Patent Application
20110113830
This invention is directed to a method of scoring and/or separating a brittle material, such as a glass or ceramic material.
One method of cutting a brittle material includes making a mechanical score on a surface of the brittle material. The score can produce a small crack that extends essentially perpendicular to the surface of the material, and may sometimes be referred to as a vent crack or simply vent. Stress applied to the score line, such that a tension stress is produced across the score line (and consequently the vent crack), grows the vent so that it extends across the full thickness of the material, thereby separating the material into several pieces. The stress may be applied, for example, by bending the material, hence a term often applied to the technique is “score and snap”.
The mechanical score and snap method, wherein a score is produced by the mechanical application of a hard scoring wheel or scribe, suffers in that substantial damage is done to the surface, and to some meaningful depth into the brittle material, so that the edges of the separated pieces are weakened by the presence of small cracks or chips produced during the scoring.
To alleviate this damage, laser scoring techniques were developed that used a laser beam to form a score line, after which stress was again applied. According to this technique, a surface of the brittle material was heated by a laser beam. A cooling fluid was then applied to the heated glass, and the accompanying high stress was capable of producing a rupture of the brittle material at the surface thereof and forming a vent crack. Separation occurred after the subsequent application of a bending stress. Variations of the technique include so-called full body separation wherein, instead of first forming a score line, the heating and cooling is sufficient to produce a vent that extends through the full thickness of the brittle material without the application of a subsequent bending stress. While laser scoring has proved to be superior to mechanical scoring, the technique suffers from inconsistencies, largely as a result of the cooling phase.
A method of separating a brittle material, such as a sheet of glass, is disclosed. The method employs a laser to heat the brittle material along a predetermined path, followed by a stream of a cooling fluid, for example, water, produced by a nozzle that cools the heated predetermined path. The nozzle is capable of producing a stream that is substantially columnar (i.e. substantially cylindrical) for at least about 30 mm, preferably in excess of 50 mm. The length of the columnar portion of the stream is referred to as the coherence length of the stream. It has been found that consistency of the separation process, such as in the straightness of the score or cut, uniformity of the vent depth and overall process repeatability can be significantly increased if the coherent portion of the stream contacts the brittle material along the heated predetermined path.
In one embodiment, a method of forming a vent crack in a brittle material comprising heating a surface of the brittle material with a laser along a predetermined path, cooling the heated surface of the brittle material with a coherent stream of cooling liquid dispensed by a nozzle, the stream comprising a coherence length equal to or greater than 50 mm and a diameter in the range from about 70 micrometers to about 150 micrometers and wherein a working distance between the nozzle aperture and the surface of the brittle material is less than the coherence length of the stream.
Preferably, the coherent stream of cooling liquid is formed by a convergent nozzle with a circularly symmetric aperture. In other embodiments the coherent stream of cooling liquid is formed by a nozzle having a straight walled orifice with a circularly symmetric aperture. The working distance between the aperture of the nozzle and the surface of the brittle material is greater than 5 mm, and in some instances can be in excess of 50 mm.
The brittle material may be glass, and in some embodiments is a continuous ribbon of glass, such as might be produced in a fusion downdraw process.
If the brittle material is to be separated by the application of a mechanical stress, the vent crack may comprise a score (score line). In this instance, a tension stress may be produced across the score line by bending, or a tension may be produced by applying a linear force on the material (for example, by applying a pulling force).
In other cases, the vent crack can extend through a full thickness of the brittle material after the cooling such that the brittle material is separated.
Some applications of the method comprise separating a glass ribbon, wherein the ribbon has a temperature that exceeds 300° C. The ribbon may be non-planar, in which case the long working distance (e.g. long coherence length) of the stream allows for cutting and/or scoring without adjusting the position of the nozzle relative to the surface of the ribbon. That is, the distance between the nozzle aperture and the surface of the brittle material varies along the predetermined path, but without significant effect on the character of the formed vent crack.
Preferably, a pressure of the cooling liquid in the nozzle is in a range between about 0.35 kg/cm2 and about 0.70 kg/cm2.
