Patent Application
20140352717
The invention relates to a method for decomposing an oxide layer containing chromium, iron, nickel, and optionally zinc and radionuclides using an aqueous oxidative decontamination solution containing permanganic acid and a mineral acid, flowing in a circuit (K1), wherein the oxidative decontamination solution is adjusted to a pH≦2.5, especially for decomposing oxide layers deposited on the interior surfaces of areas or components of a nuclear power plant.
The invention particularly relates to a method for extensive decomposition of the radionuclides in the primary system and the auxiliary system in a nuclear power plant using the available operating medium and the operating system of the power plant itself.
During the generating operation of a PWR (pressurized water reactor) nuclear power plant, with an operating temperature of >180° C. and reducing conditions on the interior surfaces of the systems and components wetted by the medium, oxidic protective layers (Fe0.5Ni1.0Cr1.5O4, NiFe2O4) are formed. In this process, radionuclides are incorporated into the oxide matrix as well. The goal of chemical decontamination methods is to break down this oxide layer in order to remove the incorporated radionuclides. The goal of this procedure is to minimize the radiation exposure of the maintenance staff in case of a maintenance operation insofar as possible, or in the case of dismantling of the nuclear reactor, to allow the components to be returned to a recycling program without problems.
The oxide protective layers are not removable chemically based on their composition and structure. Using a prior oxidative chemical treatment of the oxide structure, these can be broken up and the difficult-to-dissolve oxide matrix converted to readily soluble metal oxides. This breaking up of the oxidized matrix is done by oxidation of the trivalent chromium to hexavalent chromium:
Fe0.5Ni1.0Cr1.5O4/NiFe2O4/Fe3O4→Oxidation→CrO42−,FeO,NiO,Fe2O3 Equation (1)
Throughout the world, so-called permanganate preoxidation according to equation (2) has become used as an oxidation treatment, wherein the following three oxidation treatments are available:
“NP” oxidation=nitric acid+potassium permanganate (nitric acid,permanganate) (see, for example, EP-B-0 675 973)
“AP” oxidation=sodium hydroxide+potassium permanganate (alkaline,permanganate) “HP” oxidation+permanganic acid (see, for example, WO-A-2007/062743),
Mn-VII+Cr-III→Mn-IV+Cr-VI (Equation 2)
The manganese ion is present in permanganate at an oxidation number of 7 and is reduced to an oxidation number of 4 according to equation (2), while at the same time the chromium, present in the trivalent oxidation state, is oxidized up to an oxidation number of. 6. According to equation (2), 2 mol MnO4− are required for the oxidation of 1 mol Cr2O3,
Chemical decontamination of an entire primary system including all activity-carrying auxiliary systems was previously performed only in a few nuclear power plants. In recent years about 50 different decontamination methods were developed worldwide. Of all these methods, the only technologies that became widely used were those based on initial preoxidation with permanganates (MnO4−), e.g., (EP 0 071 336, EP 0 160 831 B1, EP 242 449 B1, EP 0 355 628 B1, EP 0 753 196 B1, EP 1 082 728 B1).
Available chemical decontamination methods are fundamentally performed with the following process sequence at this time:
Step I: preoxidation step
Step II. reduction step
Step III. decontamination step
Step IV: decomposition step
Step V: final cleanup step.
All methods use permanganate (potassium permanganate, permanganic acid) for preoxidation (I.) and oxalic acid for reduction (II.). The methods only differ in the decontamination step (III.). Different chemicals and chemical mixtures are used here.
The decontamination methods to date are based on the previously explained concept. The poorly soluble oxide protective layers are converted in a preoxidation step into more readily soluble oxide compounds and remain on the surface of the system. Therefore no removal of activity from the systems to be decontaminated takes place during the preoxidation. No decrease in the radiation dose rate takes place during this time phase of decontamination with existing methods.
Only after the second process step (II.) of the reduction of the permanganate and the manganese dioxide formed with oxalic acid and in the decontamination step (III.) are the oxides dissolved and the dissolved cations/radionuclides removed and bound to ion exchange resins.
