Method for heat treating PTC devices

Information

  • Patent Grant
  • 6582647
  • Patent Number
    6,582,647
  • Date Filed
    Thursday, September 30, 1999
    25 years ago
  • Date Issued
    Tuesday, June 24, 2003
    21 years ago
Abstract
The present invention provides a method for heat treating a polymer PTC composition to increase the peak resistivity of the composition making it especially well suited for high voltage applications. A polymer PTC composition having a melting point temperature Tmp is provided. The temperature of the polymer PTC composition is increased at a rate, r1, to a temperature greater than Tmp. The temperature of polymer PTC composition is held at the temperature greater than Tmp for a predetermined period of time. Then the temperature of the polymer PTC composition is decreased to a temperature less than Tmp at a rate, r2, wherein r2 is greater than r1.
Description




TECHNICAL FIELD




The present invention relates generally to a process for heat treating conductive polymer compositions and electrical devices to improve their electrical properties.




BACKGROUND OF THE INVENTION




It is well known that the resistivity of many conductive materials change with temperature. Resistivity of a positive temperature coefficient (“PTC”) material increases as the temperature of the material increases. Many crystalline polymers, made electrically conductive by dispersing conductive fillers therein, exhibit this PTC effect. These polymers generally include polyolefins such as polyethylene, polypropylene, polyvinylidene fluoride and ethylene/propylene copolymers. Certain doped ceramics such as barium titanate also exhibit PTC behavior.




At temperatures below a certain value, i.e., the critical or switching temperature, the PTC material exhibits a relatively low, constant resistivity. However, as the temperature of the PTC material increases beyond this point, the resistivity sharply increases with only a slight increase in temperature.




Electrical devices employing polymer and ceramic materials exhibiting PTC behavior have been used as overcurrent protection in electrical circuits. Under normal operating conditions in the electrical circuit, the resistance of the load and the PTC device is such that relatively little current flows through the PTC device. Thus, the temperature of the device due to I


2


R heating remains below the critical or switching temperature of the PTC device. The device is said to be in an equilibrium state (i.e., the rate at which heat is generated by I


2


R heating is equal to the rate at which the device is able to lose heat to its surroundings).




If the load is short circuited or the circuit experiences a power surge, the current flowing through the PTC device increases and the temperature of the PTC device (due to I


2


R heating) rises rapidly to its critical temperature. At this point, a great deal of power is dissipated in the PTC device and the PTC device becomes unstable (i.e., the rate at which the device generates heat is greater than the rate at which the device can lose heat to its surroundings). This power dissipation only occurs for a short period of time (i.e., a fraction of a second), however, because the increased power dissipation will raise the temperature of the PTC device to a value where the resistance of the PTC device has become so high that the current in the circuit is limited to a relatively low value. This new current value is enough to maintain the PTC device at a new, high temperature/high resistance equilibrium point, but will not damage the electrical circuit components. Thus, the PTC device acts as a form of a fuse, reducing the current flow through the short circuit load to a safe, relatively low value when the PTC device is heated to its critical temperature range. Upon interrupting the current in the circuit, or removing the condition responsible for the short circuit (or power surge), the PTC device will cool down below its critical temperature to its normal operating, low resistance state. The effect is a resettable, electrical circuit protection device.




Devices having higher resistance in the tripped state, i.e., at its new, high temperature/high resistance equilibrium point, are useful for high voltage applications. However, often during the manufacturing process of PTC devices the polymer composition is exposed to high temperatures, mechanical shear, thermal gradients and other influences which affect the electrical properties of the polymer composition, and particularly lower the peak resistance of the device rendering it unacceptable for higher voltage applications. Additionally, the resistance of the device can be adversely affected when the device is soldered to a PC board, once again rendering the device unacceptable for specific applications.




SUMMARY OF THE INVENTION




The present invention is directed to a method of heat treating a polymer PTC composition to raise the peak resistivity of the material. By raising the peak resistivity of the material, an electrical circuit protection device employing the material will exhibit an increased resistance in the trip or fault state. Devices heat treated according to the present invention are especially well suited for high voltage applications.




