Patent Grant
9353460
1. Field of the Disclosure
The present disclosure is directed to a method for forming metal structures, and in particular, a method for forming metal structures by co-axial electrospinning.
2. Background
Micron and submicron metallic fibers have great potential for many applications. Examples of such applications include electronic devices, sensors, thermal management, biomedical fields, such as wound dressing materials, body wall repairs, tissue scaffolds and antimicrobial filters. Other applications include employing metal fibers in xerographic components to improve the electrical and thermal conductivity without adversely affecting performance. For fuser applications, providing adequate thermal conductivity can allow increased fusing speeds, improved fusing latitude and enable low fusing temperatures.
Metallic fibers reported in the literature have been prepared by electrospinning a metal oxide or salt with a polymer binder, such as PVB or PVA, followed by removing the polymer binder with high temperature treatment. The methodology involves a high temperature reduction process using hydrogen (e.g., 300° C.), which is not practical for some applications. (Ref. a) Adv. Mater. 2006, 18, 2384-2386. b) Nano Lett. 2010, 10, 4242-4248).
Alternative methods for making metal fibers and/or metal dots at relatively low temperatures would be a welcome step forward in the art.
An embodiment of the present disclosure is directed to a method of forming a metal structure. The method comprises providing a dispersion of metal nanoparticles. A solution comprising a transient polymer and solvent is also provided. The dispersion of metal nanoparticles and the solution are coaxially electrospun to form a fiber comprising the metal nanoparticles and the transient polymer. The fiber is heated to decompose the transient polymer and form a metallic structure.
Another embodiment of the present disclosure is directed to a method of forming a metal nanostructure. The method comprises providing a dispersion of metal nanoparticles and a solution comprising a transient polymer. The dispersion of metal nanoparticles and the solution are coaxially electrospun to form a plurality of core-shell fibers. The dispersion of metal nanoparticles forms a fiber core and the transient polymer forms a polymer shell surrounding the fiber core. The core-shell fiber is heated to form a metallic nanostructure. The heating of the core-shell fiber comprises heating to a first temperature to melt the metal nanoparticles, and then heating the core-shell nanofibers to a second temperature to remove the polymer, the second temperature being higher than the first temperature. The metal nanostructure has at least one dimension that is less than 500 nm.
It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the present teachings, as claimed.
The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments of the present teachings and together with the description, serve to explain the principles of the present teachings.
It should be noted that some details of the figure have been simplified and are drawn to facilitate understanding of the embodiments rather than to maintain strict structural accuracy, detail, and scale.
Reference will now be made in detail to embodiments of the present teachings, examples of which are illustrated in the accompanying drawings. In the drawings, like reference numerals have been used throughout to designate identical elements. In the following description, reference is made to the accompanying drawings, which form a part thereof, and in which is shown by way of illustration a specific exemplary embodiment in which the present teachings may be practiced. The following description is, therefore, merely exemplary.
The present application is directed to a method of forming a metal structure by a co-axial electrospinning process. An embodiment of the process is illustrated by the flow diagram of
The metal nanoparticle dispersions employed in the processes of the present disclosure can comprise any suitable metal nanoparticles. Examples include nanoparticles comprising at least one metal selected from the group consisting of silver, gold, copper, nickel, iron, palladium, silver-copper alloy, gold-copper alloy, nickel-copper alloy, and silver-gold alloy. In an embodiment, the nanoparticles comprise silver, such as a silver-copper alloy, silver-gold alloy or substantially pure organoamine stabilized silver nanoparticles.