During the preoxidation (I.) in all previously used decontamination technologies, manganese oxyhydrate [MnO(OH)2] and manganese dioxide (MnO2) form, as is clearly shown by equations (3) and (4).
2MnO4−+Cr2O3+H2O→2MnO(OH)2+2CrO42−+H2O
2MnO(OH)2→2MnO2+2H2O (Equation 3)
4KMnO4+4HNO3+2Cr2O3+4H2O→4MnO(OH)2+4KNO3+2H2Cr2O7
4MnO(OH)2→4MnO2+4H2O (Equation 4)
The manganese dioxide is insoluble and deposits on the inner surface of the components/systems. With increasing manganese oxyhydrate/manganese dioxide deposition, the desired oxidation of the oxidic protective layer is impeded. In addition the converted iron and nickel oxides remain undissolved on the surface, so that the barrier layer on the surface is further thickened.
At the end of the preoxidation step, the following new chemical compounds, introduced or formed in process step (I.), are present:
In the preoxidation solution: KMnO4, NaOH or HNO3, colloidal MnO(OH)2, CrO42− and Cr2O72−.
Thus at the end of the preoxidation step, all metal oxides including the radionuclides are still present in the system to be decontaminated. Part of the manganese oxyhydrate formed [MnO(OH)2] was carried into system areas without flow passing through and can no longer be carried out/removed in the subsequent process steps.
According to the prior art, no decrease in radioactivity occurs, thus no decontamination, occurs during oxidation of the oxide layer, since practically no cations that could be removed with the aid of the cation exchanger are dissolved out of the oxide layer. Instead the breakdown of the oxide layer is accomplished in a second process step with the aid of oxalic acid, preceded by a reduction step for reducing excess permanganic acid and manganese oxyhydrate. Only after these process steps are cations removed from the cleanup solution (decontamination solution) by ion exchange.
The goal of the present invention is that of avoiding the drawbacks of the prior art, especially permitting simplification of the process sequence, wherein the formation of manganese dioxide and oxalate is to be avoided. The formation of CO2 should at least be reduced. The release of oxidic particles also should be largely avoided.
According to the invention the goal is essentially accomplished in that the oxidation of the oxide layer and its dissolution takes place in a single treatment step with the aid of the aqueous decontamination solution, that sulfuric acid is used as the mineral acid for adjusting the pH, and that after decomposition of the permanganic acid, while maintaining the circulation, the solution flows over a bypass line of the circuit to a cation exchanger in which divalent cations and divalent radionuclides present in the solution are fixed, with simultaneous liberation of sulfate and dichromate anions.
According to the invention it is intended that the pH be established at the beginning of the process sequence by addition of sulfuric acid. During the oxidative decomposition of the layer and the process steps performed in this connection, no further addition of sulfuric acid is required.
In particular it is intended that after enrichment of the solution with dichromic acid at a predetermined concentration, especially 300 ppm or less, preferably 100 ppm or less, the solution will flow over a bypass line to an anion exchanger in which the dichromate will be fixed with simultaneous liberation of the SO4− ions.
In this process the quantity of anion exchange resin used is adapted to the quantity of dichromate ions to be fixed.
According to the invention it is planned for the permanganate concentration in the oxidative decontamination solution to be adjusted such that after the predetermined dichromate concentration has been reached, the permanganate ions will have been consumed by chemical oxidation reactions, wherein in particular the following equation is applicable:
Total consumption of HMnO4 [kg]=Cr-III load [kg]×U
According to the invention a method for breaking down the radioactivity load in components and systems is provided, wherein the oxide layers of the inner surfaces wetted with the medium are removed with an oxidative decontamination solution. In this process the oxidative decontamination can be performed with the power plant's existing systems without the aid of auxiliary external decontamination systems, the reduction of activity can take place without formation of manganese dioxide and precipitation of other cations as well as without production of CO2 and without release of oxide particles, and the metal oxides can be simultaneously dissolved chemically and fixed as cations/anions together with the manganese and the nuclides (Co-60, Co-58, Mn-54, etc.) on ion exchange resins.
