1. Technical Field
The technology relates to methods and structures for making vertical-cavity light-emitting devices.
2. Discussion of the Related Art
Early types of semiconductor laser diodes that are still in use today, known as edge-emitting laser diodes, are designed to emit radiation from an edge of a laser diode chip. In these devices, the direction or beam axis of the laser cavity and the direction of the emitted lasing beam are parallel to a “process” plane of the semiconductor substrate on which the edge-emitting lasers are formed. Typically, after the laser diodes are formed, the substrate is diced or cleaved to form a laser diode chip, the chip is packaged, a current is applied across the laser diode's junction, and laser radiation is emitted from an edge of the chip.
A vertical cavity surface emitting laser (VCSEL) is a type of semiconductor laser that was conceptualized and developed in the 1980s and '90s. VCSELs are characterized by the formation of a vertical laser cavity that is oriented perpendicular to the process plane of the substrate on which the laser is formed. The laser cavity may be defined by two parallel optical reflectors sandwiching an active region of the laser diode. VCSELs may also be diced from a substrate and packaged. Lasing radiation for a VCSEL is emitted in a direction that is out of the process plane of the chip, and is perpendicular to the direction of emission for an edge-emitting laser diode.
Compared with conventional edge-emitting laser diodes, a VCSEL may have advantages of (1) on-wafer testing of device performance, (2) better beam profile and far-field patterns, (3) better mode stability and wider free spectral range due to a shorter cavity length, (4) possibility of a very low threshold current, (5) a generally higher manufacturing yield, (6) a higher packing density on a substrate and therefore lower cost, and (7) improved compatibility with planar microfabrication techniques. VCSELs in the infrared and red spectral range are currently being used for telecommunication and industrial applications.
Methods and structures associated with fabricating vertical light-emitting devices such as VCSELs are described. The methods may be used to fabricate VCSELs from III-nitride materials such as gallium nitride (GaN). Conductivity-based electrochemical (EC) etching may be used during fabrication to form a semiconductor/air distributed Bragg reflector and a current-guiding structure on the bottom side of a vertical light-emitting device. The current-guiding structure may enhance a spatial overlap between an active region of the device (where carrier recombination takes place) and a resonant cavity of the device. The current-guiding structure may be formed from a portion of a semiconductor layer that is first converted to porous semiconductor, and then converted to a porous oxide.
According to some embodiments, a semiconductor light-emitting device comprises a substrate, an active region comprising semiconductor material, wherein the active region has a first area, a doped semiconductor region located between the active region and the substrate having a second area smaller than the first area, and a porous oxide extending around the doped semiconductor region and located between the active region and the substrate. At least a portion of the active region may be configured for carrier recombination and photon generation.
According to some aspects, the active region and doped semiconductor region comprise III-nitride material. In some implementations, the porous oxide may comprise gallium oxide, aluminum-gallium oxide, or indium-gallium oxide. In some aspects, the porous oxide may be formed in and from a same layer of material as the doped semiconductor region. In some implementations, the doped semiconductor region comprises n-type conductivity material. In some aspects, the active region may be configured to produce photons when electrical current flows through the active region. According to some implementations, the active region comprises multiple quantum wells formed from layers of III-nitride material.
In some aspects, a semiconductor light-emitting device may further comprise a contact layer of semiconductor material formed between the doped semiconductor region and the substrate, wherein a doping density of the contact layer is less than a doping density of the doped semiconductor region. In some implementations, a doping density of the contact layer is between approximately 5×1017 cm−3 and approximately 2×1018 cm−3 and a doping density of the doped semiconductor region is between approximately 3×1018 cm−3 and approximately 1×1019 cm−3.
