Patent Application
20210231556
The present invention relates to a technique for estimating a fracture starting point of high-strength steel due to hydrogen embrittlement.
High-strength steel suffers ductility loss and significant strength reduction due to hydrogen penetrating into the steel. This phenomenon is called hydrogen embrittlement (Non-Patent Literature 1).
Fracture of steel due to hydrogen embrittlement is thought to be caused by locally accumulated hydrogen and is said to occur when local hydrogen content in steel reaches or exceeds a threshold. For example, when a notched test piece with a groove formed in a surface thereof is used, hydrogen will accumulate on a notch root, producing a local stress concentration site, and the stress concentration site is considered to serve as a fracture starting point of steel (Non-Patent Literature 2).
Also, in examining a fracture starting point after fracture of steel due to hydrogen embrittlement, a method is used that involves observing a fracture surface under a microscope or the like and estimating the fracture starting point from a fracture form (Non-Patent Literature 3).
However, in actual environments, high-strength steel has various forms, and when a smooth test piece without a notch is used, there is no notch root where hydrogen can accumulate and a stress concentration site is unknown, making it difficult to estimate a fracture starting point. Even if a method for observing a fracture surface under a microscope is used, it is difficult to clearly identify a convergent point of a streaky wavefront regarded to be a fracture starting point, and the fracture starting point can be estimated only with coarse accuracy.
The present invention has been made in view of the above circumstances and has an object to estimate a fracture starting point of steel due to hydrogen embrittlement with high accuracy.
To solve the above problem, according to claim 1, there is provided a steel fracture starting point estimation method for estimating a fracture starting point of steel, the method causing a computer to execute: a first step of calculating a hydrogen concentration distribution in steel-to-be-estimated when the steel fractures due to hydrogen embrittlement; a second step of calculating critical hydrogen content at which the steel-to-be-estimated fractures due to hydrogen embrittlement; and a third step of reading the hydrogen concentration distribution out of a storage unit, calculating, from the hydrogen concentration distribution, a location in the steel in which hydrogen concentration of the critical hydrogen content is distributed, and designating the location in the steel as the fracture starting point of the steel-to-be-estimated.
According to claim 2, in the steel fracture starting point estimation method according to claim 1, the first step includes calculating a hydrogen diffusion coefficient of the steel-to-be-estimated based on variation of hydrogen content in the steel with time on assumption that hydrogen diffuses in the steel, and calculating the hydrogen concentration distribution using a diffusion equation based on the hydrogen diffusion coefficient.
According to claim 3, in the steel fracture starting point estimation method according to claim 1 or 2, the first step includes calculating the hydrogen concentration distribution when the steel-to-be-estimated fractures with constant tensile stress being applied, and the second step includes charging the steel-to-be-estimated with hydrogen until saturation, calculating hydrogen content corresponding to the constant tensile stress using measurement data of tensile stress at fracture in a tensile test conducted repeatedly with an amount of charged hydrogen being varied, and designating the hydrogen content as the local critical hydrogen content.
According to claim 4, there is provided a steel fracture starting point estimation device that estimates a fracture starting point of steel, the steel fracture starting point estimation device comprising: a hydrogen concentration distribution calculation unit adapted to calculate a hydrogen concentration distribution in steel-to-be-estimated when the steel fractures due to hydrogen embrittlement; a local critical hydrogen content calculation unit adapted to calculate critical hydrogen content at which the steel-to-be-estimated fractures due to hydrogen embrittlement; and a fracture starting point estimation unit adapted to read the hydrogen concentration distribution out of a storage unit, calculate, from the hydrogen concentration distribution, a location in the steel in which hydrogen concentration of the critical hydrogen content is distributed, and designate the location in the steel as the fracture starting point of the steel-to-be-estimated.
According to claim 5, in the steel fracture starting point estimation device according to claim 4, the hydrogen concentration distribution calculation unit calculates a hydrogen diffusion coefficient of the steel-to-be-estimated based on variation of hydrogen content in the steel with time on assumption that hydrogen diffuses in the steel, and calculates the hydrogen concentration distribution using a diffusion equation based on the hydrogen diffusion coefficient.
According to claim 6, in the steel fracture starting point estimation device according to claim 4 or 5, the hydrogen concentration distribution calculation unit calculates the hydrogen concentration distribution when the steel-to-be-estimated fractures with constant tensile stress being applied; and the local critical hydrogen content calculation unit charges the steel-to-be-estimated with hydrogen until saturation, calculates hydrogen content corresponding to the constant tensile stress using measurement data of tensile stress at fracture in a tensile test conducted repeatedly with an amount of charged hydrogen being varied, and designates the hydrogen content as local critical hydrogen content.
