Aspects of the present disclosure relate to energy generation and storage. More specifically, certain embodiments of the disclosure relate to a method and system for conductive polymer monomers as cathode additives for silicon-based lithium ion batteries.
Conventional approaches for battery cathodes may be costly, cumbersome, and/or inefficient—e.g., they may be complex and/or time consuming to implement, and may limit battery lifetime.
Further limitations and disadvantages of conventional and traditional approaches will become apparent to one of skill in the art, through comparison of such systems with some aspects of the present disclosure as set forth in the remainder of the present application with reference to the drawings.
A system and/or method for conductive polymer monomers as cathode additives for silicon-based lithium ion batteries, substantially as shown in and/or described in connection with at least one of the Figures, as set forth more completely in the claims.
These and other advantages, aspects and novel features of the present disclosure, as well as details of an illustrated embodiment thereof, will be more fully understood from the following description and drawings.
The development of portable electronic devices and electrification of transportation drive the need for high performance electrochemical energy storage. Small-scale (<100 Wh) to large-scale (>10 KWh) devices primarily use lithium-ion (Li-ion) batteries over other rechargeable battery chemistries due to their high-performance.
The anode 101 and cathode 105, along with the current collectors 107A and 107B, may comprise the electrodes, which may comprise plates or films within, or containing, an electrolyte material, where the plates may provide a physical barrier for containing the electrolyte as well as a conductive contact to external structures. In other embodiments, the anode/cathode plates are immersed in electrolyte while an outer casing provides electrolyte containment. The anode 101 and cathode are electrically coupled to the current collectors 107A and 107B, which comprise metal or other conductive material for providing electrical contact to the electrodes as well as physical support for the active material in forming electrodes.
The configuration shown in
In an example scenario, the battery 100 may comprise a solid, liquid, or gel electrolyte. The separator 103 preferably does not dissolve in typical battery electrolytes such as compositions that may comprise: Ethylene Carbonate (EC), Fluoroethylene Carbonate (FEC), di-fluoroethylene carbonate (DiFEC), trifluoropropylene carbonate (TFPC), vinyl carbonate (VC), Propylene Carbonate (PC), Dimethyl Carbonate (DMC), Ethyl Methyl Carbonate (EMC), Diethyl Carbonate (DEC), etc. with dissolved lithium hexafluorophosphate (LiPF6), lithium tetrafluoroborate (LiBF4), lithium hexafluoroarsenate monohydrate (LiAsF6), lithium perchlorate (LiClO4), lithium bis(trifluoromethanesulfonyl)imide (LiTFSI), lithium bis(fluorosulfonyl)imide (LiFSI), lithium difluoro(oxalate)borate (LiDFOB), lithium bis(oxalato)borate (LiBOB), and lithium triflate (LiCF3SO3), lithium tetrafluorooxalato phosphate (LTFOP), lithium difluorophosphate (LiPO2F2), lithium pentafluoroethyltrifluoroborate (LiFAB), and lithium 2-trifluoromethyl-4,5-dicyanoimidazole (LiTDI), lithium bis(2-fluoromalonato)borate (LiBFMB), lithium 4-pyridyl trimethyl borate (LPTB) and lithium 2-fluorophenol trimethyl borate (LFPTB), lithium catechol dimethyl borate (LiCDMB), etc. The separator 103 may be wet or soaked with a liquid or gel electrolyte. In addition, in an example embodiment, the separator 103 does not melt below about 100 to 120° C., and exhibits sufficient mechanical properties for battery applications. A battery, in operation, can experience expansion and contraction of the anode and/or the cathode. In an example embodiment, the separator 103 can expand and contract by at least about 5 to 10% without failing, and may also be flexible.
The separator 103 may be sufficiently porous so that ions can pass through the separator once wet with, for example, a liquid or gel electrolyte. Alternatively (or additionally), the separator may absorb the electrolyte through a gelling or other process even without significant porosity. The porosity of the separator 103 is also generally not too porous to allow the anode 101 and cathode 105 to transfer electrons through the separator 103.
The anode 101 and cathode 105 comprise electrodes for the battery 100, providing electrical connections to the device for transfer of electrical charge in charge and discharge states. The anode 101 may comprise silicon, carbon, or combinations of these materials, for example. Typical anode electrodes comprise a carbon material that includes a current collector such as a copper sheet. Carbon is often used because it has excellent electrochemical properties and is also electrically conductive. Anode electrodes currently used in rechargeable lithium-ion cells typically have a specific capacity of approximately 200 milliamp hours per gram. Graphite, the active material used in most lithium ion battery anodes, has a theoretical energy density of 372 milliamp hours per gram (mAh/g). In comparison, silicon has a high theoretical capacity of 4200 mAh/g at high temperature and 3579 mAh/g at room temperature. In order to increase volumetric and gravimetric energy density of lithium-ion batteries, silicon may be used as the active material for the cathode or anode. Silicon anodes may be formed from silicon composites, with more than 50% silicon, for example.
