Patent Application
20160104555
High voltage direct current (HVDC) cables are important components of HVDC grids and they account for more than one third of the system cost. Compared to alternating current (AC) cables, there are unique challenges that are specifically related to DC cables, such as nonlinear electric field distribution and the distortion/enhancement of electric fields due to space charge accumulation.
Currently, there are two types of HVDC cables commercially available. One type of cable employs a lapped insulation system, such as oil-paper insulation or mass impregnated paper insulation. These cables are proven to have very good reliability and can operate at very high voltage levels. However, they are expensive because of their complicated structure and they also raise environmental concerns. The other type of HVDC cable includes those with extruded polymer insulation. The state-of-the-art extruded insulation is a special grade of crosslinked polyethylene (XLPE) for HVDC applications, such as the “Superclean” XLPE. This material is different from the generic XLPE insulation used for AC cables. The HVDC XLPE materials are typically special grades of resin with very low amount of defects. The cable manufacture processes employed to make these cables are very tightly controlled to ensure a low defect rate.
In order to try to minimize space charge accumulation, additional prolonged heating steps, which limit throughput, are needed for the state-of-the-art extruded HVDC cables. All the foregoing considerations contribute to the high cost for the currently-available extruded HVDC cables.
Accordingly, a need exists for cables and methods that allow for improved electric field distribution, preferably at reduced costs over the presently-available cables and methods.
Briefly, the present invention satisfies the need for improved electrical field distribution in HVDC cables. For example, it has been found that, with the proper selection of resin chemistry, filler type, filler content, and optional surface modification of the filler, a resultant composition and method employing the same allow for suppressed space charge accumulation, and enable HVDC cable solutions with high reliability and low cost.
In one aspect, the invention provides a method for improving the electric field distribution in a high voltage direct current cable. The method includes providing a cable comprising a conductor, a protective jacket, a shield layer disposed inside the jacket, and an insulation layer disposed inside the shield layer, surrounding the conductor, said insulation layer comprising ethylene-propylene rubber, talc, and montmorillonite.
In another aspect, the invention provides a method of making a high voltage direct current cable. The method includes encasing a metal conductor within an insulation layer which, as described above, comprises ethylene-propylene rubber, talc, and montmorillonite.
In another aspect, the invention provides a HVDC cable.
In another aspect, the invention provides a grid system comprising the inventive HVDC cable.
The present invention will hereinafter be described in conjunction with the following drawing figures, which are not necessarily drawn to scale, and wherein like numerals denote like elements.
Aspects of the present invention and certain features, advantages, and details thereof, are explained more fully below with reference to the non-limiting embodiments illustrated in the accompanying drawings. Descriptions of well-known materials, fabrication tools, processing techniques, etc., are omitted so as to not unnecessarily obscure the invention in detail. It should be understood, however, that the detailed description and the specific examples, while indicating embodiments of the invention, are given by way of illustration only, and are not by way of limitation. Various substitutions, modifications, additions and/or arrangements within the spirit and/or scope of the underlying inventive concepts will be apparent to those skilled in the art from this disclosure.
The presently disclosed HVDC cables and methods address the problems of space charge accumulation, undesirable electric field enhancement in HVDC applications, and/or excessive costs associated with known HVDC cables and methods.
The invention addresses the problems in the art by introducing a new type of HVDC extruded cable insulation. Advantageous space charge performance is achieved by adding special fillers during the cable manufacturing processes, which specifically optimize DC cable performance while simultaneously avoiding the additional costs associated with XLPE DC cables due to, e.g., special resin grade, special manufacturing processes, and post-manufacturing treatments. Thus, the present invention offers novel DC cables and processes that improve performance and can significantly reduce the cost of HVDC systems, thereby helping to promote HVDC adoption, and to achieve higher grid efficiency and flexibility.
Unlike the state-of-the-art XLPE insulation which relies on resins with ultrahigh purity, embodiments of the presently disclosed methods, nanoclay-reinforced EPR cables are formed by intentionally adding fillers with the proper characteristics, which also advantageously provides for a much wider array of options when optimizing the properties of insulation.
In one aspect, the invention provides a method for improving the electric field distribution in a high voltage direct current cable. The method includes providing a cable comprising a conductor, a protective jacket, a shield layer disposed inside the jacket, and an insulation layer disposed inside the shield layer, surrounding the conductor, said insulation layer comprising ethylene-propylene rubber, talc, and montmorillonite. The invention also provides the described cable.
In some embodiments, any and/or all additives (e.g., rubber, talc, and/or montmorillonite) are homogenously dispersed within the ethylene-propylene rubber.