In an embodiment, a stabilizer is employed in the dispersion of metal nanoparticles. The stabilizer comprises an organoamine. The stabilizer can be an organoamine stabilizer such as those described in U.S. Pat. No. 7,270,694, which is incorporated by reference herein in its entirety. In an embodiment, the organoamine can comprise a hydrocarbylamine having at least 4 carbon atoms. In an embodiment, the organoamine can be selected from the group consisting of butylamine, pentylamine, hexylamine, heptylamine, octylamine, nonylamine, decylamine, hexadecylamine, undecylamine, dodecylamine, tridecylamine, tetradecylamine, diaminopentane, diaminohexane, diaminoheptane, diaminooctane, diaminononane, diaminodecane, dipropylamine, dibutylamine, dipentylamine, dihexylamine, diheptylamine, dioctylamine, dinonylamine, didecylamine, methylpropylamine, ethylpropylamine, propylbutylamine, ethylbutylamine, ethylpentylamine, propylpentylamine, butylpentylamine, tributylamine, trihexylamine and mixtures of two or more thereof. In an embodiment, the stabilizer can be dodecylamine.
The metal nanoparticles can be dispersed in an organic based solution. In embodiments, an organic solvent can be an organic hydrocarbon solvent containing from about 6 to about 28 carbon atoms, which may be substituted or unsubstituted, and can be an aliphatic or aromatic hydrocarbon. Exemplary hydrocarbons may include aliphatic hydrocarbons such as heptane, undecane, dodecane, tridecane, tetradecane, isoparaffinic hydrocarbons such as isodecane, isododecane, and commercially available mixtures of isoparaffins such as ISOPAR E, ISOPAR G, ISOPAR H, ISOPAR L and ISOPAR M (all of which are manufactured by Exxon Mobil Chemical Company of Houston, Tex.), and the like; cyclic aliphatic hydrocarbons such as bicyclopropyl, bicyclopentyl, bicyclohexyl, cyclopentylcyclohexane, spiro[2,2]heptane, bicyclo[4,2,0]octanehydroindane, decahydronaphthalene (i.e., bicyclo[4.4.0]decane or decalin), and the like; aromatic hydrocarbons such as toluene, benzene, xylenes chlorobenzene, o-dichlorobenzene; and mixtures thereof. In an example, the organic fluid includes toluene.
The solution can comprise any suitable transient polymer that facilitates fiber formation and that can be removed from the electrospun co-axial fiber by thermal degradation within the desired temperature range. Examples of suitable transient binder compounds include polyalkylene carbonates, such as poly(propylene carbonate), poly(ethylene carbonate) and poly(butylene carbonate).
An example of co-axial electrospinning apparatus 20 that can be employed for carrying out the process of the present disclosure is illustrated in FIG. 2. Such apparatus are generally well known in the art. A spinneret 22 can include a first injector 26 concentrically positioned within in a second injector 28. Second injector 28 includes a metal tip 24. The second injector 28 can deliver a solution 30. The first injector 26 can deliver the dispersion of metal nanoparticles 32. The solution 30 and the dispersion of metal nanoparticles 32 can be delivered simultaneously from the spinneret 22 as a charged jet 34. During extrusion of the fiber, the metal tip 24 is electrified to charge the jet 34 by techniques that are well known in the art. The charged jet 34 can be collected on a collector 36.
By employing a co-axial electrospinning apparatus in this manner, the solution and the dispersion of metal nanoparticles can be spun into one or more fibers. In an embodiment, the fibers are core-shell fibers.
Referring back to text block 8 of the flow diagram of
In an embodiment, temperatures used during the heating of the fiber are less than 350° C. For example, in a two step process, a temperature of the first heating step may be chosen from temperatures ranging from about 100° C. to about 180° C.; and the temperature of the second heating step may be chosen from temperatures ranging from about 200° C. to about 300° C. The temperatures employed will vary depending on the specific materials used for the fiber, and may be outside these ranges.
It was surprisingly found that during heating, the metal accumulated at both edges of the core-shell fiber 50, leaving the central portion of the fiber with little or no metal. In an embodiment, the migration of the metal to the edges of the core-shell and the removal of the polymer by thermal degradation resulted in the one as-spun fiber becoming two relatively narrow metal nanostructures.