In an example scenario, the anode 101 and cathode 105 store the ion used for separation of charge, such as lithium. In this example, the electrolyte carries positively charged lithium ions from the anode 101 to the cathode 105 in discharge mode, as shown in
While the battery 100 is discharging and providing an electric current, the anode 101 releases lithium ions to the cathode 105 via the separator 103, generating a flow of electrons from one side to the other via the coupled load 109. When the battery is being charged, the opposite happens where lithium ions are released by the cathode 105 and received by the anode 101.
The materials selected for the anode 101 and cathode 105 are important for the reliability and energy density possible for the battery 100. The energy, power, cost, and safety of current Li-ion batteries need to be improved in order to, for example, compete with internal combustion engine (ICE) technology and allow for the widespread adoption of electric vehicles (EVs). High energy density, high power density, and improved safety of lithium-ion batteries are achieved with the development of high-capacity and high-voltage cathodes, high-capacity anodes and functionally non-flammable electrolytes with high voltage stability and interfacial compatibility with electrodes. In addition, materials with low toxicity are beneficial as battery materials to reduce process cost and promote consumer safety.
The performance of electrochemical electrodes, while dependent on many factors, is largely dependent on the robustness of electrical contact between electrode particles, as well as between the current collector and the electrode particles. The electrical conductivity of silicon anode electrodes may be manipulated by incorporating conductive additives with different morphological properties. Carbon black (SuperP), vapor grown carbon fibers (VGCF), graphite, graphene, etc. and/or a mixture of these have previously been incorporated separately into the anode electrode resulting in improved performance of the anode. The synergistic interactions between the two carbon materials may facilitate electrical contact throughout the large volume changes of the silicon anode during charge and discharge.
State-of-the-art lithium-ion batteries typically employ a graphite-dominant anode as an intercalation material for lithium. Silicon-dominant anodes, however, offer improvements compared to graphite-dominant Li-ion batteries. Silicon exhibits both higher gravimetric (3579 mAh/g vs. 372 mAh/g for graphite) and volumetric capacities (2194 mAh/L vs. 890 mAh/L for graphite). In addition, silicon-based anodes have a lithiation/delithiation voltage plateau at about 0.3-0.4V vs. Li/Li+, which allows it to maintain an open circuit potential that avoids undesirable Li plating and dendrite formation. While silicon shows excellent electrochemical activity, achieving a stable cycle life for silicon-based anodes is challenging due to silicon's large volume changes during lithiation and delithiation. Silicon regions may lose electrical contact from the anode as large volume changes coupled with its low electrical conductivity separate the silicon from surrounding materials in the anode.
In addition, the large silicon volume changes exacerbate solid electrolyte interphase (SEI) formation, which can further lead to electrical isolation and, thus, capacity loss. Expansion and shrinkage of silicon particles upon charge-discharge cycling causes pulverization of silicon particles, which increases their specific surface area. As the silicon surface area changes and increases during cycling, SEI repeatedly breaks apart and reforms. The SEI thus continually builds up around the pulverizing silicon regions during cycling into a thick electronic and ionic insulating layer. This accumulating SEI increases the impedance of the electrode and reduces the electrode electrochemical reactivity, which is detrimental to cycle life.
Among all the potential cathode active materials, Ni-rich NCA (Nickel cobalt aluminum oxide) and NCM (Nickel Cobalt Manganese Oxide) are considered to be most promising. Ni-rich NCA or NCM cathodes show excellent thermodynamic stability and specific capacity as high as 200 mAh/g. Although NCA or NCM are best known for long-term stability and high energy density, they have also been shown to be problematic due to poor cycle stability and low electronic conductivity.
It is generally believed that the capacity of the cathode materials is one of the major limiting factors for the energy density of Li-ion batteries. Therefore, Ni-rich cathode materials (such as NCA, NCM) and Li-rich layered oxide cathode materials have been considered and explored as the possible future choices because of their high specific capacity and low cost. These materials are especially useful if they can be coupled with high capacity and low-voltage anode materials, such as Si. However, these cathode materials have some fundamental challenges, such as irreversible phase transition from hexagonal through cubic to rock salt structure, mechanical crack of the secondary particle structure, electrolyte depletion that is often accompanied by impedance increase and volumetric swelling of the batteries, as well as gelation of cathode slurry in the slurry-making process.
Notwithstanding continuing improvements in cathode technology, there remains a need to address technological hurdles concerning the cyclability, rate capability, and thermal stability. Cell performance deterioration in Ni-rich cathode-based cells has been proposed to be associated with aggressive chemical, structural and mechanical degradation occurring on both Ni-based cathode the high capacity anodes (e.g., Si-dominant anodes and the like). The deterioration may be due in part to (i) parasitic oxidation of electrolyte components catalyzed by the delithiated cathodes at high voltage, (ii) dissolution of the active cathode material aggravated by acidic species attack from the electrolyte (e.g., HF), (iii) irreversible structural changes induced by large internal strains during repeated delithiation/lithiation, (iv) sustainable parasitic electrolyte reduction and consumption of active Li ions in forming a thick and unstable SEI layer on the surface of anodes, triggered by the crossover of the active mass dissolution products from the cathode sides (e.g. transition metal ions).
