Abstract
This invention relates to a method of improving the corrosion and wear resistance of a transport trailer surface. More specifically the present invention relates to a method of laser alloying the surface of a transport trailer to enhance the corrosion and wear resistant properties of the surface.
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




This invention relates to a method of improving the corrosion and wear resistance of a transport trailer surface. More specifically the present invention relates to a method of laser alloying the surface of a transport trailer to enhance the corrosion and wear resistant properties of the surface.




2. Description of the Prior Art




Transport trailer surfaces are used to transport materials that are abrasive and/or corrosive. In many applications materials having abrasive properties, such as gravel or larger rocks, are dumped into, or slid off of, transport trailer surfaces resulting in surface wear and abrasion. Prior art transport trailer surfaces often have short lives as a result of the abrasive and corrosive forces to which they are exposed.




SUMMARY OF THE INVENTION




The present invention is directed toward a method or process for improving the corrosion and wear resistance of a material transport trailer surface. The present invention comprises applying a precursor layer comprising metallic or ceramic powders to a material transport trailer surface. The precursor layer has a thickness in the range of 50-150 microns.




The present invention further comprises irradiating the surface of the trailer with a laser at a sufficient energy level and for a sufficient time to melt a portion of the surface while the surface is moving relative to the laser beam.











DESCRIPTION OF THE FIGURES





FIG. 1A

is a block diagram depicting a first method of the present invention.





FIG. 1B

is a block diagram depicting a second method of the present invention.





FIG. 1C

is a block diagram depicting a third method of the present invention.





FIG. 2

is a top view of a transport trailer surface being processed by a method of the present invention.





FIG. 3

is an enlarged top view of the laser beam cross sectional area on the transport trailer surface when practicing the method of the present invention.











DESCRIPTION OF THE PREFERRED EMBODIMENTS




The present invention comprises applying a precursor layer comprising metallic or ceramic powders to a material transport trailer surface, as shown in Block


10


of FIG.


1


A and in FIG.


2


. The precursor layer has a thickness in the range of 50-150 microns.




In one embodiment of the present invention, wherein the trailer surface comprises an aluminum alloy, the powder within the precursor, comprises tungsten or silicon carbide, as shown in Block


11


of FIG.


1


B. In another preferred embodiment, wherein the trailer surface comprises steel, the powder within the precursor, comprises chromium and nickel, as shown in Block


13


of FIG.


1


C.




The present invention further comprises irradiating the surface of a trailer


20


with a laser beam


22


at a sufficient energy level and for a sufficient time to melt the portion of the trailer surface while the surface is moving relative to the laser beam, as shown in Block


12


of FIG.


1


A. In a preferred embodiment wherein the trailer surface comprises an aluminum alloy, the irradiating uses a laser having a power density in the range of 115-135 kilowatts/cm


2


as shown in Block


15


of FIG.


1


B. In another preferred embodiment, the irradiating is performed at a power density of 125 kilowatts/cm


2


.




In another preferred embodiment, the surface and the laser beam are moved relative to each other at a translation rate in the range of 2,500-9,000 millimeters per minute as shown in Block


15


of FIG.


1


B. Such relative movement may be accomplished by moving the laser beam relative to a stationary surface, moving the surface relative to a stationary laser beam, or moving both the surface and the laser beam at different speeds and/or in different directions.




In one preferred embodiment, the irradiating is performed with a laser beam


22


having a rectangular cross sectional area, as shown in FIG.


3


. In another preferred embodiment, the longer sides


24


of said rectangular cross sectional area are perpendicular to the translation axis


30


of the laser beam relative to the surface, as shown in

FIGS. 2 and 3

.




In another preferred embodiment, the longer sides of the rectangular cross sectional area


24


of the laser beam have a length of at least 2.8 millimeters. In another preferred embodiment, the shorter sides


26


of the rectangular cross sectional area of the laser beam have a length of at least 0.4 millimeters. A rectangular beam profile having the dimensions described above can be achieved by aligning a spherical lens closest to the beam, a second cylindrical lens closest to the substrate and a first cylindrical lens between the spherical lens and the second cylindrical lens. The spherical lens should have a focal length of 152.4 millimeters. The first cylindrical lens should have a focal length of 203.2 millimeters. The second cylindrical lens should have a focal length of 152.4 millimeters. The spherical lens and the first cylindrical lens should be spaced apart by five millimeters. The first cylindrical lens and second cylindrical lens should be spaced apart by 25 millimeters.




