Method for increasing wear resistance in an engine cylinder bore and improved automotive engine

Information

  • Patent Grant
  • 6328026
  • Patent Number
    6,328,026
  • Date Filed
    Wednesday, October 13, 1999
    25 years ago
  • Date Issued
    Tuesday, December 11, 2001
    23 years ago
Abstract
This invention is directed to a method for enhancing the wear resistance of an iron engine cylinder bore comprising laser alloying of the cylinder bore with selected precursors and honing the cylinder bore to a preselected dimension. The present invention is particularly well suited for enhancing the resistance to wear caused by the corrosion caused by automotive ethanol fuel. The present invention is also directed toward an improved automotive engine comprising alloyed cylinder bores with enhanced wear resistance characteristics.
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




This invention is directed to a method for enhancing the wear resistance of a cast iron engine cylinder bore comprising laser alloying of the cylinder bore with selected precursors and honing the cylinder bore to a preselected dimension. The present invention is particularly well suited for enhancing the resistance to wear caused by the corrosion caused by automotive ethanol fuel. The present invention is also directed toward an improved automotive engine comprising alloyed cylinder bores with enhanced corrosive wear resistance characteristics.




2. Description of the Prior Art




For many decades gasoline has been the primary fuel for internal combustion engines used in automobiles and related motor vehicles. Recent concerns about fuel economy and the adverse impact of automotive emissions on air quality have resulted in increased research and development activity in the use of alcohol blended fuels to power internal combustion engines. An example of such fuels is a blend of 85% ethanol and 15% gasoline, known as “E85” automotive fuel.




Automobile manufacturers have developed and tested E85 fueled engines. Engines which have cast iron cylinder bores, and which have been operated with E85 fuel may experience excessive bore wear resulting from the corrosive effects of E85 fuel. This wear problem is particularly acute in North American countries because of the advanced fuel injection technologies used in these countries.




SUMMARY OF THE INVENTION




The present invention is directed toward a method for enhancing the corrosive wear resistance of a cast iron engine cylinder bore used with ethanol-based fuels. The method of the present invention comprises coating the interior surface of the cylinder bore with a precursor comprising alloying elements that will result in enhanced wear characteristics when alloyed with the surface of the cylinder bore, and irradiating a portion of the interior surface of the cylinder bore with a laser at a sufficient energy level and for a sufficient time to melt the precursor and a portion of the cylinder bore substrate and to cause mixing of the melted materials so that the precursor comprising alloying elements is distributed into the interior surface of the bore and alloys with the iron thereat to form an alloyed iron surface layer. Preferred alloying elements which produce enhanced wear characteristics include Ti, Zr Ni—Ti composites and Ni—Zr composites. After irradiating, the present invention comprises honing the interior surface of the cylinder bore to a preselected dimension that leaves the alloyed iron exposed. This treatment not only reduces the wear rate, but results in more consistent and uniform wear.




The present invention is also directed toward an internal combustion engine comprising at least one cast iron cylinder bore, which has an interior surface comprising an alloyed layer integrally formed with the substrate of the bore. These alloyed layers comprise one or more alloying elements which enhance the corrosive wear resistance of said bore, and are preferably selected from the group consisting of titanium, zirconium, nickel-titanium composites, and nickel-zirconium composites.











DESCRIPTION OF THE FIGURES





FIG. 1

is a block diagram of a first method embodiment of the present invention.





FIGS. 2A-2C

are isometric views of a cylinder bore being processed by the method of the present invention.





FIG. 3

is a block diagram of a second method embodiment of the present invention.





FIG. 4

is a side view of a first laser beam delivery system suitable for use in practicing the present invention.





FIG. 5

is an interior view of the cylinder bore during the irradiating step of the present invention.





FIG. 6

is a front view of the laser beam on the interior of the cylinder bore.





FIG. 7

is an isometric view of an engine of the present invention.





FIG. 8

is a side view of a second laser beam delivery system suitable for use in practicing the present invention.