From the cathode side, a number of strategies may be utilized to overcome these issues, such as cation doping for stabilizing the cathode material lattice structure, surface coating for protecting cathode particles from parasitic reactions with the electrolyte components, synthesizing concentration-gradient or core-shell structures with high Ni content core for stabilizing the material's surface chemistry, as well as using electrolyte additives for chemically trapping the released oxygen.
While some prior surface treatments with conducting polymers can be effective in ameliorating charge capacities and cycling performances for a wide range of lithium-ion batteries, all such existing treatments require additional processing steps (e.g., precipitating, washing, and/or heating) which increases the manufacturing cost.
Without negative impacts on the anode, electrolyte, and the battery manufacturing procedures or design, adding a cathode additive is considered to be another efficient, cost-effective and practically feasible strategy to overcome the barriers of layered cathode materials and to improve the full cell performance. The aspects and example embodiments described and claimed herein simplify the manufacturing process and treatments by dispersing small amount of conductive polymer monomers, such as functional thiophene compounds, functional pyrrole compounds, and functional aniline compounds, into the normal cathode-coating slurry to prepare the additive-containing cathodes for Li-ion batteries.
Conductive polymer monomers, including example embodiments comprising thiophene-based monomers, pyrrole-based monomers, and/or aniline-based monomers (e.g., 3,4-thiophenedicarboxylic anhydride (TDCA), 3,4-difluoro-2,5-bis(trimethylsilyl)thiophene (DFBTST), 1-(2-cyanoethyl) pyrrole (CEP), thiophene-2-carboxylic anhydride (TCA), 1H-pyrrole-2-carbonitrile, 1-ethenyl-1H-pyrrole, 2-ethenyl-1H-pyrrole, 1-ethynyl-1H-pyrrole, 2-ethynyl-1H-pyrrole, 3-ethynyl-1H-pyrrole, 1-vinyl-1H-pyrrole-2,5-dione, 2-ethenyl-1H-pyrrole, 1-(prop-2-enyl)pyrrole, 1,3,4-tris(prop-2-enyl)pyrrole, 1H-pyrrole-1-carboxylic anhydride, acetic 1H-pyrrole-3-carboxylic anhydride, 1-prop-2-enylpyrrole-2,5-dione, 3-prop-2-enylpyrrole-2,5-dione, 3,4-bis(prop-2-enyl)pyrrole-2,5-dione, aniline, aniline (hydrochloride), 3-(trifluoromethyl)aniline, 2-nitroaniline, 4-cyano-3-(trifluoromethyl)aniline, aniline-2-sulfonic acid, and/or 4, 4′-methylenedianiline), or other monomer structures that can form conductive polymeric structures may be used as cathode additives for different types of cathode-based materials (such as Ni-rich NCA or NCM, Li-rich, xLi2MnO3·(1−x)LiNiaCobMncO2, Li-rich layered oxides, high-voltage spinel oxides, etc.) that are incorporated into Li-ion full cells with anodes containing Si. These materials may be incorporated as additives in the cathode active material slurry, by directly adding them into the electrolyte solution, and/or by dipping the prepared cathodes into solutions or suspensions that contain these materials. Therefore, the conductive polymer monomer additive(s) may be incorporated within the cathodes or on the surface of the cathodes. This may help improve structural stability and/or enhance the ionic conductivity and lifespan of the cathode materials. In addition, the conductive polymer monomers may help form a passivation layer on the surface of the cathodes, which not only hinders the formation of LiF, carbonates, and semicarbonate compounds but also renders the nature of the cathode electrolyte interphase layer formed during electrochemical cycles. It may be that incorporating the conductive polymer monomers may inhibit the dissolution of the active material into the electrolyte and preserve the initial atomic states including the active material bulk. Regardless of mechanism, the resulting unexpected effect achieved through incorporating the conductive polymer monomers into cathodes as described herein may be helpful to further improve the cycle performance and energy density of high-capacity, high-voltage cathode based Li-ion full cells with Si anodes. At the same time, these materials may also interact with the Si anode and contribute to the SEI composition and formation. And, as mentioned above, the conductive polymer monomer-containing additive may form electronically conductive interphase films, and be beneficial to the ionic conductivity of the interphase.
In step 201, the raw electrode active material may be mixed using a binder/resin (such as PI, PAI), solvent, and conductive carbon. For example, for the cathode, Super P/VGCF (1:1 by weight), or other types carbon materials, such as graphite, graphene, etc., may be dispersed in binder solution (mixture of NMP and PVDF) for 0.5 to 2 minutes at 1500-2500 rpm. NCA cathode material powder may be added to the mixture along with NMP solvent, then dispersed for another 1-3 minutes at 1500-2500 rpm to achieve a slurry viscosity within 2000-4000 cP (total solid content of about 48%). A conductive polymer monomer-based additive may be mixed in with the slurry at this point, or may be added at a later stage in the process. A similar process may be utilized to mix the active material slurry for the anode.
