Method for inhibiting corrosion of metal imbedded in concrete

Abstract

The corrosion of ferrous-based metals imbedded in concrete containing a chloride is inhibited by drawing the chlorides away from the metal, and then applying a composition containing ammonium carbamate or ammonium carbonate to the concrete. An agent may be added to the solution to prevent any calcium hydroxide contained in the concrete from precipitating the corrosion inhibitor.

Description

BACKGROUND OF THE INVENTION

This invention relates to controlling corrosion and, more particularly, to a method for inhibiting the corrosion of ferrous-based materials imbedded in concrete containing a chloride.

In the United States, billions of dollars have been spent in the construction of highways, freeways and their associated overpasses and bridges. One of the most important problems facing the nation is determining how to maintain the integrity of this system of roads and associated structures at an acceptable cost.

A problem which reduces the integrity of roadways, related structures and buildings located near sources of saltwater, is the corrosion of the contained reinforcing material by chloride-based deicers, seawater and other sources of chlorides. These substances continuously attack the reinforcing materials within concrete, causing the roadways and structures to degrade and ultimately fail prematurely. At a potential cost of billions of dollars, the nation is confronted with the task of repairing its highway system and other structures by removing the corroding reinforcing steel and replacing it with new reinforcing material. Yet, if the corroded steel is not replaced and corrosion is allowed to continue to critical stages, the road surfaces and structures may potentially fail catastrophically with associated human losses.

In an effort to avoid such failures and possibly to find a less expensive solution than replacing the reinforcing materials, much research has been conducted to learn how to stop the corrosion of steel imbedded in concrete. Among the publications reporting such work are the following: Mozer, Bianchi and Kesler, "Corrosion of Reinforcing Bars in Concrete," Journal of American Concrete Institute, August, 1965; Tremper, "Corrosion of Reinforcing Steel"; ASTM Special Technical Publication No. 169-A; Significance of Test and Properties of Concrete Making Materials; Spellman and Stratful, "Concrete Variables and Corrosion Testing," California Department of Public Works, Division of Highways, Materials and Research Department, Research Report No. M & R 635116; Gouda and Monfore, Journal of PCA Research and Development Laboratories, Ser. 1175, September, 1965. In addition to these publications, on August 14, 1992, DIALOG INFORMATION SERVICES published abstracts of publications which describe various tests and research projects directed to the problem of inhibiting the corrosion of steel imbedded in concrete. The abstracts describe, for example, using sodium nitrite, calcium nitrite, the lignosulphonates, and calcium magnesium acetate as corrosion inhibitors.

The published literature appears to indicate that concrete, alone, inhibits the corrosion of imbedded reinforcing steel. The corrosion may in some instances be chemical, but it is more commonly electrochemical in nature. The area of the steel where metal ions go into solution in an amount chemically equivalent to the reaction at cathodic regions is the anodic region. If the metal is iron, it goes into solution and forms ferrous ions, Fe.sup.++, plus two electrons, 2e.sup.-, to maintain an equilibrium of electrical charges. An equivalent quantity of hydrogen is plated out as a thin film at the adjacent surface regions of the metal known as the cathode. This thin film of hydrogen inhibits further corrosion of the iron surface. The anodic and cathodic reactions are summarized as follows:

At anode: Fe.fwdarw.Fe.sup.++ +2e.sup.- (1) At cathode: 2H.sup.+ +2e.sup.- .fwdarw.H.sub.2 (2)

The reaction at the cathode regions is relatively slow in alkaline media because the concentration of hydrogen is very low. This reaction rate is increased, however, by the depolarizing action of dissolved oxygen according to the following reactions:

2H.sup.+ +1/2O.sub.2 +2e.sup.31 .fwdarw.H.sub.2 O (3) Fe+H.sub.2 O+1/2O.sub.2 .fwdarw.Fe(OH).sub.2 (4) 1/2O.sub.2 +H.sub.2 O+2e.sup.- .fwdarw.2OH.sup.- (5)

The corrosion rate is proportional to the oxygen concentration, and the quantity of electricity flowing through the local galvanic cells is equivalent to the amount of metallic corrosion. With increasing anodic polarization, the overall corrosion of the metal diminishes. In ordinary conditions of reinforcing steel in concrete, where pH is high and the hydrogen ion concentration is low, and where there is essentially no oxygen supply, an anodic coating forms on the steel and stops the corrosion reaction. When chloride deicing salts are present, however, the protective iron oxide and hydrogen films are removed from the steel surface by forming soluble chloride compounds. The loss of these protective films exposes the iron or steel surface to further electrochemical attack.