In an embodiment, the metal fibers have a diameter ranging from about 40 nm to about 5 microns, such as about 100 nm to about 2 microns, or about 500 nm to about 1 microns. Depending on the parameters of the process, the metal nanostructures can be metal lines having a width less than 500 nm. For example, the width can range from about 40 nm to about 500 nm, such as about 100 nm to about 300 nm. In yet another embodiment, two linear arrays of metal dots can be formed instead of the metal lines. The dots can have diameters of, for example, 500 nm or less. By optimizing the electrospinning process parameters, such as flow-rate, applied voltage, distance between spinneret and collector, and the concentration of the polymer solution, metal fibers or dots with desired size and morphology can be obtained.
The present disclosure is also directed to a conductive layer comprising a network of a plurality of metal fibers formed by the processes of the present disclosure. The conductive layer can be formed using any suitable technique for forming a layer from metal fibers.
A 5% poly(propylene carbonate) in MEK solution was poured into a 10 mL syringe of a co-axial electrospinning apparatus. A 40 wt % Ag nanoparticle dispersion in toluene was poured into a 3 mL syringe of the apparatus. The two syringes were mounted into their respective syringe pumps (PPC on the shell channel and Ag on the core channel), and the syringes were connected to the coaxial spinneret. A glass slide (electrospinning collector) was wiped clean using isopropanol, and placed upright approximately 15 cm away from the spinneret tip. About 18-20 kv was applied at the spinneret. Fibers with about 1 μm diameter were generated and collected on the glass slide. An SEM image of the fiber is shown in
The as-spun fiber samples were heated at 130° C. for 15 minutes. Formation of silver fibers was confirmed by optical microscopy, and an SEM image of the fiber is shown at
Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the disclosure are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contains certain errors necessarily resulting from the standard deviation found in their respective testing measurements. Moreover, all ranges disclosed herein are to be understood to encompass any and all sub-ranges subsumed therein.
While the present teachings have been illustrated with respect to one or more implementations, alterations and/or modifications can be made to the illustrated examples without departing from the spirit and scope of the appended claims. In addition, while a particular feature of the present teachings may have been disclosed with respect to only one of several implementations, such feature may be combined with one or more other features of the other implementations as may be desired and advantageous for any given or particular function. Furthermore, to the extent that the terms “including,” “includes,” “having,” “has,” “with,” or variants thereof are used in either the detailed description and the claims, such terms are intended to be inclusive in a manner similar to the term “comprising.” Further, in the discussion and claims herein, the term “about” indicates that the value listed may be somewhat altered, as long as the alteration does not result in nonconformance of the process or structure to the illustrated embodiment. Finally, “exemplary” indicates the description is used as an example, rather than implying that it is an ideal.
It will be appreciated that variants of the above-disclosed and other features and functions, or alternatives thereof, may be combined into many other different systems or applications. Various presently unforeseen or unanticipated alternatives, modifications, variations, or improvements therein may be subsequently made by those skilled in the art which are also intended to be encompasses by the following claims.
| Number | Name | Date | Kind |
|---|---|---|---|
| 20050111805 | Hertz et al. | May 2005 | A1 |
| 20070113530 | Morozov et al. | May 2007 | A1 |
| 20100113857 | Ramakrishna et al. | May 2010 | A1 |
| 20100203333 | Mokhtari et al. | Aug 2010 | A1 |
| 20110151255 | Kim et al. | Jun 2011 | A1 |
| 20120208421 | Qi et al. | Aug 2012 | A1 |
| 20120282484 | Joo et al. | Nov 2012 | A1 |
| 20140027954 | Claracq et al. | Jan 2014 | A1 |
| Entry |
|---|
| Hui Wu et al., “Electrospun Metal Nanofiber Webs as High-Performance Transparent Electrode”, Nano Lett. 2010, 10, pp. 4242-4248. |
| Michael Bognitzki et al., “Preparation of Sub-micrometer Copper Fibers via Electrospinning”, Adv. Mater. 2006, 18, pp. 2384-2386. |
| Number | Date | Country | |
|---|---|---|---|
| 20150086805 A1 | Mar 2015 | US |