The present invention relates to a new method for continuously annealing and preparing a strip of high-strength steel with a view to coating it by hot dipping in a bath of molten metal, preferably by galvanisation or a treatment known as “galvannealing.”
The technical area considered here is that of the galvanisation in continuous motion, in a coating bath of zinc or of a zinc alloy, of high-alloy strips of steel, more particularly HSS steel (high strength steels). These special steels, reputed to be difficult to galvanise, are for example steels that may comprise a level of alloy elements (aluminium, manganese, silicon, chromium, etc.) of up to 2% or more, stainless steels, “dual phase”, TRIP, TWIP (up to 25% Mn and 3% Al), etc. These steel strips are generally intended to be cut and formed at a later stage by pressing, folding, etc. for applications in the construction or automobile sector for example.
It is well known that some steels do not respond well to galvanisation or to a galvannealing treatment given their specific surface reactivity. The ability to galvanise essentially depends on the proper elimination of the residues of rolling oil and on the prevention of excessive surface oxidation before the immersion in the bath of molten metal. Thus, a lack of wettability of molten zinc on shades of high-alloy steels may be encountered during the continuous galvanisation process. This decrease in wetting of zinc is explained by the presence of a layer of selective oxides in the outer layer at the surface of the strip (“outermost surface”). These selective oxides are created by the segregation of the alloy elements and their oxidation by water steam during the continuous annealing prior to the immersion in the bath of zinc. The water steam is generated at this point by the reduction of iron oxide, always present in cold-rolled bars, by the hydrogen contained in the atmosphere of annealing furnaces.
Consequently, there have been attempts to eliminate the selective oxidation on the outside or to make it migrate to the inside of the steel, to 1 or 2 μm beneath the outer layer of the surface, in order to allow the presentation of a layer of practically pure metallic iron to the molten zinc, regardless of the alloy composition and favouring the attachment of the zinc or zinc-alloy coating. This result may be obtained by various methods:
These methods generally entail working under steel-reducing atmosphere during the stage of maintaining at high temperature, which requires a low dewpoint and a high level of hydrogen (up to 75% of the gas of the atmosphere), which is an expensive gas. They all allow to improve the “galvanisability” of high-strength steels with significant but nevertheless insufficient efficiency, above all in the case of some steels with, for example, high silicon levels (about 1.5% by weight). Moreover, the methods requiring pre-deposition are very costly.
According to one example of a method already known in the state of the art, premises for annealing and preparing a steel strip for galvanisation typically comprise in the flow direction of the strip:
Of course, simpler or more complex annealing furnaces are also known that typically comprise between one and four separate sections for achieving the functions of (pre-)heating, temperature maintenance, cooling, overaging, etc., respectively.
The present invention aims to provide a solution that allows to overcome the drawbacks of the state of the art.
In particular, the invention aims to provide a method for annealing and preparing high-strength steels for galvanisation that is more economical, the latter being achieved with or without accompanying heat treatment of a galvannealing type.
The invention also aims to allow the preparation of high-strength steels for galvanisation that are free of brittleness defects.
In particular, the invention aims to provide an annealing method under confined atmosphere that is free of added hydrogen.
One additional aim of the invention is to prevent the selective oxidation of alloy elements in the outermost layer of the strip surface during the total oxidation stage in the course of the continuous annealing preceding cooling and immersion in the bath of zinc.
The present invention relates to a method for the continuous annealing and preparation of a strip of high-strength steel with a view to its hot-dip coating in a bath of molten metal, according to which said strip of steel is treated in at least two sections comprising successively, if considered in the flow direction of the strip:
Complete reduction of the iron oxide should be understood as its reduction of at least 98%.
As an advantage, the controlled oxygen level is maintained in the heating and temperature-maintenance section at between 50 and 400 ppm.
According to a first preferred embodiment of the invention, the oxidising atmosphere is separated from the reducing atmosphere by over-pressurising the oxidising atmosphere so that the oxygen introduced by the strip into the cooling and transfer zone through the airlock completely reacts, because of this overpressure, with the hydrogen contained in the cooling atmosphere by forming steam.
According to a second preferred embodiment of the invention, the hydrogen present in the cooling and transfer section, introduced into the hot gaseous flow directed upstream, is allowed to react with the oxygen coming from the heating and temperature-maintenance section in order to form steam. In this case, the cooling and transfer section is maintained at overpressure compared with the heating and temperature-maintenance section. Since the high-pressure gas cannot escape towards the bath of molten metal, it returns to the heating and temperature-maintenance zone.
According to the invention, the control of the oxygen content of the oxide layer formed in the heating and temperature-maintenance section is obtained either by modifying the gaseous mixture with the combustion air feeding the direct-flame heating means or by controlled injection of the air (or oxygen)/inert gas mixture in the case of radiation or induction heating.