DESCRIPTION OF THE PREFERRED EMBODIMENTS




The present invention is directed toward a method for enhancing the corrosive wear resistance of a cast iron engine cylinder bore used with ethanol-based fuel. The cylinder bore may be formed in a cast iron engine block, or a cast iron insert in an aluminum engine block. The method of the present invention comprises applying a precursor


40


comprising alloying elements to the interior surface of the cylinder bore


42


, (as shown in block


10


of FIG.


1


and in

FIG. 2A

) so as to provide a coating


34


(see

FIG. 4

) of alloying elements on the interior surface of the bore. The precursor may comprise a water-based mixing agent containing a suitable binder, such for adhering the alloyed elements to the bore surface.




In a preferred embodiment, the binder will be thixotropic. A binder comprising modified hydrous silicate will be thixotropic.




In another preferred embodiment, the binder will possess a low surface tension. A binder comprising acetylenic diol will possess a low surface tension.




In another preferred embodiment, the binder will comprise a bacteriocide, such as triaza-azoniatricyclodecane chloride.




In another preferred embodiment, the binder has low foaming or antifoaming properties. A binder comprising a silicone emulsion defoamer will possess antifoaming properties. Suitable binders include LISI


SM


100 and LISI


SM


101, available from Warren Paint and Color Company of Nashville, Tenn., and A-10-Braz Cement, available from Vitta, Inc. of Bethel, Conn.




In a preferred embodiment, the precursor comprises titanium powder, zirconium powder or nickel and titanium composite powder, as shown in block


20


of FIG.


3


.




In a preferred embodiment, the precursor is sprayed onto the bore surface with an air gun


43


, as shown in FIG.


2


A. Spraying preferably occurs at room temperature, as shown in block


10


of FIG.


1


.




In one preferred embodiment, the precursor comprises metallic powder that alloys with the iron to produce a surface layer which is resistant to corrosive wear caused by ethanol-based fuels. Particularly preferred alloying elements include titanium, zirconium and nickel-titanium composites which have demonstrated wear resistance at least two times better than cast iron cylinder bores that had been laser hardened, which in turn were at least two times better than cylinder bores which were untreated. The precursor coating


41


preferably has a thickness between 100-250 microns.




The method of the present invention further comprises irradiating a portion of the interior surface of the cylinder bore with a laser


44


at a sufficient energy level, and for a sufficient time, to melt the precursor and a portion of the cylinder bore substrate and to cause mixing of the melted materials so that the alloying elements are distributed into the interior surface of the bore and form an alloyed surface layer up to about 300 micrometers thick for titanium or zirconium alloyed surfaces and up to about 60 micrometers thick for the Ni—Ti alloyed surfaces, as shown in block


12


of FIG.


1


and in FIG.


2


B. In a preferred embodiment, the irradiating is performed with a fiber optic beam delivery system


46


, as shown in FIG.


2


B. Most preferably, the fiber optic beam delivery system is mounted on a periscope beam turning assembly


47


, as shown in FIG.


2


B. Irradiation intensity is sufficient to alloy the alloying elements with the bore's surface and form an alloyed layer


34


integrally formed with the substrate of the bore, as shown in FIG.


4


.




When titanium is the alloying element, the surface layer of the cylinder bore is transformed from a matrix of Pearlite with graphite flakes dispersed throughout to a matrix of Martensite with about 0.1 to about 0.3 volume fraction titanium carbide dispersed throughout, and having a microhardness of about 550 to about 830 Knoop. When zirconium is the alloying element, the surface layer of the cylinder bore is transformed from a matrix of pearlite with graphite flakes dispersed throughout to a matrix of martensite with about 0.08 to about 0.25 volume fraction zirconium carbide dispersed throughout, and having a microhardness of about 550 to about 670 knoop. When nickel-titanium (i.e. 97 wt % Ni—3 wt % Ti) powder is the alloying element, the surface layer of the cylinder bore is transformed from a matrix of Pearlite with graphite flakes dispersed throughout to a matrix of Martensite containing nickel (up to 35 wt %) with a decreasing concentration profile from the bore's surface, and with a small number (less than 3% by vol) titanium carbide particles dispersed throughout and having a microhardness of about 400 to about 500 knoop.




