Method for facilitating distinction between different steel products

BACKGROUND OF THE INVENTION
1. Field of the Invention:
The present invention relates to color-developing plated metal for springs and the method of using the same, and more specifically, to a color-developing plated metal for springs capable of being suitably distinguished in size, material and the like and the method of using the same.
2. Description of the Prior Art
A product formed of spring steel (that is, a spring) such as a coil spring or a sheet spring is used in various applications such as mechanical parts, official materials and daily necessities. The spring steel as a material for the above spring includes a spring steel wire and a spring steel sheet. As the spring steel wire, there are known a hard drawn steel wire, a piano wire and a spring stainless steel wire specified in Japanese Industrial Standard (hereinafter referred to as JIS).
These steel wires resemble each other in surface color tone, and particularly, a hard drawn steel wire cannot be distinguished from a piano wire by only the color tone. Also, in the case of a stainless steel wire, it generally is more lustrous as compared to a hard drawn steel wire and a piano wire; however, when being finished by oil drawing (wet drawing), it cannot be distinguished by color tone. Accordingly, of these steel wires after spring-forming, those resembling in size to each other have often created a problem of their mixing in size or material, and consequently, the defective spring product being liable to be erroneously assembled in a mechanical structure.
On the other hand, a steel cord for reinforcing a radial tire of an automobile is formed as follows: namely, five elementary wires each having a diameter of, for example, 0.25 mm are stranded, and the stranded wire is knitted into a belt-shape and is disposed around the periphery of the tire. Thus, the steel cord aims at reinforcement of the radial tire as a rubber-metal cord composite material. The above elementary wire is manufactured by the steps of: applying a Cu-plating as a lower layer and a Zn-plating as an upper layer on the surface of a raw wire having a diameter of 1.3mm at a plating thickness ratio of Cu:Zn=7.3; heating the plated wire at approximately 400.degree. C. for a few minutes to tens of minutes for alloying the plating layers into a Cu-30% Zn alloy; and forcibly drawing it at a reduction ratio of 96.3% to a diameter of 0.25 mm. During such processes, after heating, the color of the plating surface is changed from white to gold, which exhibits a very beautiful color tone.
In the manufacture of a steel wire mentioned above, the fact that the surface color tone of the cord is changed to gold is worthless, and the object is to improve the drawability and adhesiveness between rubber and metal by alloying the plating layer into a Cu-30% Zn alloy. Accordingly, the positive function of the coloring generated by plating the material with two different metals and applying thermal diffusion thereto was not recognized.
In addition, the steel coated with only a plating layer of Cu-30% Zn alloy has no problem in terms of corrosion resistance when it is embedded in rubber, for example, as in the case of the steel cord and thus shielded from the outside air. However, in the case of using the above steel as a formed product without shielding it from the outside air, it is insufficient for corrosion resistance and results in problems.
To prevent the above products formed of spring steel of different size and material form mixing and also to improve their beautiful appearance, there have been used the following coatings on the spring steel wire: various resin film coatings; baked coatings of paint; ion plating by PVD or CVD; and TiN coating.
However, in spring-forming, the spring steel wire is subjected to severe abrasion close to galling in passing through the forming tool, and is also subjected to a heat treatment (low temperature annealing) at 250.degree. C.-400.degree. C. for 2-10 min. after spring-forming for improving the spring characteristics. Consequently, the spring steel wire coated with a resin film or baking paint is liable to be damaged on the surface thereof during the spring-forming thereby causing peeling of the film, and also the film is softened during the low temperature annealing thus causing depressions in the film and mutual adhesion of the springs. The spring steel wire plated by ion plating does not result in the above problems; but has a disadvantage of increasing the cost. Therefore, the known techniques do not function in an adequate manner.
SUMMARY OF THE INVENTION
An object of the present invention is to facilitate the distinction among the spring steel products and to improve their surface appearance, and further to improve their corrosion resistance.
To achieve the above object, the present inventors have found that plating does not significantly deteriorate the spring characteristic of the spring steel material and improves the corrosion resistance, and further causes the plating layer to be colored during the low temperature annealing after the spring-forming, and therefore, by suitable selection of the color tone of the spring steel product, it is possible to distinguish them by size and material.
In a first aspect of the present invention, there is provided coated metal for a spring having alternate plating layers of Cu and Zn on the surface thereof, which are alloyed by a low temperature thermal diffusion after the spring-forming on the surface thereof.
In a second aspect of the present invention, there is provided a method of using said plated metal for a spring comprising the steps of: plating alternate layers of Cu and Zn with a thickness ratio of the Zn layer to the whole thickness of the plating layers at 5-45% on the surface of a spring steel wire; adjusting the final plating thickness at 2-25 .mu.m, and spring-forming it; and heating the formed product at 250.degree.-400.degree. C. (low temperature annealing), thereby coloring the plating layer thereof.