In a first aspect of the present invention there is provided a method for heat treating a polymer PTC composition having a melting point temperature T


mp


. In the first step, the temperature of the polymer PTC composition is increased at a first rate, r1, to a temperature greater than T


mp


. The temperature of the polymer PTC composition is held at this elevated temperature (greater than T


mp


) for a predetermined period of time. The temperature of the polymer PTC composition is then decreased to a temperature less than T


mp


at a second rate, r


2


, wherein r


2


is greater than r


1


.




In a second aspect of the present invention there is provided a method for heat treating a polymer PTC composition having an initial peak resistivity, R


pi


, and a melting point temperature, T


mp


. The method comprises the steps of increasing the temperature of the polymer PTC composition at a first rate, r


1


, to a temperature greater than T


mp


. The temperature of the polymer PTC composition is held at this elevated temperature (greater than T


mp


) for a predetermined period of time. Next, the temperature of the polymer PTC composition is decreased to a temperature less than T


mp


at a second rate, r


2


, wherein r


2


is greater than r


1


. After decreasing the temperature of the polymer PTC composition, the composition has a new peak resistivity, R


pn


, which is at least 1.5×R


pi


.











BRIEF DESCRIPTION OF THE DRAWINGS




A better understanding of the present invention will be had upon reference to the following detailed description and accompanying drawings.





FIG. 1

is a graphical illustration of the peak resistance of an electrical device before and after a heat treatment according to the present invention.





FIG. 2

A is a graphical illustration of the resistivity of a polymer PTC composition as a function of temperature prior to a heat treatment according to the present invention.





FIG. 2B

is a graphical illustration of the resistivity of the polymer PTC composition graphically illustrated in

FIG. 2A

after a heat treatment according to the present invention.





FIG. 3A

is a graphical illustration of the resistivity of a polymer PTC composition as a function of temperature prior to a heat treatment according to the present invention.





FIG. 3B

is a graphical illustration of the resistivity of the polymer PTC composition graphically illustrated in

FIG. 3A

after a heat treatment according to the present invention.











DETAILED DESCRIPTION OF THE INVENTION




While this invention is susceptible of embodiment in many different forms, there is shown in the drawings and will herein be described in detail preferred embodiments of the invention with the understanding that the present disclosure is to be considered as an exemplification of the principles of the invention.




It is known that the higher resistance a PTC circuit protection device has in the tripped or fault state, the higher voltages the device can withstand. This can be shown utilizing Ohm's Law and the equation for power dissipation, P


d


.




Ohm's Law




R×I=V where R is the resistance of the device; I is the current flowing in the circuit; and V is the voltage of the power source.




Power Dissipation




The power dissipated in the device: P


d


=I×V where I is the current flowing through the device and V is the voltage of the power source.




For a specific electrical application the power dissipation of the device will be a constant, k. Thus, I=k/V. Substituting I=k/V into Ohm's Law yields R×k=V


2


. Accordingly, in the tripped state the higher the resistance of the device, the more voltage the device can withstand.




By changing the crystallinity of the polymer the morphology of a PTC composition changes. For example, by increasing the crystallinity, the morphology change increases the resistivity of the composition. It has been found that the morphology of a polymer PTC composition can be changed by slowly increasing the temperature of the composition above the melting point temperature T


mp


of the polymer. The temperature of the composition is then held at the increased temperature for a predetermined time, e.g., approximately 5 minutes, preferably 10-15 minutes, or even 20 minutes. Then the temperature of the composition is decreased, preferably back down to room temperature. The best results have been obtained when the temperature of the composition is decreased at a rate greater than the rate at which the temperature of the composition is increased.




In a preferred embodiment, the temperature of the composition is increased to approximately 5-10° C. above the melting point temperature of the polymer at a rate of approximately 0.5° C. per minute. The temperature remains at the elevated value for approximately 15 minutes. Then the temperature of the composition is decreased to room temperature at a rate at least twice the rate of the temperature increase, preferably at least four times the rate of the temperature increase, and more preferably at least eight times the rate of the temperature increase.




The method for heat treating of the present invention raises the peak resistivity of the polymer PTC composition, and thus the resistance of the electrical device in the tripped state. Accordingly, devices manufactured according to the present invention yield higher rated devices which can be used in higher voltage applications.




