Method For Connecting A Conductor Comprising A Base Metal To A Terminal Element Comprising Copper By Means Of Welding As Well As A Terminal Assembly Produced Thereby

Abstract

A terminal assembly comprises a conductor including a base metal, a terminal element including copper, and a weld seam at which the terminal element is welded to the conductor. The weld seam has a layer including a copper alloy or of a mixture including copper and at least one base metal.

Description

FIELD OF THE INVENTION

The present invention relates to a terminal assembly and, more particularly, to a terminal assembly having a conductor comprising a base metal and a terminal element comprising copper connected to the conductor.

BACKGROUND

For weight and cost reasons, cable harnesses and plug-in connectors are increasingly being miniaturized in the automotive industry. The cable harnesses and the terminal elements in plug-in connectors are traditionally produced from copper or a copper alloy. However, copper is very heavy and is relatively expensive. The automotive industry is increasingly focusing on alternative conductor materials which are lighter and more economical than copper, for example conductors made of base metals.

When connecting conductors comprising a base metal to a terminal element which comprises copper, however, it is difficult to produce a reliable mechanical and electrical connection. Mechanically connecting a conductor and a terminal assembly which consist of different metals or metal alloys is problematic, in particular in view of the strict requirements set for plug-in connectors in the automotive industry. These are exposed to high physical stresses and therefore have to withstand high forces. Further, the connection of a terminal element comprising copper to a conductor comprising a base metal is electrochemically problematic because the point of contact of copper to the base metal is at risk of corrosion. Corrosion not only weakens the mechanical connection, but also makes it difficult to transport charge if the oxide layer formed is insulating.

SUMMARY

A terminal assembly according to the invention comprises a conductor including a base metal, a terminal element including copper, and a weld seam at which the terminal element is welded to the conductor. The weld seam has a layer including a copper alloy or of a mixture including copper and at least one base metal.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will now be described by way of example with reference to the accompanying Figures, of which:

FIG. 1A is sectional side view of an electrical wire;

FIG. 1B is a sectional end view of the electrical wire;

FIG. 1C is a plan view of a plurality of terminal elements;

FIG. 2 is a sectional side view of a terminal assembly including the electrical wire connected to a terminal element;

FIG. 3 is an image of a surface of a coating according to an embodiment; and

FIG. 4 is an image of a surface of a coating according to another embodiment.

DETAILED DESCRIPTION OF THE EMBODIMENT(S)

Exemplary embodiments of the present invention will be described hereinafter in detail with reference to the attached drawings, wherein like reference numerals refer to like elements. The present invention may, however, be embodied in many different forms and should not be construed as being limited to the embodiments set forth herein. Rather, these embodiments are provided so that the present disclosure will be thorough and complete and will fully convey the concept of the disclosure to those skilled in the art.

In the following description, “base metal” should be understood to be all metals which have, in the electrochemical voltage series, a standard electrode potential which is smaller than the standard electrode potential of hydrogen. “Welding” should be understood to mean the permanent connection of components by applying heat and/or pressure. A “coating” is the application of a firmly adhering layer of formless material onto the surface of a carrier material; the layer which arises is the “coating”.

A terminal assembly 18 according to the invention is shown in FIG. 2. The terminal assembly 18 includes an electrical conductor 1 and a terminal element 2 connected to the electrical conductor 1.

The conductor 1, as shown in FIGS. 1A, 1B, and 2, is part of an electrical wire 3 and is disposed in an insulating cover 4. At one end, the cover 4 of the electrical wire 3 is removed so that the conductor 1 is exposed at this end. A region of the exposed conductor 1 which is adapted to be welded to the terminal element 2, as described below, is a conductor weld joint 5. In an embodiment, the conductor 1 is aluminum. The conductor 1 can consist of aluminum or an electrically conductive aluminum alloy. The conductor 1 has a round conductor cross-section 6, shown in FIG. 1B, between 5 and 120 mm². In other embodiments, the conductor cross-section 6 is between 6 and 80 mm² or between 30 and 40 mm². In other embodiments, the conductor 1 can have any n-sided cross-section, such as an oval or any other cross-section.