In some implementations, a semiconductor light-emitting device may further comprise a first distributed Bragg reflector located between the doped semiconductor region and the substrate. The first distributed Bragg reflector may comprise alternating layers of air and III-nitride material. In some aspects, a semiconductor light-emitting device may further include at least one undoped semiconductor layer between the doped semiconductor region and the first distributed Bragg reflector. In some cases, a semiconductor light-emitting device may further comprise a conductive layer having a doping density between approximately 5×1017 cm−3 and approximately 2×1018 cm−3 located between the doped semiconductor region and the first distributed Bragg reflector, and an undoped semiconductor layer between the conductive layer and the first distributed Bragg reflector, wherein a doping density of the doped semiconductor region is between approximately 3×1018 cm−3 and approximately 1×1019 cm−3.
According to some implementations, a semiconductor light-emitting device may further comprise a second distributed Bragg reflector located on a side of the active region away from the substrate. In some aspects, the second distributed Bragg reflector may comprise layers of dielectric material.
The foregoing aspects, implementations, and features may be included in any suitable combination in an embodiment of a semiconductor light-emitting device, and may be included in any suitable combination in one or more of the following method embodiments for making an integrated light-emitting device.
According to some embodiments, a method for making an integrated light-emitting device may comprise acts of forming a mesa on a substrate that comprises an active region of semiconductor material and a doped semiconductor layer located between the active region and substrate, etching a portion of the doped semiconductor layer to form a porous semiconductor region extending around a remaining doped and unetched semiconductor region, wherein the porous semiconductor region and doped semiconductor region are located between the active region and the substrate, and converting the porous semiconductor region to a porous oxide.
In some aspects, forming the doped semiconductor layer may comprise epitaxially growing an n-type conductivity layer of III-nitride material. A method may further include forming a contact layer of semiconductor material adjacent the doped semiconductor layer, wherein a doping density of the contact layer is less than a doping density of the doped semiconductor layer. In some implementations, a method may further include forming the doped semiconductor layer and contact layer from III-nitride material, doping the contact layer with a doping density between approximately 5×1017 cm−3 and approximately 2×1018 cm−3, and doping the doped semiconductor layer with a doping density between approximately 3×1018 cm−3 and approximately 1×1019 cm−3.
According to some implementations, the etching comprises electrochemical etching with a hydrofluoric-based etchant. The etching may further comprise applying a bias between approximately 7 volts and approximately 20 volts between the semiconductor layer and an electrode in the etchant. In some aspects, converting the porous semiconductor region comprises oxidizing the porous semiconductor to form gallium oxide.
In some implementations, a method for making an integrated light-emitting device may further comprise forming a first distributed Bragg reflector located between the doped semiconductor region and the substrate. The act of forming the first distributed Bragg reflector may comprise epitaxially growing one or more layers of n-type III-nitride semiconductor material and on or more layers of undoped III-nitride semiconductor material, etching a hole adjacent the mesa to expose sidewalls of the layers of n-type III-nitride semiconductor material, and electrochemically etching at least a portion of the layer or layers of n-type III-nitride semiconductor material to form at least one air gap between the mesa and the substrate.
In some implementations, the layer or layers of n-type III-nitride semiconductor material comprise GaN and have a doping density between approximately 8×1018 cm−3 and approximately 5×1019 cm−3. The etching a portion of the doped semiconductor layer and electrochemically etching at least a portion of the layer or layers of n-type III-nitride semiconductor material may be performed in a same etching step. A method for making an integrated light-emitting device may further comprise forming at least one undoped semiconductor layer between the doped semiconductor region and the first distributed Bragg reflector.
In some implementations, a method may further comprise forming a second distributed Bragg reflector located on a side of the active region away from the substrate. Forming the second distributed Bragg reflector may comprise depositing layers of dielectric material.
The foregoing and other aspects, embodiments, and features of the present teachings can be more fully understood from the following description in conjunction with the accompanying drawings.
The skilled artisan will understand that the figures, described herein, are for illustration purposes only. It is to be understood that in some instances various aspects of the embodiments may be shown exaggerated or enlarged to facilitate an understanding of the embodiments. The drawings are not necessarily to scale, emphasis instead being placed upon illustrating the principles of the teachings. In the drawings, like reference characters generally refer to like features, functionally similar and/or structurally similar elements throughout the various figures. Where the drawings relate to microfabrication of integrated devices, only one device may be shown to simplify the drawings. In practice, a large plurality of devices may be fabricated in parallel. The drawings are not intended to limit the scope of the present teachings in any way.
