Method for forming polymer composite films using a removable substrate

Abstract
The invention is a method for forming polymer composite films using a removable substrate comprising:(a) forming a first dispersion of a first perfluorinated polymer containing sites convertible to ion exchange groups dispersed in a first dispersant having: a boiling point less than about 110.degree. C.; a density of from about 1.55 to about 2.2; and a solubility parameter of from greater than about 7.1 to about 8.2 hildebrands;(b) depositing the first dispersion onto a first removable substrate;(c) heating the first dispersion at a temperature sufficient for form and fuse a first polymer film;(d) forming a second dispersion of a second perfluorinated polymer containing sites convertible to ion exchange groups and a second dispersant having: a boiling point less than about 110.degree. C.; a density of from about 1.55 to about 2.2; and a solubility parameter of from greater than about 7.1 to about 8.2 hildebrands;(e) depositing the second dispersion onto the first film;(f) heating the second dispersion for a time and at a temperature sufficient to form and fuse a second polymer film;(g) bonding the first film to the second film, thereby forming a composite film; and(h) removing the first substrate.Particularly preferred as a first and as a second dispersant is a compound represented by the general formula:XCF.sub.2 -CYZX'wherein:X is selected from the group consisting of F, Cl, Br, and I;X' is selected from the group consisting of Cl, Br, and I;Y and Z are independently selected from the group consisting of H, F, Cl, Br, I and R';R' is selected from the group of perfluoroalkyl radicals and chloroperfluoroalkyl radicals having from 1 to 6 carbon atoms.The most preferred first and second dispersant is 1,2-dibromotetrafluoroethane.
Description

The invention is a method for forming polymer composite films using a removable substrate and particularly for forming ion exchange active composite membranes using a removable substrate.
BACKGROUND OF THE INVENTION
Ion exchange active fluoropolymer films have been widely used in industry, particularly as ion exchange membranes in chlor-alkali cells. Such membranes are made from fluorinated polymers having sites convertible to ion exchange active groups attached to pendant groups from the polymeric backbone.
Such polymers are usually thermoplastic and may be fabricated into films or sheets while in their molten form using mechanical extrusion equipment. However, such equipment is operated in the temperature region near the crystalline melting point of the polymer, which is commonly near the decomposition temperature of some of the polymers. Thus, decomposition may be a problem when some polymers are formed into films by conventional methods. Likewise, it is difficult to make such polymers into films thinner than about 10 microns using such techniques. In addition, it is difficult to make films of consistent thickness. It would be highly desirable to be able to make thin films having a consistent thickness.
Forming membrane structures and support structures into multiple layers is the subject of several patents and applications including U.S. Pat. Nos. 3,925,135; 3,909,378; 3,770,567; and 4,341,605. However, these methods use complicated procedures and equipment including such things as vacuum manifolds, rolls and release media.
Prior art methods for fabricating films from perfluorinated polymers have been limited by the solubility of the polymers and the temperature-dependent viscosity-shear rate behavior of the polymers. To overcome these characteristics of perfluorinated carboxylic ester polymers, workers have tried to swell the polymers using various types of swelling agents and to reduce the fabrication temperatures of the polymers to practical ranges by extraction. Extraction methods have been taught in, for example, U.S. Pat. No. 4,360,601. There, low molecular weight oligomers were removed from carboxylic ester polymers. Polymer "fluff" was extracted in a Soxhlet device at atmospheric pressure for 24 hours (see Examples 1 and 3 of U.S. Pat. No. 4,360,601). Such treatments has been found to make some fluorinated carboxylic ester copolymers more processible and operate more efficiently in a chlor-alkali cell when in a hydrolyzed form. Such extractions modify the fabricated polymer article, for example, by forming grease of the polymer as shown in Example 3 of U.S. Pat. No. 4,360,601.
In addition, such extractions seem to lower processing temperatures of carboxylic ester polymers after isolation. Isolation means separation from the polymerization latex by conventional methods of deactivating the surfactant such as freezing, heating, shearing, salting out or pH adjustment.
British Patent 1,286,859 teaches that highly polar organic "solvents" dissolve small amounts a fluorinated vinyl ether/tetrafluoroethylene copolymer in its thermoplastic form. Thermoplastic form means the polymer is in a form which can be molded or processed above some transition temperature (such as the glass transition temperature or the melting point) without altering its chemical structure or composition. The patent teaches the use of the following materials "solvents": butanol, ethanol, N,N-dimethylacetamide, and N,N-dimethylaniline.
Similar approaches have been used to swell membranes in their ionic forms. Ionic forms of membranes are membranes which have been converted from their thermoplastic form (--SO.sub.3 F or --COOCH.sub.3) to their ionic forms (--SO.sub.3 M or --COOM) where M is H.sup.+, K.sup.+, Na.sup.+, or NH.sub.4 .sup.+ or other metal ion.
Prior art workers have used highly polar solvents or mixtures of solvents on substantially perfluorinated polymers and less polar solvents on fluorinated polymers containing hydrocarbon components as co-monomers, ter-monomers or crosslinking agents.
