This invention relates generally to the field of carpets, and more particularly to carpets having antimicrobial properties.
Various antimicrobial treatments are currently used in the carpet industry to impart antimicrobial properties to the manufactured carpet. The most popular methods include topical applications and dry cure applications of antimicrobial compounds to the carpet substrate. However, conventional antimicrobial treatment methods used in the industry have damaging effects on carpet performance attributes such flame resistance, soil resistance, and color fastness. For example, many antimicrobial compounds, when applied topically to a carpet substrate following a fluoropolymer treatment and prior to drying in a dryer, will increase the flammability of the carpet.
In one aspect, a method of treating a carpet substrate is provided. The method may include applying a composition comprising a first antimicrobial compound and a fluoropolymer to the carpet substrate.
In another aspect, a method of treating a carpet substrate is provided that comprises applying a first antimicrobial compound and a fluoropolymer to the carpet substrate, and thereafter steaming the carpet substrate.
In another aspect, a treatment composition is provided for imparting durable antimicrobial properties to a carpet. The treatment composition may comprise a fluoropolymer; an antimicrobial compound selected from a group consisting of zinc pyrithione, a silver-containing antimicrobial compound and combinations thereof; and a foamer.
Carpet products treated with the treatment composition or treated in accordance with the methods are also provided.
Methods have been developed to provide a carpet with durable antimicrobial properties using modern continuous application equipment without negating or diminishing other desirable performance characteristics of the carpet. The present method can impart antimicrobial properties to a variety of carpet materials comprising various types of fibers including, but not limited to, nylon, polyester, wool, polypropylene, PTT, silk, cotton, rayon, acetate, and combinations thereof.
It has been discovered that durable antimicrobial properties may be imparted to a carpet in a continuous, single-step treatment with a fluoropolymer without diminishing combined performance attributes. In one embodiment, one or more antimicrobial compounds are applied via foam in an exhaust application step utilizing a foam applicator such as a Küsters Fluicon™ foam applicator (Andritz Küsters GmbH) immediately before feeding the carpet into a steamer. Once the carpet exits the steamer, it typically is washed and extracted prior to entrance into the dryer.
One embodiment of the method is illustrated in
In a preferred embodiment, a treatment composition is applied to the carpet substrate. The treatment composition may be in the form of a foam and may comprise a fluoropolymer, a foamer, magnesium sulfate liquid, zinc pyrithione, and a zirconium phosphate-based ceramic ion-exchange resin containing silver. Various fluoropolymers may be used including, but not limited to, Centapel EFP-7, commercially available from Centaur Technologies (Dalton, Ga.), Unidyne™ TG 580, TG 581, TG 2211 and TG 2511, all of which are commercially available from Daikin America, Inc. (Orangeburg, N.Y.); PM 1396, PM 1399, PM 1400 and PM 1451, all of which are commercially available from 3M Specialty Chemicals Division (St. Paul, Minn.); Capstone™ RCP and Capstone™ TUC, both of which are commercially available from DuPont (Wilmington, Del.). In some embodiments, an aqueous composition of the treatment composition contains 3M PM 1399 which is commercially available from 3M Innovative Products (Minneapolis, Minn.). The fluoropolymer may be provided in an amount of about 0.05 to about 20% owg (on the weight of the goods), or about 0.4% owg. The magnesium sulfate liquid may be provided in an amount of about 0.1 to about 20% owg, or about 2.0% owg.
Various foamers may be used including, but not limited to, Centafoam YEP-10, which is available from Centaur Technologies. The foamer may comprise about 0.1 to about 100 g/l of the treatment composition or about 4.0 g/l of the treatment composition. The treatment may also comprise Centafresh, which is available from Centaur Technologies, in an amount of about 7 g/sq.yd. of carpet substrate. The treatment composition may also comprise various pH adjusting additives such as System 404, which is available from Phoenix Chemical (Calhoun, Ga.). The pH of the treatment composition may be about 2.0 to about 12.0, or about 2.1.
The treatment composition may comprise various antimicrobial compositions including, but not limited to, zinc pyrithione and silver-containing antimicrobial compounds. The zinc pyrithione may comprise about 1 to about 50,000 ppm of the treatment composition or about 500 ppm of the treatment composition. Various silver-containing antimicrobial compounds may be used including Alphasan, which is available from Milliken Chemicals (Spartanburg, S.C.). The silver-containing antimicrobial compound may comprise about 1 to about 50,000 ppm of the treatment composition or about 200 ppm of the treatment composition.
In one embodiment, after the carpet substrate is treated with the fluoropolymer and antimicrobial compound composition, the carpet substrate is immediately steamed in the steamer 14. The carpet substrate is then rinsed and extracted by the washing apparatus 16 and dried in the dryer 18.
It has been observed that treating the carpet substrate with a fluoropolymer and an antimicrobial compound in a single stage results in unexpected synergistic effects and improved performance properties. In particular, the treated carpet demonstrates durable antimicrobial properties, excellent stain repellency and color fastness without diminished flame resistance.
In each of the following examples tufted filament polyester carpet dyed with disperse dyes were from Beaulieu of America (Chatsworth, Ga.) were used for the sample carpet substrates.