Gouda and Monfore have stated, "Since areas that corrode are anodic, valuable information may be obtained on a macroscopic scale by forcing the whole metal to be anodic. This can be accomplished by applying an external voltage between the metal as an anode and an auxiliary electrode as cathode. Polarization current densities of from 1 to 1000 micro-amperes per cm.sup.2 are usually applied in such tests, presumably by approximating the values encountered in actual local cells."

Iron is above hydrogen in the electromotive force series, and corrodes readily when not imbedded in concrete and exposed to either oxygen or to hydrogen ions. Water in the open atmosphere may contain both hydrogen ions and dissolved oxygen, and thus may corrode steel.

The difficulty of developing an inhibitor to stop the corrosion of steel in concrete is evident from the amount of unsuccessful research which has so far been conducted. In the publication by Mozer, Bianchi and Kesler entitled "Corrosion of Reinforcing Bars in Concrete", the authors explain at page 927 that:

"Anodic inhibitors contain materials such as alkalies, phosphates and chromates which form either iron salts or a ferric oxide film on the anodic surface thus preventing ferrous ions from entering the solution. Such anodic inhibitors are effective only in high concentrations. If they are added in insufficient quantities, the corrosion reaction may be locally intensified. On the other hand, high concentrations may adversely affect the concrete. Therefore, the use of conventional anodic inhibitors cannot be recommended until more complete and fundamental investigations have been conducted."

In light of this statement, to avoid the local intensification of the corrosion reaction, the inhibitor should cover the entire surface of the steel and, furthermore, should not deleteriously affect the surrounding concrete.

SUMMARY OF THE INVENTION

The present invention has been made in view of the above-explained inadequacies of the known art and has as an object to provide a method of inhibiting the corrosion of metal imbedded in concrete containing chlorides, without adversely affecting the concrete.

Additional objects and advantages of the present invention will become apparent from the description which follows, or by practice of the invention.

To achieve the objects of invention, as embodied and broadly described herein, the method for inhibiting corrosion of a metal imbedded in concrete which contains a chloride according to the invention comprises:

applying water to the concrete to draw chloride ions away from the metal and into the water;

making the metal cathodic to draw chloride ions away from the metal and into the water;

removing the water containing chloride ions; and

applying a composition comprising ammonium carbonate to the concrete.

Further to achieve the objects of the invention as embodied and broadly described herein, the method for inhibiting the corrosion of a metal imbedded in concrete which contains a chloride, comprises the steps of:

applying water to the concrete to draw chloride ions away from the metal and into the water;

removing the water containing chloride ions; and

applying a composition comprising ammonium carbamate to the concrete.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

U.S. Pat. No. 5,275,752 to Hansen discloses using ammonium carbamate as an inhibitor for the corrosion of steel by chlorides, and U.S. patent application Ser. No. 08/137,931 to Hansen, filed Oct. 19, 1993, discloses using ammonium carbonate for this same purpose.

These applications to Hansen disclose that at least one part of ammonium carbamate or ammonium carbonate is required to inhibit the corrosion of one part of sodium chloride, or 0.6 parts of chloride. To stop the corrosion of steel, it is important to reduce the concentration of the chlorides in the vicinity of the steel, and to transport the inhibitor to the steel at a sufficient concentration. In view of these and other objectives, tests were conducted to determine a method to stop the corrosion of steel which is imbedded in concrete.

The problems associated with inhibiting the corrosion of steel imbedded in concrete can be better understood by knowing the chemistry of ammonium carbamate and the ammonium carbonates, and knowing that these two chemicals may react with any lime or calcium hydroxide produced in concrete during setting.

Ammonium carbamate, NH.sub.2 COONH.sub.4, is produced by reacting two moles of ammonia with one mole of carbon dioxide under high pressure conditions. An important characteristic of ammonium carbamate is that it may hydrate to ammonium carbonate. In "Urea Its Properties and Manufacture," George Tsei-yu Chao explains at page 202 that:

"It is a generally wrong impression that ammonium carbamate will combine with water to form ammonium carbonate very quickly. However, the facts show that ammonium carbamate is a much more stable compound than ammonium carbonate. The rate of hydration of ammonium carbamate is very slow, not only in the solid state, but also in a water solution. The reaction of ammonium carbamate with water reaches a limit after long standing." (Emphasis added).