In another embodiment, a method of separating edges of a glass ribbon is disclosed comprising forming a continuous ribbon of glass, the continuous ribbon of glass comprising a viscous region and an elastic region, heating a surface of the continuous ribbon of glass in the elastic region with a laser along a predetermined path. The heated predetermined path is then cooled with a coherent stream of cooling liquid dispensed by a nozzle, the stream comprising a coherence length equal to or greater than 50 mm and a diameter in the range from about 70 micrometers to about 150 micrometers to separate an edge from the continuous ribbon of glass. A working distance between the nozzle aperture and the surface of the continuous ribbon of glass is less than the coherence length of the stream.
In some instances a temperature of the continuous ribbon of glass in the elastic region before the heating is greater than about 300° C. Preferably, the working distance between the nozzle aperture and the surface of the continuous ribbon of glass is greater than about 5 mm. Preferably, the pressure of the cooling liquid in the nozzle is in a range between about 0.35 kg/cm2 and about 0.70 kg/cm2. The nozzle preferably comprises a divergent, circularly symmetric orifice or a straight walled, circularly symmetric orifice
In some embodiment, the continuous ribbon of glass in the elastic region is non-planar.
The invention will be understood more easily and other objects, characteristics, details and advantages thereof will become more clearly apparent in the course of the following explanatory description, which is given, without in any way implying a limitation, with reference to the attached Figures. It is intended that all such additional systems, methods, features and advantages be included within this description, be within the scope of the present invention, and be protected by the accompanying claims.
In the following detailed description, for purposes of explanation and not limitation, example embodiments disclosing specific details are set forth to provide a thorough understanding of the present invention. However, it will be apparent to one having ordinary skill in the art, having had the benefit of the present disclosure, that the present invention may be practiced in other embodiments that depart from the specific details disclosed herein. Moreover, descriptions of well-known devices, methods and materials may be omitted so as not to obscure the description of the present invention. Finally, wherever applicable, like reference numerals refer to like elements.
While laser scoring techniques employing a laser to first heat a brittle material along a predetermined line and wherein the heated zone on the brittle material is immediately cooled by a cooling fluid, are well known in the art. However, while laser scoring is superior to mechanical scoring techniques in terms of the resultant edge strength, they may suffer from inconsistencies in the vent crack formation that can lead to wander of the vent (undesired changes in the vent propagation direction at the surface of the brittle material) and variations in the vent propagation in a direction transverse to the surface. More simply, the depth of the vent crack can vary, resulting in a variation in the quality of the edge surface of the finally separated individual pieces. This inconsistency can be traced to the nature of cooling.
Shown in
A liquid stream 22 produced by a simple nozzle opening goes through at least several phases depicted in
By simple nozzle what is meant is a single, circularly symmetric orifice. Three simple orifices are shown in
Returning to
A long coherence length is useful, for example, when scoring and/or cutting a brittle material having an uneven surface. By employing a stream having a long coherence length enables a long working distance between the nozzle aperture and the work piece (brittle material), and movement of the nozzle as the surface topology varies is unnecessary and facilitates faster scoring and/or cutting speed. For example, working distances in excess of 5 mm may be used, such as a working distance in the range between about 10 mm and 50 mm, in a range between 20 mm and 50 mm, in a range between 30 mm and 50 mm or in a range between 40 mm and 50 mm.
In accordance with one embodiment, a surface of a brittle material is irradiated and heated along a predetermined path with a laser beam produced by a laser, and quickly thereafter cooled with a stream of liquid discharged by a nozzle. The nozzle may be, for example, a simple divergent or straight walled nozzle having a circularly symmetric aperture and orifice. A coherence length of the stream is equal to or greater than 50 mm, and a distance between the nozzle aperture and the surface of the brittle material is less than the coherence length of the stream. A diameter of the coherent stream is in the range between 70 micrometers and 150 micrometers.
The use of a coherent stream of cooling liquid also facilitates accurate scoring and/or cutting of brittle material at high temperature, such as separating the edges from a glass ribbon as the high temperature ribbon is drawn from a forming apparatus. The drawing of a glass ribbon is well known in the art, and will not be described in detail, however, such methods include float methods, downdraw methods including fusion downdraw and slot draw, and up draw methods.
In an exemplary fusion downdraw method, illustrated in
It should be emphasized that the above-described embodiments of the present invention, particularly any “preferred” embodiments, are merely possible examples of implementations, merely set forth for a clear understanding of the principles of the invention. Many variations and modifications may be made to the above-described embodiments of the invention without departing substantially from the spirit and principles of the invention. All such modifications and variations are intended to be included herein within the scope of this disclosure and the present invention and protected by the following claims.