A laser heat-affected zone underlies the alloyed layer and has a thickness as low as about 20-40 microns for the Ni—Ti alloyed layer to about 100-200 microns for the Ti and Zr alloyed layers. Martensite alone, such as is formed by laser hardening only (i.e. without alloying), is not as effective to resist corrosive wear as when Zr or Ti carbides are present. When a high amount of nickel is present in the Martensite, the titanium carbide and zirconium carbide content can be reduced to achieve the same corrosive wear resistance.




In another preferred embodiment, the irradiating is performed with an Nd:YAG laser with a fiber optic beam delivery system and periscope beam turning assembly, as illustrated in FIG.


4


. The laser may have a power in the range of 1-3 kilowatts and operated at a standoff distance of 100-150 millimeters, as shown in FIG.


4


. The term “standoff distance”, as used herein, is the distance between the surface being irradiated and the last focusing element. In

FIG. 4

, the standoff distance is the sum of Z+R, and the last focusing element is lens


51


.

FIG. 4

also discloses the use of turning a mirror


53


to redirect the laser beam onto the interior surface of the cylinder bore.




In another preferred embodiment, the irradiation is performed with a 3 kilowatt Nd:YAG laser passed through a fiber optic delivery system to a lens assembly


47


which focuses the beam onto the cylinder bore surface. In a preferred embodiment, the laser beam is directed at an angle, θ, of 35° to the surface of the cylinder bore, and is therefore less susceptible to damage.




In one preferred embodiment, the irradiating is performed with a laser beam having (1) a rectangular cross section


50


, (as shown in FIG.


6


), (2) a cross sectional area of 1.5 square millimeters to 2.5 square millimeters, and (3) a wavelength of 1.06 microns.




A rectangular beam profile having the dimensions described above can be achieved by aligning a spherical lens closest to the beam, a second cylindrical lens closest to the substrate and a first cylindrical lens between the spherical lens and the second cylindrical lens. In one embodiment, the spherical lens should have a focal length of 101.6 millimeters, the first cylindrical lens should have a focal length of 203.2 millimeters, and the second cylindrical lens should have a focal length of 152.4 millimeters. In this same embodiment, the spherical lens and the first cylindrical lens may be spaced apart by five millimeters, and the first cylindrical lens and second cylindrical lens may be spaced apart by 15 millimeters. The spacing of the lens will affect the rectangular beam dimensions.




In a preferred embodiment, the irradiating is performed in a multiplicity of successive adjacent tracks


52


extending axially from the cylinder bore rim to a lower end region


49


, as shown in FIG.


5


. Though the tracks


52


may extend the full length of the bore, from top to bottom, they may also be provided only near the top (e.g. approximately the top 25 millimeters) of the bore where most of the corrosive wear occurs. A translation rate of 750-1500 millimeters per minute of the laser beam relative to the cylinder bore is suitable for practicing the present invention when operating at a power level of about 1200 to about 2000 watts.




Each of the tracks


52


extends from the top of the cylinder and has a length differential


54


from its adjacent track, as shown in FIG.


5


. In a preferred embodiment, this length differential is at least two millimeters. As a result, the lower end regions of the tracks form a saw toothed or zigzagged pattern


56


, as shown in FIG.


5


. The zigzagged pattern reduces and/or avoids damage from piston ring contact at the interface between the alloyed and nonalloyed regions of the bore. The spacing between the center lines of adjacent tracks is preferably less than the beam width, and each of the tracks has a length in the range of 22-28 millimeters. In a preferred embodiment, the irradiation which forms each track begins in the bore at the lower end of the track and moves upward to the cylinder bore rim.




After irradiating the present invention comprises honing the interior surface of the cylinder bore to a preselected dimension, as shown in block


14


of FIG.


1


and in FIG.


2


C. Preferably, the honing is performed using a rotatable honing tool


38


, as shown in

FIG. 2C

, and most preferably in two stages—first with an alumina stone, and second with a diamond stone, as shown in block


14


of FIG.