In step 203, the cathode slurry may be coated on an aluminum foil at a loading of, e.g., 15-35 mg/cm2. Similarly, the anode slurry may be coated on a copper foil at a loading of 3-6 mg/cm2, which may undergo drying in step 205 resulting in less than 13-20% residual solvent content. In another example scenario, a conductive polymer monomer-based additive may be incorporated by dipping the coated foil in a solution or suspension containing the desired conductive polymer monomer additive(s).
In step 207, an optional calendering process may be utilized where a series of hard pressure rollers may be used to finish the film/substrate into a smoother and denser sheet of material.
In step 209, the active material (i.e., electrode coating layer) may be pyrolyzed by heating to 500-1200° C. such that carbon precursors are partially or completely converted into glassy carbon. Pyrolysis can be done either in roll form or after punching in step 211. If done in roll form, the punching is done after the pyrolysis process. The punched electrode may then be sandwiched with a separator and cathode with electrolyte to form a cell. If the conductive polymer monomer-based additive has not been incorporated up to this point, it may be added after pyrolysis in the cell fabrication process as an electrolyte additive, for example. In step 213, the cell may be subjected to a formation process, comprising initial charge and discharge steps to lithiate the anode, with some residual lithium remaining and cell testing to determine performance.
This process is shown in the flow diagram of
In step 303, the slurry may be coated on a polymer substrate, such as polyethylene terephthalate (PET), polypropylene (PP), or Mylar. The slurry may be coated on the PET/PP/Mylar film at a loading of 3-6 mg/cm2 (with 13-20% solvent content) for the anode and 15-35 mg/cm2 for the cathode, and then dried to remove a portion of the solvent in step 305. In another example scenario, a conductive polymer monomer-based additive may be incorporated by dipping the green layer coated substrate in a solution or suspension containing the desired conductive polymer monomer(s). An optional calendering process may be utilized where a series of hard pressure rollers may be used to finish the film/substrate into a smoothed and denser sheet of material.
In step 307, the green film may then be removed from the PET, where the active material may be peeled off the polymer substrate, the peeling process being optional for a polypropylene (PP) substrate, since PP can leave ˜2% char residue upon pyrolysis. The peeling may be followed by a cure and pyrolysis step 309 where the film may be cut into sheets, and vacuum dried using a two-stage process (100-140° C. for 14-16 hours, 200-240° C. for 4-6 hours). The dry film may be thermally treated at 1000-1300° C. to convert the polymer matrix into carbon.
In step 311, the pyrolyzed material may be flat press or roll press laminated on the current collector, where for aluminum foil for the cathode and copper foil for the anode may be coated with polyamide-imide with a nominal loading of 0.35-0.75 mg/cm2 (applied as a 5-7 wt % varnish in NMP, dried 10-20 hour at 100-140° C. under vacuum). In flat press lamination, the active material composite film (i.e., electrode coating layer) may be laminated to the coated aluminum or copper using a heated hydraulic press (30-70 seconds, 250-350° C., and 3000-5000 psi), thereby forming the finished composite electrode. In another embodiment, the pyrolyzed material may be roll-press laminated to the current collector. In yet another example scenario, a conductive polymer monomer-based additive may be incorporated by dipping the coated foil in a solution or suspension containing the desired conductive polymer monomer(s).
In step 313, the electrodes may then be sandwiched with a separator and electrolyte to form a cell. If the conductive polymer monomer-based additive has not been incorporated up to this point, it may be added after pyrolysis in the cell fabrication process as an electrolyte additive, for example. The cell may be subjected to a formation process, comprising initial charge and discharge steps to lithiate the anode, with some residual lithium remaining, and testing to assess cell performance.
As illustrated in the disclosure and example embodiments below, preparing a cathode (and a battery incorporating such a cathode) with an additive comprising at least one conductive polymer monomer provides several advantages. For example, incorporating an amount of at least one conductive polymer monomer additive into the cathode manufacturing process can provide a battery having increased cycle lifespan, increased safety, increased thermal stability of the electrolyte, enhanced high temperature performance of the battery cells, decreased electrolyte consumption/degradation, and decreased impedance increase in electrode interfaces.
In accordance with the disclosure, solutions and/or suspensions in solvents, (e.g., organic solvents) containing at least one conductive polymer monomer and/or mixtures thereof, are prepared and are capable of being incorporated in the manufacture of cathodes, and battery cells including such cathodes.