When referring to the drawings in the following detailed description, spatial references “top,” “bottom,” “upper,” “lower,” “vertical,” “horizontal,” and the like may be used. For example, “vertical” may be used to refer to a direction normal to the substrate surface, and “horizontal” may be used to refer to a direction parallel to the substrate surface when referring to the drawings. “Upper,” “top,” or “above” may be used to refer to a vertical direction away from the substrate, whereas “lower,” “bottom,” or “below” may be used to refer to a vertical direction toward the substrate. Such references are used for teaching purposes, and are not intended as absolute references for embodied devices. An embodied device may be oriented spatially in any suitable manner that may be different from the orientations shown in the drawings.
The features and advantages of the embodiments will become more apparent from the detailed description set forth below when taken in conjunction with the drawings.
Among the various types of vertical-cavity light-emitting devices possible with the processes described herein, a GaN VCSEL is expected to be an important new device configuration for high-end lighting applications such as automobile headlight, micro-projector, and low-droop, high-power lamps. A GaN VCSEL can access the purple/blue spectral range (400-450 nm), which is useful for high-brightness white-light sources. Currently, difficulties associated with fabricating vertical cavities in III-nitride systems have impeded the commercial realization of GaN VCSELs.
A vertical-cavity light-emitting device that is formed as a VCSEL may include bottom-side and top-side reflectors. The principle of light amplification in a VCSEL is not very different from that in conventional laser diodes. Applying electrical bias across the laser diode's p- and n-type layers and active region causes the injection of electrons and holes from the n-type 120 and p-type 140 layers, respectively, into the active region 130. The electrons and holes recombine radiatively to create photons, or electromagnetic radiation. Under a sufficiently high level of current injection, the active region 130 can reach population inversion and photon amplification by stimulated emission can occur. If the cavity reflectors have a sufficiently high reflectance, round-trip gain in the laser cavity may equal round-trip loss so that continuous-wave lasing operation is sustained producing an output laser beam 160.
In some implementations, a laser cavity for a VCSEL may be formed as a microcavity. A microcavity may have a length L that has a value similar to or within a factor of 5 of the lasing wavelength for the VCSEL. A length of a microcavity may be an integral number of half-wavelengths, according to some embodiments, where the length accounts for refractive indices of materials within the microcavity. For example, the cavity reflectors are effectively located at nodes of a standing optical wave that is amplified within the laser cavity. In some embodiments, a microcavity VCSEL may have a distance L between its cavity reflectors between approximately 80 nanometers and approximately 2 microns. The behavior of electromagnetic waves inside a microcavity may be defined by allowable longitudinal optical modes of the microcavity. For example, photons in certain allowed modes will be amplified through stimulated emission, leading to highly efficient generation of coherent photons.
The inventors have recognized and appreciated that successful fabrication of vertical-cavity light-emitting devices may include (1) forming an efficient active region for carrier-photon conversion, (2) forming integrated, high-quality reflectors on opposing sides of the active region, and (3) controlling spatial flow of current through the active region such that photon production by carrier recombination overlaps well with modes of a resonant cavity formed by the high-quality reflectors. The inventors have observed that since 1999, there have been few demonstrations of VCSEL operation in III-nitride materials, and believe this is primarily due to fabrication challenges posed by the integrated reflectors (item 2), and more particularly the bottom-side reflector. Although their have been limited demonstrations of III-nitride VCSELs, these devices are not yet commercially available.
