A Li-ion battery consists of two electrodes (anode and cathode), a membrane separating anode from cathode, and electrolyte. Electrodes consist of an active material, a binder, a carbon-based additive and current collectors. Aluminum/Copper foils are typical current collectors for Li-ion batteries. Usually, the active material is printed on the surface of the current collectors using a slurry consisting of the active material, the additive, a binder, and a proper solvent. After preparation of the electrode, an electrically conductive tab is attached to the current collector to get the current out of the battery. Commonly, the tab is a strip of aluminum/copper/nickel foil, which is welded to the current collector foil of the electrodes.
The following presents a simplified summary of one or more aspects of the present disclosure in order to provide a basic understanding of such aspects. This summary is not an extensive overview of all contemplated aspects and is intended to neither identify key or critical elements of all aspects nor delineate the scope of any or all aspects. Its purpose is to present some concepts of one or more aspects in a simplified form as a prelude to the more detailed description that is presented later.
In the case of self-standing electrodes, free of binder and comprising the active material powder in a carbon nanotube matrix, and in which no collector foil is present, a method is needed for transporting the current from the electrodes. In other words, it is necessary to solve the problem of tab attachment to the electrode, which does not have any current collector foils.
In some embodiments, the present disclosure is directed to a self-standing electrode comprising: a body comprising a composite material having electrode active material particles in a three-dimensional cross-linked network of carbon nanotubes; a member extending outward from the body, the member comprising the composite material; and a battery tab secured to the member.
In some embodiments, the present disclosure is directed to a method of making a self-standing electrode, the method comprising: aerosolizing or fluidizing an electrode active material to produce an aerosolized or fluidized electrode active material; and co-depositing the aerosolized or fluidized electrode active material and carbon nanotubes to form a self-standing electrode; and securing a battery tab to the electrode such that each of at least a first face and a second face of the electrode is in contact with the battery tab.
In some embodiments, the present disclosure is directed to a self-standing electrode comprising: a self-standing body that is free of a binder and comprises a composite material having electrode active material particles in a three-dimensional cross-linked network of carbon nanotubes, wherein the self-standing body includes a first face and a second face opposite the first face; and a battery tab secured to the self-standing body that comprises: a body; a first leg extending from the body of the battery tab; and a second leg extending from the body of the battery tab, wherein the self-standing electrode body is positioned between the first leg and the second leg, and the first leg contacts the first face of the self-standing body and the second leg contacts the second face of the self-standing body.
These and other aspects of the invention will become more fully understood upon a review of the detailed description, which follows.
The detailed description set forth below in connection with the appended drawings is intended as a description of various configurations and is not intended to represent the only configurations in which the concepts described herein may be practiced. The detailed description includes specific details for the purpose of providing a thorough understanding of various concepts. However, it will be apparent to those skilled in the art that these concepts may be practiced without these specific details.
The present disclosure provides self-standing electrodes comprising a composite of carbon nanotubes and electrode active materials, with a battery tab secured to the outside, and methods of making the same.
In some embodiments, the present disclosure is directed to a self-standing electrode comprising: a body comprising a composite material having an electrode active material in a three-dimensional cross-linked network of carbon nanotubes; a member extending outward from the body, the member comprising the composite material; and a battery tab secured to the member.
As used herein, “electrode active material” refers to the material hosting Lithium in an electrode. The term “electrode” refers to an electrical conductor where ions and electrons are exchanged with an electrolyte and an outer circuit. “Positive electrode” and “cathode” are used synonymously in the present description and refer to the electrode having the higher electrode potential in an electrochemical cell (i.e. higher than the negative electrode). “Negative electrode” and “anode” are used synonymously in the present description and refer to the electrode having the lower electrode potential in an electrochemical cell (i.e. lower than the positive electrode). Cathodic reduction refers to a gain of electron(s) of a chemical species, and anodic oxidation refers to the loss of electron(s) of a chemical species.
As used herein, the term “about” is defined as being close to as understood by one of ordinary skill in the art. In one non-limiting embodiment, the term “about” is defined to be within 10%, preferably within 5%, more preferably within 1%, and most preferably within 0.5%.
In a non-limiting example, the electrode active material may be any solid, metal oxide powder that is capable of being aerosolized. In an illustrative example, the metal oxide is a material for use in the cathode of the battery. Non-limiting examples of metal oxides include oxides of Ni, Mn, Co, Al, Mg, Ti, and any mixture thereof. The metal oxide may be lithiated. In an illustrative example, the metal oxide is lithium nickel manganese cobalt oxide (LiNiMnCoO2). The metal oxide powders can have a particle size defined within a range between about 1 nanometer and about 1000 microns, or any integer or subrange in between. In a non-limiting example, the metal oxide particles have an average particle size of about 1 μm to about 10 μm. In a non-limiting example, the metal oxide particles have an average particle size of about 1 nm to about 10 nm. Metals in lithium metal oxides according to the present disclosure may include but are not limited to one or more alkali metals, alkaline earth metals, transition metals, aluminum, or post-transition metals, and hydrates thereof.
“Alkali metals” are metals in Group I of the periodic table of the elements, such as lithium, sodium, potassium, rubidium, cesium, or francium.
“Alkaline earth metals” are metals in Group II of the periodic table of the elements, such as beryllium, magnesium, calcium, strontium, barium, or radium.
“Transition metals” are metals in the d-block of the periodic table of the elements, including the lanthanide and actinide series. Transition metals include, but are not limited to, scandium, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, technetium, ruthenium, rhodium, palladium, silver, cadmium, lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium, hafnium, tantalum, tungsten, rhenium, osmium, iridium, platinum, gold, mercury, actinium, thorium, protactinium, uranium, neptunium, plutonium, americium, curium, berkelium, californium, einsteinium, fermium, mendelevium, nobelium, and lawrencium.
“Post-transition metals” include, but are not limited to, gallium, indium, tin, thallium, lead, bismuth, or polonium.
As used herein, suitable composites or mixtures of “an electrode active material and carbon nanotubes” include, but are not limited to, self-standing electrodes such as those disclosed in U.S. patent application Ser. No. 15/665,171, entitled “Self Standing Electrodes and Methods for Making Thereof,” filed Jul. 31, 2017, which is hereby incorporated by reference herein in its entirety. In some aspects, the electrode active material is selected from graphite, hard carbon, silicon, silicon oxides, lithium metal oxides, lithium iron phosphate, sulfur, and lithium metal particles. In some aspects, the electrode active material is selected from graphite, hard carbon, silicon, silicon oxides, lithium metal oxides, lithium metal, and lithium iron phosphate.
In some aspects, the battery tab comprises a metal (including metal alloys). Metals in battery tabs according to the present disclosure may include, but are not limited to, alkali metals, alkaline earth metals, transition metals, aluminum, and post-transition metals, and alloys comprising the same.
