Patent Application
20130154151
Natural polymers are produced in nature by absorbing carbon dioxide, a greenhouse gas responsible for global warming. The materials containing natural biopolymers will have reduced environmental foot print in terms of the overall energy savings, reduction of greenhouse gas emissions, etc. throughout the life cycle of the products, including raw material productions, manufacturing, distribution, use, end-of-life disposal, etc. In particular, there is an increased business need to develop biomaterial-based and biodegradable thin films for use in the field of absorbent articles, such as infant and child care products, feminine hygiene products, and adult incontinence products, etc. For instance, these films can be employed in backsheets of absorbent articles. None of the current commercially available biomaterial-based and biodegradable materials alone meet the application needs of such products. Polylactic acid, for example, is generally too rigid for quiet flexible film applications and tends to have performance in use issues, such as causing noisy rustles for adult feminine products. Aliphatic-aromatic copolyester films, such as Ecoflex® films are synthetic polymer films made from petroleum and do not contain any natural or biomaterial-based polymer component needed for the intended application and their costs are also too high for such intended applications. Pure copolyester films also exhibit poor converting processability for fabricating cast films. The resultant films are too sticky and cannot be collected by winding up on a roll. The copolyester cast films also tend to block easily making it very difficult, if not impossible, to separate into individual layers after it is produced. Thermoplastic starch has also been tried, but it cannot be made into thin films due to limited processability. Pure thermoplastic starch films are also very brittle and too rigid to be useful for soft flexible film applications.
In view of these difficulties and shortcomings of currently available materials, an unmet need exists in the thin films for personal care product applications. It is highly desirable to invent relatively inexpensive polymer blend formulations that can be used to create soft and malleable thermoplastic cast film that contains a significant amount of naturally-derived biodegradable components.
In accordance with one embodiment, a method for forming a thermoplastic composition is disclosed. The method comprises supplying a renewable biopolymer, polyolefin, and a compatibilizer to a feed section of an extruder, wherein the compatibilizer has a polar component and a non-polar component. A liquid plasticizer is directly injected into the extruder so that the plasticizer mixes with the biopolymer, polyolefin, and compatibilizer to form a blend. The blend is melt processed within the extruder to form the thermoplastic composition.
In accordance with another embodiment of the present invention, a method for forming a film is disclosed. The method comprises supplying a renewable biopolymer, polyolefin, and a compatibilizer to a feed section of an extruder, wherein the compatibilizer has a polar component and a non-polar component. A liquid plasticizer is directly injected into the extruder so that the plasticizer mixes with the biopolymer, polyolefin, and compatibilizer to form a blend. The blend is melt processing within the extruder to form a thermoplastic composition. The composition is extruded through a die and onto a surface to form a film, wherein the film has a thickness of about 50 micrometers or less.
Other features and aspects of the present invention are discussed in greater detail below.
A full and enabling disclosure of the present invention, including the best mode thereof, directed to one of ordinary skill in the art, is set forth more particularly in the remainder of the specification, which makes reference to the appended figures in which:
Repeat use of reference characters in the present specification and drawings is intended to represent same or analogous features or elements of the invention.
As used herein, the term “biodegradable” generally refers to a material that degrades from the action of naturally occurring microorganisms, such as bacteria, fungi, and algae; environmental heat; moisture; or other environmental factors.
The degree of degradation may be determined according to ASTM Test Method 5338.92.
As used herein, the term “renewable” generally refers to a material that can be produced or is derivable from a natural source that is periodically (e.g., annually or perennially) replenished through the actions of plants of terrestrial, aquatic or oceanic ecosystems (e.g., agricultural crops, edible and non-edible grasses, forest products, seaweed, or algae), microorganisms (e.g., bacteria, fungi, or yeast), and so forth
Reference now will be made in detail to various embodiments of the invention, one or more examples of which are set forth below. Each example is provided by way of explanation of the invention, not limitation of the invention. In fact, it will be apparent to those skilled in the art that various modifications and variations may be made in the present invention without departing from the scope or spirit of the invention. For instance, features illustrated or described as part of one embodiment, may be used on another embodiment to yield a still further embodiment. Thus, it is intended that the present invention covers such modifications and variations as come within the scope of the appended claims and their equivalents.
Generally speaking, the present invention is directed to a method for forming a thermoplastic composition that contains a combination of a renewable biopolymer (e.g., starch polymer) with a polyolefin that enhances the processability of the biopolymer and also helps improves certain mechanical properties of the resulting film. Contrary to conventional techniques for incorporating a biopolymer into a thermoplastic composition, the method of the present invention does not involve pre-compounding the biopolymer with a plasticizer. Instead, the biopolymer and polyolefin are supplied to the extruder at a feed section. The plasticizer is directly injected into the extruder in the form of a liquid so that it forms a thermoplastic biopolymer in situ within the extruder and then a homogeneous blend. In this manner, the costly and time-consuming steps of pre-encapsulation or pre-compounding of the plasticizer and biopolymer into a thermoplastic biopolymer are not required. Despite facing a number of challenges, the present inventors have found that the in situ addition of the plasticizer is facilitated by a compatibilizer having a polar component with an affinity for the biopolymer and a non-polar component with an affinity for the polyolefin. Such a compatibilizer can have both short- and long-term benefits to the composition. Namely, when the polymers are initially added to the extruder, the compatibilizer can help facilitate the ability of the biopolymer to be melt processed for a short time until it can be rendered thermoplastic through mixture with the plasticizer. Further, upon mixing with the plasticizer, the compatibilizer can also help ensure that the resulting composition remains generally homogeneous and does not separate into constituent phases. This results in a finely dispersed polymer system that exhibits the combined attributes of good polymer processability, biodegradability, and mechanical strength.
Various embodiments of the present invention will now be described in more detail.
A. Biopolymer
The biopolymer that is employed in the thermoplastic composition of the present invention may include, for instance, starches, as well as other carbohydrate polymers, such as cellulose or cellulose derivatives (e.g., cellulose ethers and esters), hemicellulose, etc.; lignin derivatives; protein materials (e.g., gluten, soy protein, zein, etc.); algae materials; alginate; etc., as well as combinations thereof. For example, starch is a biopolymer composed of amylose and amylopectin. Amylose is essentially a linear polymer having a molecular weight in the range of 100,000-500,000, whereas amylopectin is a highly branched polymer having a molecular weight of up to several million. Although starch is produced in many plants, typical sources includes seeds of cereal grains, such as corn, waxy corn, wheat, sorghum, rice, and waxy rice; tubers, such as potatoes; roots, such as tapioca (i.e., cassaya and manioc), sweet potato, and arrowroot; and the pith of the sago palm.
Broadly speaking, any natural (unmodified) and/or modified starch may be employed in the present invention. Modified starches, for instance, are often employed that have been chemically modified by typical processes known in the art (e.g., esterification, etherification, oxidation, acid hydrolysis, enzymatic hydrolysis, etc.). Starch ethers and/or esters may be particularly desirable, such as hydroxyalkyl starches, carboxymethyl starches, etc. The hydroxyalkyl group of hydroxylalkyl starches may contain, for instance, 1 to 10 carbon atoms, in some embodiments from 1 to 6 carbon atoms, in some embodiments from 1 to 4 carbon atoms, and in some embodiments, from 2 to 4 carbon atoms. Representative hydroxyalkyl starches such as hydroxyethyl starch, hydroxypropyl starch, hydroxybutyl starch, and derivatives thereof. Starch esters, for instance, may be prepared using a wide variety of anhydrides (e.g., acetic, propionic, butyric, and so forth), organic acids, acid chlorides, or other esterification reagents. The degree of esterification may vary as desired, such as from 1 to 3 ester groups per glucosidic unit of the starch.
Regardless of whether it is in a native or modified form, the starch may contain different percentages of amylose and amylopectin, different size starch granules and different polymeric weights for amylose and amylopectin. High amylose starches contain greater than about 50% by weight amylose and low amylose starches contain less than about 50% by weight amylose. Although not required, low amylose starches having an amylose content of from about 10% to about 40% by weight, and in some embodiments, from about 15% to about 35% by weight, are particularly suitable for use in the present invention. Examples of such low amylose starches include corn starch and potato starch, both of which have an amylose content of approximately 20% by weight. Such low amylose starches typically have a number average molecular weight (“Mn”) ranging from about 50,000 to about 1,000,000 grams per mole, in some embodiments from about 75,000 to about 800,000 grams per mole, and in some embodiments, from about 100,000 to about 600,000 grams per mole, as well as a weight average molecular weight (“Mw”) ranging from about 5,000,000 to about 25,000,000 grams per mole, in some embodiments from about 5,500,000 to about 15,000,000 grams per mole, and in some embodiments, from about 6,000,000 to about 12,000,000 grams per mole. The ratio of the weight average molecular weight to the number average molecular weight (“Mw/Mn”), i.e., the “polydispersity index”, is also relatively high. For example, the polydispersity index may range from about 20 to about 100. The weight and number average molecular weights may be determined by methods known to those skilled in the art.