In a third aspect of the present invention, there is provided plated metal for a spring having a Ni-plating layer on the surface thereof and subsequent alternate layers of Cu and Zn to be alloyed by a low temperature thermal diffusion after the spring-forming.
In a fourth aspect of the present invention, there is provided a method of using the said coated metal for a spring comprising the steps of: applying a three-layer plating of a Ni-layer as a lower layer, a Cu-layer as an intermediate layer and a Zn-layer as an upper layer, adjusting a thickness ratio of the Zn layer to the total thickness of the Cu-layer and Zn layer at 5-45% on the surface of a spring steel wire; adjusting the Ni-layer thickness and the total thickness of Cu-layer and Zn layer at 2-30.mu.m and 2-25.mu.m, respectively, and spring-forming it; and heating the formed product at 250.degree.-400.degree. C. (low temperature annealing), thereby coloring the plating layer thereof.
Prior to description of the preferred embodiments, there will be described the function of the present invention.
A Cu-Zn alloy plating layer alloyed by heating of two-layer plating of Cu-Zn can exhibits various color tones according to the heating conditions and the content of Zn, which makes easy the distinction thereof.
Further, a three-layer plating of a lower Ni-layer, an intermediate Cu-layer, and an upper Zn-layer, when it is heated at a relatively low temperature so as not to yield mutual diffusion between the lower Ni-layer and the intermediate Cu-layer, the intermediate Cu-layer and the upper Zn-alloy are alloyed by the mutual diffusion, to thus form a Cu-Zn alloy placing layer. This can exhibit various color tones according to the heating conditions and the content of Zn, thus making easy the distinction thereof.
The present invention is intended to prevent the mixing of the products formed of spring steel different in size and material by utilizing the difference in the color tone of the color developing plating layer, and to improve the corrosion resistance by the Cu-Zn alloy plating layer and Ni-plating layer as a lower layer. However, if the characteristic of the product formed of spring steel is significantly deteriorated in use due to the presence of the color-developing plating layer present for distinction, it cannot be put to practical use. Accordingly, the color-developing plating layer is intended to be in the optimal condition. Also, the Ni-plating layer as a lower layer is present in the optimal condition. The present invention has been completed as a result of close investigation of the optimal conditions with regard to the distinction among products, the spring characteristic and corrosion resistance. Hereinafter, this will be specifically described with reference to the accompanying drawings.
A hard drawn steel wire is plated with a two-layer plating (lower layer: Cu, upper layer: Zn) at a ratio of the thickness of the upper Zn-layer to the whole plating thickness of 30% and is drawn and formed into a coil spring. The formed hard drawn steel wire is heated under various conditions of temperatures and times and is then examined for change in color tone of the plating surface, which gives the results as shown in FIG. 1.
Further, a hard drawn steel wire is plated with a three-layer plating (lower layer: Ni, intermediate layer: Cu, upper layer: Zn) at a ratio of the thickness of the Zn-layer to the total plating thickness of the Cu-layer and the Zn-layer of 30%, and is drawn and formed into a coil spring. The formed hard drawn steel wire is heated under the same conditions as those in the above case plated with the two-layer plating and is then examined for change in color tone of the plating surface, which gives the same results as shown in FIG. 1.
The change in color tone is closely dependent on the heating temperature and the heating time. There almost instantaneously occurs a color change from white to gold capable of being distinguished by the naked eye under the following condition: in the temperature range of the practical low temperature annealing (250.degree.-400.degree. C.), when being at 250.degree. C., the healing time is 4 min. or more, and when being at 400.degree. C., the heating time is 2 min. or more.
As a result of such experiments, the heating time <t> required for generating the above color change in a temperature T (.degree. C.) within the range of 250.degree.-400.degree. C. is expressed as the following equation (1).
log t.gtoreq.1.193-2,386.times.10.sup.-3 T (1)
Further, the hard drawn steel wire is plated with the same two-layer plating as the above at various plating thicknesses, and is drawn and spring-formed in the same manner as the above. The resultant hard drawn steel wire is then heated at 400.degree. C. for 5 min. or more to form a Cu-Zn alloy plating layer, which gives the relationship between the content of Zn(%) in the alloy and the color tone as shown in FIG. 2.
Also, the hard drawn steel wire is plated with the same three-layer plating as the above at various plating thicknesses, and is drawn and spring-formed in the same manner as the above. The resultant hard drawn steel wire is then heated at 400.degree. C. for 5 min. or more for alloying Cu in the intermediate layer and Zn in the upper layer by mutual diffusion to thus form a Cu-Zn alloy plating layer, which gives the same relationship as that in the case plated with the two-layer plating.
