Patent Application
20090291205
This disclosure relates to a repair process and, more particularly, to a method for removing a metallic coating from a nickel substrate in a repair process.
Airfoils and other articles typically operate in relatively harsh environments. For instance, an airfoil may operate under high temperatures, corrosive conditions, and a variety of different stress states. Typically the article is designed with an alloy material to withstand the harsh environment. However, the article may also include a coating for additional protection. For example, the coating may be a diffused aluminide or ceramic coating. After a period of use, the article may be repaired or restored before another cycle of use.
An example method for a repair process includes subjecting a substrate coated with a protective metallic coating to a nitric acid solution and then subjecting the substrate with the protective metallic coating to a hydrochloric acid solution to remove the protective metallic coating from the substrate. The substrate includes about 5 wt %-15 wt % of chromium, about 2 wt %-8 wt % of cobalt, about 2 wt %-6 wt % of tungsten, about 0.5 wt %-2.5 wt % of titanium, about 8 wt %-16 wt % of tantalum, about 2 wt %-8 wt % of aluminum, hafnium in an amount no greater than 1 wt %, and a balance of nickel.
In another aspect, an example method for a repair process includes subjecting a nickel-based substrate coated with a protective metallic coating to a nitric acid solution having a molarity of 0.07M-0.80M at a first temperature of about 65° F.-160° F. and then subjecting the nickel-based substrate coated with the at least one protective metallic coating to a hydrochloric acid solution having a molarity of 0.65M-0.85M at a second temperature of about 120° F.-180° F. to remove the protective metallic coating from the nickel-based substrate. In this example, the nickel-based substrate includes hafnium in an amount no greater than 1 wt %.
In another aspect, an example method for a repair process includes subjecting a substrate coated with a protective metallic coating to a nitric acid solution having a molarity of 0.07M-0.80M at a first temperature of about 65° F.-160° F. and then subjecting the substrate coated with the protective metallic coating to a hydrochloric acid solution having a molarity of 0.65M-0.85M at a second temperature of about 120° F.-180° F. to remove the protective metallic coating from the substrate. In this example, the substrate includes about 5 wt %-15 wt % chromium, about 2 wt %-8 wt % cobalt, about 2 wt %-6 wt % tungsten, about 0.5 wt %-2.5 wt % titanium, about 8 wt %-16 wt % tantalum, about 2 wt %-8 wt % aluminum, hafnium in an amount no greater than 1 wt %, and a balance of nickel.
The various features and advantages of the disclosed examples will become apparent to those skilled in the art from the following detailed description. The drawings that accompany the detailed description can be briefly described as follows.
In the disclosed example, the article for the repair includes a nickel-based substrate coated with at least one protective metallic coating. The nickel-based substrate may include any composition that is suitable for the intended use of the article. In one example, the nickel-based substrate includes about 5 wt %-15 wt % of chromium, about 2 wt %-8 wt % of cobalt, about 2 wt %-6 wt % of tungsten, about 0.5 wt %-2.5 wt % of titanium, about 8 wt % 16 wt % of tantalum, about 2 wt %-8 wt % of aluminum, hafnium in an amount no greater than 1 wt %, and a balance of nickel. In a further example, the nickel-based substrate includes about 9.5 wt %-10.5 wt % of chromium about 4.5 wt %-5.5 wt % of cobalt, about 3.75 wt %-4.25 wt % of tungsten, about 1.25 wt %-1.75 wt % of titanium, about 11.75 wt %-12.25 wt % of tantalum, about 4.75 wt %-5.25 wt % of aluminum, about 0.25 wt %-0.45 wt % of hafnium, and the balance of nickel. The term “about” as used in this description relative to compositions or other values refers to possible variation in the given value, such as normally accepted variations or tolerances in the art.
In the above example compositions, the hafnium may be present in the form of hafnium carbide and may be undesirably susceptible to chemical etching by certain acid stripping solutions. Therefore, the given example alloys of the nickel-based substrate may be sensitive to the type of stripping solution, solution concentration, length of time exposed to the solution, and solution temperature used to remove the at least one protective metallic coating. As will be described below, the disclosed method 10 and stripping solutions limit or eliminate chemical etching of the nickel-based substrate.
The at least one protective metallic coating may be any desired composition and may include a single coating or multiple coatings, depending upon the type of article. In some examples, the article may also include a ceramic top coat, such as yttria stabilized zirconia, that may be removed using a known removal technique prior to using the method 10.
In one example, the at least one protective metallic coating includes a diffused chromium coating. The diffused chromium coating may be comprised of a minimum of 20 wt % of chromium and iron in an amount no greater than 3 wt %.
Optionally, the at least one protective metallic coating also includes a second coating on top of the diffused chromium coating. For example, the second coating includes nickel, cobalt, chromium, aluminum, yttrium, hafnium, and silicon. In a further example, the second coating includes about 20 wt %-24 wt % of cobalt, about 15 wt %-19 wt % of chromium, about 10 wt %-15 wt % of aluminum, about 0.2 wt %-1 wt % of yttrium, about 0.1 wt %-0.4 wt % of hafnium, about 0.2 wt %-0.6 wt % of silicon, and a balance of nickel. In a further example, the second coating includes about 22 wt % of cobalt, about 17 wt % of chromium, about 12.5 wt % of aluminum, about 0.6 wt % of yttrium, about 0.25 wt % of hafnium, about 0.4 wt % of silicon, and the balance of the nickel.