However, each of the prior art methods for swelling, dispersing or extracting the polymers has certain shortcomings which are known to those practicing the art. Polar solvents have the potential for water absorption or reactivity with the functional groups during subsequent fabrication operations, thus making poor coatings, films, etc. High boiling solvents are difficult to remove and frequently exhibit toxic or flammability properties. Functional form (ionic forms) of the polymers can react with solvents. (See Analytical Chem., 1982, Volume 54, pages 1639-1641).
The more polar of the solvents such as methanol, butanol esters, and ketones as used in U.S. 3,740,369; British Patent 1,286,859; and Chemical Abstracts 90:169702 have high vapor pressures at ambient conditions, which are desirable for solvent removal; however, they tend to absorb water. Their water content is undesirable because it causes problems in producing continuous coatings and films of hydrophobic polymers. In addition, polar solvents frequently leave residues which are incompatible with the polymers. Also, they frequently leave residues which are reactive during subsequent chemical or thermal operations if they are not subsequently removed.
Another approach taken by the prior art workers to form films from fluoropolymers include the use of high molecular weight "solvents" which have been produced by halogenating vinyl ether monomers. (See British Patent 2,066,824A).
The swelling of the functional (ionic) forms of the fluoropolymers by polar or hydrophilic agents has been known for some time. In addition, the solvent solubility parameters were compared to the swelling effect of 1200 equivalent weight Nafion ion exchange membrane (available from E. I. DuPont Company) by Yeo at Brookhaven Laboratory (see Polymer, 1980, Volume 21, page 432).
The swelling was found to be proportional to two different ranges of the solubility parameter and a calculation was developed for optimizing ratios of solvent mixtures. Ionic forms of functional fluoropolymers may be treated in such a manner, however, the subsequent physical forming or manipulation of the polymers into usable configurations by any thermal operation is limited when the polymers are in the functional forms. In addition, non-ionic forms of polymers treated in this manner are also limited in the thermoplastic processing range by the stability of the functional group bonds.
Other solvation methods have used temperatures near the crystalline melting points of the polymers being solvated, thus requiring either high boiling point "solvents" or high pressure vessels to maintain the system in a solid/liquid state. See Analytical Chem., 1982, Volume 54, pages 1639-1641.
Burrell states the theory of Bagley [J. Paint Tech., Volume 41, page 495 (1969)]predicts a non-crystalline polymer will dissolve in a solvent of similar solubility parameter without chemical similarity, association, or any intermolecular force. However, he fails to mention anything about the solubility of polymers demonstrating crystallinity.
SUMMARY OF THE INVENTION
The invention is a method for forming polymer composite films using a removable substrate comprising:
(a) forming a first dispersion of a first perfluorinated polymer containing sites convertible to ion exchange groups and a first dispersant having: a boiling point less than about 110.degree. C.; a density of from about 1.55 to about 2.97 grams per cubic centimeter; and a solubility parameter of from greater than about 7.1 to about 8.2 hildebrands;
(b) depositing the first dispersion onto a first removable substrate;
(c) heating the first dispersion at a temperature sufficient to form and fuse a first polymer film;
(d) forming a second dispersion of a second perfluorinated polymer containing sites convertible to ion exchange groups and a second dispersant having: a boiling point less than about 110.degree. C.; a density of from about 1.55 to about 2.97 grams per cubic centimeter; and a solubility parameter of from greater than about 7.1 to about 8.2 hildebrands;
(e) depositing the second dispersion onto the first film;
(f) heating the second dispersion for a time and at a temperature sufficient to form and fuse a second polymer film;
(g) bonding the first film to the second film, thereby forming a composite film; and
(h) removing the first substrate.
Particularly preferred as a first and as a second dispersant is a compound represented by the general formula:
XCF.sub.2 -CYZX'
wherein:
X is selected from the group consisting of F, Cl, Br, and I;
X' is selected from the group consisting of Cl, Br, and I;
Y and Z are independently selected from the group consisting of H, F, Cl, Br, I and R';
R' is selected from the group of perfluoroalkyl radicals and chloroperfluoroalkyl radicals having from 1 to 6 carbon atoms.
The most preferred first and second dispersant is 1,2-dibromotetrafluoroethane.
DETAILED DESCRIPTION OF THE INVENTION
Dispersion, as used herein, means a composition containing a treating agent and a perfluorinated polymer containing sites convertible to ion exchange groups. The polymer is at least partially dissolved in the dispersant and is dispersed into the dispersant.
The present invention can be used to make ion exchange composite films suitable for use in electrolytic cells, fuel cells and gas or liquid permeation units.
