The invention relates to methods for the deposition of thin film adhesion layers, and more particularly to silicon thin film adhesion layers for protective layers and even more particularly to such films as used on thin film magnetic heads.
In U.S. Pat. No. 6,503,406 to Hsiao, et al. the use of a silicon adhesion layer with a carbon protective layer for a magnetic transducer is described. Grill, et al., in U.S. Pat. No. 5,159,508 disclose a dry process for forming a protective coating over the slider prior to the lithographic process. The protective coating comprises two layers, the first layer an adhesion layer, e.g. silicon, and a second layer of amorphous carbon. The ABS is then formed on the slider covered with the protective coating.
U.S. Pat. No. 6,086,730 to Liu, et al., describes a method for sputtering a carbon protective layer with a high sp3 bond content which involves applying relatively high voltage pulses to the carbon target. Liu ′730 asserts that the resulting carbon overcoat has good durability and corrosion resistance down to low thicknesses. In addition to the pulsed DC sputtering with above mentioned characteristics, Liu also notes that the substrate can have a negative voltage bias in order to enhance the ta-C:H characteristics of the carbon film. Nominally the substrate is biased negative to the ground, so that there is potential of additional bombardment of the substrate by the argon ion used to sputter the target or to accelerate the carbon ions that may have formed during sputtering at high target bias potential. When substrate bias is applied, the positive ions of carbon and argon will be accelerated toward the substrate during deposition. Liu does not note, however, that argon atoms can be incorporated in the carbon film with undesirable results.
In the typical sputtering process, the atmosphere of the reaction chamber contains a noble gas which is most commonly argon, but helium, neon, krypton, and xenon are commonly mentioned as alternatives. (See for example, U.S. Pat. No. 6,569,293 to Makowiecki, et al.)
In U.S. published application No. 20030113588, Jun. 19, 2003, Uwazumi, Hiroyuki, et al. indicate that the concentration of the atoms of one of the inert gases remaining in the underlayer on a magnetic thin film disk is reduced by mixing the one inert gas with a different inert gas having larger atomic weight and radius. The magnetic layer is laminated onto the underlayer. The underlayer is deposited in a gas atmosphere containing argon and at least one of krypton and xenon in an amount sufficient to reduce the argon remaining in the underlayer to less than 1,000 ppm. Such a gas atmosphere contains at least 10% of krypton or xenon, and pressurized to a range of 30-70 mTorr. The underlayer is formed with a film structure composed of fine grains, which are suitable for epitaxial growth of the magnetic layer.
In U.S. Pat. No. 6,236,543 Han, et al., describe the use filtered cathodic arc (FCA) deposition to form landing pads for a slider air-bearing surface (ABS) of tetrahedral amorphous carbon (t-aC). The t-aC is extremely hard and highly stressed. The pads are fabricated after the slider has been coated with an adhesion layer such as Si, SiC, SiO2 or Si3N4, and a carbon overcoat of diamond-like-carbon (DLC) or t-aC has been formed. The pads are formed by filtered cathodic arc deposition, which uses carbon ions from a graphite cathode and a filter that removes macroparticles. The resulting t-aC material is said to have properties virtually equal to those of diamond, including high stress and hardness associated with nearly ubiquitous sp3 bonds. Other benefits of t-aC are a reduction in surface energy and wettability.
In order to improve the performance of magnetic thin film transducers the protective overcoat 45 and the adhesion layer 43 must be made as thin as possible to reduce the separation from the magnetic media and still maintain the protective function.
The applicants disclose a method of physical vapor deposition (PVD) in which xenon is used as the operating gas in the vacuum chamber in the deposition of an adhesion layer, preferably silicon, which allows the adhesion layer to be ultra-thin with improved durability over prior art films. The use of argon as is typical in the prior art results in argon atoms being incorporated into the ultra-thin silicon film with deleterious results. In films that are only several angstroms thick, the contamination of the film with argon or other elements can yield a film with reduced adhesion performance and in some cases noble atoms such as argon can escape the film leaving voids or pinholes. The use of the larger and heavier xenon atoms in the vacuum chamber produces a substantially purer film with reduced risk of voids and pinholes. In a preferred embodiment the use of xenon as the operating gas for deposition of the silicon adhesion layer is combined with the use of a filtered cathodic arc (FCA) process to deposit the protective overcoat, preferably carbon based, on a magnetic recording head.