In some aspects, the metal may be copper, aluminum, nickel, gold, silver, palladium, platinum, or alloys thereof. In some aspects, the metal may be copper or aluminum. The battery tab may be in any solid physical form, including but not limited to, foil, strips, wire, rod, grid, or mesh. In some aspects, the battery tab has a thickness of about 5 μm to about 2000 μm, or any integer or subrange in between. In some aspects, the battery tab has a thickness of about 100 μm. In some aspects, the battery tab has a thickness of about 15 μm. In some aspects, the battery tab has a width of about 0.001 cm to about 100 cm, or any subrange in between. In some aspects, the battery tab has a width of about 0.5 cm. Tab width and thickness depend on the electrode size and the weight of the active material in it, and, therefore, the current the tab needs to carry. Based on the conductance of tab material, and the current it needs to carry, the minimal tab geometry (especially its cross-section area) can be calculated. The same considerations apply to the size of the protruding “member”, and, for large electrodes, direct attachment of the tab to the main body of the electrode (especially along one of the edges, such as shown in
In some aspects, the member has at least a first face and a second face, each of the first face and the second face having a surface area of at least 5 mm×5 mm. The member or protrusion can be wider, narrower or the same width as the tab.
For example, in
As another non-limiting example,
In some aspects, the self-standing electrode body does not have a member or protrusion, and the tab can be attached to the main body of the electrode directly. For example,
The tab can fully or partially envelop the protruding member (see, e.g.,
In some aspects, a first portion of the single sheet of metal that is in contact with the first face of the member is connected to a second portion of the single sheet of metal that is in contact with the second face of the member via one or more welds, rivets, staples, clamps, or clips. In some aspects, the one or more welds or rivets may go through the member, from the first face to the second face. The number of welds or rivets is not limited in any way. In other aspects, welds or rivets may not be used.
In some aspects, the battery tab has a thickness of about 5 to about 200 μm, or any integer or subrange in between, and a width of less than about 1 cm, or any integer or subrange in between. The battery tab thickness and width suitably depend on the electrode size and shape, weight of the active material, type of the active material, and conductivity of the material the electrode is made of, and other parameters of the battery, and, thus, the current it generates/consumes, as will be known to those of ordinary skill in the art. Other battery parameters affecting the current include, but are not limited to, particle size and shape of the active material; electrolyte composition and concentration (i.e., which solvent(s) are used and in which proportions, which salt(s) are used and in which concentrations); whether it is liquid, gel or solid electrolyte (and the type of the solid electrolyte); the separator membrane (if it is present) composition and geometry, electrodes arrangement in the battery, and many other design and manufacturing parameters, as well as the quality of all components involved. In some aspects, the battery tab thickness is about 10 to about 150 μm, and the battery tab width is about 0.5 cm. In some aspects, the battery tab is suitably long enough to extend past the battery enclosure (which may be, e.g., a pouch) from the site of the tab attachment to the electrode, i.e., one end of the tab is attached to the electrode inside the battery; the other end is outside of the battery; so that the external load can be electrically connected to it. In some cases, such as in batteries with multiple or complex electrodes, the tab is suitably long enough to reach either another electrode or an attachment point to another tab, or to be attached to the battery housing (e.g., in cylindrical or prismatic batteries). The typical length of the commercially available tabs suitable for use with the electrodes and methods of the present disclosure is about 10 cm or less.
The electrode may be of any thickness, such as from about 1 μm to about 10 mm, or any integer or subrange in between. In some aspects, the electrode has a thickness of about 10 μm to about 300 μm. In some aspects, the electrode has a thickness of about 20 μm to about 300 μm. In some aspects, the electrode has a thickness of about 20 μm to about 100 μm. Suitable electrode thickness may depend on the application for the electrode, as will be known to those of ordinary skill in the art. In a non-limiting example, suitable electrode thickness for a car battery may be about 300 μm. In a non-limiting example, suitable electrode thickness for sensors may be from about 10 μm to about 20 μm. In addition, without wishing to be bound by any particular theory, the energy density and/or charge density of the electrode may depend on electrode thickness.
In some aspects, the battery tab secured to the member comprises two sheets of a metal that are in contact with the first face and the second face of the member, and that are connected to each other via one or more welds, rivets, staples, clamps, or clips. In some aspects, the two sheets are connected to each other via one weld or rivet. In some aspects, the two sheets are connected to each other via two or more welds or rivets. It is within the level of ordinary skill in the art to vary and/or optimize the number of welds or rivets, for a given electrode and/or application thereof. In some aspects, the one or more welds or rivets travel through the member. In some aspects, the first face of the member is opposite the second face. Tools, materials, and methods for welding and riveting include those known in the art. Rivets and clamps (such as spring compression clamps) are suitably made of the same material as the tab. Materials for the tab are suitably selected based on the particular chemistry of the battery and based on the electrochemical potential of the electrode it is attached to. In lithium batteries, the cathode tab is typically aluminum, while anode tab is typically copper or nickel; but for other chemistry of the battery other metals can be used. For example, the rivets, staples, or clips can be made of very electrochemically inert metals (e.g., noble metals like gold or platinum). In another non-limiting example, certain grades of stainless steel can also be used, depending on the particular chemistry of the battery (i.e., which active materials and which electrolyte are used). Welds may be formed using any suitable method known in the art, including but not limited to spot welding or ultrasonic welding. Staples, rivets, and clamps may be installed using any suitable method known in the art.
In other embodiments, the present disclosure is directed to a method of making a self-standing electrode, the method comprising: aerosolizing or fluidizing an electrode active material to produce an aerosolized or fluidized electrode active material; and co-depositing the aerosolized or fluidized electrode active material and carbon nanotubes, to form a self-standing electrode; and securing a battery tab to the electrode such that each of at least a first face and a second face of the electrode is in contact with the battery tab. All aspects described with respect to the electrode apply to the method with equal force. In some aspects, this co-depositing may be onto a porous surface. In some aspects, the method further comprises the step of, before securing the battery tab to the electrode, shaping the self-standing electrode to form a body and a member extending outward from the body, and the battery tab is secured to the member.
In some aspects, the battery tab comprises a metal. In some aspects, the metal is aluminum or copper. The metal may be in any solid physical form, including but not limited to one or more wires, grids, meshes, foils, rods, or sheets.
In some aspects, the securing comprises folding a single sheet of metal over the electrode or member protruding therefrom (
In some aspects, the one or more welds or rivets travel through the electrode. In some aspects, the at least two faces are at least two opposite faces. In some aspects, the securing comprises contacting each of two faces of the electrode with a respective metal sheet; and connecting the respective metal sheets to one another via one or more welds, rivets, staples, clamps, or clips.
Without wishing to be bound by any particular theory, it is believed that welding or riveting does not impose a limitation on electrode thickness. For example, welding or riveting may be used on electrodes with thickness ranging from about 1 μm to about 5000 μm, or any integer or subrange in between. Preferably, welding or riveting is used on electrodes with thickness ranging from about 10 μm to about 300 μm. In some aspects, folding may be used on electrodes with thickness ranging from about 10 μm to about 5000 μm, or any integer or subrange in between. Preferably, folding is used with electrodes with thickness ranging from about 100 μm to about 300 μm.
