Patent Grant
8777085
The subject method and system for retreading a track wheel is generally directed to reconditioning and/or reworking worn wheels for various vehicles operated on track rails. The subject method and system provide for their restoration, such that the wheels may be re-used rather than discarded. More specifically, the subject method and system are directed to the ‘retreading’ of such a worn track wheel sufficient to reconstitute its original profile.
Railway-type track wheels such as these are used on various types of vehicles, both powered and non-powered. Locomotives, railroad cars, cable cars, mining cars, wagons, coaches, and the like are but a few examples. In most track wheeled vehicles, power is applied by driving some or all of the track wheels, with traction relying on friction between the track wheel—typically formed of steel—and the railway tracks, which are typically also formed of steel or other metallic material.
During the course of repeated use, the wheels of these vehicles and track wheels wear out due to friction, slipping, and constant load against the railway track. Some track wheels tend to wear out more rapidly because they are typically formed of steel having a generally low Rockwell hardness as measured on a Rockwell hardness Scale.
Track wheels are typically formed of metallic material, such as steel. They are formed generally with a tread portion that slightly tapers inward from an outer flange portion. This keeps laterally opposed wheels engaged on the rail tracks they ride on. However, there tends to be slippage between the flange of a given wheel and the track rail it engages, leading to pronounced wear of wheel's flange area. The tread of the wheel also tends to wear from the lateral swaying of the railway vehicle which tends to result, especially when the vehicle travels at higher speeds.
Typically, once the track wheel is worn, as determined by applicable safe operating standards—such as for safe minimum thickness of the flange—the wheel is disposed of. It is not unusual for railroad maintenance vehicles to wear through multiple sets of wheels during a typical year of operation. Invariably, this is at considerable replacement cost.
As shown in
There are various systems known in the art relating to track wheels. For example, U.S. Pat. No. 1,519,029 is directed to a process for renovating worn flanged wheels. This reference first mentions the method of turning down a steel ‘tyre’ in which material is removed from the wheel to sculpt a new surface results in loss of valuable material. This method necessitated the need to match the wheel on the opposing side of the axle with the same amount of material removed.
The reference prescribes filling of material from the worn-down contour line B to the line E, then shaping the surface according to the prescribed contour line D. The approach is to keep quite close to the worn down tread so that the desired shape can be obtained with minimal cutaway of original material. The sectional surface to be obtained is limited on the one hand by B and E and on the other hand by D and comprises only a small fraction of that which would have had to be removed by the prior method. Accordingly, waste of the wheel's costly material turned to scrap is minimized. However, the fill material is limited to the flange area E. Part of the wheel material is necessarily turned down thereafter to obtain the prescribed contour line D.
U.S. Pat. No. 6,746,064 is directed to a composite wheel for tracked vehicles. The reference prescribes a wheel and flange of heat treated steel suitable for a particular end use. A portion of the inside surface of wheel flange, including the area of frictional contact between the wheel flange and rail, is machined away. A welded overlay of low friction material is applied to replace the material removed from an inside surface of flange.
Such known references, however, fail to provide a suitable system or method for resurfacing a worn track wheel to reconstitute its various portions, such as the tread and flange surfaces, to their original profile as disclosed herein.
It is therefore an object of this present invention to provide a wheel resurfacing system and method for resurfacing a worn track wheel to its original profile.
This and other objects are attained by a wheel resurfacing system formed in accordance with the present invention. The system comprises a support for maintaining the worn track wheel, a welding device, a controller, and a surface processing device. The worn railway wheel has a circumferential surface defining a flange and a tread surface. The welding device provides a welding material. The welding device and the worn track wheel rotate one relative to the other at a predetermined rate. The welding device forms a welded layer from the welding material by adaptively aggregating annular beads along a circumferential surface of the wheel, whereby the welded layer forms a curvilinear profile slanted away from the flange. The surface processing device is applied to the welded layer to form a substantially uniform surface to reconstitute the worn railway wheel to its original profile.