Referring to FIG. 2, in the range of 20-45% of Zn, there appears the beautiful color tone of gold functioning to distinguish and preventing the mixing of the different materials, and which also significantly improves the surface appearance. Further, in the range of 5-10% Zn, there appears the color tone strongly affected by the color of Cu (red copper color) of a plating component, which is significantly different from the color of white (color of Zn) of the as-plated surface, and consequently, the spring thus treated is sufficiently distinguished from the ordinary spring having the surface colored in white (color of metal), it thus having a practical use.
One of the important properties of the product formed of spring steel lies in the corrosion resistance. From this viewpoint, the spring plated with the same two-layer plating as shown in FIG. 2 is examined,which gives a relationship between the Zn (%) in a Cu-Zn alloy plating layer and the rusting time (the time when the material becomes corroded) by a salt spray test using a solution containing 3% salt. The results are shown in FIG. 3. It is evident from this Figure that at a plating layer thickness of 2 .mu.m or more, the corrosion resistance is improved with increase in Zn content (%), and at a Zn content of 5-45%, the rusting time is made longer as compared with the non-plated hard drawn steel wire. It is apparent that the presence of the plating layer does not deteriorate the characteristic of the spring material but preferably improves it. At a plating layer thickness of 1 .mu.m, the plating layer is affected by the irregularities of surface of the spring material, thus exerting no effect on improvement of the corrosion resistance. In addition, when using a SUS 304 stainless steel wire in place of the hard steel drawn wire as a spring wire, the rusting time is obtained by adding the value as shown in FIG. 3 to the rusting time (185 hrs.) of the SUS 304 stainless steel spring itself.
Further, the spring plated with the same three-layer plating as the above is examined, which gives a relationship between the Zn (%) in a Cu-Zn alloy plating layer and the rusting time (the time the material becomes corroded) on the different thicknesses of the alloy plating layer and the lower Ni-layer, by a salt spray test using a solution containing 3% salt. The results are shown in FIG. 3. It is evident from this Figure that the corrosion resistance is improved by the presence of the Cu-Zn alloy plating layer, the rusting time is made longer with increase in Zn content thus improving the corrosion resistance. In particular, at a Zn content of 10% or more, the corrosion resistance is preferably improved, and the thickness thereof is preferably 2 .mu.m or more. As for the lower Ni-plating layer, the thickness thereof is preferably 2 .mu.m or more. In the case of the Cu-Zn alloy plating layer of 1 .mu.m and the lower Ni-plating layer of 1 .mu.m, the plating layer is affected by the irregularities of surface of the spring material which decreases the effect of improving the corrosion resistance. Preferably, each thickness of the Cu-Zn alloy plating layer and the lower Ni-layer is 2 .mu.m or more. The corrosion resistance is enhanced with increase in each thickness. However, when the thicknesses of the Cu-Zn alloy plating layer and the Ni-plating layer exceed 25 .mu.m and 30 .mu.m, respectively, the corrosion resistance is not enhanced in proportion to the increase in the thicknesses. Accordingly, economically, the thicknesses of the Cu-Zn alloy plating layer and the Ni-plating layer are respectively 25 .mu.m or less and 30 .mu.m or less, respectively.
Hard drawn steel wire material of 3.5 mm is plated with a two-layer plating of Cu-Zn and is drawn at a reduction ratio of 91.7% to a diameter of 1 mm.phi., after which it is heated at 400.degree. C. for 5 min. to be thus alloyed. Similarly, a stainless steel wire material of 2.5 mm.phi. is plated with a two-layer plating and is drawn at a reduction ratio of 84% to a diameter of 1 mm.phi., after which it is heated under the same condition as the above, to be thus alloyed. FIG. 4 shows a relationship between the Hunter's rotational bending fatigue strength and Zn content (%) with respect to the above wire materials. The hard drawn steel wire and the stainless steel wire are not reduced in fatigue strength at the plating layer thickness of 25 .mu.m or less; however, they are apparently reduced in fatigue strength at the plating layer thickness of 30 .mu.m. Accordingly, in practical use, the plating thickness is, preferably, less than 30 .mu.m. The same is true for the coil spring (spring steel product).
The above data is obtained for the spring steel material being a wire and the product formed of spring steel being a coil spring; however, the data is almost similar to that in the case of the spring steel material being a sheet and the product formed of spring steel being a sheet spring.
In summary, in the two-layer plating of Cu-Zn for the product formed of a spring steel, the following condition is preferable: the Cu-Zn alloy composition is within the range of 4-45% Zn in view of the color tone effect; the plating thickness is 2 .mu.m or more in view of corrosion resistance, and is 25 .mu.m or less in view of preventing reduction in fatigue strength; and the low temperature annealing condition for coloring is 250.degree. C..times.4 min. or more to 400.degree. C..times.2 min. or more.