Non-ionic forms of perfluorinated polymers described in the following U.S. Pat. Nos. are suitable for use in the present invention: 3,282,875; 3,909,378; 4,025,405; 4,065,366; 4,116,888; 4,123,336; 4,126,588; 4,151,052; 4,176,215; 4,178,218; 4,192,725; 4,209,635; 4,212,713; 4,251,333; 4,270,996; 4,329,435; 4,330,654; 4,337,137; 4,337,211; 4,340,680; 4,357,218; 4,358,412; 4,358,545; 4,417,969; 4,462,877; 4,470,889; and 4,478,695; European Patent Application 0,027,009. These polymers usually have equivalent weights of from about 500 to about 2000.
Particularly preferred for the formation of each layer of the composite films of the present invention are copolymers of monomer I with monomer II (as defined below). Optionally, a third type of monomer may be copolymerized with I and II.
The first type of monomer is represented by the general formula:
CF.sub.2 =CZZ' (I)
where:
Z and Z' are independently selected from the group consisting of --H, --Cl, --F, or CF.sub.3.
The second monomer consists of one or more monomer selected from compounds represented by the general formula:
Y-(CF.sub.2).sub.a -(CFR.sub.f (CFR'.sub.f).sub.c -0-[CF(CF.sub.2 X)-CF.sub.2 -0].sub.n -CF=CF.sub.2 (II)
where:
Y is selected from the group consisting of --SO.sub.2 Z, --CN, --COZ and C(R.sup.3.sub.f)(R.sup.4.sub.f)OH;
Z is I, Br, Cl, F, OR, or NR.sub.1 R.sub.2 ;
R is a branched or linear alkyl radical having from 1 to about 10 carbon atoms or an aryl radical;
R.sup.3.sub.f and R.sup.4.sub.f are independently selected from the group consisting of perfluoroalkyl radicals having from 1 to about 10 carbon atoms;
R.sub.1 and R.sub.2 are independently selected from the group consisting of H, a branched or linear alkyl radical having from 1 to about 10 carbon atoms or an aryl radical;
a is 0-6;
b is 0-6;
c is 0 or 1;
provided a+b+c is not equal to 0;
X is Cl, Br, F or mixtures thereof when n>1;
n is 0 to 6; and
R.sub.f and R'.sub.f are independently selected from the group consisting of F, Cl, perfluoroalkyl radicals having from 1 to about 10 carbon atoms and fluorochloroalkyl radicals having from 1 to about 10 carbon atoms.
Particularly preferred is when Y is --SO.sub.2 F or --COOCH.sub.3 ; n is 0 or 1; R.sub.f and R'.sub.f are F; X is Cl or F; and a+b+c is 2 or 3.
Although the polymers of each layer can have the same or different radicals for Y, the most preferred composite polymer is one where the polymer of one layer has Y as -SO.sub.2 F and the polymer of the other layer has Y as --COOCH.sub.3.
By composite films we mean film composed of two or more different polymers. These polymers may differ by type or concentration of sites convertible to ion exchange group. These different polymers are disposed in layers parallel to the film surface.
The third and optional monomer suitable is one or more monomers selected from the compounds represented by the general formula:
Y'-(CF.sub.2).sub.a' -(CFR.sub.f).sub.b' -(CFR'.sub.f) -0-[CF(CF.sub.2 X')-CF.sub.2 -O].sub.n' -CF.dbd.CF.sub.2 (III)
where:
Y' is F, Cl or Br;
a' and b' are independently 0-3;
c' is 0 or 1;
provided a'+b'+c' is not equal to 0;
n' is 0-6;
R.sub.f and R'.sub.f are independently selected from the group consisting of Br, Cl, F, perfluoroalkyl radicals having from about 1 to about 10 carbon atoms, and chloroperfluoroalkyl radicals having from about 1 to about 10 carbon atoms; and
X' is F, Cl, Br, or mixtures thereof when n'>1.
Conversion of Y to ion exchange groups is well known in the art and consists of reaction with an alkaline solution.
The monomer FSO.sub.2 CF.sub.2 CF.sub.2 OCF=CF.sub.2 has a density of about 1.65 grams per cubic centimeter and a polymer of tetrafluoroethylene has a density of about 2.2 grams per cubic centimeter. A copolymer of this monomer with tetrafluoroethylene would, thus, have a density between the two values.
It has been discovered that certain perhalogenated dispersants have a surprising effect of dispersing the polymers, especially when the polymers are in a finely divided state.
Dispersants suitable for use in the present invention should have the following characteristics:
a boiling point less than about 110.degree. C.;
a density of from about 1.55 to about 2.97 grams per cubic centimeter;
a solubility parameter of from greater than about 7.1 to about 8.2 hildebrands.
It is desirable that the dispersant has a boiling point of from about 30.degree. C. to about 110.degree. C. The ease of removal of the dispersant and the degree of dispersant removal is important in producing various films, coatings and the like, without residual dispersant; hence a reasonable boiling point at atmospheric pressure allows convenient handling at room conditions yet effective dispersant removal by atmospheric drying or mild warming.