1


.




An automotive internal combustion engine


36


, in accordance with the present invention, comprises a multiplicity of iron cylinder bores, each of which comprises an alloyed surface layer


34


integrally formed with the substrate of the bore, and includes one or more alloying elements which enhance the corrosive wear resistance of the iron bore to corrosion.




Comparative tests were conducted to evaluate the effectiveness of laser alloying cast iron cylinder bores to improve corrosive wear resistance. More specifically, three types of samples were bench tested using a Cameron-Plint reciprocating machine that rubbed a nitrided stainless steel piston ring back and forth across the samples under an applied load of 495 MPa (hertzian stress) in the presence of a lubricant mixture comprising 40% E85 fuel, 10% water and 50% 5W30 lubricating oil. The test was conducted at 40° C. for 20 hours. Control samples were of two types—(1) untreated cast iron, and (2) laser-hardened (but not alloyed) cast iron. Test samples were laser-alloyed as set forth above using the following alloying elements (1) Ti, (2) Zr, (3) 48Ni/1A1


2


O


3


/1Fe


2


O


4


, (4) 40Ni/30Cr/28Mo/2Mn, (5) 47.5Ni/2.5Ti, (6) 48.5Ni/1.5A1, (7) 47Ni/1.5A1/1.5Mn, and (8) Ni.




These tests showed that (1) the untreated samples displayed wear depths (in microns) between about 2.9μ-18.3μ(mostly ca. 3-8μ), (2) the laser-hardened samples displayed wear depths between about 1.8μ and 2.5μ, (3) the Ti-alloyed samples displayed wear depths of 1μ or less, (4) the Zr-alloyed samples display wear depths of about 1μ, and (5) the Ni—Ti samples displayed wear depths of about 1μ. Some others samples fared better than the laser-hardened samples, but less than the preferred Ti, Zr, Ni—Ti samples. In this regard, see Table 1 wherein (1) the wear data reported in the column labeled “L” was wear experienced for tests where the rubbing of the piston ring on the cylinder bore was done in a direction parallel to the direction the laser traveled during alloying (i.e. axially of the bore); and (2) the wear data reported in the column labeled “T” was wear experienced for tests where the rubbing of the piston ring on the cylinder bore was done in a direction transverse to the direction the laser traveled during alloying (i.e. circumferentially of the bore.















TABLE 1













Wear Depth (Microns)
















Sample




“L”




“T”











Untreated




 3.3-18.3




2.9-15.4







Laser hardened




1.8-2.5




=







Ti




<1




<1







Zr




<1




<1







Ni—Ti




˜1




˜1







40 Ni/30 Cr/28 Mo/2 Mn




0.8-1.5




1.3-2.2







47 Ni/1.5 Al/1.5 Mn




  2-2.5




1.4-1.8







48.5 Ni/1.5 Al




1.5-3  




=







48 Ni/1 Al


2


O


3


/1 Fe


2


O


4






1.9-3.1




=







25 ZRB


2


/25 Ni




  1-1.5




=







Ni




2-3




=















The foregoing disclosure and description of the invention are illustrative and explanatory. Various changes in the size, shape, and materials, as well as in the details of the illustrative construction may be made without departing from the spirit of the invention.