Persons having ordinary skill in the art are away of how to obtain ethylene propylene rubber. In some embodiments, ethylene-propylene (EP) base polymer is obtained by copolymerizing ethylene and propylene via the Ziegler-Natta process. The resulting blocky copolymer is termed ethylene-propylene rubber (EPR) due to its rubbery characteristics. A variation of EP includes a diene monomer, at the level of 3-7% by weight, forming a terpolymer labeled as ethylene-propylene-diene (EPDM). As used herein, the terms “ethylene-propylene rubber” (used interchangeably with “EPR”) is intended to encompass both EP and EPDM. In various embodiments, EPR comprises one or more additional components such as processing aids and ingredients to fulfill various functional and physical requirements. Table 1 provides a non-exhaustive list of commercially available EPRs that may be used in the present invention, together with a summary of their respective properties. In the table, ENB is Ethylidene Norbornene, a type of diene.
In some embodiments, the inventive method comprises transmitting high voltage direct current through the cable. The targeted voltage rating ranges from 10 kV to 600 kV. The service life is typically expected to be greater than 25 years. There are mainly two types of HVDC systems, namely, those with line commutated converters (LCC) and those with voltage sourced converters (VSC). In LCC systems, the polarity of voltage needs to be reversed if the direction of power flow needs to be changed. In VSC systems, the voltage is maintained at the same polarity. Correspondingly, the cable insulation in the LCC systems must be able to withstand the voltage polarity reversal, while those in the VSC systems do not necessarily need to satisfy this requirement. HVDC transmission is well within the knowledge of persons having ordinary skill in the art.
In some embodiments, the montmorillonite in the insulation layer comprises montmorillonite that has been modified with a quaternary ammonium compound. For example, in some embodiments, the montmorillonite comprises at least one of (i) montmorillonite modified with dimethyl, benzyl, hydrogenated tallow, quaternary ammonium (e.g., commercially available as Cloisite 10A, sold by BYK Additives & Instruments); and (ii) montmorillonite modified with dimethyl, dehydrogenated tallow, quaternary ammonium (e.g., commercially available as Cloisite 20A, sold by BYK Additives & Instruments).
Typical properties of Cloisite 10A and Cloisite 20A are as follows:
Cloisite 10A:
Typical properties:
Typical dry particle sizes: (microns, by volume)
Density:
Cloisite 20A:
Typical properties:
Typical dry particle sizes: (microns, by volume)
Density:
The montmorillonite (MMT) may be comprised within a wide variety of commercially available natural and organically modified clays. Commercially available organically modified clays are available from, e.g., BYK Additives & Instruments (Cloisite clays) and Nanocor (Nanomer clays). A listing of some non-exclusive available offerings, along with select clay properties provided by the manufacturer, are shown in Tables 2 and 3.
(Clay is also silane treated)
In some embodiments, the montmorillonite present in the insulation layer has an average particle size of 10 nm to 1 mm (for example, 10, 50, 100, 150, 200, 250, 300, 350, 400, 450, 500, 550, 600, 650, 700, 750, 800, 850, 900, 950, 1000, 1500, 2000, 2500, 3000, 3500, 4000, 4500, 5000, 5500, 6000, 6500, 7000, 7500, 8000, 8500, 9000, 9500, 10000, 10500, 11000, 11500, 12000, 12500, 13000, 13500, 14000, 14500, 15000, 15500, 16000, 16500, 17000, 17500, 18000, 18500, 19000, 19500, 20000, 30000, 40000, 50000, 60000, 70000, 80000, 90000, 100000, 200000, 300000, 400000, 500000, 600000, 700000, 800000, 900000, or 1000000 nm), including any and all ranges and subranges therein (e.g., 100 nm to 500 μm).
In some embodiments, the insulation layer comprises 0.05 phr to 30 phr (e.g., 0.05, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 12, 14, 16, 18, 20, 22, 24, 26, 28, or 30 phr) montmorillonite, including any and all ranges and subranges therein. “Phr” is a known unit, which stands for parts per hundred parts of resin (e.g., for each 100 phr of EPR base polymer, there may be, in some embodiments, 0.05 phr to 30 phr MMT). In certain embodiments, the insulation layer comprises 0.5 phr to 10 phr montmorillonite.
Talc is a mineral composed of hydrated magnesium silicate. In some embodiments, the talc present in the insulation layer has an average particle size of 10 nm to 1 mm (for example, 10, 50, 100, 150, 200, 250, 300, 350, 400, 450, 500, 550, 600, 650, 700, 750, 800, 850, 900, 950, 1000, 1500, 2000, 2500, 3000, 3500, 4000, 4500, 5000, 5500, 6000, 6500, 7000, 7500, 8000, 8500, 9000, 9500, 10000, 10500, 11000, 11500, 12000, 12500, 13000, 13500, 14000, 14500, 15000, 15500, 16000, 16500, 17000, 17500, 18000, 18500, 19000, 19500, 20000, 30000, 40000, 50000, 60000, 70000, 80000, 90000, 100000, 200000, 300000, 400000, 500000, 600000, 700000, 800000, 900000, or 1000000 nm), including any and all ranges and subranges therein (e.g., 100 nm to 500 μm).