Two teams (Tokyo University and Sandia Labs/Brown University) demonstrated the use of epitaxial AlGaN/GaN distributed Bragg reflectors (DBR) as the bottom-side reflectors with dielectric oxide stacks as the top-side reflectors. This hybrid configuration led to the first demonstration of an electrically-injected VCSEL in 2008. However, the inventors recognize that preparation of the bottom DBRs by epitaxy is very difficult. A large number (40 to 60) of AlGaN/GaN pairs are required to achieve a high reflectivity (R˜99%) due to the very low contrast of index of refraction between AlGaN and GaN layers. Also, the control of strain induced by epitaxial growth of the different layers is another significant challenge for that reflector structure. Further, the AlGaN/GaN multi-layer reflector has a very narrow bandwidth (˜15 nm), which makes it difficult to fabricate the structure to match allowed lasing wavelengths for the VCSEL.
In another approach, Nichia Chemical used a laser liftoff (LLO) technique to separate an InGaN/GaN p-n epitaxial structure from a sapphire substrate, and to expose the bottom side (n-side) for the deposition of a dielectric mirror. Although this approach can avoid the complexity of a multi-layer epitaxial DBR reflector, the use of LLO adds other processing complexity, and it essentially voids the advantage of on-wafer testing. Further, LLO typically requires a relatively thick active region for the laser, which increases the cavity length and reduces the mode spacing for a laser. This can degrade the longitudinal mode quality of a VCSEL.
In both of these approaches for fabricating VCSELs, a dielectric current-blocking layer was employed on the p-side or top-side of the device. The inventors have recognized and appreciated that current diffusion on the n-side or bottom-side could undermine device performance, and that implementing current blocking on the bottom-side poses fabrication challenges. For example, addition of an oxide blocking layer can disrupt epitaxial growth.
The inventors have conceived of methods and structures for fabricating vertical-cavity light-emitting devices that include bottom-side, wide-band, high-reflectance mirrors and bottom-side current-guiding structures that can prevent unwanted current spreading at the active region. In some embodiments, the methods and structures may be used for manufacturing III-nitride VCSEL devices with reduced complexity and allow for on-wafer testing. According to some embodiments, a bottom-side or n-side reflector may be formed through lateral electrochemical (EC) etching as a GaN/air multilayer DBR. Because of the refractive index contrast for the semiconductor/air DBR, the bottom-side reflector exhibits a wider bandwidth (˜150 nm) with only four layer pairs than conventional AlGaN/GaN DBR structures having 40 to 60 layer pairs. Additionally, a bottom-side current-guiding and blocking layer may be formed by lateral porosification of highly-doped GaN to a selected distance using EC etching, followed by a controlled oxidation to convert the nanoporous GaN to an insulating nanoporous gallium oxide.
The processes described below may be used with various types of III-nitride materials (e.g., GaN and GaN alloys such as InGaN, AlGaN, InGaAlN, etc.) When other III-nitride materials are used, the conversion of nanoporous material may result in onther oxides, e.g., indium-gallium oxide, aluminum-gallium oxide, indium-gallium-aluminum oxide, etc. In other implementations, the processes may be extended to other semiconductor systems (e.g., Si, SiC, InP, GaAs, and their respective alloys) for which EC etching conditions are known.
According to some embodiments, a vertical-oriented light-emitting device may be fabricated using a multilayer structure 201 comprising a substrate 105, as depicted in
According to some embodiments, a base layer 210 may be epitaxially grown from the substrate 105 or from a buffer layer (e.g., AlN, SiC, Al2O3) deposited on a substrate. In some embodiments, the base layer may be bonded to the substrate 105. The base layer may comprise a III-nitride material that is undoped, according to some embodiment. For example, the base layer 210 may comprise undoped or unintentionally-doped gallium nitride (u-GaN). A doping density of the base layer may be less than 1017 cm−3.
In some implementations, the base layer 210 may be between approximately 100 nm and approximately 2 microns thick. The base layer may be grown to a thickness for which a density of defects (resulting from epitaxial growth of a lattice-mismatched semiconductor) reduces to levels acceptable for integrated-circuit devices. For example, a density of defects at a top surface of the base layer 210 may be less than about 109 defects cm−2 in some embodiments, less than about 106 defects cm−2 in some embodiments, less than about 104 defects cm−2 in some embodiments, less than about 102 defects cm−2 in some embodiments, and yet less than about 10 defects cm−2 in some embodiments.