The heat treatment method of the present invention can be applied to polymer PTC compositions made according to any commonly known method, including those disclosed in U.S. Pat. No. 4,237,441, the disclosure of which is herein incorporated by reference. The heat treatment can also be applied to PTC compositions composed of different polymers, including co-polymers; e.g., polyolefins. Suitable polyolefins include: polyethylene, polyvinylidene fluoride, polypropylene, polybutadiene, polyethylene acrylates, ethyleneacrylic acid copolymers, ethylene/propylene copolymers, and modified polyolefins, i.e., a polyolefin having a carboxylic acid or a carboxylic acid derivative grafted thereto. Preferably the polymers of the compositions treated according to the present invention have a crystallinity of at least 20%, more preferably at least 50%, and especially at least 70%. It is important, however, that during the heat treatment the temperature of the polymer is raised above its melting point, thus altering the crystalline structure of the polymer and changing the morphology of the PTC composition.




Electrical circuit protection devices can be made according to any commonly known procedure; e.g., laminating metal foil electrodes to a PTC element as disclosed in U.S. Pat. Nos. 4,689,475 and 4,800,253, the disclosures of which are herein incorporated by reference. Examples of other circuit protection devices and methods for making them are disclosed in U.S. Pat. Nos. 5,814,264, 5,880,668, 5,884,391, 5,900,800, the disclosures of which are each incorporated herein by reference.




EXAMPLE 1




With reference to

FIG. 1

, the heat treatment method of the present invention was carried out on an electrical circuit protection device having a PTC element composed of a modified polyethylene (i.e., approximately 99% by weight polyethylene and 1% by weight maleic anhydride) and carbon black. Before the heat treatment the device had a peak resistance (i.e., the resistance of the device in the tripped state) of approximately 90 ohms. The device was treated by raising the temperature of the device by approximately 0.5° C. per minute to approximately 5-10° C. above the melting point temperature of the polymer PTC composition. The temperature was held at this point for approximately 15 minutes. Then the temperature was rapidly decreased at a rate of approximately 4.0° C. per minute to approximately room temperature. The peak resistance of the device was then measured and determined to be approximately 180 ohms.




EXAMPLE 2




Referring now to

FIGS. 2A and 2B

, the same heat treatment method as described above in Example 1 was carried out on a circuit protection device having a polymer PTC composition composed of polyvinylidene fluoride and carbon black. As disclosed in

FIG. 2A

, prior to the heat treatment the peak resistance of the device was approximately 700 ohm. As disclosed in

FIG. 2B

, after the heat treatment the peak resistance of the same device was approximately 1,000 ohm.




EXAMPLE 3




Referring now to

FIGS. 3A and 3B

, the same heat treatment method as described above in Example 1 was carried out on a polymer PTC composition composed of polyethylene and carbon black. As disclosed in

FIG. 3A

, prior to the heat treatment the peak resistivity of the composition was approximately 9×10


4


. As disclosed in

FIG. 3B

, after the heat treatment the peak resistivity of the composition was approximately 9×10


5


. The heat treated composition experienced a ten-fold increase in peak resistivity which makes the composition more suited for higher voltage applications than the non-treated composition.




It should be understood by those having ordinary skill in the art that the present method for heat treating may be incorporated into the process for making a circuit protection device at different steps; e.g., the heat treatment method may be carried out solely on the polymer PTC composition, or on a completed electrical circuit protection device. Since a completed device will not be exposed to additional thermal or mechanical energy which may alter the crystalline structure of the polymer and hence the electrical characteristics of the device, the method of the present is preferably applied to a completed device.



