Patent Application
20050146068
1. Field of the Invention
The invention relates to a method for making a foam sheet, more particularly to a method for making a foam sheet having ventilation holes.
2. Description of the Related Art
A foam sheet made of polyurethane is formed with a plurality of holes spontaneously after foaming. Therefore, the insole made therefrom has good ventilation. However, polyurethane is a relatively expensive material for the insole. Another kind of foam sheet for the insole is made of ethylene-vinyl acetate copolymer (EVA), which is relatively inexpensive as compared to polyurethane. However, the foam sheet made of EVA is not formed with ventilation holes after foaming. Therefore, additional processing is required to provide the ventilation holes for the foam sheet made of EVA. As shown in
Although the aforesaid method can provide the foam sheet 5 with the ventilation holes 501, it has the following shortcomings:
1. When the foam sheet 5 is pierced by the solid pin 6, the elasticity of portions of the foam sheet 5 near the ventilation holes 501 may be reduced due to the punching action of the solid pin 5.
2. Waste 502 of the foam sheet 5 as a result of removal by the hollow pin 7 can not be reused.
3. When the EVA blank 3 is foamed and crosslinked by heating, the portion of the EVA blank 3 distal from the mold has a slower reaction time as compared to the portion of the EVA blank 3 proximate to the mold. It is required to lengthen the reaction time so as to complete the foaming and crosslinking of the EVA blank 3. Therefore, a large amount of energy is required to complete the foaming of the EVA blank 3.
4. The ventilation holes 501 formed by the piercing of the solid pin 6 or the hollow pin 7 will result in scratches at the annular surfaces thereof due to the punching of the solid pin 6 or the hollow pin 7.
Therefore, the object of the present invention is to provide a method for making a foam sheet having ventilation holes, which will provide the foam sheet with the ventilation holes spontaneously after foaming, which is relatively efficient in terms of energy and blank usage, and which enhances the quality of the foam sheet product.
In one aspect of this invention, the method for making a foam sheet having ventilation holes according to this invention includes the steps of: (a) preparing first and second molds, each of which includes lower and upper mold parts separably closed to each other so as to define first and second mold cavities for the first and second molds, respectively, and providing the second mold with a plurality of pins extending into the second mold cavity, the second mold cavity of the second mold being larger than the first mold cavity of the first mold; (b) placing a foamable blank into the first mold cavity of the first mold; (c) foaming the blank in the first mold cavity; (d) placing the blank foamed in step (c) into the second mold cavity, and piercing the blank through the use of the pins; and (e) foaming the blank to form a foam product within the second mold cavity while being pierced by the pins.
In another aspect of this invention, the method for making a foam sheet having ventilation holes according to this invention includes the steps of: (a) preparing a mold including lower and upper mold parts separably closed to each other so as to define a mold cavity, and providing the mold with a plurality of pins extending into the mold cavity; (b) placing a foamable blank into the mold cavity of the mold, and piercing the blank through the use of the pins; and (c) foaming the blank to form a foam product in the mold cavity of the mold while piercing the blank.
Other features and advantages of the present invention will become apparent in the following detailed description of the preferred embodiments with reference to the accompanying drawings, of which:
Referring to
A) preparing first and second molds:
As shown in
B) placing a foamable blank within the first mold:
As shown in
C) foaming the blank within the first mold:
The first mold 10 is heated to a temperature between the first and second foaming temperatures so as to permit the first foaming agent (I) to react in the first mold cavity 13 of the first mold 10 and to initiate foaming of the blank 100. At this time, the second foaming agent has yet to react since the temperature in the first mold cavity 13 of the first mold 10 is lower than the second foaming temperature of the second foaming agent (II).
D) removing the blank foamed in step C) from the first mold:
When the first foaming agent (I) has reacted completely, the first mold 10 is opened, and the blank 100 foamed in step C) is removed from the first mold cavity 13. The blank 100 expands continuously outside the first mold cavity 13 due to the elevated temperature thereof to form a semi-foamed blank 200.
E) placing the semi-foamed blank within the second mold:
As shown in
F) foaming the blank in the second mold to form a foam product:
The second mold 20 is heated to the second foaming temperature of the second foaming agent (II) so as to permit the second foaming agent (II) to react in the second mold cavity 24 of the second mold 20 and to foam the semi-foamed blank 300 to form a foam product 300 within the second mold cavity 24 while being pierced by the pins 23.
G) cooling the foam product:
The foam product 300 formed within the second mold cavity 24 is cooled so as to solidify the foam product 300. The second mold 20 is then opened, and the foam product 300 is removed from the second mold 20.
H) slicing and dividing the foam product:
The foam product 300 having a plurality of through-holes 310 is sliced and divided into a plurality of foam sheets 400 having a plurality of ventilation holes 410.
In view of the foregoing, the method of this invention can achieve the following advantages over the prior art:
(1) Since the blank 200 is foamed to form the foam product 300 within the second mold cavity 24 while being pierced by the pins 23, the foam product 30 is formed with a plurality of through-holes 310 simultaneously. Additional punching processing is not required after the foam product is formed. Therefore, the shortcomings of the prior art in respect to waste and scratches at the ventilation holes can be overcome.
(2) Since the second mold 20 is provided with a plurality of pins 23, the heat can be conducted to the blank 200 via the pins 23 when the second mold 20 is heated. Therefore, the energy and the reaction time required to foam the blank 200 when forming the foam product 300 can be reduced.
Referring to
Referring to
1) preparing a mold:
The mold includes lower and upper mold parts separably closed to each other so as to define a mold cavity. The mold is further provided with a plurality of pins extending into the mold cavity.
2) placing a foamable blank into the mold:
A foamable blank is placed into the mold cavity of the mold, and is pierced through the use of the pins.
3) foaming the foamable blank to form a foam product:
The foamable blank is foamed to form a foam product having a plurality of through-holes in the mold cavity of the mold while piercing the foamable blank.
4) cooling the foam product:
The foam product is cooled in the mold cavity of the mold.
5) removing the foam product:
The foam product after cooling is removed from the mold cavity of the mold.
6) slicing and dividing the foam product:
The foam product is sliced and divided into a plurality of foam sheets having a plurality of ventilation holes.
In addition to EVA, other materials customarily used in the art, such as styrene butadiene rubber or acrylonitrile butadiene rubber, can be used as the primary component of the foamable blank. Furthermore, in addition to the insole, the foam sheet made by the method of the present invention can be used in other applications, such as a cushion mounted within a shoulder strap of a back-pack, a shoulder pad for garments, a filler for a knee protector, and the like.
While the present invention has been described in connection with what is considered the most practical and preferred embodiments, it is understood that this invention is not limited to the disclosed embodiments but is intended to cover various arrangements included within the spirit and scope of the broadest interpretation so as to encompass all such modifications and equivalent arrangements.