The particular mode of welding or fastening used may depend on the thickness of the electrode, as well as on the tab material and thickness, and can be determined by those of ordinary skill in the art. In a non-limiting example, for very thick electrodes (i.e., 200-5000 μm), it may be preferable to use clamps (
In one non-limiting example,
Without wishing to be bound by any particular theory, it is believed that welding or riveting may lower the contact resistance of the battery tab-secured self-standing electrode; i.e., welding or riveting may increase the degree of contact between the electrode and the battery tab at the interface. As will be known to those of ordinary skill in the art, the lower the degree of contact, the higher the contact resistance, and the greater the degree of energy loss. It may be preferable to minimize the degree of energy loss, for example, by increasing the degree of contact between the electrode and the battery tab at the interface. With thicker electrodes, it may be desirable to lower the contact resistance in the battery tab-secured self-standing electrodes by welding, riveting, or other suitable means as will be known in the art.
In some aspects, the method further comprises the step of, before securing the battery tab to the electrode, shaping the self-standing electrode to form a body and a member extending outward from the body, and wherein the battery tab is secured to the member. Aspects of battery tab attachment to the electrode body apply to battery tab attachment to the electrode member with equal force, and vice versa.
The battery tab may be sized such that the width of the battery tab does not exceed the width of the electrode body or member. In some aspects, the width of the battery tab is less than the width of the electrode body or member, by less than about 50 mm, such as by less than about 40 mm, less than about 30 mm, less than about 20 mm, or less than about 10 mm, or any integer or subrange in between. The difference in width between the battery tab and the electrode body or member may depend on the electrode active materials and/or the metal used in the battery tab, and/or on the application of the battery tab-secured electrode. In some aspects, the shaping of the self-standing electrode to form the body and the member extending outward from the body comprises cutting the self-standing electrode so as to leave a member extending outward from the body. Alternatively, the electrode might be deposited (from the aerosolized mixture of components) onto a porous surface shaped as the final shape of the electrode (with all desired protrusions, etc.), and no further shaping/cutting is necessary.
In some aspects, the battery tab attachment may be a multi-layer battery tab attachment, such as shown in
In some aspects, the co-depositing the aerosolized active material and carbon nanotubes comprises contacting the aerosolized electrode active material powder with the carbon nanotubes in a carrier gas to form a mixture of the carbon nanotubes and the aerosolized electrode active material powder; collecting the mixture on the porous surface; and removing the carrier gas. Suitable methods and apparatuses for contacting the aerosolized electrode active material powder with the carbon nanotubes in a carrier gas to form a mixture of the carbon nanotubes and the aerosolized electrode active material powder, suitable porous surfaces, and suitable methods and apparatuses for removing carrier gases are known to those of ordinary skill in the art and include, but are not limited to, those disclosed in U.S. patent application Ser. No. 15/665,171, entitled “Self Standing Electrodes and Methods for Making Thereof,” filed Jul. 31, 2017, which is hereby incorporated herein by reference in its entirety. Carbon nanotubes suitable for use in the methods of the present disclosure include single-walled nanotubes, few-walled nanotubes, and multi-walled nanotubes. In some aspects, the carbon nanotubes are single-walled nanotubes. Few-walled nanotubes and multi-walled nanotubes may be synthesized, characterized, co-deposited, and collected using any suitable methods and apparatuses known to those of ordinary skill in the art, including those used for single-walled nanotubes.
In some aspects, the co-depositing comprises co-depositing the aerosolized or fluidized electrode active material and carbon nanotubes onto a porous surface to form a binderless self-standing electrode.
The apparatus for providing the aerosolized mixture of carbon nanotubes and electrode active materials is not limited in any way. In an illustrative example as shown in
Optionally, the apparatus 5 may include a plurality of porous substrates 40, 41 to allow for the continuous production of self-standing electrodes 60, 61. Although only two porous substrates are shown, it is to be understood than any number of porous substrates may be included in the apparatus 5. In a non-limiting example, when the flow of the mixed aerosolized stream 30 across the porous substrate 40 produces the self-standing electrode 60 of the desired thickness, a valve 33 may be adjusted to transfer the flow of the mixed aerosolized stream 30 to a second porous substrate 41. The self-standing electrode 60 may be removed from the first porous substrate 40 during formation of the self-standing electrode 61 on the porous substrate 41. When the flow of the mixed aerosolized stream 30 across the second porous substrate 41 produces the self-standing electrode 61 of a desired thickness, the valve 33 may be adjusted to transfer the flow of the mixed aerosolized stream 30 back to the first porous substrate 40. The thickness and/or cross-sectional area of the self-standing electrode 61 may be the same, or different, than the cross-sectional area of the self-standing electrode 60. For example, the self-standing electrode 61 may have a greater thickness and/or cross-sectional area than the self-standing electrode 60.
It is to be understood that a variety of different methods may be used for automatically switching the valve 33 to redirect the flow of the mixed aerosolized stream 30 from one porous substrate to the other. Illustrative examples of systems that may be used to adjust the valve 33 to redirect the flow of the mixed aerosolized stream 30 include one or more sensors for detecting the thickness of the self-standing electrodes 60 and 61, one or more pressure sensors for monitoring a pressure drop across the porous substrates 40 and 41 that corresponds to a desired thickness of the self-standing electrodes 60 and 61, a timer that switches the valve 33 after a set time corresponding to a desired thickness of the self-standing electrodes 60 and 61 for a given flow rate of the mixed aerosolized stream 30, and any combination thereof; after the one or more pressure sensors measures a pressure drop associated with the desired thickness of the self-standing electrode 60 or 61 on porous substrate 40 or 41, or after the one or more thickness sensors detect the desired thickness of the self-standing electrode 60 or 61 on porous substrate 40 or 41, or after the timer measures the set time corresponding to the desired thickness of self-standing electrode 60 or 61 on porous substrate 40 or 41, the mixture is redirected from one porous substrate to the other. It is also to be understood that the porous substrates 40 and/or 41 may have a cross-sectional area that matches the desired cross-sectional area required for use in the battery cell to be made with the self-standing electrode 60 and/or 61. Accordingly, the self-standing electrodes 60 and/or 61 would require no further processing of the cross-sectional area, such as cutting, before assembly in the final battery cell. It is to be understood that the configuration of the vessel 10 is not intended to be limited in any way.
As shown in
As shown in
As an alternative to the specific apparatus noted above where the electrode active material is mixed with the nanotubes after the nanotubes are formed, the electrode active material can be mixed in situ in a fluidized bed reactor or chamber with the nanotubes as the nanotubes are formed.
In some aspects, the co-depositing the aerosolized or fluidized electrode active material and carbon nanotubes comprises simultaneously contacting with the porous surface the aerosolized or fluidized electrode active material and the carbon nanotubes, wherein the aerosolized or fluidized electrode active material and the carbon nanotubes were not previously in contact with one another.