In certain exemplary embodiments, a plurality of transverse grooves are formed on the circumferential surface of the worn track wheel before applying the welded layer. The worn track wheel may also be preheated to a predetermined temperature before applying the welded layer.
In another exemplary embodiment, the wheel resurfacing system may be used to fortify a worn railway wheel to its original profile. The system comprises a support for maintaining the worn railway wheel, a welding device, and a surface processing device. The worn railway wheel has a circumferential surface defining a flange surface and a tread surface. The welding device and the worn railway wheel rotate one relative to the other at a predetermined rate. The welding device comprises a welding material having Rockwell hardness greater than the worn railway wheel. The welding device forms a welded layer using the welding material by adaptively aggregating annular beads along the circumferential surface of the wheel. The annular beads are disproportionately aggregated at an intermediate contour between the flange and tread surfaces, forming a curvilinear profile slanted away from the flange. The surface processing device is applied to the welded layer to form a substantially uniform surface to suitably reconstitute the railway wheel to its original profile.
In another exemplary embodiment, a method for resurfacing an uneven wear on a worn railway wheel from an original profile comprises the steps of (1) supporting the worn railway wheel and a welding device, (2) adaptively aggregating annular beads formed from a welding material along a circumferential surface of the worn railway wheel to form a welded layer, and (3) surface processing the welded layer to form a substantially uniform surface to reconstitute the worn railway wheel to its original profile. The worn railway wheel and the welding device rotate one relative to the other at a predetermined rate in this process, and the reconstituted circumferential surface includes flange and tread surfaces.
The disclosed method for resurfacing the worn railway wheel may further comprise the step of preheating the worn railway wheel to a predetermined temperature before the step of adaptively aggregating the annular beads. The metallurgical composition of the worn railway wheel may be determined before the step of adaptively aggregating the annular beads.
Those skilled in the art will appreciate the scope of the present invention and realize aspects thereof after reading the following detailed description of the preferred embodiments in association with the accompanying illustrative figures.
The accompanying illustrative figures incorporated in and forming part of this specification depict several aspects of the invention, and together with the description serve to explain the principles of the invention.
The embodiments set forth below represent the necessary information to enable those skilled in the art to practice the invention and illustrate the best mode of practicing the invention. In light of the illustrated Figures and the following description, those skilled in the art will understand the concepts of the invention and recognize applications of these concepts not particularly addressed herein. It should be understood that these concepts and applications fall within the scope of the disclosure and accompanying Claims.
Wherever possible in the following description, similar reference numerals will refer to corresponding elements on parts of different Drawings unless otherwise indicated.
Referring to
To reconstitute and rebuild the worn-out flange 310, acute taper region 320, and worn tread surface 330, the worn track wheel 300 is preferably sampled to determine the metallogical properties of the wheel. In accordance with a preferred embodiment, the metallurgical properties of the wheel are used to determine a welding rod having compatible properties.
Turning briefly to the flow of processes illustrated in
Preferably, the analysis of the wheel undertaken in Step 1 includes x-ray or any other suitable imaging of the wheel's internal structure. This checks for internal cracks or other faults in the wheel's worn structure (not readily visible on the surface) which may compromise its structural integrity enough to preclude safe re-use, even in resurfaced and reconstituted form. Faulty wheels are thus screened and discarded as necessary.
Depending on the material composition of the wheel, moreover, Step 1 may further include a pre-heating process, whereby the worn track wheel is preheated to a predetermined temperature (such as 500° to 700° F., for example). Such pre-heating serves to prepare the wheel's metallic material for the welding material, making it more receptive to the new material (which has been selected in suitable manner for material compatibility with the wheel). Especially where higher pre-heating temperatures are used, pre-heating treatment of the worn wheel is preferably carried out in situ, with the wheel mounted in position on the given support/table for weld processing.
In Step 2, which may or may not be combined with Step 1 depending on the requirements of a particular application, the wheel is mounted on a support or table (such as support 760 in
In Step 3, the wheel is weld-processed. As described in following paragraphs, a plurality of annular beads of welding material are adaptively aggregated in controlled manner upon a circumferential surface of the worn track wheel as it undergoes turning displacement relative to the welding device. This forms a welded layer having a suitable curvilinear profile tapering away from the wheel flange. Sufficient welding material is applied to form the welded layer that subsequent surface processing suitably removes just the newly-added layer, rather than diminishing any portion of the original/native material of the track wheel.