In contrast to the decontamination concepts described in the preceding, according to the invention the chemical transformation of the poorly soluble oxides to readily soluble oxides, the dissolution of the oxides/radionuclides and the removal and fixing of the dissolved cations on cation exchangers takes place in a single process step, which is known as the oxidative decontamination step.
Furthermore and in contrast to the prior art, according to the invention in the course of the preoxidation step the permanganic acid introduced is completely converted to the Mn2+ cation. Manganese oxyhydrate precipitation does not take place.
Five equivalents (electrons) are made available for oxidation of Cr2O3 through the reaction of Mn-VII to Mn-II. This means that almost twice the quantity of Cr2O3 can be oxidized to chromate/dichromate according to the teaching of the invention compared with the previous decontamination methods.
In the previous permanganate-based decontamination concepts, for each 100 g permanganate ions used:
For the decontamination concept according to the present invention, per 100 g of permanganate ions used
In contrast to the previous decontamination methods, only the following chemical compounds resulting from the oxidative decontamination step remain in the system:
The continuing presence of H2Cr2O7 and H2SO4 is advantageous since both of these compounds are consumed in the remaining process sequence and thus they are desirable in the process technology. The dichromate protects the basic material of the system and the component from chemical attacks, and the sulfuric acid guarantees the low pH value required over the entire process, as is also illustrated based on
The hematite (Fe2O3) remaining in the system cannot be dissolved by mineral acids with oxidative properties (for example, nitric acid). Therefore in a subsequent step, a so-called hematite step, the Fe2O3 is dissolved and then the dissolved Fe ion is bound to cation exchangers.
According to the teaching of the invention both the pH and the permanganic acid and the proton source (sulfuric acid) are balanced with respect to one another according to a fixed logistical scheme in such a way that during the performance of the oxidative decontamination step:
The formation of manganese dioxide described in the preceding by NP, AP and HP oxidation is avoided according to the invention by using permanganic acid in the acid range (pH≦2.5, preferably pH≦2.2, especially pH≦2). The Mn2+ formed in the acid medium in accordance with the invention is already removed from the solution by cation exchangers during the oxidative decontamination step according to equation (5):
a) 6HMnO4+5Cr2O3+2H+
6Mn2++5Cr2O72−+4H2O Equation (5)
b) Mn2++H2KIT
[Mn2+KIT]+2H+
According to the invention the chemical reaction corresponding to equation (5) definitely leads to the formation of Mn2+. The reaction is proton (H+ ion)-controlled.
If not enough protons (H+) are available in the course of the oxidative decontamination step, the chemical reaction proceeds according to equations (3) and (4). Manganese oxyhydrate/manganese dioxide forms as the final product.
According to the present invention the required pH of <2.5, preferably ≦2.2, preferably pH≦2.0 is established with additional sulfuric acid. Of all the available mineral acids, sulfuric acid meets the requirements for the decontamination process according to the invention, such as
Because of the characteristics listed above, sulfuric acid remains available at the end of the oxidative decontamination step for use in successive steps.
The oxides (NiO, Ni2O3, FeO) are already dissolved by sulfuric acid during the oxidation step.
If another mineral acid should be suitable in place of sulfuric acid for accomplishing the method according to the invention, such a mineral acid will also be covered by the invention.
According to the present invention, sulfuric acid will be used for the pH adjustment. The quantity of sulfuric acid required to avoid MnO(OH)2 formation is based on the permanganate concentration. With increasing permanganate concentration, the pH must be reduced, i.e., a higher acid concentration must be set (see
The following pH values may be taken as guidelines:
In accordance with the present invention, depending on the permanganate content of the solution, the sulfuric acid requirement can be calculated as follows by way of the pH:
The calculation of the H2SO4 requirement without including the dissolved cations is performed according to equations (6 and 7);
pH=X−[(mg/kg HMnO4 used)×9E-05] Equation (6)
mg/kg H2SO4═Y×pH−Z Equation (7)
During the performance of the oxidative decontamination step, the concentration of free protons (H+) is reduced by the formation of metal sulfates. The quantities of dissolved Fe, Ni, Zn, and Mn cations are therefore included in the determination of the additional mineral acid requirement according to the following formula:
Mg SO4−2/liter=[mg cation/liter]*[cation-specific factor].