Claims
  • 1. An improved automotive engine comprising a multiplicity of a cast iron cylinder bores, each of said bores comprising a top and an interior alloyed surface layer extending from the surface of said bore to a predetermined depth into said bore, each of said surface layers comprising at least one alloying element that enhances the corrosive wear resistance of said bore.
  • 2. The engine of claim 1, wherein said alloying elements are selected from the group consisting of titanium, zirconium, nickel-titanium composites and nickel-zirconium composites.
  • 3. The engine of claim 1, wherein said alloyed surface layer comprises titanium or zirconium and has a thickness that is less than or equal to 300 micrometers.
  • 4. The engine of claim 1, wherein said alloyed surface layer comprises nickel-titanium and has a thickness that is less than or equal to 60 micrometers.
  • 5. The automotive engine of claim 4, wherein said alloyed surface layer comprises titanium carbide particles.
  • 6. The automotive engine of claim 5, wherein the volumetric concentration of titanium carbide in said alloyed surface layer is less than three percent.
US Referenced Citations (76)
Number Name Date Kind
3705758 Haskel Dec 1972
3848104 Locke Nov 1974
3855986 Wiss Dec 1974
3986767 Rexer et al. Oct 1976
4015100 Gnanamuthu et al. Mar 1977
4017708 Engel et al. Apr 1977
4157923 Yen et al. Jun 1979
4212900 Serlin Jul 1980
4322601 Serlin Mar 1982
4434189 Zeplatynsky Feb 1984
4475027 Pressley Oct 1984
4480169 Macken Oct 1984
4495255 Draper et al. Jan 1985
4535218 Krause et al. Aug 1985
4617070 Amende et al. Oct 1986
4638163 Braunlich et al. Jan 1987
4644127 La Rocca Feb 1987
4720312 Fukuizumi et al. Jan 1988
4724299 Hammeke Feb 1988
4746540 Kawasaki et al. May 1988
4750947 Yoshiwara et al. Jun 1988
4801352 Piwczyk Jan 1989
4839518 Braunlich et al. Jun 1989
4847112 Halleux Jul 1989
4898650 Wu et al. Feb 1990
4904498 Wu Feb 1990
4964967 Hashimoto et al. Oct 1990
4981716 Sundstrom Jan 1991
4998005 Rathi et al. Mar 1991
5032469 Merz et al. Jul 1991
5059013 Jain Oct 1991
5072092 Ritcher et al. Dec 1991
5095386 Scheibengraber Mar 1992
5124993 Braunlich et al. Jun 1992
5130172 Hicks et al. Jul 1992
5147999 Dekumbis et al. Sep 1992
5196672 Matsuyama et al. Mar 1993
5208431 Uchiyama et al. May 1993
5230755 Pierantoni et al. Jul 1993
5247155 Steen et al. Sep 1993
5257274 Barrett et al. Oct 1993
5265114 Sun et al. Nov 1993
5267013 Spence Nov 1993
5290368 Gavigan et al. Mar 1994
5308431 Maher et al. May 1994
5314003 Mackay May 1994
5319195 Jones et al. Jun 1994
5322436 Horng et al. Jun 1994
5331466 Van Saarloos Jul 1994
5334235 Dorfman et al. Aug 1994
5352538 Takeda et al. Oct 1994
5363821 Rao et al. Nov 1994
5387292 Morishige et al. Feb 1995
5406042 Engelfriet et al. Apr 1995
5409741 Laude Apr 1995
5411770 Tsai et al. May 1995
5430270 Findlan et al. Jul 1995
5446258 Mordike Aug 1995
5449536 Funkhouser et al. Sep 1995
5466906 McCune, Jr. et al. Nov 1995
5484980 Pratt et al. Jan 1996
5486677 Maischner et al. Jan 1996
5491317 Pirl Feb 1996
5514849 Findlan et al. May 1996
5530221 Benda et al. Jun 1996
5546214 Black et al. Aug 1996
5563095 Frey Oct 1996
5614114 Owen Mar 1997
5643641 Turchan et al. Jul 1997
5659479 Duley et al. Aug 1997
5671532 Rao et al. Sep 1997
5766693 Rao Jun 1998
5829405 Godel Nov 1998
5874011 Ehrlich Feb 1999
5958521 Zaluzec et al. Sep 1999
6095107 Kloft et al. Aug 2000