Further, in the three-layer plating (lower layer: Ni, intermediate layer: Cu, upper layer: Zn) for the product formed of a spring steel, the thickness of the lower Ni-layer is preferably 2 .mu.m or more in view of the corrosion resistance, and 30 .mu.m or less in view of economy. In a color Cu-Zn alloy plating layer, the following condition is preferable: the Cu-Zn alloy composition is within the range of 10-45% Zn in view of the color tone effect; the plating thickness is 2 .mu.m or more in view of the corrosion resistance, and is 25 .mu.m or less in the view of economy; and the low temperature annealing condition for coloring is 250.degree. C..times.4 min. or more to 400.degree. C..times.2 min. or more.
The color developing coated metal for springs and the method of using the same according to the present invention is made in consideration of the above condition. Accordingly, it is possible to achieve the color tone effect of the color Cu-Zn alloy plating layer without deteriorating the spring characteristic thereby facilitating the distinction among spring steel formed products, and also to improve the surface appearance. Further, it is possible to improve the corrosion resistance by the Cu-Zn alloy plating layer and the lower Ni-plating layer.
In addition, the method of using coated metal according to the present invention is made to satisfy the above condition and comprises the steps of: applying two-layer plating (lower layer: Cu, upper layer: Zn) or three-layer plating (lower layer: Ni, intermediate layer: Cu, upper layer: Zn) on the surface of the spring steel material; spring-forming it; heating the formed steel at 250.degree.-400.degree. C. (low temperature annealing) thereby making the plating layer becoming colored, to thus obtain the color-developing coated metal according to the present invention. However, the color-developing coated metal for springs may be obtained by other methods. For example, by a method comprising the steps of: heating the above spring material at 250.degree.-400.degree. C. for making the plating layer colored, and then spring-forming it, followed by annealing; but this method makes the manufacturing processes complex because of adding one process step, that is, a heating process step. Consequently, in the present method, the plating layer is colored by the low temperature annealing indispensable after the spring-forming process, and therefore, the present invention is simple in the manufacturing processes and hence is economically excellent.

BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a view for explaining the relationship between the heating time and temperature, and color tone change in a Cu-Zn plating layer of a spring formed product;
FIG. 2 is a view for explaining the relationship between the Zn content and the color tone in a Cu-Zn plating layer of a Spring formed product;
FIG. 3 is a view for explaining the relationship between the Zn content, and the rusting time in a Cu-Zn plating layer of a Spring formed product concerning different plating layer thickness; and
FIG. 4 is a view for explaining the relationship between the Zn content and the Hunter's rotational fatigue strength in a Cu-Zn plating layer of a spring formed product with different plating layer thickness.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
Hereinafter, the exemplary embodiments will be described with reference to the accompanying drawings.
EXAMPLE 1
A hard drawn steel wire containing 0.82% C was subjected to lead parenting, pickling and descaling to thus form a raw wire of 3.5 mm.phi.. The raw wire was plated with two-layer plating of a lower layer of Cu and an upper layer of Zn using a two-bath continuous electro-plating bath. In this case, Cu plating was applied under the following conditions: bath composition is CuSO.sub.4 :130g/1 and 62% H.sub.2 SO.sub.4 : 33cc/1 solution; pH is 1.5; temperature is 30.degree. C.; plating current density is 5A/dm.sup.2 ; and anode is Cu plate. Zn plating was applied under the following condition: bath composition is ZnSO.sub.4 .multidot.7H.sub.2 O; 410 g/l, AlCl.sub.3 .multidot.H.sub.2 O: 20g/l, and Na.sub.2 SO.sub.4 L 75g/l solution; pH is 4; current density is 5A/dm.sup.2 ; and anode is Zn plate. The plating times were set at five values for changing the Zn thickness ratio to the whole thickness: namely, 0, 5, 30, 45, and 50%. At the same time, the whole plating thickness was adjusted to become 2 .mu.m, 25 .mu.m and 30 .mu.m after drawing.
After being plated with the two-layer plating, the raw wire was drawn 8 times in the usual manner at a reduction ratio of 91.7% to a diameter of 1 mm.phi., to thus obtain an elementary wire within a strength level equivalent to 1 mm.phi. of JIS 3521 hard drawn steel wire SWC. The elementary wire of 1 mm.phi. was formed into tight springs having an outside diameter of 10 mm, length of 20 mm and a number of winding of 20. Each tight spring was heated at 150.degree. C..times.7 min., 200.degree. C..times.5 min., 250.degree. C..times.4 min., 300.degree. C..times.3.5 min., and 400.degree. C..times.2 min., and was examined for the colored state. Each tight spring after being heated was cooled and was examined for corrosion resistance by a salt spray test. Also, the elementary wire of 1 mm was subjected to the same heat treatment as the above, which was measured for tensile strength, torsion value and fatigue strength. The results are shown in Table 1.