B. Plasticizer
As indicated above, a liquid plasticizer is also employed in the thermoplastic composition to help render the biopolymer melt-processable. For example, starches normally exist in the form of granules that have a coating or outer membrane that encapsulates the more water-soluble amylose and amylopectin chains within the interior of the granule. When heated, polar solvents (“plasticizers”) may soften and penetrate the outer membrane and cause the inner starch chains to absorb water and swell. This swelling will, at some point, cause the outer shell to rupture and result in an irreversible destructurization of the starch granule. Once destructurized, the starch polymer chains containing amylose and amylopectin polymers, which are initially compressed within the granules, will stretch out and form a generally disordered intermingling of polymer chains. Upon resolidification, however, the chains may reorient themselves to form crystalline or amorphous solids having varying strengths depending on the orientation of the starch polymer chains. Because the starch (natural or modified) is thus capable of melting and resolidifying, it is generally considered a “thermoplastic starch.”
Suitable liquid plasticizers may include, for instance, polyhydric alcohol plasticizers, such as sugars (e.g., glucose, sucrose, fructose, raffinose, maltodextrose, galactose, xylose, maltose, lactose, mannose, and erythrose), sugar alcohols (e.g., erythritol, xylitol, malitol, mannitol, glycerol (or glycerin), and sorbitol), polyols (e.g., ethylene glycol, propylene glycol, dipropylene glycol, butylene glycol, and hexane triol), etc. Also suitable are hydrogen bond forming organic compounds which do not have hydroxyl group, including urea and urea derivatives; anhydrides of sugar alcohols such as sorbitan; animal proteins such as gelatin; vegetable proteins such as sunflower protein, soybean proteins, cotton seed proteins; and mixtures thereof. Other suitable plasticizers may include phthalate esters, dimethyl and diethylsuccinate and related esters, glycerol triacetate, glycerol mono and diacetates, glycerol mono, di, and tripropionates, butanoates, stearates, lactic acid esters, citric acid esters, adipic acid esters, stearic acid esters, oleic acid esters, and other acid esters. Aliphatic acids may also be used, such as ethylene acrylic acid, ethylene maleic acid, butadiene acrylic acid, butadiene maleic acid, propylene acrylic acid, propylene maleic acid, and other hydrocarbon based acids. A low molecular weight plasticizer is preferred, such as less than about 20,000 g/mol, preferably less than about 5,000 g/mol and more preferably less than about 1,000 g/mol.
The relative amount of biopolymers and plasticizers employed in the thermoplastic composition may vary depending on a variety of factors, such as the molecular weight of the biopolymer, the type of biopolymer (e.g., modified or unmodified), the affinity of the plasticizer for the biopolymer, etc. Typically, however, the weight ratio of biopolymers to plasticizers is from about 1 to about 10, in some embodiments from about 1.5 to about 8, and in some embodiments, from about 2 to about 6. For example, biopolymers may constitute from about 5 wt. % to about 50 wt. %, in some embodiments from about 10 wt. % to about 40 wt %, and in some embodiments, from about 15 wt. % to about 30 wt. % of the composition, while plasticizers may constitute from about 0.5 wt. % to about 20 wt. %, in some embodiments from about 1 wt. % to about 15 wt. %, and in some embodiments, from about 5 wt. % to about 10 wt. % of the composition. It should be understood that the weight of biopolymers referenced herein includes any bound water that naturally occurs in the starch before mixing it with other components to form the thermoplastic starch. Starches, for instance, typically have a bound water content of about 5% to 16% by weight of the starch.
C. Polyolefin
As indicated above, a polyolefin is also employed in the film. Among other things, the polyolefin helps to counteract the stiffness of the biopolymer, thereby improving ductility and melt processability of the film. Such polyolefins are typically employed in an amount of from about 10 wt. % to about 50 wt. %, in some embodiments from about 20 wt. % to about 45 wt. %, and in some embodiments, from about 25 wt. % to about 40 wt. % of the polymer content of the thermoplastic composition.
Exemplary polyolefins for this purpose may include, for instance, polyethylene, polypropylene, blends and copolymers thereof. In one particular embodiment, a polyethylene is employed that is a copolymer of ethylene and an α-olefin, such as a C3-C20 α-olefin or C3-C12 α-olefin. Suitable α-olefins may be linear or branched (e.g., one or more C1-C3 alkyl branches, or an aryl group). Specific examples include 1-butene; 3-methyl-1-butene; 3,3-dimethyl-1-butene; 1-pentene; 1-pentene with one or more methyl, ethyl or propyl substituents; 1-hexene with one or more methyl, ethyl or propyl substituents; 1-heptene with one or more methyl, ethyl or propyl substituents; 1-octene with one or more methyl, ethyl or propyl substituents; 1-nonene with one or more methyl, ethyl or propyl substituents; ethyl, methyl or dimethyl-substituted 1-decene; 1-dodecene; and styrene. Particularly desired α-olefin co-monomers are 1-butene, 1-hexene and 1-octene. The ethylene content of such copolymers may be from about 60 mole % to about 99 mole %, in some embodiments from about 80 mole % to about 98.5 mole %, and in some embodiments, from about 87 mole % to about 97.5 mole %. The α-olefin content may likewise range from about 1 mole % to about 40 mole %, in some embodiments from about 1.5 mole % to about 15 mole %, and in some embodiments, from about 2.5 mole % to about 13 mole %.
The density of the polyethylene may vary depending on the type of polymer employed, but generally ranges from 0.85 to 0.96 grams per cubic centimeter (“g/cm3”). Polyethylene “plastomers”, for instance, may have a density in the range of from 0.85 to 0.91 g/cm3. Likewise, “linear low density polyethylene” (“LLDPE”) may have a density in the range of from 0.91 to 0.940 g/cm3; “low density polyethylene” (“LDPE”) may have a density in the range of from 0.910 to 0.940 g/cm3; and “high density polyethylene” (“HDPE”) may have density in the range of from 0.940 to 0.960 g/cm3. Densities may be measured in accordance with ASTM 1505. Particularly suitable ethylene-based polymers for use in the present invention may be available under the designation EXACT™ from ExxonMobil Chemical Company of Houston, Tex. Other suitable polyethylene plastomers are available under the designation ENGAGE™ and AFFINITY™ from Dow Chemical Company of Midland, Mich. Still other suitable ethylene polymers are available from The Dow Chemical Company under the designations DOWLEX™ (LLDPE) and ATTANE™ (ULDPE). Other suitable ethylene polymers are described in U.S. Pat. No. 4,937,299 to Ewen et al.; U.S. Pat. No. 5,218,071 to Tsutsui et al.; U.S. Pat. No. 5,272,236 to Lai, et al.; and U.S. Pat. No. 5,278,272 to Lai, et al., which are incorporated herein in their entirety by reference thereto for all purposes.
Of course, the present invention is by no means limited to the use of ethylene polymers. For instance, propylene polymers may also be suitable for use as a semi-crystalline polyolefin. Suitable propylene polymers may include, for instance, polypropylene homopolymers, as well as copolymers or terpolymers of propylene with an α-olefin (e.g., C3-C20), such as ethylene, 1-butene, 2-butene, the various pentene isomers, 1-hexene, 1-octene, 1-nonene, 1-decene, 1-unidecene, 1-dodecene, 4-methyl-1-pentene, 4-methyl-1-hexene, 5-methyl-1-hexene, vinylcyclohexene, styrene, etc. The comonomer content of the propylene polymer may be about 35 wt. % or less, in some embodiments from about 1 wt. % to about 20 wt. %, and in some embodiments, from about 2 wt. % to about 10 wt. %. The density of the polypropylene (e.g., propylene/α-olefin copolymer) may be 0.95 grams per cubic centimeter (g/cm3) or less, in some embodiments, from 0.85 to 0.92 g/cm3, and in some embodiments, from 0.85 g/cm3 to 0.91 g/cm3. Suitable propylene polymers are commercially available under the designations VISTAMAXX™ from ExxonMobil Chemical Co. of Houston, Tex.; FINA™ (e.g., 8573) from Atofina Chemicals of Feluy, Belgium; TAFMERT™ available from Mitsui Petrochemical Industries; and VERSIFY™ available from Dow Chemical Co. of Midland, Mich. Other examples of suitable propylene polymers are described in U.S. Pat. No. 6,500,563 to Datta, et al.; U.S. Pat. No. 5,539,056 to Yang, et al.; and U.S. Pat. No. 5,596,052 to Resconi, at al., which are incorporated herein in their entirety by reference thereto for all purposes.
Any of a variety of known techniques may generally be employed to form the polyolefins. For instance, olefin polymers may be formed using a free radical or a coordination catalyst (e.g., Ziegler-Natta or metallocene). Metallocene-catalyzed polyolefins are described, for instance, in U.S. Pat. No. 5,571,619 to McAlpin at al.; U.S. Pat. No. 5,322,728 to Davis et al.; U.S. Pat. No. 5,472,775 to Obijeski at al.; U.S. Pat. No. 5,272,236 to Lai et al.; and U.S. Pat. No. 6,090,325 to Wheat, et al., which are incorporated herein in their entirety by reference thereto for all purposes.
The melt flow index (MI) of the polyolefins may generally vary, but is typically in the range of about 0.1 grams per 10 minutes to about 100 grams per 10 minutes, in some embodiments from about 0.5 grams per 10 minutes to about 30 grams per 10 minutes, and in some embodiments, about 1 to about 10 grams per 10 minutes, determined at 190° C. The melt flow index is the weight of the polymer (in grams) that may be forced through an extrusion rheometer orifice (0.0825-inch diameter) when subjected to a force of 2160 grams in 10 minutes at 190° C., and may be determined in accordance with ASTM Test Method D1238-E.
