Patent Application
20210178362
This application is based upon and claims priority to Chinese Patent Application No. 201911271764.3, filed on Dec. 12, 2019, the entire contents of which are incorporated herein by reference.
The present invention relates to the field of nano-material synthesis, and in particular to a method for assembling and synthesizing a Cu2O particle-supported porous copper benzene-1,3,5-tricarboxylate (CuBTC).
Metal-organic-frameworks (MOFs) are a novel group of porous crystalline structures, which have attracted wide attention in recent years. MOFs are characterized by a large surface area, a controllable pore size and shape, adjustable porosity and surface function. MOFs have broad application in adsorption reactions. Thus far, copper-based MOFs have attracted the most attention for their use as novel adsorbents. For example, CuBTC, with Cu3(BTC)2 as a formula unit, is a well-known MOF with high surface area and pore volume. CuBTC is especially suitable for some processes, e.g., gas storage, separation, catalysis, and adsorption due to its excellent properties. As a formula unit, CuBTC has been widely used for its adsorption capacity. There are only two types of cage structures, however: tetrahedral side pocket (about 5 Å in diameter, with 3.5 A windows) and larger square cavity (9×9 Å), both of which interrupt diffusion of relatively large molecules. Therefore, to improve mass transfer performance, it is necessary to increase the pore size and maintain the microporous structure to obtain a larger specific surface area.
Considerable research focuses on achieving meso-porous, e.g., by direct synthesis, by ligand extension, by post-treatment, and by template. These methods, however, have several drawbacks. In the ligand extension method, for example, ligands are usually expensive and difficult to synthesize.
In the post-treatment method and the template method, the post-treatment may involve arduous and lengthy processes. When synthesis of MOFs done in situ, templates are usually incorporated into frameworks randomly. Although removing templates or other molecules may produce meso-pores in MOFs, the meso-pores tend to cause either partial or complete framework collapse leading to decreased crystallinity, low porosity and poor stability. In this regard, integration of novel and conventional ligands into an MOFs appears to provide promise. As a defective ligand, the ligand can be introduced into an MOF crystal during synthesis, which produces coordinatively unsaturated metal sites and functional meso-pores. This method has the limitation, however, that the enlarged pore size still exposes an insufficient number of active sites.
Exposing more active sites typically has an important effect on adsorption properties of adsorbents. It has been shown that Cu2O may strongly bind to pollutants, for example, through sigma bonds and n-n interactions. Evaluating the adsorption property of Cu2O-modified activated carbon (AC), therefore, it was found that the adsorption property decreased gradually when the amount of Cu2O coated on the AC was increased. This quantitative inverse relationship is caused by steric hindrance and nanoparticle size. Therefore, it is desirable to provide a well-exposed active site with adjustable porosity.
To overcome the above defects, the present invention provides a method for synthesizing a Cu2O particle-supported porous CuBTC with adjustable pore size distribution that exhibits constant crystallinity and morphology of the layered porous cube.
The present invention provides the following technical solution: a method for assembling and synthesizing a Cu2O particle-supported porous CuBTC, including the following steps of:
1) dissolving 1.4-1.6 g of polyvinylpyrrolidone (PVP) in ethanol solution to obtain a PVP-ethanol solution;
2) dissolving 2.1-2.2 g of copper salt in distilled water, and mixing with 0.6-0.7 g of trimesic acid, 0-0.9 g of salicylic acid, and the PVP-ethanol solution obtained in step 1) under stirring;
3) conducting a hydrothermal reaction on the mixed solution obtained in step 2) at 120° C. to obtain Cu2O particle-supported porous CuBTC.
Further, in the hydrothermal reaction in step 3), 0.5-1.5 g of citric acid is dissolved in distilled water to obtain 0.5-1.5 M citric acid solution. The citric acid solution is mixed with the mixtures obtained in steps 1) and 2) under stirring for 0.5-1 h, and then transferred into a 100 ml hydrothermal reactor. The hydrothermal reactor is sealed and placed in an oven for the hydrothermal reaction at 120° C.
Further, in the hydrothermal reaction in step 3), 1-2 g of tartaric acid is dissolved in distilled water to obtain 1-2 M tartaric acid solution. The tartaric acid solution is mixed with the mixtures obtained in steps 1) and 2) under stirring for 0.5-1 h, and then transferred into a 100 ml hydrothermal reactor; the hydrothermal reactor is sealed and placed in an oven for the hydrothermal reaction at 120° C.