Chao further explains on page 204 that "The effect of time on the degree of hydration of ammonium carbamate was studied for around 2 and 6 per cent solutions . . . Even at such dilute concentrations, the hydration never exceeds 80 per cent even after 24 hours".

According to Chao, the hydration of ammonium carbamate produces a double salt known as ammonium carbonate. The double salt is one part ammonium carbamate and one part ammonium bicarbonate, and forms according to the chemical reaction:

NH.sub.2 COONH.sub.4 .fwdarw.NH.sub.4 HCO.sub.3.NH.sub.2 COONH.sub.4 +NH.sub.3

Ammonium carbamate is more stable than ammonium carbonate, and it probably has to hydrate to ammonium carbonate to become reactive. Less than 80% of the ammonium carbamate hydrates, even in a 2% to 6% solution, and only one-half of the double salt that is produced is the reactive compound ammonium bicarbonate. The release of ammonia explains the fact that excess ammonia inhibits the hydration of ammonium carbamate to ammonium carbonate.

Using the information provided by Chao, the following calculations estimate the conditions which may exist in a 3% water solution of ammonium carbamate and ammonium carbonate that is allowed to stand for at least 24 hours.

From a 3% solution, 80% of the ammonium carbamate may hydrate, and the associated ammonia released will react with the water to produce ammonium hydroxide. The following chemical reaction gives the calculated products based on ammonium carbamate having a molecular weight of 78, water of 18, ammonium bicarbonate of 79 and ammonium hydroxide of 35. ##STR1## The resulting products of this reaction would be:

(a) [(3% .times.0.8)/(2.times.78)].times.(78+79)=2.42% of the double salt which consists of 1.2% ammonium carbamate and 1.22% of ammonium bicarbonate;

(b) [(3% .times.0.8)/(2.times.78)].times.35=0.54% of ammonium hydroxide; and

(c) 3% .times.0.2=0.6% of the ammonium carbamate is not reacted.

From the 3% ammonium carbamate solution, after 80% of the ammonium carbamate had hydrated, only 1.22% of ammonium bicarbonate would be available to react with any calcium hydroxide present in the concrete. The remaining 1.8% (0.6%+1.2%) would remain as ammonium carbamate in the presence of 0.54% ammonium hydroxide, and retard the hydration of the remaining ammonium carbamate.

Commercial ammonium carbonate is the same double salt that is hydrated from ammonium carbamate, namely NH.sub.4 HCO.sub.3.NH.sub.2 COONH.sub.4. For a 3% solution of ammonium carbonate, if 80% of the ammonium carbamate of the double salt were to hydrate according the following chemical reaction: ##STR2##

The products of the reaction would be:

(a) (3% .times.0.2)=0.6% of the double salt remaining of which about 0.3% is ammonium bicarbonate and about 0.3% is ammonium carbamate;

(b) [(3% .times.0.8)/314](158)=1.21% of ammonium bicarbonate produced from hydrating the ammonium carbamate contained in the ammonium carbonate;

(c) [(3% .times.0.8)/314](158)=1.21% of ammonium bicarbonate released when the associated ammonium carbamate is hydrated; and

(d) [(3% .times.0.8)/314](35)=0.27% ammonium hydroxide.

After hydration of the ammonium carbonate had occurred, the resulting composition would be 0.3% ammonium carbamate, 2.42% ammonium bicarbonate and 0.27% ammonium hydroxide, as set forth in TABLE 1.

TABLE I______________________________________Products of Hydration (wt. %)Compound Ammonium Ammonium Ammonium AmmoniumIn Solution Carbamate Carbonate Bicarbonate Hydroxide______________________________________Ammonium 1.8 2.42* 1.22 0.54CarbamateAmmonium 0.3 0.6* 2.42 0.27Carbonate______________________________________ *About onehalf of the ammonium carbonate is ammonium bicarbonate and abou onehalf is ammonium carbamate and these percentages are included in the percentages of ammonium carbamate and ammonium bicarbonate.