Claims
  • 1. A method for heat treating a polymer PTC composition, the method comprising the steps of:providing a polymer PTC composition having a melting point temperature Tmp; increasing the temperature of the polymer PTC composition at a first rate, r1, to a temperature greater than Tmp; holding the polymer PTC composition at the temperature greater than Tmp for a predetermined period of time; decreasing the temperature of the polymer PTC composition to a temperature less than Tmp at a second rate, r2, wherein r2 is greater than r1.
  • 2. The method of claim 1, wherein the temperature less than Tmp is room temperature.
  • 3. The method of claim 1, wherein the temperature greater than Tmp is at least 5-10° C. greater than Tmp.
  • 4. The method of claim 1, wherein r2 is at least two times greater than r1.
  • 5. The method of claim 1, wherein r2 is at least four times greater than r1.
  • 6. The method of claim 1, wherein r2 is at least eight times greater than r1.
  • 7. The method of claim 1, wherein the polymer PTC composition comprises a polyolefin having a crystallinity of at least 20%.
  • 8. The method of claim 7, wherein the polyolefin has a crystallinity of at least 50%.
  • 9. The method of claim 1, wherein the polymer PTC composition comprises polyethylene.
  • 10. The method of claim 1, wherein the polymer PTC composition comprises polyvinylidene fluoride.
  • 11. The method of claim 1, wherein the polymer PTC composition comprises a modified polyolefin.
  • 12. A method for heat treating a polymer PTC composition having an initial peak resistivity, Rpi, and a melting point temperature, Tmp, the method comprising the steps of:increasing the temperature of the polymer PTC composition at a first rate, r1, to a temperature greater than Tmp; holding the polymer PTC composition at the temperature greater than Tmp for a predetermined period of time; decreasing the temperature of the polymer PTC composition to a temperature less than Tmp at a second rate, r2, wherein r2 is greater than r1; and after decreasing the temperature of the polymer PTC composition, the composition has a new peak resistivity, Rpn, which is at least 1.5×Rpi.
  • 13. The method of claim 12, wherein Rpn is at least 2×Rpi.
  • 14. The method of claim 12, wherein Rpn is at least 10×Rpi.
  • 15. A method for heat treating an electrical circuit protection device having a PTC element and two electrodes, the PTC element being composed of a polymer PTC composition having a melting point temperature, Tmp, and an initial peak resistivity, Rpi, the method comprising the steps of:increasing the temperature of the polymer PTC composition at a first rate, r1, to a temperature greater than Tmp; holding the polymer PTC composition at the temperature greater than Tmp for a predetermined period of time; decreasing the temperature of the polymer PTC composition to a temperature less than Tmp at a second rate, r2, wherein r2 is greater than r1 such that the polymer PTC composition has a new peak resistivity, Rpn, which is at least 1.5×Rpi.
  • 16. The method of claim 15, wherein the predetermined period of time is in a range of approximately 10-15 minutes.
DESCRIPTION

This application claims benefit of Prov. No. 60/102,602 filed Oct. 1, 1998.