In an example scenario, one or more conductive polymer monomers may be used as a cathode additive to improve cycle performance of Li[NixCoyAl1−x-y]O2 (NCA) or Li[NixCoyMn1−x-y]O2 (NCM) (including NCM811, NCM622, NCM532, NCM442, NCM111, etc.) and other cathode active materials described herein, that are incorporated into cathode-based Li-ion full cells with all other types of Si anodes. Furthermore, one or more conductive polymer monomers as described herein may be used as a cathode additive to improve cycle performance for LCO and/or LMO cathode-based full cells with different Si anodes. In example embodiments at least one conductive polymer monomer selected from thiophene-based monomers, pyrrole-based monomers, and/or aniline-based monomers may also be utilized as a cathode additive to improve cycle performance for Li-rich, xLi2MnO3·(1−x)LiNiaCobMncO2 cathode-based full cells with different Si anodes, as well as for a cathode additive to improve cycle performance for Ni-rich layered oxides (LiNi1−xMxO2, where M=Co, Mn, and Al)-based Li-ion full cells with different Si anodes. In another example, conductive polymer monomers may be used as a cathode additive to improve cycle performance for Li-rich layered oxides (LiNi1+xM1−xO2, where M=Co, Mn, and Ni)-based Li-ion full cells with different Si anodes. In yet another example, conductive polymer monomers may be used as a cathode additive to improve cycle performance for high-voltage spinel oxides (LiNi0.5Mn1.5O4) cathode Li-ion full cells with different Si anodes.
Conductive polymer monomers may also be used as a cathode additive to improve cycle performance for high-voltage polyanionic compounds (phosphates, sulfates, silicates, etc.) cathode-based Li-ion full cells with different anodes, including Si and Si-dominant anodes. The conductive polymer monomers as incorporated in any of the above examples may be selected from any type of monomer that, upon polymerization, forms a conductive polymer structure, including the example embodiments of thiophene-, pyrrole-, and aniline-based monomer that are described herein. Such example embodiments of conductive polymer monomers may be utilized as a cathode additive to improve cycle performance of all of the aforementioned cathode-based Li-ion full cells with different Si anodes.
In another example scenario, intermediates, including reactive intermediates/free radicals, partially polymerized materials, and the like, derived from one or more conductive polymer monomers (e.g., precursors of, or partially reacted/polymerized forms of thiophene, pyrrole, and aniline monomers, etc.) or other conductive polymer monomer-containing materials or precursor materials may be utilized as a cathode additive to improve cycle performance of all of the aforementioned cathode-based Li-ion full cells with different Si anodes.
Each of the aforementioned materials may be incorporated in a cathode active material slurry, or deposited on a cathode active material (i.e., electrode coating layer) after being formed on a substrate or foil, by dipping in a second slurry or depositing with other layer deposition techniques. The conductive polymer monomer additive may comprise 5% or less of the cathode active material (e.g., 5.0%, 4.5%, 4.0%, 3.5%, 3.0%, 2.5%, 2.0%, 1.5%, 1.0%, 0.5%, 0.25%, or 0.1%) by weight. In another example embodiment, the conductive polymer monomer additive may comprise 2% (wt) or less of the cathode active material. In yet another example, the conductive polymer monomer-containing additive may comprise 1% (wt) or less of the cathode active material.
A conductive polymer monomer-containing additive-based solution may be utilized to directly coat or incorporate the polymer monomer(s) into cathode active material (i.e., electrode coating layer). The solvent in the solution may comprise any solvent that is capable of solubilizing or dispersing at least a portion of the conductive polymer monomer in solution. Some example embodiments of a solvent may include common organic solvents such as, for example, alcohols, ethers, aromatic solvents, CS2, cyclohexane, toluene or other similar solvents.
The anodes used with the conductive polymer monomer-additive cathodes disclosed here may comprise >50% silicon in the active material and heat-treated to above 300 degrees Celsius. In another example scenario, the anodes may comprise >25% silicon in the active material and heat-treated to above 300 degrees Celsius. In yet another example scenario, the anodes may comprise >50% silicon in the active material and heat-treated to above 400 degrees Celsius.
In an example embodiment of the disclosure, a method and system are described for conductive polymer monomer-containing chemicals as cathode additives for silicon-based lithium ion batteries. The battery may comprise a silicon-based anode, an electrolyte, and a cathode. The cathode may comprise an active material and a conductive polymer monomer-containing additive. The cathode active material may comprise one or more of nickel cobalt aluminum oxide (NCA), nickel cobalt manganese oxide (NCM) including, for example, Ni-rich NCM90 (9,0.5,0.5), NCM811, NCM622, NCM532, NCM442, NCM333, NCMA, lithium iron phosphate (LFP), lithium cobalt oxide (LCO), and lithium manganese oxide (LMO), Ni-rich layered oxides (LiNi1−xMxO2, where M=Co, Mn, or Al), Li-rich xLi2MnO3·(1−x)LiNiaCobMncO2, Li-rich layered oxides (LiNi1+xM1−xO2, where M=Co, Mn, or Ni), high-voltage spinel oxides (LiNi0.5Mn1.5O4), high-voltage polyanionic compounds including, for example, phosphates, sulfates, silicates, and the like, as well as other cathode materials.