The calculation of the H2SO4 requirement including the dissolved cations is performed according to equation (7′).
mg/kg H2SO4=[y×pH−z]+[(K1*F1)+(K2F2)+ . . . (Kn*Fn)] Equation (7′)
wherein K1, K2 . . . Kn respectively represent mg cation/liter and F1, F2 . . . Fn is the specific factor of the respective cation.
The following applies for the cations below:
Appreciable Zn fractions are present in the protective layer when the so-called Zn operating mode is carried out in the power operation of the nuclear power plant.
Depending on the Fe/Cr/Ni/Zn composition of the protective layer, according to the present invention, depending on the quantity of HMnO4 used, in each case it is possible to calculate in advance the exact quantities of the individual cations released in the oxidative decontamination step. This is possible since the HMnO4 quantity used is 100% converted into Mn2+ and the quantity of dichromate generated is formed stoichiometrically. The quantity of oxidized Cr-III in turn gives the amount of Fe—/Cr—/Ni—/Zn oxides converted and thus Fe—/Ni—/Zn—/Mn ions produced in the oxidative decontamination step.
During the oxidative oxide conversion and the simultaneously proceeding dissolution of the new oxide structures, the system to be decontaminated is operated in a circuit without the involvement of an ion exchanger. This will be explained theoretically on the basis of
Calculation of the quantity of the dissolved cation and the remaining Fe2O3 is performed according to the following formulas as a function of the quantity of permanganic acid used and the composition of the oxide matrix:
Cations dissolved in the oxidative decontamination step according to HMnO4 quantity introduced:
[g] Fe-II=[g HMnO4 quantity introduced]×0.72×[wt % Fe]/[wt % Cr]×0.33
[g] Ni-II=[g HMnO4 quantity introduced]×0.72×[wt % Ni]/[wt % Cr]
[g] Zn-II=[g HMnO4 quantity introduced]×0.72×[wt % Zn]/[wt % Cr]
[g] Mn-II=[g HMnO4 quantity introduced]×0.46.
Iron oxide transformed to Fe2O3 in the oxidative decontamination step per HMnO4 addition is dissolved in the hematite step:
[g] Fe2O3=[HMnO4 quantity introduced]×0.72×[wt % Fe]/[wt % Cr*]×0.67×1.43
According to the invention the quantity of HMnO4 introduced determines the quantity of the oxide layer that can be released from the oxide matrix of the Fe/Cr/Ni protective layer.
According to the present invention a maximum permanganic acid concentration of 150 ppm per oxidative decontamination step is to be used, which is correspondingly repeated as a function of the previously determined or estimated chromium concentration, as was explained in the preceding.
To minimize the required use of sulfuric acid—also called merely mineral acid in the following—the oxidative decontamination step is preferably conducted with an HMnO4 concentration of ≦50 ppm HMnO4. The following chemical partial reactions take place during the oxidative decontamination step:
Oxidation and dissolution of Cr2O3 bound in the protective layer (Fe0.5Ni1.0Cr1.5O4):
6HMnO4+5Cr2O3+6H2SO4→6MnSO4+5H2Cr2O7+4H2O Equation (8)
Through the oxidation of the Cr-III oxide to water-soluble dichromate, Ni is released from the composite protective layer and is then present as Ni-II-oxide (NiO) or Ni-III-oxide (Ni2O3). Then the Ni oxides are dissolved in an intermediate step by HMnO4 and formation of Ni(MnO4)2 according to equation (9):
NiO+2HMnO4+5H2O→[Ni(MnO4)2×6H2O] Equation (9)
With increasing HMnO4 consumption, relocation of the Ni-II from Ni-permanganate to Ni-dichromate (equation 10) or Ni-sulfate (equation 11) occurs.