US Referenced Citations (118)
Number Name Date Kind
2978665 Vernet et al. Apr 1961 A
3241026 Andrich Mar 1966 A
3243753 Kohler Mar 1966 A
3351882 Kohler et al. Nov 1967 A
3591526 Kawashima et al. Jul 1971 A
3823217 Kampe Jul 1974 A
3828332 Rekai Aug 1974 A
3858144 Bedard et al. Dec 1974 A
4124747 Murer et al. Nov 1978 A
4169816 Tsien Oct 1979 A
4177376 Horsma et al. Dec 1979 A
4177446 Diaz Dec 1979 A
4188276 Lyons et al. Feb 1980 A
4223209 Diaz Sep 1980 A
4237441 van Konynenburg et al. Dec 1980 A
4238812 Middleman et al. Dec 1980 A
4259657 Ishikawa et al. Mar 1981 A
4272471 Walker Jun 1981 A
4304987 van Konynenburg Dec 1981 A
4318220 Diaz Mar 1982 A
4327351 Walker Apr 1982 A
4329726 Middleman et al. May 1982 A
4330703 Horsma et al. May 1982 A
4330704 Jensen May 1982 A
4367168 Kelly Jan 1983 A
4383942 Davenport May 1983 A
4388607 Toy et al. Jun 1983 A
4413301 Middleman et al. Nov 1983 A
4426546 Hotta et al. Jan 1984 A
4426633 Taylor Jan 1984 A
4445026 Walker Apr 1984 A
4475138 Middleman et al. Oct 1984 A
4534889 van Konynenburg et al. Aug 1985 A
4548740 von Tomkewitsch et al. Oct 1985 A
4560498 Horsma et al. Dec 1985 A
4617609 Utner et al. Oct 1986 A
4685025 Carlomagno Aug 1987 A
4689475 Kleiner et al. Aug 1987 A
4724417 Au et al. Feb 1988 A
4732701 Nishii et al. Mar 1988 A
4749623 Endo et al. Jun 1988 A
4774024 Deep et al. Sep 1988 A
4775778 van Konynenburg et al. Oct 1988 A
4800253 Kleiner et al. Jan 1989 A
4801785 Chan et al. Jan 1989 A
4857880 Au et al. Aug 1989 A
4876439 Negahori Oct 1989 A
4878038 Tsai Oct 1989 A
4880577 Okita et al. Nov 1989 A
4882466 Friel Nov 1989 A
4884163 Deep et al. Nov 1989 A
4907340 Fang et al. Mar 1990 A
4910389 Sherman et al. Mar 1990 A
4924074 Fang et al. May 1990 A
4951382 Jacobs et al. Aug 1990 A
4955267 Jacobs et al. Sep 1990 A
4959632 Uchida Sep 1990 A
4966729 Carmona et al. Oct 1990 A
4967176 Horsma et al. Oct 1990 A
4971726 Maeno et al. Nov 1990 A
4973934 Saito et al. Nov 1990 A
4980541 Shafe et al. Dec 1990 A
4983944 Uchida et al. Jan 1991 A
5068061 Knobel et al. Nov 1991 A
5089801 Chan et al. Feb 1992 A
5106538 Barma et al. Apr 1992 A
5106540 Barma et al. Apr 1992 A
5136365 Pennisi et al. Aug 1992 A
5140297 Jacobs et al. Aug 1992 A
5142263 Childers et al. Aug 1992 A
5143649 Blackledge et al. Sep 1992 A
5171774 Ueno et al. Dec 1992 A
5174924 Yamada et al. Dec 1992 A
5189092 Koslow Feb 1993 A
5190697 Ohkita et al. Mar 1993 A
5195013 Jacobs et al. Mar 1993 A
5212466 Yamada et al. May 1993 A
5214091 Tanaka et al. May 1993 A
5227946 Jacobs et al. Jul 1993 A
5231371 Kobayashi Jul 1993 A
5241741 Sugaya Sep 1993 A
5247276 Yamazaki Sep 1993 A
5247277 Fang et al. Sep 1993 A
5250226 Oswal et al. Oct 1993 A
5250228 Baigrie et al. Oct 1993 A
5257003 Mahoney Oct 1993 A
5268665 Iwao Dec 1993 A
5280263 Sugaya Jan 1994 A
5281845 Wang et al. Jan 1994 A
5289155 Okumura et al. Feb 1994 A
5303115 Nayar et al. Apr 1994 A
5313184 Greuter et al. May 1994 A
5337038 Taniguchi et al. Aug 1994 A
5351026 Kanbara et al. Sep 1994 A
5351390 Yamada et al. Oct 1994 A
5358793 Hanada et al. Oct 1994 A
5374379 Tsubokawa et al. Dec 1994 A
5382384 Baigrie et al. Jan 1995 A
5382938 Hansson et al. Jan 1995 A
5399295 Gamble et al. Mar 1995 A
5412865 Takaoka et al. May 1995 A
5488348 Asida et al. Jan 1996 A
5493266 Sasaki et al. Feb 1996 A
5500996 Fritsch et al. Mar 1996 A