These calculations are estimates of the actual percentages of the various products of hydration. They are presented for the purposes of illustrating the relative concentrations of the chemicals which may exist in water solutions, and explaining why ammonium carbamate is less reactive with respect to calcium hydroxide than ammonium carbonate. These calculations also explain why ammonium carbamate is more stable in inhibiting the corrosion of steel in concrete than is ammonium carbonate. The test results described below were performed to find the compositions and methods which would stop and then inhibit the corrosion of steel which is imbedded in concrete.

Testing Procedures

A modified version of the method used by Gouda and Monfore was used to demonstrate the inhibiting effect that both ammonium carbamate and ammonium carbonate have on steel imbedded in concrete, and to determine a method for using these compounds to stop the corrosion of the steel. All tests were conducted at ambient temperature.

The test pieces used in each test were made by cutting cylindrical 1/4 inch reinforcing steel into 43/8 inch lengths. The test pieces were cleaned with a 1-1-1 trichloroethane solvent. The bottom 1/8 inch of each test piece was then coated with paraffin wax. A 1/2 inch wide coating of wax was also applied around each of the test pieces at about 3.0 to 31/2 inches from the bottom edge. The distance of 27/8 inches (7.3 cm) between the wax coatings gave an exposed surface area on the test pieces of 14.6 cm.sup.2.

For each test, the following concrete mixture was used:

______________________________________1/4 inch gravel 216.5 gramsSand 84.5 gramsType II Cement 64.0 gramsSodium chloride 1.6 grams (2.5 wt. % of cement)Water 35.0 gramsTotal 501.6 grams______________________________________

This mix produced a relatively dry concrete, which contained sufficient water to be formed into a cylinder. The sodium chloride was dissolved in and added with the water to approximate the condition that exists in concrete after it has absorbed a solution of salt or sodium chloride which causes the contained reinforcing steel to corrode.

The concrete mix was cast into a cylindrical polystyrene container having a 46 mm diameter and a 107 mm height. Next, 56, 3/16 inch diameter holes were drilled in the side of each container, and 13 holes were drilled into the bottom. A steel test piece was imbedded in each of the cylinders of concrete to a depth of about 31/4 inches, exposing 14.6 cm.sup.2 of the test pieces to the concrete.

After the concrete set for at least 24 hours, the concrete and imbedded steel test pieces were placed into various solutions of ammonium carbamate or ammonium carbonate to stop the corrosion of the steel. While in the solutions, the steel test pieces were connected into a circuit, as described by Gouda and Monfore, to determine the effect of the inhibitors in stopping the corrosion of the steel.

The test pieces were immersed so that the top of the concrete was approximately even with the top of the solution. The solution was contained in a 1500 ml beaker along with a platinum electrode connected to the negative side of two 1.5 volt batteries connected in series. The positive end of the batteries was connected through two 10,000 ohm resistors, a 2,500 ohm resistor, and a 1,000 ohm resistor, arranged in series. The opposite terminal of the resistors was connected to the positive terminal of an electronic ammeter. The negative pole of the ammeter was connected to the top of the steel piece being tested so as to impose a positive charge upon the steel piece and make it anodic.

In addition to the concrete cylinder and the platinum electrode, a saturated potassium chloride bridge was also immersed in the solution being tested. The bridge was part of a circuit which connected the test solution to a saturated potassium chloride solution in an adjoining container in which a calomel electrode was immersed. The calomel electrode was connected to a terminal of an electronic voltmeter and the other terminal of the voltmeter was connected to the top of the steel test piece. This second circuit was used to measure the potential difference between the calomel electrode and the steel test piece when a positive charge was imposed on the steel test piece to cause a current of about 10 .mu.a/cm.sup.2 to flow through its surface.

After the corrosion of the steel test piece had been stopped, an anodic coating would build on the test piece and produce a high potential difference between it and the calomel electrode. In those instances when the corrosion produced by the sodium chloride contained in the concrete was not stopped, the test piece became negative relative to the calomel electrode.

The potential difference between the steel test piece and the calomel electrode of each of the corrosion inhibitors was, except for two tests, at a constant current density of about 10 .mu.a/cm.sup.2.

The following working examples are provided to illustrate some of the advantages of the invention and are not limitative of its scope. All parts and percentages are by weight unless otherwise indicated.