It is desirable that the dispersant has a density of from about 1.55 to about 2.97 grams per cubic centimeter. The polymers of the present invention have densities on the order of from about 1.55 to about 2.2 grams per cubic centimeter. Primarily, the polymers have densities in the range of from about 1.6 to about 2.2 grams per cubic centimeter. Dispersants of the present invention will therefore swell, dissolve and disperse small particles of this polymer, aided by the suspending effects of the similarity in densities.
The prior art did not balance density. They were interested in forming solutions and solutions do not separate.
Solubility parameters are related to the cohesive energy density of compounds. The calculation of solubility parameters is discussed in U.S. Pat. No. 4,348,310, the teachings of which are incorporated by reference for the purposes of their teachings on solubility parameters.
It is desirable that the dispersant has a solubility parameter of from greater than about 7.1 to about 8.2 hildebrands. The similarity in cohesive energy densities between the dispersant and the polymer determine the likelihood of dissolving, swelling and dispersing the polymer in the dispersant.
It is preferable that the dispersant has a vapor pressure of up to about 760 millimeters of mercury at the specified temperature limits at the point of dispersant removal. The dispersant should be conveniently removed without the necessity of higher temperatures or reduced pressures involving extended heating such as would be necessary in cases similar to U.S. Pat. No. 3,692,569 or the examples in British Patent 2,066,824A in which low pressures (300 millimeters) had to be employed as well as non-solvents to compensate for the higher boiling points and low vapor pressures of the complex solvents.
It has been found that dispersants represented by the following general formula are particularly preferred provided they also meet the characteristics discussed above (boiling point, density, and solubility parameter):
XCFhd 2-CYZ-X'
wherein:
X is selected from the group consisting of F, Cl, Br, and I;
X' is selected from the group consisting of Cl, Br, and I;
Y and Z are independently selected from the group consisting of H, F, Cl, Br, I and R';
R' is selected from the group of perfluoroalkyl radicals and chloroperfluoroalkyl radicals having from 1 to 6 carbon atoms.
The most preferred dispersants are 1,2-dibromotetrafluoroethane (commonly known as Freon 114 B 2)
BrCF.sub.2 -CF.sub.2 Br and 1,2,3-trichlorotrifluoroethane (commonly known as Freon 113):
ClF.sub.2 C-CCl.sub.2 F
Of these two dispersants, 1,2-dibromotetrafluoroethane is the most preferred dispersant. It has a boiling point of about 47.3.degree. C, a density of about 2.156 grams per cubic centimeter, and a solubility parameter of about 7.2 hildebrands.
1,2-dibromotetrafluoroethane is thought to work particularly well because, though not directly polar, it is highly polarizable. Thus, when 1,2-dibromotetrafluoroethane is associated with a polar molecule, its electron density shifts and causes it to behave as a polar molecule. Yet, when 1,2-dibromotetrafluoroethane is around a non-polar molecule, it behaves as a non-polar dispersant. Thus, 1,2-dibromotetrafluoroethane tends to dissolve the non-polar backbone of polytetrafluoroethylene and also the polar, ion-exchange-containing pendant groups. Its solubility parameter is calculated to be from 7.13 to 7.28 hildebrands.
It is surprising that an off-the-shelf, readily-available compound such as 1,2-dibromotetrafluoroethane would act as a solvent for the fluoropolymers described above. It is even more surprising that 1,2-dibromotetrafluoroethane happens to have a boiling point, a density and a solubility parameter such that it is particularly suitable for use as a solvent/dispersant in the present invention.
In practicing the present invention, the polymer may be in any physical form. However, it is preferably in the form of fine particles to speed dissolution and dispersion of the particles into the dispersant. Preferably, the particle size of the polymers is from about 0.01 microns to about 840 microns. Most preferably, the particle size is less than about 250 microns.
To dissolve and disperse the polymer particles into the dispersant, the polymer particles are placed in contact with the dispersant of choice and intimately mixed. The polymer and the dispersant may be mixed by any of several means including, but not limited to, shaking, stirring, milling or ultrasonic means. Thorough, intimate contact between the polymer and the dispersant is needed for optimum dissolution and dispersion.
The polymers of the present invention are dissolved and dispersed into the dispersants at concentrations ranging from about 0.1 to about 50 weight percent of polymer to dispersant. At concentrations below about 0.1 weight percent, there is insufficient polymer dissolved and dispersed to be effective as a medium for coating articles or forming films within a reasonable number of repetitive operations. Conversely, at concentrations above about 50 weight percent there is sufficient polymer present as a separate phase such that viable, coherent films and coatings of uniform structure cannot be formed without particulate agglomerates, etc.
Preferably, the concentration of the polymer in the dispersant is from about 0.1 to about 20 weight percent. More preferably, the concentration of the polymer in the dispersant is from about 0.3 to about 10 weight percent. Most preferably, the concentration is from about 5 to about 15 weight percent.