As a comparative example, the bare wire of 1 mm.phi. formed by drawing the above raw wire of 3.5 mm.phi., and the polyester coating elementary (color tone: red) wire was tested in the same manner as the above. The polyester coating elementary wire was formed by drawing the patented steel wire of 3.5 mm.phi. to a diameter of 1 mm.phi. and dipping it in a solution formed by diluting polyester paint by thinner, followed by baking by a two-bake/two-coat system. The results are shown in Table 1.
TABLE 1__________________________________________________________________________Plating thickness Zn in plating Wire Tensile Torsion test Fatique Rusting(.mu.m) after heating diameter strength Torsion Fracture strength time in saltMaterial Total Cu Zn (%) (mm) (N/mm.sup.2) value surface (N/mm.sup.2) spray Remarks__________________________________________________________________________Hard 2 2 0 0 1.0 2120 25 good 580 10 Comparativesteel Examplewire 2 1.9 0.1 5 1.0 2100 22 good 570 12 Working(SWC) 2 1.4 0.6 30 1.0 2110 22 good 570 25 Example 2 1.1 0.9 45 1.0 2090 28 good 565 35 2 1.0 1.0 50 1.0 2090 24 good 570 39 Comparative 25 25 0 0 1.0 2070 27 good 560 25 Example 25 23.75 1.25 5 1.0 2040 24 good 560 27 Working 25 17.5 7.5 30 1.0 2060 24 good 570 55 Example 25 13.75 11.25 45 1.0 2060 25 good 560 60 25 12.5 12.5 50 1.0 2040 25 good 565 60 Comparative 30 30 0 0 1.0 2030 23 good 400 30 Example 30 28.5 1.5 5 1.0 2010 26 good 420 32 30 21.0 9.0 30 1.0 2000 27 good 400 55 30 16.5 13.5 45 1.0 2010 26 good 410 65 30 15.0 15.0 50 1.0 2040 26 good 420 65Bare wire -- -- -- *2 1.0 2170 24 good 590 5*1 -- -- -- *2 1.2 2160 27 good 585 *3__________________________________________________________________________ (Note) *1 . . . polyester coat wire *2 . . . no heating *3 . . . no rust after 300 hr
EXAMPLE 2
A stainless steel wire for a spring is subjected to bright annealing to be softened, to thus form a raw wire of 2.5 mm.phi.. The raw wire was plated with a two-layer plating and drawn in the same manner as in Example 1. The elementary wire of 1 mm.phi. was formed into a coil spring and heated, which was subjected to the same test as in Example 1.
Also, as a comparative example, the bare elementary wire of 1 mm.phi. formed by drawing the raw wire of 2.5 mm.phi. was tested. The results are shown in Table 2.
As is apparent from Tables 1 and 2, with a plating thickness ranging from 2 to 25 .mu.m, either of the tensile strength, torsion value characteristic, fatigue strength or corrosion resistance is preferable as an elementary wire for a spring. However, with a plating layer thickness of 30 .mu.m, the fatigue strength is significantly reduced, thus not having a practical use. The polyester coating elementary wire is excellent in corrosion resistance.
TABLE 2__________________________________________________________________________Plating thickness Zn in plating Wire Tensile Torsion test Fatique Rusting(.mu.m) after heating diameter strength Torsion Fracture strength time in saltMaterial Total Cu Zn (%) (mm) (N/mm.sup.2) value surface (N/mm.sup.2) spray Remarks__________________________________________________________________________Stainless 2 2 0 0 1.0 1970 12 good 310 200 Comparativesteel Examplewire for 2 1.9 0.1 5 1.0 1960 10 good 300 200 Workingspring 2 1.4 0.6 30 1.0 1950 8 good 315 220 Example(WPB) 2 1.1 0.9 45 1.0 1960 9 good 300 225 2 1.0 1.0 50 1.0 1960 10 good 310 230 Comparative 25 25 0 0 1.0 1940 10 good 290 210 Example 25 23.75 1.25 5 1.0 1940 12 good 290 220 Working 25 17.5 7.5 30 1.0 1930 10 good 295 240 Example 25 13.75 11.25 45 1.0 1920 8 good 290 250 25 12.5 12.5 50 1.0 1940 7 good 300 250 Comparative 30 30 0 0 1.0 1910 6 good 180 218 Example 30 28.5 1.5 5 1.0 1900 12 good 195 220 Working 30 21.0 9.0 30 1.0 1900 10 good 190 240 Example 30 16.5 13.5 45 1.0 1910 11 good 190 250 30 15.0 15.0 50 1.0 1920 12 good 180 250 ComparativeBare wire -- -- -- -- 1.0 1970 10 good 310 190 Example__________________________________________________________________________
EXAMPLE 3
In the elementary wire as shown in Example 1, the whole plating thickness after drawing was set to be 5 .mu.m instead of 2 .mu.m. It was formed into a coil spring, followed by heating, and was examined for a colored state. Similarly to Example 1, the thickness ratio of Zn in the alloy plating layer was made at 0, 5, 30, 45, and 50%. As is apparent from Table 3, when the plating thickness ratio of Zn layer in two-layer plating is adjusted to the extent that the Zn content in the alloy plating layer is within the range of 5-45%, the color tone is significantly changed by the heat treatment, and consequently, by the use of this color change, it is possible to positively distinguish the spring steel formed products. Also, the present invention is superior compared to when using a resin coating because the resin coating suffers from surface deterioration, such as galling in forming, decoloration and fusing. In addition, in the case of the coil spring in Example 2, (elementary wire: stainless steel wire), when the plating thickness ratio of Zn layer in the two layer plating was adjusted to the extent that the Zn content was within the range from 2 to 45% similarly to the above, the color tone was similarly changed.