Preferably in Step 4, the weld-processed wheel is thermally ‘decompressed’ to preserve its reconstituted structure. That is, the very hot, just weld-processed wheel is gradually lowered in temperature back to ambient ranges. A controlled cool-down of the newly-reconstituted wheel reduces the potential for warping, cracking, or other such effects of metal fatigue and the like, due to overly rapid cool down. Various processes may be used to control cool-down, such as progressive, stepped decreases in the wheel's immediate thermal environment over a predetermined time period. Suitable heating measures may be employed, for example, to step the wheel's temperature down in stepped decrements from, say, 750° F.-to-500° F.-to 450° F.-to 350° F.-to 250° F.-and so on down to ambient temperature, with the temperature being maintained at each step for a certain dwell time, such as 20 or 30 minutes, as appropriate for the particular requirements of the intended application.
The controlled thermal environment may be provided in any suitable manner. For example, the entire wheel support/table assembly may be disposed within an oven-type assembly. Alternatively, one or more heating elements may be disposed about the mounted wheel to apply the required levels of controlled heating to progressively lower the wheel's temperature.
In step 5, the weld-processed and sufficiently cooled wheel undergoes surface processing to recover its original, unworn profile. Preferably, this includes the use of such things as a milling or grinding member to grind the welded layer down to the required surface contour. In the disclosed example, a grinding stone is employed to form a substantially uniform, and even polished, surface which restores a like-new original profile for the wheel.
Turning back to
When welding the beads 430, a spin welding or welding position manipulator is preferably used to either set the wheel in a cradle and rotated in controlled manner, so that the welding beads 430 may be put on correctly, or the welding device 410 is controlled to let spin and/or rotated. Alternatively, a combination of movements may be suitably employed for both the worn wheel 400 and the welding device 410.
As mentioned, the welding device 410 is coupled with a welding rod that is electrically energized at the tip 440 to melt into the worn track wheel's 400 metal. While the welding is taking place, the applied flux covering 420′ blankets the weld beads 430 to protect them from oxidation and contamination
In a preferred embodiment, the welding device 410 and the worn track wheel 400 rotate one relative to the other at a predetermined rate. The rate is controlled by an electronic controller that automatically adjusts the voltage, which is directly related to the length of the arc, and the current, which in turn affects heat input. During the welding process, as shown in
As illustrated in
It will normally be difficult to reconstitute the integral taper region 210 in one pass, and multiple passes would be necessary. An alternative approach would be to use a welding rod big enough to fully cover the integral taper region 210 at once; however, it is not economically feasible. Moreover, the resultant heat is likely to be excessive, potentially causing unwanted effects on the wheel. In the disclosed embodiment, as each welding bead 430 is applied with a welding pass, the welding bead 430 substantially hardens before the next pass comes around. The next pass would thus move the welding device's tip 440 sufficiently to extend the area of coverage with the next applied bead 430.
In a preferred embodiment, the worn track wheel 400 is preheated to approximately 500° F. before the welding process. During the welding process, air pockets in the weld are mitigated. As mentioned, air pockets in the weld tend to compromise the strength and integrity of the reconstituted wheel, leading to premature chipping and cracking of the weld.
Depending on the specific requirements and resources of each particular application, the amount of time incurred for each pass would vary accordingly. In certain embodiments, with certain types of wheels, 5-15 passes or bead layers varied according to the depth of the integral taper region 210 may be necessary to build up a suitable original profile.
While the term “bead” is used for convenience, the weld resulting from each pass may not be in precisely beaded form. The weld would be applied preferably with a steady contiguous forming of beads, with the next bead “melting” into the previously applied bead. A self-filling or self-leveling of the built-up weld occurs while preventing crevices as the weld material melts into the wheel.