In some embodiments, the insulation layer comprises 1 phr to 100 phr talc (e.g., 1, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, or 100 phr), including any and all ranges and subranges therein. In certain embodiments, the insulation layer comprises 10 phr to 60 phr talc.
In some embodiments, the insulation layer further comprises a vinyl silane. In non-limiting embodiments, the vinyl silane may be tris (2-methoxyethoxy)(vinyl)silane, dodecyltriethoxysilane, and/or doctadecyltriethoxysilane. In some embodiments, the insulation layer comprises 0 to 10 phr (e.g., 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10 phr) vinyl silane. In certain embodiments, the insulation layer comprises less than or equal to 2 phr vinyl silane. In some embodiments, a silane surface treatment has been applied to the talc in the insulation layer.
In some embodiments, the insulation layer further comprises kaolin (kaolinite aluminiumsilicate) (e.g., Burgess KE).
In some embodiments, the insulation layer further comprises a processing aid. In certain embodiments, the processing aid comprises low density polyethylene (LDPE) and wax. In some embodiments, the processing aid contains from 0 to 15 phr wax, and from 0 to 15 phr of LDPE (e.g., 0, 1, 2, 3, 4, or 5 phr), including any and all ranges and subranges therein.
In some embodiments, the insulation layer comprises one or more of the following additives: crosslinking agent, such as dicumyl peroxide (DCP), 0-5 phr; zinc oxide (0-10 phr); red lead, i.e., Pb304 (0-10 phr); antioxidant, such as the Agerite® Resin D® (Polymerized 1,2-dihydro-2,2,4-trimethylquinoline), 0-5 phr.
In some embodiments, the insulation layer has a field enhancement factor (FEF), which is a measure of space charge, calculated as follows:
of less than or equal to 0.2 (20%). For example, in some embodiments, the FEF is 0 to 0.5 (i.e., 0% to 50%), (e.g., 0, 0.01, 0.02, 0.03, 0.04, 0.05, 0.1, 0.15, 0.2, 0.25, 0.3, 0.35, 0.4, 0.45, or 0.5), including any and all ranges and subranges therein (e.g., 0.1 to 0.2).
In some embodiments, the insulation layer has a relax time of 0 to 600 seconds (for example, less than or equal to 600, 550, 500, 500, 450, 400, 350, 300, 250, 200, 150, 120, 110, 100, 90, 80, 70, 60, 50 seconds, etc.), including any and all ranges and subranges therein (e.g., 30 to 101 seconds).
In some embodiments, the insulation layer has a breakdown strength of greater than or equal to 160 kV/mm, and/or resistivity of greater than or equal to 10 TOhm-m (=1013 Ohm-m) at 50° C., and/or temperature coefficient of conductivity less than or equal to 0.15/° C.
In another aspect, the invention provides a method of making a high voltage direct current cable. The method includes encasing a metal conductor within an insulation layer which, as described above, comprises ethylene-propylene rubber, talc, and montmorillonite.
In another aspect, the invention provides a HVDC cable as described above.
In another aspect, the invention provides a grid system comprising the inventive HVDC cable.
The invention will now be further illustrated, but not limited, by the following examples.
EPR Compositions & Properties
Various EPR insulation layer compositions, both in accordance with embodiments of the invention and not (e.g., not comprising both MMT and talc), were prepared and tested. The compositions and their respective properties are summarized in Table 4 below. In the table, MMT refers to montmorillonite; VS refers to vinyl silane (specifically, tris(2-methoxy ethoxy)); Wax refers to a paraffin wax (having a solidification point of 58-60° C.); LDPE refers to low density polyethylene (LDPE); FEF refers to Field Enhancement Factor; Relax Time refers to space charge relaxation time; In general, the electrical conductivity of the insulation layer can be expressed as a function of temperature (T) and electric field (E): σ(T, E)=σ0 exp(αT+βE), and Temp. Coefficient refers to the temperature coefficient (α) of conductivity, where (β) is the field coefficient of conductivity, and (τ) is the space charge relaxation time constant (i.e., time constant for the exponential decay of space charge after voltage is turned off), as in the formula
where ρ(t) is the space charge density at time t, with t=0 corresponding to the moment when the voltage is turned off, and t=∞ corresponding to very long time (e.g., t>>100 τ).