5543705 Uezono et al. Aug 1996 A
5554679 Cheng Sep 1996 A
5610436 Sponaugle et al. Mar 1997 A
5747147 Wartenberg et al. May 1998 A
5777541 Vekeman Jul 1998 A
5801612 Chandler et al. Sep 1998 A
5814264 Cai et al. Sep 1998 A
5817423 Kajimaru et al. Oct 1998 A
5818676 Gronowicz, Jr. Oct 1998 A
5831510 Zhang et al. Nov 1998 A
5849129 Hogge et al. Dec 1998 A
5852397 Chan et al. Dec 1998 A
5864281 Zhang et al. Jan 1999 A
5874885 Chandler et al. Feb 1999 A
Foreign Referenced Citations (52)
Number Date Country
1254323 May 1989 CA
1253332 Apr 1965 DE
2626513 Dec 1977 DE
209311 Apr 1984 DE
0 169 059 Jan 1986 EP
0 229 286 Jul 1987 EP
0 460 790 Dec 1991 EP
0 588 136 Mar 1994 EP
0 731 475 Sep 1996 EP
0 790 625 Aug 1997 EP
0 827 160 Mar 1998 EP
0 901 133 Mar 1999 EP
541222 Nov 1941 GB
604695 Jul 1948 GB
1172718 Dec 1969 GB
1449261 Sep 1976 GB
1604735 Dec 1981 GB
50-33707 Dec 1972 JP
52-62680 May 1977 JP
53-104339 Aug 1978 JP
58-81264 May 1983 JP
58-81265 May 1983 JP
58-162877 Sep 1983 JP
58-162878 Sep 1983 JP
60-196901 Oct 1985 JP
62-79418 Apr 1987 JP
62-79419 Apr 1987 JP
62-181347 Aug 1987 JP
63-85864 Apr 1988 JP
63-146403 Jun 1988 JP
1-104334 Apr 1989 JP
2-109226 Apr 1990 JP
3-221613 Sep 1991 JP
3-271330 Dec 1991 JP
4-096202 Jul 1992 JP
5-109502 Apr 1993 JP
6-181102 Jun 1994 JP
6-124803 Aug 1994 JP
60-298148 Oct 1994 JP
7-094018 Apr 1995 JP
7-161503 Jun 1995 JP
9-199302 Jul 1997 JP
WO 9314511 Jul 1993 WO
WO 9401876 Jan 1994 WO
WO 9508176 Mar 1995 WO
WO 9531816 Nov 1995 WO
WO 9533276 Dec 1995 WO
WO 9534084 Dec 1995 WO
WO 9812715 Mar 1998 WO
WO 9829879 Jul 1998 WO
WO 9834084 Aug 1998 WO
WO 9903113 Jan 1999 WO
Non-Patent Literature Citations (26)
Entry
Yoshio Sorimachi, Ichiro Tsubata and Noboru Nishizawa, The Transactions of the Institute of Electronics and Communications Engineers of Japan—Analysis of Static Self Heating Characteristics of PTC Thermistor Based on Carbon Black Graft Polymer, vol. J61-C, No. 12, pp. 767-774 (Dec. 25, 1978).
Ichiro Tsubata and Yoshio Sorimachi, Faculty of Engineering, Niigata University—PTC Characteristics and Components on Carbon Black Graft Polymer, pp. 31-38 (with translation).
Yoshio Sorimachi and Ichiro Tsubata, The Transactions of the Institute of Electronics and Communication Engineers of Japan—Characteristics of PTC Thermistor Based on Carbon Black Graft Polymer, vol. J60-C, No. 2, pp. 90-97 (Feb. 25, 1977).
Yoshio Sorimachi and Ichiro Tsubata, Electronics Parts and Materials, Niigata University—The Analysis of Current Falling Characteristics on C.G. (Carbon Black Graft Polymer)—PTC Thermistor, Shingaku Gihou, vol. 9, pp. 23-27 ED-75-35, 75-62 (1975) (with Translation).
B. Wartgotz and W.M. Alvino, Polymer Engineering and Science—Conductive Polyethylene Resins from Ethylene Copolymers and Conductive Carbon Black, pp. 63-70 (Jan., 1967).
Kazuyuki Ohe and Yoshihide Naito, Japanese Journal of Applied Physics—A New Resistor Having an Anomalously Large Positive Temperature Coefficient, vol. 10, No. 1, pp. 99-108 (Jan., 1971).
Ichiro Tsubata and Naomitsu Takashina, 10th Regional Conference on Carbon—Thermistor with Positive Temperature Coefficient Based on Graft Carbon, pp. 235-236 (1971).
J. Meyer, Polymer Engineering and Science—Glass Transition Temperature as a Guide to Selection of Polymers Suitable for PTC Materials, vol. 13, No. 6, pp. 462-468 (Nov., 1973).