[3Ni(MnO4)26H2O]+5Cr2O3+2NiO+6H2SO4
6MnSO4+5NiCr2O7+12H2O Equations (10)
NiCr2O7+H2SO4→NiSO4+H2Cr2O7 Equation (11)
Through the oxidation of Cr-III oxide with formation of water-soluble dichromate, additional Fe is released from the oxide matrix and is then present as Fe-II oxide (FeO) or Fe-III oxide (Fe2O3). FeO is easily dissolved by sulfuric acid (equation 12). Fe2O3 on the other hand is not sufficiently dissolved by sulfuric acid and therefore remains in the system and is dissolved in the subsequent process step that was mentioned, the hematite step (see below) and fixed on cation exchange resins.
FeO+H2SO4→FeSO4+H2O Equation (12)
To speed up the oxidative decontamination step, a process temperature of 60° C. to 120° C. is preferably established.
In accordance with the present invention the oxidative decontamination preferably takes place in a temperature range of 95° C. to 105° C.
After conversion of the permanganate has taken place according to equations (8) to (12), the connection of the special, power plant-specific cation exchanger is performed (KIT).
This will also be illustrated on the basis of
The prerequisite for connecting in the cation exchanger is that the permanganate has been converted completely or essentially completely to Mn2+ and the solution is free from MnO4− ions (guideline value <2 ppm MnO4).
During the operation of the cation exchanger KIT, the divalent cations (Mn-II, Fe-II, Zn-II and Ni-II) as well as the divalent radionuclides (Co-58, Co-60, Mn-54) are removed from the solution. At the same time the corresponding anions (sulfate and dichromate) are released and are again available to the process. See equations (13) and (14).
Release of the sulfate with formation of sulfuric acid:
MnSO4+H2KIT→H2SO4+[Mn2+-KIT]
NiSO4+H2KIT→H2SO4+[Ni2+−KIT]
FeSO4+H2KIT→H2SO4+[Fe2+-KIT]
Fe(SO4)3+3H2KIT→3H2SO4+[Fe3+-KIT] Equation (13)
Release of the dichromate with formation of dichromic acid:
NiCr2O7+H2KIT→H2Cr2O7+[Ni2+-KIT] Equation (14)
The cation exchanger KIT is operated at a process temperature of ≦100° C.
The cation exchanger KIT is operated until all dissolved cations are fixed on the cation exchange resin.
In accordance with the present invention, after the cation cleanup has been performed, permanganic acid is again added and the previously-explained process steps are repeated until the dichromic acid concentration has reached a prespecified value such as 300 ppm or less.
In
This sequence (
The maximum dichromic acid concentration is preferably limited to 100 ppm.
Once the specified dichromic acid concentration has been reached, the dichromate is removed from the solution with the anion exchanger AIT (see FIG. 6—cleanup circuit K3).
The prerequisite for inclusion of the anion exchanger is that all permanganate ions have been consumed by the chemical oxidation reaction and the solution is free from permanganate ions (see FIG. 6—cleanup circuit K3).
The quantity of the anion exchanger used is based on the dichromate load in the solution to be cleaned up. Only an amount of anion exchanger is made available, the capacity of which is sufficient for uptake of the dichromate. In this way it is ensured that the sulfuric acid concentration in the solution does not change.
In the first phase of the anion exchanger cleanup, both the sulfate ions of the sulfuric acid and the dichromate ions of the dichromic acid are bound to the anion exchange resins. Once the anion exchange resin is 100% loaded with dichromate and sulfate, upon further loading of the anion exchanger with sulfate ions and dichromate ions, the already-fixed sulfate ions are displaced by dichromate ions. This process continues until the anion exchanger is 100% loaded with dichromate ions and all sulfate ions are once again available for oxidative decontamination.