The dispersion of the polymer into the dispersant can be conducted at room temperature conditions. However, the optimum dispersion effects are best achieved at temperatures from about 10.degree. C. to about 50.degree. C. At temperatures above about 50.degree. C. the measures for dissolving and dispersing the polymer have to include pressure confinement for the preferred dispersants or method of condensing the dispersants. Conversely, at temperatures below about 10.degree. C. many of the polymers of the present invention are below their glass transition temperatures thus causing their dispersions to be difficult to form at reasonable conditions of mixing, stirring, or grinding.
The dispersion of the polymers of the present invention into the dispersant are best conducted at atmospheric pressure. However, dispersion effects can be achieved at pressures from about 760 to about 15,000 millimeters mercury or greater. At pressures below about 760 millimeters mercury, the operation of the apparatus presents no advantage in dissolving and dispersing polymers, rather hindering permeation into the polymers and thus preventing forming of the dispersions.
Conversely, pressures above about 760 millimeters mercury aid in dissolving and dispersing polymers very little compared to the difficulty and complexity of the operation. Experiments have shown that at about 20 atmospheres the amount of polymer dissolved and dispersed in the dispersant is not appreciably greater.
After the polymer first dispersion of the present invention has been formed, it is fixed to a substrate by sintering or compression to fix the polymer from the dispersion to the substrate.
The following methods are suitable for fixing the dispersion of the present invention to a substrate. Dipping the substrate into the dispersion, followed by air drying and sintering at the desired temperature with sufficient repetition to build the desired thickness. Spraying the dispersion onto the substrate is used to advantage for covering large or irregular shapes. Pouring the dispersion onto the substrate is sometimes used. Painting the dispersion with brush or roller has been successfully employed. In addition, coatings may be easily applied with metering bars, knives, or rods. Usually, the coatings or films are built up to the thickness desired by repetitive drying and sintering.
The type of substrate upon which the dispersion of the present invention may be applied can include such things as glass, aluminum foil, polytetrafluoroethylene tape, polytetrafluoroethylene sheets, metal sheets, or other polymer films or objects.
The substrate upon which the dispersion is to be deposited is cleaned or treated in such a way as to assure uniform contact with the dispersion. The substrate can be cleansed by washing with a degreaser or similar solvent followed by drying to remove any dust or oils from objects to be used as substrates. Metals should usually be acid etched, then washed with a solvent to promote adhesion, if desired, unless the metal is new in which case degreasing is sufficient.
After being cleaned, the substrates may be pre-conditioned by heating or vacuum drying prior to contact with the dispersions and the coating operation. Temperatures and pressures in the following ranges are preferably used: about 20 millimeters mercury at about 110.degree. C. or thereabout is sufficient in all cases; however, mild heat is usually adequate, on the order of about 50.degree. C. at atmospheric pressure.
After preparation, the substrates are coated with the dispersion by any of several means including, but not limited to, dipping, spraying, brushing, pouring. Then the dispersion may be evened out using scraping knives, rods, or other suitable means. The dispersion can be applied in a single step or in several steps depending on the concentration of the polymer in the dispersion and the desired thickness of the coating or film.
Following the application of the dispersion, the dispersant is removed by any of several methods including, but not limited to, evaporation or extraction. Extraction is the use of some agent which selectively dissolves or mixes with the dispersant but not the polymer.
These removal means should be employed until a uniform deposition of polymer is obtained and a continuous film is formed.
The dispersant removal is typically carried out by maintaining the coated substrate at temperatures ranging from about 10.degree. C. to about 110.degree. C., with the preferred heating range being from about 20.degree. C. to about 100.degree. C. The heating temperature selected depends upon the boiling point of the dispersant.
Heating temperatures are customarily in the range of from about 20.degree. C. to about 50.degree. C. for 1,2-dibromotetrafluoroethane.
The pressures employed for the removal of the dispersant from the coated substrate can range from about 20 mm mercury to about 760 mm mercury depending on the nature of the dispersant, although pressures are typically in the range of from about 300 mm mercury to about 760 mm mercury for 1,2-dibromotetrafluoroethane.
The forming of the coating or film can be carried out as part of the polymer deposition and dispersant removal process or as a separate step by adjusting the thermal and pressure conditions associated with the separation of the polymer from the dispersant. If the dispersion is laid down in successive steps, a continuous film or coating free from pinholes can be formed without any subsequent heating above ambient temperature by control of the rate of evaporation. This can be done by vapor/liquid equilibrium in a container or an enclosure; therefore, the dispersant removal step can be merely a drying step or a controlled process for forming a coating or film. If the dispersant is removed as by flash evaporation, a film will not form without a separate heating step.
After the dispersant has been removed, the residual polymer and substrate, as a separate step, is preferably subjected to a heat source of from about 150.degree. C. to about 380.degree. C. for times ranging from about 10 seconds to about 120 minutes, depending upon the thermoplastic properties of the polymers. The polymers having melt viscosities on the order of 5 .times.10.sup.5 poise at about 300.degree. C. at a shear rate of 1 sec..sup.-1 as measured by a typical capillary rheometer would require the longer times and higher temperatures within the limits of the chemical group stability. Polymers with viscosities on the order of 1 poise at ambient temperatures would require no further treatment.