J. Meyer, Polymer Engineering and Science—Stability of Polymer Composites as Positive-Temperature-Coefficient Resistors, vol. 14, No. 10, pp. 706-716 (Oct., 1974).
Yoshio Sorimachi and Ichiro Tsubata, Shengakeekai Parts Material—Characteristics of PTC-Thermistor Based on Carbon Black Graft Polymer, vol. 9, Paper, No. UDC 621.316.825.2:678.744.32-13:661.666.4 (1974).
Carl Klason and Josef Kubat, Journal of Applied Polymer Science—Anomalous Behavior of Electrical Conductivity and Thermal Noise in Carbon Black-Containing Polymers at Tg and Tm', vol. 19, pp. 831-845 (1975).
M. Narkis, A. Ram and F. Flashner, Polymer Engineering and Science—Electrical Properties of Carbon Black Filled Polyethylene, vol. 18, No. 8 pp. 649-653 (Jun., 1978).
Andries Voet, Rubber Chemistry and Technology—Temperature Effect of Electrical Resistivity of Carbon Black Filled Polymers, vol. 54, pp. 42-50.
M. Narksi, A. Ram and Z. Stein, Journal of Applied Polymer Science—Effect of Crosslinking on Carbon Black/Polyethylene Switching Materials, vol. 25, pp. 1515-1518 (1980).
Frank A. Doljack, IEEE Transactions on Components Hybrids and Manufacturing—Technology, PolySwitch PTC Devices-A New Low-Resistance Conductive Polymer-Based PTC Device for Overcurrent Protection, vol. CHMT, No. 4, pp. 372-378 (Dec., 1981).
Keizo Miyasaka, et al., Journal of Materials Science—Electrical Conductivity of Carbon-Polymer Composites as Function of Carbon Content, vol. 17, pp. 1610-1616 (1982).
D.M. Bigg, Conductivity in Filled Thermoplastics—An Investigation of the Effect of Carbon Black Structure, Polymer Morphology, and Processing History on the Electrical Conductivity of Carbon-Black-Filled Thermoplastics, pp. 501-516.
J. Yacubowicz and M. Narkis, Polymer Engineering and Science—Dielectric Behavior of Carbon Black Filled Polymer Composites, vol. 26, No. 22, pp. 1568-1573 (Dec., 1986).
Mehrdad Ghofraniha and R. Salovey, Polymer Engineering and Science—Electrical Conductivity of Polymers Containing Carbon Black, vol. 28, No. 1, pp. 5863 (Mid-Jan., 1988).
J. Yacubowicz and M. Narkis, Polymer Engineering and Science—Electrical and Dielectric Properties of Segregated Carbon Black-Polyethylene Systems, vol. 30, No. 8, pp. 459-468 (Apr., 1990).
Biing-Lin Lee, Polymer Engineering and Science—Electrically Conductive Polymer Composites and Blends, vol. 32, No. 1, pp. 36-42 (Mid-Jan., 1992).
H.M. Al-Allak, A.W. Brinkman and J. Woods, Journal of Materials Science-I-V Characteristics of Carbon Black-Loaded Crystalline Polyethylene, vol. 28, pp. 117-120 (1993).
Hao Tang, et al., Journal of Applied Polymer Science—The Positive Temperature Coefficient Phenomenon of Vinyl Polymer/CB composites, vol. 48, pp. 1795-1800 (1993).
V.A. Ettel, P. Kalal, INCO Specialty Powder Products, Advances in Pasted Positive Electrode, (J. Roy Gordon Research Laboratory, Missisauga, Ont.), Presented at NiCad 94, Geneva, Switzerland, Sep. 19-23, 1994.
F. Gubbels, et al., Macromolecules—Design of Electrical Conductive Composites: Key Role of the Morphology on the Electrical Properties of Carbon Black Filled Polymer Blends, vol. 28 pp. 1559-1566 (1995).
Hao Tang, et al., Journal of Applied Polymer Science—Studies on the Electrical Conductivity of Carbon Black Filled Polymers, vol. 59, pp. 383-387 (1996).
Provisional Applications (1)
Number Date Country
60/102602 Oct 1998 US