In example embodiments, the pyrrole-based monomer that may be added to the cathode may comprise any one or more pyrrole monomer(s) that can polymerize to form a conductive polymer structure. In some example embodiments the pyrrole-based monomer may be polymerized under oxidizing conditions to form a conductive polymer. In some example embodiments the pyrrole-based monomer may be polymerized under reducing conditions to form a conductive polymer. In some example embodiments the pyrrole-based monomer may be selected from one or more of the monomers in Table 1.
In example embodiments, the aniline-based monomer that may be added to the cathode may comprise any one or more aniline monomer(s) that can polymerize to form a conductive polymer structure. In some example embodiments the aniline-based monomer may be polymerized under oxidizing conditions to form a conductive polymer. In some example embodiments the aniline-based monomer may be polymerized under reducing conditions to form a conductive polymer. In some example embodiments the aniline-based monomer may be selected from one or more of the monomers in Table 2.
In example embodiments, the thiophene-based monomer that may be added to the cathode may comprise any one or more thiophene monomer(s) that can polymerize to form a conductive polymer structure. In some example embodiments the thiophene-based monomer may be polymerized under oxidizing conditions to form a conductive polymer. In some example embodiments the thiophene-based monomer may be polymerized under reducing conditions to form a conductive polymer. In some example embodiments the thiophene-based monomer may be selected from one or more of the monomers in Table 3.
Accordingly, the conductive polymer monomer additive may comprise one or more of pyrrole-based, aniline-based, and thiophene-based monomers, including the example monomers described above. The conductive polymer monomer-containing additive may comprise 5% or less by weight of the active material, or 1% or less by weight of the active material.
As described above, example embodiments in accordance with the disclosure provide a cathode that may include the conductive polymer monomer-containing additive, or combinations thereof, as described herein. Other example embodiments in accordance with the disclosure, provide an anode that may include the conductive polymer monomer-containing additive, or combinations thereof, as described herein. As described herein in such example embodiments, the anode may comprise an active material that comprises between 50% to 95% silicon. Yet other example embodiments in accordance with the disclosure, provide an electrolyte that may include the conductive polymer monomer-containing additive, or combinations thereof, as described herein. In such example embodiments, the electrolyte such as the example electrolytes disclosed herein may comprise a liquid, solid, or gel, or combinations thereof. Thus, the example embodiments described herein provide for a battery, or one or more battery components that may include the conductive polymer monomer-containing additive, or combinations thereof, as described herein. In example embodiments, the battery may comprise a lithium ion battery.
An electrolyte composition may be prepared in accordance with the disclosure. As an example embodiment, one or more conductive polymer monomers may be included in an electrolyte by adding such monomer(s) at about 0.5 wt % or 1 wt % or more (e.g., up to about 5 wt %) to the electrolyte such as, for example, an electrolyte that may comprise 1.2M LiPF6 in FEC/EMC (3/7 wt %). In such example embodiments, amounts of one or more conductive polymer monomer additives may be added and may include from about 0.5% to about 1.0% (wt) of one or more additives, such as 3,4-thiophenedicarboxylic anhydride (TDCA), thiophene-2-carboxylic anhydride (TCA), 3,4-difluoro-2,5-bis(trimethylsilyl)thiophene (DFBTST), and 1-(2-cyanoethyl) pyrrole (CEP), or any combination thereof. The additive-containing electrolyte may be incorporated into cells such as, for example, half or full cells, or a battery that may be constructed with an anode (e.g., Si-dominant anode) and a cathode (e.g., NCM811) and may be tested at about 1 C/0.5 C charge/discharge processes with a working voltage window of about 4.2V to 3.1V.
In accordance with some example embodiments of the disclosure, the functional conductive polymer monomer-containing additives may be used as part of a Li-ion battery. In some embodiments, the conductive polymer monomer-containing additives may be part of an electrode, such as part of a cathode or Si-containing (e.g., Si dominant) anode. In other example embodiments, the conductive polymer monomer-containing additives may be used, alone or in any combination with each other, as an additive for an electrolyte. In accordance with the disclosure, some example embodiments provide for soluble conductive polymer monomer-containing additives that may be incorporated as an electrolyte additive, and for insoluble conductive polymer monomer-containing additives that may be used as part of an electrode, or as an insoluble electrolyte additive. In some example embodiments a combination of conductive polymer monomer additives can be incorporated including, for example, a combination of soluble and insoluble conductive polymer monomer additives. Procedures for incorporating electrolyte additives in a Li-ion battery suitable for use with the present invention include known processes, as well as the processes described in co-pending U.S. patent application Ser. No. 16/430,302 (filed Jun. 3, 2019), Ser. No. 16/430,298 (filed Jun. 3, 2019), and Ser. No. 16/722,746 (filed Dec. 20, 2019), as well as U.S. provisional patent application Ser. Nos.: 62/857,700 (filed Jun. 5, 2019) and 62/857,742 (filed Jun. 5, 2019) each of which is hereby incorporated herein by reference in their entirety.