The present invention is not limited to a coil spring; but may be applied for a spring material that requires a low temperature annealing after forming (forming material, torsional spring and sheet spring and the like) or the material similar thereto.
EXAMPLE 4
A hard drawn steel wire containing 0.82% was subjected to lead parenting, pickling and descaling to thus form a raw wire of 3.5 mm.phi.. The raw wire was plated with a three-layer plating of a lower layer of Ni, an intermediate layer of Cu and an upper layer of Zn using a three-bath continuous electro-plating bath. In this case, Ni plating was applied under the following condition: bath composition is nickel sulfamic acid: 450g/l, nickel chloride: 15g/l and boric acid: 30g/l; pH is 4; temperature is 50.degree. C.; and plating current density is 8A/dm.sup.2. Cu-plating was applied under the following condition: bath composition is CuSO.sub.4 130g/l and 62% H.sub.2 SO.sub.4 :33cc/l solution; pH is 1.5; temperature is 30.degree. C.; plating current density is 5A/dm.sup.2 ; and anode is Cu plate. Zn plating was applied under the following condition: bath composition is ZnSO.sub.4 .multidot.7H.sub.2 O: 410g/l, AlCl.sub.3 .multidot.HO: 20g/l, and Na.sub.2 SO.sub.4 : 75g/l solution; pH is 4; current density is 5A/dm.sup.2 ; and anode is Zn plate. The plating times were set at five values for changing the Zn-layer thickness ratio to the total thickness of Cu-layer and Zn-layer: namely, 0, 5, 10, 45, and 50%. At the same time, the total plating thickness of Ni-plating layer, Cu-layer and Zn-layer was adjusted to become 0, 1, 2, 5, 25 and 30.mu.m after drawing.
After being plated with a three-layer plating, the raw wire was drawn 8 times in the usual manner at a reduction ratio of 91.7% to a diamener of 1 mm.phi., to thus obtain an elementary wire within a strength level equivalent to 1 mm.phi. of JIS 3521 hard drawn steel wire SWC. The elementary wire of 1 mm.phi. was formed into tight springs having an outside diameter of 12 mm, length of 20 mm and a number of winding of 20. Each tight spring was heated under a condition of 150.degree. C..times.7 min., 200.degree. C..times.5 min., 250.degree. C..times.4 min., 300.degree. C..times.3.5 min., and 400.degree. C..times.2 min., which was examined for the colored state. Each tight spring after being heated was cooled and was examined for corrosion resistance by a salt spray test. Also, the elementary wire of 1 mm.phi. was subjected to the same heat treatment as the above, which was measured for tensile strength, torsion value and fatigue strength. The results are shown in Tables 4 to 6.
As a comparative example, the bare wire of 1 mm.phi. formed by drawing the above raw wire of 3.5 mm.phi., and the polyester coating elementary (color tone: red) wire was tested in the same manner as the above. The polyester coating elementary wire was formed by drawing the patented steel wire of 3.5 mm.phi. to a diameter of 1 mm.phi. and dipping it in a solution formed by diluting polyester paint by thinner, followed by baking by a two-bake/two-coat system. The results are shown in Table 3.