In a preferred embodiment, the laser beam is moved along a linear path or track


32


relative to the surface, as shown in FIG.


2


. In a preferred embodiment, the track index, x, is less than or equal to the width of the laser beam, as shown in FIG.


2


. The term “track index”, as used herein, refers to the distance between center lines of adjacent tracks.




In another preferred embodiment, the method of the present invention further comprises repeating the irradiating along at least one track


34


adjacent and parallel to the most recently irradiated track, as shown in Block


16


of FIG.


1


A and in FIG.


2


. In another preferred embodiment, the irradiating uses at least two laser beams simultaneously, as shown in FIG.


2


.




In a preferred embodiment, the present invention comprises directing a shielding gas at the region of the surface being irradiated, as shown in Block


14


of

FIG. 1A

In a preferred embodiment, the shielding gas is nitrogen as shown in Block


21


of

FIG. 1C

, or argon as shown in Block


19


of FIG.


1


B.




The foregoing disclosure and description of the invention are illustrative and explanatory. Various changes in the size, shape, and materials, as well as in the details of the illustrative construction may be made without departing from the spirit of the invention.



Claims
  • 1. A method for laser alloying a metallic material transport trailer surface comprising:a. applying a precursor layer comprising metallic or ceramic powders to said material transport trailer surface, said precursor layer having a thickness in a range of 50-150 microns; and b. irradiating said surface with a laser beam having a rectangular cross sectional area at a sufficient energy level and for a sufficient time to melt a portion of said surface while said surface and said laser beam are moved relative to each other along a linear tract at a translation rate in the range of 2,500-9,000 millimeters per minute and wherein said laser beam has a width.
  • 2. The method of claim 1, wherein said surface comprises aluminum and said irradiating uses a laser having a power density of in a range of 115-135 kilowatts/cm2.
  • 3. The method of claim 1, wherein said rectangular cross sectional area comprises two opposing longer sides that are perpendicular to the translation axis of said laser beam relative to said surface.
  • 4. The method of claim 3, wherein said longer sides of said rectangular cross sectional area have a length of at least 2.8 millimeters.
  • 5. The method of claim 4, wherein said shorter sides of said rectangular cross sectional area have a length of at least 0.4 millimeters.
  • 6. The method of claim 1, wherein said laser beam is moved along a linear path relative to said surface.
  • 7. The method of claim 1, wherein said irradiating uses at least two laser beams simultaneously.
  • 8. The method of claim 1, further comprising directing a shielding gas at said surface while it is being irradiated.
  • 9. A method for a metallic material transport trailer surface comprising:a. applying a precursor layer comprising metallic or ceramic powders to said material transport trailer surface, said precursor layer having a thickness in a range of 50-150 microns; b. irradiating said surface with a laser beam having a rectangular cross sectional area at a sufficient energy level and for a sufficient time to melt a portion of said surface while said surface and said laser beam are moved relative to each other along a linear tract at a translation rate in the range of 2,500-9,000 millimeters per minute; and c. directing a shielding gas at said surface while it is being irradiated.