According to claim 7, there is provided a steel fracture starting point estimation program that causes a computer to function as the steel fracture starting point estimation device according to any one of claims 4 to 6.
The present invention makes it possible to estimate a fracture starting point of steel due to hydrogen embrittlement with high accuracy.
An embodiment of the present invention will be described below with reference to the drawings.
The hydrogen concentration distribution calculation unit 11 has a function to calculate a hydrogen concentration distribution in high-strength steel to be estimated (hereinafter referred to as the steel-to-be-estimated or the steel) when the steel fractures due to hydrogen embrittlement and store the hydrogen concentration distribution in the storage unit 3. The hydrogen concentration distribution calculation unit 11 has a function to calculate a hydrogen diffusion coefficient of the steel-to-be-estimated based on variation of hydrogen content in the steel with time on assumption that hydrogen diffuses in the steel and calculate the hydrogen concentration distribution in the steel using a diffusion equation based on the calculated hydrogen diffusion coefficient. The hydrogen concentration distribution calculation unit 11 has a function to calculate the hydrogen concentration distribution in the steel-to-be-estimated when the steel fractures with constant tensile stress being applied.
The local critical hydrogen content calculation unit 12 has a function to calculate critical hydrogen content (local critical hydrogen content) at which the steel-to-be-estimated fractures due to hydrogen embrittlement. A tensile test is conducted by charging the steel-to-be-estimated with hydrogen until saturation. The local critical hydrogen content calculation unit 12 has a function to calculate hydrogen content corresponding to the constant tensile stress using measurement data of tensile stress at fracture in a tensile test conducted repeatedly with an amount of charged hydrogen being varied, and designate the hydrogen content as local critical hydrogen content.
The fracture starting point estimation unit 13 has a function to read data on the hydrogen concentration distribution out of the storage unit 3, calculate, from the hydrogen concentration distribution, a location in the steel in which hydrogen concentration of the critical hydrogen content (local critical hydrogen content) is distributed, and output the calculated location in the steel to the display unit 5 as a fracture starting point of the steel-to-be-estimated.
Next, a steel fracture starting point estimation method performed by the steel fracture starting point estimation device 1 will be described. The steel fracture starting point estimation device 1 performs the following steps. To estimate a fracture starting point of high-strength steel, plural pieces of high-strength steel of the same shape and same material are prepared in advance.
Step 1;
In step 1, a hydrogen concentration distribution in steel is calculated when the steel fractures due to hydrogen embrittlement. Step 1 will be described concretely below.
Step 1-1;
First, the time until the steel fractures due to hydrogen embrittlement is measured. Step 1-1 will be described concretely below.
According to the present embodiment, a constant-load test is conducted on steel rods by applying constant tensile stress to the steel rods while charging hydrogen into the steel rods and the time until the steel fractures is measured. That is, by continuing to charge the steel rods with hydrogen while maintaining constant tensile stress, the fracture time of the steel as a function of increase in hydrogen content is measured.
As test pieces of steel, for example, smooth round bars 50 cm long and 7 mm in diameter are used. As a method for hydrogen charging, a cathodic charging method is used, where the cathodic charging method involves immersing steel in an aqueous electrolytic solution and applying a negative potential. As a value of the constant load (tensile stress), stress 0.7 times the tensile strength of the steel is used. As the aqueous electrolytic solution, 1 mol/L of an aqueous sodium bicarbonate solution is used, and as an applied voltage, 1 V vs. SSE is used.
A constant-load test was conducted by applying tensile stress 0.7 times the tensile strength of the steel while charging hydrogen into the steel rods. A result was that the fracture time of the steel was 1.5 hours from the start of the hydrogen charging. A measurer stores the measured fracture time of the steel in the storage unit 3.
Step 1-2;
Next, a hydrogen diffusion coefficient of the steel is calculated based on variation of hydrogen content in the steel with time on assumption that hydrogen diffuses in the steel, and the hydrogen concentration distribution in the steel upon elapse of the fracture time of the steel measured in step 1-1 is calculated using a diffusion equation based on the calculated hydrogen diffusion coefficient. Step 1-2 will be described concretely below.
First, to calculate the hydrogen diffusion coefficient, the variation of hydrogen content in the steel with time is measured. In the present embodiment, using such stress (e.g., 0.5 times the tensile strength of the steel) that no fracture due to hydrogen embrittlement occurs as the stress for the constant-load test, the steel is charged with hydrogen by the same method as above, and the variation of hydrogen content in the steel with time is measured. In measuring the hydrogen content, for example, thermal desorption spectroscopy (TDS) is used. Regarding TDS measurement conditions, for example, measurements are taken up to a temperature of 500° C. at a temperature increase rate of 10° C./min.