The following chemicals were also used in the examples: Zinc Pyrithione, an antimicrobial compound available from Arch Chemicals (Norwalk, Conn.); Alphasan, a silver containing antimicrobial compound available from Milliken Chemicals (Spartanburg, S.C.); Invasan RCD, a sugar-derived freshener available from Huntsman Textile Effects (Switzerland); Centafresh, available from Centaur Technologies; PM 1399, a fluoropolymer available from 3M Innovative Products (Minneapolis, Minn.); Centafoam YEP-10, a foamer available from Centaur Technologies; Centex Binder, a binding agent available from Centaur Technologies; System 404, available from Phoenix Chemical (Calhoun, Ga.); and magnesium sulfate liquid.
A foam was prepared containing 3M PM 1399 at 0.4% owg (on the weight of the goods), magnesium sulfate liquid at 2.0% owg, Centafoam YEP-10 at 4.0 g/l, Centafresh at 7 g/sq. yd. The pH of the foam was adjusted to 2.1 with System 404. The foam solution was applied to a polyester filament carpet at 100% wet pick up. The carpet was then subjected to steam for 60 seconds then rinsed and extracted prior to entrance into the dryer.
A polyester filament carpet was treated in a two step application process. The first step was an exhaust application at 100% wet pick up via foam. The solution used in the first step contained 3M PM 1399 at 0.4% owg (on the weight of the goods), magnesium sulfate liquid at 2.0% owg, Centafoam YEP-10 at 4.0 g/l, Centafresh at 7 g/sq.yd. The pH of the foam was adjusted to 2.1 with System 404. The foam solution was applied to the fiber and then the carpet was subjected to steam for 60 seconds then rinsed and extracted.
After extraction the carpet was treated with the second step. The second step was an 8% wet pick up topical foam application. The solution used in the second step contained Alphasan at 1000 ppm with Centafoam YEP-10 at 4.0 g/l. The solution was applied to the fiber by topical foam and then the carpet was placed into an oven at 140 degrees C. until dry.
A polyester filament carpet was treated in a two step application process. The first step was an exhaust application at 100% wet pick up via foam. The solution used in the first step contained 3M PM 1399 at 0.4% owg (on the weight of the goods), magnesium sulfate liquid at 2.0% owg, Centafoam YEP-10 at 4.0 g/l, Centafresh at 7 g/sq.yd. The pH of the foam was adjusted to 2.1 with System 404. The foam solution was applied to the fiber and subjected to steam for 60 seconds then rinsed and extracted.
After extraction the carpet was treated with the second step. The second step was an 8% wet pick up topical foam application. The solution used in the second step contained Alphasan at 1000 ppm with 0.5% owg Centex Binder and Centafoam YEP-10 at 4.0 g/l. The solution was applied to the fiber by topical foam and then the carpet was placed into an oven at 140 degrees C. until dry.
A polyester filament carpet was treated in a two step application process. The first step was an exhaust application at 100% wet pick up via foam. The solution used in the first step contained 3M PM 1399 at 0.4% owg (on the weight of the goods), magnesium sulfate liquid at 2.0% owg, Centafoam YEP-10 at 4.0 g/l, Centafresh at 7 g/sq.yd. The pH of the foam was adjusted to 2.1 with System 404. The foam solution was applied to the fiber and then the carpet was subjected to steam for 60 seconds then rinsed and extracted.
After extraction the carpet was treated with the second step. The second step was an 8% wet pick up topical foam application. The solution used in the second step contained Zinc Pyrithione at 500 ppm and Centafoam YEP-10 at 4.0 g/l. The solution was applied to the fiber by topical foam and the carpet was then placed into an oven at 140 degrees C. until dry.
A polyester filament carpet was treated in a two step application process. The first step was an exhaust application at 100% wet pick up via foam. The solution used in the first step contained 3M PM 1399 at 0.4% owg (on the weight of the goods), magnesium sulfate liquid at 2.0% owg, Centafoam YEP-10 at 4.0 g/l, Centafresh at 7 g/sq.yd. The pH of the foam was adjusted to 2.1 with System 404. The foam solution was applied to the fiber and the carpet was subjected to steam for 60 seconds then rinsed and extracted.
After extraction the carpet was treated with the second step. The second step was an 8% wet pick up topical foam application. The solution used in the second step contained Zinc Pyrithione at 500 ppm with 0.5% owg Centex Binder and Centafoam YEP-10 at 4.0 g/l. The solution was applied to the fiber by topical foam and the carpet was then placed into an oven at 140 degrees C. until dry.
A polyester filament carpet was treated in a two step application process. The first step was an exhaust application at 100% wet pick up via foam. The solution used in the first step contained 3M PM 1399 at 0.4% owg (on the weight of the goods), magnesium sulfate liquid at 2.0% owg, Centafoam YEP-10 at 4.0 g/l, Centafresh at 7 g/sq.yd. The pH of the foam was adjusted to 2.1 with System 404. The foam solution was applied to the fiber and the carpet was subjected to steam for 60 seconds then rinsed and extracted.
