peak intensities of each phase at their main diffraction angle. The ratio d1/d2 is linked to a weight ratio. The advantage of the invention is that d3/d4 ranging between 1.15 and 1.40 leads to d1/d2 at least divided by two compared to alumina cements according to the prior art (Fondu® for instance).

[0033] The grinder 5 is represented in a detailed manner on FIG. 4 and its operating conditions enable controlling the size distribution.

[0034] This grinder 21 comprises an inlet 22 and an outlet 23.

[0035] The tube 24 of the grinder is a thick sheet metal cylinder divided over its length into chambers, two of which have been represented on FIG. 5: the chamber 25 and the chamber 26. The chambers are separate by partitions 27 drilled with slots 28 used for retaining the grinding load and for letting the material through once it has been ground thinly enough.

[0036] The grinding load is made of spherical pebbles 29, 30 and the walls of the grinding tube carry uplifting 31 or sorting 32 shields. The size distribution of the load obtained depends on the diameter of the pebbles 29, 30, the number of chambers 25, 26 as well as the partitions 27 and their slot 28 as well as the filling coefficient of the grinder.

[0037] Grinding increases the total surface of the grains and measuring this surface often constitutes a significant criterion for assessing the grinding degree.

[0038] As exact measurement of such an area cannot be contemplated, it is generally approached by measuring the specific Blaine surface expressed in cm2/g. This method is divulged in the approved French standard NF-EN-196-6 of August 1990.

[0039] Fineness of the cement is measured in the form of mass surface, expressed in cm2 per gram, while monitoring the time taken by a fixed air quantity to travel through a bed of compacted cement with specific sizes and porosity.

[0040] The mass surface of the cement is proportional to {square root}t where t is the time necessary to a given air quantity to run through the bed of compacted cement.

[0041] The device enabling this measurement is represented on FIG. 5-A. A pressure gauge 33 consists of glass tubes 34 carrying engraved marks 36, 37, 38 and 39. The upper section of the pressure gauge comprises a recess 40, honed and intended for receiving the cell 41 represented on FIG. 5-B. A pear 42 enables creating a depression between the opening 43 of the pressure gauge at atmospheric pressure and the basis of the cell. This depression measured with reference to the marks engraved can be maintained by means of a valve 44.

[0042] When measuring, a bed of compacted cement 45, perfectly defined, should be formed, inside the cell 41. This cell is placed inside the recess 40 of the pressure gauge 33. A depression defined and created by the pear 42 is maintained by acting on the valve 44.

[0043] Measuring the time necessary to return to pressure balance between both legs of the pressure gauge is characteristic of the cement fineness.

[0044] The method for measuring the fineness has been described here succinctly and it should be referred to the standard mentioned above that will provide all the characteristics of the device and the operating mode.

[0045] The specific Blaine surface SBS ranges here between 2,000 and 3,000 cm2/g.

[0046] The size distributions of the cements are often represented on a Rosin Rammler diagram defined by the standard X 11-635, such as represented as a bilogarithmic co-ordinate.

[0047] It is known that the size distribution adheres, according to certain theories, to an exponential law:

[0048] The rejection R(x) for a given diameter x is R(x)=1−P(x) where,

P (x)=1−exp [−(x/xo)n]

[0049] where xo is a dimension parameter that corresponds to the value of x for which P=1−1/e.

[0050] There results a linear equation from this size distribution while considering the logarithms of both terms of this equation, then again the logarithms of these logarithms. We obtain therefore:

log (−log (1−P(x))=n(log x−log xo)+log (log e)

[0051] Thus, the size distribution is represented by the value of the gradient of this straight line.

[0052] According to the invention, this gradient ranges between 0.75 and 0.90.

[0053] Moreover, the cement fineness obtained after grinding is characterised by the mass percentage of particles with diameter greater than this value.

[0054] The size distribution is controlled by measuring, in laboratory, samples taken during manufacture.

