Patent Application
20230343489
This application is based upon and claims the benefit of priority from Chinese Patent Application No. 202010782781.X, filed Aug. 6, 2020, the content of which is incorporated herein by reference in its entirety.
The present disclosure relates to the technical field of a Direct Current (DC) bushing, and in particular to a method for developing an epoxy resin impregnated glass fiber DC bushing.
The DC bushing, as a current-carrying conductor, passes through a box or a wall with different potential from the potential of the DC bushing, and plays the role of insulation and mechanical support, which is one of the key devices for ensuring the safe and stable operation of the system. The traditional DC bushing (of the converter transformer) mostly adopts an oil-impregnated paper and glue-impregnated paper production process. However, the oil-impregnated paper bushing has a risk of oil leakage, and the glue-impregnated paper bushing is prone to absorption of moisture, causing several bushing failures and accidents occurred during the operation of the system. Compared with these two types of bushings, the DC bushing (of the converter transformer) produced through the epoxy resin impregnated glass fiber process has a pure solid structure, is oil-free and maintenance-free, does not decompose, and has excellent mechanical strength and anti-seismic performance without risk of combustion and explosion. The core of the bushing is made of a non-moisture-absorbing material with a lower dielectric loss. The technical difficulties in adopting such a process are as follows. (1) The winding temperature of the epoxy resin impregnated glass fiber can affect the initial curing process of the core of the bushing. (2) The design of the length and the thickness of the capacitive screen of the core of the DC bushing (of the converter transformer) can affect the field strength distribution of the bushing. (3) The design of the connection between the tap or voltage screen of the core of the DC bushing (of the converter transformer) and outside of the bushing can affect the space charge accumulation effect at the medium interface of the bushing.
The purpose of embodiments of the present disclosure is to provide a method for developing an epoxy resin impregnated glass fiber Direct Current (DC) bushing.
To achieve the above purpose, the embodiments of the present disclosure provide the technical solutions as follows. A method for developing an epoxy resin impregnated glass fiber DC bushing includes the following operations.
A bushing design parameter is selected according to a length parameter of each layer of capacitive screen or resistive screen designed depending on insulation requirements, a winding machine program is determined according to the bushing design parameter, and a core is wound according to the winding machine program, in which the core begins to be initially cured during winding of the core.
After the winding of the core is completed, the core is cured by an oven according to a preset oven temperature and duration.
The cured core is machined according to a preset core design drawing.
After an inner wall of a flange is polished and cleaned and is subjected to a heating pretreatment by an oven, glue is injected at a position of a glue injection hole of the flange to glue the core and the flange.
A collector ring, a hollow composite insulator and a voltage-equalizing sealing cover are sequentially assembled on the glued core, and a conductive rod, a wiring board and a voltage-equalizing ball are mounted on the glued core.
Various tests are performed on the bushing according to a preset standard of bushing for DC system.
In some optional embodiments, a thickness between each two layers of capacitive screens or resistive screens is the same, and a thickness of each layer of capacitive screen or resistive screen is selected from the bushing design parameter in a range of 2.5 mm to 5 mm.
In some optional embodiments, a winding temperature in the winding machine program is in a range of 90° C. to 120° C.
In some optional embodiments, during the machining of the cured core, an amount of feed for rough machining is no more than 0.5 mm, and an amount of feed for fine machining is no more than 0.1 mm.
In some optional embodiments, the method further includes the following operation. After the glue is injected at the position of the glue injection hole of the flange, it is required to stand for 24 hours.
In some optional embodiments, the method further includes the following operation. After the inner wall of the flange is polished and cleaned, an adhesive is evenly applied at the inner wall of the flange.
In some optional embodiments, the method further includes the following operation. After the heating pretreatment is performed by the oven, the flange is secured to the core and a sealing ring is mounted on the core.
In some optional embodiments, the method further includes the following operation. Before the collector ring, the hollow composite insulator and the voltage-equalizing sealing cover are sequentially assembled on the glued core and the conductive rod, the wiring board and the voltage-equalizing ball are mounted on the glued core, an oil-impregnated end of the glued core is sprayed with paint.