A cathode may be prepared in accordance with the disclosure. For example, 3,4-difluoro-2,5-bis(trimethylsilyl)thiophene (DFBTST) may be incorporated into the manufacturing process of a cathode, such as NCM811, and added at about 1% by weight of the active material in accordance with an example embodiment of the disclosure.
Referring to
In an example scenario, the long-term cycling programs comprise: (i) At the 1st cycle, charge at 0.33 C to 4.2 V until 0.05 C, rest 5 minutes, discharge at 0.33 C to 3.1 V, rest 5 minutes; and (ii) from the 2nd cycle, charge at 1 C to 4.2 V until 0.05 C, rest 5 minutes, discharge at 0.5 C to 3.1 V, rest 5 minutes. After every 100 cycles, the test conditions in the 1st cycle may be repeated, which corresponds to the spikes in the curves depicted in
As depicted in
In accordance with another example embodiment of the disclosure, another illustrative cathode may be prepared that incorporates at least one conductive polymer monomer. For example, a thiophene-based monomer such as 3,4-thiophenedicarboxylic anhydride (TCDA) may be incorporated into the manufacturing process of a cathode, such as NCM811, and added at about 0.5% by weight of the active material in accordance with an example embodiment of the disclosure.
Referring to
In an example scenario, the long-term cycling programs comprise: (i) at the 1st cycle, charge at 0.33 C to 4.2 V until 0.05 C, rest 5 minutes, discharge at 0.33 C to 3.1 V, rest 5 minutes; and (ii) from the 2nd cycle, charge at 1 C to 4.2 V until 0.05 C, rest 5 minutes, discharge at 0.5 C to 3.1 V, rest 5 minutes. After every 100 cycles, the test conditions in the 1st cycle may be repeated, which corresponds to the spikes in the curves depicted in
As depicted in
Thus, the disclosure provides example embodiments that relate to a battery, the battery comprising: a silicon-based anode, an electrolyte, and a cathode, wherein the cathode comprises an active material and a conductive polymer monomer additive comprising an aniline, a pyrrole, or a thiophene, or a combination thereof. In other example embodiments, the disclosure relates to a battery, the battery comprising: a silicon-based anode, an electrolyte, and a cathode, wherein the anode comprises an active material and a conductive polymer monomer additive comprising an aniline, a pyrrole, or a thiophene, or a combination thereof. In yet other example embodiments, the disclosure relates to a battery, the battery comprising: a silicon-based anode, an electrolyte, and a cathode, wherein the electrolyte comprises an electrolyte material and a conductive polymer monomer additive comprising an aniline, a pyrrole, or a thiophene, or a combination thereof.
The disclosure provides example embodiments that relate to a cathode, wherein the cathode may comprise an active material and a conductive polymer monomer additive comprising an aniline, a pyrrole, or a thiophene, or a combination thereof.
The disclosure provides example embodiments that relate to an anode, wherein the anode may comprise an active material and a conductive polymer monomer additive comprising an aniline, a pyrrole, or a thiophene, or a combination thereof.
The disclosure provides example embodiments that relate to an electrolyte, wherein the electrolyte may comprise an electrolyte material and a conductive polymer monomer additive comprising an aniline, a pyrrole, or a thiophene, or a combination thereof.
The disclosure provides example embodiments that relate to a method of forming a battery, wherein the method may comprise: forming a battery comprising a silicon-based anode, an electrolyte, and a cathode, wherein the cathode, the anode, and/or the electrolyte comprises a conductive polymer monomer additive comprising an aniline, a pyrrole, or a thiophene, or a combination thereof. In some example embodiments the disclosure provides a method of forming a cathode, an anode, and/or an electrolyte comprising adding a conductive polymer monomer additive comprising an aniline, a pyrrole, or a thiophene, or a combination thereof to the cathode, the anode, and/or the electrolyte.
