20230295869
-
Publication Number
20230295869
-
Date Filed
July 26, 20213 years ago
-
Date Published
September 21, 2023a year ago
-
Inventors
- THEIL; Perrine
- POUGET; Emmanuel
- PUILLET; Magali
-
Original Assignees
- Elkem Silicones France SAS
-
CPC
-
-
International Classifications
- D06M15/643
- D06M10/00
- D06M10/10
- D06M11/79
Abstract
The present invention relates to a coating method wherein a silicone composition crosslinkable by polyaddition reactions is used to form a silicone elastomer on an open-work and/or elastic textile medium. The crosslinking of the silicone composition is obtained by irradiating with UV radiation, the source of which is a UV-LED lamp.
Claims
- 1. A method for coating a silicone composition X which is crosslinkable by polyaddition reaction to form a silicone elastomer on an open-work and/or elastic textile medium S, comprising a), b) and c):
a) a silicone composition X which is crosslinkable by polyaddition reactions is provided, comprising:
at least one organopolysiloxane A having, per molecule, at least two C2-C6 alkenyl groups bonded to the silicon,at least one organopolysiloxane B having, per molecule, at least two SiH units, anda catalytically effective amount of at least one hydrosilylation catalyst C, which is activatable by UV irradiation,b) said silicone composition X is deposited continuously or discontinuously on at least one face of said textile medium S, andc) said silicone composition X is crosslinked by irradiation with UV radiation, a source of which is a UV-LED lamp.
- 2. The method as claimed in claim 1, wherein the textile medium S is a lace or an elastic strip.
- 3. The method as claimed in claim 1, wherein the silicone composition X further comprises at least one organopolysiloxane compound A′ having, per molecule, a single C2-C6 alkenyl group bonded to the silicon.
- 4. The method as claimed in claim 1, wherein the silicon composition X additionally comprises a filler D, optionally a mineral filler of silica type.
- 5. The method as claimed in claim 1, wherein the silicone composition X:
does not contain any crosslinking inhibitor; optionally, does not contain I-ethynyl-1-cyclohexanol (ECH); and/ordoes not contain any adhesion-promoting compound.
- 6. The method as claimed in claim 1, wherein the silicone composition X comprises, based on the total weight of the silicon composition X:
from 50% to 90%, optionally from 60% to 87%, of an organopolysiloxane A having, per molecule, at least two C2-C6 alkenyl groups bonded to the silicon,from 0.1% to 10%, optionally from 0.5% to 5%, of an organopolysiloxane B having, per molecule, at least two SiH units,from 2 ppm to 400 ppm, optionally from 5 ppm to 200 ppm, of a hydrosilylation catalyst C (calculated by weight of metal),from 5% to 20%, optionally from 8% to 18% of a filler D, optionally silica, optionally treated with a compatibilizerand optionally from 4% to 20%, optionally from 8% to 18%, of an organopolysiloxane A′ having, per molecule, a single C2-C6 alkenyl group bonded to the silicon.
- 7. The method as claimed in claim 1, wherein the UV-LED lamp used during irradiation (c) emits radiation having a wavelength of 365 nm, 385 nm, 395 nm or 405 nm, optionally 365 nm.
- 8. The method as claimed in claim 1, wherein the crosslinking (c) is carried out at a temperature of between 15° C. and 60° C., optionally between 20° C. and 40° C., and optionally at ambient temperature.
- 9. A textile medium S coated on at least one face with a silicone elastomer which can be obtained by the method as defined in claim 1 .
- 10. A product comprising the coated textile medium S as claimed in claim 9 in the field of clothing, optionally lingerie optionally as lace for one or more of tops, bottoms, or bras, and/or sports clothing, hygiene items, and/or medical devices, optionally compression bandage or dressing.
Priority Claims (1)
Number |
Date |
Country |
Kind |
2008079 |
Jul 2020 |
FR |
national |
PCT Information
Filing Document |
Filing Date |
Country |
Kind |
PCT/FR2021/000081 |
7/26/2021 |
WO |
|