The embodiments of the present disclosure provide a method for developing an epoxy resin impregnated glass fiber DC bushing, which has the following beneficial effects.
In the embodiments of the present disclosure, the epoxy resin impregnated glass fiber is wound at the high temperature in a range of 90° C. to 120° C., so as to facilitate the initial curing process of the core. The length of each layer of the capacitive screen or the resistive screen wound by the semi-conductive tape is designed depending on insulation requirements, and the thickness of each layer of capacitive screen or resistive screen is designed in a range of 2.5 mm to 5 mm, so that the reasonable field strength distribution of the bushing is achieved, and the design with equal thickness reduces the difficulty of the winding process of the core of the bushing. A collector ring connected to the tap or the voltage screen is provided inside the bushing near the flange, which is grounded to release the accumulated charges (or space accumulated charges) generated during operation, thereby ensuring the reliable operation of the products.
In the drawings, “a” represents the thickness between each two layers of capacitive screens (or resistive screens) of the core of the DC bushing; and “b1” and “b2” represent two layers of capacitive screens (or resistive screens) of the core of the DC bushing.
The technical solutions in the embodiments of the present disclosure will be clearly and completely described below with reference to the accompanying drawings in the embodiments of the present disclosure. Obviously, the embodiments described here are merely some rather than all of the embodiments of the present disclosure. The examples of the embodiments are shown in the accompanying drawings, in which the same or similar reference numerals denote the same or similar elements or the elements with the same or similar functions from beginning to end. The embodiments described below with reference to the accompanying drawings are exemplary, which are intended to explain the present disclosure, but should not be constructed as a limitation of the present disclosure.
The embodiments of the present disclosure provide a method for developing an epoxy resin impregnated glass fiber Direct Current (DC) bushing.
In operation 11, a bushing design parameter is selected according to a length parameter of each layer of capacitive screen or resistive screen designed depending on insulation requirements, a winding machine program is determined according to the bushing design parameter, and a core is wound according to the winding machine program, in which the core begins to be initially cured during winding of the core.
In operation 12, after the winding of the core is completed, the core is cured by an oven according to a preset oven temperature and duration.
In operation 13, the cured core is machined according to a preset core design drawing.
In operation 14, after an inner wall of a flange is polished and cleaned and is subjected to a heating pretreatment by an oven, glue is injected at a position of a glue injection hole of the flange, to glue the core and the flange.
In operation 15, a collector ring, a hollow composite insulator and a voltage-equalizing sealing cover are sequentially assembled on the glued core, and a conductive rod, a wiring board and a voltage-equalizing ball are mounted on the glued core.
In operation 16, various tests are performed on the bushing according to a preset standard of bushing for DC system.
In some optional embodiments, a thickness between each two layers of capacitive screens or resistive screens is the same, and a thickness of each layer of capacitive screen or resistive screen is selected from the bushing design parameter in a range of 2.5 millimeters (mm) to 5 mm.
In some optional embodiments, a winding temperature in the winding machine program is in a range of 90° C. to 120° C.
In some optional embodiments, during the machining of the cured core, an amount of feed for rough machining is no more than 0.5 mm, and an amount of feed for fine machining is no more than 0.1 mm.
In some optional embodiments, the method further includes the following operation. After the glue is injected at the position of the glue injection hole of the flange, it is required to stand for 24 hours.
In some optional embodiments, the method further includes the following operation. After the inner wall of the flange is polished and cleaned, an adhesive is evenly applied at the inner wall of the flange.
In some optional embodiments, the method further includes the following operation. After the heating pretreatment is performed by the oven, the flange is secured to the core and a sealing ring is mounted on the core.
In some optional embodiments, the method further includes the following operation. Before the collector ring, the hollow composite insulator and the voltage-equalizing sealing cover are sequentially assembled on the glued core and the conductive rod, the wiring board and the voltage-equalizing ball are mounted on the glued core, an oil-impregnated end of the glued core is sprayed with paint.