After extraction the carpet was treated with the second step. The second step was an 8% wet pick up topical foam application. The solution used in the second step contained Invasan at 500 ppm and Centafoam YEP-10 at 4.0 g/l. The solution was applied to the fiber by topical foam and the carpet was then placed into an oven at 140 degrees C. until dry.
A polyester filament carpet was treated in a two step application process. The first step was an exhaust application at 100% wet pick up via foam. The solution used in the first step contained 3M PM 1399 at 0.4% owg (on the weight of the goods), magnesium sulfate liquid at 2.0% owg, Centafoam YEP-10 at 4.0 g/l, Centafresh at 7 g/sq.yd. The pH of the foam was adjusted to 2.1 with System 404. The foam solution was applied to the fiber and the carpet was subjected to steam for 60 seconds then rinsed and extracted.
After extraction the carpet was treated with the second step. The second step was an 8% wet pick up topical foam application. The solution used in the second step contained Invasan at 500 ppm with 0.5% owg Centex Binder and Centafoam YEP-10 at 4.0 g/l. The solution was applied to the fiber by topical foam and the carpet was then placed into an oven at 140 degrees C. until dry.
A polyester filament carpet was treated in a two step application process. The first step was an exhaust application at 100% wet pick up via foam. The solution used in the first step contained 3M PM 1399 at 0.4% owg (on the weight of the goods), magnesium sulfate liquid at 2.0% owg, Centafoam YEP-10 at 4.0 g/l, Centafresh at 7 g/sq.yd. The pH of the foam was adjusted to 2.1 with System 404. The foam solution was applied to the fiber and the carpet was subjected to steam for 60 seconds then rinsed and extracted.
After extraction the carpet was treated with the second step. The second step was an 8% wet pick up topical foam application. The solution used in the second step contained Alphasan at 200 ppm, Zinc Pyrithione at 500 ppm and Centafoam YEP-10 at 4.0 g/l. The solution was applied to the fiber by topical foam and the carpet was then placed into an oven at 140 degrees C. until dry.
A polyester filament carpet was treated in a two step application process. The first step was an exhaust application at 100% wet pick up via foam. The solution used in the first step contained 3M PM 1399 at 0.4% owg (on the weight of the goods), magnesium sulfate liquid at 2.0% owg, Centafoam YEP-10 at 4.0 g/l, Centafresh at 7 g/sq.yd. The pH of the foam was adjusted to 2.1 with System 404. The foam solution was applied to the fiber and the carpet was subjected to steam for 60 seconds then rinsed and extracted.
After extraction the carpet was treated with the second step. The second step was an 8% wet pick up topical foam application. The solution used in the second step contained Alphasan at 200 ppm, Zinc Pyrithione at 500 ppm with 0.5% owg Centex Binder and Centafoam YEP-10 at 4.0 g/l. The solution was applied to the fiber by topical foam and the carpet was then placed into an oven at 140 degrees C. until dry.
A foam was prepared containing 3M PM 1399 at 0.4% owg (on the weight of the goods), magnesium sulfate liquid at 2.0% owg, Centafoam YEP-10 at 4.0 g/l, Centafresh at 7 g/sq.yd., Alphasan at 200 ppm, Zinc Pyrithione at 500 ppm. The pH of the foam was adjusted to 2.1 with System 404. The foam solution was applied to the carpet and the carpet was subjected to steam for 60 seconds then rinsed and extracted prior to being placed into the dryer.
A foam was prepared containing 3M PM 1399 at 0.4% owg (on the weight of the goods), magnesium sulfate liquid at 2.0% owg, Centafoam YEP-10 at 4.0 g/l, Centafresh at 7 g/sq.yd., Invasan at 1,000 ppm. The pH of the foam was adjusted to 2.1 with System 404. The foam solution was not applied to the carpet due to coagulation and precipitation.
A polyester filament carpet sample was maintained non-treated for use as a control.
All test samples of EXAMPLES 1-12 were subjected to American Association of Textile Chemists and Colorists (AATCC) test method 138, undergoing 10 cycles wash/extractions. The samples were further subjected to AATCC test method 123, a pill test for flammability, a repellency test, and a 40 hour light fastness test.
As demonstrated in TABLE ONE, a synergistic effect exists with co-exhaustion of Zinc Pyrithione, Alphasan, Centafresh, PM 1399, and Centafoam YEP-10. Superior results were achieved with this unexpected discovery. Excellent antibacterial/antifungal results, repellency, and light fastness were achieved without causing flammability failures.
Many variations exist for the conditions previously outlined in the examples. Those skilled in the art recognize the many variations for equipment and conditions involving exhaust and topical application of chemical treatments. Previously outlined descriptions are supplied as examples and are not meant to be exclusive.
This application is a divisional of U.S. patent application Ser. No. 12/683,914, filed on Jan. 7, 2010, and claims the benefit of U.S. Provisional Patent Application No. 61/143,108, filed on Jan. 7, 2009. These applications are incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61143108 | Jan 2009 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12683914 | Jan 2010 | US |
| Child | 14062488 | US |