Foreign Referenced Citations (12)
Number Date Country
4126351 Feb 1993 DE
876870A1 Apr 1998 EP
279692 Nov 1988 JP
401083676A Mar 1989 JP
381082 Apr 1991 JP
3115587A May 1991 JP
403115531A May 1991 JP
5285686 Nov 1993 JP
1557193 Apr 1990 RU
1743770 Jun 1992 RU
WO 9521720 Aug 1995 WO
WO 9747397 Dec 1997 WO
Non-Patent Literature Citations (48)
Entry
Ayers, et al.; “A Laser Processing Technique for Improving the Wear Resistance of Metals,” Journal of Metals, Aug. 1981, 19-23.
Belvaux, et al.; “A method for Obtaining a Uniform Non-Gaussian Laser Illumination,” Optics Communications, vol. 15, No. 2, Oct. 1975, 193-195.
Bett, et al.; “Binary phase zone-plate arrays for laser-beam spatial-intensity distribution conversion,” Applied Optics, vol. 34, No. 20, Jul. 10, 1995, 4025-4036.
Bewsher, et al.; “Design of single-element laser-beam shape projectors,” Applied Optics, vol. 35, No. 10, Apr. 1, 1996, 1654-1658.
Breinan et al.; “Processing material with lasers,” Physics Today, Nov. 1976, 44-50.
Bruno, et al.; “Laserbeam Shaping for Maximum Uniformity and Maximum Loss, A Novel Mirror Arrangement Folds the Lobes of a Multimode Laserbeam Back onto its Center,” Lasers & Applications, Apr. 1987, 91-94.
Chen, et al.; “The Use of a Kaleidoscope to Obtain Uniform Flux Over a Large Area in a Solar or Arc Imaging Furnace,” Applied Optics, vol. 2, No. 3, Mar. 1963, 265-571.
Christodoulou, et al.; “Laser surface melting of some alloy steels,” Metals Technology, Jun. 1983, vol. 10, 215-222.
Cullis, et al.; “A device for laser beam diffusion and homegenisation,” J. Phys. E:Sci. Instrum., vol. 12, 1979, 688-689.
Dahotre, et al., “Development of microstructure in laser surface alloying of steel with chromium,” Journal of Materials Science, vol. 25, 1990, 445-454.
Dahotre, et al., “Laser Surface Melting and Alloying of Steel with Chromium,” Laser Material Processing III, 1989, 3-19.
Fernelius, et al.; “Design and Testing of a Refractive Laser Beam Homogenizer,” Airforce Writing Aeronautical Laboratories Report, (AFWAL-TR-84-4042), Sep. 1984, 46 pages.
Frieden; “Lossless Conversion of a Plane Laser Wave to a Uniform Irradiance,” Applied Optics, vol. 4, No. 11, Nov. 1965, 1400-1403.
Galletti, et al.; “Transverse-mode selection in apertured super-Gaussian resonators: an experimental and numerical investigation for a pulsed CO2 Doppler lidar transmitter,” Applied Optics, vol. 36, No. 6, Feb. 20, 1997, 1269-1277.
Gori, et al.; “Shape-invariance range of a light beam,” Optics Letters, vol. 21, No. 16, Aug. 15, 1996, 1205-1207.
Grojean, et al.; “Production of flat top beam profiles for high energy lasers,” Rev. Sci. Instrum. 51(3), Mar. 1980, 375-376.
Hella, “Material Processing with High Power Lasers,” Optical Engineering, vol. 17, No. 3, May-Jun. 1978, 198-201.
Ignatiev, et al.; “Real-time pyrometry in laser machining,” Measurement and Science Technology, vol. 5, No. 5, 563-573.
“Laser Removing of Lead-Based Paint” Illinois Department of Transportation, Jun. 1992, 26 pages.
Jones, et al.; “Laser-beam analysis pinpoints critical parameters,” Laser Focus World, Jan. 1993, 123-130.
Khanna, et al.; “The Effect of Stainless Steel Plasma Coating and Laser Treatment on the Oxidation Resistance of Mild Steel,” Corrosion Science, vol. 33, No. 6, 1992, 949-958.
“New Products” Laser Focus World, Aug. 1996, 173.
Lugscheider, et al.; “A Comparison of the Properties of Coatings Produced by Laser Cladding and Conventional Methods,” Surface Modification Technologies V, The Institute of Materials, 1992, 383-400.