The co-depositing may occur over any duration of time. Without wishing to be bound by any particular theory, the thickness of the binderless, collectorless self-standing electrode may be determined by one or more factors including but not limited to the duration of time of co-depositing, the flow rate of the mixture of the carbon nanotubes and the aerosolized electrode active material powder, and the concentrations of the aerosolized electrode active material and/or the carbon nanotubes. In some aspects, about 20 minutes of co-depositing may result in a binderless, collectorless self-standing electrode with a thickness of about 30 μm. In some aspects, about 2 hours of co-depositing may result in a binderless, collectorless self-standing electrode with a thickness of about 100 μm. Those of ordinary skill in the art will be able to vary those factors to obtain self-standing electrodes of desired thickness and/or other properties, such as electric charge or energy charge. For example, the aforementioned flow rate and/or concentrations may be varied using the methods and apparatuses disclosed in U.S. patent application Ser. No. 15/665,171, entitled “Self Standing Electrodes and Methods for Making Thereof,” filed Jul. 31, 2017, which is hereby incorporated by reference herein in its entirety. In some aspects, the overall thickness of the electrode is about 10 μm to about 5000 μm. In some aspects, the overall thickness of the electrode is about 20 μm to about 100 μm.
In some aspects, the securing comprises: contacting each of two faces of the electrode with a respective metal sheet; and connecting the respective metal sheets to one another via one or more welds, rivets, staples, clamps, or clips. In some aspects, the two faces are two opposite faces. In some aspects, the one or more welds, rivets, or staples travels through the electrode.
In addition, the thickness of the binderless, collectorless self-standing electrode may be modified by pressing, which may reduce the overall thickness by as much as 5 times, such as by about 4 times, by about half, by about 1.5 times, or any range in between. For example, a binderless, collectorless self-standing electrode with a thickness of 100 μm may be pressed to a thickness of 50 μm (i.e., reduced overall thickness by half), or a binderless, collectorless self-standing electrode with a thickness of 500 μm may be pressed to a thickness of 100 μm (i.e, reduced overall thickness by 5 times). In some aspects, pressing reduces overall thickness by half. In some aspects, pressing reduces overall thickness by about 1.5 times to by about 3 times. Pressing may also modify the density of the electrode. Suitable methods and apparatuses for pressing electrodes are known in the art are include but are not limited to those disclosed in U.S. patent application Ser. No. 15/665,171, entitled “Self Standing Electrodes and Methods for Making Thereof,” filed Jul. 31, 2017, which is hereby incorporated by reference herein in its entirety.
As will be known to those of ordinary skill in the art, pressing or compression may improve electrical and/or mechanical contact between the battery tab and the composite, and it may also make the composite mechanically stronger. However, too much compression or pressing can hinder electrolyte access to the inner parts of the electrode, and complicate the movement of lithium ions in and out of the electrode, thereby worsening battery dynamic characteristics. Alternatively, too thick of an electrode may hold sufficient energy, but be too slow to produce energy or may not be suitably flexible. Alternatively still, it may be desirable to obtain an electrode foil that is flexible without formation of cracks and/or delaminations. On the other hand, if the electrode is too thin, energy production may be rapid but it may be the case that not enough energy is produced. In addition, it may be desirable to regulate the distance between the rolls or rollers in a rolling press or calendaring machine, or between the plates of a platen press. It is within the knowledge of those of ordinary skill in the art to determine optimal pressing thickness based on the properties desired in the electrode.
Binderless, collectorless self-standing electrodes suitable for use in the methods or apparatuses of the present disclosure may be flexible or not flexible. As used herein, an electrode that is “flexible” is able to be bent without cracking or breaking. As will be known to those of ordinary skill in the art, flexibility may depend on one or more chemical and/or material factors, including but not limited to composition and degree of compression. For example, very strongly compressed electrodes may be very rigid and can even become brittle. Similarly, low nanotube content electrodes can also be mechanically weak and may even shed particles of active material. However, in other non-limiting examples, self-standing electrode material may be too flexible if the material wrinkles, folds, or rolls on itself easily, as this might complicate stretching and spreading it over the desired area, e.g., during the battery layers stacking, or during the insertion into an enclosure. Higher nanotube content contributes to flexibility and mechanical strength.
In some embodiments, the present disclosure is directed to a self-standing electrode comprising: a self-standing body that is free of a binder and comprises a composite material having electrode active material particles in a three-dimensional cross-linked network of carbon nanotubes, the self-standing body includes a first face and a second face opposite the first face; and a battery tab secured to the self-standing body that comprises: a body; a first leg extending from the body of the battery tab; and a second leg extending from the body of the battery tab, wherein the self-standing electrode body is positioned between the first leg and the second leg, and the first leg contacts the first face of the self-standing body, and the second leg contacts the second face of the self-standing body. All aspects described with respect to the aforementioned embodiments apply to the present embodiment with equal force, and vice versa.
The battery tab body refers to the portion of the battery tab not in contact with the self-standing electrode. The first and second legs of the battery tab are the portions of the battery tab in direct contact with first and second face of the self-standing electrode, respectively.
In some aspects, the first leg covers less than 50% of the surface area of the first face of the self-standing body, and the second leg covers less than 50% of the surface area of the second face of the self-standing body.
In some aspects, the first leg covers less than 33% of the surface area of the first face of the self-standing body, and the second leg covers less than 33% of the surface area of the second face of the self-standing body.
In some aspects, the first leg covers less than 25% of the surface area of the first face of the self-standing body, and the second leg covers less than 25% of the surface area of the second face of the self-standing body.
Battery tabs may be secured to the self-standing electrode body by any suitable means, including but not limited to those described for securing of battery tabs to members protruding from self-standing electrode bodies, such as folding, spot welding, or riveting. Spot welding or riveting may be performed using methods and apparatuses known to persons of ordinary skill in the art, and spot welds or rivets may be applied to connect the self-standing electrode body and the battery tab in any number and pattern or array suitable to secure the battery tab to the self-standing electrode body.
In some aspects, the first leg and the second leg each extends outward from the body of the battery tab, at least a first connection extends from the first leg and through the self-standing body to the second leg, and a first portion of the self-standing body is positioned between the body of the battery tab and the first connection. In some aspects, a second connection extends from the first leg and through the self-standing body to the second leg, and a second portion of the self-standing body is positioned between the first connection and the second connection. In some aspects, the first connection and the second connection are spot welds. In other aspects, the first connection and the second connection are rivets. In some aspects, the first connection and the second connection are ultrasonic welds. In some aspects, the tab is attached directly to the self-standing body. In some aspects, the tab is attached perpendicular to the edge of the main body of the electrode. In some aspects, the tab is attached at an angle to the edge. In some aspects, the tab comprises a single sheet of metal folded over the electrode. In some aspects, the tab comprises two sheets, each placed on an opposite face of the electrode. In some aspects, the tab is attached to a protrusion from the body, the protrusion being wider than the tab or of about the same width as the tab. In some aspects, the tab is attached to a protrusion from the body, the protrusion being narrower than the tab. In some aspects, the tab is folded over an edge of the main body of the electrode, or a protrusion therefrom, and the tab is secured by welds, rivets, staples, clamps, or clips. In some aspects, each of the first leg and the second leg comprises two or more layers of metal foil. In some aspects, the battery tab comprises two sheets of metal folded over the electrode.