D. Compatibilizer
To improve the compatibility and dispersion characteristics of biopolymers and polyolefins, a compatibilizer is employed in the thermoplastic composition. Typically, the compatibilizer constitutes from about 0.1 wt. % to about 15 wt. %, in some embodiments from about 0.5 wt. % to about 10 wt. %, and in some embodiments, from about 1 wt. % to about 5 wt. % of the composition. The compatibilizer generally possesses a polar component provided by one or more functional groups that are compatible with the biopolymer and a non-polar component provided by an olefin that is compatible with the polyolefin. The olefin component of the compatibilizer may generally be formed from any linear or branched α-olefin monomer, oligomer, or polymer (including copolymers) derived from an olefin monomer. For example, the compatibilizer may include polyethylene-co-vinyl acetate (EVA), polyethylene-co-vinyl alcohol (EVOH), polyethylene-co-acrylic (EAA), etc. in which the olefin component is provided by the polyethylene backbone. In other embodiments, the olefin component may be formed from an α-olefin monomer, which typically has from 2 to 14 carbon atoms and preferably from 2 to 6 carbon atoms. Examples of suitable monomers include, but not limited to, ethylene, propylene, butene, pentene, hexene, 2-methyl-1-propene, 3-methyl-1-pentene, 4-methyl-1-pentene, and 5-methyl-1-hexene. Examples of polyolefins include both homopolymers and copolymers, i.e., polyethylene, ethylene copolymers such as EPDM, polypropylene, propylene copolymers, and polymethylpentene polymers. An olefin copolymer can include a minor amount of non-olefinic monomers, such as styrene, vinyl acetate, diene, or acrylic and non-acrylic monomer. Functional groups may be incorporated into the polymer backbone using a variety of known techniques. For example, a monomer containing the functional group may be grafted onto a polyolefin backbone to form a graft copolymer. Such grafting techniques are well known in the art and described, for instance, in U.S. Pat. No. 5,179,164. In other embodiments, the monomer containing the functional groups may be copolymerized with an olefin monomer to form a block or random copolymer.
Regardless of the manner in which it is incorporated, the functional group of the compatibilizer may be any group that provides a polar segment to the molecule, such as a carboxyl group, acid anhydride group, amide group, imide group, carboxylate group, epoxy group, amino group, isocyanate group, group having oxazoline ring, hydroxyl group, and so forth. Maleic anhydride modified polyolefins are particularly suitable for use in the present invention. Such modified polyolefins are typically formed by grafting maleic anhydride onto a polymeric backbone material. Such maleated polyolefins are available from E.I. du Pont de Nemours and Company under the designation Fusabond®, such as the P Series (chemically modified polypropylene), E Series (chemically modified polyethylene), C Series (chemically modified ethylene vinyl acetate), A Series (chemically modified ethylene acrylate copolymers or terpolymers), or N Series (chemically modified ethylene-propylene, ethylene-propylene diene monomer (“EPDM”) or ethylene-octene). Alternatively, maleated polyolefins are also available from Chemtura Corp. under the designation Polybond® and Eastman Chemical Company under the designation Eastman G series, and AMPLIFY™ GR Functional Polymers (maleic anhydride grafted polyolefins). In one particular embodiment, the compatibilizer is a graft copolymer of polyethylene and maleic anhydride having the structure shown below:
The cyclic anhydride at one end is chemically bonded directly into the polyethylene chain. The polar anhydride group of the molecule could, in one embodiment, associate with hydroxyl groups of a starch biopolymer via both hydrogen bonding and polar-polar molecular interactions and a chemical reaction to form an ester linkage during the melt extrusion process. The hydroxyls of the starch will undergo esterification reaction with the anhydride to achieve a ring-opening reaction to chemically link the starch polymer to the maleic anhydride to the grafted polyethylene. This reaction is accomplished under the high temperatures and pressures of the extrusion process.
E. Additional Biodegradable Polymer
Generally speaking, a majority of the polymers employed in the composition are biodegradable polymers. For example, from about 50 wt. % to about 90 wt. %, in some embodiments from about 55 wt. % to about 80 wt. %, and in some embodiments, from about 60 wt. % to about 75 wt. % of the polymers employed in the composition are biodegradable polymers. In one embodiment, for example, substantially all of the biodegradable polymers are renewable biopolymers, such as described above. Alternatively, however, other types of biodegradable polymers may also be employed to help further improve the ability to melt process the thermoplastic composition. In such embodiments, the additional biodegradable polymers may constitute from about 10 wt. % to about 70 wt. %, in some embodiments from about 20 wt. % to about 60 wt. %, and in some embodiments, from about 30 wt. % to about 50 wt. % of the polymer content of the thermoplastic composition, while the biopolymers may likewise constitute from about 1 wt. % to about 35 wt. %, in some embodiments from about 5 wt. % to about 30 wt. %, and in some embodiments, from about 10 wt. % to about 25 wt. % of the polymer content of the thermoplastic composition.
One particularly suitable type of biodegradable polymer that may be employed in conjunction with the biopolymer is a biodegradable polyester. Such biodegradable polyesters typically have a relatively low glass transition temperature (“Tg”) to reduce stiffness of the film and improve the processability of the polymers. For example, the Tg may be about 25° C. or less, in some embodiments about 0° C. or less, and in some embodiments, about −10° C. or less. Likewise, the melting point of the biodegradable polyesters is also relatively low to improve the rate of biodegradation. For example, the melting point is typically from about 50° C. to about 180° C., in some embodiments from about 80° C. to about 160° C., and in some embodiments, from about 100° C. to about 140° C. The melting temperature and glass transition temperature may be determined using differential scanning calorimetry (“DSC”) in accordance with ASTM D-3417 as is well known in the art. Such tests may be employed using a THERMAL ANALYST 2910 Differential Scanning calorimeter (outfitted with a liquid nitrogen cooling accessory) and with a THERMAL ANALYST 2200 (version 8.10) analysis software program, which is available from T.A. Instruments Inc. of New Castle, Del.
The biodegradable polyesters may also have a number average molecular weight (“Mn”) ranging from about 40,000 to about 120,000 grams per mole, in some embodiments from about 50,000 to about 100,000 grams per mole, and in some embodiments, from about 60,000 to about 85,000 grams per mole. Likewise, the polyesters may also have a weight average molecular weight (“Mw”) ranging from about 70,000 to about 240,000 grams per mole, in some embodiments from about 80,000 to about 190,000 grams per mole, and in some embodiments, from about 100,000 to about 150,000 grams per mole. The ratio of the weight average molecular weight to the number average molecular weight (“Mw/Mn”), i.e., the “polydispersity index”, is also relatively low. For example, the polydispersity index typically ranges from about 1.0 to about 4.0, in some embodiments from about 1.2 to about 3.0, and in some embodiments, from about 1.4 to about 2.0. The weight and number average molecular weights may be determined by methods known to those skilled in the art.
The biodegradable polyesters may also have an apparent viscosity of from about 100 to about 1000 Pascal seconds (Pa·s), in some embodiments from about 200 to about 800 Pa·s, and in some embodiments, from about 300 to about 600 Pa·s, as determined at a temperature of 170° C. and a shear rate of 1000 sec−1. The melt flow index of the biodegradable polyesters may also range from about 0.1 to about 10 grams per 10 minutes, in some embodiments from about 0.5 to about 8 grams per 10 minutes, and in some embodiments, from about 1 to about 5 grams per 10 minutes. The melt flow index is the weight of a polymer (in grams) that may be forced through an extrusion rheometer orifice (0.0825-inch diameter) when subjected to a load of 2160 grams in 10 minutes at a certain temperature (e.g., 190° C.), measured in accordance with ASTM Test Method D1238-E.
Of course, the melt flow index of the biodegradable polyesters will ultimately depend upon the selected film-forming process. For example, when extruded as a cast film, higher melt flow index polymers are typically desired, such as about 4 grams per 10 minutes or more, in some embodiments, from about 5 to about 12 grams per 10 minutes, and in some embodiments, from about 7 to about 9 grams per 10 minutes. Likewise, when formed as a blown film, lower melt flow index polymers are typically desired, such as less than about 12 grams per 10 minutes or less, in some embodiments from about 1 to about 7 grams per 10 minutes, and in some embodiments, from about 2 to about 5 grams per 10 minutes.