A pre-stamped strip 7 shown in FIG. 2B has a plurality of terminal elements 2 which have been stamped out of a single a metal sheet. Each terminal element 2, as shown in FIGS. 1C and 2, has a contact section 8 and a terminal section 9. The contact section 8 is the region with which the terminal element 2 is later electrically contacted by a mating plug element, for example as a part of an electrical plug connector. The terminal region 9 is the part with which the terminal element 2 is connected to the conductor 1. The terminal region 9 comprises a terminal weld joint 10 at which the terminal element 2 is welded to the electrical conductor 1.

The terminal element 2 comprises copper and can, for example, be a contact element of a plug-in connector. In order to improve the welding of the terminal element 2 comprising copper to the conductor 1 comprising a base metal, a layer made up of a copper alloy or a mixture comprising copper and at least one base metal is applied at least at a weld joint 5, 10, before the conductor 1 and the terminal element 2 are welded together. In an exemplary embodiment, the terminal element 2 is coated; the terminal section 9 of the terminal element 2 is coated at least in sections, in particular in the region of the terminal weld joint 10.

The coating process is shown in FIG. 1C. A solid coating material 14 is applied. In an embodiment, the coating material 14 is a powder having a particle size up to 60 μm. In other embodiments, the particle size may be 1 to 50 μm or 1 to 35 μm. The coating material 14 can be applied by thermal spraying; in the embodiment shown, the coating material 14 is applied by cold gas spraying. For this purpose, a gas jet 11 is introduced into a spray nozzle 12, heated up in the spray nozzle 12, accelerated and pressed out through the nozzle outlet 13. The coating material 14 is injected into the gas jet 11 as a solid, for example, as a powder. The injected spray particles are accelerated in the gas jet 11 and applied onto the terminal section 9 of a terminal element 2 at a high speed. In this manner, a coating zone 15, within which the spray particles are applied onto the substrate, can be restricted to the desired regions of the terminal element 2. A layer is formed by the spray particles being flattened when they impact on the terminal section 9 and mainly remain adhered by mechanical clamping. The gas jet 11 is in this case generally heated, depending on the method, to temperatures at which the spray particles in the gas jet 11 can be fused, surface-fused, or joined by fusing.

A coating by cold gas spraying, as in the shown embodiment, can be performed continuously. To do so, for example, the coating zone 15 of the nozzle 12 can be guided successively over the terminal weld joints 10 in the pre-stamped strip 7. Alternatively, the coating zone 15 of the nozzle 12 could be stationary and the individual terminal elements 2 within a strip 7 can be successively guided through the coating zone 15.

The coating material 14, in an embodiment, has a mixture comprising copper and at least one base metal. The base metal of the mixture can, for example, be selected from the group comprising zinc, aluminum, tin, iron, nickel, manganese, and oxides of the aforementioned metals. In an embodiment, the coating material 14 is a mixture having alumina powder, zinc powder and copper powder. Such a mixture forms a well-adhering coating on a terminal element 2 as a carrier material.

FIG. 3 shows a scanning electron microscope image of a coating 14 of a mixture made up of 40% zinc powder (purity 96%), 30% alumina powder (purity 99.4%) and 30% copper powder (purity 99.5%). As shown in FIG. 3, both copper and the base metals zinc and aluminum are contained and uniformly distribute in the coating 14.

An alternative coating 14 is shown in the scanning electron microscope image in FIG. 4, in which the powder of a brass alloy was applied by cold gas spraying onto a terminal element 2 having CuSn 0.15 base material. In an exemplary embodiment, the brass powder has a copper content of 70%, a zinc content of 30% and has a particle size smaller than <32 μm. As shown in FIG. 4, both copper and zinc are uniformly distributed in the coating 14 and are applied on the carrier in a well adhering manner. In other embodiments, the zinc content of the brass can be between 10 and 70%, between 20 and 40%, or between 28 and 32%. Instead of brass, it is also possible to use any desired other copper alloy comprising copper and a base metal. For example, a copper alloy selected from the group comprising CuSn, CuZnxSny, CuFe, CuNiSi, CuAlxy can be applied. If coating takes place with brass, the applied brass can have lead or at least one further alloy element. The at least one further alloy element can be selected from the group of aluminum, iron, manganese, nickel, silicon and tin.

After the copper alloy or the mixture has been applied as the coating 16 at least at the conductor weld joint 5 at the conductor 1 and/or at the terminal weld joint 10 at the terminal element 2, the conductor weld joint 5 and the terminal weld joint 10 are brought together and the conductor 1 and the terminal element 2 are welded there. The welding process is shown schematically in FIG. 2 by an arrow 17.