In a preferred embodiment, such as illustrated in
The grooves 530 may be mechanically or otherwise formed by any suitable means known in the art. The grooves 530 are formed to guard against de-lamination of the weld and to create better adhesion in the restored wheel. The grooves 530 which may be of any shape, contour, or configuration, may be transversely directed or otherwise oriented to have an angular displacement off the central axis of the worn track wheel 500. As mentioned, an x-ray or other suitable process may also be employed to check against cracks or air pockets in the weld which may threaten the integrity of the reconstituted wheel.
Proper care needs to be taken when pre-treating or scoring the surface of the wheel so as not to compromise the structural integrity of the restored wheel. Scoring could be detrimental to the structure or integrity of the worn wheel; however, when appropriate measures are taken, like ensuring suitably limited depth and extent of the grooves 530 and how the grooves are made, the integral taper region 210 and tread surface 520 may be reconstituted with better adhesion of the weld material than might otherwise result. This would contribute to a wheel hardness level possibly even greater than that of the original track wheel 100.
In one preferred embodiment, after sufficient layers of welding beads 630 have been formed on the welded track wheel 600, the welded track wheel 600 is then subjected to a grinding or other surface processing to smooth out its profile. Such a process is depicted in
Depending on the requirements of a particular application, the welded track wheel 600 may be subjected to heat treatment for further hardening In any event, the processed wheel is preferably ‘decompressed’ thermally from its high temperatures. This avoids the deleterious results of metal fatigue and the like, by effecting a gradual cool-down of the wheel as described in preceding paragraphs.
During the welding process, the welded beads harden almost immediately upon formation. Given the desired evenness and continuity of the welded beads, the precision and consistency of a welding machine is preferable. Robotic welders, welding manipulators, CNC machines, or any other suitable equipment known in the art may be employed.
In a preferred embodiment as depicted in
In
Other than the welding device structure 710, 720 shown, the welding device employed may alternatively include a welding tip having hooked electrodes. When touched with a welding rod material, voltage and current controlled by the controller creates the electrical energy that melts the rod. The welding rod is typically fed from a rolled wire-loop batch.
At the time of welding, a separate flux applicator is then used to release flux material onto the annular beads 780. The flux produces a gas that forms a gaseous pocket around the welding point which seals out ambient air that could otherwise introduce impurities into the welded material. Much like the granular flux covering shown in the disclosed embodiment, the flux gas preserves a substantially pure environment immediately about the welding point.
As illustrated in
In one embodiment, the disclosed system is used as a wheel resurfacing system for resurfacing a worn railway wheel 300 substantially to its original profile (integral taper region 210 and tread surface 120). A support 760 may be used for maintaining the worn track wheel 700. The track wheel 700 includes a circumferential surface defining a first surface projecting or worn-out flange 110 from a second surface or tread surface 120. The welding device may include an arc welder.
In another embodiment, the disclosed system is used to also fortify and resurface the worn track wheel 700 to its original profile. A welding material having a Rockwell hardness greater than the worn railway wheel 700 is selected in forming a welded layer by adaptively aggregating annular beads along the circumferential surface made up of worn-out flange 310, acute taper region 320 and worn tread surface 330. For example, a typical rail wheel used in railroad maintenance applications ranges in Rockwell hardness of 28-32 but welding material used may have a Rockwell hardness of greater than 42. The annular beads disproportionately aggregate at an intermediate contour between the worn-out flange 310 and acute taper region 320, whereby the welded layer forms a curvilinear profile slanted away from the worn-out flange 310.
In a preferred embodiment, a controller, which may be microprocessor controlled, is programmed to selectively aggregate the annular beads at specific positions along the circumferential surface of the worn railway wheel 700. In an alternative embodiment, the controller is used to control the relative displacement of the worn railway wheel 700 to the welding device 710 so as to allow multiple passes of the welding device 710 over a previously welded annular bead which results in “stacking” of the annular beads. The controller may selectively control a plurality of parameters to adaptively aggregate the plurality of annular beads including a predetermined rate of relative rotation between the welding unit and support unit, position of the welding unit, current and voltage of the welding device, standoff of the welding device, relative angle of the welding device to the worn wheel, dwell time of the welding device etc.