Examples of suitable biodegradable polyesters include aliphatic polyesters, such as polycaprolactone, polyesteramides, modified polyethylene terephthalate, polylactic acid (PLA) and its copolymers, terpolymers based on polylactic acid, polyglycolic acid, polyalkylene carbonates (such as polyethylene carbonate), polyhydroxyalkanoates (PHA), poly-3-hydroxybutyrate (PHB), poly-3-hydroxyvalerate (PHV), poly-3-hydroxybutyrate-co-4-hydroybutyrate, poly-3-hydroxybutyrate-co-3-hydroxyvalerate copolymers (PHBV), poly-3-hydroxybutyrate-co-3-hydroxyhexanoate, poly-3-hydroxybutyrate-co-3-hydroxyoctanoate, poly-3-hydroxybutyrate-co-3-hydroxydecanoate, poly-3-hydroxybutyrate-co-3-hydroxyoctadecanoate, and succinate-based aliphatic polymers (e.g., polybutylene succinate, polybutylene succinate adipate, polyethylene succinate, etc.); aromatic polyesters and modified aromatic polyesters; and aliphatic-aromatic copolyesters. In one particular embodiment, the biodegradable polyester is an aliphatic-aromatic copolyester (e.g., block, random, graft, etc.). The aliphatic-aromatic copolyester may be synthesized using any known technique, such as through the condensation polymerization of a polyol in conjunction with aliphatic and aromatic dicarboxylic acids or anhydrides thereof. The polyols may be substituted or unsubstituted, linear or branched, polyols selected from polyols containing 2 to about 12 carbon atoms and polyalkylene ether glycols containing 2 to 8 carbon atoms. Examples of polyols that may be used include, but are not limited to, ethylene glycol, diethylene glycol, propylene glycol, 1,2-propanediol, 1,3-propanediol, 2,2-dimethyl-1,3-propanediol, 1,2-butanediol, 1,3-butanediol, 1,4-butanediol, 1,2-pentanediol, 1,5-pentanediol, 1,6-hexanediol, polyethylene glycol, diethylene glycol, 2,2,4-trimethyl-1,6-hexanediol, thiodiethanol, 1,3-cyclohexanedimethanol, 1,4-cyclohexanedimethanol, 2,2,4,4-tetramethyl-1,3-cyclobutanediol, cyclopentanediol, triethylene glycol, and tetraethylene glycol. Preferred polyols include 1,4-butanediol; 1,3-propanediol; ethylene glycol; 1,6-hexanediol; diethylene glycol; and 1,4-cyclohexanedimethanol. Representative aliphatic dicarboxylic acids that may be used include substituted or unsubstituted, linear or branched, non-aromatic dicarboxylic acids selected from aliphatic dicarboxylic acids containing 1 to about 10 carbon atoms, and derivatives thereof. Non-limiting examples of aliphatic dicarboxylic acids include malonic, malic, succinic, oxalic, glutaric, adipic, pimelic, azelaic, sebacic, fumaric, 2,2-dimethyl glutaric, suberic, 1,3-cyclopentanedicarboxylic, 1,4-cyclohexanedicarboxylic, 1,3-cyclohexanedicarboxylic, diglycolic, itaconic, maleic, and 2,5-norbornanedicarboxylic. Representative aromatic dicarboxylic acids that may be used include substituted and unsubstituted, linear or branched, aromatic dicarboxylic acids selected from aromatic dicarboxylic acids containing 1 to about 6 carbon atoms, and derivatives thereof. Non-limiting examples of aromatic dicarboxylic acids include terephthalic acid, dimethyl terephthalate, isophthalic acid, dimethyl isophthalate, 2,6-napthalene dicarboxylic acid, dimethyl-2,6-naphthalate, 2,7-naphthalenedicarboxylic acid, dimethyl-2,7-naphthalate, 3,4′-diphenyl ether dicarboxylic acid, dimethyl-3,4′ diphenyl ether dicarboxylate, 4,4′-diphenyl ether dicarboxylic acid, dimethyl-4,4′-diphenyl ether dicarboxylate, 3,4′-diphenyl sulfide dicarboxylic acid, dimethyl-3,4′-diphenyl sulfide dicarboxylate, 4,4′-diphenyl sulfide dicarboxylic acid, dimethyl-4,4′-diphenyl sulfide dicarboxylate, 3,4′-diphenyl sulfone dicarboxylic acid, dimethyl-3,4′-diphenyl sulfone dicarboxylate, 4,4′-diphenyl sulfone dicarboxylic acid, dimethyl-4,4′-diphenyl sulfone dicarboxylate, 3,4′-benzophenonedicarboxylic acid, dimethyl-3,4′-benzophenonedicarboxylate, 4,4′-benzophenonedicarboxylic acid, dimethyl-4,4′-benzophenonedicarboxylate, 1,4-naphthalene dicarboxylic acid, dimethyl-1,4-naphthalate, 4,4′-methylene bis(benzoic acid), dimethyl-4,4′-methylenebis(benzoate), etc., and mixtures thereof.
The polymerization may be catalyzed by a catalyst, such as a titanium-based catalyst (e.g., tetraisopropyltitanate, tetraisopropoxy titanium, dibutoxydiacetoacetoxy titanium, or tetrabutyltitanate). If desired, a diisocyanate chain extender may be reacted with the copolyester to increase its molecular weight. Representative diisocyanates may include toluene 2,4-diisocyanate, toluene 2,6-diisocyanate, 2,4′-diphenylmethane diisocyanate, naphthylene-1,5-diisocyanate, xylylene diisocyanate, hexamethylene diisocyanate (“HMDI”), isophorone diisocyanate and methylenebis(2-isocyanatocyclohexane). Trifunctional isocyanate compounds may also be employed that contain isocyanurate and/or biurea groups with a functionality of not less than three, or to replace the diisocyanate compounds partially by tri-or polyisocyanates. The preferred diisocyanate is hexamethylene diisocyanate. The amount of the chain extender employed is typically from about 0.3 to about 3.5 wt. %, in some embodiments, from about 0.5 to about 2.5 wt. % based on the total weight percent of the polymer.
The copolyesters may either be a linear polymer or a long-chain branched polymer. Long-chain branched polymers are generally prepared by using a low molecular weight branching agent, such as a polyol, polycarboxylic acid, hydroxy acid, and so forth. Representative low molecular weight polyols that may be employed as branching agents include glycerol, trimethylolpropane, trimethylolethane, polyethertriols, 1,2,4-butanetriol, pentaerythritol, 1,2,6-hexanetriol, sorbitol, 1,1,4,4,-tetrakis (hydroxymethyl)cyclohexane, tris(2-hydroxyethyl) isocyanurate, and dipentaerythritol. Representative higher molecular weight polyols (molecular weight of 400 to 3000) that may be used as branching agents include triols derived by condensing alkylene oxides having 2 to 3 carbons, such as ethylene oxide and propylene oxide with polyol initiators. Representative polycarboxylic acids that may be used as branching agents include hemimellitic acid, trimellitic (1,2,4-benzenetricarboxylic) acid and anhydride, trimesic (1,3,5-benzenetricarboxylic) acid, pyromellitic acid and anhydride, benzenetetracarboxylic acid, benzophenone tetracarboxylic acid, 1,1,2,2-ethane-tetracarboxylic acid, 1,1,2-ethanetricarboxylic acid, 1,3,5-pentanetricarboxylic acid, and 1,2,3,4-cyclopentanetetracarboxylic acid. Representative hydroxy acids that may be used as branching agents include malic acid, citric acid, tartaric acid, 3-hydroxyglutaric acid, mucic acid, trihydroxyglutaric acid, 4-carboxyphthalic anhydride, hydroxyisophthalic acid, and 4-(beta-hydroxyethyl)phthalic acid. Such hydroxy acids contain a combination of 3 or more hydroxyl and carboxyl groups. Especially preferred branching agents include trimellitic acid, trimesic acid, pentaerythritol, trimethylol propane and 1,2,4-butanetriol.
The aromatic dicarboxylic acid monomer constituent may be present in the copolyester in an amount of from about 10 mole % to about 40 mole %, in some embodiments from about 15 mole % to about 35 mole %, and in some embodiments, from about 15 mole % to about 30 mole %. The aliphatic dicarboxylic acid monomer constituent may likewise be present in the copolyester in an amount of from about 15 mole % to about 45 mole %, in some embodiments from about 20 mole % to about 40 mole %, and in some embodiments, from about 25 mole % to about 35 mole %. The polyol monomer constituent may also be present in the aliphatic-aromatic copolyester in an amount of from about 30 mole % to about 65 mole %, in some embodiments from about 40 mole % to about 50 mole %, and in some embodiments, from about 45 mole % to about 55 mole %.
In one particular embodiment, for example, the aliphatic-aromatic copolyester may comprise the following structure:
wherein, m is an integer from 2 to 10, in some embodiments from 2 to 4, and in an embodiment, 4;
n is an integer from 0 to 18, in some embodiments from 2 to 4, and in an embodiment, 4;
p is an integer from 2 to 10, in some embodiments from 2 to 4, and in an embodiment, 4;
x is an integer greater than 1; and y is an integer greater than 1.
One example of such a copolyester is polybutylene adipate terephthalate, which is commercially available under the designation ECOFLEX® F BX 7011 from BASF Corp. Another example of a suitable copolyester containing an aromatic terephtalic acid monomer constituent is available under the designation ENPOL™ 8060M from IRE Chemicals (South Korea). Other suitable aliphatic-aromatic copolyesters may be described in U.S. Pat. Nos. 5,292,783; 5,446,079; 5,559,171; 5,580,911; 5,599,858; 5,817,721; 5,900,322; and 6,258,924, which are incorporated herein in their entirety by reference thereto for all purposes.