  • 10. The method of claim 9, wherein said rectangular cross sectional area comprises two longer sides, each of said longer sides having a length of at least 2.8 millimeters and two shorter sides, each of said shorter sides having a length of at least 0.4 millimeters.
  • 11. The method of claim 9, wherein said trailer surface comprises an aluminum alloy and said powder comprises tungsten, silicon carbide or tungsten carbide.
  • 12. The method of claim 9, wherein said trailer surface comprises steel and said powder comprises chromium and nickel.
US Referenced Citations (77)
Number Name Date Kind
3705758 Haskal Dec 1972
3848104 Locke Nov 1974
3986767 Rexer et al. Oct 1976
4015100 Gnanamuthu et al. Mar 1977
4017708 Engel et al. Apr 1977
4157923 Yen et al. Jun 1979
4212900 Serlin Jul 1980
4218494 Belmondo et al. Aug 1980
4322601 Serlin Mar 1982
4401726 Gnanamuthu Aug 1983
4434189 Zaplatynsky Feb 1984
4475027 Pressley Oct 1984
4480169 Macken Oct 1984
4495255 Draper et al. Jan 1985
4535218 Krause et al. Aug 1985
4615903 Miller Oct 1986
4617070 Amende et al. Oct 1986
4638163 Braunlich et al. Jan 1987
4644127 La Rocca Feb 1987
4720312 Fukuizumi et al. Jan 1988
4724299 Hammeke Feb 1988
4732778 Kawasaki Mar 1988
4739093 Mehta et al. Apr 1988
4746540 Kawasaki et al. May 1988
4750947 Yoshiwara et al. Jun 1988
4801352 Piwczyk Jan 1989
4832982 Mori et al. May 1989
4839518 Braunlich et al. Jun 1989
4847112 Halleux Jul 1989
4898650 Wu et al. Feb 1990
4904498 Wu Feb 1990
4964967 Hashimoto et al. Oct 1990
4981716 Sundstrom Jan 1991
4998005 Rathi et al. Mar 1991
5059013 Jain Oct 1991
5095386 Scheibengraber Mar 1992
5124993 Braunlich et al. Jun 1992
5130172 Hicks et al. Jul 1992
5147999 Dekumbis et al. Sep 1992
5182430 Lagain Jan 1993
5196672 Matsuyama et al. Mar 1993
5208431 Uchiyama et al. May 1993
5230755 Pierantoni et al. Jul 1993
5247155 Steen et al. Sep 1993
5257274 Barrett et al. Oct 1993
5265114 Sun et al. Nov 1993
5267013 Spence Nov 1993
5290368 Gavigan et al. Mar 1994
5308431 Maher et al. May 1994
5314003 Mackay May 1994
5319195 Jones et al. Jun 1994
5322436 Horng et al. Jun 1994
5331466 Van Saarloos Jul 1994
5352538 Takeda et al. Oct 1994
5387292 Morishige et al. Feb 1995
5406042 Engelfriet et al. Apr 1995
5409741 Laude Apr 1995
5411770 Tsai et al. May 1995
5430270 Findlan et al. Jul 1995
5446258 Mordike Aug 1995
5449536 Funkhouser et al. Sep 1995
5466906 McCune, Jr. et al. Nov 1995
5484980 Pratt et al. Jan 1996
5486677 Maischner et al. Jan 1996
5491317 Pirl Feb 1996
5496593 Tsai et al. Mar 1996
5514849 Findlan et al. May 1996
5530221 Benda et al. Jun 1996
5546214 Black et al. Aug 1996
5563095 Frey Oct 1996
5614114 Owen Mar 1997
5643641 Turchan et al. Jul 1997
5659479 Duley et al. Aug 1997
5759641 Dimitrienko et al. Jun 1998
5874011 Ehrlich Feb 1999
5912057 Nishimura et al. Jun 1999
5952057 Parks Sep 1999
Foreign Referenced Citations (8)
Number Date Country
876870A1 Apr 1998 EP
63-278692 Nov 1988 JP
381082 Apr 1991 JP
5285686 Nov 1993 JP
1557193 Apr 1990 SU
1743770 Jun 1992 SU
WO 9521720 Aug 1995 WO
WO 9747397 Dec 1997 WO
Non-Patent Literature Citations (50)
Entry
Derwent Abstract of DE 4126351A to Fraunhofer Ges Foerderung, Feb. 1993.*
Abstract (source unknown) of JP401083676A “Wear Resistant AI Alloymenker” to Kanazawa et al, Mar. 29, 1989.*