After welding, a terminal assembly 18 shown in FIG. 2 is formed, a weld seam 19 of which has a layer of a copper alloy, or of a mixture comprising copper, and at least one base metal. The conductor 1 and the terminal element 2 can be friction-welded, for example welded by means of ultrasonic welding. For this purpose, a mechanical ultrasonic vibration is generated in the high-frequency range, generally from 20 to 35 kHz, and is introduced into the joining partners, in this case the conductor 1 and the terminal element 2. The high-frequency mechanical vibration leads to heating by boundary friction and results in a serration and hooking of the joining partners. As a result, a mechanically reliable connection can be generated between a conductor 1 comprising a base metal, for example aluminum, and a terminal element 2 comprising copper. The weld connection according to the invention is more reliable and capable of withstanding higher tractive and peeling forces than is the case with a direct welding without the coating according to the invention.

By coating with a copper alloy or with a mixture comprising copper and at least one base metal, a connecting layer is applied at the weld seam 19. This connecting layer improves the connection of the conductor 1 to the terminal element 2 both mechanically and in terms of electrical conductivity. The coating protects the region of the conductor 1 which is connected to the terminal element 2 from the formation of an insulating corrosion layer which impedes the electron transport across the surface as a conductor current from the conductor 1 onto the terminal element 2. The base metal is present together with copper in the applied coating, either in a mixture or a copper alloy, such that corrosion occurs, if at all, at most partially and not across the surface. Furthermore, the coating improves the mechanical connection between the conductor 1 and the terminal element 2 by improving the suitability for welding and the weld connection quality.

Claims

1. A method, comprising: providing a conductor including a base metal and a terminal element including copper;coating at least a weld joint of the conductor and/or the terminal element with a copper alloy or a mixture including copper and at least one base metal; andwelding the conductor to the terminal element after performing the coating step.

2. The method of claim 1, wherein the terminal element is coated in the coating step.

3. The method of claim 1, wherein a solid coating material is applied to form the coating, the coating material being a powder.

4. The method of claim 3, wherein the powder has a particle size of up to 60 μm.

5. The method of claim 4, wherein the particle size is 1 to 50 μm.

6. The method of claim 5, wherein the particle size is 1 to 35 μm.

7. The method of claim 1, wherein the coating step is performed by a thermal spraying process.

8. The method of claim 7, wherein the thermal spraying process is a cold gas spraying process.

9. The method of claim 1, wherein the conductor and the terminal element are friction-welded in the welding step by ultrasonic welding.

10. A terminal assembly, comprising: a conductor including a base metal;a terminal element including copper; anda weld seam at which the terminal element is welded to the conductor, the weld seam having a layer including a copper alloy or of a mixture including copper and at least one base metal.

11. The terminal assembly of claim 10, wherein the conductor includes aluminum.

12. The terminal assembly of claim 11, wherein the conductor consists of aluminum or an aluminum alloy.

13. The terminal assembly of claim 10, wherein the conductor has a conductor cross-section of 5 to 120 mm2.

14. The terminal assembly of claim 13, wherein the conductor cross-section is 6 to 80 mm2

15. The terminal assembly of claim 14, wherein the conductor cross-section is 30 to 40 mm2.

16. The terminal assembly of claim 10, wherein the mixture has at least one base metal selected from the group consisting of zinc, aluminum, tin, iron, nickel, manganese and oxides of the aforementioned metals.

17. The terminal assembly of claim 10, wherein the copper alloy is selected from the group consisting of CuSn, CuZnxSny, CuFe, CuNiSi, CuAlxy and brass.

18. The terminal assembly of claim 17, wherein the copper alloy is brass and a zinc content of the brass is between 10% and 70%.

19. The terminal assembly of claim 18, wherein the zinc content of the brass is between 20% and 40%.

20. The terminal assembly of claim 19, wherein the zinc content of the brass is between 28 and 32%.

21. The terminal assembly of claim 18, wherein the brass includes lead and/or at least one further alloy element.

22. The terminal assembly of claim 21, wherein the at least one further alloy element is selected from the group consisting of aluminum, iron, manganese, nickel, silicon and tin.