F. Other Additives
Besides the components noted above, still other additives may also be incorporated into the composition, such as melt stabilizers, dispersion aids (e.g., surfactants), processing stabilizers, heat stabilizers, light stabilizers, antioxidants, heat aging stabilizers, whitening agents, antiblocking agents, bonding agents, lubricants, fillers, etc. For example, the film may include a mineral filler, such as talc, calcium carbonate, magnesium carbonate, clay, silica, alumina, boron oxide, titanium oxide, cerium oxide, germanium oxide, etc. The filler-containing film can be stretched to form breathable films. When employed, the mineral filler(s) typically constitute from about 0.01 wt. % to about 40 wt. %, in some embodiments from about 0.1 wt. % to about 30 wt. %, and in some embodiments, from about 0.5 wt. % to about 20 wt. % of the thermoplastic composition.
Dispersion aids may, for example, be employed to help create a uniform dispersion of the biopolymer/plasticizer and retard or prevent separation of the blend into constituent phases. When employed, the dispersion aid(s) typically constitute from about 0.01 wt. % to about 10 wt. %, in some embodiments from about 0.1 wt. % to about 5 wt. %, and in some embodiments, from about 0.5 wt. % to about 4 wt. % of the thermoplastic composition. Although any dispersion aid may generally be employed in the present invention, surfactants having a certain hydrophilic/lipophilic balance (“HLB”) may improve the long-term stability of the composition. The HLB index is well known in the art and is a scale that measures the balance between the hydrophilic and lipophilic solution tendencies of a compound. The HLB scale ranges from 1 to approximately 50, with the lower numbers representing highly lipophilic tendencies and the higher numbers representing highly hydrophilic tendencies. In some embodiments of the present invention, the HLB value of the surfactants is from about 1 to about 20, in some embodiments from about 1 to about 15 and in some embodiments, from about 2 to about 10. If desired, two or more surfactants may be employed that have HLB values either below or above the desired value, but together have an average HLB value within the desired range.
One particularly suitable class of surfactants for use in the present invention is nonionic surfactants, which typically have a hydrophobic base (e.g., long chain alkyl group or an alkylated aryl group) and a hydrophilic chain (e.g., chain containing ethoxy and/or propoxy moieties). For instance, some suitable nonionic surfactants that may be used include, but are not limited to, ethoxylated alkylphenols, ethoxylated and propoxylated fatty alcohols, polyethylene glycol ethers of methyl glucose, polyethylene glycol ethers of sorbitol, ethylene oxide-propylene oxide block copolymers, ethoxylated esters of fatty (C8-C18) acids, condensation products of ethylene oxide with long chain amines or amides, condensation products of ethylene oxide with alcohols, fatty acid esters, monoglyceride or diglycerides of long chain alcohols, and mixtures thereof. In one particular embodiment, the nonionic surfactant may be a fatty acid ester, such as a sucrose fatty acid ester, glycerol fatty acid ester, propylene glycol fatty acid ester, sorbitan fatty acid ester, pentaerythritol fatty acid ester, sorbitol fatty acid ester, and so forth. The fatty acid used to form such esters may be saturated or unsaturated, substituted or unsubstituted, and may contain from 6 to 22 carbon atoms, in some embodiments from 8 to 18 carbon atoms, and in some embodiments, from 12 to 14 carbon atoms. In one particular embodiment, mono- and di-glycerides of fatty acids may be employed in the present invention.
As indicated above, the thermoplastic composition of the present invention is formed by melt blending together a biopolymer, plasticizer, polyolefin, and a compatibilizer together within an extruder. More particularly, the polymeric components may be supplied separately or together to a feed section of the extruder (e.g., hopper) and the liquid plasticizer can be directly injected into the extruder at the same location, or at a location downstream therefrom. Despite not being pre-compounded with the plasticizer prior to being fed to the extruder, the present inventors have discovered that the biopolymer can still be readily processed. In this manner, the costly and time-consuming steps of pre-encapsulation or pre-compounding of the plasticizer and biopolymer are not required.
Referring to
A hopper 40 is also located adjacent to the drive 124 for supplying the biopolymer, polyolefin, and/or other materials through an opening 142 in the barrel 114 to the feed section 132. Opposite the drive 124 is the output end 144 of the extruder 80, where extruded plastic is output for further processing to form a film, which will be described in more detail below. A plasticizer supply station 150 is also provided on the extruder barrel 114 that includes at least one hopper 154, which is attached to a pump 160 to selectively provide the plasticizer through an opening 162 to the melt section 134. In this manner, the plasticizer may be mixed with the polymers in a consistent and uniform manner. Of course, in addition to or in lieu of supplying the plasticizer to the melt section 134, it should also be understood that it may be supplied to other sections of the extruder, such as the feed section 132 and/or the mixing section 136. For example, in certain embodiments, the plasticizer may be directly injected into the hopper 40 along with other polymeric materials.
The pump 160 may be a high pressure pump (e.g., positive displacement pump) with an injection valve so as to provide a steady selected amount of plasticizer to the barrel 114. If desired, a programmable logic controller 170 may also be employed to connect the drive 124 to the pump 160 so that it provides a selected volume of plasticizer based on the drive rate of the screw 120. That is, the controller 170 may control the rate of rotation of the drive screw 120 and the pump 160 to inject the plasticizer at a rate based on the screw rotation rate. Accordingly, if the rotation rate of the screw 120 is increased to drive greater amounts of plastic through the barrel 114 in a given unit of time, the pumping rate of the pump 160 may be similarly increased to pump proportionately greater amounts of plasticizer into the barrel 114.
The plasticizer and polymeric components may be processed within the extruder 80 under shear and pressure and heat to ensure sufficient mixing. For example, melt processing may occur at a temperature of from about 75° C. to about 280° C., in some embodiments, from about 100° C. to about 250° C., and in some embodiments, from about 150° C. to about 200° C. Likewise, the apparent shear rate during melt processing may range from about 100 seconds−1 to about 10,000 seconds−1, in some embodiments from about 500 seconds−1 to about 5000 seconds−1, and in some embodiments, from about 800 seconds−1 to about 1200 seconds−1. The apparent shear rate is equal to 4Q/πR3, where Q is the volumetric flow rate (“m3/s”) of the polymer melt and R is the radius (“m”) of the capillary (e.g., extruder die) through which the melted polymer flows.
Once processed in the extruder, the melt blended composition may flow through a die to form an extrudate that is in the form of a strand, sheet, film, etc. If desired, the extrudate may be optionally cooled using any of a variety of techniques. In one embodiment, for example, the extrudate is cooled upon exiting the die using a multi-stage system that includes at least one water-cooling stage and at least one air-cooling stage. For example, the extrudate may be initially contacted with water for a certain period time so that it becomes partially cooled. The actual temperature of the water and the total time that it is in contact with the extrudate may vary depending on the extrusion conditions, the size of the extrudate, etc. For example, the temperature of the water is typically from about 10° C. to about 60° C., in some embodiments from about 15° C. to about 40° C., and in some embodiments, from about 20° C. to about 30° C. Likewise, the total time that water is in contact with the extrudate (or residence time) is typically small, such as from about 1 to about 10 seconds, in some embodiments from about 2 to about 8 seconds, and in some embodiments, from about 3 to about 6 seconds. If desired, multiple water cooling stages may be employed to achieve the desired degree of cooling. Regardless of the number of stages employed, the resulting water-cooled extrudate is typically at a temperature of from about 40° C. to about 100° C., in some embodiments from about 50° C. to about 80° C., and in some embodiments, from about 60° C. to about 70° C., and contains water in an amount of from about 2,000 to about 50,000 parts per million (“ppm”), in some embodiments from about 4,000 to about 40,000 ppm, and in some embodiments, from about 5,000 to about 30,000 ppm.
After the water-cooling stage(s), the extrudate is also subjected to at least one air-cooling stage in which a stream of air is placed into contact with the extrudate. The temperature of the air stream may vary depending on the temperature and moisture content of the water-cooled extrudate, but is typically from about 0° C. to about 40° C., in some embodiments from about 5° C. to about 35° C., and in some embodiments, from about 10° C. to about 30° C. If desired, multiple air-cooling stages may be employed to achieve the desired degree of cooling. Regardless of the number of stages employed, the total time that air is in contact with the extrudate (or residence time) is typically small, such as from about 1 to about 50 seconds, in some embodiments from about 2 to about 40 seconds, and in some embodiments, from about 3 to about 35 seconds. The resulting air-cooled extrudate is generally free of water and has a low moisture content, such as from about 500 to about 20,000 parts per million (“ppm”) in some embodiments from about 800 to about 15,000 ppm, and in some embodiments, from about 1,000 to about 10,000 ppm. The temperature of the air-cooled extrudate may also be from about 15° C. to about 80° C., in some embodiments from about 20° C. to about 70° C., and in some embodiments, from about 25° C. to about 60° C.
The specific configuration of the multi-stage cooling system may vary as would be understood by those skilled in the art. Referring to
Any known technique may be used to form a film from the blended and optionally cooled composition, including blowing, casting, flat die extruding, etc. In one particular embodiment, the film may be formed by a blown process in which a gas (e.g., air) is used to expand a bubble of the extruded polymer blend through an annular die. The bubble is then collapsed and collected in flat film form. Processes for producing blown films are described, for instance, in U.S. Pat. No. 3,354,506 to Raley; U.S. Pat. No. 3,650,649 to Schippers; and U.S. Pat. No. 3,801,429 to Schrenk et al., as well as U.S. Patent Application Publication Nos. 2005/0245162 to McCormack, et al. and 2003/0068951 to Boggs, et al., all of which are incorporated herein in their entirety by reference thereto for all purposes. In yet another embodiment, however, the film is formed using a casting technique.