As is apparent form Tables 4 through 6, in the tight spring after heating, with the thickness of a lower Ni-layer being 2 .mu.m or more and the thickness of Cu-Zn alloy layer being 2 .mu.m or more, all of the tensile strength, torsion value characteristic, fatigue strength and corrosion resistance are preferable as an elementary wire for a spring. Also, this tight spring exhibits excellent corrosion resistance at a thinner thickness of the Cu-Zn alloy plating layer as compared to a spring having the Cu-Zn alloy plating layer without the lower Ni-plating layer. Further, when the thickness of the lower Ni-plating layer exceeds 30 .mu.m and the thickness of the Cu-Zn alloy plating layer exceeds 25 .mu.m, the corrosion resistance is not improved in proportion to the increase in the thickness.
TABLE 3__________________________________________________________________________Plating thickness Heating Zn in plating Color tonebefore heating (.mu.m) condition after heating before afterClass Total Cu Zn .degree.C. min. (%) heating heating Surface__________________________________________________________________________Com- 5 5 0 150 7 0 red red Goodparative 5 5 0 200 5 0 red red (galling,Example 5 5 0 250 4 0 red red discolor- 5 5 0 300 3.5 0 red red ation, 5 5 0 400 2 0 red red fusing: 5 4.75 0.25 150 7 5 white white absence) 5 4.75 0.25 200 5 5 white whiteWorking 5 4.75 0.25 250 4 5 white goldExample 5 4.75 0.25 300 3.5 5 white gold 5 4.75 0.25 400 2 5 white goldCom- 5 3.50 1.50 150 7 30 white whiteparative 5 3.50 1.50 200 5 30 white whiteExampleWorking 5 3.50 1.50 250 4 30 white goldExample 5 3.50 1.50 300 3.5 30 white gold 5 3.50 1.50 400 2 30 white goldCom- 5 2.75 2.25 1.50 7 45 white whiteparative 5 2.75 2.25 200 5 45 white whiteExampleWorking 5 2.75 2.25 250 4 45 white goldExample 5 2.75 2.25 300 3.5 45 white gold 5 2.75 2.25 400 2 45 white goldCom- 5 2.50 2.50 150 7 50 white whiteparative 5 2.50 2.50 200 5 50 white whiteExample 5 2.50 2.50 250 4 50 white white 5 2.50 2.50 300 3.5 50 white white 5 2.50 2.50 400 2 50 white white*1 100 -- -- 200 5 -- red muddy *2 red__________________________________________________________________________ (Note) *1 . . . comparative example (polyester coat) *2 . . . galling, discoloration, fusing: presence
TABLE 4__________________________________________________________________________ Zn in Cu--Zn WireSpring alloy plating diame- Tensile Torsion Test Rustingsteel Plating thickness (.mu.m) after heating ter strength Torsion Fracture time in saltmaterial Ni Cu Zn (%) (mm) (N/mm.sup.2) value surface spray (hr) Remarks__________________________________________________________________________Hard 1 0 1.0 0 0 1.0 2130 25 good 4 Compara-steel 1 0 0.95 0.05 5 1.0 2110 26 good 7 tivewire 1 0 0.90 0.10 10 1.0 2110 25 good 6 Example(SWC) 1 0 0.55 0.45 45 1.0 2080 25 good 7 1 0 0.5 0.5 50 1.0 2100 25 good 12 2 1 1.0 0 0 1.0 2100 24 good 4 Compara- 2 1 0.95 0.05 5 1.0 2080 26 good 6 tive 2 1 0.90 0.10 10 1.0 2070 26 good 6 Example 2 1 0.55 0.45 45 1.0 2100 27 good 7 2 1 0.5 0.5 50 1.0 2100 24 good 10 4 0 3.6 0.4 10 1.0 2120 25 good 14 Working 4 2 1.90 0.1 5 1.0 2100 25 good 16 Example 4 2 1.80 0.2 10 1.0 2040 23 good 18 4 2 1.10 0.90 45 1.0 2050 21 good 48 4 2 1.0 1.0 50 1.0 2100 26 good 50 Comparative Example__________________________________________________________________________
TABLE 5__________________________________________________________________________ Zn in Cu--Zn WireSpring alloy plating diame- Tensile Torsion Test Rustingsteel Plating thickness (.mu.m) after heating ter strength Torsion Fracture time in saltmaterial Total Ni Cu Zn (%) (mm) (N/mm.sup.2) value surface spray (hr) Remarks__________________________________________________________________________Hard 10 0 7 3 30 1.0 2100 25 good 40 Workingsteel 10 5 4.75 0.25 5 1.0 2120 21 good 28 Examplewire 10 5 4.50 0.50 10 1.0 2080 23 good 32(SWC) 10 5 2.75 2.25 45 1.0 2060 23 good 75 10 5 2.5 2.5 50 1.0 2090 22 good 80 Comparative 55 0 38.5 16.5 30 1.0 2040 26 good 60 Example 55 30 23.75 1.25 5 1.0 2040 27 good 50 Working 55 30 22.5 2.5 10 1.0 2030 24 good 55 Example 55 30 13.75 11.25 45 1.0 2040 24 good 95 55 30 12.5 12.5 50 1.0 2040 24 good 100 Comparative Example__________________________________________________________________________