In another preferred embodiment, the metallurgical composition of the railroad railway wheel 700 may be determined before the step of adaptively aggregating the annular beads 780. A solvent may also be used to clean the wheel before adaptively aggregating the annular beads 780.
Although this invention has been described in connection with specific forms and embodiments thereof, it will be appreciated that various modifications other than those discussed above may be resorted to without departing from the spirit or scope of the invention as defined in the appended claims. For example, functionally equivalent elements may be substituted for those specifically shown and described, certain features may be used independently of other features, and in certain cases, particular locations of elements, steps, or processes may be reversed or interposed, all without departing from the spirit or scope of the invention as defined in the appended claims.
This application is a Divisional patent application of application Ser. No. 13/046,524, filed on 11 Mar. 2011, now U.S. Pat. No. 8,177,115, which was based on provisional application Ser. No. 61/313,470, filed 12 Mar. 2010. The entire disclosure of the prior application, Ser. No. 13,046,524, from which an oath or declaration is supplied, is considered a part of the disclosure of the accompanying Divisional application and is hereby incorporated by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1519029 | Gollwitzer | Dec 1924 | A |
| 2909642 | Landis | Oct 1959 | A |
| 3002081 | Wenzel | Sep 1961 | A |
| 3184839 | Gerlach | May 1965 | A |
| 3207881 | Pagan | Sep 1965 | A |
| 3266702 | Parent et al. | Aug 1966 | A |
| 3526948 | Stern et al. | Sep 1970 | A |
| 4540870 | Kaufmann | Sep 1985 | A |
| 4711146 | Lung et al. | Dec 1987 | A |
| 4918805 | Liszka et al. | Apr 1990 | A |
| 5773779 | Morlock | Jun 1998 | A |
| 5825655 | Nakagawa et al. | Oct 1998 | A |
| 5914055 | Roberts et al. | Jun 1999 | A |
| 5927167 | Naumann et al. | Jul 1999 | A |
| 6128820 | Nolan et al. | Oct 2000 | A |
| 6347550 | Kroening et al. | Feb 2002 | B1 |
| 6494683 | Nolan et al. | Dec 2002 | B1 |
| 6746064 | Petrek et al. | Jun 2004 | B1 |
| 20030029845 | Tamura et al. | Feb 2003 | A1 |
| 20040014405 | Boms et al. | Jan 2004 | A1 |
| 20060042436 | Closmann | Mar 2006 | A1 |
| 20060266122 | Pagano et al. | Nov 2006 | A1 |
| 20060272746 | Kapoor et al. | Dec 2006 | A1 |
| 20070075192 | Mian et al. | Apr 2007 | A1 |
| 20080000947 | Derrien et al. | Jan 2008 | A1 |
| 20080202296 | Heimann | Aug 2008 | A1 |
| 20090078689 | Brass et al. | Mar 2009 | A1 |
| 20090090163 | Mian et al. | Apr 2009 | A1 |
| 20100005935 | Ross | Jan 2010 | A1 |
| 20100064811 | Kroning et al. | Mar 2010 | A1 |
| 20100076631 | Mian | Mar 2010 | A1 |
| 20110101717 | Zdrojewski | May 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| S54-126645 | Oct 1979 | JP |
| 2003-305569 | Oct 2003 | JP |
| 2041785 | Aug 1995 | RU |
| 2095211 | Nov 1997 | RU |
| 2106949 | Mar 1998 | RU |
| 2121420 | Nov 1998 | RU |
| 2143962 | Jan 2000 | RU |
| Entry |
|---|
| Derwent-Acc-No. 1996-050034 Falconer et al. corresponds to ZA-9500959A (1996). |
| Derwent-Acc-No. 2008-F75924 Kang et al. corresponds to KR-759842B1 (2008). |
| Number | Date | Country | |
|---|---|---|---|
| 20130186938 A1 | Jul 2013 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61313470 | Mar 2010 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13046524 | Mar 2011 | US |
| Child | 13459766 | US |