EXAMPLE 1

Test No. G21C1 was conducted to illustrate the effects of not reducing the concentration of chlorides surrounding a steel test piece. Without preliminarily soaking the concrete and imbedded steel test piece in distilled water, or in a water solution of ammonium carbamate, the concrete and steel test piece was immersed in a 2.8% solution of ammonium carbamate in distilled water. The results measured for this test are set forth in TABLE 1.

TABLE 1______________________________________Test No. G21C1 ElapsedCurrent time Voltage.mu.a/cm.sup.2 (min) (mv) Remarks______________________________________ 0 0 -205 no imposed current on steel electrode13 10 -7 190 .mu.a flowed through exposed 14.6 cm.sup.2 of the steel test piece13 20 -7613 30 -10813 40 -126 insufficient ammonium carbamate reaching steel to stop corrosion13 50 -13913 60 -14613 460 -177The applied current was turned off until following day.13 1340 -390 no imposed current on steel test piece13 1350 -500 190 .mu.a flowed through the test piece13 1360 -69 sufficient ammonium carbamate apparently reaching electrode to begin to form an anodic coating13 1370 +8013 1380 +16313 1390 + 17113 1400 +131 small mobile chloride ions causing erratic voltage13 1410 +11213 1420 +18013 1430 -20 chloride ions again dissolving the anodic coating, exposing the test piece to further corrosion13 1440 -3013 1450 -57______________________________________

EXAMPLE 2

In Test No. G24C1, the concrete and imbedded steel test piece was preliminarily immersed overnight in a 3% water solution of ammonium carbamate. The results of this test are reported in TABLE 2. Comparing these results with those for Test No. G21C1 given in TABLE 1, the preliminary immersion at least partially reduced the concentration of the chloride ions in the vicinity of the electrode, and also transported some amount of ammonium carbamate directly to the electrode.

TABLE 2______________________________________Test No. G24C1 ElapsedCurrent time Voltage.mu.a/cm.sup.2 (min) (mv) Remarks______________________________________0 0 -250 no imposed current on steel electrode8.5 10 -210 125 .mu.a flowed through the steel8.5 20 -298.5 30 +170 soaking the test piece overnight in a 3% solution of ammonium carbamate enabled sufficient ammonium carbamate to reach the steel and form an anodic coating, but the chloride ions were so mobile that positive charge on the steel attracted sufficient chloride ions to dissolve the anodic coating and leave it exposed to corrosion8.5 40 +4008.5 50 +4808.5 55 +5058.5 60 +4958.5 70 +3958.5 80 +2708.5 90 +1538.5 100 +748.5 110 +748.5 120 +588.5 130 +568.5 140 +738.5 155 +508.5 160 +978.5 170 +72______________________________________

EXAMPLE 3

Test No. G28C1 was conducted to determine a method to remove a maximum percentage of the chloride ions within the concrete from the test piece surface and the surrounding area, which also allows the ammonium carbamate to move through the concrete and build an anodic coating on the test piece.

In this test, the concrete and imbedded steel test piece was immersed in distilled water for two days to draw a maximum amount of the chloride ions from within the concrete. After the two-day period, the water containing the chloride ions was removed and the test piece was placed in a water solution containing 6% ammonium carbamate. To allow the ammonium carbamate sufficient time to reach the test piece, the test piece was immersed in this solution for one day. At the end of one day, a positive voltage was imposed on the electrode and 150 .mu.a was caused to flow through it. The results of this test are illustrated in TABLE 3.

TABLE 3______________________________________Test No. G28C1 ElapsedCurrent time Voltage.mu.a/cm.sup.2 (min) (mv) Remarks______________________________________ 0 0 -350 no imposed current on the electrode10 10 -50 150 .mu.a flowed through steel10 15 +1010 20 +144 The two day immersion in distilled water removed sufficient chloride ions from the electrode to enable the additional one day immersion in a 6% solution of ammonium carbamate to reach the steel test piece and promote formation of an anodic coating on the electrode to inhibit further corrosion of the test piece.10 25 +23410 30 +44010 35 +51510 40 +55510 45 +62510 50 +64510 55 +65510 60 +66510 65 +67010 70 +67710 75 +68010 80 +68510 85 +68510 90 + 68510 95 +690______________________________________

EXAMPLE 4

In Test No. G28C2, the test piece, as in Test No. G28C1, was immersed in distilled water for two days to draw a maximum amount of the chloride ions away from the concrete. After two days, the water was removed and the concrete and test piece was placed in a 3% solution of ammonium carbamate for one additional day before an electric current was applied to the electrode to make it anodic. The lower 3% concentration of ammonium carbamate was used to determine the effect of the solution concentration on the test results. The results are set forth in TABLE 4.