The most preferred treatment temperatures are from about 270.degree. C. to about 350.degree. C. and a time of from about 0.2 to about 45 minutes for the most preferred polymers for use in the present invention. Such polymers form thin continuous films under the conditions described above.
After the polymer from the dispersion has been fixed to its substrate, it is contacted with a second polymer dispersion formed in the same manner used to form the first dispersion. Thereafter, the second dispersion is fused to form the second film and to bond the second film to the first film. The second film is formed and the two films are fused together by heating the two films at a temperature, at a pressure and for a time sufficient to bond the two polymers together. Such temperatures are usually from about 150 to about 380.degree. C. The pressures suitable pressures up to about 2000 psi. The times are from about 10 seconds to about 120 minutes.
Thereafter, the removable substrate should be removed. A variety of means can be used to remove the substrate including chemically etching the substrate away, vaporizing the substrate, dissolving the substrate, peeling the substrate from the film, peeling the film from the substrate, and other physical or chemical means.
Composite films of varying thicknesses can be easily produced by the methods and means described above. Such films are suitable as membranes, when in their ionic forms, for use in electrochemical cells. They are particularly useful for the electrolysis of sodium chloride brine solutions to produce chlorine gas and sodium hydroxide solutions. Membranes prepared according to the present invention have surprisingly good current efficiencies when used in chlor-alkali cells.
Steps f and g in the Summary of the Invention can be alternately accomplished in one coordinated operation, rather than separately. That is, the second film may be formed and fused at the same time it is being fused to the first film.





EXAMPLES
Example 1
A copolymer of CF.sub.2 =CF.sub.2 and CF.sub.2 =CFOCF.sub.2 CF.sub.2 COOCH.sub.3 was prepared as followed:
50 g of CF.sub.2 =CFOCF.sub.2 CF.sub.2 COOCH.sub.3 was added to 250 g of deoxygenated water containing 3 grams of NH.sub.4 O.sub.2 CC.sub.7 F.sub.15, 1.5 grams of Na.sub.2 HPO.sub.4. 7H.sub.2 O and 1.0 gram of NaH.sub.2 PO.sub.4.H.sub.2 O in a glass reactor with stirring at 800 rpm. Next, 50 ml of deoxygenated water containing 0.05 (NH.sub.4).sub.2 S.sub.2 O.sub.8 was injected into the reactor and the reactor was kept under a positive pressure of 220 psig tetrafluoroethylene at 50.degree. C. for 180 minutes. The reactor was vented and the contents was acidified with 50 ml 6N HCl to coagulate the latex and cause the polymer to separate from the emulsion. The polymer was filtered, vigorously washed to remove inorganics, soap and residual monomers and then vacuum dried for 16 hours at 85.degree. C. The dried polymer weighed 99.2 grams and upon titration was found to be 856 equivalent weight.
A dispersion of the 856 equivalent weight carboxylic ester polymer was made by mixing about 49 grams of the polymer with about 304 grams of 1,2-dibromotetrafluoroethane.
A polymer having an equivalent weight of about 850 was prepared according to the following procedure:
About 784 grams of CF.sub.2 =CFOCF.sub.2 CF.sub.2 SO.sub.2 F were added to about 4700 grams of deoxygenated water containing about 25 grams NH.sub.4 O.sub.2 CC.sub.7 F.sub.15, about 18.9 gr Na.sub.2 HPO.sub.4. 7H.sub.2 O, about 15.6 grams of NaH.sub.2 PO.sub.4.H.sub.2 O and about 4 grams of (NH.sub.4).sub.2 S.sub.2 O.sub.8 under a positive pressure of about 192 pounds per square inch gauge (psig) of tetra.TM.fluoroethylene at about 60.degree. C. for about 88 minutes. The reactor was vented under heat and vacuum to remove residual monomers. The reactor contents was frozen, thawed, and vigorously washed to remove residual salts and soap.
About 30 grams of the polymer was made into a dispersion using about 270 grams of 1,2-dibromotetrafluoroethane. The dispersion was coated onto an aluminum foil and heated to about 300.degree. C. for about 1 minute. The coating and heating steps were repeated until a coating about 4 mils thick (about 102 microns) was achieved.
A piece of aluminum foil was coated with a dispersion of the 856 EW carboxylic ester copolymer. The dispersant was allowed to air dry and the coated foil was fused for 1 minute at 250.degree. C. between polytetrafluoroethylene coated glass cloth sheets. The process was repeated to build a 1 mil thick (25.4 .mu.) film. The carboxylic ester copolymer film on the foil was then coated in a like manner with an 850 equivalent weight fluorosulfonyl copolymer dispersion to build a fluorosulfonyl copolymer film until the total film thickness of the two combined films was 5 mils (12.7 .mu.). The coated foil was placed polymer side down on top of a sized polytetrafluoroethylene fabric (Prodesco Inc. 12 .times.12 leno weave cloth) which was in turn placed on a vacuum table. The vacuum was applied and the table was placed under a heated platen for about 4 minutes at about 250.degree. C. The polytetrafluoroethylene fabric was firmly bonded to the support layer polymer.