Abstract (source unidentified) of JP403115531A “Production of Remelted Camshaft” to Yamamoto et al, May 16, 1991.*
Abstract (source unidentified) of JP 40311587A “Production of Remelted Cam Shaft” to Ouchi et al, May 16, 1991.*
ASM Handbook, vol. 6, Welding, Brazing and Soldering, 1993 no month.
Ayers, et al.; “A Laser Processing Technique for Improving the Wear Resistance of Metals,” Journal of Metals, Aug. 1981, 19-23.
Belvaux, et al.; “A Method for Obtaining a Uniform Non-Gaussian Laser Illumination,” Optics Communications, vol. 15, No. 2, Oct. 1975, 193-195.
Bett, et al.; “Binary phase zone-plate arrays for laser-beam spatial-intensity distribution conversion,” Applied Optics, vol. 34, No. 20, Jul. 10, 1995, 4025-4036.
Bewsher, et al.; “Design of single-element laser-beam shape projectors,” Applied Optics, vol. 35, No. 10, Apr. 1, 1996, 1654-1658.
Breinan, et al.; “Processing material with lasers,” Physics Today, Nov. 1976, 44-50.
Bruno, et al.; “Laserbeam Shaping for Maximum Uniformity and Maximum Loss, A Novel Mirror Arrangement Folds the Lobes of a Multimode Laserbeam Back onto its Center,” Lasers & Applications, Apr. 1987, 91-94.
Chen, et al.; “The Use of a Kaleidoscope to Obtain Uniform Flux Over a Large Area in a Solar or Arc Imaging Furnace,” Applied Optics, vol. 2, No. 3, Mar. 1963, 265-571.
Christodoulou, et al.; “Laser surface melting of some alloy steels,” Metals Technology, Jun. 1983, vol. 10, 215-222.
Cullis, et al.; “A device for laser beam diffusion and homogenisation,” J. Phys.E:Sci. Instrum., vol. 12, 1979, 668-689 no month top of p. 689 illegible.
Dahotre, et al., “Development of microstructure in laser surface alloying of steel with chromium,” Journal of Materials Science, vol. 25, 1990, 445-454 no month.
Dahotre, et al., “Laser Surface Melting and Alloying of Steel with Chromium,” Laser Material Processing III, 1989, 3-19 no month.
Fernelius, et al.; “Design and Testing of a Refractive Laser Beam Homogenizer,” Airforce Writing Aeronautical Laboratories Report, (AFWAL-TR-84-4042), Sep. 1984, 46 pages.
Galletti, et al.; “Transverse-mode selection in apertured super-Gaussian resonators: an experimental and numerical investigation for a pulsed CO2 Doppler lidar transmitter,” Applied Optics, vol. 36, No. 6, Feb. 20, 1997, 1269-1277.
Gori, et al.; “Shape-invariance range of a light beam,” Optics Letters, vol. 21, No. 16, Aug. 15, 1996, 1205-1207.
Grojean, et al.; “Production of flat top beam profiles for high energy lasers,” Rev. Sci. Instrum. 51(3), Mar. 1980, 375-376.
Hella, “Material Processing with High Power Lasers,” Optical Engineering, vol. 17, No. 3, May-Jun. 1978, 198-201.
Ignatiev, et al.; “Real-time pyrometry in laser machining,” Measurement and Science Technology, vol. 5, No. 5, 563-573 1994—no month 1st column, ever other page partly illegable.
“Laser Removing of Lead-Based Paint” Illinois Department of Transportation, Jun. 1992, 26 pages J. Janssen.
Jones et al.; “Laser-beam analysis pinpoints critical parameters,” Laser Focus World, Jan. 1993, 123-130.
Khanna, et al.; “The Effect of Stainless Steel Plasma Coating and Laser Treatment on the Oxidation Resistance of Mild Steel,” Corrosion Science, vol. 33, No. 6, 1992, 949-958 no month.
Lugscheider, et al.; “A Comparison of the Properties of Coatings Produced by Laser Cladding and Conventional Methods,” Surface Modification Technologies V, The Institute of Materials, 1992, 383-400 no month.