In any of the above example embodiments, the battery, the cathode, or the method may comprise a cathode active material comprising one or more of: nickel cobalt aluminum oxide (NCA), nickel cobalt manganese oxide (NCM), lithium iron phosphate (LFP), lithium cobalt oxide (LCO), and lithium manganese oxide (LMO), Ni-rich layered oxides of the structure LiNi1−xMxO2 where M=Co, Mn, or Al, Li-rich xLi2MnO3(1−x)LiNiaCobMncO2, Li-rich layered oxides of the structure LiNi1+xM1−xO2 where M=Co, Mn, or Ni, and spinel oxides LiNi0.5Mn1.5O4. In example embodiments, the battery, the cathode, or the method may comprise a conductive polymer monomer additive that comprises at least one thiophene selected from 3,4-thiophenedicarboxylic anhydride (TDCA), 3,4-difluoro-2,5-bis(trimethylsilyl)thiophene (DFBTST), 1-(2-cyanoethyl) pyrrole (CEP), or thiophene-2-carboxylic anhydride (TCA). In example embodiments, the battery, the cathode, or the method may comprise a conductive polymer monomer additive that comprises at least one pyrrole selected from 1H-pyrrole-2-carbonitrile, 1-ethenyl-1H-pyrrole, 2-ethenyl-1H-pyrrole, 1-ethynyl-1H-pyrrole, 2-ethynyl-1H-pyrrole, 3-ethynyl-1H-pyrrole, 1-vinyl-1H-pyrrole-2,5-dione, 2-ethenyl-1H-pyrrole, 1-(prop-2-enyl)pyrrole, 1,3,4-tris(prop-2-enyl)pyrrole; 1H-pyrrole-1-carboxylic anhydride, acetic 1H-pyrrole-3-carboxylic anhydride, 1-prop-2-enylpyrrole-2,5-dione, 3-prop-2-enylpyrrole-2,5-dione, or 3,4-bis(prop-2-enyl)pyrrole-2,5-dione. In example embodiments, the battery, the cathode, or the method may comprise a conductive polymer monomer additive that comprises at least one aniline selected from aniline, aniline (hydrochloride), 3-(trifluoromethyl)aniline, 2-nitroaniline, 4-cyano-3-(trifluoromethyl)aniline, aniline-2-sulfonic acid, or 4, 4′-methylenedianiline. In such example embodiments, the conductive polymer monomer additive may comprise 5% or less by weight of the active material. In further such example embodiments, the conductive polymer monomer additive may comprise 1% or less by weight of the active material. In example embodiments, the battery may comprise an anode comprising an active material that comprises between 50% to 95% silicon. In some example embodiments, the battery may comprise a lithium ion battery. In some further example embodiments, the battery comprises an electrolyte comprising a liquid, solid, or gel.
In some example embodiments, the disclosure provides a cathode that may comprise an active material and at least one conductive polymer monomer additive comprising an aniline, a pyrrole, or a thiophene, wherein the thiophene may be selected from 3,4-thiophenedicarboxylic anhydride (TDCA), 3,4-difluoro-2,5-bis(trimethylsilyl)thiophene (DFBTST), or thiophene-2-carboxylic anhydride (TCA); the pyrrole may be selected from 1-(2-cyanoethyl) pyrrole (CEP), 1H-pyrrole-2-carbonitrile, 1-ethenyl-1H-pyrrole, 2-ethenyl-1H-pyrrole, 1-ethynyl-1H-pyrrole, 2-ethynyl-1H-pyrrole, 3-ethynyl-1H-pyrrole, 1-vinyl-1H-pyrrole-2,5-dione, 2-ethenyl-1H-pyrrole, 1-(prop-2-enyl)pyrrole, 1,3,4-tris(prop-2-enyl)pyrrole, 1H-pyrrole-1-carboxylic anhydride, acetic 1H-pyrrole-3-carboxylic anhydride, 1-prop-2-enylpyrrole-2,5-dione, 3-prop-2-enylpyrrole-2,5-dione, or 3,4-bis(prop-2-enyl)pyrrole-2,5-dione; the aniline may be selected from aniline, aniline (hydrochloride), 3-(trifluoromethyl)aniline, 2-nitroaniline, 4-cyano-3-(trifluoromethyl)aniline, aniline-2-sulfonic acid, or 4,4′-methylenedianiline.
As utilized herein, “and/or” means any one or more of the items in the list joined by “and/or”. As an example, “x and/or y” means any element of the three-element set {(x), (y), (x, y)}. In other words, “x and/or y” means “one or both of x and y”. As another example, “x, y, and/or z” means any element of the seven-element set {(x), (y), (z), (x, y), (x, z), (y, z), (x, y, z)}. In other words, “x, y and/or z” means “one or more of x, y and z”. As utilized herein, the term “exemplary” means serving as a non-limiting example, instance, or illustration. As utilized herein, the terms “e.g.,” and “for example” set off lists of one or more non-limiting examples, instances, or illustrations. As utilized herein, a battery, circuitry or a device is “operable” to perform a function whenever the battery, circuitry or device comprises the necessary hardware and code (if any is necessary) or other elements to perform the function, regardless of whether performance of the function is disabled or not enabled (e.g., by a user-configurable setting, factory trim, configuration, etc.).
While the present invention has been described with reference to certain embodiments, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted without departing from the scope of the present invention. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the present invention without departing from its scope. Therefore, it is intended that the present invention not be limited to the particular embodiment disclosed, but that the present invention will include all embodiments falling within the scope of the appended claims.
| Number | Name | Date | Kind |
|---|---|---|---|
| 20150050555 | Fukumine | Feb 2015 | A1 |
| 20170200943 | Kawakami | Jul 2017 | A1 |
| 20200388881 | Ji | Dec 2020 | A1 |
| Number | Date | Country |
|---|---|---|
| 2017041355 | Feb 2017 | JP |
| WO-2018075469 | Apr 2018 | WO |
| Entry |
|---|
| Machine translation of JP 2017-041355A (Year: 2017). |
| Number | Date | Country | |
|---|---|---|---|
| 20210336268 A1 | Oct 2021 | US |