Claims
  • 1. A method for forming polymer composite films using a removable substrate comprising:
  • (a) forming a first dispersion of a first perfluorinatedpolymer containing sites convertible to ion exchange groups and a dispersant having: a boiling point less than about 110.degree. C.; a density of from about 1.55 to about 2.97 grams per cubic centimeter; and a solubility parameter of from greater than about 7.1 to about 8.2 hildebrands, wherein the prefluorinated polymer in the dispersion has a particle size of from about 0.01 micron to about 840 microns;
  • (b) depositing the first dispersion onto a first removable substrate;
  • (c) heating the first dispersion at a temperature sufficient to form an fuse a first polymer film;
  • (d) forming a second dispersion of a second perfluorinated polymer containing sits convertible to ion exchange groups and a second dispersant having: a boiling point less than about 110.degree. C.; a density of from about 1.55 to about 2.97 grams per cubic centimeter; and a solubility parameter of from greater than about 7.1 to about 8.2 hildebrands, wherein the perfluorinated polymer in the dispersion has a particle size of from about 0.01 micron to about 840 micron;
  • (e) depositing the second dispersion onto the first film;
  • (f) heating the second dispersion for a time and at a temperature sufficient to form and fuse a second polymer film;
  • (g) bonding the first film to the second film; thereby forming a composite film; and
  • (h) removing the first substrate wherein the first and the second dispersants are independently represented by the general formula:
  • XCF.sub.2 -CYZX'
  • where:
  • X is selected from the group consisting of F, Cl, Br, and I;
  • X' is selected from the group consisting of Cl, Br, and I;
  • Y and Z are independently selected from the group consisting of H, F, Cl, Br, I and R';
  • R' is selected from the group of perfluoralkyl radicals and chloroperfluoralkyl radicals having from 1 to 6 carbon atoms.
  • 2. The method of claim 1 wherein the first and the second perfluorinated polymers are independently selected from the group of copolymers formed from a first type of monomer and a second type of monomer:
  • wherein the first type of monomer is represented by the general formula:
  • CF.sub.2 =CZZ' (I)
  • where:
  • Z and Z' are independently selected from the group consisting of --H, --Cl, --F, or CF.sub.3; and
  • the second monomer is represented by the general formula:
  • Y-(CF.sub.2).sub.a -(CFR.sub.f).sub.b -(CFR'.sub.f).sub.c -0-[CF(CF.sub.2 X)-CF.sub.2 -O].sub.n -CF.dbd.CF.sub.2 (II)
  • where:
  • Y is selected from the group consisting of --SO.sub.2 Z, --CN, --COZ and C(R.sup.3.sub.f)(R.sup.4.sub.f)OH;
  • Z is I, Br, Cl, F, OR, or NR.sub.1 R.sub.2;
  • R is a branched or linear alkyl radical having from 1 to about 10 carbon atoms or an aryl radical;
  • Rhu 3.sub.f and R.sup.4.sub.f independently selected from the group consisting of perfluoroalkyl radicals having from 1 to about 10 carbon atoms;
  • R.sub.1 and R.sub.2 are independently selected from the group consisting of H, a branched or linear alkyl radical having from 1 to about 10 carbon atoms or an aryl radical;
  • a is 0-6;
  • b is 0-6;
  • c is 0 or 1;
  • provided a+b+c is not equal to 0;
  • X is Cl, Br, F or mixtures thereof when n>1;
  • n is 0 to 6; and
  • R.sub.f and R'.sub.f are independently selected from the group consisting of F, Cl, perfluoroalkyl radicals having from 1 to about 10 carbon atoms and fluorochloroalkyl radicals having from 1 to about 10 carbon atoms.
  • 3. The method of claim 2 wherein the first and the second perfluorinated polymers independently include a third type of monomer wherein the third type of monomer is one or more monomers represented by the general formula:
  • Y'-(CF.sub.2).sub.a' -(CFR.sub.f).sub.b' -(CFR'.sub.f).sub.c' -0-[CF(CF.sub.2 X')-CF.sub.2 -0 (III)
  • where:
  • Y' is F, Cl or Br;
  • a' and b' are independently 0-3;
  • c' is 0 or 1;
  • provided a'+b'+c' is not equal to 0;
  • n' is 0-6;
  • R.sub.f and R'.sub.f independently selected from the group consisting of Br, Cl, F, perfluoroalkyl radicals having from about 1 to about 10 carbon atoms, and chloroperfluoroalkyl radicals having from about 1 to about 10 carbon atoms; and
  • X' is F, Cl, Br, or mixtures thereof when n'>1.
  • 4. The method of claim 1 wherein the boiling point of the first and second dispersant is from about 30.degree. C. to about 110.degree. C.
  • 5. The method of claim 1 wherein the density of the first and the second dispersant is from about 1.55 to about 2.2 grams per cubic centimeter.