Manna, et al.; “The One-dimensional Heat Transfer Model for Laser Surface Alloying of Chromium on Copper Substrate,” Department of Metallurgical & Materials Engineering, Indian Institute of Technology, vol. 86, N. 5, May 1995, 362-364.
Mazille, et al.; “Surface Alloying of Mild Steel by Laser Melting of Nickel and Nickel/Chromium Precoatings,” Materials Performance Maintenance, Aug. 1991, 71-83.
Molian; “Characterization of Fusion Zone Defects in Laser Surface Alloying Applications,” Scripta Metallurgica, vol. 17, 1983, 1311-1314 no month.
Molian; “Effect of Fusion Zone Shape on the Composition Uniformity of Laser Surface Alloyed Iron,” Scripta Metallurgica, vol. 16, 1982, 65-68 no month.
Molian; Structure and hardness of laser-processed Fe-O.2%C-5%Cr and Fe-0.2%C-10%Cr alloys; Journal of Materials Science, vol. 20, 1985, 2903-2912 no month.
“Line-Focussing Optics for Multiple-Pass Laser Welding,” NASA Tech Briefs MFS-29976, date unknown.
“Cylindrical Lenses,” Newport Technical Guide,, date unknown, N-68.
“Fused Silica Cylindrical Lenses,” Newport Technical Guide,, date unknown, N-68.
Oswald, et al.; “Measurement and modeling of primary beam shape in an ion microprobe mass analyser,” IOP Publishing Ltd., 1990, 255-259 no month.
Renaud, et al., “Surface Alloying of Mild Steel by Laser Melting of an Electroless Nickel Deposit Containing Chromium Carbides,” Materials & Manufacturing Processes, 6(2), 1991 no month, but is a reprint from a Nov. 1990 publication 315-330.
Smurov, et al.; “Peculiarities of pulse laser alloying: Influence of a spatial distribution of the beam,” J. Appl. Phys. 71(7), Apr. 1, 1992, 3147-3158.
“Spawr Integrator,” Spawr Optical Research, Inc., Data Sheet No. 512, Jun. 1986.
Veldkamp, et al.; “Beam profile shaping for laser radars that use detector arrays,” Applied Optics, vol. 21, No. 2, Jan. 15, 1982, 345-358.
Veldkamp; “Laser Beam Profile Shaping with Binary Diffraction Gratings,” Optics communications, vol. 38, No. 5,6, Sep. 1, 1981, 381-386.
Veldkamp; barely readable “Laser beam profile shpaing with interlaced binary diffraction gratings,” Applied Optics, vol. 21, No. 17, Sep. 1, 1982, 3209-3212.
Veldkamp; “Technique for generating focal-plane flattop laser-beam profiles,” Rev. Sci. Instru., vol. 53, No. 3, Mar. 1982, 294-297.
Walker, et al.; “Laser surface alloying of iron and 1C-1•4Cr steel with carbon,” Metals Technology, vol. 11, Sep. 1984, 5 pages.
Walker, et al.; “The laser surface-alloying of iron with carbon,” Journal of Material Science vol. 20, 1985, 989-995 no month.
Wei, et al.; “Investigation of High-Intensity Beam Characteristics on Welding Cavity Shape and Temperature Distribution,” Journal of Heat Transfer, vol. 112, Feb. 1990, 163-169.
Charschan, “Lasers in industry,” Laser Processing Fundamentals, (Van Nostrand Reinhold Company), Chapter 3, Sec. 3-1, 139-145. No date given, but predates 11/79.
Fernelius, et al; “Calculations Used in the Design of a Refractive Laser Beam Homogenizer,” Airforce Writing Aeronautical Laboratories Report, (AFWAL-TR-84-4047), Aug. 1984, 18 pages (11 pages & i-Vii +cover sheet).
Jain, et al.; “Laser Induced Surface Alloy Formation and Diffusion of Antimony in Aluminum,” Nuclear Instruments and Method, vol. 168, 275-282, 1980 no month.
Molian; “Estimation of cooling rates in laser surface alloying processes,” Journal of Materials Science Letters, vol. 4, 1985, 265-267 no month.
“High Power CW Nd:YAG Laser Transformation Hardening,” Hobart Laser Products, 2 pages no date or author.