Herein, illustratively, in the operation that various tests are performed on the bushing according to the preset standard of bushing for DC system, the preset standard GB/T22674-2008 can be specifically adopted to perform various tests on the bushing. The standard GB/T22674-2008 is the standard of bushing for DC system, which is one of National Standards of the People's Republic of China. Of course, the embodiments of the present disclosure are not limited to the above standard of bushing for DC system.
The method for developing an epoxy resin impregnated glass fiber DC bushing according to the embodiments of the present disclosure are described below in combination with the specific examples.
First Example
The embodiments of the present disclosure provide a method for developing an epoxy resin impregnated glass fiber DC bushing, which includes the following operations.
In S1, the core is wound. According to a length parameter of each layer of capacitive screen or resistive screen designed depending on insulation requirements, a bushing design parameter is selected in such a manner that a thickness between each two layers of capacitive screens or resistive screens is the same, and a thickness of each layer of capacitive screen or resistive screen is 2.5 mm; a winding machine program is determined according to the bushing design parameter; and a core is wound according to the winding machine program, in which a winding temperature in the winding machine program is 90° C., and the core is gradually initially cured during winding of the core.
In S2, the core is cured. After the winding of the core is completed, the core is sent into an oven and cured according to a preset reasonable oven temperature and duration to ensure that the core is completely cured.
In S3, the cured core is machined. The cured core is machined according to a preset core design drawing. During the machining, an amount of feed for rough machining is 0.1 mm, and an amount of feed for fine machining is 0.02 mm Then the machining of the core is completed.
In S4, the core and a flange are glued to each other. After an inner wall of the flange is polished and cleaned, the inner wall of the flange is evenly applied with an adhesive and is followed by being subjected to a heating pretreatment by the oven, the flange then is secured at a suitable position of the core and a sealing ring is mounted on the core, and glue is injected at a position of a glue injection hole of the flange by using a glue gun to glue the core and the flange, and let it stand for 24 hours.
In S5, the components are assembled. An oil-impregnated end of the glued core (of the DC bushing of the converter transformer) is sprayed with paint, a collector ring, a hollow composite insulator and a voltage-equalizing sealing cover are sequentially assembled on the glued core, and a conductive rod, a wiring board and a voltage-equalizing ball are mounted on the glued core.
In S6, tests are performed on the bushing. Various tests are performed on the bushing according to a standard GB/T22674-2008 (a national standard of bushing for DC system).
Second Example
The embodiments of the present disclosure further provide a method for developing an epoxy resin impregnated glass fiber DC bushing, which includes the following operations.
In S1, the core is wound. According to a length parameter of each layer of capacitive screen or resistive screen designed depending on insulation requirements, a bushing design parameter is selected in such a manner that a thickness between each two layers of capacitive screens is the same, and a thickness of each layer of capacitive screen or resistive screen is 3 mm; a winding machine program is determined according to the bushing design parameter; and a core is wound according to the winding machine program, in which a winding temperature in the winding machine program is 95° C., and the core is gradually initially cured during winding of the core.
In S2, the core is cured. After the winding of the core is completed, the core is sent into an oven and cured according to a preset reasonable oven temperature and duration to ensure that the core is completely cured.
In S3, the cured core is machined. The cured core is machined according to a preset core design drawing. During the machining, an amount of feed for rough machining is 0.2 mm, and an amount of feed for fine machining is 0.04 mm. Then the machining of the core is completed.
In S4, the core and a flange are glued to each other. After an inner wall of the flange is polished and cleaned, the inner wall of the flange is evenly applied with an adhesive and is followed by being subjected to a heating pretreatment by the oven, the flange is then secured at a suitable position of the core and a sealing ring is mounted on the core, and glue is injected at a position of a glue injection hole of the flange by using a glue gun to glue the core and the flange, and let it stand for 24 hours.
In S5, the components are assembled. An oil-impregnated end of the glued core (of the DC bushing of the converter transformer) is sprayed with paint, a collector ring, a hollow composite insulator and a voltage-equalizing sealing cover are sequentially assembled on the glued core, and a conductive rod, a wiring board and a voltage-equalizing ball are mounted on the glued core.