In some preferred aspects, as shown in
In other preferred aspects, as shown in
In a more preferred aspect, as shown in
In the aspects shown in
Without wishing to be bound to any particular theory, it is believed to be beneficial to have an increased nanotube content on the faces of the self-standing electrode body (or member protruding therefrom) facing the tab, to improve mechanical adhesion and electrical contact between the tab and the self-standing electrode body (or member protruding therefrom), such as shown in
The electrode of the present disclosure may be used in a pouch cell, such as a flexible pouch cell. If the electrode is used in a pouch cell (including flexible pouch cells), the quality of the electrical contact between the tab and the self-standing electrode (as well as mechanical strength of the connection) can be improved if during the pouch cell assembly at least a part of the contact area between the tab and the electrode is positioned in a heat seal of the enclosure, as shown at
As will be known to those of ordinary skill in the art, the typical enclosure is made of a polymer-coated metal foil. On one side, the polymer is thermoplastic (commonly—some form of polyethylene), on the other—thermally stable polymer. Suitable foils include commercially available foils, including but not limited to those described in U.S. Patent Application No. 62/727,922, entitled “Flexible Lithium-Ion Battery,” filed on Sep. 6, 2018, which is hereby incorporated by reference herein in its entirety. The cell is assembled such that the thermoplastic polymer sides of the enclosure foils face each other. Then a heat sealer is used. The heat sealer squeezes the two enclosure foils between pre-heated dies, and holds under pressure for a pre-set time. The thermoplastic polymer melts. After the dies are released, the thermoplastic solidifies and holds the enclosure foils together. In the so-called soft seal process, the metal dies are covered with a somewhat soft material, which has enough give to allow sealing tab foils and/or wires into the seal. The typical width of the heat seal is 4-6 mm. When connecting tabs to self-standing electrodes according to the present disclosure, additional squeezing during the heat sealing process will improve the contact between the tab and the electrode, and the solidified thermopolymer will prevent them from separating, as well as prevent lateral movements, which can lead to tab breaking off the electrode. In some cases (especially for thick electrodes and tabs), an additional heat seal polymer (commercially available as a strip) might be required for proper sealing.
A protrusion (a protruding member, also referred to as a “member”) of a self-standing electrode can serve as a spot for tab attachment (
The electrodes shown in
A 15 μm-thick commercially available carbon-coated foil was folded over the edge of the electrode, and all further operations were performed using this “sandwich” structure. The aluminum tab (straight edges, 100 μm thick, 5 mm wide) was then folded over the edge of the “sandwich,” and several spot welds were formed through all layers. The tab was then folded outwards from the electrode and secured with additional spot welds. Excess carbon-coated foil was then trimmed.
This written description uses examples to disclose the invention, including the preferred embodiments, and also to enable any person skilled in the art to practice the invention, including making and using any devices or systems and performing any incorporated methods. The patentable scope of the invention is defined by the claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal language of the claims. Aspects from the various embodiments described, as well as other known equivalents for each such aspect, can be mixed and matched by one of ordinary skill in the art to construct additional embodiments and techniques in accordance with principles of this application.
This application claims priority to U.S. Patent Application No. 62/559,254, entitled “Method and Structure for Battery Tab Attachment to a Self-Standing Electrode Without Current Collector or Binder,” filed Sep. 15, 2017, which is incorporated herein by reference in its entirety.
Number | Name | Date | Kind |
---|---|---|---|
3513034 | Teti | May 1970 | A |
3772084 | Scholle | Nov 1973 | A |
5985175 | Fan et al. | Nov 1999 | A |
7094385 | Beguin et al. | Aug 2006 | B2 |
7288870 | Mitcham et al. | Oct 2007 | B2 |
7348101 | Gozdz et al. | Mar 2008 | B2 |
7622059 | Bordere et al. | Nov 2009 | B2 |
7999028 | Lin et al. | Aug 2011 | B2 |
8083905 | Choi et al. | Dec 2011 | B2 |
8084158 | Chu et al. | Dec 2011 | B2 |
8293204 | Khodadadi et al. | Oct 2012 | B2 |
8435676 | Zhamu et al. | May 2013 | B2 |
8465871 | Juzkow | Jun 2013 | B2 |
8628747 | Zachariah et al. | Jan 2014 | B2 |
8703092 | Ziegler | Apr 2014 | B2 |
8787001 | Fleischer et al. | Jul 2014 | B2 |
8825178 | Feng et al. | Sep 2014 | B2 |
8883113 | Richter et al. | Nov 2014 | B2 |
8974960 | Manthiram et al. | Mar 2015 | B2 |
8986872 | Lev et al. | Mar 2015 | B2 |
9034421 | Mikhaylik et al. | May 2015 | B2 |
9167736 | Shah et al. | Oct 2015 | B2 |
9396829 | Mann et al. | Jul 2016 | B2 |
9406985 | Amaratunga et al. | Aug 2016 | B2 |
9450266 | Hosaka et al. | Sep 2016 | B2 |
9502734 | Lim et al. | Nov 2016 | B1 |
9615473 | Kim | Apr 2017 | B2 |
9692056 | Liu et al. | Jun 2017 | B1 |
9711763 | Sohn et al. | Jul 2017 | B2 |
9782082 | Gannon et al. | Oct 2017 | B2 |
9786872 | Suh et al. | Oct 2017 | B2 |
9807876 | Catchpole | Oct 2017 | B2 |
9812681 | Heo | Nov 2017 | B2 |
9859586 | Suh et al. | Jan 2018 | B2 |
9887644 | Kim et al. | Feb 2018 | B2 |
9941492 | Suh et al. | Apr 2018 | B2 |
9972868 | Choi et al. | May 2018 | B2 |
9979225 | Bernhard | May 2018 | B2 |
10033031 | Wang et al. | Jul 2018 | B2 |