Further, a mass of the salicylic acid is 0.4-0.5 g.
Further, the mass of the salicylic acid is 0.7-0.8 g.
Further, the mass of the salicylic acid is 0.8-0.9 g.
Further, the copper salt is Cu(NO3)2.3H2O.
Further, a molar ratio of the ethanol solution in step 1) to the distilled water in step 2) is 1:1.
Further, both the ethanol solution in step 1) and the distilled water in step 2) are 30 ml in volume.
Further, the hydrothermal reaction in step 3) lasts for 12 h.
The present invention has the following advantages: 1) The method for assembling and synthesizing a Cu2O particle-supported porous CuBTC provided by the present invention needs no template or complexing agent and is easy to operate. Moreover, because neither template nor complexing agent is used, meso-pores produced by the method will not lead to framework collapse caused by incorporation of the template or complexing agent into a framework, thereby improving the crystallinity, porosity, and stability of the synthesized Cu2O particle-supported porous CuBTC.
2) The present invention introduces salicylic acid during the synthesis of CuBTC. The salicylic acid, as a ligand precursor, forms a new ligand under the catalysis of Cu ion at a certain temperature. The new ligand lacks an active coordination site relative to trimesic acid, and a porous CuBTC material is formed through the unsaturated coordination of the ligand. Meanwhile, during the generation of the new ligand, a certain number of reducing substances are produced, which catalyzes the reduction of a Cu cluster to a Cu2O nano-material in the presence of oxygen.
3) The method for synthesizing the Cu2O particle-supported porous CuBTC provided by the present invention is green, mild, simple, and feasible; not only does the method for assembling and synthesizing a ligand produce a hierarchical porous structure, but also maintains basically the same morphology and crystallinity. Particularly, the resulting porous CuBTC framework is supported with ultrafine Cu2O nanoparticles. The composite produced thereby, i.e., Cu2O particle-supported porous CuBTC, can adsorb high-energy molecules.
4) Addition of citric acid or tartaric acid as auxiliary acidifier in the hydrothermal reaction plays a guiding role in the growth of the synthesized porous Cu2O particle-supported porous CuBTC. The Cu2O particle-supported porous CuBTC synthesized by auxiliary acidifier-assisted hydrothermal reaction has a better heterogeneous spatial phase, a smaller molecular volume and steric hindrance, and reacts with Cu2O in the space network structure of the Cu2O particle-supported porous CuBTC more easily, to obtain a Cu2O particle-supported porous CuBTC with better performance with the aid of the auxiliary acidifier.
The present invention will be described below in more detail with reference to the examples and the drawings. Particularly:
Taken in conjunction with the accompanying drawings, the following paragraphs describe the technical solutions in exemplary embodiments of the present invention. The described examples are merely a part rather than all of the examples of the present invention. All other examples obtained by a person of ordinary skill in the art based on the examples of the present invention without creative efforts shall fall within the protection scope of the present invention.
A method for assembling and synthesizing a Cu2O particle-supported porous CuBTC of this example includes the following steps.
1) 1.4 g of polyvinylpyrrolidone (PVP) was dissolved in 30 ml of ethanol solution to obtain a PVP-ethanol solution.
2) 2.1 g of Cu(NO3)2.3H2O was dissolved in 30 ml of distilled water, and mixed with 0.6 g of trimesic acid, 0 g of salicylic acid, and the PVP-ethanol solution obtained in step 1) under stirring.
3) A hydrothermal reaction was conducted on the mixed solution obtained in step 2) at 120° C. for 12 h. Specifically, in the hydrothermal reaction, 0.5 g of citric acid was dissolved in distilled water to obtain 0.5 M citric acid solution. The citric acid solution was mixed with the mixtures obtained in steps 1) and 2) under stirring for 0.5 h, and then transferred into a 100 ml hydrothermal reactor; the hydrothermal reactor was sealed and placed in an oven for the hydrothermal reaction at 120° C., to obtain Cu2O particle-supported porous CuBTC.
This example differs from Example 1 only in that: in the hydrothermal reaction, 1 g of citric acid was dissolved in distilled water to obtain 1 M citric acid solution. The above citric acid solution was mixed with the mixtures obtained in steps 1) and 2) under stirring for 0.8 h, and then transferred into a 100 ml hydrothermal reactor. The hydrothermal reactor was sealed and placed in an oven for the hydrothermal reaction at 120° C.