If the dichromate ions are removed from the solution, permanganic acid is once again added and the process starts again as described previously (
The repetition of the step sequences is continued until no further cation expulsion takes place. If, after execution of the previous sequences, all cations and anions are fixed on ion exchangers, only sulfuric acid is still present in the solution.
It is customary according to the prior art, after preoxidation is complete, to reduce the excess permanganate with oxalic acid (step (II.) and then initiate the decontamination step (step III.) by addition of further decontamination chemicals.
At the time of the reduction (step II.) in these methods, all constituents of the preoxidation step (residual permanganate, colloidal MnO(OH)2, chromate and nickel permanganate) as well as all transformed metal oxides on the system and component surface are still present in the solution.
Since the metal ions can be present, partially in dissolved form (MnO4−, CrO42−) and as readily soluble metal oxides (NiO, FeO, MnO2/MnO(OH)2), even during the second process step of the reduction (step II.), high cation contents appear in the solution.
At the same time, as a result of reduction of the permanganate, chromate and manganese dioxide with the oxalic acid, large amounts of CO2 form (see equation (15)). This CO2 formation occurring on the surface leads to mobilization of oxide particles, which then deposit in regions of the system with little flow and lead to an increase in the dose rate there.
2HMnO4+7 H2C2O4→2MnC2O4+10CO2+8H2O
MnO2+2H2C2O4→MnC2O4+2CO2+2H2O
Cr2O72−+3H2C2O4+8(H3O)+→2Cr3++6CO2+15H2O Equations (15)
The release of oxide particles described in the preceding does not occur with the invention. At the time of the oxalic acid addition both the solution and the system surface are free from permanganate, manganese dioxide and chromate/dichromate. The unwanted CO2 evolution and release of oxide particles do not occur.
The oxalate compounds formed from divalent cations and the reduction chemical oxalic acid have only limited solubility in water. Depending on the process temperature, the solubility of the divalent cations is:
It can be calculated that large quantities of cations are released during a primary system decontamination using the previous decontamination methods in each decontamination cycle. Even during the reduction step this results in oxalate precipitation on the inner surfaces of the system.
The oxide protective layers of a primary system of a pressurized water nuclear power plant usually provide an overall oxide load of 1,900 kg to 2,400 kg [Fe,Cr,Ni-oxide].
In the decontamination of a primary system of a pressurized water reactor, therefore, the following maximum cation releases must be anticipated:
During the primary system decontamination 3 decontamination cycles are usually performed. At an overall volume of about 600 m3 and a uniform distribution of cations over 3 cycles, the following concentrations of divalent cations per cycle are to be expected:
This rough calculation shows that in all previous decontamination methods which use oxalic acid for reduction and/or decontamination, formation of Fe2+ and Ni2+ oxalates cannot be avoided.
As was previously discussed, if oxalate residues remain in the system after the end of a decontamination cycle, more permanganate must be used in the next cycle, as equations (16) show:
3NiC2O4+2HMnO4+H2O
3NiO+2MnO(OH)2+6CO2
3FeC2O4+2HMnO4+H2O
3FeO+2MnO(OH)2+6CO2 Equation (16)
With no improvement in the decontamination result, this leads to a higher permanganate demand and consequently to increased MnO(OH)2 deposition on the surfaces and ultimately to a higher production of radioactive waste. In addition the cation carryover into the following cycle increases, the risk of further oxalate formation rises, and the amount of ion exchange resins is increased again.
The already dissolved radionuclides (Co-58, Co-60, Mn-54) are incorporated into the oxalate layer. This leads to recontamination in the systems.
As was previously described, according to the present invention the divalent cations released (Ni, Mn, Fe, Zn) and the dichromate are present in dissolved form in the oxidative decontamination step and the fixation of the cations and anions takes place at a nearby time on the ion exchange resin. The oxalate deposition that previously occurred during performance of chemical decontamination does not take place.