Manna, et al.; “A One-dimensional Heat Transfer Model for Laser Surface Alloying of Chromium on Copper Substrate,” Department of Metallurgical & Materials Engineering, Indian Institute of Technology, vol. 86, N. 5, May 1995, 362-364.
Mazille, et al.; “Surface Alloying of Mild Steel by Laser Melting of Nickel and Nickel/Chromium Precoatings,” Materials Performance Maintenance, Aug. 1991, 71-83.
Molian; “Characterization of Fusion Zone Defects in Laser Surface Alloying Applications,” Scripta Metallurgica, vol. 17, 1983, 1311-1314.
Molian; “Effect of Fusion Zone Shape on the Composition Uniformity of Laser Surface Alloyed Iron,” Scripta Metallurgica, vol. 16, 1982, 65-68.
Molian; Structure and hardness of laser-processed Fe-0.2%C-5%Cr and Fe-0.2%C-10%Cr alloys; Journal of Materisla Science, vol. 20, 1985, 2903-2912.
“Line-Focussing Optics for Multiple-Pass Laser Welding, ” NASA Tech Briefs MFS-29976, date unknown.
“Cylindrical Lenses,” Newport Technical Guide, date unknown, N-65.
“Fused Silica Cylindrical Lenses,” Newport Technical Guide, date unknown, N-68.
Oswald, et al.; “Measurement and modeling of primary beam shape in an ion microprobe mass analyser,” IOP Publishing Ltd., 1990, 255-259.
Renaud, et al., “Surface Alloying of Mild Steel by Laser Melting of an Electroless Nickel Deposit Containing Chromiun Carbides,” Materials & Manufacturing Processes, 6(2), 1991, 315-330.
Smurov, et al.; “Peculiarities of pulse laser alloying: Influence of spatial distribution of the beam,” J. Appl. Phys. 71(7), Apr. 1, 1992, 3147-3158.
“Spawr Integrator,” Spawr Optical Research, Inc., Data Sheet No. 512, Jun. 1986.
Veldkamp, et al.; “Beam profile shaping for laser radars that use detecttor arrays,” Applied Optics, vol. 21, No. 2, Jan. 15, 1982, 345-358.
Veldkamp; “Laser Beam Profile Shaping with Binary Diffraction Gratings,” Optics communication, vol. 38, No. 5,6, Sep. 1, 1981, 381-386.
Veldkamp; “Laser beam profile shaping with interlaced binary diffraction gratings, ” Applied Optics, vol. 21, No. 17, Sep. 1, 1982, 3209-3212.
Veldkamp; “Technique for generating focal-plane flattop laser-beam profiles,” Rev. Sci. Instru., vol. 53, No. 3, Mar. 1982, 294-297.
Walker, et al.; “Laser surface alloying of iron and 1C-1.4Cr steel with carbon,” Metals Technology, vol.11, Sep. 1984, 5 pages.
Walker, et al.; “The laser surface-alloying of iron with carbon,” Journal of Material Science vol.20, 1985, 989-995.
Wei, et al.; “Investigation of High-Intensity Beam Characteristics on Welding Cavity Shape and Temperature Distribution,” Journal of Heat Transfer, vol. 112, Feb. 1990, 163-169.
Charschan, “Lasers in industry,” Laser Processing Fundamentals, (Van Nostrand Reinhold Company), Chapter 3, Sec. 3-1, 139-145.
Fernelius, et al; “Calculations Used in the Design of a Refractive Laser Beam Homogenizer,” Airforce Writing Aeronautical Laboratories Report, (AFWAL-TR-84-4047), Aug. 1984, 18 pages.
Jain, et al.; “Laser Induced Surface Alloy Formation and Diffusion of Antimony in Aluminum,” Nuclear Instruments and Method, vol.168, 275-282, 1980.
Molian; “Estimation of cooling rates in laser surface alloying processes,” Journal of Materials Science Letters, vol. 4, 1985, 265-267.
“High Power CW Nd:YAG Laser Transformation Hardening,” Hobart Laser Products, 2 pages.
ASM Handbook, vol. 6, Welding, Brazing, and Soldering,1993.