TABLE 4______________________________________Test No. G28C2 ElapsedCurrent time Voltage.mu.a/cm.sup.2 (min) (mv) Remarks______________________________________ 0 0 -285 no imposed current on electrode10 5 -61 150 .mu.a flowing through steel10 10 -3010 15 +75 As in Test No. G28C1, the two day immersion in distilled water drew enough chlorides away from the electrode to allow the additional one day soak in a 3% solution of ammonium carbamate to penetrate the concrete and promote formation of an anodic coating on the electrode and inhibit further corrosion of the steel test piece.10 20 +18210 25 +43010 30 +53510 35 +59010 40 +62010 45 +64010 50 +65310 55 +66510 60 +67010 65 +67510 70 +68010 75 +68510 80 + 68710 85 +68510 90 +690______________________________________

As explained above, at least one part of ammonium carbamate is required to inhibit the corrosion of about 0.6 parts of chloride. Furthermore, to inhibit corrosion it is important to reduce the concentration of chloride and to increase the concentration of the ammonium carbamate in the area of the test piece surface. Based on the results of Examples 3 and 4, the two day immersion in distilled water drew a sufficient amount of chloride ions from the test pieces to enable the ammonium carbamate solutions to penetrate the concrete and build an anodic coating on the imbedded steel and inhibit corrosion.

Regarding the rate of build up of the anodic coating, the test results indicate that there is a minor difference between the effects of 3% and 6% solutions of ammonium carbamate. Because the amount of chloride, and the porosity and general condition of the concrete may vary significantly, the concentration of ammonium carbamate in the applied solutions and the amount of time the solutions are applied to the concrete have to be controlled as mandated by the encountered conditions. For example, for increasing levels of porosity or decreasing concentration of chloride, a smaller application period would be needed because the ammonium carbamate would be able to reach the test piece in a decreasing amount of time. Also, the temperature of the environment may affect the rate at which the corrosion inhibitor reaches the test piece.

EXAMPLE 5

In this test, ammonium carbonate was used as the corrosion inhibitor. It was learned that a two day immersion of the concrete and test piece in distilled water, followed by a one day immersion in an ammonium carbonate solution does not, under the test conditions, stop the corrosion of imbedded steel. It was determined that additional measures are required for this purpose. Particularly, a procedure was sought to draw a larger percentage of chloride ions away from the steel test piece, and further to prevent the ammonium carbonate from being precipitated by any calcium hydroxide present in the concrete as a product of setting.

It was determined that the following procedure achieves both objectives: (1) immersing the concrete and test piece in distilled water for two days; (2) while still immersed in the distilled water, making the steel test piece cathodic and the platinum electrode anodic, so as to drive the negative chloride ions, Cl.sup.-, away from the steel test piece and into the surrounding water; and (3) after the reverse current treatment of the steel test piece, removing the water containing chloride ions and possibly calcium hydroxide and then placing the concrete and test piece in a water solution containing 4.1% ammonium carbonate and an agent which prevents calcium hydroxide from precipitating ammonium carbonate as calcium carbonate.

Such an agent has to either precipitate or complex calcium. Suitable reagents are, for example, the ortho and polyphosphates, sodium carbonate, the sodium or potassium silicates, and chelating agents such as EDTA. Because concrete is a calcium silicate, sodium silicate was selected as the agent to use in this test to precipitate any calcium hydroxide present. Because sodium silicate produces a silica gel in ammonium carbonate solutions, a weak solution of sodium silicate must be used. A 0.25% solution of Philadelphia Quartz's "O" Silicate was determined to be a suitable solution. The concrete and imbedded steel test piece was immersed in a solution of 4.1% ammonium carbonate plus 0.25% "O" Silicate for one day before the test was started.

At regular time intervals during the test, the pH of the solution was measured and recorded, and the concentration of chloride in the solution was measured and recorded.

The test piece in this Test No. J12C1 was made cathodic with a current of 300 .mu.a, or 20 .mu.a/cm.sup.2, flowing through it. The test results are given in TABLE 5.