Reflector layers 215 may be formed (e.g., by epitaxial growth) over the base layer 210. The reflector layers may be formed using any suitable chemical vapor deposition (CVD) process (such as metalorganic chemical vapor deposition) or an atomic layer deposition (ALD) process. The reflector layers may comprise one or more layer pairs of alternating conductivity. In some embodiments, a layer pair may comprise a first layer 222 of heavily doped (n++ doping) n-type III-nitride material and a second layer 212 of undoped or unintentionally-doped III-nitride material. A doping density of the heavily doped layers may be between approximately 8×1018 cm−3 and approximately 5×1019 cm−3, according to some embodiments. There may be between 1 and 10 reflector layer pairs for the bottom-side reflector. In some implementations, there may be four or five reflector layer pairs.
Thicknesses of the reflector layers 215 may be such that a respective layer corresponds to an odd number of quarter wavelengths (e.g., λ/4, 3λ/4, 5λ/4, etc.) for a peak emission wavelength λ (measured in air) that will be emitted by the finished light-emitting device. In some embodiments, the undoped layers 212 remain in a finished device, so that the refractive index of the layer should be taken into account when determining a thickness for the layers. For example, a layer thickness 3λ/4 may be reduced by the refractive index value n212 for determining the thicknesses of the undoped layers 212. Portions of the heavily doped layers 222 may be removed in a finished device (at least adjacent an active area of the light-emitting device), so that the layer thickness may be an odd number of quarter wavelengths as measured in air.
In some implementations, an undoped highly resistive layer 214 (e.g., a layer having a resistivity greater than approximately 103 ohm-cm) may be formed over the reflector layers, e.g., by epitaxial growth. The resistive layer may comprise a III-nitride material. In some implementations, the resistive layer 214 electrically isolates the reflector layers and lower substrate from the device. The resistive layer 214 may also provide a crystal template for subsequent growth of the device layers. In some embodiments, the undoped layer 214 may provide a spacing function. For example, the undoped layer 214 may be used to adjust an optical distance between the two cavity reflectors of a microcavity laser, so that the two reflectors are effectively located at nodes of a standing optical wave within the laser cavity.
Device layers 224, 226, 230, 240, may all be formed over the resistive layer 214. Some device layers may be formed by epitaxial growth (e.g., using any suitable chemical vapor deposition (CVD) process or atomic layer deposition (ALD) process), during which dopants may be added to dope the layers to a selected doping density. According to some embodiments, a lightly doped (n− doping) n-side conductive layer 224 comprising III-nitride material may be formed adjacent the resistive layer 214. A dopant density for the conductive layer may be between approximately 5×1017 cm−3 and approximately 2×1018 cm−3. The conductive layer 224 may have n-type conductivity and be used in a finished device for external electrical connection, for example, through a contact pad, wire 175, or conductive interconnect formed to contact the conductive layer. A thickness of the conductive layer may be between approximately 50 nm and approximately 500 nm, according to some embodiments, though smaller or greater thicknesses may be used in some embodiments.
A highly doped (n+ doping) current-guiding layer 226 comprising III-nitride material may be formed adjacent the conductive layer 224. According to some embodiments, a dopant density for the current-guiding layer may be between approximately 3×1018 cm−3 and approximately 1×1019 cm−3. The conductivity of the current-guiding layer 226 may be n-type. A resistivity of the current-guiding layer may be between approximately 5×10−4 ohm-cm and approximately 0.01 ohm-cm, in some embodiments. A thickness of the current-guiding layer may be between approximately 50 nm and approximately 500 nm, according to some embodiments, though smaller or greater thicknesses may be used in some embodiments. In some implementations, the current-guiding layer may be between approximately 100 nm and approximately 250 nm thick.
