METHOD FOR FORMING A LAYER OF COLOURED GLASS ON A GLASS SUBSTRATE BY FLAME PYROLYSIS

Abstract

A process includes the formation of a colored glass layer on a glass substrate by flame pyrolysis of a solution including at least one precursor of a cobalt, iron, manganese, chromium, silver, copper, gold or selenium oxide, alone or as a mixture of several of them. Moreover, a glass substrate is coated with a layer of colored glass obtained by such a process.

Description

The invention relates to the production of articles made of colored glass.

The color of a glass is given to it by its composition.

Thus, when it is desired to change from the production of colorless glass to the production of colored glass or from the production of colored glass to the production of glass of another color, it is possible first of all to think of changing the composition of the starting materials on one and the same plant. However, the glass obtained in the transitional phase, before stabilization of the new color desired, is obtained in a large amount and has to be discarded.

On the other hand, colored glass can be obtained via thin layers, such as formed by cathode sputtering, in particular magnetron cathode sputtering. However, the color is obtained by interference and thus can only be obtained on one side: either in transmission or in reflection, but not both.

Another route consists in forming a colored coating by the sol-gel process. For example, a glass substrate can be printed by means of a sol-gel solution using silk screen printing or another technique. The sol-gel coating has to be dried and cured in order to exhibit the color and the mechanical strength desired. This process is relatively lengthy and can only be carried out outside the production line.

The invention has had the objective of obtaining colored glass in a simple and practical way, not requiring in particular the modification of the composition of starting materials of a glass substrate, relatively short in time and being able to be carried out on the line for the production of the glass substrate.

This objective is achieved by the invention which consequently has as subject matter a process for the formation of a colored glass layer on a glass substrate by flame pyrolysis of a solution comprising at least one precursor of a cobalt, iron, manganese, chromium, silver, copper, gold or selenium oxide, alone or as a mixture of several of them.

The color of the glass thus coated is visible in transmission and in reflection. Flame pyrolysis requires a simple plant which can be easily incorporated on a float glass line, for example.

Varied colors can be obtained in this way: blue with a cobalt or manganese oxide, yellow with a chromium or silver oxide, red with a copper oxide, purple with a manganese oxide, pink and ruby red with a gold oxide, orangey yellow to red with a selenium oxide. It is possible, by varying the composition of metal oxides, to obtain colors such as green, gray and brown, and each color in varied shades.

According to other preferred characteristics of the process of the invention:

• • precursors in solution are introduced into and then decomposed in a burner to give glass nanoparticles which are deposited on said glass substrate at a temperature between ambient temperature and 600° C.;
  • said precursors consist of organometallic compounds and/or salts;
  • said precursors are soluble in alcoholic solution;
  • the distance from the burner to the glass substrate is at most equal to 10 mm, preferably to 8 mm and particularly preferably to 6 mm; there is thus obtained a layer of colored glass which is dense, as can be characterized with a scanning electron microscope; the further the burner from the substrate, the larger the particles deposited, the layer formed becomes porous until existing in the form of a powder no longer constituting a layer. The distance from the burner to the glass substrate is at least equal to 2 mm.

Another subject matter of the invention is a glass substrate coated with a layer of colored glass obtained by a process as described above, characterized in that the thickness of the layer of colored glass is between 50 and 10 000 nm.

The invention is now illustrated by the following examples.

EXAMPLE 1

A 1% by weight cobalt acetylacetonate solution is prepared which has the following composition (amounts shown in grams):

Absolute ethanol           480 (g)
Tetraethoxysilane (TEOS)   65
Aluminum tri(sec-butoxide) 10
Triethoxyborane            55
Magnesium methoxyethoxide  5
Calcium methoxyethoxide    8
Potassium t-butoxide       3
Cobalt acetylacetonate     1.5
Hydrochloric acid          2

A layer of blue glass is formed by flame pyrolysis on a 10 cm×10 cm sample of soda-lime glass. The above solution is sprayed onto the sample in the flame with the orifice of a burner in the form of a slit with a length of 20 cm.

The flow rates employed in the burner are:

2 ml/min of the above solution,160 l/min of air and8 1/min of propane.

The burner is moved above the glass sample at an unchanging distance of 5 mm and at a speed of 3 m/min.

The glass sample is at a temperature of between 450 and 600° C.

Thirty passes of the burner above the sample are carried out.

The thickness of the layer deposited is between 200 and 600 nm.

The coated sample is blue in transmission and in reflection.

EXAMPLE 2

A 500 ml solution in ethanol of the following oxide precursors is prepared:

Tetraethoxysilane

Triethoxyborane

Sodium nitrateLithium ethoxide andCobalt acetylacetonate.

The amounts are such that the blue glass of the layer which is formed by flame pyrolysis comprises, as % by weight:

SiO2 56 (%)
B2O3 12
Na2O 28
LiO  2
CoO  2

The conditions of example 1 are reproduced but with a flow rate of the solution of precursors of 1 ml/min.

The distance from the burner to the glass sample is 4 mm.

The sample is at a temperature of between 500 and 600° C.

Twelve passes of the burner above the sample are carried out here.

The thickness of the layer deposited is between 50 and 150 nm.

The coated sample is blue in transmission and in reflection.

EXAMPLE 3

Example 2 is reproduced, additionally using calcium methoxyethoxide as CaO precursor.

The composition of the blue glass layer formed by flame pyrolysis is, as % by weight:

SiO2 74 (%)
Na2O 14
CaO  10.2
CoO  1.8

The operating conditions and the observations with regard to the product obtained are the same as in example 2.

In the three examples, the layer formed is dense, as may be observed with a scanning electron microscope.

Claims

1. A process comprising forming a colored glass layer on a glass substrate by flame pyrolysis of a solution comprising at least one precursor of a cobalt, iron, manganese, chromium, silver, copper, gold or selenium oxide, alone or as a mixture of several of them.

2. The process as claimed in claim 1, wherein precursors in solution are introduced into and then decomposed in a burner to give glass nanoparticles which are deposited on said glass substrate at a temperature between ambient temperature and 600° C.

3. The process as claimed in claim 2, wherein said precursors consist of organometallic compounds and/or salts.

4. The process as claimed in claim 2, wherein said precursors are soluble in alcoholic solution.

5. The process as claimed in claim 1, wherein a distance from the burner to the glass substrate is at most equal to 10 mm.

6. A glass substrate coated with a layer of colored glass obtained by a process as claimed in claim 1, wherein a thickness of the layer of colored glass is between 50 et 10 000 nm.