Referring to
Once cast, the film 10a may then be optionally oriented in one or more directions to further improve film uniformity and reduce thickness. Orientation may also form micropores in a film containing a filler, thus providing breathability to the film. For example, the film may be immediately reheated to a temperature below the melting point of one or more polymers in the film, but high enough to enable the composition to be drawn or stretched. In the case of sequential orientation, the “softened” film is drawn by rolls rotating at different speeds of rotation such that the sheet is stretched to the desired draw ratio in the longitudinal direction (machine direction). This “uniaxially” oriented film may then be laminated to a fibrous web. In addition, the uniaxially oriented film may also be oriented in the cross-machine direction to form a “biaxially oriented” film. For example, the film may be clamped at its lateral edges by chain clips and conveyed into a tenter oven. In the tenter oven, the film may be reheated and drawn in the cross-machine direction to the desired draw ratio by chain clips diverged in their forward travel.
Referring again to
The resulting film 10b may then be wound and stored on a take-up roll 60. While not shown here, various additional potential processing and/or finishing steps known in the art, such as slitting, treating, aperturing, printing graphics, or lamination of the film with other layers (e.g., nonwoven web materials), may be performed without departing from the spirit and scope of the invention.
The film of the present invention may be mono- or multi-layered. Multilayer films may be prepared by co-extrusion of the layers, extrusion coating, or by any conventional layering process. For example, the film may contain from two (2) to fifteen (15) layers, and in some embodiments, from three (3) to twelve (12) layers. Such multilayer films normally contain at least one base layer and at least one skin layer, but may contain any number of layers desired. For example, the multilayer film may be formed from a base layer and one or more skin layers, wherein the base layer is formed from the thermoplastic composition of the present invention. In most embodiments, the skin layer(s) are formed from a thermoplastic composition such as described above. It should be understood, however, that other polymers may also be employed in the skin layer(s), such as polyolefin polymers (e.g., linear low-density polyethylene (LLDPE) or polypropylene).
The thickness of the film of the present invention may be relatively small to increase flexibility. For example, the film may have a thickness of about 50 micrometers or less, in some embodiments from about 1 to about 40 micrometers, in some embodiments from about 2 to about 35 micrometers, and in some embodiments, from about 5 to about 30 micrometers. Despite having such a small thickness, the film of the present invention is nevertheless able to retain good mechanical properties during use. One parameter that is indicative of the relative dry strength of the film is the ultimate tensile strength, which is equal to the peak stress obtained in a stress-strain curve, such as obtained in accordance with ASTM Standard D638-08. Desirably, the film of the present invention exhibits a peak stress (when dry) in the machine direction (“MD”) of from about 10 to about 100 Megapascals (MPa), in some embodiments from about 15 to about 70 MPa, and in some embodiments, from about 20 to about 60 MPa, and a peak stress in the cross-machine direction (“CD”) of from about 2 to about 40 Megapascals (MPa), in some embodiments from about 4 to about 40 MPa, and in some embodiments, from about 5 to about 30 MPa.
Although possessing good strength, the film is relatively ductile. One parameter that is indicative of the ductility of the film is the percent strain of the film at its break point, as determined by the stress strain curve, such as obtained in accordance with ASTM Standard D608-08. For example, the percent strain at break of the film in the machine direction may be about 100% or more, in some embodiments about 150% or more, and in some embodiments, from about 200% to about 600%. Likewise, the percent strain at break of the film in the cross-machine direction may be about 200% or more, in some embodiments about 250% or more, and in some embodiments, from about 300% to about 800%. Another parameter that is indicative of ductility is the modulus of elasticity of the film, which is equal to the ratio of the tensile stress to the tensile strain and is determined from the slope of a stress-strain curve. For example, the film typically exhibits a modulus of elasticity (when dry) in the machine direction (“MD”) of from about 10 to about 400 Megapascals (“MPa”), in some embodiments from about 20 to about 200 MPa, and in some embodiments, from about 40 to about 80 MPa, and a modulus in the cross-machine direction (“CD”) of from about 10 to about 400 Megapascals (“MPa”), in some embodiments from about 20 to about 200 MPa, and in some embodiments, from about 40 to about 80 MPa.
If desired, the film of the present invention may be laminated to one or more nonwoven web facings to reduce the coefficient of friction and enhance the cloth-like feel of the composite surface. Exemplary polymers for use in forming nonwoven web facings may include, for instance, polyolefins, e.g., polyethylene, polypropylene, polybutylene, etc.; polytetrafluoroethylene; polyesters, e.g., polyethylene terephthalate and so forth; polyvinyl acetate; polyvinyl chloride acetate; polyvinyl butyral; acrylic resins, e.g., polyacrylate, polymethylacrylate, polymethylmethacrylate, and so forth; polyamides, e.g., nylon; polyvinyl chloride; polyvinylidene chloride; polystyrene; polyvinyl alcohol; polyurethanes; polylactic acid; copolymers thereof; and so forth. If desired, biodegradable polymers, such as those described above, may also be employed. Synthetic or natural cellulosic polymers may also be used, including but not limited to, cellulosic esters; cellulosic ethers; cellulosic nitrates; cellulosic acetates; cellulosic acetate butyrates; ethyl cellulose; regenerated celluloses, such as viscose, rayon, and so forth. It should be noted that the polymer(s) may also contain other additives, such as processing aids or treatment compositions to impart desired properties to the fibers, residual amounts of solvents, pigments or colorants, and so forth.
Monocomponent and/or multicomponent fibers may be used to form the nonwoven web facing. Monocomponent fibers are generally formed from a polymer or blend of polymers extruded from a single extruder. Multicomponent fibers are generally formed from two or more polymers (e.g., bicomponent fibers) extruded from separate extruders. The polymers may be arranged in substantially constantly positioned distinct zones across the cross-section of the fibers. The components may be arranged in any desired configuration, such as sheath-core, side-by-side, pie, island-in-the-sea, three island, bull's eye, or various other arrangements known in the art. Multicomponent fibers having various irregular shapes may also be formed.
Fibers of any desired length may be employed, such as staple fibers, continuous fibers, etc. In one particular embodiment, for example, staple fibers may be used that have a fiber length in the range of from about 1 to about 150 millimeters, in some embodiments from about 5 to about 50 millimeters, in some embodiments from about 10 to about 40 millimeters, and in some embodiments, from about 10 to about 25 millimeters. Although not required, carding techniques may be employed to form fibrous layers with staple fibers as is well known in the art. For example, fibers may be formed into a carded web by placing bales of the fibers into a picker that separates the fibers. Next, the fibers are sent through a combing or carding unit that further breaks apart and aligns the fibers in the machine direction so as to form a machine direction-oriented fibrous nonwoven web. The carded web may then be bonded using known techniques to form a bonded carded nonwoven web.
If desired, the nonwoven web facing used to form the nonwoven composite may have a multi-layer structure. Suitable multi-layered materials may include, for instance, spunbond/meltblown/spunbond (SMS) laminates and spunbond/meltblown (SM) laminates. Another example of a multi-layered structure is a spunbond web produced on a multiple spin bank machine in which a spin bank deposits fibers over a layer of fibers deposited from a previous spin bank. Such an individual spunbond nonwoven web may also be thought of as a multi-layered structure. In this situation, the various layers of deposited fibers in the nonwoven web may be the same, or they may be different in basis weight and/or in terms of the composition, type, size, level of crimp, and/or shape of the fibers produced. As another example, a single nonwoven web may be provided as two or more individually produced layers of a spunbond web, a carded web, etc., which have been bonded together to form the nonwoven web. These individually produced layers may differ in terms of production method, basis weight, composition, and fibers as discussed above. A nonwoven web facing may also contain an additional fibrous component such that it is considered a composite. For example, a nonwoven web may be entangled with another fibrous component using any of a variety of entanglement techniques known in the art (e.g., hydraulic, air, mechanical, etc.). In one embodiment, the nonwoven web is integrally entangled with cellulosic fibers using hydraulic entanglement. A typical hydraulic entangling process utilizes high pressure jet streams of water to entangle fibers to form a highly entangled consolidated fibrous structure, e.g., a nonwoven web. The fibrous component of the composite may contain any desired amount of the resulting substrate.
The basis weight of the nonwoven web facing may generally vary, such as from about 5 grams per square meter (“gsm”) to 120 gsm, in some embodiments from about 8 gsm to about 70 gsm, and in some embodiments, from about 10 gsm to about 35 gsm. When using multiple nonwoven web facings, such materials may have the same or different basis weights.
The film of the present invention may be used in a wide variety of applications, such as a packaging film, such as an individual wrap, packaging pouch, or bag for the disposal of a variety of articles, such as food products, paper products (e.g., tissue, wipes, paper towels, etc.), absorbent articles, etc. Various suitable pouch, wrap, or bag configurations for absorbent articles are disclosed, for instance, in U.S. Pat. No. 6,716,203 to Sorebo, et al. and U.S. Pat. No. 6,380,445 to Moder et al., as well as U.S. Patent Application Publication No. 2003/0116462 to Sorebo, et al., all of which are incorporated herein in their entirety by reference thereto for all purposes.