[0055] According to the results of these measurements, we can correct the grinding time, the filling ratio of the grinder and, more generally, the parameters of the grinder.

[0056] A major breakthrough of this invention is the making of quality alumina cement not only thanks to these chemical or mineralogical properties, but also by controlling and maximising the size distribution.

[0057] The ratio d3/d4 and the firing conditions determine the chemical composition. It enables better stability of the consistency before setting in ready-made products and contributes to the workability of the mortar.

[0058] Although the invention cannot be limited by this explanation, it may be assumed that the size distribution determining the apparent surface of the cement, in contact with water during usage, also acts on the hardening and workability conditions. The combination of the mineralogical or chemical properties of the cement and of its size distribution properties enables achieving exceptional result.

[0059] Different standardised measuring methods enable quantification of the hardening, in particular the initial and the final setting. The method subject to the approved French standard NF-EN-196-3 of March 1990, known as the Vicat method, has been used therein.

[0060] The composition of the mortar is according to the standard NF P15-315, i.e. cement/sand ratio=1/2.7 and water/cement ratio=0.4. The set is measured at 20° C., the samples have been immersed in water or cured at a relative humidity superior to 90%.

[0061] Flow value measurements have complied with the standard ASTM-C230-90.

[0062] A certain quantity of standardised mortar is applied on a calibrated plate subject to a number (25) of shocks. The flow value of cement is measured after these shocks. The set of parameters of this device is duly specified in the standard mentioned above and this device is calibrated.

[0063] Resistance (compressive strength) after 6 hours and 24 hours are measured according to the standard EN 196-1: the test is performed on prisms of 40×40×160 mm, at a temperature of −20° C. Prior to this measurement, the prisms are cured for 24 hours at a relative humidity superior to 90%, then immersed in water till the measurement.

EXAMPLES

[0064] The examples hereunder, in which the samples complying with the invention are compared with samples of the prior art, bear out improved flow value and better final resistance of the products obtained according to the invention, whereas the initial and the final setting remained substantially unchanged, in comparison with the products of the prior art.

	Prior art	Invention
	Sample 1	Sample 2	Sample 3	Sample 4	Sample 5
d3/d4	1.2	1.06	1.01	1.24	1.40
FeO %	2.5	1.2	2.1	4.5	4.74
Reject 90% m	7	7.2	2.4	3	2.7
Rammler gradient	0.72	0.70	0.80	0.80	0.85
Blaine fineness	3160	3260	3426	3182	3135
Initial setting/Final setting	250/290	180/240	150/180	200/240	205/295
(minutes)
Flow value %	100	100	60	>150	150
Compressive strength 6h	22	42	46	48	21
(Mpa)
Compressive	52	68	57	60	60
strength 24h (Mpa)

Claims

1. A method of making alumina cement in which a batch composition is obtained, from an initial mixture consisting essentially of bauxite and of limestone, the said composition is baked in a furnace in order to form a clinker containing alumina oxide Al2O3, —A—, and lime CaO, —C—, partially in the form C12A7 on the one hand and in the form CA on the other, whereas the said clinker is then ground with other possible secondary constituents to form the cement,

2. A method according to claim 1, characterised in that the Blaine fineness of the cement ranges between 2,000 and 5,000 cm2/g.

3. A method according to claim 1, characterised in that the Blaine fineness of the cement is around 3,500 cm2/g.

4. A method according to any of the claims 1 to 3, characterised in that the furnace is a reverberatory furnace.

5. A method according to any of the claims 1 to 3, characterised in that the furnace is an electrical furnace.

6. An alumina cement comprising alumina oxide Al2O3, —A—, and lime CaO, —C—, wherein the concentration d3 in alumina Al2O3, —A— and the concentration d4 in lime CaO, —C— in the initial mixture are such that d3/d4 ranges between 1.15 and 1.40, and its size distribution represented in a Rosin Rammler diagram has a gradient ranging between 0.75 and 0.90.