Comparative Space Charge Accumulation Testing.
Thin samples of both EPR and “Superclean” XLPE (state-of-the-art DC insulation resin) were subjected to high field (100 kV/mm). The results are shown in
Comparative Electric Field Distribution Testing.
Electric field enhancement measurements were performed under typical operating electric fields (20 kV/mm) for 12 hours on ˜1 mm thick melt-processed samples without any additional treatments. The tests were conducted at room temperature. Compared to the test performed at 100 kV/mm, which aims at probing the intrinsic space charge dynamic under very high fields, the 20kV/mm electric field is close to the real operation field in HVDC cables.
Additional Comparative Testing.
Additional comparative testing was done to compare Example A, an EPR formulation used in an insulation layer embodiment of the present invention (which includes MMT and Talc), with Example B, a formulation outside of the present invention. The formulations of Examples A and B are presented in Table 5, below.
Properties of Examples A and B were determined, and are reproduced in Table 6 below. Aging test standards ANSI S-94-649 (oxidation stability for cable rubber) and ASTM D573 (accelerated oven aging of rubber in air) were used.
As shown in the space charge row above, the difference between Example A and Example B is that for Example A, the addition of MMT reduces the relaxation time constant. The importance of this is that for the HVDC systems with line-commutated converters (LCC systems), the polarity of the voltage is reversed back and force, and the transition time from one polarity to the other is typically several minutes. If the relaxation time is faster than this transition time, then the space charge can follow the change of voltage and hence minimize the electric field enhancement during the voltage polarity reversal process.
Comparative space charge performance testing was conducted for Examples A and B above, as well as for a comparative unfilled EPR (lacking MMT and talc) and a state-of-the-art extruded DC cable insulation (Superclean DC XLPE Insulation) using pulsed electroacoustic method; applied field: 17 kV/mm; sample thickness: 1.6 mm sample; temperature: 60° C.; thermal gradient across sample: 2° C./mm). Results are summarized in Table 7 below. This test condition represents the typical operating condition in a cable in terms of electric field level and temperature gradient.
As shown above, for the state-of-the-art XLPE and the unfilled EPR, the FEF is high. Inventive Example A advantageously had considerably decreased relaxation time as compared to comparative Example B.
While additional thermal treatment could reduce the field enhancement factor of the Superclean DC XLPE, if this were to be implemented on cables, it would take several weeks to finish the degassing. On the other hand, the data above were measured on samples without any degassing. The polymer pellets were pressed at 160 deg C. for 15 min, and then taken out, and then measured without any additional thermal treatment. A benefit of the present invention is that the low field enhancement factors can be achieved in the absence of any degassing. Furthermore, it has advantageously been found that the addition of MMT significantly shortens the relaxation time.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used herein, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprise” (and any form of comprise, such as “comprises” and “comprising”), “have” (and any form of have, such as “has” and “having”), “include” (and any form of include, such as “includes” and “including”), “contain” (and any form contain, such as “contains” and “containing”), and any other grammatical variant thereof, are open-ended linking verbs. As a result, a method or device that “comprises”, “has”, “includes” or “contains” one or more steps or elements possesses those one or more steps or elements, but is not limited to possessing only those one or more steps or elements. Likewise, a step of a method or an element of a device that “comprises”, “has”, “includes” or “contains” one or more features possesses those one or more features, but is not limited to possessing only those one or more features.
As used herein, the terms “comprising,” “has,” “including,” “containing,” and other grammatical variants thereof encompass the terms “consisting of” and “consisting essentially of.”
The phrase “consisting essentially of” or grammatical variants thereof when used herein are to be taken as specifying the stated features, integers, steps or components but do not preclude the addition of one or more additional features, integers, steps, components or groups thereof but only if the additional features, integers, steps, components or groups thereof do not materially alter the basic and novel characteristics of the claimed composition, device or method.
All publications cited in this specification are herein incorporated by reference as if each individual publication were specifically and individually indicated to be incorporated by reference herein as though fully set forth.
Subject matter incorporated by reference is not considered to be an alternative to any claim limitations, unless otherwise explicitly indicated.
Where one or more ranges are referred to throughout this specification, each range is intended to be a shorthand format for presenting information, where the range is understood to encompass each discrete point within the range as if the same were fully set forth herein.
While several aspects and embodiments of the present invention have been described and depicted herein, alternative aspects and embodiments may be affected by those skilled in the art to accomplish the same objectives. Accordingly, this disclosure and the appended claims are intended to cover all such further and alternative aspects and embodiments as fall within the true spirit and scope of the invention.
This invention was made with government support under contract number DE-AR0000231 awarded by the U.S. Department of Energy. The government has certain rights in the invention.