At the end of the oxidative decontamination step sequences, the hematite step is performed. In this process step the hematite (Fe2O3) is dissolved according to equation (17):
Fe2O3+6H2C2O4→2[Fe(C2O4)3]3−+3H2O Equation (17)
Because of the sulfuric acid underlayering, the solubility of the Me-II oxalates in the hematite step is distinctly higher than in the other decontamination technologies.
The formation of oxalates and their deposition on the interior surfaces of the system does not take place because of the low Me-II cation concentrations and the distinctly higher solubility of the Me oxalates.
The oxalic acid concentration in the hematite step should be 50 to 1000 ppm H2C2O4.
An oxalic acid concentration of ≦100 ppm should preferably be established.
During the hematite step, the dissolved cations are bound to cation exchangers. Here, the dissolution of the hematite and the fixation of the dissolved Fe ions are performed simultaneously (see FIG. 4—Phases of the Hematite Step).
The hematite step is continued until no further iron is removed from the system.
After the end of the hematite step, the oxalic acid remaining in the solution is decomposed with permanganic acid, forming carbon dioxide (equation 18)).
5H2C2O4+2HMnO4+2H2SO4→2MnSO4+10CO2+8H2O Equation (18)
Following performance of the hematite step, the total step sequence of oxidative decontamination can be repeated. This repetition is directed toward residual Cr2O3 still to be digested in the system. After the second oxidative decontamination step, another hematite step is performed.
Each nuclear power plant has its own specific oxide structure, oxide composition, dissolution behavior of the oxides and oxide/activity load. Only assumptions can be made in planning a decontamination. Only during performance of the decontamination will it then be found whether the assumptions initially made were correct.
Therefore a decontamination concept must be capable of being adapted to the respective changes during its performance.
With the present invention it is possible to react systematically to all conceivable new requirements. The detailed steps shown above can be repeated as necessary depending on the type and quantity of the oxide/activity load present in the system.
Decontamination according to the present invention requires only low chemical concentrations compared to the previous process technologies. The required quantities of chemicals therefore can be added with the built-in metering systems already present in nuclear power plants (NPP), and the cations obtained can be removed using the cleanup system already present in the NPP (cation exchanger). No large external decontamination equipment need be installed.
By controlling the overall process from the power plant control room of the nuclear power plant, the process parameters can be quickly adapted to any new requirements (chemical addition rate, chemical concentrations, process temperature, time of KIT and AIT exchanger connection into the circuit, sequence of steps, etc.).
If necessary the process variations can be continued until the desired activity removal or the desired reduction in dose rate has been achieved.
The sulfuric acid present in the solution remains in solution during the performance of all process steps. The concentration is not changed. Only at the end of the overall decontamination performance are the sulfate ions bound to the anion exchanger AIT during the final cleanup (see
Additional details, advantages and features of the invention can not only be obtained from the claims—individually and/or in combination—but also from the drawings, described previously and also explained further below, which are self-explanatory.
The drawings show the following:
It is clear from
Then once again permanganic acid is added to the solution, which is no longer flowing through the cation exchanger, corresponding to the Cr−3 oxide to be oxidized. Addition of sulfuric acid is not necessary as long as the quantity per kg solution is calculated according to equations (7) and (7′). After the dichromic acid concentration has reached a predetermined value, the solution flows over the bypass through the anion exchanger AIT, in which dichromate ions are fixed in the previously described manner. Then sulfuric acid and hematite remain in the solution.
The hematite is removed from the solution according to
In process step D1, chemical conversion of the low solubility Fe, Cr, Ni structure into readily soluble oxide forms takes place with the aid of permanganic acid. The dissolution of the converted oxide forms is achieved with sulfuric acid. In terms of process technology, this is performed in a circulating operation K1 (
During phase D2—just as during phase D1—the circulating operation K1 is maintained unchanged and the connection of the cation exchangers is done in bypass operation. The cleanup rate (flow rate) through the cation exchanger (m3/h) relative to the total volume of the system to be decontaminated [m3] is predetermined from the respective system design of the nuclear power plant. The bypass operation K2 with ongoing circulation operation K1 of the cation exchanger is continued until all cations are bound to the cation exchanger KIT. The total time required for this is predetermined by the available cleanup rate.