This example differs from Example 1 and 2 only in that: in the hydrothermal reaction, 1.5 g of citric acid was dissolved in distilled water to obtain 1.5 M citric acid solution. The above citric acid solution was mixed with the mixtures obtained in steps 1) and 2) under stirring for 1 h, and then transferred into a 100 ml hydrothermal reactor; the hydrothermal reactor was sealed and placed in an oven for the hydrothermal reaction at 120° C.
A method for assembling and synthesizing a Cu2O particle-supported porous CuBTC of this example includes the following steps.
1) 1.45 g of PVP was dissolved in 30 ml of ethanol solution to obtain a PVP-ethanol solution.
2) 2.13 g of Cu(NO3)2.3H2O was dissolved in 30 ml of distilled water, and mixed with 0.635 g of trimesic acid, 0.45 g of salicylic acid, and the PVP-ethanol solution obtained in step 1) under stirring.
3) A hydrothermal reaction was conducted on the mixed solution obtained in step 2) at 120° C. for 12 h. Specifically, in the hydrothermal reaction, 1 g of tartaric acid was dissolved in distilled water to obtain 1 M tartaric acid solution. The above tartaric acid solution was mixed with the mixtures obtained in steps 1) and 2) under stirring for 0.5 h, and then transferred into a 100 ml hydrothermal reactor. The hydrothermal reactor was sealed and placed in an oven for the hydrothermal reaction at 120° C., to obtain Cu2O particle-supported porous CuBTC (1).
This example differs from Example 4 only in that: in the hydrothermal reaction, 1.5 g of tartaric acid was dissolved in distilled water to obtain 1.5 M tartaric acid solution. The above tartaric acid solution was mixed with the mixtures obtained in steps 1) and 2) under stirring for 0.8 h, and then transferred into a 100 ml hydrothermal reactor. The hydrothermal reactor was sealed and placed in an oven for the hydrothermal reaction at 120° C.
This example differs from Example 4 and 5 only in that: in the hydrothermal reaction, 2 g of tartaric acid was dissolved in distilled water to obtain 2 M tartaric acid solution. The above tartaric acid solution was mixed with the mixtures obtained in steps 1) and 2) under stirring for 0.5-1 h, and then transferred into a 100 ml hydrothermal reactor. The hydrothermal reactor was sealed and placed in an oven for the hydrothermal reaction at 120° C.
A method for assembling and synthesizing a Cu2O particle-supported porous CuBTC of this example includes the following steps.
1) 1.55 g of PVP was dissolved in 30 ml of ethanol solution to obtain a PVP-ethanol solution.
2) 2.17 g of Cu(NO3)2.3H2O was dissolved in 30 ml of distilled water, and mixed with 0.675 g of trimesic acid, 0.65 g of salicylic acid, and the PVP-ethanol solution obtained in step 1) under stirring.
3) A hydrothermal reaction was conducted on the mixed solution obtained in step 2) at 120° C. for 12 h to obtain Cu2O particle-supported porous CuBTC (1.5), and a scanning electron micrograph thereof is shown in
A method for assembling and synthesizing a Cu2O particle-supported porous CuBTC of this example includes the following steps.
1) 1.6 g of PVP was dissolved in 30 ml of ethanol solution to obtain a PVP-ethanol solution.
2) 2.2 g of Cu(NO3)2.3H2O was dissolved in 30 ml of distilled water, and mixed with 0.7 g of trimesic acid, 0.85 g of salicylic acid, and the PVP-ethanol solution obtained in step 1) under stirring.
3) A hydrothermal reaction was conducted on the mixed solution obtained in step 2) at 120° C. for 12 h to obtain Cu2O particle-supported porous CuBTC (2).
Nitrogen adsorption-desorption isotherms, pore size distributions, and XRD patterns were tested for the Cu2O particle-supported porous CuBTC obtained in Examples 1, 4, 7, and 8 of the present invention. The results are shown in
From
From
From
For the purposes of promoting an understanding of the principles of the invention, specific embodiments have been described. It should nevertheless be understood that the description is intended to be illustrative and not restrictive in character, and that no limitation of the scope of the invention is intended. Any alterations and further modifications in the described components, elements, processes or devices and any further applications of the principles of the invention as described herein, are contemplated as would normally occur to one skilled in the art to which the invention pertains.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201911271764.3 | Dec 2019 | CN | national |