An active layer 230 may then be formed adjacent the current-guiding layer 226. The active layer may be configured to generate photons through carrier recombination. In some embodiments, the active layer may comprise a p-n or p-i-n junction for a light-emitting diode. In some implementations, the active layer 230 comprises multiple thin layers of alternating heterogeneous III-nitride materials that form a multiple quantum well (MQW) structure. For example, an MQW structure may comprise alternating layers of InGaN and GaN, according to some embodiments. In some aspects, an MQW structure may comprise AlInGaN and GaN layers. There may be between two and twenty such layer pairs in an MQW structure. A thickness of the active layer 230 may be between approximately 50 nm and approximately 200 nm, according to some embodiments, though smaller or greater thicknesses may be used in some cases.
In some implementations, a p-side conductive layer 240 is formed adjacent the active layer. The p-side conductive layer may be formed from a III-nitride material (e.g., p-GaN:Mg), and have a doping density between approximately 1015 cm−3 and approximately 1019 cm−3. A thickness of the p-side conductive layer 240 may be between approximately 50 nm and approximately 500 nm, according to some embodiments, though smaller or greater thicknesses may be used in some embodiments.
In some implementations, the resistive layer 214, conductive layer 224, current-guiding layer 226 and p-side conductive layer 240 all comprise device-quality GaN semiconductor material. In other implementations, other materials may be used. In some implementations, combinations of III-nitride materials may be used in a device. For example, some layers may comprise GaN whereas other layers may comprise AlGaN and/or InGaN.
Referring to
A transparent conductor 260 may be deposited over the layers as depicted in
According to some embodiments, a resist 270 may be patterned over the transparent conductor, and a sequence of etching steps may be executed to form a mesa structure 205, as depicted in
Lateral electrochemical (EC) etching may then be used to convert at least a portion of the highly-doped layer 226 to a porous semiconductor material 228, as depicted in
The lateral EC etching may be timed so that the nanoporous region extends partway into the mesa 205, but leaves a central region 227 of the highly-doped semiconductor layer 226 unetched, so that electrical current may flow through the central region. According to some embodiments, the EC etching and porosification extends between approximately 5 microns and approximately 15 microns from and edge of the mesa 205 into a the current-guiding layer. The remaining unetched region may have a lateral dimension or diameter between approximately 1 micron and approximately 50 microns, according to some embodiments. Smaller or larger diameters may be implemented in other embodiments. In some embodiments, the electrochemical etching may use a hydrofluoric-based etchant, though other etchants (e.g., oxalic acid, sulfuric acid, phosphoric acid, hydrochloric acid, potassium hydroxide, sodium hydroxide, nitric acid, or sodium chloride) may be used in other embodiments. In some implementations, the acid or base solutions may be non-aqueous.
The phrase “electrochemical etching” or “EC etching” is used consistently with its recognized meaning in the field of microfabrication to refer to a process in which a material is etched in an etchant bath while applying a bias voltage between the etchant (also referred to as electrolyte) and the material to be etched. Electrochemical etching differs from photoelectrochemical (PEC) etching in that PEC etching requires illumination of the material for etching to occur, whereas EC etching does not require illumination of the material for etching to occur. Accordingly, EC etching is recognized in the field of microfabrication as a different process from PEC etching. An advantage of EC etching is that it is not susceptible to etch-rate variations that can arise from non-uniform illumination of a material. An additional advantage of EC etching is that etching can occur in buried regions or regions that may not be illuminated by external light.
During EC etching of the highly-doped current-guiding layer 226, a bias voltage may be applied between the etchant and the mesa and may have a value between approximately 5 volts and approximately 60 volts, in some embodiments. In some cases, a bias voltage may be between 1 volt and approximately 60 volts. The inventors have found that the applied bias voltage may depend upon the etchant used and the doping density of the layer to be etched. Depending upon the etching parameters (doping density, etchant, temperature, and bias voltage) a III-nitride material may be either (1) not etched or etched slowly, (2) porosified, or (3) completely removed. Therefore careful control of the etching conditions is maintained to porosify a portion of the current-guiding layer 226.