TABLE 6__________________________________________________________________________ Zn in Cu--Zn WireSpring alloy plating diame- Tensile Torsion Test Rustingsteel Plating thickness (.mu.m) after heating ter strength Torsion Fracture time in saltmaterial Total Ni Cu Zn (%) (mm) (N/mm.sup.2) value surface spray (hr) Remarks__________________________________________________________________________Hard 75 0 52.5 22.5 30 1.0 2010 26 good 75 Comparativesteel 75 40 33.25 1.75 5 1.0 2010 25 good 60 Examplewire 75 40 31.5 3.50 10 1.0 2030 25 good 65(SWC) 75 40 19.25 15.75 45 1.0 2010 26 good 100 75 40 17.5 17.5 50 1.0 2010 26 good 105Bare -- -- -- -- -- 1.0 2160 24 good 0.5wire*1 -- -- -- -- -- 1.2 2160 27 good *2__________________________________________________________________________ (Note) *1 . . . polyester coat wire *2 . . . no rust after 300 hr
EXAMPLE 5
In the elementary wire of 1 mm.phi. as shown in Example the whole plating thickness after drawing was set to be 4 .mu.m and the thickness ratio of the Zn-layer to the total thickness of the Cu-layer and the Zn layer is changed to 0, 5, 10, 45, and 50%. Each wire was formed into a coil spring, followed by heating, and was examined for a colored state. The results are shown in Table 7 along with the manufacturing conditions such as the plating layer thickness and heating condition. As is apparent from Table 7, when the thickness ratio of the Zn-layer is selected as 10 to 45%, the Zn content in the Cu-Zn alloy plating layer after heat treatment becomes 10 to 45%. Thus, by the heat treatment under the condition of 250.degree. C..times.4 min. or more to 400.degree. C..times.2 min. or more, the color tone is changed into gold, which makes it possible to positively distinguish the spring steel formed products. Further, the present invention is superior to when a resin coating is used because the resin coating suffers from surface deterioration such as galling in forming, decoloration and fusing.
The present invention is not limited to a coil spring; but may be applied to a spring material that requires a low temperature annealing after forming (forming material, torsion spring and sheet spring and the like) or a material similar thereto.
TABLE 7__________________________________________________________________________Plating thickness Heating Zn in Cu- Color tonebefore heating (.mu.m) condition Zn alloy before afterClass Ni Cu Zn .degree.C. min. plating (%) heating heating Surface__________________________________________________________________________Com- 4 0 4 0 150 7 0 red dark red Goodparative 4 0 4 0 200 5 0 red dark red (galling,Example 4 0 4 0 250 4 0 red dark red discolor- 4 0 4 0 300 3.5 0 red dark red ation, 4 0 4 0 400 2 0 red dark red fusing:Com- 4 2 1.90 0.10 150 7 5 white white absence)parative 4 2 1.90 0.10 200 5 5 white whiteExample 4 2 1.90 0.10 250 4 5 white white 4 2 1.90 0.10 300 3.5 5 white white 4 2 1.90 0.10 400 2 5 white white 4 2 1.80 0.20 150 7 10 white white 4 2 1.80 0.20 200 5 10 white whiteWorking 4 2 1.80 0.20 250 4 10 white goldExample 4 2 1.80 0.20 300 3.5 10 white gold 4 2 1.80 0.20 400 2 10 white goldCom- 4 2 1.10 0.90 150 7 45 white whiteparative 4 2 1.10 0.90 200 5 45 white whiteExampleWorking 4 2 1.10 0.90 250 4 45 white goldExample 4 2 1.10 0.90 300 3.5 45 white gold 4 2 1.10 0.90 400 2 45 white goldCom- 4 2 1.0 1.0 150 7 50 white whiteparative 4 2 1.0 1.0 200 5 50 white whiteExample 4 2 1.0 1.0 250 4 50 white white 4 2 1.0 1.0 300 3.5 50 white white 4 2 1.0 1.0 400 2 50 white white*1 -- -- 200 5 -- red dark red *2__________________________________________________________________________ (Note) *1 . . . polyester coat *2 . . . galling, discoloration, fusing: presence

Number	Name	Date
3954420	Hyner et al.	May 1976
3966183	Mayer, Sr.	Jun 1976
4013488	Ramqvist et al.	Mar 1977
4417956	McCoy	Nov 1983
4791025	Hiromori et al.	Dec 1988
4859289	Nishimura et al.	Aug 1989

Method for facilitating distinction between different steel products

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

Parent Case Info

US Referenced Citations (6)

Divisions (1)