The non-oxidising or inert gas is preferably nitrogen or argon.
As an advantage, the molten metal is zinc or one of its alloys.
As a further advantage, the heating and temperature-maintenance zone is free of any reducing atmosphere.
The method for hot-dip coating is preferably galvanisation or a galvannealing treatment.
Still according to the invention, the atmosphere both in the heating and temperature-maintenance section and in the cooling and transfer section has a dewpoint lower than or equal to −10° C. and preferably −20° C.
According to a preferred embodiment, the strip is heated up to a temperature between 650° C. and 1,200° C., which includes the maintenance temperature.
According to another preferred embodiment, the strip is then cooled to a temperature higher than 450° C. at a cooling speed between 10 and 100° C./s.
One economical method, proposed according to the invention, aims to implement the annealing stage in preparation for galvanisation without the addition of hydrogen, a gas which is ten times as expensive as a more common gas such as nitrogen and which is moreover the cause of serious brittleness defects in strong steels.
The invention aims to achieve perfect galvanisation for all shades of strong steel. To prevent oxidation of the alloy elements on the outermost surface, one proposal is to inject an air/nitrogen mixture into the furnace during the entire cycle of (pre-)heating and maintenance of the bar at high temperature.
This method therefore does not require the separation of the atmosphere in the entire heating/temperature-maintenance part, as is the case in other methods (for example JP-A-2003/342645) where low-pressure reactive zones are incorporated into this part of the furnace.
The oxygen of the air/nitrogen mixture will have the effect of creating two simultaneous and competing reactions in the annealing section:
The alloy elements also participate in the reduction of the iron oxide when they migrate to the steel/iron oxide interface.
The air/nitrogen atmosphere of the heating/temperature-maintenance part must however be separated and partially isolated from the non-oxidising atmosphere of the strip cooling and transfer stages as far as the bath of zinc. To this end, the oxidising atmosphere will preferably be maintained at high pressure compared with the non-oxidising atmosphere in such a way that the oxygen introduced by the bar completely reacts with the hydrogen contained in the atmosphere of the cooling section.
In such a configuration, a steel comprising i.a. 1.2% aluminium will, for example, be heated and annealed to a temperature of 800° C. in an atmosphere with 100 ppm of oxygen in nitrogen. At the end of the temperature maintenance, which lasts one minute, the bar is cooled to 500° C. at a speed of 50° C./s in an atmosphere with 4% hydrogen and 0.1% water steam, which corresponds to a dewpoint of −20° C. This bar is then immersed at a temperature of 470° C. into a bath of zinc with 0.2% aluminium and maintained at 460° C. After a 3-second immersion, the coating is wringed so as to leave an 8-μm zinc layer. Such a zinc deposit is then perfectly wetting and has adherence qualities that are comparable to those obtained for an ordinary low-carbon steel.
To cite another example, the same method may be applied to a steel with i.a. 1.5% silicon. However, in this case, it will be necessary to increase the oxygen level to 300 ppm during the heating/temperature-maintenance stage in order to obtain a comparable result. This increase in the oxygen level is necessary since silicon delays the diffusion of iron by providing a silicon oxide barrier at the steel/iron oxide interface.
Another way of working is to allow the usual flow to establish itself from the bath of zinc to the heating section and to allow the very low level of hydrogen (<0.5%) of the transfer/cooling section to react with the oxygen of the heating/temperature-maintenance part in order to form water steam. Extra oxygen may be added at the exit from the temperature-maintenance section to neutralise the entry of hydrogen, the levels implemented always being positioned very far from the danger zone, i.e. the explosive zone (4% H2 in the air).
Indeed, a high hydrogen level is not necessary in the cooling section since the carbon of the steel will be sufficient to reduce the thin layer of iron oxide created in the heating/temperature-maintenance part and the metallic iron thus prepared will ensure good wettability by zinc during the immersion of the bar in the bath.
To be effective, this method will have to provide a means for controlling the oxygen level in the furnace within the range of 50 to 1,000 ppm. In fact, a too-low level will not allow to create a layer of iron oxide sufficiently impervious to the diffusion of the alloy elements towards the outermost surface and a too-high level of oxygen will produce a too-thick iron-oxide layer that will not be reduced during the cooling and transfer stages leading towards the bath of zinc. This oxygen level will preferably be within a range of 50 to 400 ppm.
The present invention has a certain number of advantages, including in particular the fact that:
| Number | Date | Country | Kind |
|---|---|---|---|
| 2006/0201 | Mar 2006 | BE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/BE2007/000026 | 3/13/2007 | WO | 00 | 7/23/2009 |