The invention teaches that using xenon instead of argon for the vacuum deposition of silicon or similar material in ultra-thin films yields surprisingly superior results. The prior art has taught that the noble gases argon, krypton and xenon are essentially interchangeable for use in a PVD process. The applicants have found that intrinsic properties of the films can be improved by reducing the incorporation of atoms of the operating gas into the film. The larger and heavier xenon atoms are incorporated into an ultra-thin silicon film at a rate that can be an order of magnitude lower than the rate of argon incorporation. The superior silicon film is particularly important when it will be subjected to a process used to form diamond-like carbon (DLC) such as the filtered cathodic arc (FCA) which uses high energy ions to form the bonds of DLC. The combination of the silicon adhesion layer deposited using xenon and an FCA deposited DLC is particularly useful for a magnetic recording head which requires a hard, dense, impervious protective layer structure that can be less than 25 angstroms thick. In general, the silicon layer for a magnetic head should be less than 20 angstroms. Although in the embodiments described below an ion beam generator and a plasma beam neutralizer are used in the PVD process, the results should apply to magnetron sputtering and any other process which have previously used argon as the operating gas.
In an experiment performed by the applicants, a silicon film was deposited using argon as the operating gas in a PVD process in accordance with the prior art. Xray relectometry (XRR) density measurements of the resulting film were higher than the theoretical values for a silicon film indicating that heavier argon atoms had contaminated the film. A second silicon film was PVD deposited using xenon as the operating gas. This film's XRR density measurement was near the theoretical value for silicon confirming that the film was substantially free of xenon or other contaminating atoms. The data also show that the film was substantially free from pinholes or voids, since these would result in a lower than expected density value.
In another experiment two sets of magnetic heads were prepared using a PVD process to deposit a silicon adhesion layer approximately 6 angstroms thick. Silicon target(s) were used with an ion beam generator for the primary ion source, an operating gas and a plasma beam neutralizer (PBN) gas. For one set of heads the silicon adhesion layer was deposited using xenon as the operating gas and argon was used for the PBN gas. The second set of heads was processed according to the prior art using argon for both gases. On each set of heads a diamond-like carbon (DLC) protective layer of approximately 9 angstroms was deposited on the silicon using an FCA process. Tests of the corrosion resistance were performed on both types of heads. A 7 hour NaCl solution dip test was followed with optical examination of S1, S2, P1 and P2. For graphing, the binary cutoff criterion for each structures was selected as 20% corrosion of the ABS surface area. The percentages of heads with P2, P1, S2 and S2 showing an area greater than 20% corrosion for each of the two groups of heads are shown in
Another test of corrosion properties that was performed was a 7 hour NaCl solution dip followed by 3 hours of a US NaCl solution dip test. The same optical examination of Si, S2, P1 and P2 described above was performed. The percentages of heads with P2, P1, S2 and S2 showing an area greater than 20% corrosion for each of the two groups of heads are shown in
Another method of evaluating corrosion was used for the MR sensor.
The results above were achieved even though argon was being used as the PBN gas. The PBN gas typically is less than 5% of the total gas in the vacuum chamber. The PVD process described above can be further improved by using xenon as the PBN gas.
The invention has been described with respect to use on thin film magnetic heads, but other uses and applications which can benefit from the properties of the adhesion and protective layer properties of the invention will be apparent to those skilled in the art.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5159508 | Grill et al. | Oct 1992 | A |
| 6086730 | Liu et al. | Jul 2000 | A |
| 6086796 | Brown et al. | Jul 2000 | A |
| 6236543 | Han et al. | May 2001 | B1 |
| 6429097 | Voutsas | Aug 2002 | B1 |
| 6503406 | Hsiao et al. | Jan 2003 | B1 |
| 6569293 | Makowiecki et al. | May 2003 | B1 |
| 6795275 | Anan et al. | Sep 2004 | B2 |
| 20020187405 | Carcia | Dec 2002 | A1 |
| 20030113588 | Uwazumi et al. | Jun 2003 | A1 |
| Number | Date | Country |
|---|---|---|
| 2002053954 | Feb 2002 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20050045468 A1 | Mar 2005 | US |