After the end of phases D1 and D2, a process technology hold point is provided. The further process steps are directed toward the total oxide content of the system to be decontaminated. If large amounts of chromium are present in the oxide matrix, it is advisable to repeat phases D1 and D2. This repetition process D1+D2 can be continued until the dichromate concentration in the decontamination solution has reached a value of, for example, 100 ppm dichromate. Then process step D3 follows. At the time of phase D3, sulfuric acid and dichromic acid are present in the decontamination solution. The dichromic acid is removed from the solution by means of bypass operation of an anion exchanger. During phase D3 the circulating operation K1 of the system to be decontaminated is operated further without change. The addition of the anion exchange circuit K3 is done in bypass operation. The bypass range of the cation exchange circuit K2 can also be further operated. The bypass operation K3 of the anion exchanger is continued until the dichromate ions are bound to the anion exchanger AIT. The time required for this is determined by the available cleanup rate. The reduction of the dichromate concentration is advantageously continued up to a final concentration of less than 10 ppm. Through the persistence of small quantities of dichromate in the solution, the properties of dichromate for protecting the base material are maintained.
After the end of phase D3, a second process technology hold point is programmed. In the course of the hold point 2, the further procedure is determined, including the considerations described below. The additional process steps are directed toward the total oxide load of the system to be decontaminated. If a large oxide load is present, the process sequence D1 to D3 must be repeated several times before the hematite step is initiated, wherein the number of sequences D1 to D3 is preferably limited to a maximum of 4 times. In the hematite step, designated as phase D4, the hematite Fe2O3 produced in the oxidative decontamination step is dissolved in a sulfuric acid-oxalic acid solution. At the same time, fixation of the dissolved iron on the cation exchanger KIT takes place. Sulfuric acid and oxalic acid are again released from the beginning by cation withdrawal, and are continuously available for the hematite solution process. During the total phase D4 both the circulating operation K1 of the system to be decontaminated and the cation exchange circuit K2 are operated. The connection of the cation exchange circuit K2, in which the iron is fixed, takes place in bypass operation. The hematite dissolution phase, thus phase D4, is operated until no further appreciable iron removal takes place.
In the subsequent process step D5, in which sulfuric acid and oxalic acid are present, the oxalic acid is degraded oxidatively to CO2. The oxidative degradation is accomplished by means of HMnO4. In this process only the circuit K1 is operated, without the cation exchanger K2 or the anion exchanger K3 having flow through it. After degradation of the oxalic acid, sulfuric acid and Mn sulfate are present in the solution. Only after degradation has taken place will the Mn2+ be bound to the cation exchanger by connecting in circuit K2.
After the end of the hematite step a process technology hold point 3 is programmed in. During the hold point 3 the further procedure is determined. The continuing process steps are based on the total oxide load of the system to be contaminated. If a large oxide load is present, process steps D1 to D5 must be repeated until the desired decontamination result (dose rate reduction) has been reached. When this occurs, the final cleanup step will be performed. Chemically this means that sulfuric acid is removed from the system. This is performed with anion exchange resins D6. During process step D6 both the large circulating operation K1 of the system to be decontaminated and the anion exchange circuit K3 are operated. The bypass operation K3 of the anion exchanger is continued until the sulfate ions are bound to the anion exchanger ATT. The total time required for this is predetermined by the available cleanup rate.
Repetition of the individual phases D1 to D6 in and of themselves does not occur. Instead, process steps D1+D2 or D1+D2+D3 or D1+D2+D3+D4 or D1+D2+D3+D4+D5 are repeated several times.
| Number | Date | Country | Kind |
|---|---|---|---|
| 11181978.5 | Sep 2011 | EP | regional |
| 102011083380.3 | Sep 2011 | DE | national |
| 102011084607.7 | Oct 2011 | DE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2012/068485 | 9/20/2012 | WO | 00 | 8/5/2014 |