  • 6. The method of claim 1 wherein the solubility parameter of the first and second dispersant is from greater than about 7.1 to about 7.5 hildebrands.
  • 7. The method of claim 1 wherein the density of the first and second dispersant and the density of the first and second polymer are both from abut 1.55 to about 2.2 grams per cubic centimeter.
  • 8. The method of claim 1 wherein X and X' are Br.
  • 9. The method of claim 1 wherein X and X' are Cl.
  • 10. The method of claim 1 wherein the first and the second polymers are present in the first and the second dispersions at a concentration of from about 0.1 to about 50 weight percent.
  • 11. The method of claim 1 wherein the first and the second polymers are present in the first and the second dispersions at a concentration of from about 0.3 to about 30 weight percent.
  • 12. The method of claim 1 wherein the removable substrate is aluminum.
  • 13. The method of claim 1 wherein the substrate is removed by dissolving with a solvent for the substrate.
  • 14. The method of claim 1 wherein the substrate is removed by an alkaline solution.
  • 15. The method of claim 1 including heating the coated substrate to a temperature of up to about 30020 C. to fuse the first film to the second film.
  • 16. The method of claim 1 wherein steps (f) and (g) are conducted simultaneously.
US Referenced Citations (49)
Number Name Date Kind
3282875 Connolly et al. Nov 1966
3671345 Barnes et al. Jun 1972
3692569 Grot Sep 1972
3740369 Proskow Jun 1973
3770567 Grot Nov 1973
3909378 Walmsley Sep 1975
3925135 Grot Dec 1975
4025405 Dotson et al. May 1977
4065366 Oda et al. Dec 1977
4112149 Babinsky Sep 1978
4116888 Ukihashi et al. Sep 1978
4123336 Seko et al. Oct 1978
4126588 Ukihashi et al. Nov 1978
4147844 Babinsky et al. Apr 1979
4151052 Goto et al. Apr 1979
4176215 Molnar et al. Nov 1979
4178218 Seko Dec 1979
4192725 Dotson et al. Mar 1980
4209635 Munekata et al. Jun 1980
4212713 Suhara et al. Jul 1980
4251333 Suhara et al. Feb 1981
4259226 Suhara et al. Mar 1981
4270996 Suhara et al. Jun 1981
4298697 Baczek et al. Nov 1981
4329435 Kimoto et al. May 1982
4330654 Ezzell et al. May 1982
4337137 Ezzell Jun 1982
4337211 Ezzell et al. Jun 1982
4340680 Asawa et al. Jul 1982
4341605 Solenberger et al. Jul 1982
4348310 Silva et al. Sep 1982
4357218 Seko Nov 1982
4358412 Ezzell et al. Nov 1982
4358545 Ezzell et al. Nov 1982
4360601 Copeland et al. Nov 1982
4386787 Covitch et al. Jun 1983
4417969 Ezzell et al. Nov 1983
4421579 Covitch et al. Dec 1983
4437951 Bissot et al. Mar 1984
4437952 Smith et al. Mar 1984
4462877 Ezzell Jul 1984
4469579 Covitch et al. Sep 1984
4470889 Ezzell et al. Sep 1984
4478695 Ezzell et al. Oct 1984
4545886 de Nora et al. Oct 1985
4610762 Birdwell Sep 1986
4650551 Carl et al. Mar 1987
4650711 Carl et al. Mar 1987
4654104 McIntyre et al. Mar 1987
Foreign Referenced Citations (12)
Number Date Country
0027009 Apr 1981 EPX
0066369 Dec 1982 EPX
0122049 Oct 1984 EPX
1584426 Dec 1969 FRX
1245923 Sep 1971 GBX
1286859 Aug 1972 GBX
2051091A Jan 1981 GBX
2060703A May 1981 GBX
2064586A Jun 1981 GBX
2066824A Jul 1981 GBX
2069006A Aug 1981 GBX
2101160 Jan 1983 GBX
Non-Patent Literature Citations (6)
Entry
Journal of the Electrochemical Society, vol. 131, Part I, No. 1-6, 1984, pp. 1350-1352.
Chemical Abstract No. 90:169702z, vol. 90, 1979, "Cation Exchange Membrane".
J. Paint Tech., vol. 41, p. 495, 1969, "Hydrogen Bonding Effects in Non-Electrolyte Solutions".
Analytical Chem., vol. 54, pp. 1639-1641, 1982 "Dissolution of Perfluorinated Ion Containing Polymers".
"Dual Cohesive Energy Densities of Perfluorosulfonic Acid (Nafion) Membrane", Richard S. Yeo, Polymer, p. 432, vol. 21, Apr. 1980.
"Solubility Characteristics of Perfluorinated Polymers with Sulfonyl Fluoride Functionality", G. H. McCain and M. J. Covitch, Journal Electrochemical Society: Electrochemical Science and Technology, Jun. 1984, pp. 1350-1352.
Continuations (1)
Number Date Country
Parent 739936 May 1985