In S6, tests are performed on the bushing. Various tests are performed on the bushing according to a standard GB/T22674-2008 (a national standard of bushing for DC system).
Third Example
The embodiments of the present disclosure further provide a method for developing an epoxy resin impregnated glass fiber DC bushing, which includes the following operations.
In S1, the core is wound. According to a length parameter of each layer of capacitive screen or resistive screen designed depending on insulation requirements, a bushing design parameter is selected in such a manner that a thickness between each two layers of capacitive screens or the resistive screens is the same, and a thickness of each layer of capacitive screen or resistive screen is 3.5 mm; a winding machine program is determined according to the bushing design parameter; and a core is wound according to the winding machine program, in which a winding temperature in the winding machine program is 100° C., and the core is gradually initially cured during winding of the core.
In S2, the core is cured. After the winding of the core is completed, the core is sent into an oven and cured according to a preset reasonable oven temperature and duration to ensure that the core is completely cured.
In S3, the cured core is machined. The cured core is machined according to a preset core design drawing. During the machining, an amount of feed for rough machining is 0.3 mm, and an amount of feed for fine machining is 0.06 mm. Then the machining of the core is completed.
In S4, the core and a flange are glued to each other. After an inner wall of the flange is polished and cleaned, the inner wall of the flange is evenly applied with an adhesive and is followed by being subjected to a heating pretreatment by the oven, the flange is then secured at a suitable position of the core and a sealing ring is mounted on the core, and glue is injected at a position of a glue injection hole of the flange by using a glue gun to glue the core and the flange, and let it stand for 24 hours.
In S5, the components are assembled. An oil-impregnated end of the glued core (of the DC bushing of the converter transformer) is sprayed with paint, a collector ring, a hollow composite insulator and a voltage-equalizing sealing cover are sequentially assembled on the glued core, and a conductive rod, a wiring board and a voltage-equalizing ball are mounted on the glued core.
In S6, tests are performed on the bushing. Various tests are performed on the bushing according to a standard GB/T22674-2008 (a national standard of bushing for DC system).
Fourth Example
The embodiments of the present disclosure further provide a method for developing an epoxy resin impregnated glass fiber DC bushing, which includes the following operations.
In S1, the core is wound. According to a length parameter of each layer of capacitive screen or resistive screen designed depending on insulation requirements, a bushing design parameter is selected in such a manner that a thickness between each two layers of capacitive screens is the same, and a thickness of each layer of capacitive screen or resistive screen is 4 mm; a winding machine program is determined according to the bushing design parameter; and a core is wound according to the winding machine program, in which a winding temperature in the winding machine program is 110° C., and the core is gradually initially cured during winding of the core.
In S2, the core is cured. After the winding of the core is completed, the core is sent into an oven and cured according to a preset reasonable oven temperature and duration to ensure that the core is completely cured.
In S3, the cured core is machined. The cured core is machined according to a preset core design drawing. An amount of feed for rough machining is 0.4 mm, and an amount of feed for fine machining is 0.08 mm. Then the machining of the core is completed.
In S4, the core and a flange are glued to each other. After an inner wall of the flange is polished and cleaned, the inner wall of the flange is evenly applied with an adhesive and is followed by being subjected to a heating pretreatment by the oven, the flange is then secured at a suitable position of the core and a sealing ring is mounted on the core, and glue is injected at a position of a glue injection hole of the flange by using a glue gun to glue the core and the flange, and let it stand for 24 hours.
In S5, the components are assembled. An oil-impregnated end of the glued core (of the DC bushing of the converter transformer) is sprayed with paint, a collector ring, a hollow composite insulator and a voltage-equalizing sealing cover are sequentially assembled on the glued core, and a conductive rod, a wiring board and a voltage-equalizing ball are mounted on the glued core.
In S6, tests are performed on the bushing. Various tests are performed on the bushing according to a standard GB/T22674-2008 (a national standard of bushing for DC system).
Fifth Example
The embodiments of the present disclosure further provide a method for developing an epoxy resin impregnated glass fiber DC bushing, which includes the following operations.