TABLE 5______________________________________Test No. J12C1Elapsedtime Voltage [Cl.sup.- ](min) (mv) pH (ppm) REMARKS______________________________________ 0 -775 8.6810 -74020 -77030 -79040 -80450 -82060 -830 8.80 32070 -70380 -84090 -855100 -860 chloride concentration not increasing and large negative voltage suggested that coating had been removed from electrode, and that additional reverse current will remove little additional chlorides from test piece110 -865120 -885 8.82 320130 -835140 -1500150 -953160 -953170 -950180 -925 8.71 310______________________________________

In this test, 1.6 grams of sodium chloride was added to the 500 gram mix. About 450 grams of this mix was formed into a concrete test piece. The concrete contained 1.6(450/500)=1.44 grams of sodium chloride, or (1.44/58.5)35.5=0.87 gram of chloride. At a concentration of 320 ppm of chloride in 1100 grams of test solution, the test solution contained 0.000320.times.1100=0.352 gram of chloride that had been drawn out of the concrete. This procedure removed 0.352 g/0.87 g=40% of the chloride from the test piece.

The data reported below in TABLE 6 give the potential between the steel test piece imbedded in concrete, treated as described above, and then immersed in a 4.1% water solution of ammonium carbonate plus 0.25% of "O" silicate. The electrode was made anodic relative to a calomel electrode and 150 .mu.a of current was caused to flow through the 14.6 cm.sup.2 of exposed electrode. TABLE 6 illustrates the results measured for this test.

TABLE 6______________________________________ ElapsedCurrent time Voltage.mu.a/cm.sup.2 (min) (mv) Remarks______________________________________ 0 0 0 no imposed current on electrode10 15 -675 150 .mu.a flowed through the steel10 25 -648 as test began, high negative voltage indicated that anodic coating had been removed from electrode10 35 -62810 45 -62010 55 -60310 65 -59110 75 -579 readings showed voltage becoming increasingly positive, indicating that anodic coating was forming10 85 -57310 95 -56210 105 -55310 115 -54610 125 -53010 135 -52010 155 -47110 165 -42010 175 -31810 185 -23010 195 -15010 205 010 215 -1010 220 +6210 225 +123The anodic coating was building and test stopped overnight. 0 0 -250 no current imposed on electrode10 5 -150 150 .mu.a flowing through electrode10 10 -7210 15 +310 20 +12310 25 +22010 30 +30210 35 +38010 40 +44210 45 +49910 50 +551 The corrosion of the test piece was stopped.10 60 +62010 70 +63010 80 +64210 90 +64610 100 +650______________________________________

EXAMPLE 6

This test, Test No. J28C1, was a duplicate of Example 5 so as to confirm the results of Test No. J12C1. The steel test piece was made cathodic and a current of 300 .mu.a, or 20 .mu.a/cm.sup.2, was caused to flow through it.

TABLE 7______________________________________Test No. J28C1Elapsedtime Voltage [Cl.sup.- ](min) (mv) pH (ppm) REMARKS______________________________________ 0 -420 11.63 18010 -45520 -60230 -65040 -655 current flow erratic, voltage was -1000mv five minutes earlier50 -850 11.62 18060 -76070 -72580 -88090 -950100 -710 11.67 180120 -790130 -985140 -800150 -775The applied electric current was turned off overnight.-475 11.40 190-670-750-835 11.35 200______________________________________

As in Test No. J12C1, there were about 1.44 grams of sodium chloride, or 0.87 grams of chloride, in the concrete. An amount of 200 ppm of chloride in 1100 grams of solution equals 0.22 grams of chloride removed from the concrete. This amount indicates that 0.22 g/0.87 g=25% of the chloride was leached from the concrete. This percentage is only 25%/40%=63% of the amount of chloride leached in Test No. J12C1. Although a lower percentage of chlorides had been removed, the ammonium carbonate still inhibited the corrosion of the imbedded steel.

As in Test No. J12C1, the data reported in TABLE 8 below give the potential between the steel test piece imbedded in concrete, treated as described above, and then immersed in a 4.1% water solution of ammonium carbonate plus 0.25% of "O" silicate. The electrode was made anodic relative to a calomel electrode and 150 .mu.a of current was caused to flow through the 14.6 cm.sup.2 of exposed electrode.