10090556 | Rho et al. | Oct 2018 | B2 |
10096803 | Iseri et al. | Oct 2018 | B2 |
10122010 | Tajima et al. | Nov 2018 | B2 |
10147915 | Song et al. | Dec 2018 | B2 |
10199851 | Hiroki et al. | Feb 2019 | B2 |
10217971 | Takahashi et al. | Feb 2019 | B2 |
20030084847 | Wood et al. | May 2003 | A1 |
20030099883 | Ochoa et al. | May 2003 | A1 |
20040086783 | Fong et al. | May 2004 | A1 |
20040234445 | Serp et al. | Nov 2004 | A1 |
20050008778 | Utsugi et al. | Jan 2005 | A1 |
20050063891 | Shaffer et al. | Mar 2005 | A1 |
20050148887 | Reiter et al. | Jul 2005 | A1 |
20050209392 | Luo et al. | Sep 2005 | A1 |
20050221185 | Sakata et al. | Oct 2005 | A1 |
20060039849 | Resasco et al. | Feb 2006 | A1 |
20060078489 | Harutyunyan et al. | Apr 2006 | A1 |
20060116443 | Probst et al. | Jun 2006 | A1 |
20060151318 | Park et al. | Jul 2006 | A1 |
20060245996 | Xie et al. | Nov 2006 | A1 |
20070224106 | Sakakibara et al. | Sep 2007 | A1 |
20070274899 | Wolf et al. | Nov 2007 | A1 |
20080131351 | Wang et al. | Jun 2008 | A1 |
20080210550 | Walther et al. | Sep 2008 | A1 |
20080233402 | Carlson et al. | Sep 2008 | A1 |
20080258117 | Sakakibara et al. | Oct 2008 | A1 |
20090117026 | Shimazu et al. | May 2009 | A1 |
20090142659 | Lai et al. | Jun 2009 | A1 |
20090208708 | Wei et al. | Aug 2009 | A1 |
20090226704 | Kauppinen et al. | Sep 2009 | A1 |
20090274609 | Harutyunyan et al. | Nov 2009 | A1 |
20090286675 | Wei et al. | Nov 2009 | A1 |
20100000441 | Jang et al. | Jan 2010 | A1 |
20100038602 | Plee | Feb 2010 | A1 |
20100112443 | Blomgren et al. | May 2010 | A1 |
20100140560 | Wang et al. | Jun 2010 | A1 |
20100178543 | Gruner et al. | Jul 2010 | A1 |
20100221606 | Nalamasu et al. | Sep 2010 | A1 |
20100276644 | Wolf et al. | Nov 2010 | A1 |
20100285352 | Juzkow et al. | Nov 2010 | A1 |
20100285358 | Cui et al. | Nov 2010 | A1 |
20110060162 | Tatsuhara et al. | Mar 2011 | A1 |
20110111279 | Smithyman et al. | May 2011 | A1 |
20110123429 | Bordere et al. | May 2011 | A1 |
20110150746 | Khodadadi et al. | Jun 2011 | A1 |
20110158892 | Yamaki | Jun 2011 | A1 |
20110171398 | Oladeji | Jul 2011 | A1 |
20110177393 | Park et al. | Jul 2011 | A1 |
20110281156 | Boren et al. | Nov 2011 | A1 |
20110311874 | Zhou et al. | Dec 2011 | A1 |
20120105370 | Moore | May 2012 | A1 |
20120107683 | Kim et al. | May 2012 | A1 |
20120132861 | Tamamitsu et al. | May 2012 | A1 |
20120138148 | Harutyunyan | Jun 2012 | A1 |
20120141864 | Juzkow et al. | Jun 2012 | A1 |
20120149824 | Hooke et al. | Jun 2012 | A1 |
20120177934 | Vogel et al. | Jul 2012 | A1 |
20120193602 | Lieber et al. | Aug 2012 | A1 |
20120241666 | Hong et al. | Sep 2012 | A1 |
20120282522 | Axelbaum et al. | Nov 2012 | A1 |
20120315539 | Lashmore et al. | Dec 2012 | A1 |
20120321911 | Watanabe et al. | Dec 2012 | A1 |
20130040229 | Grigorian et al. | Feb 2013 | A1 |
20130065130 | Ban et al. | Mar 2013 | A1 |
20130106026 | Wang et al. | May 2013 | A1 |
20130149440 | Pyzik et al. | Jun 2013 | A1 |
20130171485 | Kodera et al. | Jul 2013 | A1 |
20130189565 | Lashmore et al. | Jul 2013 | A1 |
20130224551 | Hiralal et al. | Aug 2013 | A1 |
20130256011 | Chang et al. | Oct 2013 | A1 |
20130323583 | Phares | Dec 2013 | A1 |
20140013588 | Wang et al. | Jan 2014 | A1 |
20140021403 | Kim et al. | Jan 2014 | A1 |
20140057178 | He et al. | Feb 2014 | A1 |
20140065447 | Liu | Mar 2014 | A1 |
20140141248 | Noyes | May 2014 | A1 |
20140170490 | Izuhara et al. | Jun 2014 | A1 |
20140255782 | Jabbour et al. | Sep 2014 | A1 |
20140326181 | Kim | Nov 2014 | A1 |
20140370347 | Jung et al. | Dec 2014 | A1 |
20150010788 | Aria et al. | Jan 2015 | A1 |
20150037239 | Sue et al. | Feb 2015 | A1 |
20150044581 | Holme et al. | Feb 2015 | A1 |
20150064521 | Watanabe et al. | Mar 2015 | A1 |
20150087858 | Ci et al. | Mar 2015 | A1 |
20150133569 | Gong et al. | May 2015 | A1 |
20150188112 | Adre et al. | Jul 2015 | A1 |
20150200417 | Song et al. | Jul 2015 | A1 |
20150207143 | Wu et al. | Jul 2015 | A1 |
20150207168 | Do et al. | Jul 2015 | A1 |
20150233010 | Pan et al. | Aug 2015 | A1 |
20150236366 | Chang et al. | Aug 2015 | A1 |
20150243451 | Kim et al. | Aug 2015 | A1 |
20150243452 | Gruner et al. | Aug 2015 | A1 |
20150255828 | Momo et al. | Sep 2015 | A1 |
20150279578 | Martini et al. | Oct 2015 | A1 |
20150325820 | Sohn et al. | Nov 2015 | A1 |
20150333302 | Johns et al. | Nov 2015 | A1 |
20150340684 | Voillequin et al. | Nov 2015 | A1 |
20150340741 | Kim et al. | Nov 2015 | A1 |
20150349325 | Chen et al. | Dec 2015 | A1 |
20150364750 | Maheshwari et al. | Dec 2015 | A1 |
20150380738 | Zhou et al. | Dec 2015 | A1 |
20160013457 | Suh et al. | Jan 2016 | A1 |
20160013458 | Suh et al. | Jan 2016 | A1 |
20160020437 | Sohn et al. | Jan 2016 | A1 |
20160023905 | Wei | Jan 2016 | A1 |
20160036059 | Tokune et al. | Feb 2016 | A1 |
20160040780 | Donahue | Feb 2016 | A1 |
20160049569 | Negrin | Feb 2016 | A1 |
20160079629 | Abe et al. | Mar 2016 | A1 |
20160082404 | Pigos | Mar 2016 | A1 |
20160094079 | Hiroki et al. | Mar 2016 | A1 |
20160126554 | Beneventi et al. | May 2016 | A1 |
20160149193 | Seong | May 2016 | A1 |
20160149253 | Yi et al. | May 2016 | A1 |
20160166837 | Strommer et al. | Jun 2016 | A1 |
20160329533 | Tajima | Nov 2016 | A1 |
20160365544 | Lee et al. | Dec 2016 | A1 |
20160372717 | Noda | Dec 2016 | A1 |
20170005504 | Rho et al. | Jan 2017 | A1 |
20170018799 | Jeong | Jan 2017 | A1 |
20170033326 | Goto et al. | Feb 2017 | A1 |
20170040582 | Kim | Feb 2017 | A1 |
20170155098 | Park et al. | Jun 2017 | A1 |
20170155099 | Song et al. | Jun 2017 | A1 |
20170214052 | Xu | Jul 2017 | A1 |
20170263972 | Rho et al. | Sep 2017 | A1 |
20170288255 | Kim et al. | Oct 2017 | A1 |
20170338439 | Yokoyama | Nov 2017 | A1 |
20170338449 | Rho et al. | Nov 2017 | A1 |
20170338489 | Miwa et al. | Nov 2017 | A1 |
20180026236 | Lee et al. | Jan 2018 | A1 |