In S1, the core is wound. According to a length parameter of each layer of capacitive screen or resistive screen designed depending on insulation requirements, a bushing design parameter is selected in such a manner that a thickness between each two layers of capacitive screens or resistive screens is the same, and a thickness of each layer of capacitive screen or resistive screen is 5 mm; a winding machine program is determined according to the bushing design parameter; and a core is wound according to the winding machine program, in which a winding temperature in the winding machine program is 120° C., and the core is gradually initially cured during winding of the core.
In S2, the core is cured. After the winding of core is completed, the core is sent into an oven and cured according to a preset reasonable oven temperature and duration to ensure that the core is completely cured.
In S3, the cured core is machined. The cured core is machined according to a preset core design drawing. During the machining, an amount of feed for rough machining is 0.5 mm, and an amount of feed for fine machining is 0.1 mm. Then the machining of the core is completed.
In S4, the core and a flange are glued to each other. After an inner wall of the flange is polished and cleaned, the inner wall of the flange is evenly applied with an adhesive, and is followed by being subjected to a heating pretreatment by the oven, the flange is then secured at a suitable position of the core and a sealing ring is mounted on the core, and glue is injected at a position of a glue injection hole of the flange by using a glue gun to glue the core and the flange, and let it stand for 24 hours.
In S5, the components are assembled. An oil-impregnated end of the glued core (of the DC bushing of the converter transformer) is sprayed with paint, a collector ring, a hollow composite insulator and a voltage-equalizing sealing cover are sequentially assembled on the glued core, and a conductive rod, a wiring board and a voltage-equalizing ball are mounted on the glued core.
In S6, tests are performed on the bushing. Various tests are performed on the bushing according to a standard GB/T22674-2008 (a national standard of bushing for DC system).
As shown in
Overall, in the embodiments of the present disclosure, the epoxy resin impregnated glass fiber is wound at the high temperature in a range of 90° C. to 120° C., so as to facilitate the initial curing process of the core. The length of each layer of the capacitive screen (or the resistive screen) wound by the semi-conductive tape is designed depending on insulation requirements, and the thickness of each layer of the capacitive screen (or the resistive screen) is designed in a range of 2.5 mm to 5 mm, so that the reasonable field strength distribution of the bushing is achieved, and the design with equal thickness reduces the difficulty of the winding process of the core of the bushing. A collector ring connected to the tap or the voltage screen is provided inside the bushing near the flange, which is grounded to release the accumulated charges (or space accumulated charges) generated during operation, thereby ensuring the reliable operation of the product.
The methods disclosed in the several method embodiments provided by the present disclosure can be combined arbitrarily with each other without conflict to obtain a new method embodiment.
It can be understood by those of ordinary skill in the art that all or part of the steps of the method embodiment may be implemented by related hardware instructed through a program, the program may be stored in a computer-readable storage medium, and when the program is executed, the steps of the method embodiment are implemented. The storage medium includes: various media capable of storing program codes such as a mobile storage device, a Read-Only Memory (ROM), a Random Access Memory (RAM), a magnetic disk or a compact disc.
Or, when being implemented in form of software functional module and sold or used as an independent product, the integrated unit of the disclosure may also be stored in a computer-readable storage medium. Based on such an understanding, the technical solutions of the embodiments of the disclosure substantially or parts contributing to the conventional art may be embodied in form of software product, and the computer software product is stored in a storage medium, including a plurality of instructions configured to enable a computer device (which may be a personal computer, a server, a network device or the like) to execute all or part of the method in each embodiment of the disclosure. The storage medium includes: various media capable of storing program codes such as a mobile hard disk, a ROM, a RAM, a magnetic disk or a compact disc.
The above descriptions are only specific embodiments of the present disclosure, but the protection scope of the present disclosure is not limited thereto. Any skilled in the art, within the technical scope disclosed by the present disclosure, may easily think of variations or replacements, which should fall into the protection scope of the present disclosure. Therefore, the protection scope of the present disclosure should be subject to the protection scope of the claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 202010782781.X | Aug 2020 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2020/134362 | 12/7/2020 | WO |