The light-emitting structure may subsequently be exposed to an oxidation process that converts the nanoporous region 228 into a porous oxide region 229, as depicted in
According to some embodiments, contact pads or contact features may be formed on p-side and n-side conducting layers of the light-emitting structure, as depicted in
Contact pads to the n-side and p-side layers may be formed by any suitable lithographic process. One method for forming contact pads is to use a lift-off process. This may entail depositing a photoresist over the light-emitting structure, patterning the photoresist using photolithography to open up regions where the contacts will be formed, performing a metal deposition, and then dissolving any remaining photoresist and overlying metal to lift off excess metal and leave the contacts on the n-side and p-side layers of the device. According to some embodiments, contacts may be formed from a metal that may be deposited during a metallization level.
Referring to
A p-side reflector may be formed using a lift-off process, according to some embodiments. For example, a resist may be patterned over the light-emitting structure, and one or multiple depositions of layers for the reflector 280 may be carried out. Subsequently, the resist may be dissolved to remove reflector material from everywhere except for a top region of the mesa 205.
According to some embodiments, a resist 290 may be deposited over the light-emitting structure and a hole 292 may be patterned in the resist adjacent the mesa 205, as depicted in
In some embodiments, a via may be formed using a laser drilling process and without the use of a resist 290. For example, a laser beam may be focused on the substrate and the intensity varied in time to optically drill into the semiconductor layers.
After formation of the via 294, a lateral EC etching step may then be carried out to remove portions of the highly doped layers 222, as depicted in
The bottom-side DBR and top-side reflector 280 may form a vertical, optical resonant cavity for the light-emitting device. The length of the resonant cavity may be between approximately 150 nm and approximately 5 microns, according to some embodiments. In some embodiments, the resonant cavity comprises an optical microcavity that has a length on the order of up to a few wavelengths of radiation produced in the device's active region. In some implementations, electrical current is confined and flows centrally through the resonant cavity due to the oxide 250 and porous current-guiding region 229.
Although
Although the foregoing description of a light-emitting device includes an n-region of the device on the bottom-side and a p-region of the device on the top-side, other implementations may have the n-region and p-region inverted compared to what is shown in the drawings. In such embodiments, a bottom-side reflector may be associated with a p-side of the device, and a top-side reflector 280 may be associated with an n-side of the device.
An alternative embodiment of a light-emitting device is depicted in
As described above, two lateral EC etching steps are used to form a bottom-side, porous, current-guiding region 229 and a bottom-side air/semiconductor DBR. In some implementations, these steps are carried out separately. In some embodiments, the steps may be carried out at a same time. For example, the doping density of the heavily doped layers 222 and current-guiding layer 226 may be selected such that complete removal of the heavily doped layers and porosification of the current-guiding layer occurs in a same etchant under a same bias. Additionally, dopant densities in the two layers and device dimensions may be tailored such that the desired etching distances are achieved for lateral porosification and material removal during a same etching time. For example, a dopant density in the heavily-doped layer may be selected to give a higher etching rate than the etching rate in the current guiding layer 226. Some examples of etchants, doping density ranges, bias voltages, and etching characteristics for GaN are listed in Table 1.
Example process steps were carried out for fabricating a vertical light-emitting device. In one process, a layer of n-doped GaN (approximately 5 microns thick) was laterally EC etched from the edge of a mesa to create a porous region between two III-nitride layers. The electrochemical etchant was 1:1 HF:H2O, and EC etching was carried out at room temperature and bias voltages ranging between 7 V and 20 V. The rate of lateral porosification varied from about 1 micron/minute to about 10 microns/min, depending on the bias voltage used.