If the example article is an airfoil having an airfoil section that extends from a platform section, the above example protective metallic coatings may be disposed on the airfoil section. In another example, the example protective metallic coatings are disposed on the platform section of the airfoil, and the amount of chromium in the second coating is greater than the amount of cobalt.
Additionally in the above examples, the protective metallic coatings may have any suitable thickness. For example, any of the given example protective metallic coating may have a thickness up to about 0.15 inches (3.8 millimeters). In one example, each of the protective metallic coatings has a thickness less than about 0.01 inches (0.254 millimeters). Given this description, one of ordinary skill in the art will recognize other suitable thicknesses to meet their particular needs.
To remove the given example metallic coatings from the article, the article is subjected to a nitric acid solution 12 and subsequently subjected to a hydrochloric acid solution 14. For example, the article or a group of like articles may be submerged into a first container of the nitric acid solution 12 and subsequently submerged into a second container of the hydrochloric acid solution 14. For instance, the article may be supported on a fixture or a rack in the containers. However, the article may be subjected to the solutions in any other suitable manner, such as dunking or spraying, and is not limited to submerging.
Optionally, the article is rinsed with water 16 between the nitric acid solution 12 and the hydrochloric acid solution 14 to prevent reaction between any residual nitric acid on the article and the hydrochloric acid. Additionally, the nitric acid solution 12, the hydrochloric acid solution 14, or both may be agitated to facilitate coating removal.
The combination of the nitric acid solution 12 and the hydrochloric acid solution 14 removes the at least one protective metallic coating from the substrate with little or no chemical etching of the nickel-based substrate. For example, the nitric acid solution 12 is less chemically aggressive than the hydrochloric acid solution 14 with regard to the at least one protective metallic coating. Thus, the nitric acid solution 12 infiltrates the at least one protective metallic coating and chemically “loosens” the coating before the more aggressive hydrochloric acid solution 14 chemically removes the at least one protective metallic coating to complete the removal process.
In the disclosed example, the molarity of the nitric acid solution 12 is about 0.07M-0.8M and the molarity of the hydrochloric acid solution 14 is about 0.65M-0.85M. In a further example, the molarity of the nitric acid solution 12 is about 0.15M-0.2M and the molarity of the hydrochloric acid solution is about 0.7M-0.8M. In a further example, the molarity of the nitric acid solution 12 is about 0.17M and the molarity of the hydrochloric acid solution is about 0.75M.
The disclosed nitric acid solution 12 may be prepared from mixing a technical grade of “as-received” nitric acid, such as 42° Baumé 67.5 wt % nitric acid, with an appropriate amount of water to achieve a desired molarity. Likewise, the disclosed hydrochloric acid solution 14 may be prepared from mixing a technical grade of “as-received” hydrochloric acid, such as 20° Baumé 31.5 wt % hydrochloric acid, with an appropriate amount of water to achieve a desired molarity. As can be appreciated, any concentrations of the “as-received” acids may be used to achieve the desired molarities, but the amounts of water mixed may be varied based on the “as-received” concentrations to achieve the desired molarities. Given this description, one of ordinary skill in the art will be able to recognize the appropriate amounts of water to achieve a desired molarities for a given “as-received” acid concentration.
The given example concentrations provide the benefit of effectively removing the at least one protective metallic coating without detriment to the nickel-based substrate. For example, a weaker concentration of the nitric acid solution 12 may not suitably chemically “loosen” the at least one protective metallic coating and a stronger concentration of the nitric acid solution 12 may chemically damage the nickel-based substrate. Likewise, a weaker concentration of the hydrochloric acid solution 14 may not suitably chemically remove the at least one protective metallic coating and a stronger concentration of the hydrochloric acid solution 14 may chemically damage the nickel-based substrate.
At the given example concentrations, the article is subjected to the nitric acid solution 12 at a first temperature of about 60° F.-160° F. and to the hydrochloric acid solution at a second temperature of about 120° F.-180° F. to achieve removal. In one example, the first temperature is 60° F.-80° F. and the second temperature is 140° F.-160° F. Selecting the first temperature to be near ambient provides the benefit of facilitating removal of the at least one protective metallic coating without having to heat the nitric acid solution 12.
The article may be exposed to the nitric acid solution 12 and the hydrochloric acid solution 14 for a predetermined amount of time to remove the at least one protective metallic coating. In one example, the article is subjected to the nitric acid solution 12 for about two hours and to the hydrochloric acid solution 14 for about one hour. As can be appreciated, the concentrations, times, and temperatures may be adjusted within the given ranges, depending on the thickness of the at least one protective metallic coating or other parameters. Given this description, one of ordinary skill in the art would be able to recognize other exposure times to meet their particular needs.
Although a combination of features is shown in the illustrated examples, not all of them need to be combined to realize the benefits of various embodiments of this disclosure. In other words, a system designed according to an embodiment of this disclosure will not necessarily include all of the features shown in any one of the Figures or all of the portions schematically shown in the Figures. Moreover, selected features of one example embodiment may be combined with selected features of other example embodiments.
The preceding description is exemplary rather than limiting in nature. Variations and modifications to the disclosed examples may become apparent to those skilled in the art that do not necessarily depart from the essence of this disclosure. The scope of legal protection given to this disclosure can only be determined by studying the following claims.