TABLE 8______________________________________Test No. J28C1 ElapsedCurrent time Voltage.mu.a/cm.sup.2 (min) (mv) Remarks______________________________________ 0 0 -675 no current imposed on electrode10 5 -628 150 .mu.a flowed through the steel10 15 -598 as test started, high negative voltage indicated that anodic coating had been removed from electrode10 25 -57410 35 -55510 45 -53910 55 -52410 65 -502 each reading showed voltage becoming increasingly positive, indicating that anodic coating was forming and corrosion stopped10 75 -47710 85 -43710 95 -36810 105 -27210 115 -20010 125 -12210 135 -5510 145 +5210 155 +17310 165 +300 corrosion stopped10 175 +44710 185 +51810 195 +55110 205 +57410 215 +576______________________________________

It will be apparent to those skilled in the art that the described method is suitable for use with metals other than mild steel. For example, it may be used for other types of ferrous-based metals such as steel and cast iron. In addition, the method is suitable for use in situations where the source of chloride ions is other than sodium chloride.

In addition, it will be apparent to those skilled in the art that instead of immersing the concrete and imbedded metal in water and then in a corrosion inhibiting solution, the water and solution may optionally be applied to the concrete by spraying and the like.

The foregoing description of the preferred embodiment of the invention has been presented to illustrate the principles of the invention and not to limit the invention to the particular embodiment illustrated. It is intended that the scope of the invention be defined by all of the embodiments encompassed within the following claims, and their equivalents.

Claims

1. A method for inhibiting corrosion of a metal imbedded in concrete which contains a chloride, comprising the steps of:

applying water to the concrete to draw chloride ions away from the metal and into the water;

imposing a negative voltage to the metal to cause electric current to flow through the metal and repel chloride ions away from the metal and into the water;

removing the water containing chloride ions; and

applying a composition comprising a corrosion inhibiting effective amount of ammonium carbonate to the concrete.

2. The method of claim 1, wherein water is applied to substantially the entire outer surface of the concrete.

3. The method of claim 2, wherein water is applied to the concrete by immersing concrete in water.

4. The method of claim 2, wherein the water is distilled water.

5. The method of claim 1, wherein the concrete further contains calcium hydroxide, and the steps of applying water to the concrete and imposing a negative voltage to the metal draw calcium hydroxide away from the metal and into the water.

6. The method of claim 1, wherein the step of imposing a negative voltage to the metal comprises applying a sufficient negative voltage to cause about 20 .mu.a/cm.sup.2 of electric current to flow through the metal.

7. The method of claim 1, wherein the composition is a water solution of ammonium carbonate.

8. The method of claim 7, wherein the water solution comprises an effective amount of ammonium carbonate to inhibit the corrosion of the metal by the chloride ions.

9. The method of claim 8, wherein the water solution is applied to the concrete for an effective amount of time to allow the ammonium carbonate to reach the metal and form an anodic coating on the metal surface.

10. The method of claim 5, wherein the composition further comprises an effective amount of an agent to inhibit the calcium hydroxide from precipitating the ammonium carbonate as calcium carbonate.

11. The method of claim 10, wherein the agent is sodium silicate.

12. The method of claim 1, wherein the chloride is sodium chloride.

13. The method of claim 11, wherein the metal is a ferrous-based metal.

14. A method for inhibiting the corrosion of a metal imbedded in concrete which contains a chloride, comprising the steps of:

applying water to the concrete to draw chloride ions away from the metal and into the water;

removing the water containing chloride ions; and

applying a composition comprising a corrosion inhibiting effective amount of ammonium carbamate to the concrete.

15. The method of claim 14, wherein water is applied to substantially the entire outer surface of the concrete.

16. The method of claim 15, wherein water is applied to the concrete by immersing concrete in water.

17. The method of claim 15, wherein the water is distilled water.

18. The method of claim 14, wherein the concrete further contains calcium hydroxide, and the step of applying water to the concrete draws calcium hydroxide away from the metal and into the water.

19. The method of claim 14, wherein the composition is a water solution of ammonium carbamate.

20. The method of claim 19, wherein the water solution comprises an effective amount of ammonium carbamate to inhibit the corrosion of the metal by the chloride ions.

21. The method of claim 20, wherein the water solution is applied to the concrete for an effective amount of time to allow the ammonium carbamate to reach the metal and form an anodic coating on the metal surface.

22. The method of claim 14, wherein the chloride is sodium chloride.

23. The method of claim 22, wherein the metal is a ferrous-based metal.