A result of the etching is shown in
Oxidation of NP GaN was carried out, and the resulting oxidized structure was compared the microstructure before oxidation. A portion of the nanoporous structure before oxidation is shown in
An n-side or bottom side DBR was formed from four layer pairs of alternating heavily-doped and undoped GaN layers. The heavily doped layers were completely removed by lateral EC etching to produce four air/GaN layer pairs for the DBR structure. The formation of air-gaps was confirmed by scanning electron microscopy. Micro-reflectance measurements (curve 520) were made and the results are plotted against simulated results 510 for the DBR structure, as shown in
Methods and structures described above for fabricating III-nitride vertical light-emitting devices may have certain advantages over conventional methods for fabricating VCSELs, for example. In some implementations, the fabrication of GaN/air-gap DBRs (with only a few layer pairs needed) may be an easier manufacturing process than the epitaxial growth of tens of layer pairs for AlGaN/GaN DBRs. The techniques for forming bottom-side reflectors can avoid wafer or laser lift-off (LLO) processes and may be compatible with conventional and mature LED processing. In some embodiments, the use of GaN/air-gap DBRs enables true microcavity fabrication with a cavity length on the order of the lasing wavelength, which may not be possible with epitaxial of DBR structures having tens of semiconductor/semiconductor layers or with laser lift-off structures. Further, the use of porosification and oxidation processes can enable the creation of a current-guiding layer on the n-side of a vertical light-emitting device, which can improve device efficiency and performance. It should also be noted that the methods and structures exhibit substrate-independence. For example, the methods may be implemented with sapphire, GaN, Si, or SiC substrates, whereas conventional lift-off techniques for GaN devices may only be possible with sapphire substrates. According to some embodiments, the use of conductivity-based electrochemical (EC) etching may be easier during manufacture than photo-electrochemical (PEC) etching processes that can require difficult growth and etching steps needing uniform illumination.
The terms “approximately” and “about” may be used to mean within ±20% of a target dimension in some embodiments, within ±10% of a target dimension in some embodiments, within ±5% of a target dimension in some embodiments, and yet within ±2% of a target dimension in some embodiments. The terms “approximately” and “about” may include the target dimension.
Selective etching, as used herein, comprises subjecting a substrate to an etchant that preferentially etches at least one material at a faster rate than a second material. In some cases, the second material may be formed as a hard mask (e.g., an inorganic material such as an oxide, nitride, metal, or the like) or soft mask (e.g., a photoresist or polymer). In some embodiments, the second material may be part of a device structure that has different material characteristics than the first material (e.g., doping density, material composition, or crystal structure). The etch may be a dry etch or wet etch.
The technology described herein may be embodied as a method, of which at least one example has been provided. The acts performed as part of the method may be ordered in any suitable way. Accordingly, embodiments may be constructed in which acts are performed in an order different than illustrated, which may include performing some acts simultaneously, even though shown as sequential acts in illustrative embodiments. Additionally, a method may include more acts than those illustrated, in some embodiments, and fewer acts than those illustrated in other embodiments.
Although the drawings typically depict one light-emitting device, it will be appreciated that a large number of such devices can be fabricated in parallel on a substrate. A light-emitting device fabricated according to the present teachings may be formed in an integrated circuit in large numbers and at high densities. In some embodiments, the light-emitting devices may be used in consumer electronic devices such as smart phones, tablets, PDA's, computers, televisions, sensors, lighting, projectors, displays, as well as application-specific integrated circuits.
Having thus described at least one illustrative embodiment of the invention, various alterations, modifications, and improvements will readily occur to those skilled in the art. Such alterations, modifications, and improvements are intended to be within the spirit and scope of the invention. Accordingly, the foregoing description is by way of example only and is not intended as limiting. The invention is limited only as defined in the following claims and the equivalents thereto.
This application claims the benefit of U.S. provisional Application Ser. No. 61/980,313, titled “A Method for a GaN Vertical Microcavity Surface Emitting Laser (VCSEL),” filed on Apr. 16, 2014. The entire disclosure of the foregoing application is incorporated herein by reference.
This invention was made with government support under Grant No. CMMI-1129964 awarded by the National Science Foundation. The government has certain rights in the invention.
Number | Date | Country | |
---|---|---|---|
61980313 | Apr 2014 | US |