20180062417 | Choi et al. | Mar 2018 | A1 |
20180115026 | Mairs | Apr 2018 | A1 |
20180240609 | Park et al. | Aug 2018 | A1 |
20180241081 | Deng et al. | Aug 2018 | A1 |
20180309117 | Zhu et al. | Oct 2018 | A1 |
20190027638 | Masuda et al. | Jan 2019 | A1 |
20190033602 | Lee et al. | Jan 2019 | A1 |
20190036103 | Pierce et al. | Jan 2019 | A1 |
20190088925 | Harutyunyan et al. | Mar 2019 | A1 |
20190099129 | Kopelman et al. | Apr 2019 | A1 |
20190115633 | Akihisa | Apr 2019 | A1 |
20190122464 | Delong et al. | Apr 2019 | A1 |
20190140270 | Wang et al. | May 2019 | A1 |
20190171315 | Park et al. | Jun 2019 | A1 |
Number | Date | Country |
---|---|---|
102482098 | May 2012 | CN |
102593436 | Jul 2012 | CN |
102674316 | Sep 2012 | CN |
102674316 | May 2014 | CN |
204072059 | Jan 2015 | CN |
104752651 | Jul 2015 | CN |
103219467 | Nov 2015 | CN |
103715394 | Jan 2016 | CN |
205375473 | Jul 2016 | CN |
103280846 | Aug 2016 | CN |
106024969 | Oct 2016 | CN |
205697720 | Nov 2016 | CN |
104392845 | Mar 2017 | CN |
104362326 | Aug 2017 | CN |
107086306 | Aug 2017 | CN |
107611340 | Jan 2018 | CN |
108878717 | Nov 2018 | CN |
109088071 | Dec 2018 | CN |
208690415 | Apr 2019 | CN |
106129536 | Jul 2019 | CN |
102017123752 | Mar 2019 | DE |
2 213 369 | Aug 2010 | EP |
2 476 648 | Jul 2012 | EP |
2 835 177 | Feb 2015 | EP |
6-267515 | Sep 1994 | JP |
11-31502 | Feb 1999 | JP |
11-87875 | Mar 1999 | JP |
2005-272277 | Oct 2005 | JP |
2007-49789 | Feb 2007 | JP |
2010-277925 | Dec 2010 | JP |
2015-105208 | Jun 2015 | JP |
2015-521347 | Jul 2015 | JP |
2015-220004 | Dec 2015 | JP |
2016-25077 | Feb 2016 | JP |
2016-31922 | Mar 2016 | JP |
2016-54113 | Apr 2016 | JP |
2016-73196 | May 2016 | JP |
2017-130274 | Jul 2017 | JP |
2017-147222 | Aug 2017 | JP |
2017-162637 | Sep 2017 | JP |
10-2007-0001220 | Jan 2007 | KR |
10-1548465 | Aug 2015 | KR |
10-2016-0047643 | May 2016 | KR |
10-1632109 | Jun 2016 | KR |
10-2016-0114389 | Oct 2016 | KR |
10-2016-0127641 | Nov 2016 | KR |
10-2016-0129440 | Nov 2016 | KR |
10-2016-0129500 | Nov 2016 | KR |
10-1676641 | Nov 2016 | KR |
10-1703516 | Feb 2017 | KR |
10-2017-0036478 | Apr 2017 | KR |
10-2017-0037510 | Apr 2017 | KR |
10-1729702 | Apr 2017 | KR |
10-1765459 | Aug 2017 | KR |
10-1795544 | Nov 2017 | KR |
10-2019-0040554 | Apr 2019 | KR |
WO 2005052053 | Jun 2005 | WO |
WO 2005096089 | Oct 2005 | WO |
WO 2012156297 | Nov 2012 | WO |
WO 2014102131 | Jul 2014 | WO |
WO 2014153465 | Sep 2014 | WO |
WO 2015100762 | Jul 2015 | WO |
WO 2017052248 | Mar 2017 | WO |
WO 2017120391 | Jul 2017 | WO |
WO 2017131451 | Aug 2017 | WO |
WO 2018110933 | Jun 2018 | WO |
WO 2018194414 | Oct 2018 | WO |
WO 2018194415 | Oct 2018 | WO |
WO 2019027147 | Feb 2019 | WO |
Entry |
---|
International Search Report and Written Opinion, issued by International Searching Authority in corresponding International Application No. PCT/US19/49923, dated Jan. 23, 2020. |
Communication issued by the International Searching Authority in corresponding International Application No. PCT/US19/49923, dated Nov. 13, 2019 (PCT/ISA/206). |
Communication dated Jul. 31, 2019, from the European Patent Office in counterpart European Application No. 18194454.7. |
Joo-Seong Kim et al., Supporting Information, A Half Millimeter Thick Coplanar Flexible Battery with Wireless Recharging Capability, Nano Letters 2015 15 (4), 9 Pages Total, (2015). |
Xiong PU et al., “A Self-Charging Power Unit by Integration of a Textile Triboelectric Nanogenerator and a Flexible Lithium-Ion Battery for Wearable Electronics”, Advanced Materials 27, pp. 2472-2478, (2015). |
Extended European Search Report issued in corresponding European Application No. 18184002.6 dated Nov. 30, 2018. |
Extended European Search Report issued in corresponding European Patent Application No. 18194469.5 dated Dec. 4, 2018. |
International Search Report and Written Opinion, issued by International Searching Authority in related International Application No. PCT/US2020/020993, dated Jul. 2, 2020. |
Jenax Inc., Flexible Lithium Polymer Battery J . Flex, Copyright 2014, (6 Pages Total). |
Nanalyze., A Flexible Battery from Blue Spark Technologies, Apr. 8, 2014, (4 Pages Total). |
Panasonic Corp., Panasonic Develops Bendable, Twistable, Flexible Lithium-ion Battery, Sep. 29, 2016, (8 Pages Total). |
ProLogium Technology Co., Ltd., FLCB Flexible Type LCB, Copyright 2015, (6 Pages Total). |
Sebastian Anthony., LG produces the first flexible cable-type lithium-ion battery, ExtremeTech, Aug. 30, 2012, (9 Pages Total). |
The Swatch Group Ltd., A revolutionary battery by Belenos: The Watchmaker Swatch Group Has Signed An Agreement With The Chinese Geely Group For Use Of Its Innovative New Battery., as accessed on May 29, 2019, (3 Pages Total), https://www.swatchgroup.com/en/swatch-group/innovation-powerhouse/industry-40/revolutionary-battery-belenos. |
Vishwam Sankaran., Samsung is reportedly developing a curved battery for its foldable phone, Jul. 4, 2018, (4 Pages Total). |
Xian-Ming Liu et al., “Carbon nanotube (CNT)-based composites as electrode material for rechargeable Li-ion batteries: A review”, Composite Science and Technology, vol. 72, pp. 121-144, (2012). |
Kun Kelvin Fu et al., “Flexible Batteries: From Mechanics to Devices”, 2016 American Chemical Society, ACS Publications, ACS Energy Letters 1, pp. 1065-1079, (2016). |
Sau Yen Chew et al., “Flexible free-standing carbon nanotube films for model lithium-ion batteries”, Carbon 47, pp. 2976-2983, (2009). |
Sheng Xu et al., “Stretchable batteries with self-similar serpentine interconnects and integrated wireless recharging systems” Nature communications 4:1543, DOI: 10.1038/ncomms2553, 8 Pages Total, (2013). |
Shu Luo et al., “Binder-Free LiCoO2/ Carbon Nanotube Cathodes for High-Performance Lithium Ion Batteries”, Advanced Materials 24, pp. 2294-2298, (2012). |