The film may also be employed in other applications. For example, the film may be used in an absorbent article. An “absorbent article” generally refers to any article capable of absorbing water or other fluids. Examples of some absorbent articles include, but are not limited to, personal care absorbent articles, such as diapers, training pants, absorbent underpants, incontinence articles, feminine hygiene products (e.g., sanitary napkins, pantiliners, etc.), swim wear, baby wipes, and so forth; medical absorbent articles, such as garments, fenestration materials, underpads, bedpads, bandages, absorbent drapes, and medical wipes; food service wipers; clothing articles; and so forth. Several examples of such absorbent articles are described in U.S. Pat. No. 5,649,916 to DiPalma, et al.; U.S. Pat. No. 6,110,158 to Kielpikowski; U.S. Pat. No. 6,663,611 to Blaney, et al., which are incorporated herein in their entirety by reference thereto for all purposes. Still other suitable articles are described in U.S. Patent Application Publication No. 2004/0060112 A1 to Fell et as well as U.S. Pat. No. 4,886,512 to Damico et al.; U.S. Pat. No. 5,558,659 to Sherrod et al.; U.S. Pat. No. 6,888,044 to Fell et al.; and U.S. Pat. No. 6,511,465 to Freiburger et al., all of which are incorporated herein in their entirety by reference thereto for all purposes. Materials and processes suitable for forming such absorbent articles are well known to those skilled in the art.
In this regard, one particular embodiment of a sanitary napkin that may employ the film of the present invention will now be described in more detail. For purposes of illustration only, an absorbent article can be a sanitary napkin for feminine hygiene. In such an embodiment, the absorbent article includes a main body portion containing a topsheet, an outer cover or backsheet, an absorbent core positioned between the backsheet and the topsheet, and a pair of flaps extending from each longitudinal side of the main body portion. The topsheet defines a bodyfacing surface of the absorbent article. The absorbent core is positioned inward from the outer periphery of the absorbent article and includes a body-facing side positioned adjacent the topsheet and a garment-facing surface positioned adjacent the backsheet. In one particular embodiment of the present invention, the backsheet is a film formed from the thermoplastic composition of the present invention and is generally liquid-impermeable and optionally vapor-permeable. The film used to form the backsheet may also be laminated to one or more nonwoven web facings such as described above.
The topsheet is generally designed to contact the body of the user and is liquid-permeable. The topsheet may surround the absorbent core so that it completely encases the absorbent article. Alternatively, the topsheet and the backsheet may extend beyond the absorbent core and be peripherally joined together, either entirely or partially, using known techniques. Typically, the topsheet and the backsheet are joined by adhesive bonding, ultrasonic bonding, or any other suitable joining method known in the art. The topsheet is sanitary, clean in appearance, and somewhat opaque to hide bodily discharges collected in and absorbed by the absorbent core. The topsheet further exhibits good strike-through and rewet characteristics permitting bodily discharges to rapidly penetrate through the topsheet to the absorbent core, but not allow the body fluid to flow back through the topsheet to the skin of the wearer. For example, some suitable materials that may be used for the topsheet include nonwoven materials, perforated thermoplastic films, or combinations thereof. A nonwoven fabric made from polyester, polyethylene, polypropylene, bicomponent, nylon, rayon, or like fibers may be utilized. For instance, a white uniform spunbond material is particularly desirable because the color exhibits good masking properties to hide menses that has passed through it. U.S. Pat. No. 4,801,494 to Datta, et al. and U.S. Pat. No. 4,908,026 to Sukiennik, et al. teach various other cover materials that may be used in the present invention.
The topsheet may also contain a plurality of apertures (not shown) formed therethrough to permit body fluid to pass more readily into the absorbent core. The apertures may be randomly or uniformly arranged throughout the topsheet, or they may be located only in the narrow longitudinal band or strip arranged along the longitudinal axis of the absorbent article. The apertures permit rapid penetration of body fluid down into the absorbent core. The size, shape, diameter and number of apertures may be varied to suit one's particular needs.
The absorbent article also contains an absorbent core positioned between the topsheet and the backsheet. The absorbent core may be formed from a single absorbent member or a composite containing separate and distinct absorbent members. It should be understood, however, that any number of absorbent members may be utilized in the present invention. For example, in an embodiment, the absorbent core may contain an intake member (not shown) positioned between the topsheet and a transfer delay member (not shown). The intake member may be made of a material that is capable of rapidly transferring, in the z-direction, body fluid that is delivered to the topsheet. The intake member may generally have any shape and/or size desired. In one embodiment, the intake member has a rectangular shape, with a length equal to or less than the overall length of the absorbent article, and a width less than the width of the absorbent article. For example, a length of between about 150 mm to about 300 mm and a width of between about 10 mm to about 60 mm may be utilized.
Any of a variety of different materials may be used for the intake member to accomplish the above-mentioned functions. The material may be synthetic, cellulosic, or a combination of synthetic and cellulosic materials. For example, airlaid cellulosic tissues may be suitable for use in the intake member. The airlaid cellulosic tissue may have a basis weight ranging from about 10 grams per square meter (gsm) to about 300 gsm, and in some embodiments, between about 100 gsm to about 250 gsm. In one embodiment, the airlaid cellulosic tissue has a basis weight of about 200 gsm. The airlaid tissue may be formed from hardwood and/or softwood fibers. The airlaid tissue has a fine pore structure and provides an excellent wicking capacity, especially for menses.
If desired, a transfer delay member (not shown) may be positioned vertically below the intake member. The transfer delay member may contain a material that is less hydrophilic than the other absorbent members, and may generally be characterized as being substantially hydrophobic. For example, the transfer delay member may be a nonwoven fibrous web composed of a relatively hydrophobic material, such as polypropylene, polyethylene, polyester or the like, and also may be composed of a blend of such materials. One example of a material suitable for the transfer delay member is a spunbond web composed of polypropylene, multi-lobal fibers. Further examples of suitable transfer delay member materials include spunbond webs composed of polypropylene fibers, which may be round, tri-lobal or poly-lobal in cross-sectional shape and which may be hollow or solid in structure. Typically the webs are bonded, such as by thermal bonding, over about 3% to about 30% of the web area. Other examples of suitable materials that may be used for the transfer delay member are described in U.S. Pat. No. 4,798,603 to Meyer, et al. and U.S. Pat. No. 5,248,309 to Serbiak, et al. To adjust the performance of the invention, the transfer delay member may also be treated with a selected amount of surfactant to increase its initial wettability.
The transfer delay member may generally have any size, such as a length of about 150 mm to about 300 mm. Typically, the length of the transfer delay member is approximately equal to the length of the absorbent article. The transfer delay member may also be equal in width to the intake member, but is typically wider. For example, the width of the transfer delay member may be from between about 50 mm to about 75 mm, and particularly about 48 mm. The transfer delay member typically has a basis weight less than that of the other absorbent members. For example, the basis weight of the transfer delay member is typically less than about 150 grams per square meter (gsm), and in some embodiments, between about 10 gsm to about 100 gsm. In one particular embodiment, the transfer delay member is formed from a spunbonded web having a basis weight of about 30 gsm.
Besides the above-mentioned members, the absorbent core may also include a composite absorbent member (not shown), such as a coform material. In this instance, fluids may be wicked from the transfer delay member into the composite absorbent member. The composite absorbent member may be formed separately from the intake member and/or transfer delay member, or may be formed simultaneously therewith. In one embodiment, for example, the composite absorbent member may be formed on the transfer delay member or intake member, which acts a carrier during the coform process described above.
Although various configurations of an absorbent article have been described above, it should be understood that other configurations are also included within the scope of the present invention. Further, the present invention is by no means limited to backsheets and the film of the present invention may be incorporated into a variety of different components of an absorbent article. For example, a release liner of an absorbent article may include the film of the present invention.
The present invention may be better understood with reference to the following examples.
Films were tested for tensile properties (peak stress, modulus, strain at break, and energy per volume at break) on a Sintech 1/D tensile frame. The test was performed in accordance with ASTM D638-08. Film samples were cut into dog bone shapes with a center width of 3.0 mm before testing. The dog-bone film samples were held in place using grips on the Sintech device with a gauge length of 18.0 mm. The film samples were stretched at a crosshead speed of 5.0 in/min until breakage occurred. Five samples were tested for each film in both the machine direction (MD) and the cross direction (CD). A computer program called TestWorks 4 was used to collect data during testing and to generate a stress versus strain curve from which a number of properties were determined, including modulus, peak stress, elongation, and energy to break.
The melt flow index was determined in accordance with ASTM D-1238 at a temperature of 190° C., load of 2.16 kg, and release time of 6 minutes. A Model MP600 melt indexer at Tinius Olsen Testing Machine Company, Inc. was used to measure the melt flow rates.
The moisture content was determined using a “loss on drying” method via a Compurac® moisture analyzer made from Arizona Instrument. More particularly, the initial weight of the sample was measured. This sample was then placed in oven at 130° C. to eliminate the water, cooled to ambient temperature, and reweighed. The moisture content may be determined as parts per million (“ppm”) or weight percentage (wt. %) as follows.