Since it is thought that the hydrogen in steel penetrates inside the steel by diffusion as described earlier, the hydrogen content C in the steel in an initial stage of diffusion can be approximated by Formula (1). The measurer stores Formula (1) in the storage unit 3.
where C is the hydrogen content in steel, Cs is saturated hydrogen content, a is the radius of steel, D is a hydrogen diffusion coefficient, and t is hydrogen charging time. Also, from
Formula 2
C
s=6.40 (ppm) (2)
The measurer stores the value of Formula (2), a radius a of the steel, and other values in the storage unit 3. The hydrogen concentration distribution calculation unit 11 reads Formula (1), Formula (2), the radius a of the steel, and other values out of the storage unit 3, and performs calculations by substituting the value of Formula (2), radius a of the steel, and other values into Formula (1). As a result, the hydrogen diffusion coefficient D is given by Formula (3).
Formula 3
D≅1.45×10−1(mm2/h) (3)
Next, using the calculated value of the hydrogen diffusion coefficient D as a diffusion coefficient and using an existing diffusion equation having the diffusion coefficient and time as variables, the hydrogen concentration distribution calculation unit 11 calculates the hydrogen concentration distribution in the steel at the time when fracture occurs in the steel (upon elapse of 1.5 hours found in step 1-1), for example, by a common numerical calculation method based on a difference method.
Step 2;
The hydrogen concentration distribution in steel when the steel fractures due to hydrogen embrittlement has been found in step 1. In step 2 and after-mentioned step 3, based on the hydrogen concentration distribution, along a diameter section in steel, the depth position of the hydrogen content that causes hydrogen embrittlement fracture is identified, and thereby a fracture starting point of the steel due to hydrogen embrittlement is estimated.
Thus, in step 2, a local hydrogen content (local critical hydrogen content) threshold at or above which hydrogen embrittlement fracture occurs is calculated. To measure the local critical hydrogen content, for example, a CSRT method (Non-Patent Literature 4) is used. With the CSRT method, to conduct a tensile test in such a short time that the hydrogen in steel will not undergo stress-induced diffusion, hydrogen content uniformly absorbed in the steel in advance can be assumed to be equal to the local critical hydrogen content.
Specifically, the steel is charged with hydrogen until the hydrogen content reaches saturation under no-load conditions, then a tensile test is conducted at a tension speed of 1 mm/min, and tensile stress is measured when the steel is fractured. The hydrogen content at the time when hydrogen reaches saturation is measured using TDS (thermal desorption spectroscopy) described above. The tensile test is conducted repeatedly with an applied potential for hydrogen charging being varied and the hydrogen content at the time when saturation is reached being thereby varied. The measurer stores measurement data of the tensile test in the storage unit 3.
Using the measurement results of tensile test shown in
Step 3;
Based on consideration of the local critical hydrogen content, as described in Background Art, fracture of steel due to hydrogen embrittlement occurs when local hydrogen content in the steel reaches or exceeds the local critical hydrogen content. That is, in
Therefore, the fracture starting point estimation unit 13 reads the data on the calculated hydrogen concentration distribution as well as the local critical hydrogen content out of the storage unit 3, and calculates, from the hydrogen concentration distribution, a location in the steel in which hydrogen concentration of the local critical hydrogen content is distributed as shown in
Thus, according to the present embodiment, since the steel fracture starting point estimation device 1 includes the hydrogen concentration distribution calculation unit 11 adapted to calculate a hydrogen concentration distribution in steel-to-be-estimated when the steel fractures due to hydrogen embrittlement; the local critical hydrogen content calculation unit 12 adapted to calculate critical hydrogen content at which the steel-to-be-estimated fractures due to hydrogen embrittlement; and the fracture starting point estimation unit 13 adapted to read the hydrogen concentration distribution out of the storage unit 3, calculate, from the hydrogen concentration distribution, a location in the steel in which hydrogen concentration of the critical hydrogen content is distributed, and designate the location in the steel as the fracture starting point of the steel-to-be-estimated, the fracture starting point of the steel due to hydrogen embrittlement can be estimated with high accuracy.
For example, the fracture starting point of hydrogen embrittlement can be estimated with high accuracy on the order of 10 μm, which has been difficult before. Once the fracture starting point can be estimated, the fracture time with hydrogen charging conditions (i.e., the value of Cs) changed can be predicted and the fracture time can be easily known without many tests.
Finally, the steel fracture starting point estimation device 1 described in the present embodiment can be implemented by a computer and programs, where the programs can be recorded on a recording medium or provided via a communications network.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2018-089370 | May 2018 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2019/017461 | 4/24/2019 | WO | 00 |