Zhiqian Wang et al., “Fabrication of High-Performance Flexible Alkaline Batteries by Implementing Multiwalled Carbon Nanotubes and Copolymer Separator” Advanced Materials 26, pp. 970-976, (2014). |
Zhlqiang Niu et al., “A “skeleton/skin” strategy for preparing ultrathin free-standing single-walled carbon nanotube/polyaniline films for high performance supercapacitor electrodes”, The Royal Society of Chemistry 2012, Energy & Environmental Science 5, pp. 8726-8733, (2012). |
Communication dated Jan. 6, 2021, from the Japanese Patent Office in related application No. 2020-002545. |
David Schiller, “Development of a Stretchable Battery Pack for Wearable Applications”, submitted by David Schiller, BSc., Johannes Kepler University Linz, Nov. 2019, 28 Pages Total, https://epub.jku.at/obvulihs/content/titleinfo/4605900/full.pdf. |
International Search Report and Written Opinion, issued by International Searching Authority in related International Application No. PCT/US2020/043017, dated Dec. 14, 2020. |
Communication dated Dec. 22, 2020, from the Japanese Patent Office in related application No. 2020-002026. |
A. Weidenkaff et al. “Metal Nanoparticles for the Production of Carbon Nanotube Composite Materials by Decomposition of Different Carbon Sources” Materials Science and Engineering C, vol. 19, pp. 119-123, 2002. |
A.J. Clancy et al., “A One-Step Route to Solubilised, Purified or Functionalised Single-Walled Carbon Nanotunes”, Journal of Materials Chemistry A, pp. 16708-16715, 2015. |
Beate Krause et al., “Disperability and Particle Size Distribution of CNTs in an Aqeous Surfactant Dispersion as a Function of Ultrasonic Treatment Time” Carbon 48, pp. 2746-2754, 2010. |
Chee Howe See et al., “CaCO3 Supported Co—Fe Catalysts for Carbon Nanotube Synthesis in Fluidized Bed Reactors” Particle Technology and Fluidization, vol. 54, No. 3, pp. 657-664, Mar. 2008. |
Communication dated Aug. 26, 2019, from the European Patent Office in related European Application No. 18186402.6. |
Danafar, F. et al., “Fluidized bed catalytic chemical vapor deposition synthesis of carbon nanotubes—A review,” The Chemical Engineering Journal, vol. 155, pp. 37-48, 2009. |
Dunens, O., et al., “Synthesis of Multiwalled Carbon Nanotubes on Fly Ash Derived Catalysts,” Environ. Sci. Technol., vol. 43, pp. 7889-7894, 2009. |
Extended European Search Report issued in related European Patent Application No. 18173644.8 dated Oct. 12, 2018. |
Extended Search Report of related EP Application No. 18 19 4454 dated Jul. 23, 2019. |
Hasegawa Kei et. al., “Lithium Ion Batteries Made of Electrodes with 99 wt% active materials and 1wt% carbon nanotubes without binder or metal foils”, Journal of Power Sources, vol. 321, pp. 155-162, 2016. |
Howard Wang, “Dispersing Carbon Nanotubes Usuing Surfactants” Current Opinion in Colloid & Interface Science 14, pp. 364-371, 2009. |
Hu, Liangbing et al., Thin, Flexible Secondary Li-Ion Paper Batteries, ACS Nano, vol. 4, No. 10, pp. 5843-5848, 2010. |
International Search Report and Written Opinion, issued by International Searching Authority in related International Application No. PCT/US19/49923, dated Jan. 23, 2020. |
International Search Report and Written Opinion, issued by International Searching Authority in related International Application No. PCT/US2020/039821, dated Sep. 30, 2020. |
Kim et al., “A Half Millimeter Thick Coplanar Flexible Battery with Wireless Recharging Capability”, Nano Letters, American Chemical Society, 2015, (8 Pages Total). |
Linqin Jiang et al., “Production of Aqueous Colloidal Dispersions of Carbon Nanotubes”, Journal of Colloid and Interface Science, pp. 89-94, 2003. |
Luo Shu et al., “Binder-Free LiCoO2/Carbon Nanotube Cathodes for High-Performance Lithium Ion Batteries” Advanced Materials, vol. 24, pp. 2294-2298, 2012. |
Sarah Maghsoodi et al., “A Novel Continuous Process for Synthesis of Carbon Nanotubes Using Iron Floating Catalyst and MgO Particles for CVD of methane in a fluidized bed reactor” Applied Surface Science, vol. 256, pp. 2769-2774, 2010. |
The Extended European Search Report issued in related European Patent Application No. 18186402.6 dated Oct. 11, 2018. |
Wang Ke et al., “Super-Aligned Carbon Nanotube Films as Current Collectors for Lightweight and Flexible Lithium Ion Batteries” Advanced Functional Materials, vol. 23, pp. 846-853, 2013. |
Zhao, M.Q. et al., “Towards high purity graphene/single-walled carbon nanotube hybrids with improved electrochemical capacitive performance,” Carbon, vol. 54, pp. 403-411, 2013. |
O.M. Marago, et al., “Optical trapping of carbon nanotubes”, Physica E, 40 (2008), pp. 2347-2351. |
Aminy E. Ostfeld et al., “High-performance flexible energy storage and harvesting system for wearable electronics”, www.nature.com/scientificreports, Scientific Reports, 6:26122,DOI:10.1038/srep26122, (2016), (10 Pages Total). |
Communication dated Jul. 27, 2021, issued by the Korean Intellectual Property Office in related Korean Application No. 10-2020-0005929. |
Sungmook Jung et al., “Wearable Fall Detector using Integrated Sensors and Energy Devices”, www.nature.com/scientificreports, Scientific Reports, 5:17081, DOI: 10.1038/srep17081, (2015), (9 Pages Total). |
Notice of Reasons for Rejection dated Aug. 17, 2021, from the Japanese Patent Office in related application No. 2020-002545. |
Notification of the First Office Action dated Jul. 16, 2021, from the State Intellectual Property Office of People's Republic of China in related Application No. 201710151455.7. |
Communication dated Sep. 26, 2021, issued by the Korean Intellectual Property Office in related Korean Application No. 10-2018-0058433. |
Number | Date | Country | |
---|---|---|---|
20190088925 A1 | Mar 2019 | US |
Number | Date | Country | |
---|---|---|---|
62559254 | Sep 2017 | US |