Moisture content (ppm)=[(Initial mass−Final mass)/Initial mass]*1,000,000
Moisture content (wt. %)=[(Initial mass−Final mass)/Initial mass]*100
The following materials were employed in the Examples:
Cargill gel corn starch was purchased from Cargill (Cedar Rapids, Iowa); Glycerin (Emery™ 916) was purchased from Cognis Corporation (Cincinnati, Ohio);
ECOFLEX™ F BX 7011, an aliphatic aromatic copolyester, was purchased from BASF (Ludwigshafen, Germany);
DOWLEX™ EG 2244G polyethylene resin was purchased from Dow Chemical Company (Midland, Mich.); and
FUSABOND® MB 528D, a chemically modified polyethylene resin, was purchased from DuPont Company (Wilmington, Del.).
The ZSK-30 extruder (Werner and Pfleiderer Corporation, Ramsey, N.J.) is a co-rotating, twin screw extruder, with a diameter of 30 mm and screw length up to 1328 mm. The extruder has 14 barrels. The first barrel received the mixture of starch, Ecoflex® copolyesters, polyolefins, compatibilizers, additives, etc. When glycerin injection was used, it was injected into barrel 2 with a pressurized injector connected with an Eldex pump (Napa, Calif.). The vent was opened at the end of the extruder to release moisture.
The Haake Rheomex 252 (Haake, Karlsruhe, Germany) is a single screw extruder with a diameter of 18.75 mm and a screw length of 450 mm.
The Haake Rheocord 90 (Haake, Karlsruhe, Germany) is a computer controlled torque rheometer. It is utilized for controlling rotor speed and temperature settings on the HAAKE Rheomex 252.
The ability to form a thermoplastic composition using the process of the present invention was demonstrated. More particularly, the composition was formed from 25 wt. % thermoplastic starch (corn starch and glycerin), 34 wt. % DOWLEX™ EG 2244G polyethylene, 3 wt. % FUSABOND™ MB 528D, and 38 wt. % ECOFLEX™ F BX 7011. Feeding of the corn starch was accomplished using a ZSK-30 twin screw powder feeder at the rate of 7.5 lbs/hour. Glycerin was used to fill 5 gallon pails and heated prior to resin blending. The glycerin was pumped directly into the melt-stream of the extruder using a three head liquid pump at approximately 18.9 g/min, equating to 2.5 lbs/hr. DOWLEX™ polyethylene (“PE”) was measured into a 5 gallon pail and hand mixed with FUSABOND™ 528 (“FB”). The mixture was fed into the throat of the extruder at a rate of 14.68 lbs/hr via a single screw pellet feeder. ECOFLEX™ copolyester was fed into the throat using a single screw feeder at a rate of 15 lbs/hr.
The processing conditions are set forth below in Table 1.
The strands resulting from the blending were air cooled on a belt by a series of fans located above the belt. The cool strands were collected on a cardboard sheet and then shredded into pellets for further processing. Films were cast using a Haake Rheomex 252 connected to a Haake Rheocord 90, which was responsible for monitoring and adjusting torque, screw speed, and heating. Pellets obtained from the ZSK-30 extruder were flood fed into the Haake extruder for film casting. An 8-inch film die was used in conjunction with a cooled roller and collection system to obtain a film having a thickness of approximately 25.4 micrometers.
The resulting films were stored in a standard state conditioning room overnight and tested for tensile properties as indicated above. The MD and CD properties for the films are set forth below in Tables 2-3. It should be noted that the films of Examples 1 and 5 showed a significant number of large holes. These holes were avoided when testing for physical properties.
The ability to form a thermoplastic composition using the process of the present invention was demonstrated. More particularly, the composition was formed from 25 wt. % thermoplastic starch (corn starch and glycerin), 34 wt. % DOWLEX™ EG 2244G polyethylene, 3 wt. % FUSABOND™ MB 528D, and 38 wt. % ECOFLEX™ F BX 7011. Feeding of the corn starch was accomplished using a ZSK-30 twin screw powder feeder at the rate of 7.5 lbs/hour. Glycerin was used to fill 5 gallon pails and heated prior to resin blending. The glycerin was pumped directly into the melt-stream of the extruder using a three head liquid pump at approximately 18.9 g/min, equating to 2.5 lbs/hr. DOWLEX™ polyethylene (“PE”) was measured into a 5 gallon pail and hand mixed with FUSABOND™ 528 (“FB”). The mixture was fed into the throat of the extruder at a rate of 14.68 lbs/hr via a single screw pellet feeder. ECOFLEX™ copolyester was fed into the throat using a single screw feeder at a rate of 15 lbs/hr.
The resulting strands were cooled in a water bath with varying water exposure lengths (5 feet, 10 feet, or 15 feet). The cool strands were collected on a cardboard sheet and then shredded into pellets for further processing. The processing conditions for the samples are set forth below in Table 4.
After being submerged in the 5 ft. water dip, the strands of Example 6 were too ductile to be pelletized because they did not fully cool. in Examples 7 and 8, the cooling was sufficient to allow the strands to cool and continuous pelletization was possible. Films were cast using a Haake Rheomex 252 connected to a Haake Rheocord 90, which was responsible for monitoring and adjusting torque, screw speed, and heating. Pellets obtained from the ZSK-30 extruder were flood fed into the Haake extruder for film casting. An 8-inch film die was used in conjunction with a cooled roller and collection system to obtain a film having a thickness of approximately 25.4 micrometers. The casting conditions are summarized in Table 5 below.
The resulting films were stored in a standard state conditioning room overnight and tested for tensile properties as indicated above. The MD and CD properties for the films are set forth below in Tables 6-7.
As indicated, the CD peak stress, ductility, and energy at break for the water-cooled films of Examples 6-8 was high.
The ability to form a thermoplastic composition using the process of the present invention was demonstrated. More particularly, the composition was formed from 19 wt. % corn starch, 6 wt. % glycerin, 34 wt. % DOWLEX™ EG 2244G polyethylene, 3 wt. % FUSABOND™ MB 528D, and 38 wt. % ECOFLEX™ F BX 7011. The DOWLEX™ EG 2244G polyethylene, FUSABOND™ MB 528D, and ECOFLEX™ F BX 7011 were initially dry mixed and then fed to a 64-mm co-rotating, twin screw extruder (L/D ratio=38) at a rate of 375 pounds per hour. The extruder had one feed barrel (Zone 1), six closed barrels (Zones 2-7), and finally a barrel with a vacuum stack (Zone 8). The polymer mixture was supplied to the feed barrel via a twin screw gravimetric feeder (Arbo Flat Tray Feeder). The corn starch was also fed to the feed barrel via a gravimetric feeder (Accurate Feeder) at a rate of 95 pounds per hour. Glycerin was pumped directly into the feed barrel of the extruder using a liquid gear pump at approximately 30 lbs/hr. A 12-strand die with a diameter of 0.125 inches was used to form strands from the composition. The resulting strands were cooled as shown in
Films were cast using a Haake Rheomex 252 connected to a Haake Rheocord 90, which was responsible for monitoring and adjusting torque, screw speed, and heating. Pellets obtained from the ZSK-30 extruder were flood fed into the Haake extruder for film casting. An 8-inch film die was used in conjunction with a cooled roller and collection system to obtain a film having a thickness of approximately 25.4 micrometers. The casting conditions are summarized in Table 8 below.
As indicated, the extrusion and die temperatures were quite stable, except that Zone 4 fluctuated in temperature from 283° F. to 360° F. The resin produced in this example was also evaluated for moisture content and melt flow index in the manner described above. The moisture content was 8860 ppm and the melt flow index was 2.13 grams per 10 minutes (190° C., 2.16 kg load).
Films were formed as described in Example 9, except using the casting conditions summarized in Table 9 below.
As indicated, extrusion temperatures were higher than those of Example 9. The temperature of die body was high in the early stages because of a higher screw speed, 330 rpm. After reducing the screw speed to 250 rpm, the temperature of the die body was slowly cooled down to the set point. The resin produced in this example was also evaluated for moisture content and melt flow index at run times of 60 minutes, 90 minutes, and 120 minutes. The moisture content was 4000 ppm at 60 minutes, 2600 ppm at 90 minutes, and 4378 at 120 minutes. The melt flow index was 0.28 g/10 min at 60 minutes, 0.18 g/10 min at 90 minutes, and 0.31 g/10 min at 120 minutes.
Films were cast from samples of Examples 9 and 10 using a Haake Rheomex 252 connected to a Haake Rheocord 90, which was responsible for monitoring and adjusting torque, screw speed, and heating. Pellets obtained from the ZSK-30 extruder were flood fed into the Haake extruder for film casting. An 8-inch film die was used in conjunction with a cooled roller and collection system to obtain a film having a thickness of approximately 25.4 micrometers. The casting conditions are summarized in Table 10 below.
The resulting films were stored in a standard state conditioning room overnight and tested for tensile properties as indicated above. The mean MD and CD properties for the films are set forth below in Tables 11-12.
As indicated, the MD/CD peak stress and elongation values of Example 9 were quite high. Example 10 showed lower than expected target peak stress values and elongation values, which are believed to be due holes formed in the film during casting due to unintended starch degradation during blending.
While the invention has been described in detail with respect to the specific embodiments thereof, it will be appreciated that those skilled in the art, upon attaining an understanding of the foregoing, may readily conceive of alterations to, variations of, and equivalents to these embodiments. Accordingly, the scope of the present invention should be assessed as that of the appended claims and any equivalents thereto.